Method for preparing a modified environment-friendly corn starch adhesive

Abstract

The present disclosure relates to a modified environment-friendly corn starch adhesive, comprising the following components in parts by weight: 30 parts of corn starch, 300-400 parts of water, 0.2-3 parts of oxidant, and 80-120 parts of polyvinyl alcohol, 1-5 parts of cross-linking agent, 3-5 parts of calcium chloride, 0.1-3 parts of urea, 0.2-0.5 parts of defoamer, and an appropriate amount of sodium hydroxide (to adjust pH), the cross-linking agent is a modified boric acid cross-linking agent prepared by reacting boric acid with epichlorohydrin, water and citric acid at 80-100° C. The surface of the modified boric acid cross-linking agent is bonded with a large number of epoxy groups and carboxyl groups, which can react with the carboxyl and aldehyde groups of the oxidized starch. These reactions can form synergistic effect with boric acid, which together improve the bonding efficiency and improve the adhesive strength of the colloid.

Claims

1. A modified environment-friendly corn starch adhesive, comprising the following components in parts by weight: 30 parts of corn starch, 300-400 parts of water, 0.2-3 parts of oxidant, and 80-120 parts of polyvinyl alcohol, 1-5 parts of cross-linking agent, 3-5 parts of calcium chloride, 0.1-3 parts of urea, 0.2-0.5 parts of defoamer, and an appropriate amount of sodium hydroxide (to adjust pH); wherein the cross-linking agent is a modified boric acid cross-linking agent prepared by reacting boric acid with epichlorohydrin, water and citric acid at 80-100° C.

2. The modified environment-friendly corn starch adhesive according to claim 1, wherein a mass ratio of water, boric acid, epichlorohydrin and citric acid used for modification of the boric acid cross-linking agent is 100:20-30:2-5:0.2-3.

3. The modified environment-friendly corn starch adhesive according to claim 1, wherein the corn starch has less than 0.6% protein content, 12%-14% water, and less than 0.4% sulfur dioxide.

4. The modified environment-friendly corn starch adhesive according to claim 1, wherein the oxidant is potassium permanganate.

5. The modified environment-friendly corn starch adhesive according to claim 1, wherein the defoamer is at least one kind selected from the group of water-soluble silicone Q-119 and Y-610.

6. A method for preparing the modified environment-friendly corn starch adhesive according to any one of claims 1, comprising the following steps: (1) modification of the boric acid cross-linking agent: after mixing water, boric acid, epichlorohydrin and citric acid according to a mass ratio, adding sodium hydroxide to adjust pH to 8-10, and heating a mixture to 80-100° C. to react for 1-2 h; after the reaction is completed, adding a certain amount of absolute ethanol, continuously stirring for 10-20 min, filtering and drying to obtain a modified boric acid cross-linking agent; (2) adding a amount of water to a three-necked flask, heating the water to 50° C., adding corn starch and solid potassium permanganate successively under stirring, and adjusting pH to 2-3 with hydrochloric acid; incubating a mixture for 2-3 h, then heating the mixture to 75° C., and adding the modified boric acid cross-linking agent to incubate for 1 h; then adding polyvinyl alcohol and calcium chloride, and ultrasonically dispersing them; continuously heating the mixture to 90° C. to incubate for 1 h; adding a amount of sodium hydroxide to adjust pH to neutral, adding urea, calcium chloride and defoamer to continuously incubating for 1 h, and cooling and discharging to obtain an environment-friendly corn starch adhesive.

Description

DETAILED DESCRIPTION

[0019] The present disclosure will be further described below in conjunction with embodiments, and the described embodiments are only a part of the embodiments of the present disclosure. Based on the embodiments of the present disclosure, equivalent replacements or improvements made by those of ordinary skill in the art without creative work are within the protection scope of the present disclosure. In order to ensure the transparency and service life of the starch adhesive prepared by the present disclosure, the corn starch used in the present disclosure has less than 0.6% protein content, 12%-14% water, and less than 0.4% sulfur dioxide.

Embodiment 1

[0020] A modified environment-friendly corn starch adhesive, comprising the following components in parts by weight: 30 parts of corn starch, 360 parts of water, 0.4 parts of potassium permanganate, 100 parts of polyvinyl alcohol, 3 parts of modified boric acid cross-linking agent, 4 parts of calcium chloride, 0.8 parts of urea, 0.3 parts of Q-119 type silicone defoamer, and an appropriate amount of sodium hydroxide (to adjust pH);

[0021] The method for preparing the modified environment-friendly corn starch adhesive, comprising the following steps:

[0022] (1) modification of the boric acid cross-linking agent: after mixing 100 g of water, 25 g of boric acid, 3 g of epichlorohydrin and 1 g of citric acid according to the mass ratio, adding sodium hydroxide to adjust pH to 8-10, and heating a mixture to 90° C. to react for 60 min; after the reaction is completed, adding 20 ml of absolute ethanol, continuously stirring for 15 min, filtering and drying to obtain a modified boric acid cross-linking agent.

