HIGH ASPECT RATIO IN-PLANE METAL MICRONEEDLE ARRAY, MANUFACTURING METHOD AND CLAMPING AND INSERTING AUXILIARY DEVICE THEREOF

Abstract

A high aspect ratio in-plane metal microneedle array, a manufacturing method and a clamping and inserting auxiliary device thereof is disclosed. A large-size metal sheet is cut into small metal sheets. A clamping tooling composed of two upper and lower metal cover plates is processed. Inner sides of the upper and the lower cover plates of the tooling are provided with grooves in which the metal sheets are placed and fastened by bolts. Wire cutting is conducted on the tooling and the metal sheets as a whole to obtain a plane metal microneedle array with a plurality of microneedle bodies. In addition, an assembling and clamping device and an inserting auxiliary device of the high aspect ratio in-plane metal microneedle array is provided. The assembled inserting auxiliary device is placed on skin, and the microneedle array is inserted into the skin through the auxiliary device.

Claims

1. A manufacturing method for a high aspect ratio in-plane metal microneedle array, comprising the following steps: step 1: using medical stainless steel or titanium alloy metal sheet material as a microneedle material, wherein the thickness of a metal sheet is 20-200 microns; step 2: cutting the metal sheet into small metal sheets with proper sizes, wherein length is 30-50 mm and width is 10-30 mm; step 3: processing a special sheet clamping tooling; the tooling is composed of two identical upper and lower metal cover plates, and the overall thickness of each cover plate is 5-10 mm; inner walls of the upper and the lower cover plates of the tooling are processed with grooves matched with the sizes of the small metal sheets, i.e., the lengths and widths of the grooves are consistent with the lengths and widths of the metal sheets to place the metal sheets; the depths of the grooves of the upper and the lower cover plates are 1-5 mm; through holes for passing through fastening bolts are processed at edges around upper and the lower cover plate bodies 1; step 4: placing the small metal sheets in the groove of any metal cover plate; adjusting the number of the metal sheets placed at one time according to the thickness of the sheets and the depth of the groove; recommending placing 20-200 metal sheets at one time; placing another metal cover plate on the cover plate on which the metal sheets are placed, with the groove facing the metal sheets and aligned up and down; then encapsulating and fastening the upper and the lower metal cover plates by the fastening bolts, and compacting the metal sheets to form a whole with the upper and the lower cover plates; step 5: designing the geometries and sizes of sheet in-plane metal microneedles a sheet in-plane metal microneedle array is composed of substrates and high aspect ratio microneedle bodies for a subsequent clamping part; the high aspect ratio microneedle bodies are arranged above the substrates; positioning shoulders are arranged on both sides above the substrates for positioning guidance of an inserting auxiliary device; a positioning guide groove is arranged in the lower middle of each substrate for subsequent assembly of each substrate; step 6: clamping the metal sheets and the tooling encapsulated in step 4 to a wire cutting device, determining a wire path according to the geometry and sizes of the sheet plane metal microneedles designed in step 5 by the wire cutting device, conducting wire cutting on the tooling and the metal sheets as a whole, and processing the metal sheets into the substrates and the microneedle bodies; in the wire cutting process, the tips of the microneedle bodies are cut with an 8-shaped path to ensure the sharpness of microneedle tips; in addition, during processing, both sides of the substrates are reserved for 2 to 5 mm without cutting to ensure that the clamping tooling and the metal sheets still form a whole after processing; step 7: taking off the fastening bolts on the tooling, and taking out and washing the processed metal sheets to obtain microneedle substrates which are not cut; step 8: cutting the microneedle substrates obtained in step 7, and removing the material on regions reserved on both sides of the substrates to separate the sheet in-plane metal microneedles from the metal sheets to obtain a sheet in-plane metal microneedle array with a plurality of microneedle bodies.

2. The preparation method for the high aspect ratio in-plane metal microneedle array according to claim 1, wherein the clamping tooling is made of metal material such as stainless steel and 45# steel with good electrical conductivity and high strength.

