SEPARATION FLUID, METHOD AND APPARATUS FOR RECYCLING MULTILAYER MATERIAL USING A PASSIVATION AGENT

Abstract

A method for recycling of multilayer material is disclosed. The multilayer material (10) comprises a metal layer (30) and at least one further layer (20, 40). The method comprises placing the packaging material in a vat (310) comprising a separation fluid (330) to produce a mixture of metal shreds from the metal layer (30), plastic shreds from the polymer layer (20, 40) and residual components. The separation fluid comprises a mixture comprising a mixture of water, carboxylic acid, carboxylate salt and passivation agent for passivating the surface of the metal layer.

Claims

1. A separation fluid for separating multilayer systems containing at least one metal layer and one further layer, the separation fluid comprising a mixture of water, carboxylic acid, carboxylate salt and passivation agent, wherein the passivation agent is a phosphate, phosphonate, phosphinate salt or a mixture thereof.

2. The separation fluid of claim 1, wherein the carboxylic acid is in any ratio water miscible carboxylic acid and has a pK.sub.a value of between 2.0 and 8.0.

3. The separation fluid of claim 2, wherein the carboxylic acid is selected from the group of C1-C4 fatty acids consisting of formic acid, acetic acid, propionic acid or butyric acid or mixtures thereof.

4. The separation fluid of claim 1, wherein the carboxylate salt is soluble in water (solubility>10 g carboxylate per 100 g of water at 20 C.) and has a pK.sub.b value between 6.0 and 13.0.

5. The separation fluid of claim 4, wherein the counter cation of the carboxylate salt is a metal cation or a complex cation.

6. The separation fluid of claim 5, wherein the metal cation is one of the alkali metals, earth alkali metals or ammonium.

7. The separation fluid of claim 4, wherein the carboxylate salt is the corresponding Lewis-base of the used carboxylic acid.

8. The separation fluid of claim 1, wherein the passivation agent has a water solubility larger than 0.01 g per 100 g of water at 20 C.

9. The separation fluid of claim 8, wherein a counter cation of the passivation agent is a metal cation or a complex cation.

10. The separation fluid of claim 9, wherein the metal cation is one of the alkali metals, earth alkali metals or ammonium.

11. The separation fluid of claim 1, wherein components of the separating mixture comprise 5-60% by weight of carboxylic acid, up to 5% by weight of passivation agent and 0.05-10% by weight of carboxylate salt, and 30-95% by weight of water.

12. The separation fluid of claim 1, wherein components of the separating mixture comprise 20-50% by weight of carboxylic acid, 0.02-2% by weight of passivation agent and 0.5-5% by weight of carboxylate salt, and 40-80% by weight of water.

13. A method for the separation of a metal layer from a further layer in a multiple layer material comprising: placing the multiple layer material in a vat with a separation fluid, wherein the separation fluid comprises a mixture of water, carboxylic acid, carboxylate salt and passivation agent, wherein the passivation agent is a phosphate, phosphonate, phosphinate salt or a mixture thereof.

14. The method of claim 13, further comprising at least one of sieving or filtering the separation fluid with components of the multiple layer material and thereafter sorting to obtain a first fraction of metal from the metal layer and a second fraction of plastic from the polymer layer.

15. The method of claim 13, wherein the separation is carried out at a temperature of between 20 C. and 90 C.

16. The method of claim 13, wherein the separation fluid has a pH value of between 1.5 and 5.

17. The method of claim 13, wherein the multilayer material comprises at least one metal layer, preferably an aluminium layer, and at least one polymer layer, preferably consisting of polyester or polyolefin.

18. A method for recycling packaging material comprising a multiple layer material comprising at least one metal layer and at least one further layer, wherein the method comprises: placing the packaging material in a vat comprising a separation fluid, wherein the separation fluid comprises a mixture of water, carboxylic acid, carboxylate salt and passivation agent, wherein the passivation agent is a phosphate, phosphonate, phosphinate salt or a mixture thereof.

19. An apparatus for the recycling of packaging material made from a multiple layer material comprising: a vat having a separation fluid, the separation fluid comprising a mixture of water, carboxylic acid, carboxylate salt and passivation agent, wherein the passivation agent is a phosphate, phosphonate, phosphinate salt or a mixture thereof; a transportation device for transporting the packaging material into the vat; and a sieving/filtration device for removing separated materials from the combination of the separation fluid and the packaging material.

