Method and Apparatus for Production of Cellulose Based Fuel Pellets

Abstract

A method and apparatus for production of cellulose based fuel pellets from wood logs includes steps of comminuting the wood logs to particulate wood material. The particulate material heat treated in a reactor and the pressure is reduced in a manner causing defibration of the particulate material. The material is pelletized using the softened lignin at least partially as a binder for the pellets. The comminution of the wood logs is effected as a single-step operation in which the wood logs are charged to a comminution station where at least one rotating drum provided with cutting teeth is arranged in a manner to fully comminute the wood logs. The particulate material may be fractioned and a selected size fraction used for the further treatment.

Claims

1-18. (canceled)

19. A method for production of cellulose based fuel pellets from large, elongate pieces of wood material (23), comprising (i) comminuting the large, elongate pieces of wood material (23) to particulate wood material (54), (ii) heat treating the particulate material in a reactor (61) at a temperature and for a period sufficient to soften lignin present in the particulate material, (iii) reducing pressure in the reactor to cause defibration of the particulate material, and (iv) pelletizing the material using softened lignin as a binder for the pellets, wherein the step of comminuting the large pieces of wood material (23) is performed as a single-step operation in which the large, elongate pieces of wood material are charged to a comminution station (12) with at least one rotating drum (22) provided with cutting teeth configured to fully comminute the large, elongate wood material.

20. The method as claimed in claim 19, wherein the large, elongate pieces of wood material (23) are selected from one or more of timber logs and sections of timber logs.

21. The method as claimed in claim 19, wherein the comminution yields particulate material (54) with a largest linear dimension of approximately 10 mm.

22. The method as claimed in claim 19, wherein the particulate wood material is heated in the reactor to a temperature within a range of approximately 180° C. to approximately 250° C. for a duration within a range of approximately 1 minute to approximately 15 minutes.

23. The method as claimed in claim 19, wherein the step of heat treatment is performed at least partially by pressurized steam.

24. The method as claimed in claim 19, wherein the comminution station (12) is operated under a reduced pressure, thereby decreasing an amount of dust escaping therefrom.

25. The method as claimed in claim 19, wherein the particulate material (54) is fractioned into at least two fractions and a first fraction of particulate material with a size smaller than a desired minimum size is separated from a second fraction of particulate material with a size within a desired size range, wherein the second fraction is used in the step of heat treating.

26. The method as claimed in claim 25, wherein the desired size range is between approximately 2 mm and approximately 10 mm.

27. The method as claimed in claim 25, wherein the first fraction is collected and heat treated and subsequently pelletized under lower heat or shorter duration or both as compared to the first fraction.

28. The method as claimed in claim 25, wherein the comminution station (12) is operated under a reduced pressure, thereby decreasing an amount of dust escaping therefrom.

29. The method as claimed in claim 22, wherein the particulate material (54) is fractioned into at least two fractions and a first fraction of particulate material with a size smaller than a desired minimum size is separated from a second fraction of particulate material with a size within a desired size range, wherein the second fraction is used in the step of heat treating.

30. An apparatus for production of cellulose based fuel pellets from large, elongate pieces of wood material (23), comprising: a. a comminution station (12) configured to comminute large, elongate pieces of wood into particulate wood material, b. a process plant configured to heat the particulate wood material to a temperature and for a period of time sufficient to soften lignin present in the particulate wood material, and to thereafter reduce pressure, thereby causing defibration of the particulate material and yielding treated particulate wood material, and c. pelletizing equipment to thereafter pelletize the treated particulate wood material, wherein the comminution station (12) is configured to comminute the large pieces of wood material (23) in a single-step operation via a cutting drum provided with cutting teeth, and the teeth have a size and the drum is rotated at a rotational speed to cut the elongate pieces of wood to a desired particle size.

31. The apparatus as claimed in claim 30, wherein the cutting teeth have a largest linear dimension corresponding to a largest desired linear dimension of the particulate material.

32. The apparatus as claimed in claim 30, wherein the cutting drum (22) is formed as a unitary structure with exception to the teeth.

