FLUX-CORED WIRE FOR GAS SHIELD ARC WELDING

Abstract

A flux-cored wire for gas shielded arc welding may contain, based on total mass of the wire: Fe: 78 mass % or more; TiO.sub.2: 4 mass % to 13 mass %; Mn: 1.0 mass % to 2.4 mass %; Cr: 1.0 mass % to 3.0 mass %; Mo: 0.2 mass % to 1.2 mass %; Si: 0.1 mass % to 0.8 mass %; Mg: 0.1 mass % to 1.0 mass %; fluoride (F conversion value): 0.05 mass % to 0.25 mass %; C: 0.01 mass % to 0.10 mass %; V: 0.003 mass % to 0.020 mass %; Nb: 0.003 mass % to 0.020 mass %; and B: less than 100 ppm (including 0 ppm). The contents of Mn, C, and V based on total mass of the wire may satisfy a relationship of 28Mn/(390C+2370V)0.82.

Claims

1. A flux-cored wire configured for gas shielded arc welding, comprising, based on total wire mass: Fe in an amount of 78 mass % or more; TiO.sub.2 in a range of from 4 to 13 mass %; Mn in a range of from 1.0 to 2.4 mass %; Cr in a range of from 1.0 to 3.0 mass %; Mo in a range of from 0.2 to 1.2 mass %; Si in a range of from 0.1 to 0.8 mass %; Mg in a range of from 0.1 to 1.0 mass %; fluoride in a range of from 0.05 to 0.25 mass %, based on a F conversion value; C in a range of from 0.01 to 0.10 mass %; V in a range of from 0.003 to 0.020 mass %; Nb in a range of from 0.003 mass % to 0.020 mass %; and optionally, B in an amount of less than 100 ppm, wherein the contents of Mn, C, and V based on total mass of the wire satisfy a relationship of 28Mn/(390C+2370V)0.82.

2. The wire of claim 1, wherein the contents of TiO.sub.2, Mg, Nb, and V based on the total wire mass satisfy a relationship
0.018TiO.sub.2Mg+2(Nb+V)0.12.

3. The wire of claim 1, wherein a content of at least one of P, S, and N, based on the total wire mass, is in a range of from 0 to 0.02 mass %.

4. The wire of claim 1, wherein a content of at least one of Na and K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

5. The wire of claim 2, wherein a content of at least one of P, S, and N, based on the total wire mass, is in a range of from 0 to 0.02 mass %.

6. The wire of claim 2, wherein a content of at least one of Na and K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

7. The wire of claim 3, wherein a content of at least one of Na and K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

8. The wire of claim 5, wherein a content of at least one of Na and K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

9. The wire of claim 5, wherein a content of K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

10. The wire of claim 5, wherein a content of Na, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

11. The wire of claim 5, wherein a content of Na and K, based on the total wire mass, is in a range of from 0.01 to 0.20 mass %.

12. The wire of claim 1, wherein the TiO.sub.2 is present in at least 4.5 mass %.

13. The wire of claim 1, wherein the TiO.sub.2 is present in at least 5.0 mass %.

14. The wire of claim 1, wherein the TiO.sub.2 is present in no more than 12 mass %.

15. The wire of claim 1, wherein the TiO.sub.2 is present in no more than 11 mass %.

16. The wire of claim 1, wherein the Mn is present in at least 1.1 mass %.

17. The wire of claim 1, wherein the Mn is present in at least 1.2 mass %.

18. The wire of claim 1, wherein the Mn is present in no more than 2.3 mass %.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0015] FIG. 1a is a sectional view showing a sampling position of a cylindrical test piece used for evaluation of SR crack resistance.

[0016] FIG. 1b is a sectional view showing a shape of the cylindrical test piece used for evaluation of SR crack resistance.

[0017] FIG. 1c is a view for explaining the cylindrical test piece of FIG. 1a and FIG. 1b.

[0018] FIG. 1d is a sectional view showing a ring crack test using the cylindrical test piece.

DESCRIPTION OF EMBODIMENTS

[0019] Hereinafter, embodiments for carrying out the present invention will be described in detail. The present invention is not limited to the embodiments described below.

[0020] [Component Composition of Flux-Cored Wire]

[0021] Hereinafter, a reason for limiting the component composition of the flux-cored wire for gas shielded arc welding of the embodiment (hereinafter, also simply referred to as wire) will be described. A content of the components of the wire of the present embodiment is a content based on total mass of the wire.

[0022] TiO.sub.2 content: 4 mass % to 13 mass %

[0023] TiO.sub.2 is a main component of a slag forming agent and acts as an arc stabilizer. Further, in the case where the wire contains N, Ti generated by reducing part of TiO.sub.2 by Si, Mn, Mg, and a fluoride combines with N to form TiN and the formed TiN is precipitated in the weld metal, and extremely effectively acts to prevent the formation of a ferrite band. TiO.sub.2 is a main component of the slag forming agent, a reduction reaction of the part of TiO.sub.2 is likely to be performed under a high temperature atmosphere in the arc, and the reduction reaction can be accelerated by containing TiO.sub.2 in the flux. Therefore, TiO.sub.2 is contained in the flux.

[0024] In the case where the TiO.sub.2 content is too low, stability of the arc is impaired, the wire cannot be practically used from the standpoint of weldability, and an amount of Ti generated by reduction decreases, so that a precipitation amount of TiN also decreases, and an effect of preventing the formation of the ferrite band is insufficient. Therefore, the TiO.sub.2 content is 4 mass % or more, preferably 4.5 mass % or more, more preferably 5.0 mass % or more.