Description

DESCRIPTION OF THE FIGURES

[0053] For a more complete understanding of the present invention and the advantages thereof, reference is now made to the following description and the accompanying drawings, in which:

[0054] FIG. 1 shows one illustrative example of a laminate used in an aseptic packaging, which is recycled using the separation fluid and the method of this disclosure.

[0055] FIG. 2 shows a flow diagram of the method using the teachings of this disclosure.

[0056] FIG. 3 shows an overview of the apparatus for recycling using the teachings of this disclosure.

DETAILED DESCRIPTION OF THE INVENTION

[0057] The invention will now be described with reference to the drawings. It will be understood that the embodiments and aspects of the invention described herein are only examples and do not limit the protective scope of the claims in any way. The invention is defined by the claims and their equivalents. It will be understood that features of one aspect or embodiment of the invention can be combined with the feature of a different aspect or aspects and/or embodiments of the invention.

[0058] FIG. 1 shows a non-limiting example of a laminate 10 used in an aseptic packaging. The laminate 10 comprises a first polymer layer 20, which is bonded to an aluminium layer 30, which is bonded in turn to a second polymer layer 40. Bonding agents are used between the different layers. Such bonding agents include, but are not limited to, ethylene/acrylic acid copolymer and/or polyurethane adhesives.

[0059] The laminate 10 is used, in one aspect of the invention, in an aseptic packaging, such as the ones used for stand-up pouches for beverages such as fruit juice and milk as well as tomato purees and similar fluids. Similar packaging is also used for other foods, such as snack foods, as well as for cosmetics. In some applications, one of the polymer layers is printed on one side, for example with a product description, or indeed on both sides.

[0060] In one non-limiting example of the invention, the polymer layer 20 is made of low-density polyethylene (LDPE) and the polymer layer 40 is made of polyethylene terephthalate (PET). The metal layer 30 is made of aluminium. This is not limiting of the invention and other polyolefins or plastics, such as polypropylene (PP), polyamides or polyesters, could be used. Similarly, the metal layer 30 could be an aluminium alloy or another metal.

[0061] Some types of packaging comprise only a single polymer layer 20 with the metal layer 30. For example, rejects from the production may only have the single polymer layer 20 with the metal layer 30. Other types of packaging material comprise two polymer layers 20 and 40 made of the same polymer. The teachings of this disclosure are also applicable to these types of multilayer materials and are not restricted to the multilayer materials mentioned.

[0062] FIG. 3 shows an overview diagram, which is an example of a recycling plant for the recycling of the multilayer laminates 10 of this disclosure. It will be appreciated that the plant shown in FIG. 3 is merely exemplary and is not limiting of the invention. The multilayer laminates 10 are constructed as above.

[0063] The recycling plant includes a cutting or shredding device 300, which cuts and shreds bales 50 of the packaging material made of the multilayer laminates 10. The cutting or shredding device 300 is followed by a vat 310 with an agitator 320 to stir up and agitate up the contents of the vat 310. The vat 310 contains a separation fluid 330 and a fluid dispenser 340 for dispensing the separation fluid 330 into the vat 310.

[0064] The materials can be sieved from the separation fluid 330 in a sieving device 350, and then the sieved materials will be washed with water in a washer 360. A first sorting step for separating components from the sieved materials can be conducted in wet environments, e.g. by use of float-sink-separation or centrifugation techniques, in a wet sorter 370. This results generally in two material streams. In the non-limiting example of the laminate 10 outlined above, one of the two material streams is substantially low-density polyethylene and the other of the material streams is a mixed stream comprising a mixture of aluminium and PET. The two material streams can be washed in a further washing step, if necessary.

[0065] The resulting two material streams can be dried in a drying unit 380 and subsequently purified in a dry sorting unit 390. The dry sorting, e.g. to extract the aluminium and the PET from the mixed stream, can be done, for example, by wind-sifting or electromagnetically based techniques. It will be appreciated that the sorting (wet or dry) can also be conducted in a single device or in more than two devices, depending on requirements.

