A coalescing element for aggregating droplets of an emulsion. The coalescing element includes a nonwoven web substrate. A coalescer that includes the coalescing element can also include a housing and a fluid inlet and a fluid outlet each in fluid communication with the coalescing element. The coalescing element and coalescer may be useful for emulsions that form in solvent extraction/electrowinning copper processing and for other emulsions.

Claims

1. A method of coalescing droplets in an emulsion, the emulsion comprising: a continuous aqueous phase having a pH≤5 optionally containing copper ions, and an organic phase comprising a complex of a lixiviant and copper ions, the method comprising contacting the emulsion with a nonwoven web substrate.

2. The method of claim 1, further comprising: contacting a coalescer with the emulsion, wherein the coalescer comprises: a housing; a coalescing element comprising the nonwoven web substrate located in the housing; and a fluid inlet and a fluid outlet each in fluid communication with the coalescing element, wherein a D.sub.50 droplet particle size is bigger by at least a factor of 3 upon flow out of the fluid outlet relative to the D.sub.50 droplet particle size upon flow into the fluid inlet.

3. The method of claim 2, wherein the nonwoven web substrate comprises at least one of a spunlaid, spunbond, hydroentangled, or a meltblown nonwoven web substrate.

4. The method of claim 2, wherein the nonwoven web substrate has an effective fiber diameter of 1 micrometer to 40 micrometers.

5. The method of claim 4, wherein the nonwoven web substrate includes fibers that have different effective fiber diameters.

6. The method of claim 4, wherein the nonwoven web substrate is hydrophilic.

7. The method of claim 6, wherein the nonwoven web substrate comprises a hydrophilic polymer or hydrophilic copolymer covalently bonded to the surface of its fibers.

8. The method of claim 2, wherein the nonwoven web substrate comprises two or more layers of nonwoven webs.

9. The method of claim 8, wherein at least two of the two or more layers of nonwoven webs have different effective fiber diameters.

10. The method of claim 1, wherein the nonwoven web substrate comprises at least one of a spunlaid, spunbond, hydroentangled, or a meltblown nonwoven web substrate.

11. The method of claim 1, wherein the nonwoven web substrate has an effective fiber diameter of 1 micrometer to 40 micrometers.

12. The method of claim 1, wherein the nonwoven web substrate includes fibers that have different effective fiber diameters.

13. The method of claim 1, wherein the nonwoven web substrate is hydrophilic.

14. The method of claim 13, wherein the nonwoven web substrate comprises a hydrophilic polymer or hydrophilic copolymer covalently bonded to the surface of its fibers.

15. The method of claim 1, wherein the nonwoven web substrate comprises two or more layers of nonwoven webs.

16. The method of claim 15, wherein at least two of the two or more layers of nonwoven webs have different effective fiber diameters.

17. The method of claim 1, wherein the emulsion has an organic solvent phase to aqueous acidic phase in a ratio of 1:1 to 1.5:1.

18. The method of claim 1, wherein the nonwoven web substrate has a surface energy of less than 35 dyne/cm.

19. The method of claim 1, wherein the nonwoven web substrate comprises fibers of inherently hydrophilic polymers selected from the group consisting of polyamides and poly(vinyl alcohol).

20. The method of claim 1, wherein the nonwoven web substrate has a solidity of less than 20%.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a flow schematic of a system utilizing a coalescing article.

DETAILED DESCRIPTION

(2) Provided are droplet coalescers, or coalescing articles, and systems that utilize the droplet coalescers, and methods of making and using the same. The coalescers comprise a coalescing element located in a housing or frame, the coalescing element comprising at least one nonwoven web. There are a fluid inlet and outlet in fluid communication with the coalescing element such that the emulsion flows through the nonwoven web. Such nonwoven webs may be stacked or spiraled together alone or with other layers, some of which may provide additional functionality such as spacing and/or flow enhancement.

(3) In operation, nominally small droplets entering a coalescing element agglomerate upon contact with the surface of the nonwoven web, thereby forming droplets of a larger size. For example, droplets generally agglomerate such that the D.sub.50 droplet particle size is bigger, by for example at least a factor of 3 (or 10 or 100), upon flow out of the fluid outlet relative to the D.sub.50 droplet particle size upon flow into the fluid inlet. Specifically, the droplets wick into or wet the fibers of the nonwoven web, and then move downstream with the flow. Residence time in the coalescing element is inversely related to flow rate and directly related to the fluid path through the nonwoven web and the surface area, which are designed as needed for particular applications. As the droplets progress through the web, they coalesce into larger droplets. These larger droplets (>100 μm) easily separate from the continuous phase due to Stokes' Law, often in a settling tank without further assistance.

(4) The coalescers may be used in copper SX process, where coalescence of organic solvent oil-phase droplets from water or water-phase droplets from SX organic will facilitate operations. For example, coalesced droplets would lead to easier separation in downstream operations. In mining, the use of a coalescer would allow for recovery of the valuable organic that is either lost or collected from a raffinate pond, where expensive re-processing is subsequently required. The coalescers disclosed herein can accommodate large amounts of flow at low pressure drop (up to 20,000 liters/m.sup.2/hr at less than 5 psig), which means that the coalescers are a practical technical solution that fit into existing operational demands, such as hydraulics requirements of a SX process.

(5) The nonwoven web may be formed from any suitable thermoplastic polymeric material. Suitable polymeric materials include, but are not limited to, polyolefins, poly(isoprenes), poly(butadienes), fluorinated polymers, chlorinated polymers, polyamides, polyimides, polyethers, poly(ether sulfones), poly(sulfones), poly(vinyl acetates), polyesters such as poly(lactic acid), copolymers of vinyl acetate, such as poly(ethylene)-co-poly(vinyl alcohol), poly(phosphazenes), poly(vinyl esters), poly(vinyl ethers), poly(vinyl alcohols), and poly(carbonates). The polymer used in forming the nonwoven web may be inherently hydrophilic or hydrophobic, and may be further comprise a grafted (co)polymer to alter the relative hydrophilicity/hydrophobicity or surface energy. In some embodiments, the nonwoven web substrate comprises fibers of inherently hydrophilic polymers. In some embodiments, these inherently hydrophilic polymers comprise at least one of a polyamide or poly(vinyl alcohol).

(6) Suitable polyolefins include, but are not limited to, poly(ethylene), poly(propylene), poly(1-butene), copolymers of ethylene and propylene, alpha olefin copolymers (such as copolymers of ethylene or propylene with 1-butene, 1-hexene, 1-octene, and 1-decene), poly(ethylene-co-1-butene) and poly(ethylene-co-1-butene-co-1-hexene).

(7) Suitable fluorinated polymers include, but are not limited to, poly(vinyl fluoride), poly(vinylidene fluoride), copolymers of vinylidene fluoride (such as poly(vinylidene fluoride-co-hexafluoropropylene), and copolymers of chlorotrifluoroethylene (such as poly(ethylene-co-chlorotrifluoroethylene).

(8) Suitable polyamides include, but are not limited to, poly(iminoadipolyliminohexamethylene), poly(iminoadipolyliminodecamethylene), and polycaprolactam. Suitable polyimides include, but are not limited to, poly(pyromellitimide).

(9) Suitable poly(ether sulfones) include, but are not limited to, poly(diphenylether sulfone) and poly(diphenylsulfone-co-diphenylene oxide sulfone).

(10) Suitable copolymers of vinyl acetate include, but are not limited to, poly(ethylene-co-vinyl acetate) and such copolymers in which at least some of the acetate groups have been hydrolyzed to afford various poly(vinyl alcohols).

(11) Suitable polyesters include those commonly made by condensation polymerization of hydroxyl-containing monomers and/or oligomers (e.g., chain extenders such as glycols and the like) with poly-acid-containing or poly-ester-containing monomers and/or oligomers (e.g., dicarboxylic acids or diesters such as terephthalic acid, naphthalene dicarboxylate, etc.). It should be noted that such polyesters may be made from poly-acids, or from any ester-forming equivalents of such materials (e.g., from any materials that can be polymerized to ultimately provide a polyester, such as hydroxy acid, including poly(lactic acid). Other useful polyesters include the aliphatic polyesters described in U.S. Pat. No. 6,645,618 (Perez et al.), incorporated herein by reference.

(12) As used herein, the term “nonwoven web” refers to a fabric that has a structure of individual fibers or filaments which are randomly and/or unidirectionally interlaid in a mat-like fashion.

(13) For example, the fibrous nonwoven web can be made by wet laid, carded, air laid, spunlaced, spunbonding or melt-blowing techniques or combinations thereof. Spunbonded fibers are typically small diameter fibers that are formed by extruding molten thermoplastic polymer as filaments from a plurality of fine, usually circular capillaries of a spinneret with the diameter of the extruded fibers being rapidly reduced. Meltblown fibers are typically formed by extruding the molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten threads or filaments into a high velocity, usually heated gas (e.g. air) stream which attenuates the filaments of molten thermoplastic material to reduce their diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to from a web of randomly dispersed meltblown fibers. Spunlacing uses high-speed jets of water to strike a web to intermingle the fibers of the web. Spunlacing is also known as hydroentangling and can be carried out on fibrous webs made, for example, using carded webs and air-laid webs.

(14) Further details on the manufacturing method of non-woven webs useful for practicing the present disclosure may be found in Wente, Superfine Thermoplastic Fibers, 48 INDUS. ENG. CHEM. 1342(1956), or in Wente et al., Manufacture Of Superfine Organic Fibers, (Naval Research Laboratories Report No. 4364, 1954). Useful methods of preparing the nonwoven substrates are described in U.S. RE 39,399 (Allen), U.S. Pat. No. 3,849,241 (Butin et al.), U.S. Pat. No. 7,374,416 (Cook et al.), U.S. Pat. No. 4,936,934 (Buehning), and U.S. Pat. No. 6,230,776 (Choi), each incorporated herein by reference.

(15) In some embodiments the nonwoven web is grafted with one or more grafting monomers to alter the surface characteristics thereof. The grafting monomers can graft (i.e. forming a covalent bond) to the surface of the base substrate when exposed to an ionizing radiation preferably e-beam or gamma radiation. That is, reaction of (meth)acryloyl groups of the grafting monomers with the surface of the nonwoven web substrate in the presence of the ionizing radiation results in the (co)polymer being directly grafted to the base substrate via the (meth)acrylate group.

(16) The grafting methods of the present disclosure involve the irradiation of nonwoven web substrates with ionizing radiation to prepare free radical reaction sites on such substrates upon which the functional monomers are grafted. “Ionizing radiation” means radiation of a sufficient dosage and energy to cause the formation of free radical reaction sites on the surface(s) of the polymeric nonwoven web. Ionizing radiation may include beta, gamma, electron-beam, x-ray and other electromagnetic radiation. In some instances, corona radiation can be sufficiently high energy radiation. In some embodiments, the ionizing radiation comprises ionizing e-beam or gamma radiation. The radiation is sufficiently high energy, that when absorbed by the surfaces of the nonwoven web substrate, sufficient energy is transferred to that substrate to result in the cleavage of chemical bonds in that substrate and the resultant formation of a free radical site on the substrate. The incipient free radicals on the surface initiates free radical polymerization of the monomers. One or more layers of nonwoven substrates may be subjected to the ionizing radiation.

