Multipurpose shrink sleeve printing ink

Abstract

Described herein is a printing ink or coating composition that includes: (a) one or more elastomeric polyurethane resins with amine functionality having a glass transition temperature of about −45° C. to about −70° C.; (b) one or more acrylic resins based on a methacrylate/styrene co-polymer with a glass transition temperature of about 45° C. to about 110° C.; (c) one or more nitrocellulose binders; (d) one or more solvents; and (e) optionally, one or more waxes and/or one or more colorants. The inks and coating compositions are well suited for printing onto shrink sleeve label substrates, such as by flexographic and gravure printing. The inks and coatings provide exceptional printability and resistance to chemicals, to softening, to re-wetting, and to set-off.

Claims

1. A printing ink or coating composition comprising (a) one or more elastomeric polyurethane resins with amine functionality having a glass transition temperature of about −45° C. to about −70° C.; (b) one or more acrylic resins based on a methacrylate/styrene co-polymer with a glass transition temperature of about 45° C. to about 110° C.; (c) one or more nitrocellulose binders; (d) one or more solvents; and (e) optionally, one or more waxes and/or one or more colorants, wherein the nitrocellulose binders are present in an amount of about 4 wt % to about 12 wt %.

2. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality comprise a poly(tetrahydrofuran) component.

3. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality comprise an isophorone diisocyanate component.

4. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality comprise a poly(tetrahydrofuran) component and an isophorone diisocyanate component.

5. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality comprise a poly(propylene glycol) component.

6. The printing ink or coating composition of claim 1, wherein the colorant is present in a nitrocellulose binder color concentrate.

7. The printing ink or coating composition of claim 1, wherein the solvent is selected from ethanol, n-propanol, isopropanol, ethoxy propanol, methoxy propanol, propoxy propanol, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, methoxy propyl acetate, ethoxy propyl acetate, methoxy propoxy propanol glycol ether, propanol butoxy glycol ether, methoxy butanol glycol ether, ethyl lactate, and mixtures thereof.

8. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality are present in an amount of about 5 wt % to about 45 wt %.

9. The printing ink or coating composition of claim 1, wherein the acrylic resins are present in an amount of about 1 wt % to about 20 wt %.

10. The printing ink or coating composition of claim 1, wherein the nitrocellulose resins are present in an amount of about 4 wt % to about 7 wt %.

11. The printing ink or coating composition of claim 1, wherein the printing ink or coating composition has a glass transition temperature in a first region of about −45° C. to about −70° C. and a glass transition temperature in a second region of about 65° C. to about 100° C.

12. The printing ink or coating composition of claim 1, wherein the printing ink or coating composition has a glass transition temperature of about 25° C. to about 35° C.

13. The printing ink or coating composition of claim 1, wherein the printing ink or coating composition is a gravure or flexographic ink or coating composition.

14. A shrinkable sleeve, shrink label and other flexible packaging applied with the printing ink or coating composition of claim 1.

15. A printed article, comprising a substrate and the printing ink or coating composition of claim 1.

16. A method of formulating a printing ink or coating comprising: selecting (a) one or more elastomeric polyurethane resins with amine functionality having a glass transition temperature of about −45° C. to about −70° C.; (b) one or more acrylic resins based on a methacrylate/styrene co-polymer with a glass transition temperature of about 45° C. to about 110° C.; (c) one or more nitrocellulose binders; (d) one or more solvents; and (e) optionally, one or more waxes and/or one or more colorants; and formulating components (a) to (e) into a printing ink or coating composition.

17. The printing ink or coating composition of claim 1, wherein the elastomeric polyurethane resins with amine functionality are present in amount of about 15 wt % to about 25 wt %.

18. The printing ink or coating composition of claim 1, wherein the acrylic resins are present in an amount of about 5 wt % to about 15 wt %.

19. A printing ink or coating composition comprising (a) from about 5 wt % to about 45 wt % of one or more elastomeric polyurethane resins with amine functionality having a glass transition temperature of about −45° C. to about −70° C.; (b) from about 1 wt % to about 20 wt % of one or more acrylic resins based on a methacrylate/styrene co-polymer with a glass transition temperature of about 45° C. to about 110° C.; (c) from about 4 wt % to about 12 wt % of one or more nitrocellulose binders; (d) one or more solvents; and (e) optionally, one or more waxes and/or one or more colorants.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a perspective view depicting a shrink sleeve in tubular form along the longitudinal tube axis with the ends thereof arranged to overlap in a seam-forming arrangement; and

(2) FIG. 2 is a perspective view depicting shrink sleeve arranged over a container.

