Luminescent braze preforms

Abstract

A braze preform includes a filler metal, a flux in communication with the filler metal, and a luminescent material covering at least a portion of the filler metal. The luminescent material is equal to or less than 0.15% total weight of the braze ring. Further, the luminescent material includes at least one of a luminescent ink, a solvent, and a binder. The solvent may be one of a bromide-based solvent or a non-chlorine-based solvent. The binder may be an acrylic resin.

Claims

1. A braze preform comprising: a filler metal; a flux core disposed within a cavity of the filler metal; a luminescent material that covers at least a portion of an exterior of the filler metal; and wherein the luminescent material is equal to or less than 0.15% total weight of the braze preform.

2. The braze preform of claim 1 wherein the luminescent material is burned off at or below a melting temperature of the filler metal.

3. The braze preform of claim 1 wherein the luminescent material is applied to the braze preform as a wet coating and then cured; wherein the wet coating of the luminescent material comprises at least one of luminescent ink, a solvent, and a binder.

4. The braze preform of claim 3 wherein the wet coating luminescent ink is less than 50% of the weight of the luminescent material; and wherein the solvent is greater than 50% of the weight of the luminescent material.

5. The braze preform of claim 3 wherein the binder is an acrylic resin.

6. The braze preform of claim 1 wherein the luminescent material comprises a luminescent ink and a binder, wherein the luminescent ink is less than 50% of the weight of the luminescent material.

7. The braze preform of claim 1 wherein the luminescent material covers 90%±10% of the braze preform.

8. A braze preform comprising a filler metal; a flux core at least partially surrounded by the filler metal; and a luminescent coating that covers at least a portion of the filler metal, the luminescent material comprising a luminescent ink less than 50% of the weight of the luminescent material, the luminescent material being equal to or less than 0.15% total weight of the braze preform.

9. The braze preform of claim 8 wherein the luminescent coating further includes a binder and a solvent, the solvent greater than 50% of the weight of the luminescent material.

10. The braze preform of claim 9 wherein the solvent is one of bromide based or non-chlorine based.

11. The braze preform of claim 8 wherein the luminescent coating covers 90%±10% of the braze preform; and wherein a surface layer thickness of the luminescent coating is approximately the same thickness, plus or minus 10%, as an ink layer from a permanent marker.

12. A braze ring comprising: a filler metal; a flux disposed within with the filler metal; and a luminescent material disposed on an exterior of the filler metal and covering at least a portion of the filler metal, the luminescent material being equal to or less than 0.15% total weight of the braze ring.

13. The braze ring of claim 12 wherein the luminescent material covers 90%±10% of the braze ring.

14. The braze ring of claim 12 wherein the luminescent material includes a luminescent ink, a solvent, and a binder; wherein the luminescent ink is less than 50% of the weight of the luminescent material; and wherein the solvent is greater than 50% of the weight of the luminescent material.

15. The braze preform of claim 1 wherein the luminescent material is applied to the braze preform without flux.

16. The braze preform of claim 1 wherein the luminescent material is disposed at least one discrete location on the exterior of the filler metal.

17. The braze preform of claim 8 wherein the luminescent coating has a burn off temperature below a melting temperature of the filler metal.

18. The braze preform of claim 8 wherein the luminescent coating is a) detectable by a light source that is an ultraviolet light; b) automatically detected to determine the presence of the braze preform; and c) disposed at at least one discrete location on the exterior of the filler metal.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The drawings illustrate the best mode currently contemplated of practicing the present invention.

(2) In the drawings:

(3) FIG. 1a is a schematic representation of a system in accordance with the present invention;

(4) FIG. 1b is a continuation of the schematic representation of the system in accordance with the present invention described in FIG. 1a; and

(5) FIG. 2 is a partially cut-away isometric view of a braze preform in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

(6) FIGS. 1a-1b illustrate a system 5 that is provided within a facility 2 and that can be used for brazing components 10, 15 to each other using a braze preform 20. In a representative application, the system 5 includes a preparation station 30 and a drying station 40 that are used for coating a luminescent material 25 over a filler metal 22 (FIG. 2) of the braze preform 20, explained in greater detail elsewhere herein. Assembly station 50, a detecting station 60, and a brazing station 70 are also provided in the facility 2. In a preferred embodiment, the preparation and drying stations 30, 40 are provided in a first facility 2 and the assembly, detecting, and brazing stations 50, 60, and 70 are provided in a separate facility (not shown). This may allow a manufacturer of the braze preforms 20 to treat and/or coat the braze preforms 20 with the luminescent material 25 and then provide such braze preforms 20 to a different manufacturer to use in brazing the components 10, 15 to each other using the rest of the system 5. The system 5 is configured so that presence or absence of a braze preform 20 on a component 10, 15 can be automatically determined by detecting the luminescence of the braze preform 20. This allows a yes or no decision; that is, continuing to a brazing procedure or a reject decision can be automatically made, as described in greater detail elsewhere herein.