(17) The method of grafting a ligand (co)polymer to the surface of the substrate alters the original nature of the nonwoven web substrate, as the substrate bears a grafted (co)polymer. The resulting grafted (co)polymer substrates has many of the advantages of a base nonwoven substrate (e.g., mechanical and thermal stability, porosity), but with enhanced properties such as wettability, surface energy, clog resistance and flux.

(18) The process of preparing the grafted nonwoven substrate comprises the steps of providing a nonwoven substrate, imbibing the exposed substrate with a solution comprising grafting monomers (as described below), and exposing the nonwoven substrate to ionizing radiation in an inert atmosphere, to graft polymerize said monomers to the surface of the nonwoven substrate. The imbibing step and irradiation can be done in either order.

(19) In the imbibing step, the nonwoven substrate is contacted with the imbibing solution containing one or more grafting monomers. Suitable methods of imbibing include, but are not limited to, a spray coating, flood coating, knife coating, Meyer bar coating, dip coating, and gravure coating.

(20) If irradiated prior to imbibing, the imbibing solution remains in contact with the nonwoven substrate for a time sufficient for the radical sites to initiate polymerization with the grafting monomers. When imbibed with a solution of monomers, grafting reactions are mostly completed after 12 hours exposure; generally resulting in >50% conversion of monomers to grafted polymer. As a result, the nonwoven substrate comprises grafted polymers and/or copolymers attached to the interstitial and outer surfaces of the nonwoven substrate.

(21) The imbibing solution may comprise one or more grafting monomers suitable for grafting onto surfaces of the nonwoven substrate. Any of the exemplary grafting monomers described herein can be included in the imbibing solution. In addition to the described grafting monomers, the imbibing solution can contain other materials such as, for example, one or more other non-grafting monomers for UV curing, surfactants, dyes, pigments and solvents.

(22) The concentration of each grafting monomer in the imbibing solution may vary depending on a number of factors including, but not limited to, the grafting monomer or monomers in the imbibing solution, the extent of grafting desired, the reactivity of the grafting monomer(s), and the solvent used. Typically, the total concentration of the monomers in the imbibing solution ranges from about 1 wt % to about 100 wt %, desirably, from about 5 wt % to about 30 wt %, and more desirably from about 15 wt % to about 25 wt % based on a total weight of the imbibing solution.

(23) The imbibing solution may further comprise an aqueous blend of an organic solvent and the grafting monomer(s). In some embodiments, the organic solvent is a water-miscible organic solvent.

(24) It has been found that the solvent blend influences the morphology of the grafted polymer and the resulting flux rate. The ratio of water to organic solvent can vary widely, but is typically greater than 1:1 (v/v) water to organic solvent, preferably greater than 5:1, and more preferably greater than 7:1. The ratios are generally adjusted so that the resulting grafted nonwoven substrate has the requisite hydrophilicity, surface energy and/or wettability to effectively coalesce the dispersed droplets of the emulsion.

(25) The concentration of the organic solvent in water may be optimized with respect to the fiber size of the nonwoven substrate. In general, the optimum concentration of organic solvent increases as the fiber size decreases.

(26) It is believed that by adjusting the amount of organic solvent in the imbibing solution a greater amount of monomer is grafted to the nonwoven substrate without bridging the fibers of the substrate and closing the voids. If the web voids are bridged, the nonwoven dries to a translucent appearance, and has decreased flux and reduced ability to expand on hydration. The smaller the fibers the less monomer it takes to bridge the pores of the nonwoven. Adding more organic solvent reduces the bridging, allows for increased grafted polymer content (as a function of weight percent of the nonwoven substrate) and allows for freer expansion of the article.

(27) Any such organic solvent typically has no tertiary hydrogen atoms, or other groups that would retard the graft polymerization. In some embodiments, the water miscible solvents are protic group containing organic liquids such as the lower alcohols having 1 to 4 carbon atoms, lower glycols having 2 to 6 carbon atoms, and most preferably lower glycol ethers having 3 to 6 carbon atoms and 1 to 2 ether linkages. In some embodiments higher glycols such as poly(ethylene glycol) may be used. Specific examples are methanol, ethanol, n-butanol, t-butyl alcohol, ethylene glycol, methoxyethanol, ethoxyethanol, propoxyethanol, butoxyethanol, methyl carbitol, ethyl carbitol, and mixtures thereof.

(28) In other embodiments, non-protic organic solvents that can also be used such as aliphatic esters and ketones and sulfoxides such as ethyl acetate, propyl acetate, butyl acetate, methoxyethyl acetate, ethoxyethyl acetate, propoxyethyl acetate, butoxyethyl acetate, triethyl phosphate, acetone, methyl ethyl ketone, methyl propyl ketone, and dimethyl sulfoxide.

(29) In the irradiation step the nonwoven substrate is exposed to ionizing radiation, such as e-beam radiation, in an inert atmosphere. Generally, the substrate is placed in a chamber purged of oxygen. Typically, the chamber comprises an inert atmosphere such as nitrogen, carbon dioxide, helium, argon, etc., with a minimal amount of oxygen (less than 100 ppm), which is known to inhibit free-radical polymerization.

(30) Electron beam is one useful method of grafting due to the ready-availability of commercial sources. Electron beam generators are commercially available from a variety of sources, including the ESI “ELECTROCURE” EB SYSTEM from Energy Sciences, Inc. (Wilmington, Mass.), and the BROADBEAM EB PROCESSOR from PCT Engineered Systems, LLC (Davenport, Iowa). For any given piece of equipment and irradiation sample location, the dosage delivered can be measured in accordance with ASTM E-1275 entitled “Practice for Use of a Radiochromic Film Dosimetry System.” By altering extractor grid voltage, beam diameter and/or distance to the source, various dose rates can be obtained.

(31) In the irradiation step the nonwoven substrate is exposed to a sufficient quantity of ionizing radiation, so as to form free radicals on the surfaces of the nonwoven substrate. The chamber may contain at least one device capable of providing a sufficient dose of radiation. A single device is capable of providing a sufficient dose of radiation, although two or more devices, and/or multiple passes through a single device, may be used especially for relatively thick nonwoven substrates.

(32) Dose is the total amount of energy absorbed per mass unit. Dose is commonly expressed in units of kiloGray (kGy). A gray is defined as the amount of radiation required to supply 1 joule of energy per kilogram of mass. The total dose received by the substrate depends on a number of parameters including source activity, residence time (i.e., the total time the sample is irradiated), the distance from the source, and attenuation by the intervening cross-section of materials between the source and sample. Dose is typically regulated by controlling residence time, distance to the source, or both.

(33) Generally, it was found that doses in the range of less than about 100 kGy were suitable for generating the grafted (co)polymer. Total dose requirement for any given composition will vary as a function of desired grafting objectives, monomer selected, substrate used, and the dose rate. Thus, a dose rate can be selected based on desired properties for a specified composition. The dose rate is typically in the range of 0.0005 kGy/sec (gamma) to 200 kGy/sec (E-beam).

(34) Other sources of irradiation may be used with equal grafting performance; a desirable source of ionizing radiation comprises an electron beam source because the electron beam can produce high and fast dose delivery rates. Electron beams (e-beams) are generally produced by applying high voltage to tungsten wire filaments retained between a repeller plate and an extractor grid within a vacuum chamber maintained at about 10.sup.−6 Torr. The filaments are heated at high current to produce electrons. The electrons are guided and accelerated by the repeller plate and extractor grid towards a thin window of metal foil. The accelerated electrons, traveling at speeds in excess of 10.sup.7 meters/second (m/sec) and possessing about 100 to 300 kilo-electron volts (keV), pass out of the vacuum chamber through the foil window and penetrate whatever material is positioned immediately beyond the foil window.

(35) The quantity of electrons generated is directly related to the current. As extractor grid voltage is increased, the acceleration or speed of electrons drawn from the tungsten wire filaments increase. E-beam processing can be extremely precise when under computer control, such that an exact dose and dose rate of electrons can be directed against the nonwoven substrate.

(36) The temperature within the chamber is desirably maintained at an ambient temperature by conventional means. Without intending to be limited to any particular mechanism, it is believed that the exposure of the nonwoven substrate to an electron beam results in free radical sites on the substrate surface which can then subsequently react with the grafting monomers in the imbibing step.

(37) The total dose received by the nonwoven substrate primarily affects the number of radical sites formed on the surface thereof and subsequently the extent to which the grafting monomers are grafted onto the nonwoven substrate. Dose is dependent upon a number of processing parameters, including voltage, web- or line-speed and beam current. Dose can be conveniently regulated by controlling line speed (i.e., the speed with which the nonwoven substrate passes under the irradiation device), and the current supplied to the extractor grid. A target dose (e.g., <10 kGy) can be conveniently calculated by multiplying an experimentally measured coefficient (a machine constant) by the beam current and dividing by the web speed to determine the exposure. The machine constant varies as a function of beam voltage.

(38) While the controlled amount of electron beam radiation exposure is dependent upon the residence time, the nonwoven substrate is subjected to a controlled amount of dosage ranging from a minimum dosage of about 1 kilogray (kGy) to a practical maximum dosage of less than about 200 kGy, depending on the particular polymer. For radiation sensitive polymers such as propylene polymers the amount typically ranges from a minimum dosage of about 1 kilogray (kGy) to a maximum dosage of less than about 10 kGy. Typically, the total controlled amount of dosage ranges from less than about 9 kGy to about 7 kGy for propylene polymers to avoid degradation. Less radiation sensitive polymers such as nylons or PVDF may be subjected to higher dosages, typically 10 to 70 kGy.

(39) Generally, suitable gamma ray sources emit gamma rays having energies of 400 keV or greater. Typically, suitable gamma ray sources emit gamma rays having energies in the range of 500 keV to 5 MeV. Examples of suitable gamma ray sources include cobalt-60 isotope (which emits photons with energies of approximately 1.17 and 1.33 MeV in nearly equal proportions) and cesium-137 isotope (which emits photons with energies of approximately 0.662 MeV). The distance from the source can be fixed or made variable by changing the position of the target or the source. The flux of gamma rays emitted from the source generally decays with the square of the distance from the source and duration of time as governed by the half-life of the isotope.

(40) Where irradiation precedes imbibing, the irradiated substrate, having free radical sites on the surface of the nonwoven substrate, is imbibed with the monomer solution subsequent to and not concurrent with, the irradiation step. The free radical sites generated on the surface of the nonwoven substrate have average lifetimes ranging from several minutes to several hours and progressively decay to a low concentration within about ten hours at room temperature. Lower temperatures, such as dry ice temperatures, promote longer radical lifetimes.

(41) Generally, the irradiated nonwoven substrate is imbibed with the monomer solution immediately after the irradiation step. When using e-beam the irradiated substrate is imbibed within an hour, in some cases, within ten minutes. Generally, when using gamma irradiation, the substrate should be imbibed immediately after irradiation since irradiation residence time will be long. It has been observed that if the substrate is irradiated by ionizing radiation in the presence of the grafting monomers, the performance of the grafted nonwoven substrate is inferior, presumably due to less grafted (co)polymer.

