WATER-REPELLENT KNITTED FABRIC, METHOD FOR PRODUCING WATER-REPELLENT KNITTED FABRIC, CLOTHING MADE OF WATER-REPELLENT KNITTED FABRIC, AND LAYERING INCLUDING CLOTHING

Abstract

A water-repellent knitted fabric is a knitted fabric which comprises a multifilament made of a thermoplastic resin and has a water repellent imparted to a surface of the knitted fabric or the multifilament, and satisfies the following conditions (1) to (4): (1) the number of voids between stitches of the knitted fabric is 20 to 40/[12 cm×12 cm], and the voids have a size of 7 to 25 mm.sup.2; (2) initial water repellency measured in accordance with a spray method described in JIS L-1092 is at a grade 3 or higher; (3) initial Water drainage is 70% or more; and (4) initial Bursting Strength measured in accordance with a method A described in JIS L-1096 is 200 kPa or more and 500 kPa or less.

Claims

1. A water-repellent knitted fabric that is a knitted fabric which comprises a multifilament made of a thermoplastic resin and has a water repellent imparted to a surface of the knitted fabric, and satisfies the following conditions (1) to (4): (1) the number of voids between stitches of the knitted fabric is 20 to 40/[12 cm×12 cm], and the voids have a size of 7 mm.sup.2 to 25 mm.sup.2; (2) initial water repellency measured in accordance with a spray method described in JIS L-1092 is at a grade 3 or higher; (3) initial Water drainage is 70% or more; and (4) initial Bursting Strength measured in accordance with a method A described in JIS L-1096 is 200 kPa or more and 500 kPa or less.

2. The water-repellent knitted fabric according to claim 1, wherein the multifilament comprises a plurality of single fibers having different cross-sectional shapes, and each cross-sectional shape comprises one or more projections in an outer periphery in a cross-section taken in a vertical direction to a lengthwise direction of the single fiber.

3. The water-repellent knitted fabric according to claim 1, satisfying the following condition (5): (5) an initial flexural rigidity B value is 0.0250 gf.Math.cm.sup.2/cm or less, and a 2HB value is 0.0110 gf.Math.cm/cm or less.

4. The water-repellent knitted fabric according to claim 1, satisfying the following condition (6): (6) water repellency measured in accordance with the spray method after performing home laundering 100 times in accordance with a method 103 described in JIS L-0217 is at a grade 3 or higher.

5. The water-repellent knitted fabric according to claim 1, wherein the water repellent is one, two or more selected from a fluorine-based water repellent having a perfluoroalkyl group having 6 or less carbon atoms, a silicone-based water repellent, and a hydrocarbon-based water repellent.

6. The water-repellent knitted fabric according to claim 1, wherein the water-repellent knitted fabric is formed by a mesh structure.

7. A method for producing the water-repellent knitted fabric according to claim 1, comprising: subjecting the knitted fabric comprising a multifilament made of a thermoplastic resin, having a number of voids of 20 to 40/[12 cm×12 cm] between stitches, and having a size of the voids of 7 to 25 mm.sup.2, to water absorption processing with a water absorbent, followed by water repellent processing with a water repellent.

8. Clothing to be in direct contact with the skin, made of the water-repellent knitted fabric according to claim 1.

9. Layering comprising the clothing according to claim 8, and at least one upper clothing to be directly layered on the clothing.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0109] FIG. 1A is a diagram illustrating examples of a cross-sectional shape of a single fiber included in a multifilament.

[0110] FIG. 1B is a diagram illustrating other examples of the cross-sectional shape of the single fiber included in the multifilament.

[0111] FIG. 1C is a diagram illustrating other examples of the cross-sectional shape of the single fiber included in the multifilament.

[0112] FIG. 1D is a diagram illustrating still other examples of the cross-sectional shape of the single fiber included in the multifilament.

[0113] FIG. 2A is a flowchart illustrating an example of a production method.

[0114] FIG. 2B is a flowchart illustrating another example of the production method.

[0115] FIG. 3A is a diagram illustrating steps of examples and comparative examples.

[0116] FIG. 3B is a diagram illustrating evaluation results of the examples and the comparative examples.

[0117] FIG. 3C is a diagram illustrating evaluation results of the examples and the comparative examples.

[0118] FIG. 3D is a diagram illustrating evaluation results of the examples and the comparative examples.

[0119] FIG. 3E is a diagram illustrating evaluation results of the examples and the comparative examples.

DESCRIPTION OF EMBODIMENTS

Embodiment 1

[0120] Now, a preferred embodiment of the present invention will be described with reference to the accompanying drawings, and it is noted that the present invention is not limited to the embodiment.

[0121] FIGS. 1A, 1B, 1C and 1D illustrate examples of a cross-sectional shape of a single fiber included in a multifilament.

[0122] The cross-sectional shape of the single fiber included in the multifilament is not especially limited, and any of those illustrated in FIGS. 1A, 1B, 1C and 1D can be employed.

[0123] FIG. 1A illustrates an example of a circular cross-section. FIG. 1A(i) illustrates a circular cross-section, FIG. 1A(ii) illustrates an elliptical cross-section, FIG. 1A(iii) illustrates a rounded rectangular cross-section, FIG. 1A(iv) illustrates a cross-section in the shape of continuous three balls, and FIG. 1A(v) illustrates a cross-section in the shape of continuous four balls.

[0124] The single fiber included in the multifilament preferably has two or more different cross-sectional shapes, and has one or more projections in an outer periphery in a cross-section taken in the vertical direction to the lengthwise direction of the single fiber. When a synthetic fiber having two or more different cross-sectional shapes, and having one or more projections in the outer periphery is used, fine gaps can be formed between fibers, and thus further excellent Water drainage is attained.

[0125] FIGS. 1B, 1C and 1D illustrate examples of a modified cross-sectional shape having one or more projections in the outer periphery.

[0126] FIGS. 1B(i), 1B(ii) and 1B(iv) illustrate examples having one projection in the outer periphery. FIGS. 1C(i), 1C(ii) and 1C(iii) respectively illustrate, as examples having one or more projections in the outer periphery, a cross-shaped cross-section, a star-shaped cross-section, and a triangle-shaped cross-section. FIG. 1B(iii) illustrates an example having two projections in the outer periphery.

[0127] FIG. 1D illustrates, as one of multi-leaf cross-sectional shapes, a six-leaf cross-sectional shape in which six projections (leaves) are substantially uniformly repeatedly disposed. In the drawing, R denotes a maximum distance between two opposing projections, and r denotes a diameter of a circular cross-section. In the multi-leaf cross-sectional shape, the number of projections (leaves) is not limited to six, but may be fewer or more (for example, twenty).