[0025] On the other hand, in the case where the TiO.sub.2 content is too high, viscosity of the slag is extremely large, which causes welding defects such as slag entrainment, an oxygen amount in the weld metal increases by slag entrainment, and toughness deteriorates. Therefore, the TiO.sub.2 content is 13 mass % or less, preferably 12 mass % or less, more preferably 11 mass % or less.

[0026] Mn content: 1.0 mass % to 2.4 mass %

[0027] Mn acts as a deoxidizing agent of the weld metal and has an effect of enhancing hardenability of the weld metal and improving tensile strength and toughness of the weld metal. Mn also has an effect of accelerating the reduction reaction of TiO.sub.2. In order to obtain the effects, Mn is contained in either the steel outer sheath or the flux or both.

[0028] In the case where the Mn content is too low, a sufficient deoxidation effect cannot be obtained, a blowhole is likely to be generated, and sufficient tensile strength cannot be obtained. Furthermore, reduction of TiO.sub.2 is insufficient, and an amount of TiN contributing to prevention of the formation of a ferrite band cannot be ensured. Therefore, the Mn content is 1.0 mass % or more, preferably 1.1 mass % or more, more preferably 1.2 mass % or more.

[0029] On the other hand, in the case where the Mn content is too high, fluidity of molten weld metal is excessively large, and the bead shape in a vertical and upward welding position significantly deteriorates. Further, the tensile strength of the weld metal is excessively large, a reduction amount of TiO.sub.2 is excessive, an amount of Ti dissolved in solid increases, and toughness of the weld metal deteriorates. Therefore, the Mn content is 2.4 mass % or less, preferably 2.3 mass % or less, more preferably 2.2 mass % or less.

[0030] For achieving the above object, in the case where Mn is contained in the flux, a single metal or alloys such as metal Mn, FeMn, or FeSiMn can be used. Here, in the present embodiment, the Mn content means a total element amount of Mn contained in the wire.

[0031] Cr content: 1.0 mass % to 3.0 mass %

[0032] Cr is a main component of low alloy heat resistant steel and has an effect of improving the tensile strength of the weld metal. In order to obtain the effect, Cr is contained in either the steel outer sheath or the flux or both.

[0033] In the case where the Cr content is too low, the above effect cannot be sufficiently obtained. Therefore, the Cr content is 1.0 mass % or more, preferably 1.05 mass % or more, more preferably 1.10 mass % or more.

[0034] On the other hand, in the case where the Cr content is too high, the tensile strength excessively increases, and the toughness decreases. Therefore, the Cr content is 3.0 mass % or less, preferably 2.9 mass % or less, more preferably 2.8 mass % or less.

[0035] Here, in the present embodiment, the Cr content means a total element amount of Cr contained in the wire.

[0036] Mo content: 0.2 mass % to 1.2 mass %

[0037] Like Cr, Mo is a main component of low alloy heat resistant steel and has an effect of improving the tensile strength of the weld metal. Mo has an effect of increasing temper softening resistance of the weld metal and preventing a decrease in tensile strength due to PWHT. In order to obtain the effects, Mo is contained in either the steel outer sheath or the flux or both.

[0038] In the case where the Mo content is too low, the above effect cannot be sufficiently obtained. Therefore, the Mo content is 0.2 mass % or more, preferably 0.25 mass % or more, more preferably 0.3 mass % or more.

[0039] On the other hand, in the case where the Mo content is too high, the tensile strength excessively increases, and the toughness decreases. Therefore, the Mo content is 1.2 mass % or less, preferably 1.15 mass % or less, more preferably 1.10 mass % or less.

[0040] Here, in the present embodiment, the Mo content means a total element amount of Mo contained in the wire.

[0041] Si content: 0.1 mass % to 0.8 mass %

[0042] Si acts as a deoxidizing agent of the weld metal. Si has an effect of increasing viscosity of the weld metal and adjusting the bead shape. Further, Si has an effect of accelerating the reduction reaction of TiO.sub.2. In order to obtain the effects, Si is contained in either the steel outer sheath or the flux or both.

[0043] In the case where the Si content is too low, a sufficient deoxidation effect cannot be obtained, a blowhole is likely to be generated, the viscosity of the weld metal is insufficient, and the bead shape deteriorates. Furthermore, reduction action of TiO.sub.2 is insufficient, and an amount of TiN contributing to prevention of the formation of a ferrite band cannot be ensured. Therefore, the Si content is 0.1 mass % or more, preferably 0.2 mass % or more, more preferably 0.3 mass % or more.

[0044] On the other hand, in the case where the Si content is too high, the tensile strength is excessively large, a reduction amount of TiO.sub.2 is excessive, an amount of Ti dissolved in solid increases, and toughness deteriorates. Therefore, the Si content is 0.8 mass % or less, preferably 0.75 mass % or less, more preferably 0.70 mass % or less.

[0045] In the case where Si is contained in the flux, FeSi, FeSiMn, FeSiCr, Si oxide, or the like can be used.

[0046] Here, in the present embodiment, the Si content means a total element amount of Si contained in the wire.

[0047] Mg content: 0.1 mass % to 1.0 mass %

[0048] Mg acts as a strong deoxidizing agent of the weld metal and has an effect of improving toughness. In addition, like Si and Mn, Mg has an effect of accelerating the reduction reaction of TiO.sub.2 and stabilizing yield of B into the weld metal. In order to obtain the effects, Mg is contained in either the steel outer sheath or the flux or both.