(42) Once grafted, the nonwoven substrate bearing grafted (co)polymer groups may be optionally rinsed to remove residual monomer and/or dried. In the optional rinsing step, the functionalized nonwoven substrate is washed or rinsed one or more times to remove any unreacted monomers, solvent or other reaction by-products. Typically, the functionalized substrate is washed or rinsed up to three times using a water rinse, an alcohol rinse, a combination of water and alcohol rinses, and/or another solvent rinse (e.g., acetone, methyl ethyl ketone, etc). When an alcohol rinse is used, the rinse may include one or more alcohols including, but not limited to, isopropanol, methanol, ethanol, or any other alcohol that is practical to use and an effective solvent for any residual monomer. In each rinse step, the functionalized substrate may pass through a rinse bath or a rinse spray. In some embodiments, the rinse may comprise an ionic buffer solution that would reduce swelling of the nonwoven substrate, the amount of retained water, and also avoiding weakening the nonwoven substrate during this rinse step.

(43) In the optional drying step, the grafted nonwoven substrate is dried to remove any rinse solution. Typically, the grafted nonwoven substrate is dried in oven having a relatively low oven temperature for a desired period of time (referred to herein as “oven dwell time”). Oven temperatures typically range from about 60 C to about 120 C, while oven dwell times typically range from about 120 to about 600 seconds. Any conventional oven may be used in the optional drying step. It should also be noted that in other embodiments the drying step can proceed before the rinsing step to eliminate volatile components before extraction of non-grafted residue. Following the optional drying step, the dried grafted nonwoven substrate can be taken up in roll form to be stored for future use

(44) The grafting monomers may comprise hydrophilic monomers to render the nonwoven more hydrophilic. Hydrophilic monomers include cationic monomer, anionic monomer and nonionic hydrophilic monomers, such as poly(ethylene glycol) (meth)acrylate. The hydrophilic monomer are categorized assuming neutral pH, and regardless of the state of protonation, e.g. acid-functional monomers are considered anionic due to ionization at neutral pH, but are protonated at low pH.

(45) The anionic monomer has at least one ethylenically unsaturated group capable of undergoing free radical polymerization and an anionic functional group. In some embodiments, the ethylenically unsaturated group is a (meth)acryloyl group or a vinyl group. The anionic monomer can be a weak acid, a strong acid, a salt of a weak acid, a salt of a strong acid, or combinations thereof. That is, the ionic monomer can be in a neutral state but capable of being negatively charged if the pH is adjusted. The counter ions of these salts can be, but are not limited to, alkali metals, alkaline earth metals, ammonium ions, or tetraalkylammonium ions. As the emulsion is acidic, weak and strong acids groups are protonated.

(46) Anionic (meth)acryloyl monomers may have the general formula:

(47) ##STR00001##

(48) where

(49) R.sup.1 is H or CH.sub.3;

(50) X is —O— or —NR.sup.1—,

(51) Y is a straight or branched chain alkylene, generally from 1 to 10 carbon atoms; and

(52) Z is an anionic group, which may be selected from sulphonic acid groups, phosphonic acid groups, and carboxylic acid groups, and salts thereof.

(53) Some examples of anionic monomers include (meth)acrylamidosulfonic acids of Formula (II) or salts thereof:

(54) ##STR00002##
where
R.sup.1 is H or CH.sub.3, and Y is a straight or branched alkylene having 1 to 10 carbon atoms. Examples of ionic monomers according to Formula (II) include, but are not limited to, N-acrylamidomethanesulfonic acid, 2-acrylamidoethanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, and 2-methacrylamido-2-methylpropanesulfonic acid. Salts of these acidic monomers can also be used, examples being (3-sulfopropyl)-methacrylic acid potassium salt and 2-(methacryloyloxy)ethylsulfonic acid sodium salt.

(55) Other suitable anionic monomers for the graft polymer include sulfonic acids such as vinylsulfonic acid and 4-styrenesulfonic acid; (meth)acrylamidophosphonic acids such as (meth)acrylamidoalkylphosphonic acids (e.g., 2-acrylamidoethylphosphonic acid and 3-methacrylamidopropylphosphonic acid); acrylic acid and methacrylic acid; and carboxyalkyl(meth)acrylates such as 2-carboxyethylacrylate, 2-carboxyethylmethacrylate, 3-carboxypropylacrylate, and 3-carboxypropylmethacrylate. Still other suitable acidic monomers include (meth)acryloylamido acids, such as those described in U.S. Pat. No. 4,157,418 (Heilmann), incorporated herein by reference. Examples of (meth)acryloylamido acids include, but are not limited to, N-acryloylglycine, N-acryloylaspartic acid, N-acryloyl-β-alanine, 2-acrylamidoglycolic acid, and 3-acrylamido-3-methylbutyric acid.

(56) Some exemplary ionic grafting monomers that are capable of providing a positive charge are amino (meth)acrylates or amino (meth)acrylamides of Formula IV or quaternary ammonium salts thereof. The counter ions of the quaternary ammonium salts are often halides, sulfates, phosphates, nitrates, and the like.

(57) ##STR00003##
where L is oxy or —NR.sup.1—, where R.sup.1 is H or C.sub.1-C.sub.4 alkyl; R.sup.3 is H or CH.sub.3, and Y is an alkylene (e.g. an alkylene having 1 to 10 carbon atoms, 1 to 6, or 1 to 4 carbon atoms). Each R.sup.5 is independently hydrogen, alkyl, hydroxyalkyl (i.e. an alkyl substituted with a hydroxy), or aminoalkyl (i.e. an alkyl substituted with an amino). Alternatively, the two R.sup.5 groups taken together with the nitrogen atom to which they are attached can form a heterocyclic group that is aromatic, partially unsaturated (i.e. unsaturated but not aromatic), or saturated, wherein the heterocyclic group can optionally be fused to a second ring that is aromatic (e.g. benzene), partially unsaturated (e.g. cyclohexene), or saturated (e.g. cyclohexane).

(58) It will be understood with respect to Formula IV that the grafting (meth)acrylate group may be replaced by another ethylenically unsaturated group capable of graft polymerization, such as methacrylate, (meth)acrylamide, vinyl, vinyloxy, ally, alloxy, and acetylenyl for subsequent incorporation during ionizing radiation-initiated polymerization.

(59) In some embodiments of Formula IV, both R.sup.5 groups are hydrogen. In other embodiments, one R.sup.5 group is hydrogen and the other is an alkyl having 1 to 10, 1 to 6, or 1 to 4 carbon atoms. In still other embodiments, at least one of R.sup.5 groups is a hydroxy alkyl or an amino alkyl that have 1 to 10, 1 to 6, or 1 to 4 carbon atoms with the hydroxy or amino group being positioned on any of the carbon atoms of the alkyl group. In yet other embodiments, the R.sup.5 groups combine with the nitrogen atom to which they are attached to form a heterocyclic group. The heterocyclic group includes at least one nitrogen atom and can contain other heteroatoms such as oxygen or sulfur. Exemplary heterocyclic groups include, but are not limited to imidazolyl. The heterocyclic group can be fused to an additional ring such as a benzene, cyclohexene, or cyclohexane. Exemplary heterocyclic groups fused to an additional ring include, but are not limited to, benzoimidazolyl.

(60) Exemplary amino (meth)acrylates (i.e. L in Formula IV is oxy) include N,N-dialkylaminoalkyl acrylates such as, for example, N,N-dimethylaminoethylacrylate, N,N-dimethylaminoethylmethacrylate, N,N-diethylaminoethyl acrylate, N,N-diethylaminoethylmethacrylate, N,N-dimethylaminopropylacrylate, N,N-dimethylaminopropylmethacrylate, N-tert-butylaminopropylmethacrylate, N-tert-butylaminopropylacrylate, and the like.

(61) Examples of amino (meth)acrylamides, that would be subsequently incorporated during the radiation-initiated polymerization, (i.e. L in Formula IV is —NR.sup.1—) include, for example, N-(3-aminopropyl)methacrylamide, N-(3-aminopropyl)acrylamide, N-[3-(dimethylamino)propyl]methacrylamide, N-[3-(dimethylamino)propyl]acrylamide, N-(3-imidazolylpropyl)methacrylamide, N-(3-imidazolylpropyl)acrylamide, N-(2-imidazolylethyl)methacrylamide, N-(2-imidazolylethyl)acrylamide, N-(1,1-dimethyl-3-imidazoylpropyl)methacrylamide, N-(1,1-dimethyl-3-imidazoylpropyl)acrylamide, N-(3-benzoimidazolylpropyl)acrylamide, and N-(3-benzoimidazolylpropyl)methacrylamide.

(62) Examples of quaternary salts of the ionic monomers of Formula IV include, but are not limited to, (meth)acrylamidoalkyltrimethylammonium salts (e.g. 3-methacrylamidopropyltrimethylammonium chloride and 3-acrylamidopropyltrimethylammonium chloride) and (meth)acryloxyalkyltrimethylammonium salts (e.g. 2-acryloxyethyltrimethylammonium chloride, 2-methacryloxyethyltrimethylammonium chloride, 3-methacryloxy-2-hydroxypropyltrimethylammonium chloride, 3-acryloxy-2-hydroxypropyltrimethylammonium chloride, and 2-acryloxyethyltrimethylammonium methyl sulfate).

(63) Other monomers that can provide positively charged groups to the grafted polymer include the dialkylaminoalkylamine adducts of alkenylazlactones (e.g. 2-(diethylamino)ethylamine, (2-aminoethyl)trimethylammonium chloride, and 3-(dimethylamino)propylamine adducts of vinyldimethylazlactone) and diallylamine monomers (e.g. diallylammonium chloride and diallyldimethylammonium chloride). Alternatively, azlactone monomers may be functionalized with aminoalkanols as described in US 20140046029 (Rasmussen et al.), incorporated herein by reference.

(64) In some embodiments, the cationic monomer may be an agmatine monomer of Formula V:

(65) ##STR00004##
wherein
R.sup.1 is H or C.sub.1-C.sub.4 alkyl;
R.sup.2 is a divalent alkylene, preferably having 1 to 20 carbon atoms and optionally containing an ester, amide, urethane or urea linking group;
each R.sup.3 is independently H or C.sub.1-C.sub.4 alkyl;
R.sup.4 is H, C.sub.1-C.sub.4 alkyl or —N(R.sup.3).sub.2; and X.sup.1 is —O— or —NR.sup.3—. The nonwoven web may be directly- or indirectly grafted with the agmatine monomer of Formula V, as further described in U.S. Pat. No. 8,586,338 (Rasmussen et al.), incorporated herein by reference.

