Abstract

A method of press forming that forms a press-formed product into a target shape, the method including: forming a top portion; forming a side wall portion and a flange portion such that a side wall height of the side wall portion of the press-formed product becomes larger than a side wall height of the target shape, where the side wall height of the side wall portion is formed to be larger than the side wall height of the target shape by adding a value half or less of a radius of curvature of the ridge, in a longitudinal direction vertical cross section, of the target shape; and reforming a ridge between the side wall portion and the flange portion such that the side wall height of the side wall portion becomes the side wall height of the target shape.

Claims

1. A method of press forming that forms a press-formed product into a target shape, the press-formed product having: a top portion; a side wall portion continuing from the top portion; and a flange portion continuing from the side wall portion via a ridge, the flange portion being configured to curve at least in a convex or concave manner in a height direction, the method comprising: forming the top portion having the same shape as a top portion of the target shape of the press-formed product; and forming the side wall portion and the flange portion such that a side wall height of the side wall portion of the press-formed product becomes larger than a side wall height of the target shape, where the side wall height of the side wall portion is formed to be larger than the side wall height of the target shape by adding a value half or less of a radius of curvature of the ridge, in a longitudinal direction vertical cross section, of the target shape; and reforming the ridge between the side wall portion and the flange portion such that the side wall height of the side wall portion becomes the side wall height of the target shape.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0019] FIG. 1 is a diagram illustrating a process of forming a press-formed product curved in a convex manner in a height direction by a press forming method according to an embodiment of the invention and stress distributions in the process of forming.

[0020] FIG. 2 is a diagram explaining a working effect of the press forming method according to the embodiment of the invention (part 1).

[0021] FIG. 3 is an explanatory view of a mechanism of an effect of the press forming method according to the embodiment of the invention.

[0022] FIG. 4 is a diagram illustrating an example of the effect of the press forming method according to the embodiment of the invention (part 1).

[0023] FIG. 5 is a diagram illustrating a process of forming a press-formed product curved in a concave manner in the height direction by the press forming method according to the embodiment of the invention and stress distributions in the process of forming.

[0024] FIG. 6 is a diagram explaining the working effect of the press forming method according to the embodiment of the invention (part 2).

[0025] FIG. 7 is a diagram illustrating an example of the effect of the press forming method according to the embodiment of the invention (part 2).

[0026] FIG. 8 is a diagram illustrating a target shape of the press-formed product curved in a convex manner in the height direction serving as a forming object in the embodiment of the invention ((a) is a perspective view and (b) is a longitudinal direction vertical cross section).

[0027] FIG. 9 is a diagram illustrating a curve in the height direction of the press-formed product serving as the forming object in the embodiment of the invention.

[0028] FIG. 10 is a diagram illustrating a target shape of the press-formed product curved in a concave manner in the height direction serving as a forming object in the embodiment of the invention ((a) is a perspective view and (b) is a longitudinal direction vertical cross section).

[0029] FIG. 11 is a diagram illustrating an example of the press-formed product curved in a convex manner in the height direction serving as the object in the invention ((a) is a perspective view, (b) is a side view, and (c) is a top view).

[0030] FIG. 12 is a diagram illustrating a process of forming the press-formed product curved in a convex manner in the height direction by a conventional press forming method.

[0031] FIG. 13 is a diagram illustrating deformations of a blank and stress distributions in the process of forming the press-formed product curved in a convex manner in the height direction by the conventional press forming method.

[0032] FIG. 14 is a diagram illustrating an example of the press-formed product curved in a concave manner in the height direction serving as the object in the invention ((a) is a perspective view, (b) is a side view, and (c) is a top view).

[0033] FIG. 15 is a diagram illustrating a process of forming a press-formed product curved in a concave manner in the height direction by a conventional press forming method.

[0034] FIG. 16 is a diagram illustrating deformations of the blank and stress distributions in the process of forming the press-formed product curved in a concave manner in the height direction by the conventional press forming method.

DESCRIPTION OF EMBODIMENTS

[0035] A press forming method according to an embodiment of the invention forms the press-formed product 1 curved in a convex manner in the height direction along the longitudinal direction as exemplarily illustrated in FIG. 11 in a target shape. The press forming method includes a first forming process (FIGS. 1(a) and 1(b)) and a second forming process (FIGS. 1 (b) and 1(c)). The following describes the first forming process and the second forming process.

