Abstract

The invention relates to a manufacturing process of equipment for use in the production of nonwoven fabrics and paper products. According to the present invention, a sleeve for an embossing roller is produced using additive manufacturing, specifically 3D printing. These technologies permit the preparation of pattern-forming and dewatering details in the sleeve in a single operation. The dewatering properties may thus be optimised for the selected pattern, resulting in uniform dewatering tailored for the pattern. Preferably, the technique used is stereolithography.

Claims

1. A method for preparing a sleeve for a drum for forming, pressing or molding a fibrous web, wherein the method comprises forming the sleeve by additive manufacturing.

2. The method according to claim 1, wherein the sleeve is formed using stereolithography.

3. The method according to claim 2, further comprising the step of applying a coating to the sleeve following stereolithography.

4. A sleeve for a drum for hydroembossing a fibrous web, said sleeve being prepared using additive manufacturing.

5. The sleeve according to claim 4, said sleeve being prepared using stereolithography.

6. The sleeve according to claim 4, wherein the thickness of the sleeve is at least 5 mm.

7. The sleeve according to claim 6, further comprising a pattern having a depth in the range 10% to 50% of the thickness of the sleeve.

8. The sleeve according to claim 4, wherein the water absorption capacity of the sleeve is no more than 2% by weight.

9. The sleeve according to claim 4, wherein the tensile strength of the sleeve is at least 5.8 MPa.

10. The sleeve according to claim 4, wherein the elongation at break of the sleeve is no more than 10%.

11. The sleeve according to claim 4, wherein the Shore D hardness of the sleeve is at least 80.

12. A nonwoven web with a hydroembossed pattern, said pattern being prepared using a sleeve according to claim 4.

13. (canceled)

14. An additive manufacturing process for producing a sleeve for forming, pressing or molding a fibrous web, the process comprising: providing a resin bath of a photocurable resin; repeatedly illuminating portions of the photocurable resin within the resin bath to cure the resin and form the sleeve for forming, pressing or molding a fibrous web on a layer by layer basis, wherein successive layers of the cured resin are built up on an underside or a top side of previously formed layers.

15. The process of claim 14, wherein the photocurable resin is selected from the group consisting of epoxides, urethanes, polyethers, and polyesters.

16. The process of claim 14, further comprising hydroembossing a pattern on a nonwoven fibrous web using the formed sleeve.

Description

DETAILED DESCRIPTION

[0014] The invention is defined in the independent claims. Preferable embodiments are set out in the dependent claims.

[0015] Preferably, the material for the sleeve according to the invention is photocurable resin. Examples of such resins are epoxides, urethanes, polyethers and polyesters.

[0016] In a process using stereolithography, the cylindrical sleeve may be manufactured beginning from one end of the cylinder, the cylinder being lifted successively out of the resin container. The sleeve diameter is thus limited only by the size of the resin container, and the length of the sleeve, i.e. the width of the resultant web, is limited by the maximum lifting height of the stereolithography equipment.

[0017] A further advantage when stereolithography is used is the flexibility in designing not only the location and distribution but also the shape of dewatering holes.

[0018] For the manufacturing of a dewatering embossing sleeve, all refinements and variations known in the field of stereolithography may be used, e.g. supporting components that are dissolved or otherwise removed from the printed product.

[0019] The need for supporting structures typically increases as dimensions increase. External supporting structures are preferred to internal ones, since removal of external material is considerably less risky than the removal of material inside a sleeve structure.

[0020] In the production of an embossing sleeve using stereolithography, attention must be given to the water absorption properties of the material. The water absorption must be kept as a maximum of 2% by weight, preferably no more than 1.5%, more preferably no more than 1%, more preferably no more than 0.5%, more preferably no more than 0.2%. If the water absorption is excessive, material properties such as strength and flexibility may change. Moreover, the dimensions of the sleeve may change with rising water absorption, which is reflected in difficulties in fitting the sleeve to production equipment and securing it during use. If dimensions change, the sleeve no longer fits snugly to the supporting structure. This slack in combination with fast rotation will quickly cause fatal damage.

[0021] The strength of the sleeve must be sufficient to withstand the stresses caused by rotational forces and the pressure differences due to external water pressure and reduced internal pressure for water removal. Further, the structural integrity of the sleeve must be carefully preserved during storage and transport, and this is reflected in the strength requirements.

[0022] The thickness of a sleeve according to the invention is preferably at least 5 mm, more preferably at least 6 mm, as measured from the level of the lowermost points on the undersurface to the level of the uppermost points on the upper surface.

[0023] The depth of the patterning in a sleeve according to the invention affects the pattern quality but also the strength of the sleeve. Preferably, the depth of the pattern as defined by the distance between the lowermost level in the pattern (excluding openings) to the uppermost points of the upper surface is in the range 10% to 50%, more preferably in the range 15 to 30% of the thickness of the sleeve as defined above.

[0024] The measurement of thickness and pattern depth may be carried out using e.g. structured-light 3D-scanning.

[0025] Preferably, a sleeve manufactured according to the invention should satisfy the following conditions: [0026] Tensile strength at least 55 MPa, preferably at least 56, preferably at least 57 [0027] Elongation at break max 20%, preferably max 15%, preferably max 10% [0028] Flexural strength at least 82 MPa, preferably at least 87 MPa, preferably at least 93 MPa [0029] Flexural modulus at least 2400 MPa, preferably at least 2700 MPa, preferably at least 3100 MPa [0030] Izod notched impact at least 0.4 ft-lb/in, preferably at least 0.55 ft-lb/in, preferably at least 0.7 ft-lb/in [0031] Shore D hardness at least 80, preferably at least 84, preferably at least 87

[0032] Sharp edges in the sleeve surface may cause sticking of fibers, leading to linting tendencies in the product. Thus, maximum smoothness and avoidance of any surface damage are of great importance. These requirements underline the importance of correct material choices. The surface of a 3D-printed sleeve may receive a coating finish or sealant using high quality cross-linked resins such as cyanoacrylates, Dichtol products of the Diamant® company, Mönchengladbach, Germany or Nanoseal products of the medacom company, Butzbach, Germany. Such resins may be applied e.g. by spraying or immersing, and cured by appropriate means for the resin used, as known by a person skilled in polymer chemistry.

[0033] During the finishing coating, care must be taken to provide surface coverage also in the dewatering openings, thereby also achieving the correct dimensions for those openings. Vacuum may advantageously be used for distributing the finishing coating evenly over the structure surface.

[0034] A need for specified technical design of nonwoven webs exists e.g. in layered products like diapers, sanitary pads and the like. These comprise layers having particular tasks within the structure, such as allowing a liquid to enter the structure (topsheet), for dispersing the liquid (ADL), absorbing it and preventing the liquid from escaping (backsheet). Thus, a sleeve according to the invention may be used for producing e.g. topsheets, ADL and backsheets for layered products. Further examples of applications for products prepared using a sleeve according to the invention are nonwovens used in wallpaper, upholstery, carpeting, geotextiles, filters labels, laundry aids; and wipes for use in household, medical (including sterile products), workplace and personal hygiene applications.