33. The apparatus as claimed in claim 30, wherein the cutting drum (22) is assembled as a stack of individual saw blades, allowing separate replacement of each individual blade.

34. The apparatus as claimed in claim 30, wherein the large, elongate pieces of wood material (23) include a largest log having a cross-sectional dimension and the comminution station (12) comprises one cutting drum (22) with a cross-section at least twice the cross-sectional dimension of the largest log.

35. The apparatus as claimed in claim 30, wherein the comminution station (12) comprises two cutting drums (32a, 32b).

36. The apparatus as claimed in claim 30, further comprising a chute (27) for conveying the particulate wood material (54) from the comminution station (12) to the heat treatment plant (13).

37. The apparatus as claimed in claim 30, wherein a pressure in the comminution station (12) can be reduced.

38. The apparatus as claimed in claim 30, further wherein the particulate wood material is fractionated into a first fine fraction and a second coarse fraction.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0042] Below the invention is described in further detail in the form of exemplifying embodiments illustrated by the enclosed drawings, in which:

[0043] FIG. 1 is a flow sheet of a process in which the disclosed embodiments can be applied.

[0044] FIG. 2 is a schematic, simplified side view of a core element of a disclosed embodiment.

[0045] FIG. 3 is a schematic, simplified side view of a core element of another embodiment.

[0046] FIG. 4 is a schematic simplified front view of the embodiment shown in FIG. 3.

[0047] FIG. 5 is a schematic simplified side view of the embodiment of FIG. 2, showing additional elements.

[0048] FIG. 6 is a flow chart of a preferred embodiment of step 13 from FIG. 1.

DETAILED DESCRIPTION

[0049] FIG. 1 is a simple flow chart of a process of producing black pellets from wood logs. From a store 11, wood logs are charged to a comminution station 12 where the logs are comminuted to particles of desired size in a single-step operation. The particles, sometimes also referred to as sawdust, are charged to a reactor system 13 for thermal treatment of the particles under pressure and subsequent pressure release. The flow chart is simplified in that the reactor system typically comprises a number of steps, typically drying, heating under pressure, (sudden) pressure release and eruption of material into a different reactor, subsequent further drying, involving movement of the material between different driers and reactors. Finally, the resulting fibrous material is pelletized in a pelletizer 14.

[0050] While all these steps are of interest in the overall process, an important focus and concern of the present method is the step of comminuting the timber logs to particulate matter in a manner more efficient than previously described, i.e. step 12 of FIG. 1. The timber logs may be charged to comminution undivided or after having been sectioned to large sections, e.g. sections of 2-5 meters.

[0051] FIG. 2 shows in a simplified manner a comminution station 12 with a housing 21 in which the main tool is a cutting drum 22 provided with a number of cutting teeth along its width and circumference. A log 23 is shown being charged into the comminution station from the right towards the left in a linear manner. Different mechanisms may be applied for charge of the log; in FIG. 2 a conveyor belt 24 underneath the log is indicated to contribute thereto. A number of rotatable supporting wheels or drums 25, spaced apart linearly along the path of the log charge, are arranged to support the logs from above, which is particularly important once the cutting drum starts cutting the log. The supporting wheels are typically movable up and down to account for different log diameters and are also typically provided with spring elements to allow compensation for diameter variations along the length of each individual log.

[0052] The general floor level is indicated with a line 26, while the floor may exhibit a linear groove with a lowest level indicated by the broken line 27, along which the logs are charged. The groove provides stability sideways. Sideways stability may also be provided by particularly designed conveyor belts having members to support the logs sideways as well as members to force the logs forward in the direction of the drum.

[0053] The particulate material leaving the comminution station can leave through a vertical chute 27 in order to be gravity assisted. It is preferred, in addition, to use a fan or the like to assist the movement and to ensure that the pressure in the comminution station is reduced somewhat in comparison with the ambient pressure, in order to prevent dust from escaping the station, or at least to reduce the dust release therefrom.

