DECORATIVE PART MADE BY INLAYING

Abstract

A method is for manufacturing a part including a support provided with at least one hollow filled with an aesthetic element forming a decoration on a face of the part intended to be visible. The method includes providing the support provided with the at least one hollow and providing a preform intended to form the aesthetic element of the part, and inlaying by pressing the preform into the at least one hollow of the support. The preform is made of a crystalline aluminium alloy. The inlaying is carried out at a temperature between the solidus temperature and the liquidus temperature of the crystalline aluminium alloy.

Claims

1-20. (canceled)

21. A method for manufacturing a part comprising a support provided with at least one hollow filled with an aesthetic element forming a decoration on a face of the part configured to be visible, said method comprising: providing the support provided with said at least one hollow and providing a preform configured to form the aesthetic element of the part; and inlaying by pressing the preform into said at least one hollow of the support, wherein the preform is made of a crystalline aluminium alloy, and wherein the inlaying is carried out at a temperature between the solidus temperature and the liquidus temperature of the crystalline aluminium alloy.

22. The method according to claim 21, wherein the support is made of a material chosen from among ceramic, sapphire and enamel.

23. The method according to claim 21, wherein the support is made of a zirconia-based ceramic.

24. The method according to claim 21, wherein the crystalline aluminium alloy is a 7075 alloy.

25. The method according to claim 21, wherein the support is preheated prior to the inlaying to a temperature comprised between 300 and 500° C.

26. The method according to claim 21, wherein the inlaying by hot pressing is carried out under a load of between 500 and 1000 kg.

27. The method according to claim 21, wherein the inlaying by hot pressing is carried out at a temperature comprised between 500 and 650° C.

28. The method according to claim 21, further comprising, after the inlaying, electrochemical surface treating the aesthetic element.

29. The method according to claim 28, wherein said electrochemical surface treating is carried out after mechanical grinding following the inlaying.

30. The method according to claim 28, wherein said at least one hollow opens out at several places on a face of the part configured to be non-visible, to respectively form one or more contact points for supplying current across the aesthetic element during the surface treatment.

31. A part comprising: a support provided with at least one hollow filled with an aesthetic element forming a decoration on a visible face of the part said aesthetic element being made of a crystalline aluminium alloy.

32. The part according to claim 31, wherein the support is made of a material chosen from among ceramic, sapphire and enamel.

33. The part according to claim 31, wherein the support is made of a zirconia-based ceramic.

34. The part according to claim 31, wherein the crystalline aluminium alloy is a 7075 alloy.

35. The part according to claim 31, wherein said at least one hollow opens in one or more places onto a face of the part that is configured to be non-visible,

36. The part according to claim 31, wherein the part is an external component for horology or jewellery.

37. The part according to claim 36, wherein the part is a watch bezel forming the support with at least one hollow filled with the crystalline aluminium alloy forming as the aesthetic element an index or an annular portion of the bezel.

38. The part according to claim 36, wherein the part is a case middle forming the support with at least one hollow filled with the crystalline aluminium alloy forming as the aesthetic element a portion of the case middle extending as far as a horn of the case middle.

39. The part according to claim 38, wherein said at least one hollow communicates with a bar hole arranged in the horn.

40. The part according to claim 31, wherein the aesthetic element comprises an anodized layer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0007] FIG. 1 represents a plan view of a decorative part, and in particular, a watch bezel comprising aluminium alloy indices produced by inlaying with the method according to the invention.

[0008] FIG. 2 represents a partial sectional view of this same decorative part.

[0009] FIGS. 3 to 7 schematically represent the steps of inlaying the aluminium alloy preform in the support with the method according to the invention.

[0010] FIGS. 8 and 9 respectively represent two variants of the means implemented according to the invention for holding the aesthetic element within the hollow.

[0011] FIG. 10 represents a variant of FIG. 2 with the hollows emerging on the rear face, i.e. the non-visible face of the bezel.

[0012] FIG. 11A represents a view of the front face, i.e. the visible face, of the bezel inlaid with several aesthetic elements, together with a partial sectional view of the bezel, focused on one aesthetic element. FIG. 11B represents a view of the rear face of this same bezel.