(66) In general, the monomers having the requisite cationic, anionic or nonionic groups may be graft polymerized per se, or may be indirectly grafted by graft polymerizing a monomer having a reactive functional group, such as a isocyanate group or an azlactone group, then subsequently functionalizing the grafted polymer with the requisite anionic, cationic or nonionic group. For example, the nonwoven web may be grafted with isocyanatoethylmethacrylate to yield a graft (co)polymer having pendent isocyanate groups. This (co)polymer may be subsequently functionalized with agmatine sulfate to provide a grafted (co)polymer with pendent agmatine groups. As a second example, the nonwoven may be grafted with vinyl dimethylazlactone (VDM) and subsequently reacted with an amino-alcohol to produce a grafted (co)polymer having pendent amine groups. This indirect grafting and functionalization is described in U.S. Pat. No. 8,586,338 (Rasmussen et al.).

(67) The grafted polymer optionally contains monofunctional ethylenically-unsaturated grafting monomer units having a poly(alkylene oxide) group. These monomers copolymerize with the grafting anionic monomers to form a grafted copolymer chain on the surface of the nonwoven substrate. When present, these monomers are used in amounts of 2 to 20 wt. %, more preferably 5 to 10 wt. %, relative to the total monomer weight.

(68) The monomer units having a poly(alkylene oxide) group is of the formula:
Z-Q-(CH(R.sup.1)—CH.sub.2—O).sub.m—R.sup.4,  III
wherein Z is a polymerizable ethylenically unsaturated moiety, R is a H or CH.sub.3, R.sup.4 is a H, a C.sub.1 to C.sub.4 alkyl group, aryl group, or combinations thereof and m is from 2 to 100, in some embodiments, 5 to 20, and Q is a divalent linking group selected from —O—, —NR.sup.1—, —CO.sub.2— and —CONR.sup.1.

(69) In one embodiment, the poly(alkylene oxide) group is a poly(ethylene oxide) (co)polymer. In another embodiment, the pendent poly(alkylene oxide) group is a poly(ethylene oxide-co-propylene oxide) copolymer. Such copolymers may be block copolymers, random copolymers, or gradient copolymers.

(70) Useful ethylenically unsaturated moiety, Z, of the monomer may include:

(71) ##STR00005##
wherein R.sup.1 is H or Me and r=1-10.

(72) Examples of suitable monofunctional poly(alkylene oxide) monomers include poly(ethylene oxide) (meth)acrylate, poly(propylene oxide) (meth)acrylate, poly(ethylene oxide-propylene oxide) (meth)acrylate, and combinations thereof. In some embodiments, such monomers include one nonreactive end group such as (C.sub.1-C.sub.4) alkoxy, aryloxy (e.g., phenoxy), and (C.sub.1-C.sub.4) alkaryloxy. These groups can be linear or branched. These monomers can be of a wide range of molecular weights and are commercially available from sources such as Sartomer Company, Exton, Pa.; Shinnakamura Chemical Co., Ltd., Tokyo, Japan; Aldrich, Milwaukee, Wis.; and Osaka Organic Chemical Ind., Ltd., Osaka, Japan.

(73) The grafted polymer optionally contains other ethylenically-unsaturated hydrophilic grafting monomer units having a water miscibility (water in monomer) of at least 1 wt. %, in some embodiments at least 5 weight % without reaching a cloud point, are exclusive of poly(alkylene oxide) monomers and contain no groups that would retard the grafting polymerization.

(74) Examples of suitable hydrophilic monomers include 2-hydroxyethyl(meth)acrylate (HEMA), 2-hydroxypropyl(meth)acrylate, 3-hydroxypropyl(meth)acrylate, 2, 3-dihydroxypropyl (meth)acrylate, 4-hydroxybutyl(meth)acrylate, N-vinyl caprolactam, N-vinyl acetamide, N-vinyl pyrrolidone, acrylonitrile, tetrahydrofurfuryl acrylate, acrylamide, mono- or di-N-alkyl substituted acrylamide, glycerol methacrylate, glycidyl (meth)acrylate, and combinations thereof. In some embodiments, the hydrophilic monomers include 2-hydroxyethyl(meth)acrylate (HEMA), N-vinyl pyrrolidone, N-vinyl acetamide, methylacrylamide, glycidyl (meth)acrylate and mixtures thereof.

(75) The nonwoven webs may be rendered hydrophobic and/or oleophobic by graft polymerization of a fluorine-containing monomer. In particular, the nonwoven substrate may be grafted with a poly(hexafluoropropylene oxide) monomer (and other comonomers), such as is described U.S. 2005/0249940 (Klun) and US 2012/0015002 (Ali et al.), incorporated herein by reference. Other useful poly(hexafluoropropylene oxide) monomers (HFPO monomers) and copolymers with other monomers is described in U.S. Pat. No. 6,995,222 (Buckanin et al.) incorporated herein by reference.

(76) The nonwoven web substrates useful for practicing the present disclosure typically have an effective fiber diameter of from about 0.5 to 40 micrometers, in some embodiments, from about 0.5 to 30 micrometers, 0.5 to 25 micrometers, 1 to 20 micrometers, 1 to 15 micrometers, or 1 to 10 micrometers, as calculated according to the method set forth in Davies, C. N., “The Separation of Airborne Dust and Particles,” Institution of Mechanical Engineers, London, Proceedings 1B, 1952.

(77) In some embodiments, the nonwoven web substrate includes fibers that have different effective fiber diameters. In other words, fibers in the same web or same layer of the nonwoven web substrate may have different effective fiber diameters. In some embodiments, the coalescing element disclosed herein comprises two or more nonwoven layers in a stacked relation. In some embodiments, the coalescing element disclosed herein comprises one or more nonwoven layers in a spiral-wound configuration. In some of these embodiments, at least two of the two or more layers of nonwoven webs have different effective fiber diameters. As shown in Table 4 in the Examples, below, in some embodiments, a mixture of effective fiber diameters in the nonwoven web substrate can more effectively reduce the turbidity of an emulsion than when the same effective fiber diameter is used throughout the nonwoven web substrate.

(78) The nonwoven substrate preferably has a basis weight in the range of about 10 to 400 g/m.sup.2, more preferably about 10 to 100 g/m.sup.2. The average thickness of the nonwoven substrate is preferably about 0.1 to 100 mm, more preferably about 0.25 to 5 mm for the non-functionalized, uncalendared nonwoven web. The minimum tensile strength of the nonwoven web is about 4.0 Newtons. It is generally recognized that the tensile strength of nonwovens is lower in the machine direction than in the cross-web direction due to better fiber bonding and entanglement in the latter.

(79) Nonwoven web loft is measured by solidity, a parameter that defines the solids fraction in a volume of web. Lower solidity values are indicative of greater web loft. Useful nonwoven substrates have a solidity of less than 50%, preferably less than 25%. Solidity is a unitless fraction typically represented by a:
α=m.sub.f÷ρ.sub.f×L.sub.nonwoven
where m.sub.f is the fiber mass per sample surface area, which ρ.sub.f is the fiber density; and L.sub.nonwoven is the nonwoven thickness. Solidity is used herein to refer to the nonwoven substrate itself and not to the grafted nonwoven. When a nonwoven substrate contains mixtures of two or more kinds of fibers, the individual solidities are determined for each kind of fiber using the same L.sub.nonwoven and these individual solidities are added together to obtain the web's solidity, α.

(80) As an example, the nonwoven substrate (before calendering or grafting) preferably has an average pore size of 5-50 μm. The term “average pore size” (also known as average pore diameter) is related to the arithmetic median fiber diameter and web solidity and can be determined by the following formula: where D is the average pore size, d.sub.f is arithmetic median fiber diameter, and α is the web solidity.

(81) $D=d_f\left\{{\left(\frac{2\alpha }{\pi }\right)}^{-1/2}-1\right\}$

(82) In some embodiments the nonwoven substrate preferably has a mean pore size of 1-40 microns, preferably 2-20 microns. Mean pore size may be measured according to ASTM F 316-03 “Standard Test Methods for Pore Size Characteristics of Membrane Filters by Bubble Point and Mean Flow Pore Test Method B” using Freon TF™ as the test fluid.

(83) In some embodiments, useful nonwoven webs with have a surface energy of at least 35 dyne/cm, preferably at least 40 dynes/cm, more preferably at least 45 dyne/cm. The surface energy of a substrate may be measured using the Penetrating Drop method, whereby a series of test solutions of increasing surface tension is applied to the samples until a solution of such high surface tension is used that it no longer penetrates the nonwoven web substrate. The critical wetting surface tension of the samples may be measured using Dyne Test Solutions™ available from Jemmco LLC., Mequon Wis. 53092 (general test method disclosed in Journal of Membrane Science, 33 (1987) 315-328 Wetting Criteria For The Applicability of Membrane Distillation). A series of test solutions of increasing surface tension is applied to the samples until a solution of such high surface tension is used that it no longer penetrates the substrate.

(84) In other embodiments the nonwoven web is rendered hydrophobic and/or oleophobic by grafting a fluorine-containing monomer to produce a grafted nonwoven web having a surface energy of <35 dynes/cm.

(85) Other useful hydrophobic monomers include styrene, alkyl (meth)acrylates, fluorinated olefins, fluoroalkyl-containing monomers and fluoro-ether-containing monomers, including poly(hexafluoroproylene oxide) containing monomers.

(86) In some embodiment the nonwoven web has a surface area of 15 to 50 m.sup.2 per square meter of nonwoven substrate

(87) The nonwoven webs useful for practicing the present disclosure can exhibit various degrees of wettability upon exposure to various solutions or solvents. Wettability can often be correlated to the hydrophilic character of the hydrophilic substrate. As used herein, the term “instant wet” or “instant wettability” refers to the penetration of droplets of water into a given substrate as soon as the water contacts the substrate surface, typically within less than 1 second. For example, a surface wetting energy of greater than 30 dynes/cm or larger usually results in wetting. As used herein, the term “no instant wet” refers to penetration of droplets of water into a given substrate but not as soon as the water contacts the substrate surface. As used herein, the term “no wetting” refers to the lack of penetration of droplets of water into a given substrate.

(88) Alternatively, the wettability may be measured by the Wettability Test described herein where the nonwoven web is challenged with an acidic solution, which may be pre-wetted.

(89) In some embodiments the nonwoven web has a Gurley Stiffness of at least about 100 mg, and may have a Gurley Stiffness before pleating of at least about 200 mg, at least about 300 mg, at least about 400 mg, at least about 600 mg or at least about 1000 mg. Gurley Stiffness may be determined using a Model 4171E GURLEY™ Bending Resistance Tester from Gurley Precision Instruments.

(90) Desirably, the nonwoven web is acid stable, and is not degraded when subject to the low pH conditions of the emulsions. Desirably, the fibers of the nonwoven web do not swell in contact with either the acid solutions or the organic solvents used in the process.

(91) Staple fibers may also be present in the web. The presence of staple fibers generally provides a loftier, less dense web than a web of only melt blown microfibers. In some embodiments, no more than about 20 weight percent staple fibers are present, in some embodiments, no more than about 10 weight percent. Such webs containing staple fiber are disclosed in U.S. Pat. No. 4,118,531 (Hauser), incorporated herein by reference.