DETAILED DESCRIPTION OF THE INVENTION

(3) The present inventors have found that the inventive ink and coating compositions described herein, which comprise:

(4) (a) one or more elastomeric polyurethane resins with amine functionality having a Tg of about −45° C. to about −70° C.;

(5) (b) one or more acrylic resins based on a methacrylate/styrene co-polymer with a Tg of about 45° C. to about 110° C.;

(6) (c) one or more nitrocellulose (NC) binders;

(7) (d) one or more solvents; and

(8) (e) optionally, one or more waxes and/or one or more colorants, provide improved ink/coating adhesion to a substrate, notably after the substrate film, e.g., a shrink sleeve substrate, is shrunken around the container and the ink and coating composition is thereby affixed to a shrunken sleeve. The inventive ink and coating compositions also overcome problems encountered in the state of the art relating to poor product resistance and seam solvent resistance. Set-off resistance is also improved. It has been found that during printing, cobwebbing is reduced if not eliminated, providing cleaner flexographic printing.

(9) It has further been found that not all acrylic resins that are compatible with cellulose acetate propionate (CAP) resins are compatible with polyurethane and nitrocellulose-containing ink and coating compositions. Among other reasons, this is believed to be due to poor solubility of some acrylic resins in ink and coating compositions. For example, Tables 2 and 4, infra, describe numerous ink and coating compositions containing different kinds of acrylic resins (and polyurethane resins that have and do not have amine functionality). In some instances, the acrylic resins that are employed are unsuitable because the solvent, which should be the basis of a clear and compatible solution, is often ester-based and/or ketone-based (mixtures of same may also be used). This may cause an unacceptable weakening of, for example, oriented polystyrene (OPS) shrink film, rendering it unsuitable for use. The particular polyurethane-urea resin and acrylic resin should be soluble in the selected solvent, have good flow properties, and be compatible with the nitrocellulose resin.

(10) Ink and coating compositions having the described combination of polyurethane resins with amine functionality, acrylic resins, and nitrocellulose binder resins (e.g., having the aforementioned Tg properties and/or monomer construction) exhibit desirable adhesion as evidenced by shrink coefficient, that is, compatibility between ink, coating, and shrinkable film, both before and after the film is shrunk to conform the film to the size and contour of the article to which the film is applied. Ink adhesion to the label, both before and after shrinking, is a factor in the assessed shrink coefficient numbers.

(11) Ink and coating compositions in accordance with the present disclosure exhibit suitable shrink coefficient (e.g., see Examples 2, 4, 10, 11 of Table 2). Certain comparative examples were found to be incompatible (e.g., Comparative Examples 8, 9, 12, 13, 14 and 15), e.g., the components thereof, e.g., the acrylic resins, are not compatible in the solvent. Further, Comparative Examples 1, 3, 5, 6, 7 and 16 failed the shrink coefficient test. Shrink coefficient accounts for the property or properties of a printed/cured ink or coating composition considered before and after the printed film is subjected to shrinkage. It is desired that the ink and coating compositions exhibit good adhesion, before and after shrinkage, which correlates to good shrink coefficient values. In the present application, shrinkage is achieved through a steam shrink test, which is described in the test methods section of the application.

(12) In a preferred embodiment, the finished inks or coatings of the present invention, containing the combination of aforedescribed resins exhibit Tg between −45 and −70° C.; and another between 65° C. to 100° C. when using Differential Scanning calorimetry (DSC) analysis. In another preferred embodiment the finished inks of the present invention, containing the combination of 3 resin-types described above, would have a singular Tg between 25° C. and 35° C.

(13) The elastomeric polyurethane resins having amine functionality contained the present ink and coating compositions comprise a component conferring elastomeric properties to the resin. In one aspect of the present disclosure, the inclusion of a pTHF component in the polyurethane resins confers desirable elastomeric properties upon the resins. Polyurethane resins may also include poly(propylene glycol) as a component that confers elastomeric properties upon the resins.