[0036] First Forming Process

[0037] As illustrated FIGS. 1(a) and 1(b), the first forming process forms the top portion 3 having the same shape as the target shape of the press-formed product 1 from the blank 41, and forms the side wall portion 5 and the flange portion 7 such that the side wall height (=h1) of the side wall portion 5 is larger than the side wall height (h2 in FIG. 1(c)) of the target shape (h1>h2). The side wall height h1 of the side wall portion 5 is set to be larger than the side wall height h2 of the target shape by addition of a value half or less of a radius of curvature of the flange side ridge 11 in a longitudinal direction vertical cross section of the target shape.

[0038] In the first forming process, the position of the top side ridge 9, which is the ridge between the top portion 3 and the side wall portion 5 on the blank 41, is the same as that of the target shape, and the position of the flange side ridge 11, which is the ridge between the side wall portion 5 and the flange portion 7 on the blank 41, is shifted from that of the target shape, so as to form the top portion 3 having the same shape as the target shape and form the side wall portion 5 and the flange portion 7 such that the side wall height is larger than the target shape.

[0039] In the embodiment, as illustrated in FIG. 1, the distance between the top portion 3 and the flange portion 7 in the height direction of the press-formed product 1 is the side wall height of the side wall portion 5. The side wall height of the side wall portion 5 may be a distance between the top portion 3 and the flange portion 7 in an in-plane direction on the side wall portion 5.

[0040] Second Forming Process

[0041] As illustrated in FIGS. 1(b) and 1(c), the second forming process reforms the flange side ridge 11 between the side wall portion 5 and the flange portion 7 such that the side wall portion 5 formed by the first forming process has the side wall height h2 of the target shape so as to form the press-formed product 1 having the target shape.

[0042] The following describes a working effect of the press forming method according to the embodiment with reference to FIGS. 2 to 4. FIG. 2 is a diagram of the process of forming the press-formed product 1 from the blank 41 in a side view. The first bottom dead center in FIG. 2 is the bottom dead center of forming in the first forming process. The second bottom dead center in FIG. 2 is the bottom dead center of forming in the second forming process.

[0043] As described above, the first forming process forms, from the blank 41, the side wall portion 5, the flange portion 7, and the flange side ridge 11 such that the side wall height h1 of the side wall portion 5 is larger than the side wall height h2 of the target shape. The longitudinal direction length of the flange side ridge 11 formed by the first forming process is shorter than the longitudinal direction length of the portion corresponding to the flange side ridge 11 on the blank 41 before the forming process.

[0044] For example, in FIG. 2, a point a0 and a point b0 on the blank 41 before the forming process are assumed to move to a point a1 and a point b1, respectively, at the bottom dead center of forming in the first forming process, the flange length between a1 and b1 is shorter than the flange length between a0 and b0. In this way, in the first forming process, the flange portion 7 (the flange side ridge 11) is formed by being subjected to shrink flange deformation, in which the longitudinal direction length is reduced, resulting in compressive stress being generated in the flange portion 7 in the longitudinal direction.

[0045] The succeeding second forming process reforms the flange side ridge 11 such that the side wall portion 5 has the side wall height h2 of the target shape. The longitudinal direction length of the flange side ridge 11 at the bottom dead center of forming in the second forming process is longer than the longitudinal direction length at the bottom dead center of forming in the first forming process.

[0046] For example, in FIG. 2, the point a1 and the point b1 at the bottom dead center of forming (the first bottom dead center) in the first forming process are assumed to move to a point a2 and a point b2, respectively, at the bottom dead center of forming (the second bottom dead center) in the second forming process, the flange length between a2 and b2 is longer than the flange length between a1 and b1.

[0047] In the second forming process, the flange side ridge 11 is reformed such that the longitudinal direction length of the flange portion 7 is increased, resulting in tensile deformation toward outside in the longitudinal direction acting on the flange portion 7.