(92) The nonwoven article may optionally further comprise one or more layers of scrim. For example, either or both major surfaces may each optionally further comprise a scrim layer. The scrim, which is typically a woven or nonwoven reinforcement made from fibers, is included to provide strength to the nonwoven article. Suitable scrim materials include, but are not limited to, nylon, polyester, fiberglass, and the like. The average thickness of the scrim can vary. Typically, the average thickness of the scrim ranges from about 25 to about 100 micrometers, preferably about 25 to about 50 micrometers. The layer of the scrim may optionally be bonded to the nonwoven article. A variety of adhesive materials can be used to bond the scrim to the polymeric material. Alternatively, the scrim may be heat-bonded to the nonwoven.

(93) When used in a SX applications, one or more layers of the nonwoven web may be used, each of which layers may have the same, or different average void or pore size, void volume, degree of polymer grafting, monomer composition of grafted polymer, porosity, tensile strength and surface area. In some embodiments, each subsequent layer may be the same or different. The nonwoven web substrate may be configured in any desirable shape. In some embodiments the nonwoven substrate may be pleated. Pleated grafted nonwoven coalescing elements may be combined as multiple concentric pleated elements. The nonwoven substrate may be wound spirally. Further, the nonwoven substrate may be encapsulated with a porous web to provide support and aid in handling. In SX applications, the nonwoven substrate may be disposed either vertically, or horizontally so long as the fluid may flow therethrough, and with sufficient contact time to effect the coalescence.

(94) In one embodiment, the coalescing element comprises an ungrafted polypropylene nonwoven web.

(95) In one embodiment, the coalescing element comprises an ungrafted nylon web.

(96) In one embodiment, the coalescing element comprises a polypropylene web grafted with a quaternary ammonium monomer.

(97) In one embodiment, the coalescing element comprises a polypropylene web grafted with a sulfonic acid monomer.

(98) In one embodiment, the coalescing element comprises a polypropylene web grafted with a quaternary ammonium monomer and a sulfonic acid monomer.

(99) In one embodiment, the coalescing element comprises a polypropylene web grafted with a poly(ethylene glycol) monomer.

(100) In one embodiment, the coalescing element comprises a polypropylene web grafted with a glycidyl (meth)acrylate monomer.

(101) In one embodiment the coalescing element comprises a polypropylene web grafted with 50-70 pbw N-vinyl pyrrolidone, 20-30 pbw Maptac, and 10-20 pbw AMPS, the total being 100 pbw.

(102) In one embodiment the coalescing element comprises a polypropylene web grafted with 40-60 pbw N-vinyl pyrrolidone, 25-35 pbw glycidyl methacrylate, and 25-35 pbw of a VDM-ethanolamine adduct, the total being 100 pbw.

(103) In one embodiment the coalescing element comprises a polypropylene web grafted with N-vinyl formamide.

(104) In one embodiment the coalescing element comprises a polypropylene web grafted with 40-60 pbw N-vinyl pyrrolidone, 20-30 pbw glycidyl methacrylate, and 5-20 pbw of a hydroxyethylacrylamide, the total being 100 pbw.

(105) In one embodiment the coalescing element comprises a polypropylene web grafted with N-vinyl pyrrolidone.

(106) In one embodiment the coalescing element comprises a polypropylene web grafted with 20-30 pbw N-vinyl pyrrolidone, 20-30 pbw glycidyl methacrylate, and 40-60 pbw AMPS, the total being 100 pbw.

(107) In one embodiment the coalescing element comprises a polypropylene web grafted with 30-50 pbw N-vinyl pyrrolidone, 10-20 pbw glycidyl methacrylate, and 40-60 pbw MAPTAC, the total being 100 pbw.

(108) In one embodiment the coalescing element comprises a polypropylene web grafted with 50-70 pbw N-vinyl pyrrolidone, 20-30 pbw MAPTAC, and 10-20 pbw AMPS, the total being 100 pbw.

(109) In one embodiment the coalescing element comprises a polypropylene web grafted with 50-70 pbw N-vinyl pyrrolidone, 20-30 pbw MAPTAC, 10-20 pbw AMPS, and 1 to 10 pbw HFPO-MA, the total being 100 pbw.

(110) In one embodiment the coalescing element comprises a polypropylene web grafted with 40-60 pbw N-vinyl pyrrolidone, 20-30 pbw glycidyl methacrylate, and 20-40 pbw IEM-Agmatine, the total being 100 pbw.

(111) The coalescing elements of the present disclosure desirable will achieve a percent reduction in turbidity of at least 90% (1−initial/final in NTUs) according to the Turbiditity Test measurements. Preferably the reduction is at least 95%, more preferably at least 97%

(112) Suitable materials for housing the coalescing elements have mechanical strength, providing adequate structure to withstand at least a desired rigidity, pressure rating and/or assembly into an industrial setting. Housings may comprise a supporting frame to which is attached one or more layers of the nonwoven web, and which maintain the substantial planar orientation of the nonwoven web (or layers of such nonwoven webs) relative to the flow of the emulsion. In some embodiments, the housing of the coalescing element may be the conventional mixers or settlers used in SX processes. In some embodiments the housing may be the exit pipe for the aqueous and/or the organic solvent streams. The housings may be “pressure-rated” to withstand pressures greater than atmospheric.

(113) In practice, the coalescers or coalescing articles provided herein are included in a system that handles emulsions, particularly acidic emulsions of the SX production of copper. Output of the coalescers may be supplied to any desirable process tank of any purpose that is a part of the overall emulsion handling system, usually a separator tank. Typically, the output of the coalescers, like that of the settling tanks, are recycled into the process streams.

(114) Turning to FIG. 1: In practice, the coalescers or coalescing elements provided herein are included in a solvent exchange system (shown in FIG. 1). The acidic water phase and the organic phase are mixed in the mixer 130. The output flows via a channel or pipe or separating vessel (140) to the settler (160). The phases are allowed to separate in the settler (160). The acidic water phase flows underneath an underflow (170) whereas the organic passes over an overflow (180). From there both liquid streams pass through another channel or pipe or separating vessel (140) to respective holding tanks (190). Embodiments of this disclosure are to locate the coalescing element(s) in the settler (160) and/or in the different channels, pipes or separating vessels (140).

(115) The coalescers may be used in SX applications at locations where emulsions form such as in mixers upstream of settling tanks. Thus, the coalescer would receive flow from one or more mixers. This coalescer could also be positioned at points further downstream or even within the settler. For such applications, it is noted that fouling challenges may be present and there may be a need for ancillary equipment such as a pre-filter upstream of the coalescer.

(116) Coalescence of organic-phase droplets from water or water-phase droplets from organic phase will facilitate operations of downstream equipment in the SX process.

Some Embodiments of the Disclosure

(117) In a first embodiment, the present disclosure provides a method for producing copper, the method comprising:

(118) a) providing an aqueous solution containing copper in dilute acid;

(119) b) contacting the aqueous solution with a solution of lixiviant whereby the copper is extracted by the lixiviant to produce a loaded organic solution;

(120) c) contacting the loaded organic solution with concentrated acid solution to extract the copper from the loaded organic solution into the concentrated acid solution,

(121) wherein at least one of b) or c) provides an emulsion, the method further comprising:

(122) contacting at least one of the loaded organic solution or the concentrated acid solution with a coalescing element comprising a nonwoven web substrate to coalesce droplets in the emulsion.

(123) In a second embodiment, the present disclosure provides the method of the first embodiment wherein at least one of the loaded organic solution or the concentrated acid solution exhibits a percent reduction in turbidity of at least 90% according to the Turbidity Test.

(124) In a third embodiment, the present disclosure provides the method of the first or second embodiment, wherein at least one of the loaded organic solution or the concentrated acid solution exhibits a final turbidity of <100 NTU according to the Turbidity Test.

(125) In a fourth embodiment, the present disclosure provides a method for aggregating droplets of an emulsion comprising an organic phase and an aqueous acidic phase, the method comprising:

(126) contacting a coalescer with a feed of the emulsion wherein the coalescer comprises; a housing; a coalescing element located in the housing, the coalescing element comprising at least one layer of a nonwoven web substrate; and a fluid inlet and a fluid outlet each in fluid communication with the coalescing element, wherein a D.sub.50 droplet particle size in the emulsion is bigger by at least a factor of 3 upon flow out of the fluid outlet relative to the D.sub.50 droplet particle size upon flow into the fluid inlet.

(127) In a fifth embodiment, the present disclosure provides the method of the fourth embodiment, wherein the emulsion comprises a discontinuous organic solvent phase dispersed in a continuous aqueous acidic phase.

(128) In a sixth embodiment, the present disclosure provides the method of the fourth embodiment, wherein the emulsion comprises a discontinuous aqueous acidic phase dispersed in a continuous organic solvent phase.

(129) In a seventh embodiment, the present disclosure provides a method of coalescing droplets in an emulsion, the emulsion comprising:

(130) a continuous aqueous phase having a pH≤5 optionally containing copper ions, and

(131) an organic phase comprising a complex of a lixiviant and copper ions,

(132) the method comprising:

(133) contacting the emulsion with the a nonwoven web substrate.

(134) In an eighth embodiment, the present disclosure provides the method of any one of the fourth to seventh embodiments, wherein the emulsion exhibits a percent reduction in turbidity of at least 90% according to the Turbidity Test after it contacts the nonwoven web substrate.

(135) In a ninth embodiment, the present disclosure provides the method of any one of the fifth to eighth embodiments, wherein the emulsion exhibits a final turbidity of <100 NTU according to the Turbidity Test.

(136) In a tenth embodiment, the present disclosure provides the method of any one of the first to ninth embodiments, wherein the nonwoven web substrate has a tensile strength of at least 4.0 newtons.

(137) In an eleventh embodiment, the present disclosure provides the method of any one of the first to tenth embodiments, wherein the nonwoven web substrate has a surface area of 15 to 50 m.sup.2 per square meter of nonwoven substrate.

(138) In a twelfth embodiment, the present disclosure provides the method of any one of the first to eleventh embodiments, wherein the nonwoven web substrate has a mean pore size of 1 micrometer to 40 micrometers according to ASTM F 316-03 5.

(139) In a thirteenth embodiment, the present disclosure provides the method of any one of the first to twelfth embodiments, wherein the nonwoven web substrate have a solidity of less than 20%.

(140) In a fourteenth embodiment, the present disclosure provides the method of any one of the first to thirteenth embodiments, wherein the nonwoven web substrate comprises at least one of a spunlaid, spunbond, hydroentangled, or a meltblown nonwoven substrate.

(141) In a fifteenth embodiment, the present disclosure provides the method of any one of the first to fourteenth embodiments, wherein the nonwoven web substrate has an effective fiber diameter in a range from 1 micrometer to 40 micrometers.

(142) In a sixteenth embodiment, the present disclosure provides the method of any one of the first to fifteenth embodiments, wherein the nonwoven web substrate has an effective fiber diameter in a range from 1 micrometer to 15 micrometers.

(143) In a seventeenth embodiment, the present disclosure provides the method of any one of the first to sixteenth embodiments, wherein the nonwoven web substrate includes fibers that have different effective fiber diameters.

(144) In an eighteenth embodiment, the present disclosure provides the method of any one of the first to seventeenth embodiments, wherein the nonwoven web substrate is hydrophilic.

