Method for the surface compaction and calibration of a sintered component

Abstract

According to a method for the surface compaction and calibration of a sintered component, the sintered component runs along an axis through a plurality of die sections of a die, the inner diameter of which decreases in pressing direction and wherein the individual die sections are arranged such that a following die section of the plurality of die sections directly adjoins the corresponding die section which precedes it in pressing direction, and after the surface compaction at the last die section with decreasing inner diameter there is a relaxation of the sintered component in a relief section directly adjoining the last die section, which relief section has a greater diameter than the immediately preceding last die section of the die section with a decreasing inner diameter. The sintered component is calibrated in the relief section, whereby the inner contour of the relief section corresponds with the intended contour with the nominal dimensions of the sintered component.

Claims

1. A method for the surface compaction and calibration of a sintered component, according to which the sintered component is moved along an axis from a first die opening in the direction of a second die opening of a die opposite the first die opening along the axis, wherein the sintered component during this movement passes through a plurality of die sections of the die and in this way a surface area of the sintered component is compacted, whereby in a pressing direction an inner diameter of the consecutive die sections decreases and the individual die sections are arranged such that a following die section of the plurality of die sections respectively directly adjoins the corresponding die section which precedes it in the pressing direction, and after the surface compaction at the last die section with decreasing inner diameter there is a relaxation of the sintered component in a relief section directly adjoining the last die section, wherein the relief section has a greater diameter than the immediately preceding last die section of the die section with a decreasing inner diameter, wherein the sintered component is calibrated in the relief section, whereby an inner contour of said relief section corresponds with an intended contour with nominal dimensions of the sintered component, wherein the relief section has an inner diameter which is greater by at least 0.02% than the inner diameter of the last die section with the smallest inner diameter and is not greater than the inner diameter of the first die opening, wherein the sintered component comprises a first edge and a second edge opposite the first edge in the pressing direction, which are formed at transitions between an end face applicable against the die sections and axial end surfaces of the sintered component, and wherein the first edge and the second edge of the sintered component are faceted before being introduced into the die.

2. The method as claimed in claim 1, wherein a die is used in which the relief section is formed.

3. The method as claimed in claim 1, wherein after calibration the sintered component is moved against the pressing direction again through the last die section with a decreasing inner diameter.

4. The method according to claim 1, wherein an inner contour of a second last die section of the plurality of die sections corresponds with the inner contour of the relief section.

5. The method as claimed in claim 1, wherein the first edge, which is arranged during the surface compaction and calibration of the sintered component above the second edge, is faceted to a greater degree than the second edge.

6. The method as claimed in claim 1, wherein the inner diameter of the relief section is not greater than a diameter of the first die section.

Description

(1) In a simplified, schematic representation respectively:

(2) FIG. 1 is a cross-section of a section of a die with a sintered component shortly before the insertion;

(3) FIG. 2 is the cross section of the section of the die according to FIG. 1 with the sintered component in the calibration position;

(4) FIG. 3 is a cross-section of a die for faceting the sintered component;

(5) FIG. 4 is a schematic comparison of the state of the sintered component after the sintering, after the faceting and after the surface compaction and calibration.

(6) First of all, it should be noted that in the variously described exemplary embodiments the same parts have been given the same reference numerals and the same component names, whereby the disclosures contained throughout the entire description can be applied to the same parts with the same reference numerals and same component names. Also details relating to position used in the description, such as e.g. top, bottom, side etc. relate to the currently described and represented figure and in case of a change in position should be adjusted to the new position.

(7) It should be noted at this point that the calibration of a sintered component means the processing of the latter to obtain at least approximately the nominal dimensions of the component in a die by pressure loading. The term at least approximately means that deviations from the nominal dimensions are permissible within the usual tolerance range.

(8) The term nominal dimensions is defined in the present invention to mean the final dimensions that the finished sintered component 2 should have, possibly less the expansion of the sintered component 2 after the relaxation (i.e. the ejection out of the calibrating die, as explained in more detail below) which is defined by the spring back behavior of the sintered material due to the elastic spring-back. The amount of spring-back behavior can be determined empirically. In other words the nominal dimension plus the possible expansion caused by the elastic spring-back form the final dimensions.