[0128] The cross-sectional shape having one or more projections in the outer periphery may include a shape having an oblateness of 1.1 to 5. This oblateness is a value obtained as follows: Oblatenesses are obtained, in accordance with the following expression, for all constituent filaments of a fiber to be measured, and an average of the oblatenesses is calculated.

Oblateness=(length in the long axis direction of the cross-section of the fiber)/(length in the short axis direction of the cross-section of the fiber)

[0129] In the present invention, when the multifilament is constructed by employing a modified cross-section, or by combining two or more single fibers respectively having different cross-sectional shapes, fine gaps can be formed between fibers, and thus further excellent Water drainage is obtained.

[0130] A water-repellent knitted fabric of the present embodiment is a knitted fabric which comprises a multifilament made of a thermoplastic resin and has a water repellent imparted to the knitted fabric or the multifilament.

[0131] <Water Repellent>

[0132] The water repellent may be one or more selected from a fluorine-based water repellent having a perfluoroalkyl group having 6 or less carbon atoms, a silicone-based water repellent, and a hydrocarbon-based water repellent.

[0133] It is preferable that the water repellent is caused to adhere homogeneously or substantially homogeneously onto a first main surface, a second main surface, and an inside portion in the thickness direction of the knitted fabric.

[0134] An amount of the water repellent adhered is, for example, 1.1 g/m.sup.2 to 6.0 g/m.sup.2, preferably 1.2 g/m.sup.2 to 5.0 g/m.sup.2, and more preferably 1.3 g/m.sup.2 to 4.5 g/m.sup.2. When the amount of the water repellent adhered is less than 1.1 g/m.sup.2, the laundering durability may be deteriorated in some cases, and when it exceeds 6.0 g/m.sup.2, the texture may be deteriorated in some cases.

[0135] The amount of the water repellent adhered is obtained in accordance with the following expression:

Amount of water repellent adhered (g/m.sup.2)=weight (g/m.sup.2)×wet-pick-up rate (%)×concentration (%) of water repellent×solid content concentration (%) in water repellent

[0136] A wet-pick-up rate refers to a rate of a mass of a water-repellent processing liquid adhering to the knitted fabric to a mass of a knitted fabric before the immersion obtained after immersing the knitted fabric not subjected to water-repellent processing in the water-repellent processing liquid and squeezing the resultant knitted fabric, and is calculated in accordance with the following expression. It is noted that the masses are in the unit of gram.

Wet-pick-up rate (%)={(mass of fabric after immersion and squeeze−initial mass of fabric)/initial mass of fabric}×100

[0137] The water-repellent knitted fabric of the present embodiment needs to satisfy the conditions (1) to (4) described below, and preferably further satisfies one or more of the other conditions (5) to (10).

[0138] (1) The number of voids between stitches of the knitted fabric is 20 to 40/[12 cm×12 cm], and the voids have a size of 7 mm.sup.2 to 25 mm.sup.2, and preferably the number of voids is 28 to 35/[12 cm×12 cm] and the size of the voids is 7.5 mm.sup.2 to 23 mm.sup.2.

[0139] (2) Initial water repellency is at a grade 3 or higher, and preferably at a grade 4 or higher.

[0140] (3) Initial Water drainage or Water drainage obtained after 100 times of home laundering is 70% or more, and preferably 73% or more, more preferably 75% or more, and further preferably 80% or more.

[0141] (4) Initial Bursting Strength or Bursting Strength obtained after 100 times of home laundering is 200 kPa or more and 500 kPa or less, preferably 250 kPa or more and 500 kPa or less, and more preferably 280 kPa or more and 480 kPa or less.

[0142] (5) An initial flexural rigidity B value is 0.0250 gf.Math.cm.sup.2/cm or less, and a 2HB value is 0.0110 gf.Math.cm/cm or less. Preferably, the flexural rigidity B value and the 2HB value obtained after 120 times of home laundering are respectively 0.0150 gf.Math.cm.sup.2/cm or less and 0.0200 gf.Math.cm/cm or less.

[0143] (6) Water repellency measured after performing home laundering 100 times is at the grade 3 or higher, it is preferable that the water repellency measured after performing home laundering 120 times is at the grade 3 or higher, and it is more preferable that the water repellency measured after performing home laundering 150 times is at the grade 3 or higher.

[0144] (7) A rate of change between the initial flexural rigidity value B and the flexural rigidity value B measured after performing home laundering 120 times is −75% or more, and preferably −72% or more, and a rate of change between the initial 2HB value and the 2HB value measured after performing home laundering 120 times is 75% or less.

[0145] (8) The average friction coefficient (MIU) is 0.220 or less and friction coefficient variation (MMD) is 0.0250 or less in initial surface characteristics, and the average friction coefficient (MIU) is 0.230 or less and the friction coefficient variation (MMD) is 0.0270 or less after performing home laundering 120 times.

[0146] (9) A rate of change between the initial average friction coefficient (MIU) and the average friction coefficient (MIU) measured after performing home laundering 120 times is 6.0% or less, and a rate of change between the initial friction coefficient variation (MMD) and the friction coefficient variation (MMD) measured after performing home laundering 120 times is 12.0% or less.

[0147] (10) A sample of the knitted fabric cut into a 20 cm square is placed on the inside of the forearm, and rubbed against the skin with the sample lightly held with the palm of the other arm. “Soft and gentle feel (gentle texture)” and “feel that is not rough but smooth and difficult to cling to the skin (smooth texture)” felt in this operation are subjected to sensory evaluation. Ten panelists (females in their 20s to 40s) perform the sensory evaluation by touching, and the average of scores among the ten panelists rated based on the following criteria was obtained: Good texture: 4; average: 2; and poor: 0. In the evaluation of either item, an average score of 3.0 or more can be determined as good texture.

[0148] The respective measurement methods have been already described.

[0149] When the initial flexural rigidity value B exceeds 0.0250 gf.Math.cm.sup.2/cm, the knitted fabric is hard, and hence the texture (bounce, swell, and tension) felt when worn may become poor in some cases. Although the flexural rigidity value B is reduced through home laundering, the rate of change is preferably retained at −70% or more in the present embodiment, and thus, extreme reduction of the texture otherwise caused by home laundering can be suppressed.

[0150] When the initial bending hysteresis width (2HB value) exceeds 0.0110 gf.Math.cm/cm, restorability is degraded, and hence the texture (bounce, swell, and tension) felt when worn may become poor in some cases. Although the 2HB value is increased through home laundering, the rate of change is preferably retained at 75% or less in the present embodiment, and thus, extreme reduction of the texture otherwise caused by home laundering can be suppressed.