[0048] In this way, the flange portion 7 is formed by the first forming process in such a manner to have the longitudinal direction length shorter than that of the target shape of the press-formed product 1, and in the succeeding second forming process, the flange portion 7 is formed such that the longitudinal direction length is restored to that of the target shape of the press-formed product 1. In the first forming process, a large strain is generated in the flange portion 7, resulting in compressive stress being generated. The compressive stress is, however, significantly reduced as a result of slight restoration of the strain in the second forming process. The second forming process utilizes a characteristic that the stress is sensitively largely changed in accordance with slight restoration of the strain.

[0049] The characteristic is described with reference to FIG. 3. FIG. 3 is a stress-strain diagram in the longitudinal direction from start of forming the flange portion to the second bottom dead center. As illustrated in FIG. 3, large stress is accumulated in the flange portion at the first bottom dead center in the first forming process. The stress is, however, significantly reduced by slight restoration of the strain from the first bottom dead center to the second bottom dead center by the second forming process. In this way, the invention utilizes a characteristic that the stress is sensitively largely changed in accordance with slight restoration of the strain.

[0050] As illustrated in FIG. 4, the compressive stress in the flange portion 7 at the bottom dead center of forming in the second forming process in the invention (FIG. 4(a)) is further reduced than the compressive stress in the flange portion 7 generated by a conventional press forming method (FIG. 4(b)). As a result, this reduction makes it possible to suppress springback at die release of the press-formed product 1 after the second forming process, and to reduce a change in angle made between the side wall portion 5 and the flange portion 7.

[0051] Furthermore, the press forming method according to the embodiment can not only reduce the compressive stress in the flange portion 7 but also reduce the tensile stress in the vicinity of the top side ridge 9 between the top portion 3 and the side wall portion 5.

[0052] As illustrated in FIG. 1(b), tensile stress is generated in the vicinity of the top side ridge 9 at the bottom dead center of forming in the first forming process. In the second forming process, in which the flange side ridge 11 is formed such that the side wall height becomes the target shape, tensile deformation acts on the flange portion 7 while compressive deformation acts on the top side ridge 9. As a result, as illustrated in FIG. 1(c), the tensile stress at the bottom dead center of forming in the second forming process can be reduced in the vicinity of the top side ridge 9.

[0053] As described above, the press forming method according to the embodiment reduces the tensile stress in the top side ridge 9 in addition to the reduction of the compressive stress in the flange portion 7, thereby suppressing springback in the flange portion 7. Furthermore, the first forming process and the second forming process can perform the forming without change in the angle made between the side wall portion 5 and the flange portion 7. The flange portion 7, thus, can be formed at the target angle, e.g., horizontally (a direction orthogonal to the forming direction).

[0054] As described above, in the first forming process, the side wall height of the side wall portion 5 is set to be larger than the side wall height of the target shape by addition of a value half or less of the radius of curvature of the flange side ridge 11 in the longitudinal direction vertical cross section of the target shape. The effect of the value added to the side wall height is verified in examples described later.

[0055] The above describes the press-formed product 1 (refer to FIG. 11) curved in a convex manner in the height direction. The press forming method according to the invention may be applied to forming of the press-formed product 21 curved in a concave manner in the height direction as exemplarily illustrated in FIG. 14.

[0056] When the press-formed product 21 is formed, the forming is performed by two processes as illustrated in FIG. 5, i.e., the first forming process (FIGS. 5(a) and 5(b)), and the second forming process (FIGS. 5(b) and 5(c)).

[0057] The first forming process forms the top portion 3 having the same shape as the target shape of the press-formed product 1 from the blank 41, and forms the side wall portion 5, the flange portion 7, and the flange side ridge 11 such that the side wall height h1 of the side wall portion 5 is larger than the side wall height h2 of the target shape (h1>h2) (FIGS. 5(a) and 5(b)). The side wall height h1 of the side wall portion 25 is set to be larger than the side wall height h2 of the target shape by addition of a value half or less of a radius of curvature of the flange side ridge 31 in a longitudinal direction vertical cross section of the target shape.

[0058] The succeeding second forming process reforms the flange side ridge 31 between the side wall portion 25 and the flange portion 27 such that the side wall portion 25 formed in the first forming process has the side wall height h2 of the target shape so as to form the press-formed product 21 having the target shape (FIGS. 5(b) and 5(c)).

