METHOD FOR PRODUCING A BEAM GUIDE GRID AND A BEAM GUIDE GRID PRODUCED IN ACCORDANCE WITH THE METHOD

Abstract

The invention relates to a process for producing a beam guiding grid (4), comprising a molding having a grid of passageways (40) and wall areas surrounding them, from radiation-absorbing metal powder and binder, especially tungsten powder and binder. Advantageous production is achieved in that the molding is produced by injection molding, wherein the homogenized mixture, as a prepared flowable injection compound, is injected using an injection molding machine into a molding tool (7) that produces the molding, into which movable mold cores (72) were introduced prior to filing with the molding composition.

Claims

1. A process for producing a beam guiding grid (4), consisting of a molding, provided with a grid of passageways (40) and wall areas surrounding these, from a mixture of radiation-absorbing metal powder and binder, especially tungsten powder and binder, characterized in that the molding is produced by injection molding, wherein the homogenized mixture is filled, as a flowable prepared injection compound, using an injection machine into a molding tool (7) forming the molding, into which movable mold cores (72) were introduced before the injection compound was filled in.

2. The process according to claim 1, characterized in that the binder used for the injection process is a preheated and plasticized thermoplastic or duroplastic material.

3. The process according to claim 2, characterized in that a polyether ketone, especially polyether ether ketone (PEEK), is used as the thermoplastic.

4. The process according to claim 1, characterized in that the ratio of metal powder, especially tungsten powder, to binder in volume-percent is in the range of 30/70 to 98/2.

5. The process according to claim 1, characterized in that during the molding, to make the axes of the passageways (40) align at an acute angle to one another toward a common focal pointthe mold cores (72) in the molding tool are arranged and shaped according to the orientation, the grid and the shape of the passageways (40), held outside of a wall section of the molding tool (7) on a storage unit (8) and after introduction and pre-solidification of the injection compound and prior to ejecting the molding, are withdrawn from the passageways (40).

6. The process according to claim 5, characterized in that for preparing for the molding process, the mold cores (72) are placed in molding position using a displacement (9) unit that moves the storage unit (8) with the mold cores (72) into molding position and after pre-solidification, are withdrawn from the passageways (40) by the displacement unit (9) that moves the storage unit (8).

7. The process according to claim 5, characterized in that the mold cores (72) are introduced through individually assigned feed-throughs in the wall section of the molding tool (7) and drawn through these, wherein they are held in a floating manner on the storage unit (8) to compensate for a lateral movement component in the x and/or y direction due to oblique positioning of the passageways (40) and feed-throughs during the introduction and withdrawal.

8. A beam guiding grid (4), formed from a molding with a grid of passageways (40) and X-ray or gamma ray absorbing wall areas surrounding them, molded from a homogeneously distributed metal powder bound in a binder, especially tungsten powder, according to claim 1, characterized in that the binder is a thermoplastic or duroplastic plastic or predominantly contains such a plastic.

9. The beam guiding grid (4) according to claim 4, characterized in that the passageways (40) are aligned toward a focal point with their central axes at an acute angle with respect to one another.

10. The beam guiding grid (4) according to claim 8, characterized in that the passageways (40) taper conically from a beam incidence side to a beam exit side, wherein the angle of conicity with respect to the central axis is a maximum of 1.

11. The beam guiding grid (4) according to claim 8, characterized in that the grid distance from center to center of the passageways (40) is a maximum of 2 mm and the thickness of the wall regions at their thinnest point is a maximum of 200 m.

12. An arrangement of a plurality of beam guiding grids (4) structured according to claim 8, in an optical system containing at least one X-ray source, in which the passageways (40) are aligned with their central axes toward the X-ray source.

13. The use of beam guiding grids (4) according to claim 8 in computed tomography.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0025] FIG. 1 a schematic view of the insertion of a beam guiding grid in an X-ray device such as a computed tomograph,

[0026] FIG. 2 an enlarged sectional view of a beam guiding grid in longitudinal section,

[0027] FIG. 3 a sectional top view of a beam guiding grid in schematic representation and

[0028] FIG. 4 an injection molding tool for producing a beam guiding grid in a perspective sectional view in schematic representation.

DETAILED DESCRIPTION OF THE INVENTION

[0029] In FIG. 1 the use of a beam guiding grid, also known as an anti-scattering grid or collimator, in an imaging device 1 for X-ray diagnostics is shown. At a focus point, for example at a distance of one meter, a radiation source 2 for emitting X-rays is arranged, which penetrate a body K with an object O to be examined. Then the X-rays, which contain the image information of the object O, pass through passageways 40 of the beam guiding grid 4 as primary rays 30 and are recorded by a receiver unit 5, which generally has receiver elements arranged as a matrix. Then an analyzable image of the object O is reconstructed from the individual recordings. An examination using gamma rays, i.e., with beams from the area of electromagnetic radiation following the shorter wavelength range of the X-rays, can also be performed similarly. Then the radiation source 2 is designed as a gamma radiation source and the receiver unit 5 is selected correspondingly.

[0030] As is further shown schematically in FIG. 1, at scattering centers contained, for example, in the body K, scattered radiation 31 may be formed upon passage of the beam 3, interfering with or obscuring the image obtained from the primary rays 30, so that evaluation of the image information is made difficult or can no longer take place in detail. With the beam guiding grid, scattered radiation is largely absorbed because the passageways 40 of the beam guiding grid 4 are surrounded with absorbent wall areas 41. Suitable absorbent materials which contain appropriate metals, for example tungsten or metals with similar X-ray- or gamma-ray-absorbing properties, are known in and of themselves.