[0049] In the case where the Mg content is too low, a sufficient deoxidation effect cannot be obtained, a blowhole is likely to be generated, and the oxygen amount increases to decrease the toughness. Furthermore, reduction action of TiO.sub.2 is insufficient, and an amount of TiN contributing to prevention of the formation of a ferrite band cannot be ensured. Therefore, the Mg content is 0.1 mass % or more, preferably 0.12 mass % or more, more preferably 0.14 mass % or more.

[0050] On the other hand, in the case where the Mg content is too high, a spatter generation amount increases, encapsulation of the slag is impaired, and the bead shape in the vertical and upward welding position deteriorates. Further, a reduction amount of TiO.sub.2 is excessive, an amount of Ti dissolved in solid increases, and toughness deteriorates. Therefore, the Mg content is 1.0 mass % or less, preferably 0.9 mass % or less, more preferably 0.8 mass % or less.

[0051] As an Mg source, a single metal or alloys such as metal Mg, SiMg, or NiMg can be used. Here, in the present embodiment, the Mg content means a total element amount of Mg contained in the wire.

[0052] Fluoride content (F conversion value): 0.05 mass % to 0.25 mass %

[0053] Fluorides act as an arc stabilizer. Further, the fluorides have an effect of lowering a melting point of the molten slag, and have an effect of improving fluidity and encapsulation of the molten slag and adjusting the bead shape. Further, since fluorine gas dissociated and gasified in the arc accelerates stirring of molten metal, fluorides have effects of accelerating floating or separation of the slag from the molten metal and decreasing the oxygen amount in the weld metal. Further, like Si, Mn, and Mg described above, fluorides have an effect of preventing the formation of a ferrite band by precipitating TiN in the weld metal by the combination of N and Ti formed by accelerating reduction action of TiO.sub.2. The fluorides are contained in the flux since the fluorides are a part of the slag forming agent, a reduction reaction of the part of TiO.sub.2 is likely to be performed under a high temperature atmosphere in the arc, and the reduction reaction can be accelerated by containing fluorides in the flux.

[0054] In the case where the fluoride content is too low, the above effect cannot be obtained, stability of the arc is impaired, a spatter generation amount increases, and the bead shape deteriorates. In addition, the effect of decreasing the oxygen amount in the weld metal is insufficient, and a blowhole is likely to be generated. Furthermore, since reduction of TiO.sub.2 is insufficient and an amount of Ti generated by reduction decreases, a precipitation amount of TiN also decreases, and an effect of preventing the formation of the ferrite band is insufficient. Therefore, in an F conversion value, the fluoride content is 0.05 mass % or more, preferably 0.07 mass % or more, more preferably 0.09 mass % or more.

[0055] On the other hand, in the case where the fluoride content in an F conversion value is too high, the fluidity of the slag is excessive, the encapsulation of the slag is impaired, and the bead shape significantly deteriorates. Therefore, in an F conversion value, the fluoride content is 0.25 mass % or less, preferably 0.23 mass % or less, more preferably 0.21 mass % or less.

[0056] LiF, NaF, K.sub.2SiF.sub.6, CaF.sub.2, MgF.sub.2, BaF.sub.2, or CeF.sub.3 or a fluorine oil containing CF.sub.2 can be used as the fluorides. The fluorine oil containing CF.sub.2 may be applied to a surface of the wire as a lubricant.

[0057] C content: 0.01 mass % to 0.10 mass %

[0058] Since C has effects of improving the hardenability and increasing the tensile strength and toughness of the weld metal, C is contained in either the steel outer sheath or the flux or both.

[0059] In the case where the C content is too low, the above effects cannot be sufficiently obtained. Therefore, the C content is 0.01 mass % or more, preferably 0.02 mass % or more, more preferably 0.03 mass % or more.

[0060] On the other hand, in the case where the C content is too high, the tensile strength of the weld metal is excessively large, the toughness significantly decreases, and hot crack is caused. Therefore, the C content is 0.10 mass % or less, preferably 0.095 mass % or less, more preferably 0.090 mass % or less.

[0061] In the case where C is contained in the flux, a simple substance or alloys of C such as graphite, chromium carbide, SiC, high CFeMn, or high CFeCr can be used.

[0062] V: 0.003 mass % to 0.020 mass %

[0063] V has effects of precipitating a carbide of V in the weld metal and preventing the formation of a ferrite band by preventing migration of C atoms in PWHT by the precipitate.

[0064] In the case where the V content is too low, the above effects cannot be sufficiently obtained. Therefore, the V content is 0.003 mass % or more, preferably 0.004 mass % or more, more preferably 0.005 mass % or more.

[0065] On the other hand, during PWHT, a needle-shaped fine carbide is formed by combining V with C, but in the case where the V content in the wire is excessive, the needle-shaped carbide causes the toughness of the weld metal to deteriorate significantly. Therefore, the V content is 0.020 mass % or less, preferably 0.019 mass % or less, more preferably 0.018 mass % or less.

[0066] Nb: 0.003 mass % to 0.020 mass %

[0067] Like V, Nb has effects of precipitating a carbide of Nb in the weld metal and preventing the formation of a ferrite band by preventing migration of C atoms in PWHT by the precipitate.

[0068] In the case where the Nb content is too low, the above effects cannot be sufficiently obtained. Therefore, the Nb content is 0.003 mass % or more, preferably 0.004 mass % or more, more preferably 0.005 mass % or more.