[0059] The working effect of the forming of the press-formed product 21 curved in a concave manner in the height direction is described with reference to FIGS. 6 and 7. FIG. 6 is a diagram of the process of forming the press-formed product 21 from the blank 41 in a side view. The first bottom dead center in FIG. 6 is the bottom dead center of forming in the first forming process. The second bottom dead center in FIG. 6 is the bottom dead center of forming in the second forming process.

[0060] As illustrated in FIG. 6, a point c0 and a point d0 on the blank 41 before the forming process are assumed to move to a point c1 and a point d1, respectively, at the bottom dead center of forming (the first bottom dead center) in the first forming process, the flange length between c1 and d1 is longer than the flange length between c0 and d0. In this way, in the first forming process, the flange portion 27 (the flange side ridge 31) is formed by being subjected to stretch flange deformation, in which the longitudinal direction length is increased, resulting in tensile stress being generated in the flange portion 27 in the longitudinal direction.

[0061] The succeeding second forming process reforms the flange side ridge 31 such that the side wall portion 25 has the side wall height h2 of the target shape. The longitudinal direction length of the flange side ridge at the bottom dead center of forming in the second forming process is shorter than the longitudinal direction length at the bottom dead center of forming in the first forming process.

[0062] For example, in FIG. 6, the point c1 and the point d1 at the bottom dead center of forming (the first bottom dead center) in the first forming process are assumed to move to a point c2 and a point d2, respectively, at the bottom dead center of forming (the second bottom dead center) in the second forming process, the flange length between c2 and d2 is shorter than the flange length between c1 and d1.

[0063] In the second forming process, the flange side ridge 31 is reformed such that the longitudinal direction length of the flange portion 27 is reduced, resulting in compressive deformation toward inside in the longitudinal direction acting on the flange portion 27.

[0064] In this way, the flange portion 27 is formed such that the longitudinal direction length is longer than that of the target shape of the press-formed product 21 in the first forming process, and in the succeeding second forming process, the flange portion 27 is formed such that the longitudinal direction length is restored to that of the target shape of the press-formed product 21. In the first forming process, a large strain is generated in the flange portion 27, resulting in tensile stress being generated. The tensile stress is, however, significantly reduced as a result of slight restoration of the strain in the second forming process. The reason is the same as that described with reference to FIG. 3.

[0065] As illustrated in FIG. 7, the tensile stress in the flange portion 27 at the bottom dead center of forming in the second forming process of the invention (FIG. 7(a)) is further reduced than the tensile stress in the flange portion 27 generated by the conventional press forming method (FIG. 7(b)). As a result, this reduction makes it possible to suppress springback at die release of the press-formed product 21 after the second forming process, and to reduce a change in angle made between the side wall portion 25 and the flange portion 27.

[0066] Furthermore, when the press-formed product 21 is formed by the press forming method according to the invention, not only the tensile stress in the flange portion 27 but also the compressive stress in the vicinity of the top side ridge 29 between the top portion 23 and the side wall portion 25 can be reduced.

[0067] As illustrated in FIG. 5(b), compressive stress is generated in the vicinity of the top side ridge 29 at the bottom dead center of forming in the first forming process. In the second forming process, in which the flange side ridge 31 is reformed such that the side wall height becomes the target shape, compressive deformation acts on the flange portion 27 while tensile deformation acts on the top side ridge 29. As a result, as illustrated in FIG. 5(c), the compressive stress at the bottom dead center of forming in the second forming process can be reduced in the vicinity of the top side ridge 29.

[0068] As described above, the press forming method according to the embodiment can reduce the compressive stress in the top side ridge 29 in addition to the reduction of the tensile stress in the flange portion 27, thereby further suppressing springback in the height direction in the flange portion 27. Furthermore, the first forming process and the second forming process can perform the forming without change in the angle made between the side wall portion 25 and the flange portion 27. The flange portion 27, thus, can be formed at the target angle, e.g., horizontally (a direction orthogonal to the forming direction).

