METHOD FOR DETERMINING SOFTENING TEMPERATURE OF COPPER AND COPPER ALLOY
20210247337 · 2021-08-12
Assignee
Inventors
Cpc classification
International classification
Abstract
The present disclosure relates to a method for determining a softening temperature of copper and copper alloy, including: selecting a plurality of samples of the same material, annealing the plurality of samples at different temperatures, air-cooling the plurality of samples; measuring the tensile strength of an original sample and the plurality of samples after the annealing; plotting a data of the measured tensile strength into a temperature-tensile strength curve; a temperature at which the tensile strength in the temperature-tensile strength curve drops to a certain value of an original sample tensile strength is the softening temperature of the material. The above technical solution in the present disclosure uses the tensile strength instead of hardness to measure the softening temperature. It can effectively improve the detection efficiency and reduce the cost, and can be widely used in determination of the softening temperature of fine materials of copper and copper alloy.
Claims
1. A method for determining a softening temperature of copper and copper alloy, comprising: selecting a plurality of samples of a same material, annealing the plurality of samples at different temperatures, and air-cooling the plurality of samples; measuring a tensile strength of an original sample and the plurality of samples after the annealing; and plotting a data of the measured tensile strength into a temperature-tensile strength curve; a temperature at which the tensile strength in the temperature-tensile strength curve drops to a certain value of an original sample tensile strength is the softening temperature of the material.
2. The determining method according to claim 1, wherein the material includes copper and copper alloy material having a wire diameter of less than 1.024 mm or a thickness of less than 0.51 mm.
3. The determining method according to claim 1, wherein the material is a wire, a foil, or a strip.
4. The determining method according to claim 1, wherein the annealing is performed under vacuum or inert gas protection.
5. The determining method according to claim 1, wherein the temperature of the annealing includes at least 10 different temperatures, and intervals of the 10 different temperatures are the same and are 10-20° C.
6. The determining method according to claim 1, wherein when the material is a wire, the tensile strength is measured by clamping the wire on a fixture of a tensile testing machine, a clamping distance of the fixture is a gauge length, the gauge length of the wire ranges from 200 to 250 mm, and a tensile speed is 100 mm/min.
7. The determining method according to claim 1, wherein when the material is a foil or strip, the tensile strength is measured by: processing the sample into a dumbbell-shaped structure, a middle part of the dumbbell-shaped structure with a smaller cross section is a gauge length, and both ends of the dumbbell-shaped structure with a larger section are outside the gauge length; and clamping the foil or strip on a fixture of a tensile testing machine, clamping the both ends of the dumbbell-shaped structure, a tensile speed is 100 mm/min.
8. The determining method according to claim 7, wherein a cross-sectional area of the middle part is set as S.sub.0, when 11.3√{square root over (S.sub.0)}<10 mm, the gauge length is 10 mm; when 11.3√{square root over (S.sub.0)}≥10 mm, the gauge length is 11.3√{square root over (S.sub.0)}.
9. Use of the method according to claim 1 for determining a softening temperature of fine material of copper and copper alloy.
10. The use according to claim 9, wherein the fine material includes copper and copper alloy material having a wire diameter of less than 1.024 mm or a thickness of less than 0.51 mm.
11. The determining method according to claim 1, wherein the plurality of samples is annealed for 1 hour.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0016]
[0017]
[0018]
[0019]
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0020] The embodiments of the present disclosure will be described below through exemplary embodiments. Those skilled in the art can easily understand other advantages and effects of the present disclosure according to contents disclosed by the specification. The present disclosure can also be implemented or applied through other different exemplary embodiments. Various modifications or changes can also be made to all details in the specification based on different points of view and applications without departing from the spirit of the present disclosure.
[0021] It should be noted that processing equipment or devices not specifically noted in the following embodiments are all conventional equipment or devices in the field.