[0069] On the other hand, during PWHT, a needle-shaped fine carbide is formed by combining Nb with C, but in the case where the Nb content in the wire is excessive, the needle-shaped carbide causes the toughness of the weld metal to deteriorate significantly. Therefore, the Nb content is 0.020 mass % or less, preferably 0.019 mass % or less, more preferably 0.018 mass % or less.

[0070] B content: less than 100 ppm (0.01%)

[0071] In the case where the B content is excessive, not only the strength of the weld metal is too high to decrease the toughness, but also SR cracks are likely to occur in the weld metal. Therefore, the B content is less than 100 ppm, preferably less than 80 ppm, more preferably less than 60 ppm. The lower limit of the B content is not particularly limited, that is, the B content may be 0 ppm.

[0072] Balance

[0073] The main component of the flux-cored wire of the present embodiment is Fe. As Fe, Fe constituting the outer sheath, iron powder added to the flux, Fe of alloy powder, and the like are exemplified. Here, Fe is contained in a range of 78 mass % or more and 94 mass % or less. Fe is preferably contained in 80 mass % or more. Further, Fe is preferably contained in 92 mass % or less.

[0074] The flux-cored wire of the present embodiment contains Fe, TiO.sub.2, Mn, Cr, Mo, Si, and Mg in a total amount of preferably 95 mass % or more, more preferably 98 mass % or more.

[0075] As the balance, inevitable impurities, a component selectively contained other than the above, O in the case where a component other than TiO.sub.2 are contained as oxides in the flux, or the like may be included. Here, examples of the inevitable impurities include components other than the above-described components (such as Cu: 0.1 mass % or less, Al: 0.1 mass % or less, Zr: 0.1 mass % or less, Li: 0.1 mass % or less, Co: 0.1 mass % or less, Sn: 0.02 mass % or less, Sb: 0.02 mass % or less, and As: 0.02 mass % or less), and inevitably-contained components among the components which can be selectively added as described later, and it is acceptable to contain the inevitable impurities as long as the effects of the flux-cored wire according to the present embodiment are not diminished.

[0076] 28Mn/(390C+2370V)0.82

[0077] The flux-cored wire of the present embodiment satisfies 28Mn/(390C+2370V)0.82. Here, Mn, C, and V respectively mean the contents of Mn, C, and V based on total mass of the wire. By controlling to increase the value of 28Mn/(390C+2370V), generation of a ferrite side plate which is harmful to the toughness is prevented and a transformation temperature of the weld metal decreases and coarse bainite structures decrease, so that the toughness of the weld metal is improved.

[0078] Therefore, the value of 28Mn/(390C+2370V) is 0.82 or more, preferably 0.84 or more, more preferably 0.86 or more. Here, it is practical that the value of 28Mn/(390C+2370V) is 3.00 or less.

0.018TiO.sub.2Mg+2(Nb+V)0.12

[0079] The flux-cored wire of the present embodiment preferably satisfies 0.018TiO.sub.2Mg+2(Nb+V)0.12. Here, TiO.sub.2, Mg, Nb, and V respectively mean the contents of TiO.sub.2, Mg, Nb, and V based on total mass of the wire. By controlling to decrease a value of 0.018TiO.sub.2Mg+2(Nb+V), precipitation hardening in a grain during PWHT is prevented, and a difference in strength between an inner grain and a grain boundary decreases. Hereby, the occurrence of cracks can be prevented by releasing residual stress in welding in PWHT due to grain boundary sliding.

[0080] Therefore, the value of 0.018TiO.sub.2Mg+2(Nb+V) is preferably 0.12 or less, more preferably 0.11 or less, even more preferably 0.10 or less. Here, it is practical that the value of 0.018TiO.sub.2Mg+2(Nb+V) is 0.01 or more.

[0081] P content: 0.02 mass % or less

[0082] P is a component contained as an impurity. By reducing the P content in the wire, the SR crack resistance of the obtained weld metal can be improved. Therefore, the P content is preferably 0.02 mass % or less, more preferably 0.018 mass % or less, still more preferably 0.016 mass % or less. The lower limit of the P content is not particularly limited, that is, the P content in the wire of the present embodiment may be 0%.

[0083] S content: 0.02 mass % or less

[0084] Like P, S is also a component contained as an impurity. By reducing the P content in the wire, the SR crack resistance of the obtained weld metal can be improved. Therefore, the P content is preferably 0.02 mass % or less, more preferably 0.018 mass % or less, still more preferably 0.016 mass % or less. The lower limit of the S content is not particularly limited, that is, the S content in the wire of the present embodiment may be 0%.

[0085] N content: 0.02 mass % or less

[0086] N has an effect of preventing the formation of a ferrite band in the weld metal by combining N with Ti to be precipitated as a nitride TiN. In addition, N has an effect of improving the toughness by fixing the Ti dissolved in solid as a nitride. In order to obtain the effect, N may be contained in either the steel outer sheath or the flux or both.

[0087] However, in the case where the N content is excessive, an amount of N dissolved in solid increases and the toughness deteriorates, and excessive N causes blowholes, and causes deterioration of slag removability. Therefore, the N content is preferably 0.02 mass % or less, more preferably 0.018 mass % or less, still more preferably 0.016 mass % or less.

[0088] In the case where N is contained in the flux, a metal nitride such as NCr, NSi, or NTi can be used.

[0089] N may not be contained in the wire of the present embodiment, that is, the N content in the wire of the present embodiment may be 0%.

