SiC freestanding film structure

Abstract

A SiC Freestanding Film Structure capable of preventing a functional surface of a SiC Freestanding Film Structure from being affected by a film thickness and improving strength by increasing the film thickness, the SiC Freestanding Film Structure is formed by depositing a SiC layer through a vapor deposition type film formation method. The SiC layer is deposited with respect to a first SiC layer serving as a functional surface in the SiC Freestanding Film Structure. Focusing on the functional surface and a non-functional surface positioned on front and back sides of any particular portion, the functional surface has smoothness higher than that of the non-functional surface.

Claims

1. A SiC Freestanding Film Structure formed by laminating a plurality of SiC layers on a surface of a porous substrate through a vapor deposition type film formation method, and then removing the porous substrate after the plurality of SiC layers have been laminated, comprising employing, as the porous substrate, a female-molded substrate having an inverted shape of a desired structure shape including a masking to a lower end of the porous substrate, wherein the plurality of SiC layers includes a first SiC layer, a main surface of the SiC Freestanding Film Structure is a functional surface of the first SiC layer having minute protrusions and the functional surface is configured in contact with the surface of the female-molded substrate a second SiC layer configured as a non-functional surface is deposited on a side opposite to the functional surface of the first SiC layer, wherein a corner portion of the functional surface sharper than that of the non-functional surface before removing the female-molded substrate.

2. The SiC Freestanding Film Structure according to claim 1, wherein the functional surface has the minute protrusions generated by a material property of the porous substrate.

3. The SiC Freestanding Film Structure according to claim 2, wherein the material of the porous substrate comprises graphite.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 is a diagram illustrating a configuration of a SiC Freestanding Film Structure according to an embodiment of the invention;

(2) FIGS. 2A to 2F are diagrams for describing a manufacturing process of the SiC Freestanding Film Structure according to an embodiment of the invention; and

(3) FIG. 3 is a diagram illustrating a modification of the SiC Freestanding Film Structure.

DESCRIPTION OF EMBODIMENTS

(4) A SiC Freestanding Film Structure according to an embodiment of the invention will now be described in details with reference to the accompanying drawings. Note that the following embodiments are a part of preferable modes for embodying the invention, and even some modifications for a part of the configuration may be regarded as a part of the invention as long as a specific requirement of the invention is satisfied.

(5) <Configuration>

(6) According to this embodiment, a SiC Freestanding Film Structure 10 is configured by allowing a SiC film to have a self-supporting strength. FIG. 1 shows a boat as a tool used in semiconductor wafer manufacturing. However, FIG. 1 also shows that the SiC Freestanding Film Structure 10 according to this embodiment is applicable to various shapes having unevennesses as well as a plane structure, and it is not intended to limit the shape or the application.

(7) The SiC Freestanding Film Structure 10 of FIG. 1 has one surface functioning as a boat. That is, a main surface provided with slits 16 for supporting a wafer 50 is set as a functional surface 12. As recognized from a partially enlarged view surrounded by a circle in FIG. 1, the functional surface 12 of the SiC Freestanding Film Structure 10 according to an embodiment of the invention has a plurality of minute protrusions 12b that are difficult to be obtained through mechanical machining. Since the functional surface 12 has such minute protrusions 12b, it is possible to reduce a contact area between the supported material (for example, a wafer 50) and the SiC Freestanding Film Structure 10. For this reason, it is possible to prevent the wafer 50 from adhering to the SiC Freestanding Film Structure 10 in the event of heating or cooling. In addition, it is possible to suppress a temperature difference between a portion exposed to the gas atmosphere and the contact portion.

(8) Focusing on corner portions 12a and 14a, the corner portion 12a of the functional surface 12 has a sharp corner, whereas the corresponding part (corner portion 14a) of the non-functional surface 14 has a smoother corner, compared to the functional surface 12.

(9) As described below in details, this causes the functional surface 12 of the SiC Freestanding Film Structure 10 to come into contact with the substrate 30 (see FIGS. 2A to 2F) to form a shape matching the surface shape thereof. For this reason, it is possible to match the shape of the functional surface 12 to the shape of the substrate 30 with high accuracy.

(10) <Manufacturing Process>

(11) A manufacturing process of the SiC Freestanding Film Structure 10 according to this embodiment having such a configuration will be described with reference to FIGS. 2A to 2F. First, as illustrated in FIG. 2A, a substrate 30 having inverted unevennesses of a desired structure, that is, a female-molded substrate 30 is fabricated. The substrate 30 is preferably formed of a porous material having minute pores on the surface, such as graphite. Note that a masking 32 is applied to a lower end of the substrate 30 to allow installation to a reference surface.