[0066] The separation fluid 330 is recycled in a fluid recycling device 355, mostly to be cleaned of impurities by filtration and replenishing consumed chemicals. The washing water is also recycled to clean the washing water in a water-recycling device 365. The recycling includes cross-flow filtration techniques, reverse osmosis and/or liquid-liquid extraction, which also allow reclaiming of at least some of the chemicals of the separation fluid 330 from the washing water.

[0067] FIG. 2 shows an outline of the method for recycling of the laminates 10 used in the apparatus shown in FIG. 3. The laminates 10 are collected together as bales 50 of packaging material. The laminates 10 will generally have been pressed together in the bales 50 to reduce their volume. The laminates 10 may have been washed to remove any food rest at a waste refuse collection and/or processing plant. On arrival at the recycling plant, the bales 50 are placed first into the cutting and shredding device 300 for size reduction in step 200. Batches of the cut/shred laminates 10 are then loaded into the vat 310. The agitator 320 mixes the laminates 10 in step 210 with the separation liquid 300 in the vat 310 to produce a mixture.

[0068] In step 230, the mixture of the laminates 10 and the separation fluid 330 is further agitated and stirred for a pre-defined treatment time, e.g. 4 hours, leading to a separation of the multilayer laminates 10 into its constituent layers, i.e. the first polymer layer 20 of LDPE, the aluminium layer 30 and the second polymer layer 40 of the PET (in non-limiting example described above). In general, the effect of the separation fluid 330 is to delaminate the first polymer layer 20 of LDPE and/or the second polymer layer 40 and the metal layer 30 to produce metal shred from the metal layer 30 and polymer shred from the first polymer layer 20 and the second polymer layer 40. This is achieved at a given temperature, for example between 20 C. and 90 C., during a treatment time of typically between 30 minutes and 300 minutes. In one aspect of the method, the given temperature is 70 C. In another aspect of the method for universal beverage cartons, the given temperature will be between 30 C. and 50 C. The choice of temperature and process time largely depends on the type of polymer materials and the adhesive bonding agents as well as the thickness of the single layers to be delaminated. The layers being bonded together with bonding agents from ethylene/acrylic acid copolymers delaminate at around 40 C. and those with bonding agents from polyurethane adhesives delaminate at around 70 C.

[0069] The mixture of the separation fluid 330 and the separated materials, i.e. LDPE, aluminium and PET can be removed from the vat 310 and sieved in step 240 in the sieve 350 to remove the solid materials, which include the LDPE from the first polymer layer 20, the PET from the second polymer layer 40 and most of the metal shred from the metal layer 30. The separation fluid 330 is then recycled by the device 355. The recycling is carried out by filtration in step 245 and replenishment of consumed chemicals in step 246. The recycled fluid is then placed back into the fluid dispenser 340. The filtration step 245 in device 355 removes substantially all of the solid impurities from the separating fluid 330, including the metal shred, which was not sieved out previously.

[0070] The solid material sieved out in step 240 is a mixture of the polymers and aluminium. This resulting material is washed in step 250 in the washer 360, and is then sorted in a wet sorting step 260 in the wet sorter 370 by means of a float-sink-separation or centrifugation technique into a light material, comprising mostly the LDPE, and a dense material, comprising mostly the aluminium and the PET. The light materials and the dense materials are dried separately in the steps 270 (light material) and 271 (dense material). The dried dense material is further sorted in step 280 in the dry sorter 390 by means of wind-sifting or electromagnetic techniques, to obtain an aluminium-rich material and a PET-rich material. It will be appreciated that the sorting (wet or dry) can also be conducted in one step, or in more than two steps depending on the requirements.

[0071] The washing water needs to be treated in step 255 with the water recycling device 365 before the washing water is also reused. These treatments include several filtration steps, with regular and cross-flow filtration techniques, reverse osmosis and/or liquid-liquid-extraction, which also allow at least some chemicals from the washing water to be reclaimed and transferred to the fluid recycling device 355 for reuse. In one aspect, the water recycling device 365 comprises a liquid-liquid-extraction unit combined with reverse osmosis.