[0023] (2) adding 350 g of water to a three-necked flask, heating the water to 50° C., adding 30 g of corn starch under stirring; after the corn starch is fully dispersed, adding 0.4 g of solid potassium permanganate, and adjusting pH to 2-3 with hydrochloric acid; incubating for 2.5 h, then heating the mixture to 75° C., and adding 3 g of the modified boric acid cross-linking agent and continuously stirring for 20 min to ensure that the modified boric acid cross-linking agent is completely dispersed in the system; then 100 g of polyvinyl alcohol and 4 g of calcium chloride are added, and incubating and ultrasonically dispersing for 30 min; after the dispersion is completed, continuously heating the mixture to 90° C. to incubate for 1 h; adding a certain amount of sodium hydroxide to adjust pH to neutral, adding 0.8 g of urea, and 0.3 g of the defoamer to continuously incubating for 1 h, and cooling and discharging to obtain an environment-friendly corn starch adhesive.

Embodiment 2

[0024] A modified environment-friendly corn starch adhesive, comprising the following components in parts by weight: 30 parts of corn starch, 360 parts of water, 1 part of potassium permanganate, 100 parts of polyvinyl alcohol, 3 parts of modified boric acid cross-linking agent, 4 parts of calcium chloride, 0.8 parts of urea, 0.3 parts of Y-610 type silicone defoamer, and an appropriate amount of sodium hydroxide (to adjust pH);

[0025] The method for preparing the modified environment-friendly corn starch adhesive, comprising the following steps:

[0026] (1) modification of the boric acid cross-linking agent: after mixing 100 g of water, 21 g of boric acid, 3 g of epichlorohydrin and 0.8 g of citric acid according to the mass ratio, adding sodium hydroxide to adjust pH to 8-10, and heating a mixture to 90° C. to react for 60 min; after the reaction is completed, adding 15 ml of absolute ethanol, continuously stirring for 25 min, filtering and drying to obtain a modified boric acid cross-linking agent.

[0027] (2) adding 350 g of water to a three-necked flask, heating water to 50° C., adding 30 g of corn starch under stirring; after the corn starch is fully dispersed, adding 1 g of solid potassium permanganate, and adjusting pH to 2-3 with hydrochloric acid; incubating for 2.5 h, then heating a mixture to 75° C., and adding 3 g of the modified boric acid cross-linking agent and continuously stirring for 20 min to ensure that the modified boric acid cross-linking agent is completely dispersed in the system; then adding 100 g of polyvinyl alcohol and 4 g of calcium chloride, and incubating and ultrasonically dispersing for 30 min; after the dispersion is completed, continuously heating the mixture to 90° C. to incubate for 1 h; adding a certain amount of sodium hydroxide to adjust pH to neutral, adding 0.8 g of urea, and 0.3 g of Y-610 type defoamer to continuously incubating for 1 h, and cooling and discharging to obtain an environment-friendly corn starch adhesive.

Embodiment 3

[0028] A modified environment-friendly corn starch adhesive, comprising the following components in parts by weight: 30 parts of corn starch, 380 parts of water, 0.6 part of potassium permanganate, 110 parts of polyvinyl alcohol, 4 parts of modified boric acid cross-linking agent, 4 parts of calcium chloride, 2 parts of urea, 0.3 parts of Y-610 type silicone defoamer, and an appropriate amount of sodium hydroxide (to adjust pH);

[0029] The method for preparing the modified environment-friendly corn starch adhesive, comprising the following steps:

[0030] (1) modification of the boric acid cross-linking agent: after mixing 100 g of water, 28 g of boric acid, 3 g of epichlorohydrin and 1 g of citric acid according to the mass ratio, adding sodium hydroxide to adjust pH to 8-10, and heating a mixture to 90° C. to react for 60 min; after the reaction is completed, adding 15 ml of absolute ethanol, continuously stirring for 25 min, filtering and drying to obtain a modified boric acid cross-linking agent.

[0031] (2) adding 380 g of water to a three-necked flask, heating water to 50° C., adding 30 g of corn starch under stirring; after the corn starch is fully dispersed, adding 0.6 g of solid potassium permanganate, and adjusting pH to 2-3 with hydrochloric acid; incubating for 2.5 h, then heating a mixture to 75° C., and adding 4 g of the modified boric acid cross-linking agent and continuously stirring for 20 min to ensure that the modified boric acid cross-linking agent is completely dispersed in the system; then adding 110 g of polyvinyl alcohol and 4 g of calcium chloride, and incubating and ultrasonically dispersing for 30 min; after the dispersion is completed, continuously heating the mixture to 90° C. to incubate for 1 h; adding a certain amount of sodium hydroxide to adjust pH to neutral, adding 2 g of urea, and 0.3 g of Y-610 type defoamer to continuously incubating for 1 h, and cooling and discharging to obtain an environment-friendly corn starch adhesive.

[0032] The adhesive strength of the adhesive prepared in the above embodiment s is tested by the test method which is GB/T6548-1998 adhesive strength determination method of corrugated cardboards, and the test results are:

[0033] Embodiment 1: 71.2N/10 cm;

[0034] Embodiment 2: 69.4N/10 cm;

[0035] Embodiment 3: 70.1N/10 cm.

[0036] The results of the above embodiments show that the adhesive strength of the prepared adhesives are all greater than 58.8N/10 cm, which meets the GB5034-85 corrugated cardboard standard requirements for packaging products out of the warehouse.

[0037] The above is only preferred exemplary embodiments of the present disclosure and is not intended to be limiting of the present disclosure, and any modifications, equivalent substitutions, improvements and the like within the spirit and principle of the present disclosure are intended to be embraced by the protection range of the present disclosure.