(9) FIGS. 1 and 2 show a section of a die 1 for the surface compaction and calibration of a sintered component 2 in longitudinal cross-section.

(10) The sintered component 2 consists of pressed and subsequently sintered powder metal, wherein the methods and materials for producing such a sintered blank are sufficiently known from the prior art and are therefore not explained in more detail.

(11) For the surface compaction and calibration the sintered component 2 is moved along an axis 3 through the die 1.

(12) The die 1 comprises a main die body 4, which on one die surface 5 has a first (upper) die opening 6, from which a plurality of die sections 7 to 11 lead along the axis 3 into the inside of the main die body 4. In this case the first die section 7 adjoins the first die opening 6, the last die section 11 is however closer to a second die surface 12 lying opposite the first die surfaces 5 along the axis and a second die opening 13 formed therein.

(13) The sintered component 2 is designed to be disc-like in the shown embodiment and has on a radial outer surface 14, i.e. the end face, a diameter 15, which prior to the surface compaction corresponds to a rough diameter and after the surface compaction corresponds to a smaller final diameter.

(14) In general preferably rotationally symmetrical and/or at least approximately cylindrical sintered components 2, such as in particular gears, etc., are surface compacted and calibrated by the die 1. However, other sintered components 2 can also be processed accordingly by the die 1.

(15) The surface compaction of the sintered component 2 is performed in that the latter is inserted through the first die opening 6 into the first die section 7 and is then moved into all of the additional die sections 8 to 11, wherein in each die section 7 to 11 the outer surface 14 of the sintered component 2 is pressed at least on sections of the outer surface 14 against wall faces 16 of the die sections 7 to 11. In this case one or more contact surfaces on the outer surface 14 of the sintered component 2 come into pressure contact with one or more pressing surfaces on the wall faces 16 of the die sections 7 to 11. The contact surface can be formed by a part of or the whole outer surface 14 of the sintered component 2. The pressing surface can be formed by a portion of the wall surface 16 or also by the whole wall surface 16, wherein the portion can relate to the axial extension and/or to the extension in circumferential direction.

(16) The pressing effect is achieved in that an inner diameter 17 of the die sections 7 to 11, which is defined by the internal width between opposite or cooperating sections of the pressing surface of a die section 7 to 11, is smaller respectively than the diameter 15 of the sintered component 2 before it is inserted into the respective die section 7 to 11. In general, the die sections 7 to 11 preferably have an inner contour, which corresponds to the outer contour of the sintered component 2, whereby however each die section 7 to 11 has a circumference which is smaller than the circumference of the sintered component 2 before it is inserted into the respective die section 7 to 11.

(17) The die sections 7 to 11 following one another along the axis 3 merge directly into one another (continuously), i.e. without intermediate sections, and have decreasing inner diameters 17 from the first die section 7 to the last die section 11 (monotonically), i.e. consecutive die sections 7 to 11 can be the same size or in particular can be smaller, but not larger. In this way the pressing effect on the contact surface of the sintered component 2 increases from the first die section 7 to the last die section 11, whereby a pressing direction is defined along the axis 3, which points from the first die section 7 to the last die section 11. The movement of the sintered component 2 in the die 1 is preferably linear in said pressing direction from the first die opening 6 to the last die section 11, afterwards the sintered component 2 is demolded from the die 1, preferably after a reversal of the direction of movement opposite the pressing direction through the first die opening 6.

(18) The linear movement in the direction of the axis 3 can also be overlayered by a rotational movement, whereby the sintered component 2 in the die 1 performs a screwing movement.

(19) By means of the press fit which is effective between the said contact surfaces and the said pressing surfaces, compressive stresses occur which are oriented essentially perpendicular to the contact surfaces. Said stresses acting on the contact surfaces in the sintered component 2 cause both an elastic and also a plastic deformation of the sintered component 2, wherein the plastic portion causes the remaining surface compaction. With this surface compaction the powder metal particles joined by the pressing and subsequent sintering on so-called bridges are pushed against one another strongly and deformed plastically. The pore-like cavities between the powder metal particles after sintering are thereby reduced in volume and the material density is increased in this area.