(14) In one aspect, resin components (a), (b) and (c) are present in the ink and coating compositions in the following amounts: (a) about 5 wt % to about 45 wt % elastomeric polyurethane resin, more preferably about 15 wt % to about 25 wt % @ about 30 wt % to about 35 wt % non-volatile component (NVC) solids; (b) about 1 wt % to about 20 wt % acrylic resin, more preferably about 5 wt % to about 15 wt %; and (c) about 4 wt % to about 12% wt % nitrocellulose resin, more preferably about 4 wt % to about 7 wt %. These amounts reflect the amount of the above components in the ink or coating compositions.

(15) Examples of the acrylic resins based on a methacrylate/styrene copolymer include Joncryl 581, Joncryl 587, Joncryl 678, Joncryl 682 and HSD201 (supplier: BASF Resins); and Neocryl B-819 (supplied by DSM). These resins may be used in both water- and solvent-based systems.

(16) Examples of elastomeric polyurethane resins with amine functionality include 72S (supplier BIP Oldbury Ltd), Burnock PU-5631, 3035 (DIC DPR Performance Resins) and Neorez U-471 and U-475 (DSM). Some of these resins include PPG and/or pTHF moieties in their polymer structures. Further, some or all of them include IPDI moiety in the polymer structures.

(17) Examples of nitrocellulose resins include DLX 3-5, DLXS-8, DLX30-50 (Nobel Industries), and A300 (Walsroder). In one aspect, the colorants may be incorporated into the inks and coating compositions of the present invention in the form of a nitrocellulose (NC) binder-color concentrate.

(18) Suitable solvents include ethanol, n-propanol, isopropanol, denatured alcohol (e.g., trade specific denatured alcohol (TSDA)), ethoxy propanol, methoxy propanol, propoxy propanol, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, methoxy propyl acetate, ethoxy propyl acetate, methoxy propoxy propanol glycol ether, propanol butoxy glycol ether, methoxy butanol glycol ether, ethyl lactate, and mixtures thereof.

(19) Suitable colorants include but are not limited to organic or inorganic pigments and dyes. Exemplary dyes include azo dyes, anthraquinone dyes, xanthene dyes, azine dyes, combinations thereof and the like. Exemplary organic pigments may be one pigment or a combination of pigments, such as for instance Pigment Yellow Numbers 12, 13, 14, 17, 74, 83, 114, 126, 127, 174, 188; Pigment Red Numbers 2, 22, 23, 48:1, 48:2, 52, 52:1, 53, 57:1, 112, 122, 166, 170, 184, 202, 266, 269; Pigment Orange Numbers 5, 16, 34, 36; Pigment Blue Numbers 15, 15:3, 15:4; Pigment Violet Numbers 3, 23, 27; and/or Pigment Green Number 7. Exemplary inorganic pigments include iron oxides, titanium dioxides, chromium oxides, ferric ammonium ferrocyanides, ferric oxide blacks, Pigment Black Number 7 and/or Pigment White Numbers 6 and 7. Aluminum- and mica-based pigments may also be used. Other organic and inorganic pigments and dyes can also be employed, as well as combinations that achieve the colors desired.

(20) Turning to FIG. 1, shown is a perspective view of a shrink sleeve (e) in tubular form with the ends (d1), (d2) of shrinkable substrate (a) arranged to overlap. A seam-sealing composition (not shown), may be applied to one or both of facing sides (d1), (d2) in order to form a bond in the seam (d). Color ink layer (b) and white ink layer (c) are printed on interior of shrinkable substrate (a). In the state of the art inks and coatings (i.e., prior to the present inventive ink and coating formulations), contact between points (b), (c) and (d) caused ink softening, removal and setting-off after storage on a reel. The present ink and coating compositions provide much better resistance and avoid the potentially adverse effects at the contact points.

(21) Turning to FIG. 2, shrink sleeve (e) is depicted over container (y), with container contents (x) spilling out of the container. The contents are shown seeping into the space between container (y) and sleeve (e). In the state of the art (i.e., prior to the present inventive ink and coating formulations), the spilled contents could degrade the ink layers (b), (c) printed on the inner side of the sleeve, shown here as forming the container volume indication “1 L” (e). This could cause state of the art inks to leach out of the layers and commingle with the spilled product contents (x). The present ink and coating compositions provide much better resistance and avoid the potentially adverse effects of such ink and container content interactions, such as, for example, providing better chemical resistance, thereby minimizing if not eliminating the undesirable leeching/commingling effect.