[0069] The above describes a case where the forming object is the press-formed product in which both the top portion and the flange portion are curved in a convex or concave manner in the height direction. The invention may be applied to a press-formed product in which at least the flange portion is curved in a convex or concave manner in the height direction. The top portion may have a flat surface shape without being curved in the height direction.

[0070] For example, in a press-formed product (not illustrated) in which the top portion has a flat surface shape and the flange portion is curved in a convex manner in the height direction, the top side ridge at which the top portion and the side wall portion are connected has a straight line shape along the longitudinal direction in a side view.

[0071] When such a press-formed product is formed by the press forming method according to the invention, compressive stress is generated in the flange portion and tensile stress is generated in the vicinity of the top side ridge having a straight line shape in the first forming process in the same manner as the press-formed product 1 (refer to FIG. 1). The press forming method according to the invention can reduce the compressive stress in the flange portion and the tensile stress in the vicinity of the top side ridge having a straight line shape in the second forming process, thereby making it possible to suppress springback after die release.

[0072] In a press-formed product in which the top portion has a flat surface shape and the flange portion is curved in a concave manner, tensile stress is generated in the flange portion and compressive stress is generated in the top side ridge having a straight line shape in the first forming process in the same manner as the press-formed product 21 (refer to FIG. 5). The press forming method according to the invention can reduce the tensile stress in the flange portion and the compressive stress in the vicinity of the top side ridge having a straight line shape in the second forming process, thereby making it possible to suppress springback after die release.

[0073] The above describes the press-formed product in which the side wall portion continues from one side of the top portion. The invention may be applied to a press-formed product in which a pair of side wall portions continue from two opposing sides of the top portion, i.e., which has a hat-shaped cross section.

Examples

[0074] The verification was done for checking the working effect of the press forming method according to the invention. The following describes the verification.

[0075] In an example, press forming analysis was performed on the press-formed product 1 illustrated in FIG. 8 serving as the forming object. Springback analysis was performed using the analysis result of the press forming analysis. On the basis of the springback analysis result, the springback in the flange portion 7 of the press-formed product 1 was evaluated.

[0076] In the press forming analysis, a 980 MPa grade steel sheet having a thickness of 1.2 mm was used for a blank. FIGS. 8 and 9 illustrate a target shape of the press-formed product 1 serving as the forming object. The target shape of the press-formed product 1 is specified as follows. As illustrated in FIG. 9, the radius of curvature (camber convex R in FIG. 9) of the curve having a convex manner in the height direction is 1000 mm or 500 mm. As illustrated in FIG. 8(b), the side wall height of the side wall portion 5 is 30 mm, the angle made between the top portion 3 and the side wall portion 5 is 95°, the angle made between the side wall portion 5 and the flange portion 7 is 95°, and the top portion 3 and the flange portion 7 are in parallel (the flange portion 7 is horizontal). The radius of curvature of the top side ridge 9 in the longitudinal direction vertical cross section (A-A′ arrow cross section in FIG. 8(a)) of the target shape is 5 mm. The radius of curvature of the flange side ridge 11 in the longitudinal direction vertical cross section (A-A′ arrow cross section in FIG. 8(a)) of the target shape is 6.2 mm.

[0077] The press forming analysis was performed on the process of forming the press-formed product 1 by two processes, i.e., the first forming process to perform forming by changing the side wall height of the side wall portion 5 and the second forming process to perform forming such that the side wall height becomes the target shape. In the springback analysis, springback behavior obtained by the press forming analysis of the press-formed product 1 after die release at the bottom dead center of forming in the second forming process was analyzed, and an amount of change in angle between the side wall portion 5 and the flange portion 7 before die release and after the die release was obtained as a springback amount.

[0078] In the example, the press-formed product 1 formed by the press forming method according to the invention was denoted as an example. As for comparison, the press-formed product 1 formed in a single process was denoted as a conventional example, and the press-formed product 1 that was formed by two processes, i.e., the first forming process and the second forming process, and was formed by the first forming process such that the side wall height of the side wall portion 5 was out of the range of the invention was denoted as a comparative example.