[0054] FIG. 3 shows a comminution station 12′ generally similar to the comminution station 12 shown in FIG. 2 in which two cutting drums 32a, 32b are arranged in order to handle wood logs of large diameter without having to use a cutting drum of extreme size. In all other respects, the station 12′ is similar to station 12. In addition, the embodiment of FIG. 3 is an example of comminuting the log in one single step or one single unit operation, since it all takes place during a simple linear movement of the log.

[0055] FIG. 4 is a front view of a comminution station generally similar to station 12′ in that it comprises two cutting drums. In addition to a supporting wheel or drum 25, FIG. 4 also shows supporting wheels 45 laterally at each side of the log. As an even further measure to hold and stabilize the log, the conveyor belt is shown as provided with claws 46 evenly distributed along the belt, to support the logs against lateral movement.

[0056] FIG. 4 shows the “full package” of log stabilizing means. Perhaps needless to say, the conveyor system for the logs does not have to have all these stabilizing measures, but should include stabilizing measures vertically as well as horizontally.

[0057] In FIG. 4, the front cutting drum 32a is shown in an elevated position so as to make it better distinguishable from cutting drum 32b. In practice, the cutting drums would more typically largely “overlap” one another in the vertical direction as better illustrated in FIG. 3, not leaving to cutting drum 32b to cut the entire log.

[0058] FIG. 5 shows generally the same as FIG. 2, but in a situation in which logs are actually cut into particulate matter. A second log has moved tightly up behind the first one.

[0059] In the chute 27 through which the wood particles from the log falls towards the next process step, an upwards inclined pipe 51 with a fan 53 and a dust filter 52 is arranged. The fan 53 pumps air out from the chute 27 and from the cutting station above, placing the cutting station under a pressure slightly below ambient pressure to thereby reduce dust emission from the cutting station. The power of the fan is tuned to a level at which the typical particles from the cutting fall past the pipe 51 and further down the chute, while the finest of particles and dust will be collected by the dust filter 52. The pipe 51 can also be extended and curved to a vertical direction in order to move the fan 53 and the filter 52 further away from the chute 27 with the passing particles 54.

[0060] FIG. 5 also shows another and optional feature. The chute 27 may be split into two different pipes 55 and 56 with a sieve 57 arranged so as to only allow fine particles to pass into pipe 56 while coarser particles pass into pipe 55. A fan 58 can be arranged in pipe 58 to ensure that most of the particles small enough to pass through the sieve 57 actually do enter pipe 58. In this or a similar manner it is ensured that the particles in pipe 55, which in weight will be the majority of the particulate matter, is within a desired particle range. The fine particle fraction collected from pipe 56 may be subjected to similar or different treatment than the coarse fraction from pipe 55. If used to produce pellets, the heat treatment for the fine particle fraction will typically be conducted using more lenient conditions than what is the case for the coarse fraction. It should be emphasized that FIG. 5 only provides a simplified illustration of the particle fractioning which may be performed with any particle fractioning technology known and available. The desired size range is between 2 mm and 10 mm, more preferred between 2 mm and 5 mm.

[0061] FIG. 6 is a flow chart that shows a preferred embodiment of step 13 of FIG. 1.

[0062] FIG. 6 shows to the upper left a vessel 60 for drying the particulate material to desired level of moisture, e.g. in the range 20-50 or 30-40% by weight moisture. Next, a reactor 61 for heat treatment of the particulate wood material is shown. In the reactor 61 the particulate wood material is heated under pressure in the presence of water vapor and air. The mixing ratio between water vapor and air may vary and the filling level of the reactor can likewise vary.

[0063] Temperature and residence time in the reactor may vary and are typically in the range from 180 to 250° C. and from 1 to 15 minutes. Higher temperatures and longer processing time are usually undesirable because they would lead to greater degradation, more mass loss and problems in operating the downstream process in the form of undesirable amounts of non-condensable gases, gases with strong odours, etc.

[0064] The reactor 61 typically comprises equipment and devices for controlling and monitoring the process, including valves to control pressure, means for heating and cooling of the reactor respectively, etc. This is not illustrated. The treatment in reactor 61 leads a.o. to softening of the lignin in the wood, making it useful as a binder in the subsequent pelletization.