3. A high aspect ratio in-plane metal microneedle array prepared by the method of claim 1, wherein the sheet in-plane metal microneedle array is composed of substrates and high aspect ratio microneedle bodies for a subsequent clamping part; the height of the high aspect ratio microneedle bodies is 1-5 mm, the width of a root of each microneedle body is 50-500 microns, and the thickness is the thickness of the metal sheet; the high aspect ratio microneedle bodies are arranged above the substrates; the number of the microneedles on each substrate is 3-50, and a distance is 0.25-10 mm; positioning shoulders are arranged on both sides above the substrates for positioning guidance of an inserting auxiliary device; a positioning guide groove is arranged in the lower middle of each substrate for subsequent assembly of each substrate; the high aspect ratio microneedle bodies adopt equal-strength design along the length direction, that is, the width change of the high aspect ratio microneedle bodies needs to ensure that the microneedle bodies have the same maximum bending stress at each cross section when tips are subjected to a transverse concentrated load; if the root of each microneedle body is a starting point of x axis, the x axis is located on a longitudinal symmetry axis of each microneedle body, and a width direction is assumed to be a y axis, then the equal-strength design requires that x and y satisfy the following relationship: y=C{square root over (L.sub.0x)}; in the formula, L.sub.0 is the length of the microneedle bodies, and C is a constant which comprehensively reflects the yield strength of the material, the thickness of the microneedles, and a load size.

4. An assembling and clamping device of the high aspect ratio in-plane metal microneedle array of claim 3, the assembling and clamping device comprising a main body and a partition board; wherein the main body and the partition board are made of light metal or polymer material; the main body is a box-shaped rectangular structure with one side open, and the bottom of an inner cavity is provided with a slide rail matched with the positioning guide groove at the bottom of each microneedle substrate; the bottom of the main body is provided with a threaded hole for subsequent installation of a handle; a threaded through hole is arranged on the side surface of the main body for pressing the partition board by a bolt; the high aspect plane metal microneedle array is vertically placed in the assembling and clamping device, with the microneedle bodies facing upward; the width of a cavity of the main body is consistent with the width of the microneedle substrates; the depth of the cavity is consistent with the height of the outer edge of each substrate, that is, the plane of the positioning shoulders of the substrates is the same as the plane of the upper surface of the main body; the length of the cavity is determined according to the number of the microneedle substrates to be clamped and the distances between the substrates, and a recommended length range is 10-40 mm; the partition board is of a thin rectangular structure, and is used for positioning each microneedle substrate when the microneedle array is assembled; the width of the partition board is consistent with the depth of the cavity of the main body, the length is consistent with the width of the cavity of the main body and the thickness is 1-5 mm; the bottom of the partition board is provided with a groove matched with the guide groove at the bottom of each substrate; the high aspect ratio in-plane metal microneedle array is vertically placed in the cavity of the main body of the clamping device, and each substrate is separated by the partition board; the bolt penetrates through the threaded through hole on the side surface of the clamping device and extrudes the partition board to keep each microneedle substrate stable; during clamping, the side of each microneedle substrate close to each microneedle body is higher than the upper surfaces of the partition board and the main body of the clamping device; the specific exceeding value is determined by the sizes of the positioning shoulders on both sides of the microneedle substrates; after clamping, a hand-held handle is installed at the threaded hole at the bottom of the main body of the clamping device to complete the assembly and clamping of the high aspect plane metal microneedle array.

5. The assembling and clamping device of the high aspect ratio in-plane metal microneedle array according to claim 4, wherein the main body and the partition board are made of aluminum alloy or polytetrafluoroethylene.

6. An inserting auxiliary device of the high aspect plane metal microneedle array of claim 3, the inserting auxiliary device comprising a rectangular frame main body, a positioning partition board, and positioning small spacers, wherein the rectangular frame main body and the positioning partition board are made of light metal or polymer material; the positioning small spacers and the microneedle substrates are made of the same material; the rectangular frame main body is a frame-shaped cuboid which is open up and down, and is placed above the assembling and clamping device; the length and the width of an inner frame of the rectangular frame main body are consistent with the length and the width of the cavity of the main body of the clamping device; the height of the rectangular frame main body is consistent with the height of the positioning shoulders on both sides of the microneedle substrates; both sides of the rectangular frame main body are provided with threaded through holes through which capless bolts pass, for subsequent tightening; for the positioning partition board, the height of the positioning partition board is consistent with the height of the rectangular frame main body, and the length of the positioning partition board is consistent with the length of the partition board of the clamping device; the thickness of the positioning partition board is consistent with the thickness of the partition board of the clamping device, and the corresponding positions of the positioning partition board and the microneedle bodies are lightly sanded with fine sandpaper; every two positioning partition boards are separated by the positioning small spacer, and a gap between the two positioning partition boards is used for the microneedle bodies to pass; the height of the positioning small spacers is consistent with the height of the positioning partition board, the width is smaller than the width of the positioning shoulders on both sides of the microneedle substrate by 0.1-1 mm, and the thickness is consistent with that of the microneedle substrates to ensure that the gap between the positioning partition boards is consistent with the thickness of the microneedle substrates; the positioning partition board is assembled into the rectangular frame main body; the positioning small spacers are placed at both ends of each positioning partition board to make the distance of the positioning partition boards consistent with the thickness of the microneedles; and the contact position between the positioning partition boards and the microneedle bodies is sanded to ensure that gaps exist between the microneedle bodies and the positioning partition boards to avoid serious scratching; the capless bolts pass through the threaded hole on one side of the end surface of the rectangular frame main body to press the positioning partition boards and the positioning small spacers and maintain a one-to-one correspondence with the clamping device; a skin region to be inserted is sterilized; the assembled inserting auxiliary device is placed on the skin; and the assembled microneedle array is inserted into the skin through the gap of the positioning partition boards in the auxiliary device.