[0013] FIG. 12A represents a three-dimensional view of a watch case comprising in the case middle a hollow communicating with the bar hole.

[0014] FIG. 12B represents this same watch case comprising an aesthetic element inlaid in the hollow. FIG. 12C represents this same watch case comprising the aesthetic element inlaid in the hollow and set with stones.

DETAILED DESCRIPTION

[0015] The present invention relates to a method for manufacturing a decorative part by hot-pressing, also referred to as inlaying, one or more aesthetic elements in a support provided with one or more hollows and to the decorative part obtained from the method. The part can, in particular, be an external timepiece component, such as a bezel, a dial, a case, a crown, a pusher, a crystal, a bracelet element, etc. By way of example illustrated in FIGS. 1 and 2, part 1 is a watch bezel including an annular body forming the support 2 provided with hollows 4 arranged in said support 2 for receiving the aesthetic elements 3 forming the indices.

[0016] According to the invention, the aesthetic element is made of a crystalline metal alloy and more precisely of a crystalline aluminium alloy. The support is preferably made of a low-ductile material. It may, for example, be a ceramic, sapphire, enamel. etc. Preferably, it is a ceramic and more preferably, a zirconia. Thus, the part may be a zirconia watch bezel with indices made of an aluminium alloy. In particular, it may be the 7075 alloy which comprises zinc in an amount of ˜6 wt. %. The aluminium alloy has the advantage of being malleable at low temperature as a result of its low melting temperature of around 650° C.

[0017] Support 2 comprises at least one hollow 4 made by laser etching, by machining etc. On the surface 2a of support 2 intended to be visible, hollow 4 has a shape 4a corresponding to the contour of the desired decoration. This hollow 4 may be blind (FIG. 2) or open onto a non-visible face 2b of support 2 (FIG. 10). Advantageously, the entire volume of hollow 4 is filled with aesthetic element 3 protruding from or flush with surface 2a of support 2. In a variant, it is also conceivable for the aesthetic element to fill the volume of the hollow only partially. Cavity 4 has sides 7 with a geometry suitable for optimal retention of the aesthetic element within the hollow. As shown schematically in FIG. 3, sides 7 may be substantially perpendicular to visible surface 2a of support 2 with the aesthetic element held by friction within the hollow. According to a preferred variant that is not represented, the sides are at least partially inclined with a narrowing towards the visible surface preventing the aesthetic element from moving out of the hollow. According to another preferred variant represented in FIG. 8, sides 7, whether inclined or not, are pierced with housings 5 which, once filled with the aesthetic element, form a stop which, in the same way as the inclined walls, prevent the aesthetic element from moving. According to another preferred variant shown in FIG. 9, protuberances 6 can be arranged in hollow 4 to perform a similar role to means for retaining the aesthetic element.

[0018] According to the invention, the aesthetic elements are inlaid by hot-pressing in the hollows of the support at a temperature between the solidus temperature and the liquidus temperature of the aluminium alloy forming the aesthetic element typically between 500° C. and 650° C. More precisely, the inlaying steps of the manufacturing method of the invention are schematically illustrated with reference to FIGS. 3 to 7. First of all, the support 2 provided with the one or more hollows 4 is provided. Likewise, the preform or preforms for forming the aesthetic element or elements 3 are provided. In the case of a watch bezel to be decorated with aluminium indices, the aesthetic element to be inlaid is in the form of an annular preform with a ring diameter and width of substantially equivalent dimensions to those of the indices. To prevent the preform from sticking to the press during the inlaying process, an anti-adherent layer, e.g. of boron nitride, can be applied to the press-contacting side. In a first step, the support is preheated to prevent thermal shock. Preferably, the preheating temperature is between 300 and 500° C. Next, preform 3 is placed on surface 2a of support 2 level with hollow 4 (FIG. 4). The assembly is placed in a press where the preform is heated to a temperature comprised between the solidus and liquidus temperature of the preform material, thereby softening the material prior to the pressing process. Next, a pressure P is applied to preform 3 in order to fill hollows 4 with the aluminium alloy (FIG. 5 and FIG. 6). Preferably, the load during the inlaying process is kept at a value less than 1000 kg to avoid damaging the support. This load is preferably comprised between 500 and 800 kg. This pressing cycle can be carried out in several steps with a preload step before increasing the pressure up to the maximum desired pressure. The step of inlaying the aluminium alloy in the hollows is then followed by a cooling step and possibly a mechanical grinding step such as polishing to remove the surplus of aesthetic element 3 (FIG. 7) and to create visible surfaces of the support and of the aesthetic element connected to each other without any discontinuity.