[0090] Na content: 0.01 mass % to 0.20 mass %

[0091] Na can be contained in the wire of the present embodiment as an optional component.

[0092] Since Na has an effect of stabilizing the arc, the Na content is preferably 0.01 mass % or more, more preferably 0.012 mass % or more, still more preferably 0.014 mass % or more.

[0093] On the other hand, by reducing the Na content, molten metal reservoir stability can be improved. Therefore, the Na content is preferably 0.20 mass % or less, more preferably 0.19 mass % or less, still more preferably 0.18 mass % or less.

[0094] K content: 0.01 mass % to 0.20 mass %

[0095] K can be contained in the wire of the present embodiment as an optional component.

[0096] Like Na, K has an effect of stabilizing the arc, and the K content is preferably 0.01 mass % or more, more preferably 0.012 mass % or more, still more preferably 0.014 mass % or more.

[0097] On the other hand, by reducing the K content, molten metal reservoir stability can be improved. Therefore, the K content is preferably 0.20 mass % or less, more preferably 0.19 mass % or less, still more preferably 0.18 mass % or less.

[0098] It is practical that Na and K are contained in the flux in a form of oxides such as Na.sub.2O and K.sub.2O or a form of fluorides.

[0099] Although a flux filling rate of the flux-cored wire of the present embodiment is not particularly specified, the flux filling rate can be appropriately set in consideration of wire productivity, for example, breaking of wire during molding and wiredrawing. The flux filling rate is preferably 11.0 mass % to 18.0 mass %, for example.

[0100] As a shielding gas used when welding is performed by using the flux-cored wire of the present embodiment, not only 100% CO.sub.2 gas, but also a mixed gas of Ar gas and CO.sub.2 gas, a mixed gas of Ar gas and O.sub.2 gas, or a mixed gas of Ar gas, CO.sub.2 gas, and O.sub.2 gas can be used, and any composition thereof can be used. The steel outer sheath is preferably selected depending on component composition of a material to be welded, and mild steel or alloy steel can be used. A cross-sectional shape of the wire is not necessary to be particularly specified, and there may be a seam or not. In addition, in the case where a seam is absent in the cross-sectional shape of the wire, Cu plating or Ni plating or composite plating thereof can be applied to the wire surface.

EXAMPLES

[0101] Hereinafter, the effects of the present invention will be described in more detail with reference to Examples and Comparative Examples of the present invention, but the present invention is not limited thereto.

[0102] Flux-cored wires having a wire diameter of 1.2 mm containing wire components shown in Tables 1 and 2 were used, and a groove-shaped steel plate 1 made of CrMo steel having a plate thickness of 20 mm shown in FIG. 1a, as a material to be welded, was butt-welded by gas shielded arc welding. The welding conditions are as shown below. The groove shape is a 450 V-shaped groove and has a root gap of 13 mm. The balance of the wire components shown in Tables 1 and 2 are Fe, inevitable impurities and so on, and F is an F conversion amount of fluorides. As Nb and V, analysis values of welding metal were used. The analysis values are considered equivalent to the values of Nb and V in the wire.

[0103] (Welding conditions)

[0104] Welding current: 200 A to 300 A

[0105] Arc voltage: 25 V to 32 V

[0106] Kind of shielding gas: Ar-20% CO.sub.2

[0107] Flow rate of shielding gas: 25 L/min

[0108] Preheating temperature and interpass temperature: 160 C. to 190 C.