[0072] The LDPE-rich materials can be extruded into granules in step 290. The metal shreds can be pressed into pellets in step 291 for recycling. Similarly, the PET-rich material can be compacted for shipment in step 292. The post treatment steps 290, 291 and 292 can be done in the devices 395, for example by extrusion or pressing machines.

[0073] The separating fluid 330 used in the vat 310 and coming from the fluid dispenser 340 comprises a mixture of water, carboxylic acid, carboxylate salt and passivation agent. The carboxylic acids are, for example, in any ratio water miscible C1-C4 monocarboxylic acids, such as formic acid, acetic acid, propionic acid and butyric acid. The carboxylate salt is, for example, the sodium salt of the corresponding carboxylic acid used. As an example, it will be understood that sodium acetate will be used if acetic acid is used as a water miscible monocarboxylic acid. The applied passivation agent here is the sodium dihydrogen phosphate sharing preferably the same counter ion originating from the carboxylate salt. The water is in one aspect of the invention deionised. Mainly the carboxylic acid penetrates the layer to which the metal layer is bonded and afterwards delaminates the aluminium from the adhesive layer of the multilayer material. The passivation agent is added in order to control the side reaction of aluminium dissolution, as discussed above (see eqn. (1)).

[0074] The separation fluid 330 is kept between 20 C. and 90 C., and at pH values between 1.5 and 5. The actual values are chosen depending on the properties of the input laminates 10 or other multilayer materials in the packaging material. Usually, a low pH value favours performance of the separation, but also a side reaction which results in the dissolution of the aluminium. Ideally, the method of this disclosure achieves a sufficiently high yield of metal from the metal layer 30 or the polymers from the first polymer layer 20 and the second polymer layer 40 within the treatment time, while keeping the dissolution of the metal layer 30 to a minimum. The minimal dissolution of the metal layer 30 is important for safety reasons, since dissolution of the aluminium also leads to the formation of gaseous hydrogen, which represents an explosion hazard. Furthermore, the overall economy of the process is improved by lower aluminium loss and needed chemical input. The pH value has therefore to be adjusted to the separation fluid 330 to balance between reasonable delamination time and efficient passivation afterwards.

[0075] The separation fluid 330 contains the passivation agent sodium dihydrogen phosphate in order to control the content of the dissolved aluminium in the separation fluid 330. The aluminium precipitates as aluminium phosphate under suitable conditions, by adjusting the pH value. The aluminium phosphate is a finely dispersed solid, which can be filtered out from the liquid in the step 245.

[0076] The passivation agent induces a thin passivation coverage layer of aluminium phosphate on the aluminium surfaces. These surface phosphates act as an inhibitor, partially passivating the aluminium surfaces from further chemical attack from the carboxylic acid. The reaction products leave the separation fluid 330 in solid form, aluminium phosphate, or in gaseous form, hydrogen. The passivation agent is consumed and has to be replenished. This replenishment happens in the recycling device 355 during the step 246, alongside the replenishment of the other chemicals.

Other Examples of Multiple Layer Materials Used in Packaging

[0077] Non-limiting examples of other multiple layer materials used in packaging materials include LDPE (=low-density polyethylene)/aluminium/PET, which is used in coffee packaging and drinks packaging, or PP (=polypropylene)/aluminium/polyester laminates used in coffee packaging and pet food packaging, or LDPE/aluminium/LDPE, which is used in packaging for granulated raw materials for the industry or in tooth paste tubes. Another example are the inner parts (polymer and aluminium) of aseptic universal beverage carton which are usually composed of LLDPE (=linear low density polyethylene)/aluminium/LLDPE.

Composition Examples with Corresponding Application Examples (Laboratory Scale)

[0078] The compositions listed below are merely examples of suitable formulations and are not limiting of the invention (all percentages by weight). The corresponding examples listed below to each composition are merely examples of suitable applications and are not intended to be limiting of the invention.

Composition 1

[0079]

TABLE-US-00001 Water 52.9% Acetic acid 42.5% Sodium acetate 3.5% Sodium dihydrogen phosphate 1.1%

Example 1-1

[0080] 60 g of LDPE/aluminium/PET material (flakes, 1 cm.sup.2, from beverage stand-up pouches) are stirred with 1 kg of separation liquid (composition 1) at 70 C. The detachment of the LDPE form the aluminium is complete after 2 h and the detachment of the PET from the aluminium is complete after 4 h.