[0151] When the initial average friction coefficient (MIU) is 0.220 or less, the knitted fabric is evaluated to be low in “non-slipperiness” (namely, to be slippery). Although the average friction coefficient (MIU) is increased (namely, the knitted fabric becomes less slippery) through home laundering, the rate of change is preferably retained at 6.0% or less in the present embodiment, and thus, extreme reduction of the texture otherwise caused by home laundering can be suppressed.

[0152] When the friction coefficient variation (MMD) is 0.0250 or less, the knitted fabric is evaluated to be low in “roughness”, namely, to be smooth. Although the friction coefficient variation (MMD) is increased (namely, roughness is increased) through home laundering, the rate of change is preferably retained at 12.0% or less in the present embodiment, and thus, extreme reduction of the texture otherwise caused by home laundering can be suppressed.

[0153] <Knitted Structure>

[0154] Examples of a knitted structure of the water-repellent knitted fabric include waffle, plain, smooth, circular rib, lace, mesh, blister, reversible structure, tricot, raschel, jacquard, a single knitted fabric, a double knitted fabric, a round knitted fabric, a flat knitted fabric, and a warp knitted fabric. Among these, a mesh structure is preferred from the viewpoint of excellent balance among the water repellency, the Water drainage, the Bursting Strength, and the texture.

[0155] <Knitting Density>

[0156] A knitting density of the water-repellent knitted fabric is, for example, in terms of the number of courses (C) in one inch, 20 to 60, and preferably 30 to 40, and in terms of the number of wales (W) in one inch, 15 to 50, and preferably 20 to 30. A combination of courses/inch (C) and wales/inch (W) is preferably a combination of the above-described ranges, and is preferably, for example, 32 (C)/23 (W), 32 (C)/25 (W), 35 (C)/25 (W), or the like.

[0157] <Weight of Knitted Fabric>

[0158] A weight of the water-repellent knitted fabric is, for example, 40 g/m.sup.2 to 200 g/m.sup.2, and preferably 45 g/m.sup.2 to 110 g/m.sup.2.

[0159] <Thickness of Knitted Fabric>

[0160] A thickness of the water-repellent knitted fabric is, for example, 200 μm to 1500 μm, and preferably 300 μm to 1000 μm. The thickness of the water-repellent knitted fabric is measured in accordance with a method A described in JIS L1096, 8.4 Thickness.

[0161] <Multifilament>

[0162] The multifilament made of a thermoplastic resin can be one made of, for example, a polyester-based fiber, a polyamide-based fiber or a polyolefin-based fiber.

[0163] Examples of a polyester resin composing the polyester-based fiber include aromatic polyesters such as polyethylene terephthalate, polybutylene terephthalate, and polytrimethylene terephthalate, cation-dyeable polyesters, and polylactic acids. The polyester-based fiber is preferred because of wrinkle resistance and excellent strength.

[0164] Examples of a polyamide resin composing the polyamide-based fiber include nylon 6, nylon 66, nylon 46, nylon 11, and nylon 56. The polyamide-based fiber is excellent in strength and further in water absorption, and hence can be expected to improve the Water drainage.

[0165] Examples of a polyolefin resin composing the polyolefin-based fiber include polypropylene, and polyethylene.

[0166] The multifilament made of a thermoplastic resin has a single-fiber fineness of, for example, 0.1 dtex to 10 dtex, preferably 0.3 dtex to 8 dtex, and more preferably 0.5 dtex to 6 dtex.

[0167] The multifilament made of a thermoplastic resin has a total fineness of, for example, 30 dtex to 300 dtex, preferably 30 dtex to 250 dtex, and more preferably 30 dtex to 180 dtex.

[0168] The number of filaments of the multifilament made of a thermoplastic resin is determined in accordance with the single-fiber fineness and the total fineness of a single fiber to be used, and is, for example, 2 to 400.

[0169] The multifilament includes, for example, a combined filament yarn combined with another fiber, a twisted yarn twisted with another fiber, or a false-twisted yarn.

[0170] Another fiber can be, for example, a synthetic fiber such as acrylic and polyurethane, a recycled fiber such as rayon, a semi-synthetic fiber such as acetate, and a natural fiber such as cotton and wool.

[0171] <Production Method>

[0172] A first method for producing a water-repellent knitted fabric comprises the steps of subjecting a knitted fabric comprising a multifilament made of a thermoplastic resin, having a number of voids of 20 to 40/[12 cm×12 cm] between stitches, and having a size of the voids of 7 mm.sup.2 to 25 mm.sup.2 to scouring processing, dyeing and water absorption processing (including drying), water repellent processing, and a post-treatment. In this production method, the dyeing processing may be performed simultaneously with the water absorption processing (see FIG. 2A). The post-treatment is omitted in some cases.

[0173] A second method for producing a water-repellent knitted fabric comprises the steps of subjecting a multifilament to scouring processing, dyeing and water absorption processing (including drying), water repellent processing, and a post-treatment, followed by a step of knitting processing (see FIG. 2B). The post-treatment is omitted in some cases.

[0174] Since the water repellent processing is performed in the form of a yarn, an effect to cause a water repellent to adhere to the fiber is further improved as compared with a case where it is performed in the form of a knitted fabric. Besides, the method can be employed for producing a product, such as socks, gloves, or an undergarment, employing a production method of directly knitting from a yarn.

[0175] The first method or the second method can be selected in accordance with the type and the fineness of a single fiber, the cross-sectional shape of the single fiber, the type of a knitted structure, and the like.

[0176] The water repellent processing of a multifilament is a step of causing a water repellent to adhere to the multifilament having been subjected to the water absorption processing. The water repellent processing is performed, for example, by a method in which the multifilament is continuously reeled out and conveyed from a bobbin (or a cone) where the multifilament is wound and is immersed in a water repellent bath or the like for a prescribed period of time for causing a water repellent to adhere thereon (bath conveyance), or by a method in which a hank of or a bobbin of the multifilament is immersed in a water repellent bath or the like for a prescribed period of time for causing a water repellent to adhere thereon. The water repellent processing may include a prescribed dehydrating or drying treatment.

[0177] The water repellent to be used in the water repellent processing of the multifilament is not especially limited as long as water repellency can be exhibited, and in consideration of environmental influences, the water repellant may be one or more selected from a fluorine-based water repellent having a perfluoroalkyl group having 6 or less carbon atoms, a silicone-based water repellent, and a hydrocarbon-based water repellent. It is noted that an auxiliary agent such as a crosslinking agent, a softener, an antistatic agent, or a catalyst may be used in addition to the water repellent.

[0178] An amount of the water repellent adhered on the multifilament is, for example, 1.1 g/m.sup.2 to 6.0 g/m.sup.2, preferably 1.2 g/m.sup.2 to 5.0 g/m.sup.2, and more preferably 1.3 g/m.sup.2 to 4.5 g/m.sup.2. When the amount of the water repellent adhered is less than 1.1 g/m.sup.2, the laundering durability may be deteriorated in some cases, and when it exceeds 6.0 g/m.sup.2, the texture may be deteriorated in some cases.

