THERMOPLASTIC MATERIALS HAVING BENEFICIAL PROPERTIES AND PROCESSES FOR PROVIDING THE SAME

Abstract

Methods of providing sustained sterilization of thermoplastics; providing thermoplastics that have the capacity to dispense sodium fluoride, and, a method of providing sustained sterilization of thermoplastics and providing thermoplastics that have the capacity to dispense sodium fluoride, both from the same thermoplastic article.

Claims

1. A composition of matter provided by a method of providing a thermoplastic material, said method comprising: a. providing a hydrolyzate of a silane having the general formula:
(RO).sub.3Si(CH.sub.2)nN.sup.+(R′).sub.2(R″)Cl.sup.− wherein R is an alkoxy group having 1 to 4 carbon atoms, n has a value of 3 to 8, each R′ is selected from alkyl groups having 1 to 4 carbon atoms, and R″ is the radical —(CH.sub.2)mCH.sub.3Cl.sup.− wherein m has a value of 12 to 20; b. coating particulates of a thermoplastic with said hydrolyzate; c. heating and drying said coated particulate thermoplastics to yield dry coated thermoplastic particulates; d. providing said coated thermoplastic particulates as feedstock for providing a thermoplastic material by a process selected from the group consisting of: i. melt-spinning, and ii. injection molding; wherein said thermoplastic material reduces the growth of bacteria or micro-organisms.

2. The composition of matter of claim 1, wherein said composition of matter is at least one of a fiber material and a bristle for a brush.

3. An article manufactured from the composition of matter of claim 1.

4. The article of claim 3, wherein said article is at least one of a toothbrush and a woven mesh.

5. A method of providing thermoplastics having the capacity to dispense sodium fluoride, said method comprising: a. adding a desired amount of sodium fluoride to water to form a solution; b. coating particulate thermoplastics with said solution; c. thereafter heating and drying said coated particulate thermoplastics; d. providing said coated particulate thermoplastics as feedstock for a process selected from: i. melt-spinning, and ii. injection molding.

6. The method of claim 5, wherein said feedstock for providing thermoplastic product is a coated particulate thermoplastic material.

7. The method of claim 5, wherein said feedstock for providing thermoplastic product further comprises an amount of uncoated particulate thermoplastic material.

8. The method of claim 5, wherein said coated particulate thermoplastic material is mixed with an additional thermoplastic material that is not the same as said coated particulate thermoplastic material.

9. The method of claim 5, wherein said coating is provided by spraying said solution onto said particulate thermoplastic while agitating said particulate thermoplastic; and/or wherein said coating is provided by adding said solution to said particulate thermoplastic while agitating said particulate thermoplastic.

10. The method of claim 5, wherein said coating is provided by adding said solution to said particulate thermoplastic while agitating said particulate thermoplastic.

11. The method of claim 5, wherein said thermoplastic particulate is nylon.

12. A composition of matter provided by the process of claim 5.

13. The composition of matter of claim 12, wherein said composition of matter is at least one of a fiber material and a bristle for a brush.

14. An article manufactured from the composition of matter of claim 12.

15. The article of claim 14, wherein said article is at least one of a toothbrush and a woven mesh.

16. A method of providing a thermoplastic material, said method comprising: a. providing a hydrolyzate of a silane having the general formula:
(RO).sub.3Si(CH.sub.2)nN.sup.+(R′).sub.2(R″)Cl.sup.− wherein R is an alkoxy group having 1 to 4 carbon atoms, n has a value of 3 to 8, each R′ is selected from alkyl groups having 1 to 4 carbon atoms, and R″ is the radical —(CH.sub.2)mCH.sub.3Cl.sup.− wherein m has a value of 12 to 20; b. adding a desired amount of sodium fluoride solution to said hydrolyzate; c. coating particulates of a thermoplastic with said hydrolyzate containing said sodium fluoride; d. heating and drying said coated particulates to yield dry coated particulates of thermoplastic material; e. providing said coated thermoplastic particles as feedstock for providing a thermoplastic material by a process selected from the group consisting of: i. melt-spinning, and ii. injection molding; wherein said thermoplastic material reduces the growth of bacteria or micro-organisms; and wherein thermoplastic material has the capacity to dispense sodium fluoride.