[0022] Besides, it should be understood that one or more method operations mentioned in the present disclosure are not exclusive of other method operations that may exist before or after the combined operations or that other method operations may be inserted between these explicitly mentioned operations, unless otherwise stated. It should also be understood that the combined connection relationship between one or more equipment/devices mentioned in the present disclosure does not exclude that there may be other equipment/devices before or after the combined equipment/devices or that other equipment/devices may be inserted between these explicitly mentioned equipment/devices, unless otherwise stated. Moreover, unless otherwise stated, the numbering of each method step is only a convenient tool for identifying each method step, and is not intended to limit the order of each method step or to limit the scope of the present disclosure. The change or adjustment of the relative relationship shall also be regarded as the scope in which the present disclosure may be implemented without substantially changing the technical content.
Embodiment 1
[0023] In this embodiment, the softening temperature of the copper alloy fine wire with a diameter of 0.05 mm was determined, which includes the following operations:
[0024] Eleven copper alloy wires with a diameter of 0.05 mm were used as samples, each with a length of 3 m, and the samples were subjected to vacuum annealing for an hour, in which the vacuum degree was 5.0×10.sup.−3 Pa, and the annealing temperatures were respectively 280° C., 300° C., 320° C., 340° C., 360° C., 380° C., 400° C., 420° C., 440° C., 460° C., 480° C., followed by air cooling. The air cooling means that the heated samples were directly placed in a room temperature environment to cool.
[0025] Tensile strength was measured and recorded on the samples without annealing and samples after annealing. The tensile gauge length was 200 mm and the tensile speed was 100 mm/min.
[0026] The measured data was plotted into a temperature-tensile strength curve. The abscissa represents the temperature of the annealing treatment, and the ordinate represents the tensile strength, referring to
[0027] The tensile strength of the samples without annealing (the original samples) was 390
[0028] MPa.
[0029] The temperature at which the strength of the material after the annealing treatment is reduced to 80% of the original sample strength is the softening temperature of the copper alloy fine wire with a diameter of 0.05 mm. That is, the softening temperature of the copper alloy fine wire was 351° C.
Comparative Example of Embodiment 1
[0030] In this comparative example, the softening temperature of the copper alloy fine wire with a diameter of 0.05 mm in embodiment 1 was determined according to the method in GB/T 33370-2016. The softening temperature curve drawn by the measured results is shown in
[0031] To conveniently show the advantages of the present disclosure over the method in GB/T 33370-2016, the original data obtained by the two methods are listed in Table 1.
TABLE-US-00001 TABLE 1 Tensile Hard- Tensile Hard- Tensile Hard- strength ness strength ness strength ness Original 388.74 115.97 280° C. 384.44 119.74 300° C. 374.51 116.71 Sample 389.59 118.97 soaking 385.42 118.21 soaking 374.59 117.46 388.45 122.89 for 1 h 384.93 115.24 for 1 h 374.55 116.71 118.98 116.71 122.89 117.46 119.74 118.21 118.97 123.71 114.51 119.74 118.97 114.97 118.21 119.74 116.71 320° C. 371.25 114.51 340° C. 350.67 100.13 360° C. 302.54 86.85 soaking 367.68 117.46 soaking 349.31 100.72 soaking 302.07 86.37 for 1 h 369.90 114.51 for 1 h 349.14 95.57 for 1 h 301.67 89.29 119.74 103.15 86.85 115.97 101.32 88.30 113.08 103.15 91.82 113.79 104.4 89.29 112.37 105.13 90.29 380° C. 293.54 84.51 400° C. 278.97 83.6 420° C. 270.49 78.45 soaking 294.18 88.30 soaking 276.87 81.83 soaking 269.69 79.27 for 1 h 292.79 85.90 for 1 h 276.76 84.05 for 1 h 270.09 77.23 84.05 84.51 76.44 83.60 83.15 79.69 88.79 85.9 81.83 86.37 85.9 79.69 91.31 83.15 85.44 440° C. 257.35 76.44 460° C. 246.4441 78.04 480° C. 229.94 70.16 soaking 255.28 78.45 soaking 245.78 74.5 soaking 231.2 67.79 for 1 h 255.57 77.23 for 1 h 245.39 73.38 for 1 h 230.98 70.85 77.23 75.27 71.92 77.63 74.88 77.63 78.04 76.44 70.85 78.45 74.13 70.5 76.44 73.75 67.79
[0032] For the softening temperature measured by the above two methods, the softening temperature measured by the method of the present disclosure was 351° C., and the softening temperature measured by the method in GB/T 33370-2016 was 350° C. The softening temperatures obtained by the two methods are the same. Analyzing the original data of the two methods, it is not difficult to find that the dispersion of the tensile strength data is small and the repeatability is good. The hardness data is more discrete, and it is easier to produce measurement errors than the tensile strength. Therefore, it can be considered that the softening temperature calculated by the tensile strength is more accurate.
