Device and method for online preparation of modified polylactic acid material with polylactic acid melt

Abstract

The present disclosure relates to the technical field of polymer material, and discloses a device and method for online preparation of a modified polylactic acid material with a polylactic acid melt. The device comprises a twin-screw extruder, a first solid modifier hopper, a polylactic acid melt pipeline and a polylactic acid melt feedstock metering pump, wherein the first solid modifier hopper is connected with Zone I of the twin-screw extruder, the polylactic acid melt pipeline is connected with Zone IV of the twin-screw extruder. The method for online preparation of modified polylactic acid material with the device can avoid degradation of the polylactic acid caused by the secondary processing, improve mechanical property of the prepared polylactic acid and reduce production cost.

Claims

1. A method for online preparation of a modified polylactic acid material, wherein the method is performed in a device for online preparation of a modified polylactic acid material, and the method comprises: (a) feeding the polylactic acid melt into a Zone IV of the twin-screw extruder through a polylactic acid melt pipeline; (b) adding a first solid modifier into a Zone I of the twin-screw extruder via a first solid modifier hopper; (c) feeding a liquid modifier into a Zone II of the twin-screw extruder through a liquid feedstock metering pump; (d) contacting the polylactic acid melt, the first solid modifier with the liquid modifier in Zone V of the twin-screw extruder to Zone XI of the twin-screw extruder, and extruding and granulating the obtained modified polylactic acid polymerization melt; wherein the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, and the dosage of the liquid modifier is 0.2-0.5 wt %, based on the total weight of the modified polylactic acid melt; wherein the device comprises a twin-screw extruder, a first solid modifier hopper, a polylactic acid melt pipeline and a polylactic acid melt feedstock metering pump, and the first solid modifier hopper is connected with Zone I of the twin-screw extruder, the polylactic acid melt pipeline is connected with Zone IV of the twin-screw extruder; wherein the polylactic acid melt is obtained by subjecting lactide to polymerization and devolatilization; wherein the liquid modifier is one or more selected from the group consisting of epoxidized soybean oil, tributyl citrate and adipic acid diethylene glycol monobutylether ester; wherein the first solid modifier is a toughening agent and/or a reinforcing agent.

2. The method of claim 1, wherein the device further comprises a second solid modifier hopper and a second auxiliary material hopper, wherein the second solid modifier hopper is connected with a Zone I of the twin-screw extruder; wherein the second auxiliary material hopper is connected with a Zone V of the twin-screw extruder.

3. The method of claim 1, wherein the twin-screw extruder further comprises a liquid feedstock metering pump, and the liquid feedstock metering pump is connected with the Zone II of the twin-screw extruder.

4. The method of claim 2, wherein the method further comprises: in step (b), the first solid modifier is fed into the Zone I of the twin-screw extruder via a first solid modifier hopper, and the second solid modifier is fed into the Zone I of the twin-screw extruder via a second solid modifier hopper; wherein the second solid modifier is a toughening agent and/or a reinforcing agent.

5. The method of claim 4, wherein the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, the dosage of the second solid modifier is 0-7 wt %, and the dosage of the liquid modifier is 0.2-0.5 wt %, based on the total weight of the modified polylactic acid melt.

6. The method of claim 5, wherein the dosage of the polylactic acid melt is 53-66.8 wt %, the dosage of the first solid modifier is 25-35 wt %, the dosage of the second solid modifier is 3-7 wt %, and the dosage of the liquid modifier is 0.2-0.3 wt %, based on the total weight of the modified polylactic acid melt.

7. The method of claim 2, wherein the method further comprises: in step (d), contacting the polylactic acid melt, the first solid modifier and the liquid modifier with the auxiliary material, wherein the auxiliary material is fed into the Zone V of the twin-screw extruder via the second auxiliary material hopper.

8. The method of claim 7, wherein the auxiliary material is one or more selected from the group consisting of a chain extender, a cross-linking agent, an antioxidant and a lubricant.