(145) In a nineteenth embodiment, the present disclosure provides the method of the eighteenth embodiment, wherein the nonwoven web substrate comprises fibers of inherently hydrophilic polymers.

(146) In a twentieth embodiment, the present disclosure provides the method of the nineteenth embodiment, wherein the inherently hydrophilic polymers are selected from polyamides and poly(vinyl alcohol).

(147) In a twenty-first embodiment, the present disclosure provides the method of the eighteenth embodiment, wherein the nonwoven web substrate comprises a hydrophilic (co)polymer grafted to the surface of the fibers.

(148) In a twenty-second embodiment, the present disclosure provides the method of the twenty-first embodiment, wherein the grafted (co)polymer comprises cationic, anionic or nonionic hydrophilic monomer units.

(149) In a twenty-third embodiment, the present disclosure provides the method of the twenty-first or twenty-second embodiment, wherein the weight of the grafted polymer is 0.5 to 3 times the weight of the nonwoven web substrate.

(150) In a twenty-fourth embodiment, the present disclosure provides the method of any one of the first to twenty-third embodiment, wherein the nonwoven web substrate has a surface energy of at least 35 dyne/cm.

(151) In a twenty-fifth embodiment, the present disclosure provides the method of any one of the first to twenty-third embodiments, wherein the nonwoven web is grafted with a poly(hexafluoropropylene oxide) monomer.

(152) In a twenty-sixth embodiment, the present disclosure provides the method of any one of the first to twenty-third embodiments, wherein the nonwoven web substrate has a surface energy of less than 35 dyne/cm.

(153) In a twenty-seventh embodiment, the present disclosure provides the method of any one of the first to twenty-sixth embodiments, wherein the emulsion further comprises a copper lixiviant complex.

(154) In a twenty-eighth embodiment, the present disclosure provides the method of any one of the first to twenty-seventh embodiments, wherein the nonwoven web is instantly wet according to the Wetting Test.

(155) In a twenty-ninth embodiment, the present disclosure provides the method of any one of the first to twenty-seventh embodiments, wherein the nonwoven web substrate comprises two or more layers of nonwoven webs.

(156) In a thirtieth embodiment, the present disclosure provide the method of the twenty-ninth embodiment, wherein at least two of the two or more layers of nonwoven webs have different effective fiber diameters.

(157) In a thirty-first embodiment, the present disclosure provides a coalescing element comprising a nonwoven web substrate for aggregating droplets of an emulsion comprising an aqueous acidic phase and organic solvent phase, wherein a discontinuous phase is dispersed in an continuous phase, wherein either the organic solvent phase or the aqueous acidic phase may be the continuous phase.

(158) In a thirty-second embodiment, the present disclosure provides use of a nonwoven web substrate as a coalescing element for aggregating droplets of an emulsion comprising an aqueous acidic phase and organic solvent phase, wherein a discontinuous phase is dispersed in an continuous phase, wherein either the organic solvent phase or the aqueous acidic phase may be the continuous phase.

(159) In a thirty-third embodiment, the present disclosure provides the coalescing element or use of the thirty-first or thirty-second embodiment, wherein the nonwoven web substrate has a tensile strength of at least 4.0 newtons.

(160) In a thirty-fourth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-third embodiments, wherein the nonwoven web substrate has a surface area of 15 to 50 m.sup.2 per square meter of nonwoven substrate.

(161) In a thirty-fifth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-fourth embodiments, wherein the nonwoven web substrate has a mean pore size of 1 micrometer to 40 micrometer according to ASTM F 316-03 5.

(162) In a thirty-sixth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-fifth embodiments, wherein the nonwoven web substrate have a solidity of less than 20%.

(163) In a thirty-seventh embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-sixth embodiments, wherein the nonwoven web substrate comprises at least one of a spunlaid, spunbond, hydroentangled, or a meltblown nonwoven web substrate.

(164) In a thirty-eighth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-seventh embodiments, wherein the nonwoven web substrate has an effective fiber diameter in a range from 1 micrometer to 40 micrometers.

(165) In a thirty-ninth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-eighth embodiments, wherein the nonwoven web substrate has an effective fiber diameter in a range from 1 micrometer to 15 micrometers.

(166) In a fortieth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to thirty-ninth embodiments, wherein the nonwoven web substrate includes fibers that have different effective fiber diameters.

(167) In a forty-first embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fortieth embodiments, wherein the nonwoven web substrate is hydrophilic.

(168) In a forty-second embodiment, the present disclosure provides the coalescing element or use of the forty-first embodiment, wherein the nonwoven web substrate comprises fibers of inherently hydrophilic polymers.

(169) In a forty-third embodiment, the present disclosure provides the coalescing element or use of the forty-second embodiment, wherein the inherently hydrophilic polymers are selected from polyamides and poly(vinyl alcohol).

(170) In a forty-fourth embodiment, the present disclosure provides the coalescing element or use of the forty-first embodiment, wherein the nonwoven web substrate comprises a hydrophilic (co)polymer grafted to the surface of the fibers.

(171) In a forty-fifth embodiment, the present disclosure provides the coalescing element or use of the forty-fourth embodiment, wherein the grafted (co)polymer comprises cationic, anionic, or nonionic hydrophilic monomer units.

(172) In a forty-sixth embodiment, the present disclosure provides the coalescing element or use of the forty-fourth or forty-fifth embodiment, wherein the weight of the grafted polymer is 0.5 to 3 times the weight of the nonwoven web substrate.

(173) In a forty-seventh embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to forty-sixth embodiments, wherein the nonwoven web substrate has a surface energy of at least 35 dyne/cm.

(174) In a forty-eighth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to forty-sixth embodiments, wherein the nonwoven web is grafted with a poly(hexafluoropropylene oxide) monomer.

(175) In a forty-ninth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to forty-sixth embodiments, wherein the nonwoven web substrate has a surface energy of less than 35 dyne/cm.

(176) In a fiftieth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to forty-ninth embodiments, wherein the nonwoven web is instantly wet according to the Wetting Test.

(177) In a fifty-first embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fiftieth embodiments, wherein the nonwoven web substrate comprises two or more layers of nonwoven webs.

(178) In a fifty-second embodiment, the present disclosure provides the coalescing element or use of the fifty-first embodiment, wherein at least two of the two or more layers of nonwoven webs have different effective fiber diameters.

(179) In a fifty-third embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fifty-second embodiments, wherein the emulsion comprises a discontinuous organic solvent phase and a continuous aqueous acidic phase.

(180) In a fifty-fourth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fifty-second embodiments, wherein the emulsion comprises a discontinuous aqueous acidic phase and a continuous organic solvent phase.

(181) In a fifty-fifth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fifty-fourth embodiments, wherein the emulsion further comprises a copper lixiviant complex.

(182) In a fifty-sixth embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fifty-fifth embodiments, wherein the emulsion exhibits a percent reduction in turbidity of at least 90% according to the Turbidity Test.

(183) In a fifty-seventh embodiment, the present disclosure provides the coalescing element or use of any one of the thirty-first to fifty-sixth embodiments, wherein the emulsion exhibits a final turbidity of <100 NTU according to the Turbidity Test.

(184) In a fifty-eighth embodiment, the present disclosure provides a coalescing article for aggregating droplets of an emulsion comprising an aqueous acidic phase and organic solvent phase, the coalescing article comprising:

(185) a source of the emulsion;

(186) a coalescer that receives the emulsion, the coalescer comprising: a housing; a coalescing element located in the housing, the coalescing element comprising a nonwoven web substrate; a fluid inlet and a fluid outlet, each in fluid communication with the coalescing element;

(187) and

(188) a process tank that receives flow from the coalescer.

(189) In a fifty-ninth embodiment, the present disclosure provides the coalescing article of the fifty-eighth embodiment, wherein the coalescing element is the coalescing element of any one of the thirty-first to fifty-seventh embodiments.

(190) In a sixtieth embodiment, the present disclosure provides the coalescing article of the fifty-eighth or fifty-ninth embodiment, further comprising a pre-filter that receives the emulsion from the source and supplies a filtered flow to the coalescer.

(191) The following specific, but non-limiting, examples will serve to illustrate the present disclosure.

EXAMPLES

(192) TABLE-US-00001 Material Source Agmatine sulfate Aldrich, Milwaukee, WI 2-isocyanatoethyl 2-methylacrylate Showa Denko KK, Kanagawa, Japan Ethanolamine Alfa Aesar, Ward Hill, MA Vinyldimethylazlactone (VDM)) SNPE, Princeton, NJ 1-Amino-2-propanol Aldrich, Milwaukee, WI 2-Acrylamido-2-methylpropane sulfonic acid 50% solution in Aldrich, Milwaukee, WI water (AMPS) Dioctyl sodium sulfosuccinate (DOS) Alfa Aesar, Ward Hill, MA N-vinyl pyrrilodone (NVP) TCI, Portland, Oregon Glycidal methacrylate (GMA) TCI, Portland, Oregon Methacrylamidopropyltrimethylammonium chloride (MAPTAC)- Aldrich, Milwaukee, WI 50% solution in water Hexafluoropropylene oxide methacrylate (HFPO-MA). “HFPO-MA” refers to the F[CF(CF.sub.3)CF.sub.2O].sub.6.3CF(CF.sub.3)C(O)N(H)CH.sub.2CH.sub.2OC(O)C(CH.sub.3)═CH.sub.2 methacrylic acid ester of an oligomeric hexafluoropropylene oxide alcohol made as described in Preparative Example 3 of US20050137355. N-vinyl formamide (NVF) Aldrich, Milwaukee, WI Hydroxyethyl acrylamide Aldrich, Milwaukee, WI Dimethyhexadecylaminoethyl acrylate bromide (DMHAEABr) Prepared by quaternizing dimethylaminoethyl acrylate. The dimethylaminoethyl acrylate was obtained from Aldrich, Milwaukee, WI
Test Methods

Coalescing Challenge Test

(193) This test is a modification of a published BASF test entitled “Standard Quality Control Test of LIX® Reagents”. The BASF test is a standard quality control test for solvent extraction reagents that form insoluble complexes with various metal cations (LIX® Reagents). The test is used for evaluating non-woven media for the ability to coalesce an organic copper chelate complex entrained in an aqueous continuous phase. The level of entrainment is measured by turbidity [Nephelometric Turbidity Units (NTUs)]. Challenge solution is of sufficient turbidity and stability to maintain a threshhold turbidity of at least 500 NTU for the duration of the test period. The challenge solution is then run through one or more layers of the media held in a filtration funnel and filtered at a slight vacuum. Initial and filtered turbidity as well as the filtration time are recorded.

(194) Reagents

(195) A synthetic copper electrolyte solution was prepared by adding 300 mL (340 grams) of a 20% wt/vol solution of copper sulfate in water (Ricca Chemical Company) to a 1000-mL tri-pour beaker followed by 95 grams of 95-98% sulfuric acid (Sigma Aldrich). Deionized water was then added to the beaker to bring the total volume to 600 mL (685 grams).