Example 1-2

[0081] 30 g of LDPE/aluminium/PET material (flakes, 3 cm.sup.2, from snack food packaging) are stirred with 1 kg of separation liquid (composition 1) at 70 C. The detachment of the LDPE from the aluminium is complete after 2 h and the detachment of the PET from the aluminium is complete after 4 h.

Example 1-3

[0082] 60 g of LDPE/aluminium/LDPE material (flakes, 2 cm.sup.2, from tooth paste tubes) are stirred with 1 kg of separation liquid (composition 1) at 70 C. The detachment of the LDPE from the aluminium is complete after 2 h.

Example 1-4

[0083] Three single specimens of PP/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 1) at 70 C. The detachment of the PP and of the PET from the aluminium is complete after 5 h.

Example 1-5

[0084] 30 g of LLDPE/aluminium/LLDPE+LLDPE material (flakes, 10 cm.sup.2, inner parts of aseptic beverage carton) are stirred with 1 kg of separation liquid (composition 1) at 40 C. The detachment of aluminium from the LLDPE is complete after 2 h.

Example 1-6

[0085] 20 g of OPA/aluminium/LLDPE material (flakes, 1 cm.sup.2, large volume pouch for gastronomic beer storage) are stirred with 1 kg of separation liquid (composition 1) at 70 C. The detachment of aluminium from the OPA and the LLDPE is complete after 5 h.

[0086] Examples 1-1 to 1-6 elucidate different packaging materials which can be treated with the separation fluid composition 1 within the scope of the present invention.

Composition 2

[0087]

TABLE-US-00002 Water 53.0% Formic acid 43.0% Sodium formiate 2.9% Sodium dihydrogen phosphate 1.1%

Example 2-1

[0088] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 2) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 1 h.

Composition 3

[0089]

TABLE-US-00003 Water 53.0% Propionic acid 41.8% Sodium propionate 4.1% Sodium dihydrogen phosphate 1.1%

Example 3-1

[0090] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 3) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 10 h.

[0091] The compositions 1 to 3 illustrate formulations with different carboxylic acids.

Composition 4

[0092]

TABLE-US-00004 Water 52.7% Acetic acid 43.4% Potassium acetate 2.7% Potassium dihydrogen phosphate 1.2%

Example 4-1

[0093] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 4) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 8 h.

[0094] The composition 4 illustrates a formulation with potassium as the counter cation of the carboxylate salt, potassium acetate, and the passivation agent, potassium dihydrogen phosphate.

Composition 5

[0095]

TABLE-US-00005 Water 65.4% Acetic acid 30% Sodium acetate 3.5% Sodium dihydrogen phosphate 1.1%

Example 5-1

[0096] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 5) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 6 h.

Composition 6

[0097]

TABLE-US-00006 Water 35.4% Acetic acid 60% Sodium acetate 3.5% Sodium dihydrogen phosphate 1.1%

Example 6-1

[0098] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 6) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 3.5 h.

[0099] Compositions 1, 5 and 6 illustrate formulations with different amounts of carboxylic acid.

Composition 7

[0100]

TABLE-US-00007 Water 77.2% Acetic acid 20% Sodium acetate 1.7% Sodium dihydrogen phosphate 1.1%

Example 7-1

[0101] Five single specimens of PE/aluminium/PE flakes (1 cm.sup.2, laminate sample like used beverage carton) are shaken with 20 g of separation liquid (composition 7) at 70 C. The detachment of the PE from the aluminium is complete after 3.5 h.

Composition 8

[0102]

TABLE-US-00008 Water 88.0% Acetic acid 10% Sodium acetate 0.9% Sodium dihydrogen phosphate 1.1%

Example 8-1

[0103] Five single specimens of PE/aluminium/PE flakes (1 cm.sup.2, laminate sample like used beverage carton) are shaken with 20 g of separation liquid (composition 8) at 70 C. The detachment of the PE from the aluminium is complete after 5 h.