9. The method of claim 8, wherein the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, the dosage of the liquid modifier is 0.2-0.5 wt %, the dosage of the chain extender is 0-0.3 wt %, the dosage of the cross-linking agent is 0-0.3 wt %, the dosage of the antioxidant is 0-0.5 wt %, and the dosage of the lubricant is 0-0.4 wt %, based on the total weight of the modified polylactic acid melt.

10. The method of claim 9, wherein the dosage of the polylactic acid melt is 53-66.8 wt %, the dosage of the first solid modifier is 25-35 wt %, the dosage of the liquid modifier is 0.2-0.3 wt %, the dosage of the chain extender is 0.1-0.2 wt %, the dosage of the cross-linking agent is 0.1-0.2 wt %, the dosage of the antioxidant is 0.2-0.3 wt %, and the dosage of the lubricant is 0.2-0.3 wt %, based on the total weight of the modified polylactic acid melt.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic view of a device for online preparation of a modified polylactic acid material according to the present disclosure.

DESCRIPTION OF THE REFERENCE SIGNS

(2) 1. Motor 2. Zone I of the twin-screw extruder 3. Zones II to III of the twin-screw extruder 4. Zone IV of the twin-screw extruder 5. Zone V of the twin-screw extruder 6. Zones VI to XI of the twin-screw extruder 7. Headpiece of the twin-screw extruder 8. First solid modifier hopper 9. Second solid modifier hopper 10. Polylactic acid melt feedstock metering pump 11. First auxiliary material hopper 12. Liquid feedstock metering pump 13. Second auxiliary material hopper 15. Polylactic acid melt pipeline

DETAILED DESCRIPTION

(3) The terminals and any value of the ranges disclosed herein are not limited to the precise ranges or values, such ranges or values shall be comprehended as comprising the values adjacent to the ranges or values. As for numerical ranges, the endpoint values of the various ranges, the endpoint values and the individual point value of the various ranges, and the individual point values may be combined with one another to produce one or more new numerical ranges, which should be deemed have been specifically disclosed herein.

(4) The present disclosure provides a device for online preparation of a modified polylactic acid material with a polylactic acid melt, wherein the device comprises a twin-screw extruder, a first solid modifier hopper 8, a polylactic acid melt pipeline 15 and a polylactic acid melt feedstock metering pump 10, the first solid modifier hopper 8 is connected with Zone I 2 of the twin-screw extruder, the polylactic acid melt pipeline 15 is connected with Zone IV 4 of the twin-screw extruder.

(5) In the present disclosure, it shall be noted that the polylactic acid melt is prepared by COFCO Biochemistry Co., Ltd., and the preparation method comprises the following steps: subjecting lactide to polymerization and devolatilization procedures to obtain a polylactic acid melt; wherein the lactide is purchased from Total Corbion PLA (Thailand) Ltd., with a product name Lumilact® L, a net weight 600 kg, a model number L85 and a purity 99.5%.

(6) According to the present disclosure, the device further comprises a second solid modifier hopper 9 and a second auxiliary material hopper 13, wherein the second solid modifier hopper 9 is connected with a Zone I 2 of the twin-screw extruder; the second auxiliary material hopper 13 is connected with a Zone V 5 of the twin-screw extruder.

(7) According to the present disclosure, the device also comprises a first auxiliary material hopper 11, the first auxiliary material hopper 11 is connected to a Zone I 2 of the twin-screw extruder, and is used for feeding the powder auxiliary materials.

(8) According to the present disclosure, the twin-screw extruder further comprises a liquid feedstock metering pump 12, and the liquid feedstock metering pump 12 is connected with the Zone II of the twin-screw extruder.

(9) As shown in FIG. 1, i.e., the schematic diagram of a device for online preparation of a modified polylactic acid material according to the present disclosure, the twin-screw extruder further comprises a motor 1 and a headpiece 7 of the twin-screw extruder; in addition, a Zone I 2 of the twin-screw extruder, Zones II to III 3 of the twin-screw extruder, a Zone IV 4 of the twin-screw extruder, a Zone IV 5 of the twin-screw extruder, and Zones VI to XI of the twin-screw extruder are as shown in FIG. 1.