(7) Referring now to FIG. 2, braze preform 20 includes a filler metal 22, such as aluminum, stainless steel, carbon steel, brass, copper, or any other metal or alloy, that is coated with the luminescent material 25 and which may define a brazing ring configuration or have other preformed configurations, depending on the particularly desired end-use. Suitable brazing rings or valves (such as for HVAC equipment), may be coated with the mixture, and/or other preformed brazing products which are suitable for use as filler metal 22 are available from Lucas-Milhaupt, Inc., having a place of business in Cudahy, Wis., U.S.A. under the trade names Sil-Fos® for brazing components 10, 15 that are made from copper-based materials, and Braze™ and Easy-Flo® for brazing components 10, 15 that are made from steels, stainless, and/or other ferrous materials. The filler metal 22 may be flux coated or cored, for example, as described in the commonly owned U.S. Reissue Pat. No. RE 42,329 entitled Flux Cored Preforms for Brazing, and pending U.S. application Ser. No. 12/324,410 entitled Brazing Material Containing A Flux which was filed Nov. 26, 2008 and pending U.S. application Ser. No. 12/602,053 entitled Brazing Material which was filed Jan. 5, 2011, all of which are incorporated by reference herein, in their entireties.

(8) Referring again to FIGS. 1a-1b, the luminescent material 25 in this embodiment includes multiple liquid constituents, namely, a luminescent ink 27 and a solvent 28. The solvent may be bromide based and include the non chlorine based N-TRON solvent. Luminescent ink 27 and solvent 28 are mixed together in a container 32 at the preparation station 30. Luminescent ink 27 includes any color, for example, a neon blue color, ink and the solvent 28 of this embodiment is a non-flammable, optionally other, fast-drying solvent(s). One suitable brightener is sold by www.blacklightworld.com. It is contemplated that the luminescent ink 27 can be red or some other color. Preferably, the luminescent ink 27 is invisible to the naked eye after application. That is, luminescent ink 27 preferably cannot be seen under ambient light or conventional incandescent, fluorescent, and/or other conventional lighting. The luminescent ink 27 need not be an ink or even a liquid, per se, but can instead be a powder or other solid that can be transferred to and/or adhered to the braze preforms 20. This can be done by mixing such powder or solid form of the luminescent ink 27 into the solvent 28 to form a suspension for a liquid application. Optionally, the luminescent ink 27 may be applied to the braze preforms 20 in its powered or other solid form. The coating may be applied in any thickness, but preferably is thin as well as transparent under ambient light.

(9) These are mixed in a ratio that highly dilutes the luminescent ink 27 by providing the luminescent ink 27 in a less than 50% by weight of the overall luminescent material 25. For example, a preferred embodiment has a ratio in which about 30% of the weight of the luminescent material 25 is the luminescent ink 27 and 70% of the weight of the luminescent material 25 is the solvent 28, while both the luminescent ink 27 and the solvent 28 are in liquid states in the container 32. In another embodiment, the luminescent ink 27 may be between about 10-50% of the weight of the luminescent material 25 and the solvent may be between about 50-90% of the weight of the luminescent material, before being applied to the braze preform(s) 20. Still referring to FIGS. 1a-1b, at preparation station 30, the luminescent material 25 is applied to a batch of multiple braze preforms 20 to allow each of the braze preforms 20 to luminesce. This is done by dipping, optionally soaking, the braze preforms 20 in the luminescent material within the container 32. The braze preforms 20 are then removed from the container 32 and placed in a tumbler 42 and/or other suitable drying device at drying station 40. The braze preforms 20 are agitated and tumbled in the tumbler 42 which mechanically removes some of the excess luminescent material 25, with the rest of the excess luminescent material 25 being removed by, e.g., evaporation and/or volatile release of the solvent 28 constituent. This leaves a thin coating of the luminescent material on each of the braze preforms 20 which, in most embodiments, has a higher concentration of luminescent ink 27 within the luminescent material 25 on the braze preforms 20. In other words, there is a greater ratio of luminescent ink 27 versus solvent 28 as compared to the luminescent material in its fully liquid state in the container 32.