(12) Then, as illustrated in FIG. 2B, a first SiC layer 20 is formed on the surface of the substrate 30 through a vapor deposition type film formation method. Note that the vapor deposition type film formation method may include, for example, a chemical vapor deposition (CVD) method. Here, the graphite surface of the substrate 30 has a plurality of pores. The first SiC layer 20 formed through the CVD method is also formed inside the pores provided on the surface of the substrate 30. The first SiC layer 20 provided inside the pores in this manner is used to form minute protrusions 12b provided on the functional surface 12.

(13) After formation of the first SiC layer 20, as illustrated in FIG. 2C, a laminated SiC layer 22 is formed by deposition with respect to the first SiC layer 20. Here, although it is not necessary to provide any difference in configuration between the first SiC layer 20 and the laminated SiC layer 22 deposited on the first SiC layer 20, the first SiC layer 20 is formed on the surface of the substrate 30. For this reason, the first SiC layer 20 has a shape or property matching that of the substrate 30 with high accuracy.

(14) After the thickness of the laminated SiC layer 22 reaches a level allowing a desired strength, the substrate 30 used to form the SiC layer (including the first SiC layer 20 and the laminated SiC layer 22) is removed from the reference surface, and the unnecessary part (a part over the dotted line in FIG. 2D) is cut out as illustrated in FIG. 2D. After removing the unnecessary part as illustrated in FIG. 2E, the substrate 30 is removed. In a case where graphite is employed as the substrate 30, the substrate 30 may be removed by heating the substrate 30 having the SiC layer formed thereon under a high-temperature oxidation atmosphere.

(15) The graphite heated under a high-temperature oxidation atmosphere is changed to a gas as CO.sub.2 and is burned out. For this reason, it is possible to remove the substrate 30 even for a complicated or minute shape difficult to remove through mechanical machining.

(16) By removing the substrate 30 in this manner, it is possible to form a SiC Freestanding Film Structure 10 as illustrated in FIG. 2F.

(17) <Advantageous Effects>

(18) In this manner, the SiC Freestanding Film Structure 10 according to an embodiment of the invention is formed by sequentially depositing the laminated SiC layer 22 with respect to the first SiC layer 20 as the functional surface 12. For this reason, the functional surface 12 of the SiC Freestanding Film Structure 10 has a shape matching that of the substrate 30 with high accuracy. In addition, since the shape accuracy is not affected by the film thickness, it is possible to improve the strength of the SiC Freestanding Film Structure 10 by increasing the film thickness.

(19) <Modifications>

(20) As described above, the functional surface 12 of the SiC Freestanding Film Structure 10 according to this embodiment is not affected by the film thickness. For this reason, as illustrated in FIG. 3, it is possible to maintain desired accuracy of the functional surface 12 even when the widths of trenches on the non-functional surface 14 are narrowed by increasing the film thickness of the SiC film. Therefore, it is possible to provide a SiC Freestanding Film Structure 10 having high fabrication accuracy even when a heavy weight object is disposed or held.

(21) When a metal having a smooth surface is employed as the substrate 30, surface treatment for forming minute unevennesses on the surface (such as sand blasting) may be performed to provide the functional surface 12 having the minute protrusions as described above in the embodiment. Note that, when a metal is employed in the substrate 30, the substrate 30 may be removed by dissolving the substrate 30 with a chemical solution.

(22) The CVD method has been described as a method of forming a vapor deposition type film in the aforementioned embodiment. Using the vapor deposition based on the CVD method, it is possible to uniformize the film thickness, compared to the vacuum type physical vapor deposition (PVD) method or the molecular beam epitaxy (MBE) method. For this reason, the CVD method was effective as a manufacturing method of the SiC Freestanding Film Structure in the prior art, in which the functional surface is the final deposition surface. However, in the SiC Freestanding Film Structure 10 according to an embodiment of the invention, the laminated SiC layer 22 is deposited with respect to the first SiC layer 20 of the functional surface 12. For this reason, it is possible to manufacture the product with high accuracy even when a deposition technique based on the PVD method or the MBE method as the vacuum type deposition method is applied.

(23) In the aforementioned embodiment, a boat has been described as an example of the SiC Freestanding Film Structure 10. However, the shape of the SiC Freestanding Film Structure 10 may also be applied to any shape for various purposes, such as a wafer holder or a susceptor.

REFERENCE SIGNS LIST

(24) 10 SiC Freestanding Film Structure,

(25) 12 functional surface,

(26) 12a corner portion,

(27) 12b minute protrusion,

(28) 14 non-functional surface,

(29) 14a corner portion,

(30) 16 slit,

(31) 20 first SiC layer,

(32) 22 laminated SiC layer,

(33) 30 substrate,

(34) 32 masking,

(35) 50 wafer.