(10) A second aspect of the present disclosure provides a method for online preparation of a modified polylactic acid material, wherein the method is performed in a device for online preparation of a modified polylactic acid material, the method comprises:

(11) (a) feeding the polylactic acid melt into a Zone IV 4 of the twin-screw extruder through a polylactic acid melt pipeline 15;

(12) (b) adding a first solid modifier into a Zone I 2 of the twin-screw extruder via a first solid modifier hopper 8;

(13) (c) feeding a liquid modifier into a Zone II of the twin-screw extruder through a liquid feedstock metering pump 12;

(14) (d) contacting the polylactic acid melt, the first solid modifier with the liquid modifier in Zone V 5 of the twin-screw extruder to Zone XI of the twin-screw extruder, and extruding and granulating the obtained modified polylactic acid polymerization melt;

(15) wherein the device for online preparation of a modified polylactic acid material is the aforementioned device.

(16) According to the present disclosure, the liquid modifier is one or more selected from the group consisting of epoxidized soybean oil, tributyl citrate and adipic acid diethylene glycol monobutylether ester.

(17) Wherein the epoxidized soybean oil (ESO) is a light yellow viscous oily liquid under the normal temperature, the molecular formula is C.sub.57H.sub.106O.sub.10, the molecular weight is 950, the epoxy value is greater than or equal to 6.60, the iodine value is less than or equal to 3.0, the higher is the epoxy value of the ESO, the better is the heat resistance, the lower is the iodine value, the better is the compatibility with polyvinyl chloride (PVC), the less easier it is precipitated.

(18) Wherein the tributyl citrate is generally called tri-n-butyl citrate, the chemical name of the tributyl citrate is 3-hydroxy-3-carboxyl glutaric acid tributyl ester, which is an ester compound.

(19) According to the present disclosure, the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, and the dosage of the liquid modifier is 0.2-0.5 wt %, based on the total weight of the modified polylactic acid melt; preferably, the dosage of the polylactic acid melt is 53-66.8 wt %, the dosage of the first solid modifier is 25-35 wt %, and the dosage of the liquid modifier is 0.2-0.3 wt %, based on the total weight of the modified polylactic acid melt. In the present disclosure, the total amount of dosages of the polylactic acid melt, the first solid modifier and the liquid modifier is 100%.

(20) According to the present disclosure, the method further comprises: in step (b), the first solid modifier is fed into the Zone I 2 of the twin-screw extruder via a first solid modifier hopper 8, and a second solid modifier is fed into the Zone I 2 of the twin-screw extruder via a second solid modifier hopper 9.

(21) According to the present disclosure, the first solid modifier and the second solid modifier are identical or different, each is a toughening agent and/or a reinforcing agent.

(22) In the present disclosure, the toughening agent is one or more selected from the group consisting of polybutylene adipate terephthalate, polypropylene carbonate, polybutylene succinate, polytetramethylene glycol-succinic acid/adipic acid copolyester, it is preferably polybutylene adipate terephthalate and/or polypropylene carbonate.

(23) In the present disclosure, the reinforcing agent is talc and/or calcium carbonate.

(24) According to the present disclosure, the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, the dosage of the second solid modifier is 0-7 wt %, and the dosage of the liquid modifier is 0.2-0.5 wt %, based on the total weight of the modified polylactic acid melt; preferably, the dosage of the polylactic acid melt is 53-66.8 wt %, the dosage of the first solid modifier is 25-35 wt %, the dosage of the second solid modifier is 3-7 wt %, and the dosage of the liquid modifier is 0.2-0.3 wt %, based on the total weight of the modified polylactic acid melt. In the present disclosure, the total amount of dosages of the polylactic acid melt, the first solid modifier, the second solid modifier and the liquid modifier is 100%.