(10) In another embodiment, the luminescent material 25 is applied to the braze preforms 20 by a spray application instead of by dipping, dunking, or soaking. In yet another embodiment, the application and drying are performed at the same time and/or by way of a single piece of application equipment. In such embodiment, the luminescent material 25 may be sprayed and dried at a single station, for example, by way of a combined tumbling, spray applying, and drying machine. One suitable machine is available under the trade name Rotamat coating machine from the Walther Trowal company of Belgium. The mixture with luminescent material 25 may also be sprayed on (with or without flux) in ambient or in a reduced atmosphere. In another embodiment, the luminescent material 25 may be integrated with other steps in the manufacturing process for making the braze preforms 20 themselves. In other words, the application of the luminescent material 25 may not require a separate application step(s). Instead, the luminescent material 25 may be mixed with the flux and/or other coating materials so that the luminescent material 25 is applied simultaneously with the flux and/or other coat materials as a component thereof.

(11) In another embodiment of the invention, the luminescent material 25 may include a luminescent ink 27, a solvent 28, and a binder. The binder assists the luminescent material 25 in adhering to the braze preforms 20. The binder may be an acrylic resin or other materials known in the art. In this embodiment of the invention, the luminescent material 25 is applied to the braze preforms 20 as described above in a wet coating. The luminescent material 25 is then cured after being applied to the braze preforms 20. During the curing process, the solvent 28 is removed from the luminescent material 25. A such, the cured luminescent material 25 may include a luminescent ink 27 and a binder.

(12) As stated above, the wet coating of the luminescent material 25 that is applied to the braze preforms 20 prior to curing may include a luminescent ink 27, a solvent 28, and a binder. In an exemplary embodiment, the luminescent ink 27 may be less than 50% by weight of the overall luminescent material 25. More particularly, the luminescent ink 27 may be less than 10% by weight of the overall luminescent material 25. Even more particularly, the luminescent ink may be 0.5% by weight of the overall luminescent material 25. The solvent 28 may be greater than 50% by weight of the overall luminescent material 25. More particularly, the solvent 28 may be greater than 90% by weight of the overall luminescent material 25. The binder may be 2% by weight of the overall luminescent material 25. In yet other embodiments, the luminescent material 25 may include a luminescent ink 27 and a binder, without a solvent 28.

(13) During the curing process the luminescent material 25 transitions from the wet coating to a dry finished coating. That is, the finished braze preforms 20 that are used in the brazing of joints include a cured luminescent material 25 according to the dry finished coating. The dry finished coating of the luminescent material 25 includes the luminescent ink 27 and the binder. As stated above, the solvent 28 is removed from the luminescent material 25 during the curing process, by processes such as evaporation. As a result, percentage by weight of the luminescent ink 27 and the binder in the luminescent material 25 is increased. In an exemplary embodiment of the invention, the luminescent ink 27 remains less than 50% by weight of the overall luminescent material 25, while the binder increases to greater than 50% by weight of the overall luminescent material 25. More particularly, the luminescent ink 27 becomes 20% by weight of the overall luminescent material 25, while the binder becomes 80% by weight of the overall luminescent material 25.

(14) Regardless of the particular way in which the luminescent material 25 is applied to the braze preforms 20, the luminescent material 25 may cover substantially the entire outer surface of the braze preform, for example, covering about 90%, plus or minus 10%. Or, the luminescent material 25 may cover a relatively smaller percentage of the outer surface of the braze preform 20. The luminescent material 25 may be placed at a single discrete location or multiple discrete locations that are spaced from each other on the outer surface of the braze preform 20. For embodiments of braze preforms 20 that include grooves, channels, and/or other structural features, the luminescent material 25 may be applied onto or into such grooves, channels, or other structural features, optionally adjacent such features as long as at least a portion of the luminescent material 25 can be detected by a sensor 65 as described in greater detail elsewhere herein. The coating of luminescent material 25, whether it be an entire coating, a partial coating, and/or discrete markings upon the braze preforms 20, is sufficiently hard, permanent, and can withstand shipping and handling with minimal losses. Stated another way, the luminescent material 25 upon the braze preforms 20 is permanent and will not wash off. The surface layer thickness of the coating of the luminescent material 25 is, in some embodiments, approximately the same thickness, plus or minus 10%, as would be an ink layer from a permanent marker applied to the braze preforms 20. Regardless, after leaving the preparation and/or drying stations 30, 40, the braze preforms 20 are luminescent and may be utilized elsewhere in the system 5.