[0079] Tables 1 and 2 illustrate the side wall heights h1 of the side wall portions formed by the first forming process, angles θ1, angles θ2, and angle change amounts θ1−θ2, which were obtained by the press forming analysis by changing the side wall height and the springback analysis. The angle θ1 is the angle between the side wall portion 5 and the flange portion 7 at the bottom dead center of forming. The angle θ2 is the angle between the side wall portion 5 and the flange portion 7 after die release. Table 1 illustrates the results when the radius of curvature (camber convex R) of the curve of the press-formed product 1 in the height direction was 1000 mm. Table 2 illustrates the results when the convex camber R of the press-formed product 1 was 500 mm.

TABLE-US-00001 TABLE 1 Second forming process Angle First forming process Bottom dead After change Side wall center of die amount height Flange forming release θ1 − h1 (mm) angle (°) θ1 (°) θ2 (°) θ2 (°) Conventional — 95.0 91.4 3.6 Example 1 Comparative 30 0 95.0 91.2 3.8 Example 1 Comparative 24 0 95.0 91.1 3.9 Example 2 Comparative 26 0 95.0 90.4 4.6 Example 3 Comparative 28 0 95.0 89.3 5.7 Example 4 Example 1 31 0 95.0 91.9 3.1 Example 2 32 0 95.0 92.3 2.7 Example 3 33 0 95.0 91.7 3.3 Comparative 34 0 95.0 89.2 5.8 Example 5 Comparative 36 0 95.0 87.2 7.8 Example 6

TABLE-US-00002 TABLE 2 Second forming process Angle First forming process Bottom dead After change Side wall center of die amount height Flange forming release θ1 − h1 (mm) angle (°) θ1 (°) θ2 (°) θ2 (°) Conventional — 95.0 91.1 3.9 Example 2 Comparative 30 0 95.0 91.1 3.9 Example 11 Comparative 24 0 95.0 89.0 6.0 Example 12 Comparative 26 0 95.0 89.6 5.4 Example 13 Comparative 28 0 95.0 90.6 4.4 Example 14 Example 11 31 0 95.0 91.6 3.4 Example 12 32 0 95.0 92.0 3.0 Example 13 33 0 95.0 91.2 3.8 Comparative 34 0 95.0 89.7 5.3 Example 15 Comparative 36 0 95.0 88.4 6.6 Example 16

[0080] In Tables 1 and 2, conventional examples 1 and 2 are examples in each of which the side wall portion 5 was formed at the side wall height h2 of the target shape in a single process by the conventional press forming analysis method.

[0081] Comparative examples 1 and 11 are examples in each of which the side wall height h1 of the side wall portion 5 formed by the first forming process was equal to the side wall height h2 of the target shape. The angle change amounts θ1−θ2 after the second forming process were about the same as those or were increased more than those of conventional results 1 and 2.

[0082] Comparative examples 2 to 4 and comparative examples 12 to 14 are examples in each of which the side wall height h1 of the side wall portion 5 formed by the first forming process was smaller than the side wall height h2 (=30 mm) of the target shape (h1<h2). The angle change amounts θ1−θ2 after the second forming process were larger than that of conventional example 1 or 2. The results show that springback was increased.

[0083] Examples 1 to 3 and examples 11 to 13 are examples in each of which the side wall height h1 of the side wall portion 5 formed by the first forming process was set to be larger than the side wall height h2 (=30 mm) of the target shape by addition of a value half or less of the radius of curvature (=6.2 mm) of the flange side ridge 11 in the longitudinal direction vertical cross section of the target shape. The angle change amounts θ1−θ2 after the second forming process were smaller than those of conventional examples. The results show that springback was suppressed.

[0084] Comparative examples 5 and 6 and comparative examples 15 and 16 are examples in each of which the side wall height h1 of the side wall portion 5 formed by the first forming process was set to be larger than the side wall height h2 of the target shape by addition of a value exceeding half of the radius of curvature of the flange side ridge 11 in the longitudinal direction vertical cross section of the target shape. The angle change amounts θ1−θ2 after the second forming process were larger than that of conventional example 1 or 2. The results show springback was increased.