17. A composition of matter provided by the process of claim 16.

18. The composition of matter of claim 17, wherein said composition of matter is at least one of a fiber material and a bristle for a brush.

19. An article manufactured from the composition of matter of claim 17.

20. The article of claim 19, wherein said article is at least one of a toothbrush and a woven mesh.

Description

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

[0022] The accompanying drawings are incorporated herein as part of the specification. The drawings described herein illustrate embodiments of the presently disclosed subject matter, and are illustrative of selected principles and teachings of the present disclosure. However, the drawings do not illustrate all possible implementations of the presently disclosed subject matter, and are not intended to limit the scope of the present disclosure in any way.

[0023] FIG. 1 shows release of fluoride from nylon coupon.

DETAILED DESCRIPTION OF EMBODIMENTS

[0024] It is to be understood that the presently described subject matter may assume various alternative orientations and step sequences, except where expressly specified to the contrary. It is also to be understood that the specific devices, assemblies, systems and processes illustrated in the attached drawings, and described in the following specification are simply exemplary embodiments of the inventive concepts defined herein. Hence, specific dimensions, directions or other physical characteristics relating to the embodiments disclosed are not to be considered as limiting, unless expressly stated otherwise. Also, although they may not be, like elements in various embodiments described herein may be commonly referred to with like reference numerals within this section of the application.

[0025] What has been discovered is a method that allows for solventless incorporation of silanes into thermoplastics during the melting of the thermoplastic without scorching of the thermoplastic part. Furthermore, this method also results in thermoplastic parts that demonstrate substantial antimicrobial activity for incorporation of silanes that are also proven to demonstrate antimicrobial activity.

[0026] An aqueous solution of a silane is prepared and allowed sufficient time with appropriate pH adjustment and dilution to achieve a solution or dispersion of completely hydrolyzed silane (hydrolyzate)

[0027] The silanes can be purchased from Dow Corning Corporation, Midland, Mich. and consist of silanes such as (R0).sub.3Si(CH.sub.2) n-N.sup.+ (R′).sub.2 (R″) Cl.sup.− wherein R is an alkoxy group having 1 to 4 carbon atoms, n has a value of 3 to 8, each R′ is selected from alkyl groups having 1 to 4 carbon atoms, and R″ is the radical —(CH.sub.2)mCH.sub.3Cl.sup.− wherein m has a value of 12 to 20. Preferred silanes are those having methoxy groups or ethoxy groups and an alkyl radical wherein m is 14 to 20, most preferred are methoxy groups and m equal to 18.

[0028] Such a molecule is (CH.sub.3 0).sub.3Si(CH.sub.2).sub.3N.sup.+ (CH.sub.3).sub.2(C.sub.18H.sub.37) Cl.sup.−

[0029] The hydrolyzate is then applied to a particulate thermoplastic such as pellets, or chips, and this can be accomplished in at least two ways. One method is to spray coat the particulates while agitating them in a container and the other way is to simply immerse the particulate thermoplastics into the hydrolyzate, both at room temperature.

[0030] The coated beads are then subjected to mild heat and drying to yield dry coated particulates. The dried coated particulates can then be used as is in a melt spinning operation or in injection molding. The heat and drying can be accomplished by forced hot air with the aid of an oven, a vacuum oven, a forced hot air dryer, or a coating machine capable of forced hot air drying, with drying occurring until further drying causes no significant loss of mass, insuring removal of the water.

[0031] It is believed that the unexpected success of this method (incorporation of the silane without scorching and survival of antimicrobial activity of the extruded or molded part despite the high temperatures involved in melting the thermoplastic) is due to the use of aqueous solutions of application of the silane to the particulate thermoplastics and the use of low heat when drying.

[0032] Additionally, we have discovered that soaking the final thermoplastic part in ambient water allows for a release of sodium fluoride into aqueous solution.

[0033] The compositions are useful for providing articles that are antimicrobial in nature. The compositions are also useful for delivering sodium fluoride, such as, for example, from toothbrush bristles while brushing teeth. It is also contemplated that the compositions would be useful for other brush configurations and as a woven mesh, for example in the application of clarifying and sterilizing water for drinking.