(15) Still referring to FIGS. 1a-1b, as shown at the left-hand side of assembly station 50, the braze preforms 20 are assembled onto the components 10, 15. As shown at the right-hand side of assembly station 50, multiple braze preforms 20 that are installed on a parts assembly 17 that is defined by components 10 and 15 that are assembled to each other. The braze preforms 20 are assembled onto the components 10, 15 and/or parts assembly 17 in a known automated manner. After such assembly, the components 10, 15 and/or parts assembly 17 are moved from the assembly station 50 to the detecting station 60.

(16) Still referring to FIGS. 1a-1b, at detecting station 60, presence or absence of the braze preform 20 upon the components 10, 15 and/or parts assembly 17 is determined. In a preferred embodiment, the luminescent material is invisible 25 to the naked eye and/or under normal lighting conditions. In such embodiments, detecting station 60 includes a light source 63 that emits a different wavelength of light than is emitted from a facility light source 3. In this embodiment, the facility light source 3 is a conventional overhead florescent or incandescent light source, as is typical for a manufacturing-type facility 2. The preferred light source 63 is a black light, optionally another light that can suitably cause the luminescent material 25 and thus the braze preforms 20 to luminesce. Light source 63 is positioned with respect to the braze preforms 20 within the detecting station 60 so that light emitting from the light source 63 is directed toward the braze preforms 20. Sensor 65 is positioned within the detecting station 60 so as to allow the sensor 65 to detect luminescence from the luminescent material 25 and thus the braze preforms 20. A suitable sensor 65 is a UV sensor which is available from the Keyence Corporation of America, in Elwood Park, N.J., U.S.A. A UV meter reading may indicate a level of “8” (below 4 stops) to show the coating is present. In one embodiment, the sensor 65 detects luminescence and thus the presence of the braze preform 20 on a single component 10, 15, as illustrated at the left-hand side of detecting station 60. In another embodiment, the sensor 65 detects luminescence and thus the presence of the braze preform 20 on the parts assembly 17 after the components 10, 15 have been assembled to each other, such as that shown at the right-hand side of detecting station 60.

(17) Still referring to FIGS. 1a-1b, in this embodiment, the detecting station 60 preferably provides a darkened environment in which luminescence detection occurs. The darkened environment in this embodiment is defined blocking at least some of the light from the facility light source 3 with multiple interconnected shields 64. Optionally, a single shield 64 may be used to enhance the ability of the sensor 65 to detect the luminescence and thus the presence of the braze preform 20. In another embodiment, no shields 64 are provided and the detection of luminescence is instead performed in a lit environment that is illuminated by the facility light source 3.

(18) Regardless, if the sensor 65 does not detect luminescence of the luminescent material 25, a determination is made that the braze preform 20 is absent. When such absence of the braze preform 20 is determined, the component 10, 15 or parts assembly 17 is rejected and is not sent to the brazing station 70. If the sensor 65 does detect luminescence of the luminescent material 25, a determination is made that the braze preform 20 is present. When such presence of the braze preform 20 is determined, the component 10, 15 or parts assembly 17 is accepted and is sent to the brazing station 70, for example, a go/no go test may be used to prevent parts from proceeding that do not have the coated braze preform. For embodiments in which presence or absence of the braze preform 20 is determined on a component 10 or 15 instead of the parts assembly 17, if the presence of the preform 20 is determined on the component 10 or 15, then the components 10, 15 are assembled to each other to create the parts assembly 17 which is then sent to the brazing station 70 where a brazing procedure is performed.

(19) The brazing station 70 includes a brazing furnace 72. The parts assembly 17 is placed in the brazing furnace 72 and the brazing furnace 72 is heated to a temperature required to heat the parts assembly 17 and melt the filler metal 22 of the braze preform 20 so as to join the components 10, 15 to each other by brazing. The applied mixture also does not leave any carbon residue when the material is burned during the brazing process. In the preferred embodiments in which the luminescent material 25 is invisible without being illuminated by the light source 63, any residual luminescent material 25 on the parts assembly 17 after the brazing procedure remains invisible or is non-staining of the components 10, 15. In view of the above, substantially an entire manufacturing process which includes a brazing procedure can be automated with system 5. It is understood that system 5 further includes various machines, logic controllers and other controllers, which are not discussed here because they are so well known to those skilled in the art.

(20) Various alternatives are contemplated as being within the scope of the following claims particularly pointing out and distinctly claiming the subject matter regarded as the invention.