[0109] Pass sequence: 6 layers and 12 passes

TABLE-US-00001 TABLE 1 Wire composition (mass %) TiO.sub.2 Mn Cr Mo Si Mg F C V Nb B P S N Sn Na K Example 1 12 1.9 1.3 0.4 0.4 0.2 0.12 0.07 0.006 0.011 0.0004 0.003 0.005 0.006 0.002 0.02 0.03 Example 2 5 1.8 2.1 1.0 0.6 0.4 0.10 0.08 0.005 0.005 0.0004 0.002 0.006 0.003 0.004 0.02 0.03 Example 3 6 2.3 1.4 0.5 0.4 0.2 0.14 0.06 0.006 0.006 0.0005 0.004 0.005 0.006 0.002 0.02 0.04 Example 4 7 1.1 2.2 0.9 0.6 0.5 0.12 0.04 0.004 0.011 0.0008 0.002 0.008 0.003 0.004 0.02 0.03 Example 5 6 1.9 2.8 1.0 0.6 0.3 0.10 0.07 0.008 0.008 0.0004 0.003 0.007 0.003 0.003 0.02 0.03 Example 6 6 1.8 1.2 0.6 0.4 0.3 0.15 0.05 0.006 0.01 0.0006 0.004 0.005 0.006 0.002 0.02 0.03 Example 7 7 2.0 2.3 1.1 0.4 0.2 0.12 0.07 0.007 0.007 0.0007 0.003 0.004 0.003 0.004 0.02 0.04 Example 8 8 1.9 2.2 0.3 0.5 0.4 0.13 0.06 0.008 0.009 0.0004 0.004 0.005 0.004 0.003 0.02 0.03 Example 9 6 1.8 2.3 1.1 0.7 0.2 0.12 0.05 0.006 0.005 0.0008 0.002 0.005 0.006 0.003 0.02 0.03 Example 10 7 2.0 1.5 0.4 0.2 0.4 0.10 0.07 0.008 0.007 0.0003 0.003 0.007 0.003 0.002 0.02 0.03 Example 11 6 1.9 1.6 0.6 0.6 0.9 0.12 0.05 0.005 0.008 0.0002 0.002 0.008 0.003 0.004 0.02 0.03 Example 12 6 1.9 2.4 1.0 0.4 0.1 0.13 0.05 0.006 0.011 0.0004 0.003 0 005 0.006 0.005 0.02 0.04 Example 13 7 2.0 2.4 0.9 0.5 0.4 0.24 0.07 0.007 0.005 0.0008 0.002 0.007 0.004 0.002 0.02 0.03 Example 14 6 1.8 1.3 0.4 0.4 0.2 0.06 0.08 0.005 0.006 0.0005 0.003 0.006 0.006 0.004 0.02 0.03 Example 15 6 2.1 1.4 0.6 0.6 0.5 0.15 0.09 0.006 0.007 0.0006 0.002 0.005 0.003 0.003 0.02 0.03 Example 16 6 1.9 1.3 0.4 0.5 0.2 0.12 0.03 0.009 0.005 0.0004 0.003 0.003 0.004 0.002 0.02 0.03 Example 17 7 2.3 2.4 0.9 0.4 0.2 0.13 0.04 0.017 0.007 0.0003 0.004 0.004 0.006 0.005 0.02 0.03 Example 18 8 1.9 1.3 0.5 0.6 0.4 0.16 0.07 0.004 0.005 0.0007 0.003 0.005 0.005 0.004 0.02 0.04 Example 19 6 2.0 2.4 1.0 0.4 0.2 0.12 0.05 0.005 0.019 0.0006 0.004 0.003 0.003 0.002 0.02 0.03 Example 20 7 1.8 1.3 0.4 0.4 0.3 0.14 0.07 0.006 0.004 0.0005 0.003 0.005 0.006 0.005 0.02 0.03 Example 21 7 1.7 2.5 1.1 0.5 0.2 0.12 0.06 0.007 0.007 0.009 0.003 0.004 0.005 0.003 0.02 0.03 28 Mn/(390 0.018 TiO.sub.2 C + 2370 V) Mg + 2 (Nb + V) Example 1 1.28 0.08 Example 2 1.17 0.06 Example 3 1.71 0.05 Example 4 1.23 0.09 Example 5 1.15 0.06 Example 6 1.49 0.06 Example 7 1.28 0.05 Example 8 1.26 0.09 Example 9 1.49 0.04 Example 10 1.21 0.08 Example 11 1.70 0.12 Example 12 1.58 0.04 Example 13 1.28 0.07 Example 14 1.17 0.04 Example 15 1.19 0.08 Example 16 1.61 0.05 Example 17 1.15 0.07 Example 18 1.45 0.08 Example 19 1.79 0.07 Example 20 1.21 0.06 Example 21 1.19 0.05

TABLE-US-00002 TABLE 2 Wire composition (mass %) TiO.sub.2 Mn Cr Mo Si Mg F C V Nb B P S N Sn Na K Comp. Example 1 14 2.0 1.4 0.4 0.5 0.5 0.16 0.05 0.005 0.011 0.0008 0.003 0.007 0.005 0.002 0.02 0.03 Comp. Example 2 3 1.9 2.2 0.9 0.4 0.3 0.12 0.07 0.006 0.005 0.0007 0.002 0.004 0.006 0.003 0.02 0.05 Comp. Example 3 6 2.6 1.3 0.5 0.6 0.2 0.16 0.06 0.01 0.009 0.0004 0.002 0.005 0.003 0.005 0.02 0.03 Comp. Example 4 7 0.8 2.4 1.0 0.4 0.4 0.13 0.05 0.005 0.005 0.0008 0.003 0.006 0.005 0.002 0.02 0.04 Comp. Example 5 6 1.8 3.2 0.9 0.5 0.3 0.17 0.07 0.006 0.006 0.0006 0.002 0.003 0.006 0.003 0.02 0.03 Comp. Example 6 7 1.7 0.8 0.4 0.4 0.2 0.14 0.06 0.007 0.008 0.0004 0.003 0.005 0.004 0.002 0.02 0.05 Comp. Example 7 5 1.9 2.5 1.3 0.6 0.5 0.15 0.05 0.005 0.011 0.0003 0.003 0.004 0.003 0.004 0.02 0.03 Comp. Example 8 7 1.8 1.4 0.1 0.5 0.3 0.12 0.07 0.006 0.007 0.0004 0.004 0.005 0.003 0.002 0.02 0.04 Comp. Example 9 6 2.0 2.4 1.0 0.9 0.2 0.16 0.06 0.008 0.006 0.0007 0.004 0.006 0.004 0.004 0.02 0.03 Comp. Example 10 8 1.9 1.3 0.5 0.0 0.3 0.13 0.08 0.005 0.009 0.0004 0.003 0.007 0.003 0.003 0.02 0.03 Comp. Example 11 7 1.8 2.2 0.9 0.5 1.1 0.12 0.05 0.006 0.01 0.0003 0.002 0.005 0.006 0.002 0.02 0.03 Comp. Example 12 6 1.7 2.4 1.1 0.4 0.0 0.14 0.07 0.005 0.005 0.0002 0.003 0.003 0.003 0.005 0.02 0.03 Comp. Example 13 7 1.9 1.4 0.4 0.6 0.5 0.28 0.06 0.009 0.006 0.0007 0.004 0.004 0.005 0.003 0.02 0.04 Comp. Example 14 6 1.8 2.4 0.9 0.5 0.3 0.02 0.05 0.006 0.008 0.0002 0.003 0.005 0.004 0.002 0.02 0.03 Comp. Example 15 6 1.7 1.3 0.5 0.4 0.2 0.15 0.12 0.005 0.011 0.0002 0.003 0.006 0.006 0.003 0.02 0.03 Comp. Example 16 7 1.9 2.2 1.0 0.6 0.4 0.13 0 0.008 0.005 0.0003 0.002 0.003 0.005 0.003 0.02 0.03 Comp. Example 17 9 2.0 1.3 0.6 0.5 0.5 0.12 0.06 0.023 0.009 0.0008 0.003 0.005 0.004 0.002 0.02 0.04 Comp. Example 18 6 1.8 2.4 0.9 0.6 0.2 0.15 0.07 0.001 0.007 0.0004 0.004 0.004 0.006 0.003 0.02 0.03 Comp. Example 19 9 1.7 1.4 0.4 0.4 0.4 0.13 0.05 0.009 0.022 0.0007 0.003 0.003 0.003 0.005 0.02 0.03 Comp. Example 20 6 1.8 1.3 0.5 0.5 0.3 0.15 0.06 0.008 0.001 0.0006 0.002 0.005 0.004 0.002 0.02 0.03 Comp. Example 21 8 1.7 2.4 1.1 0.4 0.2 0.12 0.07 0.006 0.011 0.011 0.004 0.006 0.006 0.005 0.02 0.03 Comp. Example 22 8 1.6 1.3 0.5 0.4 0.4 0.14 0.07 0.012 0.01 0.0006 0.004 0.003 0.004 0.003 0.02 0.03 28 Mn/(390 0.018 TiO.sub.2 C + 2370 V) Mg + 2 (Nb + V) Comp. Example 1 1.79 0.16 Comp. Example 2 1.28 0.04 Comp. Example 3 1.55 0.06 Comp. Example 4 0.71 0.07 Comp. Example 5 1.21 0.06 Comp. Example 6 1.19 0.06 Comp. Example 7 1.70 0.08 Comp. Example 8 1.21 0.06 Comp. Example 9 1.32 0.05 Comp. Example 10 1.24 0.07 Comp. Example 11 1.49 0.17 Comp. Example 12 1.22 0.02 Comp. Example 13 1.19 0.09 Comp. Example 14 1.49 0.06 Comp. Example 15 0.81 0.05 Comp. Example 16 2.81 0.08 Comp. Example 17 0.72 0.15 Comp. Example 18 1.70 0.04 Comp. Example 19 1.17 0.13 Comp. Example 20 1.19 0.05 Comp. Example 21 1.15 0.06 Comp. Example 22 0.80 0.10