[0033] Relevant professional technicians can clearly understand that for fine materials, the determination of tensile strength is much simpler than the determination of hardness.
[0034] In summary, the method for determining the softening temperature of copper and copper alloy prepared by the present disclosure has high accuracy and the operation method is simple.
Embodiment 2
[0035] In this embodiment, the softening temperature of a copper alloy foil with a thickness of 0.09 mm was determined, which includes the following operations:
[0036] Fifteen sheets of copper alloy foil with a thickness of 0.09 mm were taken as samples, and the samples were respectively subjected to annealing for an hour under argon atmosphere. The soak annealing temperatures were respectively 250° C., 260° C., 270° C., 280° C., 290° C., 300° C., 310° C., 320° C., 330° C., 340° C., 350° C., 360° C., 380° C., 390° C., 400° C., followed by air cooling.
[0037] Tensile strength was measured and recorded on the samples without annealing and samples after annealing. The samples were processed into dumbbell-shaped structures. The tensile gauge length was 10 mm, and the tensile speed was 100 mm/min.
[0038] The measured data was plotted into a temperature-tensile strength curve. The abscissa represents the temperature of the annealing treatment, and the ordinate represents the tensile strength, referring to
[0039] The tensile strength of the samples without annealing (the original samples) was 740 MPa.
[0040] The temperature at which the strength of the material after the annealing treatment is reduced to 80% of the original sample strength is the softening temperature of the samples. The softening temperature of the copper alloy foil was determined to be 288° C.
Embodiment 3
[0041] In this embodiment, the softening temperature of a pure copper strip with a thickness of 0.30 mm was determined, which includes the following operations:
[0042] Eleven samples were taken, and the samples were respectively subjected to annealing treatment for an hour under a nitrogen atmosphere. The soak annealing treatment temperatures were respectively 160° C., 170° C., 180° C., 190° C., 200° C., 210° C., 220° C., 230° C., 240° C., 250° C., and 260° C., followed by air cooling.
[0043] Tensile strength was measured and recorded on the samples without annealing treatment and the samples processor after annealing treatment. The samples were processed into dumbbell-shaped structures. The tensile gauge length was by the 10 mm, and the tensile speed was 100 mm/min.
[0044] The measured data was plotted into a temperature-tensile strength curve. The abscissa represents the temperature of the soak annealing treatment, and the ordinate represents the tensile strength, referring to
[0045] The tensile strength of the samples without annealing (the original samples) was 356 MPa.
[0046] The temperature at which the strength of the material after the soak annealing treatment is reduced to 80% of the original sample strength is the softening temperature of the samples. The softening temperature of the copper strip was determined to be 228° C.
[0047] The above-mentioned embodiments are merely illustrative of the principle and effects of the present disclosure instead of limiting the present disclosure. Modifications or variations of the above-described embodiments may be made by those skilled in the art without departing from the spirit and scope of the disclosure. Therefore, all equivalent modifications or changes made by those skilled in the art without departing from the spirit and scope of the disclosure will be covered by the appended claims.