[0179] When the water repellent processing is performed in the latter step, the amount adhered may be smaller than that described above, so as to make adjustment for ultimately attaining the above-described amount adhered.

[0180] The knitting processing is a step of knitting the multifilament into a prescribed knitted structure. Through this step, a knitted fabric comprising the multifilament made of a thermoplastic resin, having a number of voids of 20 to 40/[12 cm×12 cm] between stitches, and having a size of the voids of 7 mm.sup.2 to 25 mm.sup.2 is obtained. A knitting machine to be used for the knitting processing is, for example, a circular knitting machine, a weft knitting machine, or a warp knitting machine.

[0181] The scouring processing is a step of removing, from the knitted fabric or the multifilament, impurities such as dirt, an oil, or a starch by using, for example, a bleach, a detergent or the like. It is noted that an auxiliary agent such as a chelating agent or a penetrating agent may be used.

[0182] In the production method, alkali weight reduction processing may be performed before the dyeing/water absorption processing. The alkali weight reduction processing is a step of reducing the weight by dissolving (hydrolyzing) a surface of the knitted fabric or the multifilament with a strong alkaline solution such as caustic soda. The extent of the weight reduction is preferably determined in consideration of both the texture and the laundering durability of the water repellent. It is noted that an auxiliary agent such as a weight reduction processing accelerator may be used.

[0183] The dyeing processing is a step of dyeing the knitted fabric or the multifilament with a dye. In addition to the dye, a chelating agent, a penetration leveling agent, a disperse leveling agent, an auxiliary agent, a penetrating agent or the like may be used. Examples of a dyeing method include a method in which the knitted fabric or the multifilament having a large length is immersed for dyeing in a dyebath or the like for a prescribed period of time during continuous conveyance (such as a one-bath dyeing method, a one-bath multistage dyeing method, or a multiple bath multistage dyeing method), and a batch dyeing method such as a thermosol dyeing method, a cold pad batch method, a high pressure jet dyeing method, a high pressure beam dyeing method, a pad steam method, a pad dyeing method, or a rapid dyeing method. After performing the dyeing for a prescribed period of time, the knitted fabric or the multifilament is washed, dehydrated, and dried.

[0184] In the present production method, when the dyeing and the water absorption are simultaneously performed, a bath liquid of the dyebath may contain at least a dye and a water absorbent.

[0185] Soaping may be performed after the dyeing processing, or soaping may be performed after the water repellent processing.

[0186] The water absorbent (also designated as a water absorption processing agent) is an additive for imparting hydrophilicity to a fiber and improving affinity with water. The type of the water absorbent used in the present invention is not especially limited, and examples include polyethylene glycol, a polyethylene oxide-based compound such as a polyethylene oxide-addition polyester-based compound (such as a block copolymer of polyethylene glycol and polyethylene terephthalate), a polyethylene oxide-addition fluorine-based compound, or a polyethylene oxide-addition silicone-based compound, and dialkyl sulfosuccinate such as sodium dioleyl sulfosuccinate. One of these water absorbents may be singly used, or two or more of these may be used in combination. Among these water absorbents, a polyethylene oxide-based compound is preferred, and a polyethylene oxide-addition polyester-based compound is further preferred.

[0187] Besides, in addition to the water absorbent, a crosslinking agent, a softener, an antistatic agent, an auxiliary agent, or the like may be used.

[0188] As a role of the water absorbent in the present production method, it is used not in expectation of a water absorption function against sweat and the like when worn but in expectation of improvement of adhesion strength of the water repellent through the water repellent processing performed in the latter stage. In comparison between a case where the water repellent processing is performed using an equivalent amount of the water repellent and the present production method (in which the water repellent processing is performed after the water absorption processing) (see Example 1 and Example 9), even when an equivalent amount of the water repellent is adsorbed onto the knitted fabric or the multifilament, adhesion force of the water repellent is higher in the present production method, and therefore, the laundering durability is further increased.

[0189] The water repellent processing of the knitted fabric is a step of causing the water repellent to adhere to the knitted fabric having been subjected to the water absorption processing. The water repellent processing may be performed by, for example, a method in which the knitted fabric having a large length is immersed in a water repellent bath or the like for a prescribed period of time during continuous conveyance to cause the water repellent to adhere thereto (bath conveyance), padding, or printing (rolling). The water repellent processing may include a prescribed dehydrating/drying treatment.

[0190] The water repellent is not especially limited as long as water repellency can be exhibited, and in consideration of environmental influences, the water repellent may be one or more selected from a fluorine-based water repellent having a perfluoroalkyl group having 6 or less carbon atoms, a silicone-based water repellent, and a hydrocarbon-based water repellent. It is noted that an auxiliary agent such as a crosslinking agent, a softener, an antistatic agent, or a catalyst may be used in addition to the water repellent.

[0191] Preferably, the water repellent is homogeneously or substantially homogeneously adhered onto a first main surface, a second main surface, or an inside portion in the thickness direction of the knitted fabric. Besides, the water repellent is preferably adhered homogeneously or substantially homogeneously onto the outer periphery of the multifilament.

[0192] “Impartment” and “adhesion” of the water repellent may be attained by a chemical and/or physical mechanism.

[0193] An amount of the water repellent adhered is, for example, 1.1 g/m.sup.2 to 6.0 g/m.sup.2, preferably 1.2 g/m.sup.2 to 5.0 g/m.sup.2, and more preferably 1.3 g/m.sup.2 to 4.5 g/m.sup.2.

[0194] The post-processing (final set) is finish processing of the knitted fabric or the multifilament, and includes, for example, softening processing, a heat treatment, dimension processing and the like.

Alternative Embodiment

[0195] In the production method described above, the water absorption processing may be performed after the dyeing processing instead of simultaneously with the dyeing processing. In this case, the water absorption processing may be performed, for example, by preparing an aqueous solution containing the water absorbent, imparting the aqueous solution to the knitted fabric by a padding method, a spraying method, a kiss roller coater method, a slit coater method or the like, and then performing a dry heat treatment. The aqueous solution may contain, if necessary, a crosslinking agent, a softener, an antistatic agent, an auxiliary agent, or the like.

[0196] <Layering>

[0197] An underwear is worn directly on the skin. The underwear has water repellency, causes sweat to rapidly permeate, and prevents re-wetness. The underwear is made of the water-repellent knitted fabric having the aforementioned texture, and is made of a water-repellent knitted fabric produced by the above-described method for producing a water-repellent knitted fabric.

[0198] Although sweat successively passes through an underwear to an outerwear (moisture permeability), the underwear prevents re-wetness (caused by sweat or rain) (waterproof performance).