(196) A “Loaded Solvent Extraction Organic” was prepared by adding 160 mL of “ORFOM SX 80” hydrocarbon solvents (Chevron Phillips, Woodlands, Tex.) and 40 mL of “LIX 84-I” (2-hydroxy-5-nonylacetophenone oxime in a high flash point hydrocarbon diluent, BASF, Florham Park, N.J.) to a 1000-mL separatory funnel. 200 mL of the previously prepared synthetic copper electrolyte solution was added to the separatory funnel, the funnel was stoppered and shaken for 60 seconds. The 2 phases were allowed to separate for 10 minutes and then the lower aqueous phase was drained off and discarded. The upper organic phase was drained to a 500-mL HDPE bottle.

(197) A “Leach Solution” was prepared by adding 750 mL of deionized water and 75 mL of a 20% (wt/vol) solution of copper sulfate (Ricca Chemical Company) to a 1000-mL Tripour beaker. To this was added 10.0 grams of 95-98% sulfuric acid (Sigma Aldrich, St. Louis, Mo.) and 9.1 grams of iron (III) sulfate pentahydrate (Sigma Aldrich, St. Louis, Mo.). The solution was then stirred for 10 minutes, poured into a 1000-mL volumetric flask and de-ionized water added to the 1000 mL mark.

(198) Procedure

(199) The test vessel used was a baffled, glass mixing vessel fabricated from heavy wall glass tubing 15 cm high by 10 cm wide with a bottom take-off valve made from glass tubing. The walls of the vessel were modified to include 4 baffles that protrude 1 cm into the vessel space. The mixer was a Cole-Parmer Model 04555-25 variable speed mixer with stand. The mixer impeller (3 cm above vessel bottom) was polypropylene (1.75 inches in diameter with 6 slots, 0.125 inches deep and 0.125 inches wide, the top of the hub was 1 cm above the top of the impeller, and the shaft was 316 stainless steel, 10 cm long). 450 of the “Leach Solution” was added to the test vessel followed by 135 ml of the “Loaded Solvent Extraction Organic” (0.3:1 organic: aqueous ratio). The stirrer was started at a preset speed of 2000 rpm and the mixture stirred at that speed for precisely 3 minutes. The stirrer was stopped and phases allowed to separate for 5 minutes. Draining of the lower aqueous phase was begun to a 1000-ml Tripour beaker and after 150-ml of the aqueous phase was drained the draining was stopped and a glass vial was filled for a turbidity sample. The vial challenge solution initial turbidity was measured (“HI 88713” Turbidity Meter, Hanna, Woonscoket, R.I.) and recorded. The rest of the aqueous phase was drained into the Tripour beaker. One or more layers of test nonwoven media (47 mm disc) was placed in a filter holder (500-ml Pall Corporation 47-mm Magnetic Filter Funnel) over a 1000-ml glass KIMAX filtration flask. The flask was attached to a vacuum pump (Barnant Model 400-3901 Vacuum/Pressure Station) operating at 5 mm Hg (667 Pa). 450 ml of the drained challenge solution was added to the filter holder, the vacuum and stopwatch was started and the time for the solution to drain was recorded. A sample of the aqueous phase in the filtration flask was added to a glass vial and the turbidity measured as with the initial sample.

(200) Three different discs (47 mm) and 3 freshly made up solutions were used to test the reproducibility of the “Coalescing Challenge Test”. The media discs were similar to those of Example 7 but of a larger effective fiber diameter. Results below:

(201) TABLE-US-00002 Initial turbidity Final turbidity Filtration time (NTU) (NTU) (sec) 456 132 20 421 143 19 429 139 22

Wetting Test

(202) A single layer of test nonwoven media (47 mm disc) was weighed and then placed in a filter holder (500-ml Pall Corporation 47-mm Magnetic Filter Funnel) over a 1000-ml glass KIMAX filtration flask. The flask was attached to a vacuum pump (Barnant Model 400-3901 Vacuum/Pressure Station) operating at 5 mm Hg (667 Pa). 450 ml of the “Leach Solution” was added to the filter holder, and a vacuum was pulled until all the liquid was filtered (time varied for each solution). The media was removed from the funnel and placed between 2 pieces of filter paper (Whatman #4 filter paper, 7.0 cm) under a 850 g (40 mm wide by 58 mm high) cylindrical weight for 15 seconds to remove excess liquid. The media was then weighed on an analytical balance and the weight recorded. The media was then placed on a piece of dry filter paper (Whatman #4 filter paper, 7.0 cm). A syringe (1 mL Becton Dickenson Luer-Lok) was filled with “Leach Solution” and 10 drops were placed randomly and uniformly (as quickly as possible and all within less than 5 seconds) over the 47 mm nonwoven test disc. A stopwatch was immediately started when the last drop was placed and the time recorded until all 10 drops had completed wetted out on the nonwoven. If the drops wetted in less than one second it was recorded as “instant wetting” or “I” as recorded in Table 2. If the drops had still not wetted after 300 seconds it was simply recorded as >300 in Table 2. The test was repeated exactly the same way for each test piece of nonwoven using 10 drops of “Loaded Solvent Extraction Organic”. Results are in Table 2 where “A” refers to wet time for the aqueous “Leach Solution” and “0” refers to the organic “Loaded Solvent Extraction Organic” solution.

(203) Three different discs (47 mm) were used to test the reproducibility of the “Wetting Test”. The media discs were those of Example 18. Results below:

(204) TABLE-US-00003 Aqueous wetting Organic wetting time (sec) time (sec) Initial weight (g) Wet weight (g) A O 0.4584 0.9369 67 <5 0.5194 1.1468 54 <5 0.4831 1.1426 75 <5
Nonwoven Preparation
Polypropylene (PP) Nonwoven

(205) The polypropylene nonwoven was made by a meltblown process, which was formed by extruding the molten thermoplastic material (“3860X” polypropylene homopolymer from Total Petrochemicals, Houston, Tex.) through a plurality of fine, die capillaries as molten threads or filaments into a high velocity, usually heated gas stream which attenuates the filaments of molten thermoplastic material to reduce their diameter. Thereafter, the meltblown fibers are carried by a high velocity gas stream and are deposited on a collecting surface to form a web of randomly disbursed meltblown fibers. The microfibers of the nonwoven substrate had an effective fiber diameter (EFD) of 4.5 or 10.7 micrometers with respective basis weights of 60 or 90 g/m.sup.2 respectively.

(206) PET Nonwoven

(207) The PET polyester spunbond fiber web was purchased from Reemay, under the tradename “REEMAY 2033” from Fiberweb Filtrations, Old Hickory, Tenn. The nonwoven had an EFD of 23.2 microns and a basis weight of 102 g/m.sup.2.

(208) Polylactic Acid Nonwoven

(209) The polylactic acid nonwoven was made by a meltblown process as described for “Polypropylene (PP) Nonwoven” but using “INGEO 6252D” pellets (Natureworks LLC, Minnetonka, Minn.). The web had an EFD of 12.4 microns and basis weight of 40 g/m.sup.2.

(210) “B-24” Nylon Nonwoven

(211) “B-24” nylon-6 polymer (BASF Corporation Engineering Plastics Wyandotte, Mich.) was used to produce meltblown nonwoven substrate. The melt temperature was 295° C. with a mass flow rate of 0.25 grams/hole/minute on a standard meltblowing drilled orifice die. Hot air at 350° C. and 975 cubic feet per minute (SCFM) (27.8 cubic meters per minute (CMM)), per meter of die width, was used to attenuate the fibers. The fibers with a face velocity at impact of 1200 meters per minute (m/min) were collected 0.30 meters from the die on a foraminous stainless steel belt and were bonded under 200° C. air drawn through the web at a face velocity of 137 m/min for 0.14 seconds, followed by cooling air at 29° C., at the same face velocity, for 0.8 seconds. The collected web had a thickness of 0.4 mm before calendaring between two 25 cm diameter smooth steel rolls set at 82° C., running at 1.5 m/min with a nip pressure of 170 Newtons per lineal centimeter of web (N/lcm). The resulting web thickness was 0.25 mm. The collected web basis weight was 48 g/m.sup.2 and the web had an EFD of 4.1 microns.

(212) PET/Copolyolefin/Glass Microfiber

(213) 20% by weight “TREVIRA 255” core sheath bicomponent polyethylene terephthalate(PET)/copolyolefin fiber (Trevira, Bobingen, Germany) and 80% by weight “100 CX Micro-Strand Glass Microfiber” staple fiber (Johns Manville, Denver, Colo.) were used to make a nonwoven. The web basis weight was 200 g/m.sup.2. The glass microfiber BET fiber diameter was 5.5 microns per manufacturer specs.

(214) Polymer Preparation

(215) VDM-Ethanolamine (2-Aminoethanol Adduct of Vinyldimethylazlactone (VDM))

(216) VDM was dissolved in ethyl acetate (1 gram/20 mL) in a round bottomed flask and the mixture was stirred magnetically at 20° C. One equivalent of 2-aminoethanol was added by syringe and within 10 minutes a copious colorless precipitate formed. Stirring was continued for a total of 30 minutes and then diethyl ether (20 mL) was added. The solid was filtered, washed with diethyl ether (20 mL), and dried. Yield, approximately 85%. .sup.1H-NMR (D.sub.2O): δ 1.34 (s, 6H), 3.19 (t, 2H), 3.48 (t, 2H), 5.62 (d, 1H), 6.06 (d, 1H), 6.13 (dd, 1H).

(217) IEM-Agmatine (4-(2-(Methacryloyloxy)Ethylamino)Butyl Guanidinium Sodium Sulfate)

(218) Agmatine sulfate (100 g, 397 mmol) was dissolved in 400 mL of aqueous 1.00 N NaOH. Acetone (200 mL) was then added and the stirred mixture was cooled to 10° C. in a cold water bath. An additional 80 mL of water was added to keep the agmatine sulfate in solution. 2-Isocyanatoethyl 2-methylacrylate (58.0 mL, 411 mmol) was then added to the reaction mixture, via an addition funnel, over a period of 30 min. After stirring an additional 45 min, the reaction mixture was placed on a rotary evaporator at 20° C. After pulling off most of the acetone, the reaction mixture was transferred to a separatory funnel and washed with ethyl acetate (2×250 mL) and methylene chloride (2×200 mL). The remaining aqueous solution was adjusted to pH 7 by addition of a small amount of dilute sulfuric acid and then placed on a rotary evaporator at 20° C. to draw off any remaining volatiles. Lyophilization yielded the title compound (162 g) as a white powder. .sup.1H NMR (500 MHz, D.sub.2O) □ 6.14 (s, 1H), 5.73 (s, 1H), 4.23 (t, J=5.2 Hz, 2H), 3.45 (t, J=5.4 Hz, 2H), 3.18 (t, J=7.0 Hz, 2H), 3.12 (t, J=6.4 Hz, 2H), 1.22 (s, 3H), 1.61-1.48 (m, 4H).