[0110] The flux-cored wires of Examples and Comparative Examples were evaluated as follows. Evaluation results are shown in Tables 3 and 4.

[0111] (Evaluation of Weldability)

[0112] In addition to the above weld metal production, vertical fillet welding was performed, and an evaluation test of weldability was performed by using the flux-cored wires of Examples 1 to 21 and Comparative Examples 1 to 22. The evaluation of weldability was performed by function evaluation of stability of the arc during welding, slag removability, a spatter generation amount, and a bead shape. Flux-cored wires having comprehensively excellent weldability were evaluated as Pass: Good, and others were evaluated as Fail: Bad.

[0113] (Evaluation of Weld Metal Strength)

[0114] The obtained weld metal was subjected to PWHT at 675 C. to 705 C. for 1 hour, and then tensile strength, 0.2% proof stress, and elongation were measured by a tensile test.

[0115] Wires having a Cr content of less than 2.0% in which 0.2% proof stress is 468 MPa or more, tensile strength is within a range of 551 MPa to 689 MPa, and elongation is 19% or more were evaluated as Pass: Good, and others were evaluated as Fail: Bad.

[0116] Wires having a Cr content of 2.0% or more in which 0.2% proof stress is 537 MPa or more, tensile strength is within a range of 620 MPa to 758 MPa, and elongation is 19% or more were evaluated as Pass: Good, and others were evaluated as Fail: Bad.

[0117] (Evaluation of Toughness of Weld Metal)

[0118] The obtained weld metal was subjected to PWHT at 675 C. to 705 C. for 1 hour, and then a Charpy impact test was performed. Absorbed energy at 20 C. of a No. 4 Charpy test piece having a 2 mm V notch was measured at N=3. Wires in which the average value of absorbed energy was 27 J or more were evaluated as Pass: Good, and others were evaluated as Fail: Bad.

[0119] (SR Crack Resistance)

[0120] The obtained weld metal was not subjected to PWHT, a cylindrical test piece was sampled, and a ring crack test was performed to evaluate SR crack resistance.

[0121] First, as shown in FIG. 1a, a cylindrical test piece 10 shown in FIG. 1b was sampled from above final beads of weld metal 3. Details of the cylindrical test piece 10 are as shown in FIG. 1c, the cylindrical test piece 10 has a U notch 5 and a slit 6 leading to a cave inside the cylinder, and the U notch 5 is located above an as-cast portion of the weld metal 3, and a slit 6 is located below the as-cast portion of the weld metal 3. The U notch 5 is a U-shaped groove having a depth of 0.5 mm, a width of 0.4 mm, and a curvature radius of the bottom of 0.2 mm. The slit 6 is formed in a width of 0.5 mm.