[0199] A first upper wear is worn on the underwear. The first upper wear has a heat retaining property, a sweat absorbing/diffusing property, and a moisture controlling property, and absorbs sweat coming from the underwear to diffuse it. The first upper wear is made of a fabric of, for example, a chemical fiber of polyester, nylon, acetate, rayon or the like, a natural fiber of wool, silk, cotton or the like, or a blend of any of these.

[0200] A second upper wear is worn on the first upper wear. The second upper wear has a heat retaining property, a sweat absorbing/diffusing property, and a transpiring property to evaporate sweat. The second upper wear is made of a fabric of, for example, a chemical fiber of polyester, nylon, acetate, rayon or the like, a natural fiber of wool, silk, cotton or the like, or a blend of any of these.

[0201] A third upper wear is worn on the second upper wear. The third upper wear has a windproof property, a heat retaining property, and a waterproof breathable property to cause the evaporated sweat to permeate (pass) to the outside. The third upper wear has, for example, a three-layer structure of nylon or polyester, a fluorine film or a polyurethane film, and nylon or polyester.

[0202] An outerwear is worn on the third upper wear. The outerwear has a cold proof property, a wind proof property, a waterproof breathable property, and rain-fastness to cause the evaporated sweat to permeate (pass) to the outside. The outerwear has, for example, a three layer structure of stretchable nylon or polyester, a fluorine film or a polyurethane film, and nylon or polyester.

[0203] It is noted that these wears are not limited to those having the aforementioned functions, but the functions may be omitted or another function may be added in accordance with intended use.

[0204] <Examples and Comparative Examples of Water-Repellent Knitted Fabric>

[0205] FIG. 3A illustrates steps performed in examples and comparative examples, and FIGS. 3B to 3E illustrate evaluation results of the examples and the comparative examples.

[0206] The term “HL100” shown in a table indicates 100 times of home laundering.

[0207] <Evaluation Methods>

[0208] (1) Size of Void (Hole)

[0209] A knitted fabric obtained in each of the examples and the comparative examples was enlargedly copied at 400% using a copying machine (“C5240F”, manufactured by Canon Inc.), and the size of a void (hole) was obtained based on the thus obtained image.

Size of void (mm.sup.2)=(length of void/2)×(width of void/2)×3.14

[0210] (2) Number of Voids

[0211] A knitted fabric obtained in each of the examples and the comparative examples was enlargedly copied at 400% using a copying machine (“C5240F”, manufactured by Canon Inc.), and the number of voids included in a 12 cm×12 cm square in the thus obtained image was calculated.

[0212] (3) Water Repellency (Laundering Durability)

[0213] (3-1) Initial: Initial water repellency was measured in accordance with a spray method described in JIS L-1092.

[0214] (3-2) HL100: Water repellency of HL100 was measured in accordance with the spray method described in JIS L-1092 after performing home laundering 100 times in accordance with a method 103 described in JIS L-0217.

[0215] (3-3) HL120: Water repellency of HL120 was measured in accordance with the spray method described in JIS L-1092 after performing home laundering 120 times in accordance with the method 103 described in JIS L-0217.

[0216] (3-4) HL150: Water repellency of HL150 was measured in accordance with the spray method described in JIS L-1092 after performing home laundering 150 times in accordance with the method 103 described in JIS L-0217.

[0217] (4) Texture

[0218] (4-1) Bending Characteristics

[0219] Bending characteristic values were measured using Pure Bending Tester (“KES-FB2”, manufactured by Kato Tech Co., Ltd. A bending characteristic value was measured by using a sample (20 cm×1 cm) at a maximum curvature±2.5 cm.sup.−1. A flexural rigidity value B of a bending characteristic refers to flexural rigidity per cm of the width of a fabric, and assuming that a bending moment per cm of the width is M (gf.Math.cm/cm) and a curvature is K (cm.sup.−1), K is represented by average inclination dM/dK (gf.Math.cm.sup.2/cm) between 0.5 cm.sup.−1 and 1.5 cm.sup.−1. A hysteresis width, a 2HB value, of a bending characteristic refers to bending hysteresis (gf.Math.cm/cm) per cm of the width of a fabric.

[0220] (4-2) Average Friction Coefficient (MIU) and Friction Coefficient Variation (MMD)

[0221] An average friction coefficient (MIU) and friction coefficient variation (MMD) were measured using a surface tester (“KES-FB4”, manufactured by Kato Tech Co., Ltd.).

[0222] (4-3) Sensory Evaluation of Texture

[0223] A sample of each knitted fabric cut into a 20 cm square was placed on the inside of the forearm, and rubbed against the skin with the sample lightly held with the palm of the other arm. “Soft and gentle feel (gentle texture)” and “feel that is not rough but smooth and difficult to cling to the skin (smooth texture)” felt in this operation were subjected to sensory evaluation. Ten panelists (females in their 20s to 40s) performed the sensory evaluation by touching to obtain an average of scores of the ten panelists rated based on the following criteria: Good texture: 4; average: 2; poor: 0. In the evaluation of either item, an average score of 3.0 or more was determined as good texture.

[0224] (5) Wet-Pick-Up Rate

[0225] A wet-pick-up rate refers to a rate of a mass of a water-repellent processing liquid adhering to a knitted fabric to a mass of a knitted fabric before the immersion, obtained after immersing the knitted fabric not subjected to water-repellent processing in the water-repellent processing liquid and squeezing the resultant knitted fabric, and is calculated in accordance with the following expression. It is noted that the masses are in the unit of gram.

Wet-pick-up rate (%)={(mass of fabric after immersion and squeeze−initial mass of fabric)/initial mass of fabric}×100

[0226] (6) Amount of Water Repellent Adhered (g/m.sup.2)

Amount of water repellent adhered (g/m.sup.2)=weight (g/m.sup.2)×wet-pick-up rate (%)×concentration (%) of water repellent×solid content concentration (%) in water repellent

[0227] (7) Water Drainage

[0228] On an acrylic plate of a 20 cm square, 0.6 ml of water was dropped, and a water-repellent knitted fabric was overlayed thereon. A knitted fabric (a fabric of “Drought Force” manufactured by finetrack Co., Ltd., polyester 100%, weight: 120 g/m.sup.2) cut into a 20 cm square was overlayed on the water-repellent knitted fabric, and a load of 300 g in total (300 g/400 cm.sup.2) including an acrylic plate of a 20 cm square and an appropriate weight was applied thereto. One minute after, a mass of the knitted fabric (the fabric of Drought Force having absorbed water) was measured to calculate the Water drainage in accordance with the following expression. It is noted that a unit of the mass was gram.

Water drainage (%)=100×(mass of Drought Force having absorbed water−initial mass of Drought Force)/initial amount of water (0.6 ml)

[0229] (8) Bursting Strength

[0230] Bursting Strength was measured in accordance with the method A described in JIS L-1096.