[0085] The results described above indicated that a change in angle between the side wall portion 5 and the flange portion 7 caused by springback was able to be reduced by forming the press-formed product 1 curved in a convex manner in the height direction by two processes, i.e., the first forming process and the second forming process with a condition that the side wall height h1 of the side wall portion 5 is set to be larger than the side wall height h2 of the target shape in the first forming process by addition of a value half or less of the radius of curvature of the flange side ridge 11 in the longitudinal direction vertical cross section of the target shape.

[0086] Another example was also examined where a press-formed product curved in a concave manner in the height direction was formed by the press forming method according to the invention.

[0087] In the same manner as the press-formed product 1 curved in a convex manner described above, the press forming analysis was performed on the press-formed product 21 illustrated in FIG. 10 as an analysis object, and the springback analysis was performed using the press forming analysis result. On the basis of the springback analysis result, the springback in the flange portion 27 of the press-formed product 21 was evaluated.

[0088] In the press forming analysis, a 980 MPa grade steel sheet having a thickness of 1.2 mm was used for a blank. FIGS. 9 and 10 illustrate a target shape of the press-formed product 21 serving as the forming object. The target shape of the press-formed product 21 is specified as follows. As illustrated in FIG. 9, the radius of curvature (camber concave R in FIG. 9) of the curve having a concave manner in the height direction is 1000 mm or 500 mm. As illustrated in FIG. 10(b), the side wall height of the side wall portion 25 is 30 mm, the angle made between the top portion 23 and the side wall portion 25 is 95°, the angle made between the side wall portion 25 and the flange portion 27 is 95°, and the top portion 23 and the flange portion 27 are in parallel (the flange portion 27 is horizontal). The radius of curvature of the top side ridge 29 in the longitudinal direction vertical cross section (A-A′ arrow cross section in FIG. 10(a)) of the target shape is 5 mm. The radius of curvature of the flange side ridge 31 in the longitudinal direction vertical cross section (A-A′ arrow cross section in FIG. 10(a)) of the target shape is 6.2 mm.

[0089] The press forming analysis was performed on the process of forming the press-formed product 21 by two processes, i.e., the first forming process to perform forming by changing the side wall height h1 of the side wall portion 25 and the second forming process to reform the flange side ridge 31 in such a manner to have the side wall height h2 of the target shape. In the springback analysis, springback behavior of the press-formed product 21 after die release was analyzed, and an amount of change in angle between the side wall portion 25 and the flange portion 27 before die release and after die release was obtained as the springback amount.

[0090] The press-formed product 21 curved in a concave manner formed by the press forming method according to the invention was denoted as the example. As for comparison, the press-formed product 21 formed in a single process was denoted as the conventional example, and the press-formed product 21 that was formed by two processes, i.e., the first forming process and the second forming process, and was formed by the first forming process such that the side wall height h1 of the side wall portion 25 was out of the range of the invention was denoted as the comparative example.

[0091] Tables 3 and 4 illustrate the side wall heights h1 of the side wall portions 25 formed by the first forming process, angles θ1, angles θ2, and angle change amounts θ1−θ2, which were obtained by the press forming analysis by changing the side wall height and the springback analysis. The angle θ1 is the angle between the side wall portion 25 and the flange portion 27 at the bottom dead center of forming. The angle θ2 is the angle between the side wall portion 25 and the flange portion 27 after die release. Table 3 illustrates the results when the radius of curvature (camber concave R) of the curve of the press-formed product 21 in the height direction was 1000 mm. Table 4 illustrates the results when the camber concave R of the press-formed product 21 was 500 mm.

TABLE-US-00003 TABLE 3 Second forming process Angle First forming process Bottom dead After change Side wall center of die amount height Flange forming release θ1 − h1 (mm) angle (°) θ1 (°) θ2 (°) θ2 (°) Conventional — 95.0 91.7 3.3 Example 3 Comparative 30 0 95.0 91.7 3.3 Example 21 Comparative 24 0 95.0 91.2 3.8 Example 22 Comparative 26 0 95.0 90.8 4.2 Example 23 Comparative 28 0 95.0 88.9 6.1 Example 24 Example 21 31 0 95.0 93.2 1.8 Example 22 32 0 95.0 94.0 1.0 Example 23 33 0 95.0 93.0 2.0 Comparative 34 0 95.0 90.9 4.1 Example 25 Comparative 36 0 95.0 87.4 7.6 Example 26