(25) According to the present disclosure, the method further comprises: in step (d), contacting the polylactic acid melt, the first solid modifier and the liquid modifier with the auxiliary material, wherein the auxiliary material is fed into the Zone V 5 of the twin-screw extruder via the second auxiliary material hopper 13.

(26) According to the present disclosure, the auxiliary material is one or more selected from the group consisting of a chain extender, a cross-linking agent, an antioxidant and a lubricant.

(27) According to the present disclosure, the dosage of the polylactic acid melt is 49.5-79 wt %, the dosage of the first solid modifier is 20-50 wt %, the dosage of the liquid modifier is 0.2-0.5 wt %, the dosage of the chain extender is 0-0.3 wt %, the dosage of the cross-linking agent is 0-0.3 wt %, the dosage of the antioxidant is 0-0.5 wt %, and the dosage of the lubricant is 0-0.4 wt %, based on the total weight of the modified polylactic acid melt; preferably, the dosage of the polylactic acid melt is 53-66.8 wt %, the dosage of the first solid modifier is 25-35 wt %, the dosage of the liquid modifier is 0.2-0.3 wt %, the dosage of the chain extender is 0.1-0.2 wt %, the dosage of the cross-linking agent is 0.1-0.2 wt %, the dosage of the antioxidant is 0.2-0.3 wt %, and the dosage of the lubricant is 0.2-0.3 wt %, based on the total weight of the modified polylactic acid melt. In the present disclosure, the total amount of the dosages of the polylactic acid melt, the first solid modifier, the liquid modifier, the chain extender, the crosslinking agent, the antioxidant and the lubricant is 100%.

(28) The present disclosure also provides a modified polylactic acid material prepared with the aforementioned method.

(29) The present disclosure will be described in detail below with reference to examples.

(30) In the following Examples and Comparative Examples:

(31) (1) Mechanical Property Measurement

(32) In the present disclosure, the tensile strength and the elongation at break were tested by an intelligent electronic tensile testing machine, and the instrument with a model number XLW was purchased from the Jinan Labthink Electromechanical Technology Co., Ltd.

(33) (2) Weight Average Molecular Weight

(34) In the present disclosure, the weight average molecular weight was measured by using a gel permeation chromatograph.

(35) (3) Source of Raw Materials

(36) The polybutylene adipate terephthalate was purchased from Xinjiang Blue Ridge Tunhe Chemical Industry Joint Stock Co., Ltd.;

(37) The polypropylene carbonate was purchased from the Inner Mongolia Mengxi High-tech New Material Joint Stock Co., Ltd.;

(38) The polybutylene succinate was purchased from the BASF SE;

(39) The polytetramethylene glycol-succinic acid/adipic acid copolyester was purchased from the Kingfa science and technology Co., Ltd.;

(40) The talc was purchased from Shanghai Chengzhi Chemical Products Co., Ltd.;

(41) The calcium carbonate was purchased from Zhejiang Tianshi Nanometer Science and Technology Co., Ltd.;

(42) The tributyl citrate was purchased from Meryer (Shanghai) Chemical Technology Co., Ltd.;

(43) The epoxidized soybean oil was purchased from Dongguan Hentai Chemical Co., Ltd.;

(44) The adipic acid diethylene glycol monobutylether ester (DGBEA) was purchased from Changchun Institute of Applied Chemistry (CIAC);

(45) The chain extenders were purchased from the BASF SE;

(46) The crosslinking agent was purchased from Dongguan Huanzong Trade Co., Ltd.;

(47) The antioxidant was purchased from Tianjin Rainlon New Materials Co., Ltd.;

(48) The lubricant was purchased from the Sichuan Tianyu Oil Chemical Co., Ltd.

Example 1

(49) This example aimed to illustrate a modified polylactic acid material prepared with the device and method of the present disclosure.