[0034] Examples of thermoset plastics that are useful in this presently described subject matter include, for example, nylon, acrylic, polyurethanes, ethylene vinyl acetate. Especially useful are polyurethane polyesters and nylon.

[0035] Dental retainers are manufactured from acrylic resin thermoplastics, aligners used for movement of teeth are manufactured from polyurethane thermoplastics, boil-and-bite mouth guards are manufactured from ethylene vinyl acetate thermoplastics, mouth guards are injection molded from thermoplastics, and elastomeric orthodontic ligatures are manufactured from polyester polyurethanes.

[0036] Antimicrobial active Mouth guards used by children, especially children with braces, is a huge need as mouth guards get dirty pretty easily and children with braces more commonly have exposed cuts which presents a greater risk of infection.

EXAMPLES

[0037] The following examples illustrate the inventive method and are not meant to be limiting in any way to the general method outlined Supra, nor are the percentages of components indicated meant to be limiting, but are only illustrative.

[0038] The source of the silane was Dow Corning 5772, a 72% solution of 3-(trimethoxysilyl) propyldimethyl-octadecyl ammonium chloride in methanol. From this, a stable pH 9-10 3.6% solution of 3-(trihydoxysilyl) propyldimethyloctadecyl ammonium chloride (hydrolyzate) was prepared via 24 hour hydrolysis via aqueous dilution and addition of NaOH, with methanol removed via vacuum stripping. This was a clear pale orange solution upon formation (marketed by QuadSil Inc., Midland, Mich. as QS72-5), but became a stable milky dispersion upon standing for many weeks. Either form was successfully employed for proof of concept. Addition of sodium fluoride from 0.8-2.0% by mass rapidly converted both the solution and the dispersion to a stable gel.

Example 1

[0039] QuadSil QS72-5 (124.15 g) was combined and stirred with 1.035 g NaF to yield a stable gel.

Example 2

[0040] BASF Ultramid 8202 Polyamide 6 (Nylon 6) (10.0 g of approx. 3 mm diameter pellets) were coated with a total of 4.488 g of gel from Example 1 in a Pyrex® beaker and then stirred and dried while heating on a hot plate (>300° C.) and with the aid of a hot air gun. The result was a dry whitish coating on the pellets. Note that such heating and drying could also be accomplished using an oven or a coating machine typically used to coat tablets and candies. The dried coating represented 1.79% of the total mass of the coated pellets (1.45% 3-(trihydoxysilyl) propyldimethyloctadecyl ammonium chloride (hydrolyzate); 0.34% NaF). Approximately 20 pellets were placed in an aluminum weigh boat and heated on a hot plate (cycling between 324-353° C.) to melting while being stirred with a stainless steel spatula, which was subsequently used to press a flat coupon. The coupon, upon cooling, demonstrated no visible scorching. Coupons were also prepared in a similar manner using uncoated pellets.

Example 3

[0041] Bayer Texin® 285 aromatic (20.4 g of approx. 3 mm diameter pellets) were coated with a total of 10.105 g of gel from Example 1 in a Pyrex beaker and then stirred and dried while heating on a hot plate (>300° C.) and with the aid of a hot air gun. The result was a dry whitish coating on the pellets. Note that such heating and drying could also be accomplished using an oven or a coating machine typically used to coat tablets and candies. The dried coating represented 1.23% of the total mass of the coated pellets (1.05% 3-(trihydoxysilyl) propyldimethyloctadecyl ammonium chloride (hydrolyzate); 0.18% NaF). Approximately 20 pellets were placed in an aluminum weigh boat and heated on a hot plate (cycling between 324-353° C.) to melting while being stirred with a stainless steel spatula, which was subsequently used to press a flat coupon. The coupon, upon cooling, demonstrated no visible scorching. Coupons were also prepared in a similar manner using uncoated pellets.

Example 4: Antimicrobial Activity Evaluation of Treated Nylon and Polyurethane Thermoplastics

[0042] Antimicrobial activity employing Staphylococcus aureus was performed using Shake Test ASTM Method E2149-10 and samples Example 2 and 3. The results are presented in Table I.