(22) The following examples illustrate specific aspects of the present invention and are not intended to limit the scope thereof in any respect and should not be so construed.

EXAMPLES

(23) Test Methods:

(24) Tape Adhesion

(25) Adhesive Tape (Scotch Tape 610 from 3M) is stuck on top of a proof print of the ink using finger pressure, and is then pulled off manually. Print evaluated level of ink removal. (ASTM F2252). A score of 5 is considered a pass. A score of 1 or 3 is considered a fail.

(26) Fingernail Adhesion

(27) Proof print is laid print-side up on a hard surface and back of index fingernail scratch across surface. Print evaluated for level of ink removal. A score of 5 is considered a pass. A score of 1 or 3 is considered a fail.

(28) Wrinkle Test

(29) The proof print is grasped with thumb and forefinger at either side of print, hands approx. 1″ apart, and rotated vigorously for 20 cycles to simulate repeated flexing of print. The level of ink removal and/or damage to print surface is assessed. A score of 5 is considered a pass. A score of 1 or 3 is considered a fail.

(30) Steam Shrink Test

(31) The print is placed in a steam sterilizer (bottle sterilizer) to fully shrink it; ordinarily this occurs in about 2 to about 4 minutes. The print is then dried using a paper cloth and evaluated for tape adhesion, scratch resistance and wrinkle test for level of ink removal. A score of 5 is considered a pass. A score of 1 or 3 is considered a fail.

(32) Ink samples were produced by mixing the ink components with a bladed laboratory paddle stirrer (100 rpm) adding the materials in order by weight in accordance with the formulations described in Tables 1 and 2. Test samples were reduced to printing viscosity 18 seconds DIN4 with solvent reducer (alcohol/ester blend 4:1 ratio). Proofs were produced using wirewound K-Bar (9 micron) onto various shrink film substrates available typically from Gunze, Klockner Pentaplast. The shrink sleeve films may be polyvinylchloride, polyesters, polyethylene terephthalate (PET), glycol-modified polyesters including polyethylene terephthalate glycol (PETG), oriented polystyrene (OPS) and polypropylene. Prints were dried at room temperature (25° C., RH 50%). Tests were performed pre-shrink to assess adhesion, wrinkle resistance, fingernail scratch resistance and non-blocking tendency. Shrink coefficient values were assessed. Prints were then folded and seamed using solvent to weld the film together to make a sleeve or tube. Tubes were place over glass containers and the sleeves were shrunk using steam. The sleeves were evenly shrunk using steam generated from a bottle sterilizer. Further tests were carried out on the prints when removed from the glass containers. Shrink coefficient values were assessed. Adhesion was measured by the industry standard method using self-adhesive tape Scotch 610 placed over the printed ink surface before and after shrinkage according to ASTM F2252. See Tables 1 and 2 for results.

Example 1 (Comparative)

(33) Into a solution of 7 wt % DLX 3-5 nitrocellulose resin in ethanol (Nobel), 25 wt % pigment B15:4 (DIC Fastogen) is milled to form a color concentrate (hereinafter, the “color concentrate”). The color concentrate is let down with an acrylic resin varnish including 40 wt % solids (Joncryl 581 (BASF)) with 60 wt % solvent, incorporated at 12.5 wt % into the above to give 5 wt % solids. Polyethylene (PE) wax from Shamrock Technologies is dispersed in the above using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(34) The composition of Example 1 does not include an elastomeric polyurethane resin with amine functionality with Tg between −45 to −70° C. Thus Example 1 is comparative.

Example 2 (Inventive)

(35) The color concentrate of Example 1 was prepared, and then let down with 24.5 wt % elastomeric polyurethane from DIC under the trade name of Burnock. An acrylic resin varnish including 40 wt % solids (Joncryl 587 (BASF)) with 60 wt % solvent is incorporated at 18.8 wt % into the above to give 7.5 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(36) Example 2 includes (a) an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C.; (b) an acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C.; and (c) nitrocellulose binder.

Example 3 (Comparative)

(37) The color concentrate of Example 1 was prepared, and then let down with 18.2 wt % elastomeric polyurethane from BIP Oldbury Limited under the trade name of Surkofilm 72s. An acrylic resin varnish including 40 wt % (Joncryl 682 (BASF)) with 60 wt % solvent is incorporated at 18.8 wt % into the above to give 7.5 wt % solids. A polyethylene (PE) wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(38) Example 3 is comparative due to the absence of elastomeric polyurethane resin with amine functionality based with Tg between −45 to −70° C. The elastomeric polyurethane does not have amine functionality.