Composition 9

[0104]

TABLE-US-00009 Water 93.5% Acetic acid .sup.5% Sodium acetate 0.4% Sodium dihydrogen phosphate 1.1%

Example 9-1

[0105] Five single specimens of PE/aluminium/PE flakes (1 cm.sup.2, laminate sample like used beverage carton) are shaken with 20 g of separation liquid (composition 9) at 80 C. The detachment of the PE from the aluminium is complete after 7 h.

[0106] Compositions 1, 5, 6, 7, 8 and 9 illustrate formulations with different amounts of carboxylic acid.

Composition 10

[0107]

TABLE-US-00010 Water 54.01% Acetic acid 42.47% Sodium acetate 3.50% Sodium dihydrogen phosphate 0.02%

Example 10-1

[0108] 80 g of LDPE/aluminium/PET material (flakes, 1 cm.sup.2, from beverage stand-up pouches) are stirred with 2 kg of separation liquid (composition 10) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 4 h.

Composition 11

[0109]

TABLE-US-00011 Water 53.84% Acetic acid 42.48% Sodium acetate 3.50% Sodium dihydrogen phosphate 0.18%

Example 11-1

[0110] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 11) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 4 h.

[0111] Compositions 1, 10 and 11 illustrate formulations with different amounts of sodium dihydrogen phosphate as passivation agent.

Composition 12

[0112]

TABLE-US-00012 Water 53.7% Acetic acid 44.7% Sodium acetate 0.5% Sodium dihydrogen phosphate 1.1%

Example 12-1

[0113] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 12) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 2 h. The aluminium flakes showed first indications for corrosion.

Composition 13

[0114]

TABLE-US-00013 Water 53.5% Acetic acid 43.9% Sodium acetate 1.5% Sodium dihydrogen phosphate 1.1%

Example 13-1

[0115] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 13) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 3 h.

[0116] Compositions 1, 12 and 13 illustrate formulations with different amounts of sodium acetate as carboxylate salt.

Composition 14

[0117]

TABLE-US-00014 Water 53.05% Acetic acid 42.5% Sodium acetate 3.5% Sodium monohydrogen phosphonate (NaHPO.sub.3H) 0.95%

Example 14-1

[0118] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 14) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 4 h.

Composition 15

[0119]

TABLE-US-00015 Water 53.19% Acetic acid 42.5% Sodium acetate 3.5% Sodium phosphinate (NaPO.sub.2H.sub.2) 0.81%

Example 15-1

[0120] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 15) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 4 h.

Composition 16

[0121]

TABLE-US-00016 Water 52.5% Acetic acid 42.5% Sodium acetate 3.5% 45:55 Mixture monosodium monoethyl 1.5% phosphate and monosodium diethyl phosphate

Example 16-1

[0122] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 16) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 3 h.

Composition 17

[0123]

TABLE-US-00017 Water 52.9% Acetic acid 42.5% Sodium acetate 3.5% Monosodium methylphosphonate (CAS 2914-38-7) 1.1%

Example 17-1

[0124] Five single specimens of PE/aluminium/PET flakes (1 cm.sup.2, laminate sample like coffee packaging from foil and converter companies) are shaken with 20 g of separation liquid (composition 17) at 70 C. The detachment of the PE and of the PET from the aluminium is complete after 4 h.

[0125] Compositions 1, 14, 15, 16 and 17 illustrate formulations with different passivation agents in form of phosphate, phosphonate and phosphinate sodium salts.

[0126] The foregoing description of the preferred embodiment of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The embodiment was chosen and described in order to explain the principles of the invention and its practical application to enable one skilled in the art to utilize the invention in various embodiments as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto and their equivalents. The entirety of each of the aforementioned documents is incorporated by reference herein.

REFERENCE NUMERALS

[0127] 10 Multilayer material [0128] 20 First polymer layer [0129] 30 Metal layer [0130] 40 Second polymer layer [0131] 50 Bales [0132] 300 Cutting or shredding device [0133] 310 Vat [0134] 320 Agitator [0135] 330 Separation fluid [0136] 340 Fluid dispenser [0137] 350 Sieving device [0138] 355 Fluid recycling device [0139] 360 Washer [0140] 365 Water-recycling device [0141] 370 Wet sorter [0142] 380 Drying unit [0143] 390 Dry sorting unit [0144] 395 Post processing