[0122] Next, the obtained cylindrical test piece 10 was used to perform a ring crack test with reference to study on stress relief annealing crack (second report) (Uchiki et al, Journal of the Japan Welding Society: Vol. 33, No. 9 (1964) P. 718). In detail, as shown in FIG. 1d, in a state where bending stress was applied to the cylindrical test piece 10 in a direction indicated by arrows, the slit 6 of the test piece 10 was TIG-welded without using filler metal, and a PWHT treatment same as the above was performed in a state where tensile residual stress was applied to the U notch 5. After PWHT, optical microscope observation (magnification: 100 times) was performed on three cross sections of the ring, and in the case where no crack was recognized from the bottom of the U notch 5 in any cross section, it was evaluated as Pass: Good that occurrence of SR cracks was prevented (SR crack resistance is excellent); in the case where a crack was recognized in any one of the three cross sections, it was evaluated as Fail: Bad that the SR cracks occurred (SR crack resistance is poor).

TABLE-US-00003 TABLE 3 SR crack Weldability Strength Toughness resistance Example 1 Good Good Good Good Example 2 Good Good Good Good Example 3 Good Good Good Good Example 4 Good Good Good Good Example 5 Good Good Good Good Example 6 Good Good Good Good Example 7 Good Good Good Good Example 8 Good Good Good Good Example 9 Good Good Good Good Example 10 Good Good Good Good Example 11 Good Good Good Good Example 12 Good Good Good Good Example 13 Good Good Good Good Example 14 Good Good Good Good Example 15 Good Good Good Good Example 16 Good Good Good Good Example 17 Good Good Good Good Example 18 Good Good Good Good Example 19 Good Good Good Good Example 20 Good Good Good Good Example 21 Good Good Good Good

TABLE-US-00004 TABLE 4 Weld- SR crack ability Strength Toughness resistance Comparative Example 1 Good Bad Good Bad Comparative Example 2 Bad Good Good Good Comparative Example 3 Good Bad Good Good Comparative Example 4 Good Good Bad Good Comparative Example 5 Good Bad Good Good Comparative Example 6 Good Bad Good Good Comparative Example 7 Good Bad Good Good Comparative Example 8 Good Bad Good Good Comparative Example 9 Good Bad Good Good Comparative Example 10 Good Bad Good Good Comparative Example 11 Good Good Good Bad Comparative Example 12 Good Bad Good Good Comparative Example 13 Bad Good Good Good Comparative Example 14 Bad Good Good Good Comparative Example 15 Bad Bad Bad Good Comparative Example 16 Good Bad Good Good Comparative Example 17 Good Good Bad Bad Comparative Example 18 Good Bad Good Good Comparative Example 19 Goad Good Good Bad Comparative Example 20 Good Bad Good Good Comparative Example 21 Good Good Good Bad Comparative Example 22 Good Good Bad Good

[0123] The wire of Comparative Example 1 contained too much TiO.sub.2, and strength and SR crack resistance of weld metal were poor.

[0124] The wire of Comparative Example 2 contained too little TiO.sub.2, and weldability was poor.

[0125] The wire of Comparative Example 3 contained too much Mn, and strength of weld metal was poor.

[0126] The wire of Comparative Example 4 contained too little Mn, a value of 28Mn/(390C+2370V) was too small, and toughness of weld metal was poor.

[0127] The wire of Comparative Example 5 contained too much Cr, and strength of weld metal was poor.

[0128] The wire of Comparative Example 6 contained too little Cr, and strength of weld metal was poor.

[0129] The wire of Comparative Example 7 contained too much Mo, and strength of weld metal was poor.

[0130] The wire of Comparative Example 8 contained too little Mo, and strength of weld metal was poor.

[0131] The wire of Comparative Example 9 contained too much Si, and strength of weld metal was poor.

[0132] The wire of Comparative Example 10 contained too little Si, and strength of weld metal was poor.

[0133] The wire of Comparative Example 11 contained too much Mg, and SR crack resistance was poor.

[0134] The wire of Comparative Example 12 contained too little Mg, and strength of weld metal was poor.

[0135] The wire of Comparative Example 13 contained too much F, and weldability was poor.

[0136] The wire of Comparative Example 14 contained too little F, and weldability was poor.

[0137] The wire of Comparative Example 15 contained too much C, a value of 28Mn/(390C+2370V) was too small, and weldability, strength of weld metal, and toughness of weld metal were poor.

[0138] The wire of Comparative Example 16 contained too little C, and strength of weld metal was poor.

[0139] The wire of Comparative Example 17 contained too much V, a value of 28Mn/(390C+2370V) was too small, and toughness and SR crack resistance of weld metal were poor.

[0140] The wire of Comparative Example 18 contained too little V, and strength of weld metal was poor.

[0141] The wire of Comparative Example 19 contained too much Nb, and SR crack resistance was poor.

[0142] The wire of Comparative Example 20 contained too little Nb, and strength of weld metal was poor.

[0143] The wire of Comparative Example 21 contained too much B, and SR crack resistance was poor.

[0144] In the wire of Comparative Example 22, a value of 28Mn/(390C+2370V) was too small, and toughness of weld metal was poor.

[0145] On the other hand, all the wires of Examples 1 to 21 were excellent in weldability, strength of weld metal, toughness of weld metal, and SR crack resistance.

[0146] The present application is based on Japanese patent application No. 2018-5013 filed on Jan. 16, 2018, the contents of which are cited as reference in the present application.

REFERENCE SIGN LIST

[0147] 1 Steel plate [0148] 2 Backing metal [0149] 3 Weld metal [0150] 5 U notch [0151] 6 Slit [0152] 10 Cylindrical test piece