Example 4 (Inventive)

(39) The color concentrate of Example 1 was prepared, and then let down with 24.5 wt % Burnock PU5631, an elastomeric polyurethane resin from DIC. An acrylic resin varnish including 40 wt % solids (Neocryl B-819 (DSM)) with 60 wt % solvent is incorporated into the above at 25 wt % to give 10 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(40) Example 4 includes (a) an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C.; (b) acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C.; and (c) nitrocellulose binder. Example 4 is inventive.

Example 5 (Comparative)

(41) The color concentrate of Example 1 was prepared, and then let down with 20.0 wt % Neorez u-471, an elastomeric polyurethane available from DSM. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(42) Example 5 is comparative due to the absence of elastomeric polyurethane resin with amine functionality with Tg between −45 to −70° C.; and the absence of acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C.

Example 6 (Comparative)

(43) The color concentrate of Example 1 was prepared, and then let down with 13.0 wt % Thermoplastic Polyurethane from BIP under the trade name of Surkopak 5244. An acrylic resin varnish including 40 wt % solids (Neocryl B-890 (DSM)) with 60 wt % solvent is incorporated into the above at 25 wt % to give 10 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100% formulation.

(44) Example 6 employs thermoplastic polyurethane. It does not include an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C. Also, while Example 6 includes an acrylic resin, this resin is not based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C. Thus, Example 6 is comparative.

Example 7 (Comparative)

(45) The color concentrate of Example 1 was prepared, and then let down by incorporating an acrylic resin varnish including 40 wt % solids (Neocryl B-890 (DSM)) with 60 wt % solvent at 50 wt % into the above to give 20 wt % solids. PE wax from Shamrock Technologies is dispersed into the above using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(46) Example 7 is comparative due to the absence of an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C.; and the absence of an acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C. (Neocryl B-890 is not based on a methacrylate/styrene co-polymer).

Example 8 (Comparative)

(47) The color concentrate of Example 1 was prepared, and then let down with 32.6 wt % Burnock PU5631, an elastomeric polyurethane from DIC. An acrylic resin varnish including 40 wt % solids of Lucite resin sold under the trade name Elvacite 2013 with 60 wt % solvent is incorporated at 12.5 wt % into the above to give 5 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(48) Example 8 is comparative due to the absence of acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C. (Elvacite 2013 is not based on a methacrylate/styrene co-polymer).

Example 9 (Comparative)

(49) The color concentrate of Example 1 was prepared, and then let down with 36.0 wt % Elastomeric Polyurethane from BIP under the trade name of Surkofilm 72s. An acrylic resin varnish including 40 wt % solids (Paraloid B72 (Rohm & Haas)) with 60 wt % solvent is incorporated and mixed into the above at 6.25 wt % to give 2.5 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(50) Example 9 is comparative due to the absence of an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C. (Surkofilm 72S does not have amine functionality); and the absence of an acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C. (Paraloid B72 is not based on a methacrylate/styrene co-polymer).

Example 10 (Inventive)

(51) The color concentrate of Example 1 was prepared, and then let down with 24.5 wt % Burnock PU563, an elastomeric polyurethane resin from DIC. An acrylic resin varnish including 40 wt % solids (Joncryl 678 (BASF)) with 60 wt % solvent is incorporated at 25 wt % into the above to give 10 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(52) Example 10 is inventive due to the inclusion of an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C.; (b) an acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C.; and (c) a nitrocellulose binder.

Example 11 (Inventive)

(53) The color concentrate of Example 1 was prepared, and then let down with 17.5 wt % Burnock PU3035, an elastomeric polyurethane resin from DIC. An acrylic resin varnish including 40 wt % solids (Joncryl 682 (BASF)) with 60 wt % solvent is incorporated at 12.5 wt % into the above to give 5 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(54) Example 11 is inventive due to the inclusion of an elastomeric polyurethane resin with amine functionality having Tg between −45 to −70° C.; (b) an acrylic resin based on a methacrylate/styrene co-polymer with Tg between 45 to 110° C.; and (c) nitrocellulose binder.