[0065] Vessel 62 is a pressure release vessel into which the reaction mixture is released at end of treatment in reactor 61. At least a portion of the pressure in the reactor 61 is released abruptly, thereby expelling the reaction mixture from the reactor into the pressure release vessel 62.

[0066] The skilled artisan will appreciate that gases other than steam and air may be present in the reactor, provided that they do not interfere negatively with the process quantities. For example, the ratio between oxygen and nitrogen in the reactor be different from what is the case in air, e.g. through the addition of oxygen enriched air or oxygen consumed during the process.

[0067] On completion of reaction treatment the reaction mixture is expelled from the reactor 61 to pressure release vessel 62 via conduit 71. This is performed in a manner well known in the art. The solid particulate material with a certain quantity of moisture is moved into the pressure release tank 62 and transferred via conduit 72 to the step of pelletization, typically after a step 66 of after-drying.

[0068] The gas containing condensable components as well as components which are not condensable within the prevailing conditions, passes through conduit 73 at or near the top of the pressure release vessel 62 and is led therefrom directly to at least a heat exchanger 63.

[0069] The heat exchanger 63 cools the gas flow and ensures that the condensable components of the gas are condensed, so as to thereby reduce the volume of the gas flow. The heat of condensation received by the refrigerant is utilized as energy in any suitable manner within or outside the current process. Typically, this energy is used to preheat the air for a drying unit or for combustion. The condensate from the heat exchanger 63 contains, in addition to water, components that should be removed before the water is discharged or recycled for reuse. The condensate is discharged through conduit 75, while the gas passes to the next step in the process through conduit 76.

[0070] As regards the heat exchanger or heat exchangers 63 this or these can be indirect heat exchangers where the refrigerant is kept separate from the vent gases or it can be direct heat exchangers where cooling water is mixed with the vent gases. A combination of direct and indirect heat exchange is also an option, in which the heat exchange mainly is indirect, but where water 74 at a limited rate is sprayed into the flow of discharge gases into the heat exchanger 63 to cause a quenching of the discharge gases in conduit 73 to thereby more easily condense all condensable components in the subsequent indirect step of heat exchange.

[0071] If one chooses to use only direct heat exchange, a much larger volume of fluid needs to be handled downstream of the heat exchanger. It is therefore preferred that the heat exchange at least partially is conducted as indirect heat exchange.

[0072] The next step of the process consists of a container 64 with flexible volume, typically a “balloon”, which like other balloons has soft walls and is dimensioned so that it is able to receive the “puff” of non-condensable gases resulting from expulsion from a batch reactor operated under normal operating conditions.

[0073] The gases leaving container 64 through conduit 77 may be subjected to after-treatment in a final step, e.g. a burner 65 to burn off combustible gases before releasing non-toxic components.

[0074] It should be noted that the detailed steps according to FIG. 6 are not novel as such, but represent a favourable method for the step 13 of FIG. 1 since they combine sound economy with sound environment.

[0075] It is furthermore to be noted that the step of defibration may also be obtain using a continuous and slower pressure reduction as an alternative to the steam explosion technique. Such continuous pressure reduction may be obtained using a screw conveyor to continuously and comparatively slowly discharging the heated material from the reactor. In some contexts, the continuous process may be preferred over the steam explosion.

[0076] The final step 14 of FIG. 1, the pelletization, may be conducted in any manner known in the field, their common denominator being application of pressure and use of the heated lignin in the wood as a binder, resulting in pellets with a low, controlled level of moisture, excellent mechanical properties and a high energy content.

[0077] The inventive embodiments provide a condensed process requiring comparatively small footprint in that storage of raw material is reduced to storage of compact wood-logs, good control of the particle size and a narrow particle size distribution which in turn allows the

[0078] The advantages of the disclosed embodiments are the lower energy consumption, lower footprint, more homogeneous particle size distribution but also better particle shape in terms of shorter fibres, more suitable to be milled in the typical mills used for coal, biomass etc.