(20) The effect of the surface compaction is greatest directly on the contact surface and decreases in the direction on the inside of the sintered component 2. By means of the method typically edge layers of sintered components 2 with a thickness of several hundredths of a millimeter to several tenths of a millimeter and above are compacted.

(21) The relative movement required for performing the method between the sintered component 2 and the die 1 can be performed by moving the sintered component 2 and/or by moving the die 1, whereby the sintered component 2 and the die 1 for this are each connected to a suitable drive or a fixed frame part. During the surface compaction and the subsequent calibration the sintered component 2 is clamped between an upper punch 18 and a lower punch 19. For the downwards movement the upper punch 18 pushed from above onto the sintered component 2, the lower punch 19 thereby is pulled downwards or it is also pushed downwards by the upper punch 18. For the preferred ejection of the sintered components 2 via the first die opening 6 the lower punch 19 is pushed upwards and if necessary the upper punch 18 can be pulled upwards. For said movements of the upper punch 18 and the lower punch 19 corresponding, but not shown, drives are provided.

(22) The transition from one die section 7 to 10 to the adjoining die section 8 to 11 can be in the form of chamfering 20, or provided with a rounding, wherein in pressing direction a convex rounding can adjoin a concave rounding. In this way there can be gentle transition of the sintered component 2 from one die section 7 to 10 to the next die section 8 to 11, without there being an intentional removal of material from the sintered component 2 caused by a sharp-edged step or, that the edges at transitions of the die 1 break off. As shown in FIGS. 1 and 2, such a chamfering can also be formed on the first die opening 6. The chamfering 20 or the respective roundings are part of the respective die section 7 to 11, and thus do not form an intermediate section.

(23) Although in the embodiment variant of the die 1 shown specifically in FIGS. 1 and 2 five die sections 7 to 11 are shown, the die 1 can generally have between three and eight or more than eight such die sections.

(24) As this embodiment of the die 1 is known in principle from the aforementioned EP 2 066 468 A2, reference is made to the latter for further details. EP 2 066 468 A2 belongs in this respect concerning the surface compaction to the present description.

(25) The last die section 11 shown in FIG. 1 is the section of the die 1, which has the smallest inner diameter 17 or the smallest internal width. Directly adjoining said last die section 11 with the smallest inner diameter 17 in the die 1 a relief section 21 is provided or formed. Said relief section 21 has a larger inner diameter 22 compared to the last die section 11 immediately in front of it with a decreasing inner diameter 17. In this way the sintered component 2 can relax in this relief section 21. At the same time as this relaxation in the relief section 21 the calibration of the sintered component 2 is also performed. In addition the relief section 21 has an inner contour which corresponds to the intended contour with nominal dimensions of the sintered component 2. The inner contour of the relief section 21 is with respect to both the geometry and the geometric dimensions (as viewed in cross-section) the same as the external contour of the finished sintered component 2. Said calibration of the sintered component 2 is shown in FIG. 2.

(26) Adjoining the relief section 21 the die 1 has a further section 23. Said section 23 has an inner diameter 17 or an internal width, which corresponds to the inner diameter 17 or the internal width of the last die section 11 with the smallest inner diameter 17. The section 23 is used for guiding the lower punch 19 in the die 1.

(27) The inner diameter 22 or the internal width of the relief section 21 corresponds to the outer diameter 15 (FIG. 1) or the internal width of the finished sintered component 2. Said inner diameter 22 or said internal width of the relief section 21 is greater by at least 0.02%, in particular between 0.02% and 0.1%, than the inner diameter 17 or the internal width of the last die section 11 with the smallest inner diameter 17. However, the inner diameter 22 or the internal width of the relief section 21 is not greater than the inner diameter or the internal width of the first die opening 6. In this way it is possible to achieve the at least approximately complete relaxation of the sintered component 2.