(55) Table 3 lists Comparative Examples 12-16, in which at least one of the materials has Tg not within the appropriate specified range.

Example 12 (Comparative)

(56) The color concentrate of Example 1 was prepared, and then let down with 20 wt % elastomeric polyurethane from Coim under the trade name of Novacote AP-1220. An acrylic resin varnish including 40 wt % solids (Neocryl B-804 (DSM)) with 60 wt % solvent is incorporated and mixed at 20 wt % into the above to give 8 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(57) Example 12 is comparative due to the elastomeric polyurethane resin with amine functionality having Tg above −45° C., and an acrylic resin (methacrylate co-polymer) having Tg not in the specified range of 45° C. to 110° C. Further, the methacrylate co-polymer resin does not contain styrene moieties.

Example 13 (Comparative)

(58) The color concentrate of Example 1 was prepared, and then let down with 20 wt % elastomeric polyurethane resin from DIC under the trade name Burnock 5631. An acrylic resin varnish including 40 wt % solids (Degalan PM555 (Evonik)) with 60 wt % solvent is incorporated and mixed in at 20 wt % into the above to give 8 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(59) Example 13 is comparative due to the absence of acrylic resin that is based on methacrylate/styrene co-polymer with Tg in the specified range between 45° C. to 110° C.

Example 14 (Comparative)

(60) The color concentrate of Example 1 was prepared, and then let down with 20 wt % elastomeric polyurethane resin from DIC under the trade name Burnock 5631. An acrylic resin varnish including 40 wt % solids (Degalan LP50/02 (Evonik)) with 60 wt % solvent is incorporated and mixed at 20 wt % into the above to give 8 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(61) Example 14 is comparative due to the absence of an acrylic resin that is based on a methacrylate/styrene co-polymer with Tg between 45° C. to 110° C.

Example 15 (Comparative)

(62) The color concentrate of Example 1 was prepared, and then let down with 20 wt % elastomeric polyurethane resin from DIC under the trade name Burnock 5631. An acrylic resin varnish including 40 wt % solids (Neocryl B-804 (DSM)) with 60 wt % solvent is incorporated at 20 wt % and mixed into the above to give 8 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(63) Example 15 is comparative due to the absence of an acrylic resin that is based on methacrylate/styrene co-polymer with Tg in the Inventive range between 45° C. to 110° C.

Example 16 (Comparative)

(64) The color concentrate of Example 1 was prepared, and then let down with 12.3 wt % elastomeric polyurethane resin from Coim under the trade name of Novacoat AP1220. An acrylic resin varnish including 40 wt % solids (Joncryl 682 (BASF)) with 60 wt % solvent is incorporated at 20.0 wt % and mixed into the above to give 8 wt % solids. PE wax from Shamrock Technologies is dispersed using a high speed shear mixer. To the above, ethanol and n-propyl acetate are added and mixed to provide a 100 wt % formulation.

(65) Example 16 is comparative due to the elastomeric polyurethane/urea resin having Tg above −45° C.