[0031] So that the primary rays 30 can pass through the beam guiding grid 4 unimpeded, the passageways 40 with their absorbent wall areas are aligned on their focal point located in the radiation source 2, as is indicated in the sectional drawing according to FIG. 2. As is apparent from FIG. 3, the beam guiding grid 4 extends two-dimensionally and, for example is provided with passageways 40 with cross sections of rectangular, square, or polygonal shape; round, oval or other appropriate free-form shape.

[0032] The recording device 1 has a system comprising a plurality of adjacently arranged beam guiding grids 4 to obtain the most complete possible image of the object O. For example, the individual beam guiding grids 4 have a height (in reference to the beam passage) of between 4 and 20 mm and a length and width of several centimeters, and the cross-sectional dimension of the passageways is, for example, in the range of about one millimeter, e.g., between 0.5 and 1.5 mm. The thickness of the wall regions is between, e.g., 40 m and 200 m, for example between 60 m and 150 m, wherein a range between e.g., 80 m and 120 m can be suitable. The oblique positioning of the passageways 40 relates, for example, to a common focal point at a distance of one meter, so that the individual passageways 40 travel at an acute angle relative to one another with regard to the focal point.

[0033] As was described initially, the requirements on the described design of the beam guiding grid 4 entail a relatively high cost. To make the cost more economical, especially in view of large numbers of pieces and uniformly good workmanship, the beam guiding grids 4 according to the invention are produced using injection molding technology, wherein the design and the procedure are characterized by special measures, as is shown schematically by FIG. 4.

[0034] FIG. 4 shows an injection tool disposed in an injection molding machine at the outlet in front of an injection nozzle that injects an injection material. The injection tool has a molding tool 7 with a cavity for an injection body subsequently forming the beam guiding grid 4 or a molding 6. A plate-shaped molding 70 is arranged on the nozzle side and forms the outer peripheral contour of the molding 6. Beneath the molding 70 on the discharge side is an additional plate-shaped molding 71. In the additional molding 71 on the discharge side, passage openings are arranged, through which displaceable mold cores 72 are passed in the direction of the passageways 40 is present in the molding 6. Only a few of these pin-like mold cores 72 are shown in FIG. 4. Actually, such mold cores 72 are present for all of the passageways 40.

[0035] Each of the mold cores 72 is individually aligned at the necessary acute angle with reference to the focal point toward a vertical axis (z-axis) of the beam guiding grid 4 and the molding 6, wherein the beam guiding grid 4 and the molding 6 each extend in length and width in a plane perpendicular to in the X/y direction. With mold cores 72 introduced into the cavity, an injection composition is introduced through the corresponding nozzle of the injection molding machine for producing the molding 6 to produce the absorbent wall regions 41, wherein the injection composition is formed from a mixture of radiation-absorbing metal powder and binder, thus especially tungsten powder and binder.

[0036] The heated liquid injection composition is then cooled to a temperature that causes pre-solidification of the molding 6. Then the mold cores 72 are withdrawn from the passageways of the molding 6 by means of a holder 80 bearing the mold cores 72 by actuating an adjusting unit 9. For this purpose, the holder 80 has mold core holders 81 which permit lateral displacement with respect to the z direction during the withdrawal of the mold cores 72 from the molding 6, since during the withdrawal of the mold cores 72 in the z direction, because of the oblique positioning of the passageways 40, a lateral motion component in the X or y direction is superimposed on the mold cores 72. The mounting of the mold cores 72 in the mold core holders 81 is therefore of the floating type. Correspondingly, the floating design also makes lateral displacement in the X and y directions possible during the introduction of the mold cores 72 through the passages of the additional mold part 71 on the ejector side.

[0037] As FIG. 4 shows, for the floating support, for example, a few horizontal guides extending in the X direction for a respective line of mold cores 72 are present, while the guides with the respective mold cores 72 can in turn be displaced in the y direction, so that in the direction of the opening as well a corresponding alignment of the passageways 40 can be done to compensate during the introduction or removal of the mold cores 72.

[0038] As an advantageous measure for unmolding it has been found that the mold cores 72 are conically tapered slightly or more or less extensively in the direction toward the focal point.

[0039] The opening of the injection molding tool or molding tool 7 to eject the molding 6 or the beam guiding grid 4 takes place between the molding 70 and the additional molding 71.

[0040] It was also found during studies by the inventor that for example a thermoplastic made of polyether ketone, especially polyether ether ketone (PEEK), can be advantageously used as the binder, allowing stable properties and moldability at a relatively high temperature (e.g., between 330 C. and 450 C.). The temperature difference between the temperature during filling of the molding tool 7 and withdrawal of the mold cores 72 is, for example, 70 C., for which the temperature control system of the injection molding machine has been made appropriately controllable. Other thermoplastic binders or duroplastic binders are also conceivable. The degree of filling of the injection compound, homogeneously prepared with metal powder, falls in the range, in parts by volume of metal powder or tungsten powder, from 30/70 to 98/2 parts metal powder to binder, e.g., between 40/60 to 95/5, 50/50 to 90/10 or 60/40 to 85/15, wherein ratios falling between these may also be considered. The materials selected for the radiation-absorbing metal powder and the binder as well as the geometric ratios of the beam guiding grid and thickness of the wall areas must also be considered.

[0041] The process according to the invention gives an economical production method for beam guiding grids 4, especially in large quantities and with consistently high quality.