(28) As shown in FIGS. 1 and 2, the used die 1 is preferably designed in one piece so that the latter also comprises the relief section 21. However, it is also possible that at least the relief section is formed by a separate, independent, in particular plate-like die, which is arranged for performing the method for surface compaction and calibration of the sintered component 2 directly adjoining the die 1.

(29) According to one embodiment variant of the method for the surface compaction and calibration of the sintered component 2, it is possible that the inner contour of the second to last die section 10 of the sequence of die sections 7 to 11 with decreasing inner diameters 17 with respect to the geometric dimensions in a direction perpendicular to the pressing direction of the inner contour of the relief section 21 corresponds with the intended contour comprising the nominal dimensions. In other words, said second last die section 10 as viewed in cross-section can be designed to be identical to the cross-section of the relief section 21 and thus to the calibration cross-section both with respect to the geometry and also the geometric dimensions in cross-section.

(30) According to a further embodiment variant of the method, it is possible that the sintered component 2 has a first edge 24 and a second edge 25 opposite the latter in pressing direction (as is usual), which are formed at transitions between an end face 26 applicable to the die sections and axial end surfaces 27, 28 of the sintered component, and that the first and/or the second edge is/are faceted prior to insertion into the die. In FIG. 3 in addition a press die 29 is shown in longitudinal cross-section, by means of which such faceting can be produced by pressing.

(31) The press die comprises a first lower press part 30 and a second upper press part 31. The first and the second press parts 30, 31 comprise corresponding negative facets at the corresponding points at which the edges 24 or 25 of the sintered component 2 come to rest. The sintered component 2 is clamped after sintering between the first and the second press part 30, 31. By pushing together said two press parts 30, 31 by a predeterminable distance the sintered part 2 is given the faceting by material displacement.

(32) FIG. 4 shows a schematic state diagram of the sintered component 2. A line 32 shows the state of the edge after sintering, line 33 shows the state of the edge after processing in the press die 29 and line 34 shows the state of the edge after the surface compaction and calibration of the sintered component 2 in the die 1 (FIG. 1).

(33) The faceting of the edges 24, 25 of the sintered component 2 is in particular in the form of a rounding, as shown in FIG. 4. The largest rounding radiusthe facets can have a rounding radius which varies along its profile, as shown in FIG. 4, can be selected from a range of 0.1 mm to 5 mm.

(34) In principle, the first, upper edge 24 and the second, lower edge 25 of the sintered components 2 can be provided with the same facets. However, according to one embodiment variant preferably the first edge 24, which is arranged during the surface compaction and calibration of the sintered component 2 above the second edge 25, is more faceted (i.e. has a facet with a larger surface area), than the second edge 25.

(35) The method for the surface compaction and calibration of the sintered component 2 can also be used for the surface compaction and calibration of openings such as e.g. bores, in sintered components 2. Instead of the die 1 a punch is used which like the die 1 also comprises sections with different diameters and the corresponding calibrating section in the relaxation stage, where in this case however the diameter of the sections merging into one another increases (monotonically). All further explanations relating to the die 1 also relate analogously to the punch, wherein the details inner and outer need to be changed accordingly.

(36) The example embodiments show possible embodiment variants of the die 1 and/or the press die 29.

(37) Lastly, for the sake of formality it should be noted that for a better understanding of the structure of the die 1 and/or the press die 29 the latter has not been shown to scale in part and/or has been enlarged and/or reduced in size.

LIST OF REFERENCE NUMERALS

(38) 1 die 2 sintered component 3 axis 4 main die body 5 die surface 6 die opening 7 die section 8 die section 9 die section 10 die section 11 die section 12 die surface 13 die opening 14 outer surface 15 diameter 16 wall faces 17 inner diameter 18 upper punch 19 lower punch 20 chamfering 21 relief section 22 inner diameter 23 section 24 edge 25 edge 26 end face 27 end surface 28 end surface 29 press die 30 press part 31 press part 32 line 33 line 34 line