(219) Electron Beam Grafting Procedure

(220) The nonwoven substrate was cut into a 12″×17″ (30 cm×46 cm) sheet (8.0 g for 0 60 g/m.sup.2 web and 13.5 g for 90 g/m.sup.2 web) and purged of oxygen in a nitrogen inerted glovebox (<50 ppm O.sub.2). The inerted substrate was place in a sealed plastic bag, before removing from the glovebox. The inerted substrate in the sealed bag was conveyed through the beam on a web carrier. The irradiations were done on an ESI CB-300 electron beam (ESI “ELECTROCURE” EB SYSTEM from Energy Sciences, Inc., Wilmington, Mass.), at an accelerating voltage of 300 keV delivering a dose of 50 kGy using the monomers shown in Table 1 (except that Examples 1-4 and 19 did not use electron beam radiation and were ungrafted nonwovens). After irradiation the sealed bags were brought back into the nitrogen purged glovebox, opened and imbibed with the monomer solution, with the composition shown in Table 1. The coated substrate was allowed to react overnight (>14 hours) in the purged glovebox. The nonwoven samples were then removed from the bag and rinsed with water using a vacuum plate to pull the water through and allowed to air dry. The air dried sheet was weighed to determine grafting efficiency of the available monomer. The nonwoven samples were then “blanched” in boiling water for one hour. The samples are then cooled by placing them in a water tray and again air dried. Dry 47 mm disks were punched out of the nonwoven sheets and used for testing. Table 3 indicates the weight of grafted polymer which was obtained by subtracting the initial dry ungrafted web weight from the final dry grafted web weight.

EXAMPLES

(221) Example 1 is an ungrafted 4.5 effective fiber diameter (EFD in microns), 90 g/m.sup.2 polypropylene web, shown in Table 2, made via the melt-blown process described under “Polypropylene Nonwoven”.

(222) Example 2 is an ungrafted 4.5 EFD, 50 g/m.sup.2 nylon web, shown in Table 2, made via melt-blown process described under “B-24” Nylon Nonwoven.

(223) Example 3 is an ungrafted 23.2 EFD, 102 g/m.sup.2 polyethyleneterephthalate (PET) spunbond web described under “PET Nonwoven”.

(224) Example 4 is an ungrafted 12.4 EFD, 40 g/m.sup.2 polylactic acid web described under “Polylactic Acid Nonwoven”.

(225) Example 5 used a 10.7 EFD, 60 g/m.sup.2 polypropylene web, shown in Table 2 made via the melt blown process described under “Polypropylene Nonwoven”. The monomers (Table 2) were then covalently reacted (grafted) to the surface of the nonwoven as described under “ELECTRON BEAM GRAFTING PROCEDURE”.

(226) Example 6 was identical to Example 5 but used a 4.5 EFD polypropylene fiber.

(227) Examples 7-17 all used the 4.5 EFD polypropylene fiber of Example 1 with either 60 or 90 g/m.sup.2 as shown in Table 2. All these examples were grafted with electron beam radiation as described under “ELECTRON BEAM GRAFTING PROCEDURE”.

(228) TABLE-US-00004 TABLE 1 Electron Beam Grafting Solution Compositions Water DOS NVP NVF GMA MAPTAC AMPS Other monomers EX5 59.7 0.30 9.00 0 0 3.90 2.10 0 EX6 59.7 0.30 9.00 0 0 3.90 2.10 0 EX7 81.4 0 11.7 0 4.85 0 0 VDM-ethanol- amine 7.05 EX8 63.7 0.30 0 16 0 0 0 0 EX9 80.9 0 11.7 0 5.20 0 0 Hydroxyethyl- acrylamide 7.20 EX10 63.7 0.3 16 0 0 0 0 0 EX11 43.0 0 8.00 0 8.00 0 16.0 0 EX12 74.5 0 11.7 0 4.70 14.1 0 0 EX13 46.8 0 8.00 0 9.00 7.80 4.20 HFPO-MA 0.25 EX14 59.2 0.30 9.00 0 0 3.90 2.10 EX15 58.7 0.30 9.00 0 0 3.90 2.10 HFPO-MA 1.00 EX16 57.7 0.30 9.00 0 0 3.90 2.10 HFPO-MA 1.00 EX17 81.6 0 11.7 0 4.70 0 0 IEM- agmatine 7.05 EX18 51 0 8.00 8.00 0 0 0 DMHAEABr 8.00

(229) TABLE-US-00005 TABLE 2 Nonwoven Characterization and Test Results Wet time Filter EFD (A/O) Start End time Nonwoven Description micron g/m2 (sec) # discs NTU NTU (sec) EX1 Ungrafted Polypropylene 4.5 90 >300/I 2 716 43  26 (PP) EX2 Ungrafted Nylon (B24) 4.5 50 I/I 3 566 11  24 EX3 Ungrafted PET 23.2 102 I/I 4 635 148   7 EX4 Ungrafted Polylactic 12.4 40 >300/I 3 738 381   7 acid (6) (743) (282)  (10) EX5 PP grafted with 10.7 60 I/I 2 601 65   9 NVP, MAPTAC, AMPS EX6 PP grafted with 4.5 60 I/I 2 798 12  72 NVP, MAPTAC, AMPS EX7 PP grafted with NVP, 4.5 90 I/I 2 740 6 29 GMA, VDM- ethanolamine EX8 PP grafted with NVF 4.5 60 NM 2 696 3 31 EX9 PP grafted with NVP, 4.5 90 I/I 1 717 3 57 GMA, hydroxyethylacrylamide EX10 PP grafted with NVP 4.5 60 I/I 2 681 15  37 EX11 PP grafted with NVP, 4.5 60 I/I 2 700 8 118  GMA, AMPS EX12 PP grafted with 4.5 90 NM 1 578 5 149  NVP, GMA, MAPTAC EX13 PP grafted with 4.5 60 I/I 1 775 7 33 NVP, GMA, MAPTAC, AMPS, 0.25 HFPO-MA EX14 PP grafted with 4.5 60 NM 2 681 5 16 NVP, GMA, MAPTAC, AMPS, 0.50 HFPO-MA EX15 PP grafted with 4.5 60 NM 2 753 8 19 NVP, GMA, MAPTAC, AMPS, 1.0 HFPO-MA EX16 PP grafted with 4.5 60 NM 2 736 5 39 NVP, GMA, MAPTAC, AMPS, 2.0 HFPO-MA EX17 PP grafted with IEM- 4.5 90 I/I 2 785 8 57 agmatine EX18 PP grafted with 60 67/I 2 663 16  67 DMHAEABr EX19 PET/Copolyolefin/Glass 200 I/I 1 602 90  29 Microfiber “# discs” refers to the # of 47 mm nonwoven discs used in the “Coalescing Challenge Test” Basis weights (g/m.sup.2) were all calculated according to the method set forth in Davies, C. N., “The Separation of Airborne Dust and Particles,” Institution of Mechanical Engineers, London, Proceedings 1B, 1952.

(230) TABLE-US-00006 TABLE 3 Electron Beam Grafting Results Weight of % grafted monomer Nonwoven Description polymer (g) grafted EX1 Ungrafted Polypropylene (PP) 0 0 EX2 Ungrafted Nylon (B24) 0 0 EX3 Ungrafted PET 0 0 EX4 Ungrafted Polylactic acid 0 0 EX5 PP grafted with NVP, MAPTAC, AMPS 6.60 100 EX6 PP grafted with NVP, MAPTAC, AMPS 12.7 100 EX7 PP grafted with NVP, GMA, VDM- 23.7 100 ethanolamine EX8 PP grafted with NVF 11.6 73 EX9 PP grafted with NVP, GMA, 27.4 92 hydroxyethylacrylamide EX10 PP grafted with NVP 8.40 87 EX11 PP grafted with NVP, GMA, AMPS 24.8 100 EX12 PP grafted with NVP, GMA, MAPTAC 29.5 100 EX13 PP grafted with NVP, GMA, MAPTAC, 22.3 99 AMPS, 0.25 HFPO-MA EX14 PP grafted with NVP, GMA, MAPTAC, 11.1 89 AMPS, 0.50 HFPO-MA EX15 PP grafted with NVP, GMA, MAPTAC, 12.0 92 AMPS, 1.0 HFPO-MA EX16 PP grafted with NVP, GMA, MAPTAC, 7.5 93 AMPS, 2.0 HFPO-MA EX17 PP grafted with IEM-agmatine 30.1 100 EX18 PP grafted with DMHAEABr 28.8 100 EX19 PET/Copolyolefin/Glass Microfiber 0 0

(231) For the following Examples 20 to 27, nonwoven disc substrates having effective fiber diameters (EFD) of 27 micrometers, 14 micrometers, 8 micrometers, and 38 micrometers were made from polypropylene according to the Nonwoven Preparation method “Polypropylene (PP) Nonwoven” described above. The “B-24” Nylon Nonwoven was also used for some of the Examples, below. The designation “p” in Table 4, below, indicates that the “B-24” Nylon Nonwoven and the 8-micrometer-EFD polypropylene nonwoven discs were manually punched with an 18 gauge needle. To perform the hole punching, the 18 gauge needle was first passed through the flame of a Bunsen burner, and then the needle was punched through the nonwoven disc. For the “B-24” nylon nonwoven disc designated “4p”, 40 holes were made in the disc. For the 8-micrometer-EFD polypropylene nonwoven disc designated “8p”, nine holes were made in the disc.

(232) In Table 4, below, more than one nonwoven disc was used. The “Media Configuration” describes the number of nonwoven discs, the EFD of the nonwoven in the discs, and the arrangement of the discs used for each Example. The numbers in parenthesis indicate the results from a duplicate test.

(233) TABLE-US-00007 TABLE 4 Nonwoven Characterization and Test Results Media Configuration: # Filter time Layers × EFD in micrometers Pass # (sec) NTU EX20 2 × 27, 2 × 14, 1 × 8, 1 × 8 0 536 1 33 20.6 2 26 11.0 3 24 7.5 EX21 2 × 27, 2 × 14, 1 × 8, 2 × 27, 0 568(571) 2 × 14, 1 × 8 1 30(34) 12.8(16.6) 2 26(30) 8.8(9.6) 3 26(28) 5.4(6.6) EX3 2 × 27, 2 × 27, 2 × 14, 2 × 14, 0 780 1 × 8, 1 × 4 p 1 35(29) 4.0(5.9) 2 35(31) 3.5(3.5) EX4 2 × 27, 2 × 27, 2 × 14, 2 × 14, 0 735 1 × 8 p, 1 × 4 p 1 22 14.2 2 22 6.5 EX5 2 × 27, 2 × 14, 1 × 8, 1 × 4 p 0 641 1 24 13.2 2 21 6.5 EX6 9 × 38 0 371 1 14 144 2 13 102 3 13 70 EX7 2 × 27, 2 × 14, 1 × 8, 1 × 8 0 536 1 33 20.6 2 26 11.0 3 24 7.5 EX8 2 × 27, 2 × 14, 1 × 8, 2 × 27, 0 568 2 × 14, 1 × 8 1 30 12.8

(234) This disclosure is not limited to the above-described embodiments but is to be controlled by the limitations set forth in the following claims and any equivalents thereof. This disclosure may be suitably practiced in the absence of any element not specifically disclosed herein.