(50) As shown in FIG. 1:

(51) (a) 59.1 parts by weight of polymerized polylactic acid melt were continuously output via the polylactic acid melt pipeline 15 and fed into a polylactic acid melt feedstock metering pump 10 (hereinafter referred to as “melt feedstock metering pump”), and subsequently continuously output and fed into Zone IV 4 of the twin-screw extruder;

(52) (b) 35 parts by weight of a first solid modifier polybutylene adipate terephthalate and 5 parts by weight of a second solid modifier talc were respectively added into a first solid modifier hopper 8 and a second solid modifier hopper 9;

(53) (c) 0.3 part by weight of liquid modifier tributyl citrate was passed through a liquid feedstock metering pump 12 and fed into a Zone II of the twin-screw extruder in a lateral feeding mode;

(54) (d) 0.1 part by weight of chain extender, 0.1 part by weight of cross-linking agent, 0.2 part by weight of antioxidant and 0.2 part by weight of lubricant were uniformly mixed and then added into a second auxiliary material hopper 13, and 100 parts by weight of the prepared modified polylactic acid polymerization melt was uniformly blended in Zones V to XI of a twin-screw extruder and then extruded and granulated.

(55) The modified polylactic acid material was prepared as a consequence.

Example 2

(56) This example aimed to illustrate a modified polylactic acid material prepared with the device and method of the present disclosure.

(57) As shown in FIG. 1:

(58) (a) 53 parts by weight of polymerized polylactic acid melt were continuously output via the polylactic acid melt pipeline 15 and fed into a polylactic acid melt feedstock metering pump 10 (hereinafter referred to as “melt feedstock metering pump”), and subsequently continuously output and fed into Zone IV of the twin-screw extruder;

(59) (b) 39 parts by weight of a first solid modifier polybutylene adipate terephthalate and 7 parts by weight of a second solid modifier talc were respectively added into a first solid modifier hopper 8 and a second solid modifier hopper 9;

(60) (c) 0.2 part by weight of liquid modifier epoxidized soybean oil was passed through a liquid feedstock metering pump 12 and fed into a Zone II of the twin-screw extruder in a lateral feeding mode;

(61) (d) 0.2 part by weight of chain extender, 0.1 part by weight of cross-linking agent, 0.3 part by weight of antioxidant and 0.2 part by weight of lubricant were uniformly mixed and then added into a second auxiliary material hopper 13, and 100 parts by weight of the prepared modified polylactic acid polymerization melt was uniformly blended in Zones V to XI of a twin-screw extruder and then extruded and granulated.

(62) The modified polylactic acid material was prepared as a consequence.

Examples 3-7

(63) The modified polylactic acid material was prepared with the same device and method as in Example 1, except for that the first solid modifier, the second solid modifier, the liquid modifier, the chain extender, the crosslinking agent, the antioxidant and the lubricant in Example 1 were modified accordingly, as shown in Table 1.

(64) TABLE-US-00001 TABLE 1 To prepare 100 parts by weight of a modified polylactic acid polymerization melt Unit (part Polylactic First Second solid by weight) acid melt solid modifier modifier Liquid modifier Example 3 66.3 25 Polypropylene 5 Talc 0.3 Epoxidized carbonate soybean oil Example 4 64 25 Polybutylene 7 Talc 0.3 Adipic acid succinate diethylene glycol monobutylether ester Example 5 66.8 25 Polybutylene 5 Talc 0.3 Tributyl glycol-succinic citrate acid/adipic acid copolyester Example 6 64.1 30 Polypropylene 3 Calcium 0.3 Tributyl carbonate carbonate citrate Example 7 57.3 35 Polybutylene 5 Calcium 0.3 Epoxidized succinate carbonate soybean oil Unit (part Chain by weight) extender Crosslinking agent Antioxidant Lubricant Example 3 0.1 0.1 0.2 0.3 Example 4 0.15 0.15 0.3 0.4 Example 5 0.2 0.1 0.2 0.2 Example 6 0.1 0.2 0.3 0.3 Example 7 0.1 0.2 0.2 0.2

Comparative Example 1

(65) The modified polylactic acid material was prepared according to the same method as in Example 2, except for that the blown film grade polylactic acid chips manufactured by COFCO were used, and according to the formulation of Example 2, 53 parts by weight of polylactic acid chips were mechanically mixed with 39 parts by weight of polybutylene adipate terephthalate, 7 parts by weight of talc, 0.2 parts by weight of epoxidized soybean oil, 0.2 parts by weight of chain extender, 0.1 part by weight of cross-linking agent, 0.3 part by weight of antioxidant, and 0.2 part by weight of lubricant, and then extruded by a twin-screw extruder for granulation.