(66) TABLE-US-00001 TABLE 1 Ink Formulations Tg Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Resin/Description (° C.) (Comp.) (Inv.) (Comp.) (Inv.) (Comp.) (Comp.) NC color conc. NC/Pigment 50.0 50.0 50.0 50.0 50.0 50.0 Surkopak 5244 TPU −55 13.0 Surkofilm 72s EPU (not amine functional) −55 18.2 Neo-Rez u-471 EPU (not amine lunctional) −60 20.0 Burnock EPU (amine functional) −65 24.5 24.5 pu5631 Burnock EPU (amine functional) −70 pu3035 Joncryl 581 Acrylic (methacrylate/styrene co-polymer) 62 5.0 Joncryl 587 Acrylic (methacrylate/styrene co-polymer) 57 7.5 Neocryl B-819 Acrylic (methacrylate/styrene co-polymer) 49 10.0 Neocryl B-890 Acrylic (no styrene polymer) 70 10.0 Paraloid B72 Acrylic (no styrene polymer) 40 Elvacite 2013 Acrylic (no styrene polymer) 76 Joncryl 682 Acrylic (methacrylate/styrene co-polymer) 57 7.5 Joncryl 678 Acrylic (methacrylate/styrene co-polymer) 101 Shamrock PE Wax Powder 1.2 1.2 1.2 1.2 1.2 1.2 Ethanol/TSDA Solvent 13.3 6.9 2.1 5.9 2.8 4.6 n-Propyl Solvent 30.5 9.9 21.0 8.4 26.0 21.2 Acetate Total 100.0 100.0 100.0 100.0 100.0 100.0 Example 7 Example 8 Example 9 Example 10 Example 11 Resin/Description (Comp.) (Comp.) (Comp.) (Inv.) (Inv.) NC color conc. NC/Pigment 50.0 50.0 50.0 50.0 50.0 Surkopak 5244 TPU Surkofilm 72s EPU (not amine functional) 36.0 Neo-Rez u-471 EPU (not amine lunctional) Burnock EPU (amine functional) 32.6 24.5 pu5631 Burnock EPU (amine functional) 17.5 pu3035 Joncryl 581 Acrylic (methacrylate/styrene co-polymer) Joncryl 587 Acrylic (methacrylate/styrene co-polymer) Neocryl B-819 Acrylic (methacrylate/styrene co-polymer) Neocryl B-890 Acrylic (no styrene polymer) 20.0 Paraloid B72 Acrylic (no styrene polymer) 2.5 Elvacite 2013 Acrylic (no styrene polymer) 5.0 Joncryl 682 Acrylic (methacrylate/styrene co-polymer) 5.0 Joncryl 678 Acrylic (methacrylate/styrene co-polymer) 10.0 Shamrock PE Wax Powder 1.2 1.2 1.2 1.2 1.2 Ethanol/TSDA Solvent 4.3 7.4 0.0 5.9 18.0 n-Propyl Solvent 24.5 3.8 10.3 8.4 8.3 Acetate Total 100.0 100.0 100.0 100.0 100.0 TPU = Thermoplastic Polyurethane EPU = Elastomeric Polyurethane

(67) TABLE-US-00002 TABLE 2 Adhesion/Shrink Coefficient Before Shrinkage Adhesion (Scotch Tape 610) Scratch (Fingernail) Wrinkle Solubility OPP PET PVC OPS OPP PET PVC OPS OPP PET PVC OPS Example 01 (Comp.) C 1 5 1 3 5 5 5 5 5 5 5 5 Example 02 (Inv.) C 5 5 5 5 5 5 5 5 5 5 5 5 Example 03 (Comp.) C 5 5 5 5 5 5 5 5 5 5 5 5 Example 04 (Inv.) C 5 5 5 5 5 5 5 5 5 5 5 5 Example 05 (Comp.) C 5 5 1 3 5 5 5 5 5 5 5 5 Example 06 (Comp.) C 5 5 1 3 5 5 5 5 5 5 5 5 Example 07 (Comp.) C 5 5 1 5 5 5 5 5 5 5 5 5 Example 08 (Comp.) I NA NA NA NA NA NA NA NA NA NA NA NA Example 09 (Comp.) I NA NA NA NA NA NA NA NA NA NA NA NA Example 10 (Inv.) C 5 5 5 5 5 5 5 5 5 5 5 5 Example 11 (Inv.) C 5 5 5 5 5 5 5 5 5 5 5 5 After Steam Shrinkage Adhesion (Scotch Tape 610) Scratch (Fingernail) Wrinkle OPP PET PVC OPS OPP PET PVC OPS OPP PET PVC OPS Example 01 (Comp.) 1 1 1 1 1 1 1 1 1 1 1 1 Example 02 (Inv.) 5 5 5 5 5 5 5 5 5 5 5 5 Example 03 (Comp.) 1 5 1 5 1 5 1 3 3 5 1 5 Example 04 (Inv.) 5 5 5 5 5 5 5 5 5 5 5 5 Example 05 (Comp.) 1 5 1 3 1 5 1 3 3 1 1 3 Example 06 (Comp.) 1 1 1 1 1 1 1 1 1 1 1 1 Example 07 (Comp.) 1 5 1 3 1 5 3 5 1 5 3 5 Example 08 (Comp.) NA NA NA NA NA NA NA NA NA NA NA NA Example 09 (Comp.) NA NA NA NA NA NA NA NA NA NA NA NA Example 10 (Inv.) 5 5 5 5 5 5 5 5 5 5 5 5 Example 11 (Inv.) 5 5 5 5 5 5 5 5 5 5 5 5 Solubility: C = Compatible I = Incompatible Adhesion: 5 = Pass Full Ink Adhesion, >90% 3 = Partial Fail Ink Adhesion, ~50% Removal 1 = Fail, No Ink Adhesion, ~100% Removal NA = Not applicable. These examples were not tested further due to incompatibility.