Example 1

[0231] A false-twisted yarn of Lumiace 73T44 (manufactured by UNITIKA TRADING CO., LTD.; 73 dtex, 44 filaments, the number of projections in the outer periphery of the cross-section of a single fiber: 1, oblateness of the cross-section of the fiber: 1.6) of a polyester-based fiber was used to produce a mesh knitted fabric having the following structure.

[0232] Weight: 55 g/m.sup.2

[0233] Knitting density: 32 C/25 W

[0234] Size of void: 20.4 mm.sup.2

[0235] Number of voids: 30

[0236] A water-repellent knitted fabric was obtained by performing scouring, dyeing/water absorption processing (including drying), water repellent processing, and final set (FS) in accordance with the following formulation:

[0237] Scouring: [0238] Scouring detergent (Sunmorl FL (NICCA CHEMICAL CO., LTD.), 1 g/L, 80° C.×20 min

[0239] Dyeing Processing: [0240] Disperse dye (Dianix Black XF (DyStar), 3% omf (on weight of fiber) [0241] Auxiliary agent (Nicca Sun Salt SN-130 (NICCA CHEMICAL CO., LTD.)), 0.5 g/L [0242] Auxiliary agent (acetic acid), 0.2 cc/L [0243] Water absorbent (SR-1000 (TAKAMATSU OIL & FAT CO., LTD.)), 1 g/L [0244] Dyeing temperature: 130° C.×30 min [0245] Drying: 120° C.×2 min

[0246] Water Repellent Processing: [0247] Water repellent (LSE-009 (manufactured by Meisei Chemical Works, Ltd.)), 100 g/L [0248] Isocyanate-based crosslinking agent, Meikanate CS (Meisei Chemical Works, Ltd.), 10 g/L [0249] Melamine-based crosslinking agent, Beckamine M-3 (DIC Corporation), 5 g/L [0250] Amine salt-based catalyst, Catalyst ACX (DIC Corporation), 3 g/L

[0251] Final set: drying: 170° C.×1 min

Evaluation Results of Example 1

[0252] HL150: grade 3

[0253] Rate of change of value B between initial and HL120: −70.4%

[0254] Rate of change of 2HB value: 73.2%

[0255] Rate of change of MIU: 4.9%

[0256] Rate of change of MMD: 10.1%

[0257] Sensory evaluation of texture: 4.0

[0258] Amount of water repellent adhered: 1.7 g/m.sup.2

[0259] Water drainage: 86.2%

[0260] Bursting Strength: 303 kPa

[0261] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 2

[0262] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the weight, the knitting density, the size of a void, and the number of voids were changed as follows.

[0263] Weight: 50 g/m.sup.2

[0264] Knitting density: 32 C/23 W

[0265] Size of void: 17.3 mm.sup.2

[0266] The number of voids: 32

Evaluation Results of Example 2

[0267] HL150: grade 3

[0268] Rate of change of value B between initial and HL120: −53.7%

[0269] Rate of change of 2HB value: 53.2%

[0270] Rate of change of MIU: 4.2%

[0271] Rate of change of MMD: 11.5%

[0272] Sensory evaluation of texture: 3.6

[0273] Amount of water repellent adhered: 1.5 g/m.sup.2

[0274] Water drainage: 85.4%

[0275] Bursting Strength: 307 kPa

[0276] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 3

[0277] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that a false-twisted yarn (78 dtex, 48 filaments) including a polyester filament having single fibers with a triangle cross-section and a polyester filament having single fibers with a cross-shaped cross-section in a mass ratio of 50/50 was used, and that the weight, the knitting density, the size of a void, and the number of voids were changed as follows.

[0278] Weight: 60 g/m.sup.2

[0279] Knitting density: 32 C/23 W

[0280] Size of void: 23.0 mm.sup.2

[0281] Number of voids: 32

Evaluation Results of Example 3

[0282] HL150: grade 3

[0283] Rate of change of value B between initial and HL120: −51.0%

[0284] Rate of change of 2HB value: 43.5%

[0285] Rate of change of MIU: 4.8%

[0286] Rate of change of MMD: 9.4%

[0287] Sensory evaluation of texture: gentleness: 3.4, smoothness: 3.8

[0288] Amount of water repellent adhered: 1.9 g/m.sup.2

[0289] Water drainage: 84.1%

[0290] Bursting Strength: 290 kPa

[0291] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 4

[0292] A knitted fabric having a weight, a knitting density, a size of a void, and the number of voids as described below was obtained by using a false-twisted yarn of a polyester filament having single fibers with a circular cross-section (84 dtex, 72 filaments). The knitted fabric was subjected to scouring, dyeing processing (including drying), water repellent processing, and final set (FS) in accordance with the above-described formulation to obtain a water-repellent knitted fabric. In the dyeing processing, a water absorbent was not used.

[0293] Weight: 75 g/m.sup.2

[0294] Knitting density: 32 C/25 W

[0295] Size of void: 20.4 mm.sup.2

[0296] Number of voids: 30

Evaluation Results of Example 4

[0297] HL120: grade 3

[0298] Rate of change of value B between initial and HL120: −50.0%

[0299] Rate of change of 2HB value: 44.3%

[0300] Rate of change of MIU: 4.3%

[0301] Rate of change of MMD: 5.4%

[0302] Sensory evaluation of texture: 3.4

[0303] Amount of water repellent adhered: 2.2 g/m.sup.2

[0304] Water drainage: 75.4

[0305] Bursting Strength: 270 kPa

[0306] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 5

[0307] A mesh knitted fabric having a weight, a knitting density, a size of a void, and the number of voids as described below was produced by using a false-twisted yarn of Lumiace 73T44 used in Example 1.

[0308] Weight: 55 g/m.sup.2

[0309] Knitting density: 33 C/24 W

[0310] Size of void: 20.4 mm.sup.2

[0311] Number of voids: 31

[0312] A water-repellent knitted fabric was obtained from this knitted fabric under the same conditions as those of Example 1 except that the formulation of the water repellent processing was changed as follows (the amount of the water repellent was doubled), and that the dyeing processing was performed without using a water absorbent.