[0019] By way of example, in the case of an aluminium 7075 alloy inlay in a zirconia support, the support was preheated to 450° C., the preform was heated to 550° C. for 90 seconds and pressed under a load of around 750 kg.

[0020] Advantageously, after the mechanical grinding step, the aesthetic element is subjected to a finishing treatment. This treatment may be a selective electrochemical treatment of the inlaid metal material, and more precisely, an anodizing process with or without colouring to alter the appearance and/or the hardness of the inlaid material. As the present invention is intended mainly for electrically non-conductive supports, the difficulty lies in the supply of current to the aesthetic elements during the electrochemical treatment and via contact points which absolutely must not be visible on the decorative part. To this end, one or more of the hollows are configured to open onto a face of the decorative part that will not be visible. These hollows opening onto the non-visible face form as many contact points making it possible to supply current across the inlaid aesthetic elements. Returning to the example of the ceramic watch bezel comprising indices made by inlaying a crystalline aluminium alloy, the hollow 4 for each of the indices opens onto the rear face 2b of bezel 1, as illustrated in FIG. 10. Contact points 4b make it possible to supply current across each of the indices during the electrochemical treatment. These contact points 4b on rear face 2b of support 2 may have a smaller cross-section than that of portion 4a of the hollow opening onto visible face 2a of support 2. These contact points make it possible to perform the same electrochemical treatment for each index or optionally to combine different treatments and therefore colours by only supplying the current across one or more of the indices for each electrochemical treatment.

[0021] If aesthetic element 3 is larger in size, as in the examples of FIGS. 11A and 12B, several contact points may be required per aesthetic element in order to ensure a uniform electrochemical treatment of the aesthetic element. In FIG. 11A, for example, three aesthetic elements 3 are distributed over an annular portion of visible face 2a of bezel 1. In this configuration, aesthetic elements 3 are inlaid on substrate 2 including the indices made of non-conductive material. On its rear face 2b visible in FIG. 11B, bezel 1 is provided with several orifices 4b communicating with hollows 4 to form the contact points for supplying current across these three elements. As shown in the sectional view of FIG. 11A, two contact points 4b are provided per aesthetic element 3. FIGS. 12B and 12C represent another configuration of an aluminium aesthetic element inlaid in a hollow arranged in a support. Aesthetic element 3 extends as far as a horn 8a of the middle part of watch case 8 and comprises housings 3a for setting stones 9. In a similar manner to the other examples, the hollow receiving the aesthetic element opens at least at one location onto a non-visible face of the watch case. It is thus conceivable for hollow 4 to communicate with the bar hole 10, as illustrated in FIG. 12A. Of course, hollow 4 can communicate in several places via other through holes making it possible to create contact points supplying current to aesthetic element 3. The present invention thus makes it possible, by means of the electrical contact point(s) provided on a non-visible face of the watch case, to electrochemically treat the aesthetic element once the stones have been set.

[0022] The present invention has been more specifically illustrated for a decorative part for watchmaking, but it is evident that the method of the invention applies to the production of decorative parts in many other fields, such as jewellery, telephony, the automobile industry, etc.

KEY TO DRAWINGS

[0023] (1) Decorative part [0024] (2) Support [0025] a. Visible face [0026] b. Non-visible face [0027] (3) Aesthetic element or preform [0028] a. Housing [0029] (4) Hollow [0030] a. Portion opening onto the visible face of the support [0031] b. Portion opening onto the non-visible face of the support [0032] (5) Housing inside the hollow [0033] (6) Protuberance in the hollow [0034] (7) Side of the hollow [0035] (8) Watch case [0036] a. Horn [0037] (9) Stone [0038] (10) Bar hole