TABLE-US-00001 Two Hour |Material Avg. CFU/ml % Reduction Bacteria Control 3.32 × 10.sup.5 Not applicable Untreated Ultramid 8202 Nylon 6 1.32 × 10.sup.5 60 Untreated Texin 286 1.76 × 10.sup.5 47 Polyurethane Example 2 coupon  1.2 × 10.sup.4 96 Example 3 coupon 1.32 × 10.sup.5 60 Four Hour Material Avg. CFU/ml % Reduction Bacteria Control 3.08 × 10.sup.5  Not applicable Untreated Ultramid 8202 Nylon 6 2.8 × 10.sup.5 9 Untreated Texin 286 2.64 × 10.sup.5  14 Polyurethane Example 2 coupon 8.0 × 10.sup.3 97 Example 3 coupon 2.4 × 10.sup.4 92

Example 5

[0043] QuadSil QS72-5 (49.04 g) of was combined and stirred with 1.00 g NaF to yield a stable gel.

Example 6

[0044] BASF Ultramid® 8202 Polyamide 6 (Nylon 6) (20.30 g of approx. 3 mm diameter pellets) were coated with a total of 8.56 g of gel from Example 5 in a Pyrex beaker and then stirred and dried while heating on a hot plate (>300° C.) and with the aid of a hot air gun. The result was a dry whitish coating on the pellets. Note that such heating and drying could also be accomplished using an oven or a coating machine typically used to coat tablets and candies. The dried coating represented 1.65% of the total mass of the coated pellets.

[0045] Additional uncoated BASF Ultramid 8202 Polyamide pellets (14.78 g) were added to the coated pellets. This yielded a batch of pellets that were 99.04% Nylon, 0.61% 3-(trihydoxysilyl) propyldimethyl-octadecyl ammonium chloride (hydrolyzate), and 0.35% NaF. Approximately 2 g of pellets were placed in a circular aluminum weigh boat (50 mm diameter) and heated on a hot plate (approx. 380° C.) to melting while pressing down on the pellets with the flat end of a Pyrex beaker (while rotating the beaker to simulate stirring of the melt) for 2.5 minutes, to yield a 0.8 mm thick flat coupon. The coupon, upon cooling, demonstrated no visible scorching. Coupons were also prepared in a similar manner using uncoated pellets.

Example 7

[0046] A 1.024 g circular coupon (0.8 mm thick, 43 mm diameter; 99.04% Nylon, 0.61% 3-(trihydoxysilyl)propyldimethyloctadecyl ammonium chloride (hydrolyzate), and 0.35% NaF) trimmed from an Example 6 coupon, was placed into a 300 mL beaker along with a magnetic stir bar and 200.0 g of RO water. The beaker was covered to prevent evaporation and the contents were stirred. Fluoride concentration was measured with a fluoride selective electrode as a function of time. The results are plotted in FIG. 1.

Example 8: Antimicrobial Activity Evaluation of Treated Nylon

[0047] Antimicrobial activity employing Staphylococcus aureus and Escherichia coli was performed using Test JIS Z 2801 “Antimicrobial Products—Test for antimicrobial activity and efficacy” and samples from Example 6. The bacteria were in direct contact with the test material and covered with a coverslip in a humidity chamber for specified time points, then neutralized, dilutions made and plated out. The results are presented in Tables II and III.

TABLE-US-00002 TABLE II (Staphylococcus aureus) - Sixty Minute Time Point Material Average CFU/ml % Reduction Log Reduction Control 3.23 × 10.sup.4 Not applicable Not applicable Treated  3.3 × 10.sup.1 99.9 3

TABLE-US-00003 TABLE III (Escherichia coli) - Sixty Minute Time Point Material Average CFU/ml % Reduction Log Reduction Control 2.56 × 10.sup.4 Not applicable Not applicable Treated 5.67 × 10.sup.3 77.9 0.6

[0048] While various embodiments of the presently disclosed subject matter have been described above, it should be understood that they have been presented by way of example, and not limitation. It will be apparent to persons skilled in the relevant arts that the disclosed subject matter may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The embodiments described above are therefore to be considered in all respects as illustrative, not restrictive.