TABLE-US-00004 TABLE 4 Second forming process Angle First forming process Bottom dead After change Side wall center of die amount height Flange forming release θ1 − h1 (mm) angle (°) θ1 (°) θ2 (°) θ2 (°) Conventional — 95.0 92.2 2.8 Example 4 Comparative 30 0 95.0 91.8 3.2 Example 31 Comparative 24 0 95.0 91.5 3.5 Example 32 Comparative 26 0 95.0 91.3 3.7 Example 33 Comparative 28 0 95.0 90.1 4.9 Example 34 Example 31 31 0 95.0 92.5 2.5 Example 32 32 0 95.0 94.7 0.3 Example 33 33 0 95.0 93.4 1.6 Comparative 34 0 95.0 92.0 3.0 Example 35 Comparative 36 0 95.0 87.8 7.2 Example 36

[0092] In Tables 3 and 4, conventional examples 3 and 4 are examples in each of which the side wall height h2 of the target shape was formed in a single process by the conventional press forming analysis method.

[0093] Comparative examples 21 and 31 are examples in each of which the side wall height h1 of the side wall portion 25 formed by the first forming process was equal to the side wall height h2 of the target shape. The angle change amounts θ1−θ2 after the second forming process were about the same as those or were increased more than those of conventional results 3 and 4.

[0094] Comparative examples 22 to 24 and comparative examples 32 to 34 are examples in each of which the side wall height h1 of the side wall portion 25 formed by the first forming process was smaller than the side wall height h2 (=30 mm) of the target shape (h1<h2). The angle change amounts θ1−θ2 after the second forming process were larger than that of conventional example 3 or 4. The results show that springback was increased.

[0095] Examples 21 to 23 and examples 31 to 33 are examples in each of which the side wall height h1 of the side wall portion 25 formed by the first forming process was set to be larger than the side wall height h2 (=30 mm) of the target shape by addition of a value half or less of the radius of curvature (=6.2 mm) of the flange side ridge 31 in the longitudinal direction vertical cross section of the target shape. The angle change amounts θ1−θ2 after the second forming process were smaller than that of conventional example 3 or 4. The results show that springback was suppressed.

[0096] Comparative examples 25 and 26 and comparative examples 35 and 36 are examples in each of which the side wall height h1 of the side wall portion 25 formed by the first forming process was set to be larger than the side wall height h2 of the target shape by addition of a value exceeding half of the radius of curvature of the flange side ridge 31 in the longitudinal direction vertical cross section of the target shape. The angle change amounts θ1−θ2 after the second forming process were larger than that of conventional example 3 or 4. The results show that springback was increased.

[0097] The results described above indicated that a change in angle between the side wall portion 25 and the flange portion 27 caused by springback after die release was able to be reduced by forming the press-formed product 21 curved in a concave manner in the height direction by two processes, i.e., the first forming process and the second forming process with a condition that the side wall height h1 of the side wall portion 25 is set to be larger than the side wall height h2 of the target shape in the first forming process by addition of a value half or less of the radius of curvature of the flange side ridge 31 in the longitudinal direction vertical cross section of the target shape.

INDUSTRIAL APPLICABILITY

[0098] The present invention can provide a press forming method that forms a press-formed product having a top portion, a side wall portion and a flange portion, the flange portion being configured to curve at least in a convex or concave manner in a height direction, while suppressing springback.

REFERENCE SIGNS LIST

[0099] 1 press-formed product (curved in a convex manner) [0100] 3 top portion [0101] 5 side wall portion [0102] 7 flange portion [0103] 9 top side ridge [0104] 11 flange side ridge [0105] 21 press-formed product (curved in a concave manner) [0106] 23 top portion [0107] 25 side wall portion [0108] 27 flange portion [0109] 29 top side ridge [0110] 31 flange side ridge [0111] 41 blank [0112] 51 upper tool [0113] 53 lower tool [0114] 55 pad [0115] 61 upper tool [0116] 63 lower tool [0117] 65 pad [0118] h1 side wall height (bottom dead center in a first forming process) [0119] h2 side wall height (target shape)