(68) TABLE-US-00003 TABLE 3 Further Comparative Ink Formulations Comparative Comparative Comparative Comparative Comparative Tg Example 12 Example 13 Example 14 Example 15 Example 16 NC Color conc. NC/pigment — 50.0 50.0 50.0 50.0 50.0 Novacote AP1220 elastomeric amine −34 20.0 12.3 functional polyurethane urea Burnock PU5631 elastomeric amine −65 20.0 20.0 20.0 functional polyurethane urea Neocryl B804 Acrylic (non-styrenated) 33 8.0 8.0 Degalan PM555 Acrylic (non-styrenated) −43 8.0 Degalan LP 50/02 Acrylic (non-styrenated) 115 8.0 Joncryl 682 Acrylic (methacrylate/ 57 10.0 styrene co-polymer) Shamrock PE Wax powder 1.2 1.2 1.2 1.2 1.2 Ethanol/TSDA solvent 5.5 14.0 14.0 14.0 10.5 Normal Propyl solvent 15.3 6.8 6.8 6.8 16.0 acetate Total 100 100 100 100 100

(69) TABLE-US-00004 TABLE 4 Adhesion/Shrink Coefficient Before Shrinkage Adhesion (Scotch Tape 610) Scratch (Fingernail) Wrinkle Solubility OPP PET PVC OPS OPP PET PVC OPS OPP PET PVC OPS Example 12 (Comp.) I N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 13 (Comp.) I N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 14 (Comp.) I N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 15 (Comp.) I N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 16 (Comp.) C 5 5 1 1 5 5 5 5 5 5 3 5 After Steam Shrinkage Adhesion (Scotch Tape 610) Scratch (Fingernail) Wrinkle OPP PET PVC OPS OPP PET PVC OPS OPP PET PVC OPS Example 12 (Comp.) N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 13 (Comp.) N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 14 (Comp.) N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 15 (Comp.) N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A N/A Example 16 (Comp.) 5 5 1 1 5 5 1 1 3 5 1 1 Solubility: C = Compatible I = Incompatible Adhesion: 5 = Pass Full Ink Adhesion, >90% 3 = Partial Fail Ink Adhesion, ~50% Removal 1 = Fail, No Ink Adhesion, ~100% Removal NA = Not applicable. These examples were not tested further due to incompatibility.
Summary of Table 2:

(70) Examples 2, 4, 10 & 11 shows that the resin combinations in these samples produce an ink that is stable and gives the required ink film properties before and after the steam shrinking tests are completed on various filmic substrates.

(71) Examples 1, 3, 5, 6 and 7 shows that these resins, although compatible, give a mixed performance for adhesion that can be seen on various filmic substrates films prior to steam shrinking. After steam shrinking the ink film properties of adhesion, scratch and wrinkle on all films shows various degrees of failure.

(72) Examples 8 and 9 are shown to be incompatible when mixed, producing a solution with poor flow and instability between resin solutions. These resins used do not contain a methacrylate/styrene co-polymer.

(73) Solubility of some Comparative Examples mixtures is poor (see Table 2, Examples 8 and 9 and Table 4, Examples 12, 13, 14, 15), leading to incompatibility issues observed by the cloudy/hazing of mixtures giving rise to phase separation and poor homogeneity. This causes undesirable effects on the print process including poor adhesion to substrate, lack of film formation, and undesirable matting effect. Examples exhibiting incompatibility were not tested further.

(74) Summary of Table 4:

(75) Examples 12, 13, 14, and 15 shown to be incompatible when mixed, producing a solution with poor flow and instability between resin solutions.

(76) Example 16 shows that these resins, although compatible, give a mixed performance for adhesion that can be seen on various filmic substrates films prior to steam shrinking. After steam shrinking, the ink film properties of adhesion, scratch and wrinkle on all films shows various degrees of failure.

(77) The present invention has been described in detail, including the preferred embodiments thereof. However, it will be appreciated that those skilled in the art, upon consideration of the present disclosure, may make modifications and/or improvements on this invention that fall within the scope and spirit of the invention.