[0313] Water Repellent Processing: [0314] Water repellent: LSE-009, 200 g/L [0315] Isocyanate-based crosslinking agent: Meikanate CX, 20 g/L [0316] Melamine-based crosslinking agent: Beckamine M-3, 10 g/L [0317] Amine salt-based catalyst: Catalyst ACX, 6 g/L

Evaluation Results of Example 5

[0318] HL120: grade 3

[0319] Rate of change of value B between initial and HL120: −53.4%

[0320] Rate of change of 2HB value: 65.3%

[0321] Rate of change of MIU: 5.0%

[0322] Rate of change of MMD: 9.8%

[0323] Sensory evaluation of texture: gentleness: 3.2, smoothness: 4.0

[0324] Amount of water repellent adhered: 3.5 g/m.sup.2

[0325] Water drainage: 79.0%

[0326] Bursting Strength: 273 kPa

[0327] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 6

[0328] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that a constituent fiber was changed to a false-twisted fiber of Lumiace UV (polyester multifilament having single fibers with a modified cross-section, 84 dtex, 48 filaments, manufactured by UNITIKA TRADING CO., LTD.), and that a mesh structure having a weight, a knitting density, a size of a void, and the number of voids as described below was employed.

[0329] Weight: 75 g/m.sup.2

[0330] Knitting density: 32 C/25 W

[0331] Size of void: 20.4 mm.sup.2

[0332] Number of voids: 30

Evaluation Results of Example 6

[0333] HL150: grade 3

[0334] Rate of change of value B between initial and HL120: −54.8%

[0335] Rate of change of 2HB value: 72.5%

[0336] Rate of change of MIU: 4.7%

[0337] Rate of change of MMD: 10.2%

[0338] Sensory evaluation of texture: gentleness: 3.8, smoothness: 3.2

[0339] Amount of water repellent adhered: 2.4 g/m.sup.2

[0340] Water drainage: 77.2%

[0341] Bursting Strength: 279 kPa

[0342] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 7

[0343] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that a constituent fiber was changed to a blended fiber (92 dtex, 70 filaments) of Lumiace 73T44 and a polyester multifilament having single fibers with a triangle cross-section (19 dtex, 26 filaments), and that a mesh structure having a weight, a knitting density, a size of a void, and the number of voids as described below was employed.

[0344] Weight: 70 g/m.sup.2

[0345] Knitting density: 32 C/23 W

[0346] Size of void: 23.0 mm.sup.2

[0347] Number of voids: 32

Evaluation Results of Example 7

[0348] HL150: grade 3

[0349] Rate of change of value B between initial and HL120: −51.3%

[0350] Rate of change of 2HB value: 64.2%

[0351] Rate of change of MIU: 4.5%

[0352] Rate of change of MMD: 11.8%

[0353] Sensory evaluation of texture: gentleness: 3.4, smoothness: 3.6

[0354] Amount of water repellent adhered: 2.2 g/m.sup.2

[0355] Water drainage: 84.5%

[0356] Bursting Strength: 315 kPa

[0357] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 8

[0358] A mesh knitted fabric having a weight, a knitting density, a size of a void, and the number of voids as described below was obtained by using a blended yarn of a nylon multifilament having single fibers with a circular cross-section (33 dtex, 26 filaments) and a polyurethane monofilament (78 dtex). Then, a water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the dyeing processing was performed without using a water absorbent.

[0359] Weight: 95 g/m.sup.2

[0360] Knitting density: 75 C/52 W

[0361] Size of void: 7.9 mm.sup.2

[0362] Number of voids: 23

Evaluation Results of Example 8

[0363] HL120: grade 3

[0364] Rate of change of value B between initial and HL120: −14.3%

[0365] Rate of change of 2HB value: −9.1%

[0366] Rate of change of MIU: 14.0%

[0367] Rate of change of MMD: 28.5%

[0368] Sensory evaluation of texture: 4.0

[0369] Amount of water repellent adhered: 2.7 g/m.sup.2

[0370] Water drainage: 90%

[0371] Bursting Strength: 203 kPa

[0372] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Example 9

[0373] A knitted fabric having a weight, a knitting density, a size of a pore, and the number of voids as described below was obtained, and a water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the dyeing processing was performed without using a water absorbent.

[0374] Weight: 55 g/m.sup.2

[0375] Knitting density: 33 C/23 W

[0376] Size of void: 15.1 mm.sup.2

[0377] Number of voids: 33

Evaluation Results of Example 9

[0378] HL100: grade 3

[0379] Rate of change of value B between initial and HL120: −49.9%

[0380] Rate of change of 2HB value: 43.7%

[0381] Rate of change of MIU: 5.5%

[0382] Rate of change of MMD: 13.8%

[0383] Sensory evaluation of texture: 3.8

[0384] Amount of water repellent adhered: 1.7 g/m.sup.2

[0385] Water drainage: 75.7%

[0386] Bursting Strength: 292 kPa

[0387] Laundering durability, texture and Water drainage were good, and strength (Bursting Strength) was adequate for wearing.

Comparative Example 1

[0388] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the weight, the knitting density, the size of a void, and the number of the voids of a mesh knitted fabric were changed as follows.

[0389] Weight: 90 g/m.sup.2

[0390] Knitting density: 67 C/19 W

[0391] Size of void: 6.4 mm.sup.2

[0392] Number of voids: 52

Evaluation Results of Comparative Example 1

[0393] HL150: grade 3

[0394] Rate of change of value B between initial and HL120: −41.2%

[0395] Rate of change of 2HB value: 65.7%

[0396] Rate of change of MIU: 1.6%

[0397] Rate of change of MMD: 6.6%

[0398] Sensory evaluation of texture: gentleness: 0.7, smoothness: 2.0

[0399] Amount of water repellent adhered: 2.7 g/m.sup.2

[0400] Water drainage: 64.8%

[0401] Bursting Strength: 323 kPa

[0402] Although the Water drainage was poor because of a small size of the voids, the Bursting Strength was excellent. The initial flexural rigidity B value was 0.0391 gf.Math.cm.sup.2/cm, the 2HB value was as high as 0.0130 gf.Math.cm/cm, and the bounce was strong. Besides, the initial MIU value and MMD value were large, the surface was rough, and the sensory evaluation of the texture was poor.

Comparative Example 2

[0403] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the weight, the knitting density, the size of a void, and the number of the voids of a mesh knitted fabric were changed as follows.

[0404] Weight: 40 g/m.sup.2

[0405] Knitting density: 37 C/15 W

[0406] Size of void: 34.6 mm.sup.2

[0407] Number of voids: 25

Evaluation Results of Comparative Example 2

[0408] HL150: grade 3

[0409] Rate of change of value B between initial and HL120: −44.7%

[0410] Rate of change of 2HB value: 65.4%

[0411] Rate of change of MIU: 6.1%

[0412] Rate of change of MMD: 14.6%

[0413] Sensory evaluation of texture: gentleness: 4.0, smoothness: 2.0

[0414] Amount of water repellent adhered: 1.0 g/m.sup.2

[0415] Water drainage: 95.3%

[0416] Bursting Strength: 153 kPa

[0417] Since the size of the voids was large and the thickness was small, the Water drainage was good, but since the density and thickness were small, the Bursting Strength was low, and was not adequate for wearing. Besides, the rate of change of MIU was high, and change in the texture caused by laundering was large.