(66) The modified polylactic acid material was prepared as a consequence.

Comparative Examples 2-6

(67) The modified polylactic acid material was prepared with the same device and method as in Example 1, except for that the content of the polylactic acid melt and the content of the first solid modifier and the second solid modifier were different, as shown in Table 2.

(68) TABLE-US-00002 TABLE 2 To prepare 100 parts by weight of a modified polylactic acid polymerization melt Unit (part Polylactic First solid Second solid Liquid by weight) acid melt modifier modifier modifier Comparative 80.0 17 Polypropylene 2 Talc 0.3 Epoxi- Example 2 carbonate dized soybean oil Comparative 82.0 15 Polybutylene 1 Talc 0.1 Adipic Example 3 succinate acid diethylene glycol mono- butylether ester Comparative 51.0 40 Polybutylene 8 Talc 0.3 Tributyl Example 4 glycol-succinic citrate acid/adipic acid copolyester Comparative 46.2 36 Polypropylene 9 Calcium 0.3 Tributyl Example 5 carbonate carbonate citrate Comparative 80.4 15 Polybutylene 2 Calcium 0.6 Epoxi- Example 6 succinate carbonate dized soybean oil Unit (part Chain Crosslinking by weight) extender agent Antioxidant Lubricant Comparative 0.1 0.1 0.2 0.3 Example 2 Comparative 0.4 0.4 0.6 0.5 Example 3 Comparative 0.2 0.1 0.2 0.2 Example 4 Comparative 0.1 0.2 0.3 0.3 Example 5 Comparative 0.5 0.5 0.5 0.5 Example 6

Test Example

(69) The modified polylactic acid materials prepared in Examples 1-7 and Comparative Examples 1-6 were subjected to tests of tensile strength and elongation at break, and the results were shown in Table 3.

(70) TABLE-US-00003 TABLE 3 Weight average Tensile Elongation Production molecular weight strength at cost Samples (g/mol ) (MPa) break (%) (yuan/ton) Comparative 154,059 45.0 98 4,600 Example 1 Comparative 178,265 46.8 108 3,100 Example 2 Comparative 178,398 50.2 103 3,100 Example 3 Comparative 179,115 51.9 105 3,100 Example 4 Comparative 178855 50.6 99 3,100 Example 5 Comparative 179,065 52.0 100 3,100 Example 6 Example 1 179,174 55.0 120 3,100 Example 2 184,059 56.2 125 3,100 Example 3 180,243 54.8 118 3,100 Example 4 183,224 53.1 109 3,100 Example 5 179,986 52.9 121 3,100 Example 6 183,054 56.0 120 3,100 Example 7 181,752 52.3 119 3,100

(71) As can be seen from the results in Table 3, the polylactic acid modified materials prepared in Examples 1-7 of the present disclosure have superior properties, wherein the polylactic acid modified material prepared in Example 2 of the present disclosure has excellent properties, the weight average molecular weight is 184,059 g/mol, the tensile strength is 56.2 MPa, and the elongation at break is 125%.

(72) The above content describes in detail the preferred embodiments of the present disclosure, but the present disclosure is not limited thereto. A variety of simple modifications can be made in regard to the technical solutions of the present disclosure within the scope of the technical concept of the present disclosure, including a combination of individual technical features in any other suitable manner, such simple modifications and combinations thereof shall also be regarded as the content disclosed by the present disclosure, each of them falls into the protection scope of the present disclosure.