Comparative Example 3

[0418] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that the weight, the knitting density, the size of a void, and the number of the voids of a mesh knitted fabric were changed as follows.

[0419] Weight: 95 g/m.sup.2

[0420] Knitting density: 75 C/52 W

[0421] Size of void: 9.4 mm.sup.2

[0422] Number of voids: 12

Evaluation Results of Comparative Example 3

[0423] HL120: grade 3

[0424] Rate of change of value B between initial and HL120: −13.6%

[0425] Rate of change of 2HB value: −10.2%

[0426] Rate of change of MIU: 5.6%

[0427] Rate of change of MMD: 21.7%

[0428] Sensory evaluation of texture: 4.0

[0429] Amount of water repellent adhered: 2.8 g/m.sup.2

[0430] Water drainage: 69.3%

[0431] Bursting Strength: 210 kPa

[0432] The Water drainage was good in spite of the small number of voids, the texture was good, but the rate of change of MMD was large, and change in the texture caused by laundering was large.

Comparative Example 4

[0433] A water-repellent knitted fabric was obtained under the same conditions as those of Example 9 except that the weight, the knitting density, the size of a void, and the number of the voids of a mesh knitted fabric were changed as follows.

[0434] Weight: 70 g/m.sup.2

[0435] Knitting density: 52 C/30 W

[0436] Size of void: 11.8 mm.sup.2

[0437] Number of voids: 60

Evaluation Results of Comparative Example 4

[0438] HL100: grade 3

[0439] Rate of change of value B between initial and HL120: −63.5%

[0440] Rate of change of 2HB value: 57.6%

[0441] Rate of change of MIU: 4.4%

[0442] Rate of change of MMD: 9.8%

[0443] Sensory evaluation of texture: 4.0

[0444] Amount of water repellent adhered: 2.1 g/m.sup.2

[0445] Water drainage: 68.1%

[0446] Bursting Strength: 353 kPa

[0447] Although the size of the void was in a good range, the number of the voids was large.

Comparative Example 5

[0448] A water-repellent knitted fabric was obtained under the same conditions as those of Example 1 except that a blended yarn of a false-twisted yarn of a polyester filament having single fibers with a circular cross-section (110 dtex, 48 filaments) and a polyester filament having single fibers with a circular cross-section (44 dtex, 48 filaments) was used to obtain a mesh knitted fabric having the following structure, and that the dyeing processing was performed without using a water absorbent.

[0449] Weight: 240 g/m.sup.2

[0450] Knitting density: 32 C/49 W

[0451] Size of void: 75.3 mm.sup.2

[0452] Number of voids: 35

Evaluation Results of Comparative Example 5

[0453] HL100: grade 3

[0454] Rate of change of value B between initial and HL120: −10.4%

[0455] Rate of change of 2HB value: 10.8%

[0456] Rate of change of MIU: 4.5%

[0457] Rate of change of MMD: 30.4%

[0458] Sensory evaluation of texture: 0.0

[0459] Amount of water repellent adhered: 9.5 g/m.sup.2

[0460] Water drainage: 84.6%

[0461] Bursting Strength: 530 kPa

[0462] The weight and the thickness were large, the initial flexural rigidity value B was 0.0464 gf.Math.cm.sup.2/cm, and the 2HB value was as high as 0.0715 gf.Math.cm/cm, and the bounce was strong. Besides, the result of the sensory evaluation of the texture was poor, the feeling of wearing as an innerwear was poor, and the Bursting Strength was high.

[0463] <JIS L-1092 Spray Method: Water Repellency Test (Spray Test)>

[0464] Take three test pieces approximately 200 mm×200 mm from the sample, attach the test pieces so as not to cause wrinkles to the test piece holding frame, align the center of the spray with the center of the holding frame using a water repellency test apparatus, and align the direction of the test pieces so that they are parallel to the flow of water.

[0465] Disperse 250 mL of water in a funnel over the specimen for a duration of 25-30 seconds.

[0466] Then, remove the holding frame from the base top, hold horizontally at one end thereof, the other end with the front side of the test piece facing downward lightly dropped water droplets hit a hard object once, further hold one end turned 180°, remove the excess water droplets by operating in the same manner as before.

[0467] The wetted state of the test piece while being attached to the holding frame is compared with a comparative sample in a wet state and judged.

[0468] Provided, however, that the intermediate rating shall not be applied.

[0469] The water repellency test (spraying test) is the same test procedure as ISO 4920.

[0470] <JIS L-1096 Method A: Bursting Strength>

[0471] The Bursting Strength is measured by the Mullen method.

[0472] a) Procedure

[0473] Five test specimens of about 150 mm×150 mm are taken from the sample, and the test specimen is grasped by a clamp with a Mullen low-pressure tester or a Mullen burst tester having an accuracy equal to or higher than that, with the surface of the test specimen facing up, applying a uniform tension so as not to cause wrinkling and sagging, and pressure is applied to measure the strength (kPa) of the rubber septum to penetrate the test specimen and the strength (kPa) of the rubber septum only at the time of rupture.

[0474] b) Determine the Bursting Strength (kPa) according to the following equation, calculate the average value, and round to three significant digits.

Bs=A−B

[0475] Where: Bs: Bursting Strength (kPa);

[0476] A: Strength (kPa) at which the rubber septum pierces the test piece;

[0477] B: Strength (kPa) of the rubber septum alone at break.

[0478] <Wash>

[0479] JISL0217: Washing is performed according to the method 103 described in 1995.

[0480] Using an electric household washing machine equipped with a centrifugal dehydrator as specified in JIS C 9606, add water with a liquid temperature of 40° C. to the water level line indicating the standard amount of water in the water tub of the test equipment, add and dissolve a laundry synthetic detergent (type 1 (weakly alkaline) as specified in JIS K 3371) at a rate equivalent to the standard amount, and use this as the washing liquid.

[0481] The sample and the load cloth are put into this washing liquid so that the bath ratio becomes 1:30, and the operation is started.

[0482] After treatment for 5 minutes, stop the operation, dehydrate the sample and the load cloth with a dehydrator, and then replace the washing liquid with fresh water at 30° C. or lower, and rinse and wash for 2 minutes at the same bath ratio.

[0483] After a 2 minutes rinse wash, stop the operation, dehydrate the sample and the load cloth, rinse again for 2 minutes, dehydrate, and dry in a state not directly affected by sunlight.

[0484] <JIS L1096 8. 4 Thickness A>

[0485] Thickness is measured at a fixed time (10 s) and constant pressure (0.07 kPa) using a depth meter (Peacock Test machine) at five different locations of the sample, and the mean is calculated and rounded to two digits below the decimal point.