7. The inserting auxiliary device of the high aspect ratio in-plane metal microneedle array according to claim 6, wherein the rectangular frame main body and the positioning partition boards are made of aluminum alloy or polytetrafluoroethylene.

8. The inserting auxiliary device of the high aspect ratio in-plane metal microneedle array according to claim 6, wherein 502 glue is used at both ends of the positioning partition boards to reinforce the connection among the partition boards, the positioning small spacers and the rectangular frame main body.

Description

DESCRIPTION OF DRAWINGS

[0031] FIG. 1 is a front view in three views of a clamping device for processing;

[0032] FIG. 2 is a top view in three views of a clamping device for processing;

[0033] FIG. 3 is a side view in three views of a clamping device for processing;

[0034] FIG. 4 is a schematic diagram after a metal substrate is clamped and installed;

[0035] FIG. 5 is a schematic diagram of a sheet in-plane microneedle array with equal-strength microneedle bodies;

[0036] FIG. 6 is a schematic diagram of a wire cutting processing path;

[0037] FIG. 7 is a schematic diagram of a clamping tooling and a microneedle array substrate which are not disassembled after cutting is completed;

[0038] FIG. 8 is an overall schematic diagram of a sheet microneedle array and a substrate after cutting is completed;

[0039] FIG. 9 is a front view in three views of an assembling and clamping device of a microneedle array;

[0040] FIG. 10 is a top view in three views of an assembling and clamping device of a microneedle array;

[0041] FIG. 11 is a side view in three views of an assembling and clamping device of a microneedle array;

[0042] FIG. 12 shows a partition board for positioning a microneedle substrate in an assembling and clamping device of a microneedle array;

[0043] FIG. 13 is a front view in a schematic diagram after assembling and clamping of a microneedle array;

[0044] FIG. 14 is a top view in a schematic diagram after assembling and clamping of a microneedle array;

[0045] FIG. 15 is a side view in a schematic diagram after assembling and clamping of a microneedle array;

[0046] FIG. 16 is a front view in three views of an inserting auxiliary device of a microneedle array;

[0047] FIG. 17 is a front view in three views of an inserting auxiliary device of a microneedle array;

[0048] FIG. 18 is a front view in three views of an inserting auxiliary device of a microneedle array;

[0049] FIG. 19 shows a partition board for positioning a microneedle spacer in an inserting auxiliary device of a microneedle; and

[0050] FIG. 20 is a schematic diagram after assembling of an inserting auxiliary device of a microneedle array.

[0051] In the figures: 1 upper and lower cover plate bodies; 2 groove; 3 bolt through hole; 4 fastening bolt; 5 metal foil; 6 substrate; 7 microneedle body; 8 positioning shoulder; 9 guide groove; 10 uncut part to keep the integrity of clamping tooling; 11 main body of assembling and clamping device; 12 slide rail; 13 threaded hole; 14 threaded through hole; 15 partition board; 16 bolt; 17 hand-held handle; 18 rectangular frame main body; 19 threaded through hole; 20 positioning partition board; 21 positioning small spacer; 22 capless bolt; and 23 gap.

DETAILED DESCRIPTION

[0052] The technical solution of the present invention is described below in detail with reference to drawings. The metal microneedle arrays can be processed in batches at one time in the present invention. Through calculation based on the ideal total cutting thickness of 2 cm for wire cutting, for example, the up-down overall wall thickness of the tooling is 5 mm, the depth of the grooves is 2 mm and the thickness of each metal sheet is 100 microns. Then, the number of the microneedles that can be cut at one time is 140, which greatly improves the efficiency compared with other microneedle processing methods. Moreover, the wire cutting processing technology has relatively low cost. Thus, the microneedle array processing method provided by the present invention has low cost. After the clamping tool is used, except that the material at the path of a cutting wire is cut off, other parts are still intact, thereby improving the efficiency and reducing the cost. The clamping tooling compacts a plurality of metal sheets into a whole, which can enhance the stiffness of the workpiece, prevent processing size deviations caused by the lateral force during cutting, significantly improve the accuracy and length of the microneedles that can be processed and satisfy the processing needs of the high aspect ratio microneedles. The microneedle tips are cut with an 8-shaped processing path, thereby ensuring the processing accuracy of the microneedle tips. The microneedles adopt the equal-strength design along the width direction, which can improve the anti-buckling capability of the microneedles along the width direction, and prevent the microneedles from buckling and failing along the width direction when the microneedles are inserted into the skin. Meanwhile, a special inserting auxiliary device is used to provide additional constraints for the microneedles in the thickness direction, thereby comprehensively improving the use reliability of the high aspect ratio microneedles. Specific embodiments are as follows:

[0053] A preparation method for a high aspect ratio in-plane metal microneedle array comprises the following steps:

[0054] Step 1: using metal sheet material with good biocompatibility and excellent strength and toughness as the microneedle material. Medical 304 stainless steel sheets are adopted in the present embodiment. The stainless steel sheets have the sizes of 1000 mm in length, 100 mm in width and 80 microns in thickness.

[0055] Step 2: cutting the metal sheets in step 1 into small metal sheets 5 with proper sizes, wherein in the present embodiment, length is 50 mm, width is 25 mm and thickness is 80 microns.

[0056] Step 3: processing a special sheet clamping tooling, wherein the outer structure of the tooling is shown in FIG. 1, FIG. 2 and FIG. 3.

[0057] The clamping tooling is composed of two identical upper and lower metal cover plates 1. In the present embodiment, the upper and lower cover plates of the clamping tooling have length of 80 mm, width of 55 mm and thickness of 6 mm. Inner walls of the cover plates are provided with grooves 2 matched with the sizes of the small sheets of S2. In the present embodiment, the grooves have depths of 1.5 mm, lengths of 50 mm and widths of 25 mm. In the present embodiment, the tooling is made of stainless steel with good electrical conductivity and high strength. Six M6 bolt through holes 3 for subsequent bolt connection and fixation are processed on both sides of the clamping tooling, and the number of the holes can be adjusted according to actual needs.

[0058] Step 4: placing 100 small metal sheets 5 in the groove 2 of any metal cover plate 1 for stacking; recommending placing 20-200 metal sheets at one time; placing another metal cover plate 1 on the cover plate on which the metal sheets 5 are placed, with the groove facing the metal sheets 5 and aligned up and down; then encapsulating and fastening the upper and the lower metal cover plates 1 by the fastening bolts 4, and compacting the metal sheets 5 to form a whole with the upper and the lower cover plates 1 to obtain the whole of the encapsulated metal sheets and the processed clamping tooling as shown in FIG. 4.

[0059] Step 5: designing the geometries and sizes of sheet in-plane metal microneedles.

[0060] A sheet in-plane metal microneedle array is composed of substrates 6 and high aspect ratio microneedle bodies 7 for a subsequent clamping part. In the present embodiment, the shape of the microneedle bodies in the sheet microneedle array is shown in FIG. 5. The thickness of the microneedle bodies 7 is the thickness of the metal sheets. The microneedle bodies adopt equal-strength design along the width direction, that is, the width change of the microneedles needs to ensure that the microneedles have the same maximum bending stress at each cross section when tips are subjected to a transverse concentrated load. If the root of each microneedle is a starting point of x axis, the x axis is a longitudinal symmetry axis of each microneedle, and the width direction is assumed to be a y axis, then the equal-strength design requires that x and y satisfy the following relationship: y=C{square root over (L.sub.0x)}; in the formula, L.sub.0 is the length of the microneedles, and C is a constant. In the present embodiment, the microneedle bodies have height of 1.5 mm and bottom width of 150 microns; and C can be calculated as 0.0612 according to the bottom width and length of the microneedles. FIG. 5 is a schematic diagram of a single microneedle array. 8 in FIG. 5 is a positioning shoulder which is reserved for subsequently inserting and positioning the auxiliary device; and 9 in FIG. 5 is a positioning groove for subsequently assembling the substrates.

[0061] In the present embodiment, if the number of the microneedles on a single substrate is selected as 7, the distance is 3.5 mm, the height of each substrate excluding the microneedle body is 13 mm, and the bottom is provided with a groove 9 as shown in FIG. 5. In the present embodiment, the groove has height of 5 mm and width of 5 mm. Positioning shoulders 8 as shown in FIG. 5 are reserved on both sides of the microneedle substrate near the microneedle body for subsequent positioning when the microneedle array is inserted. In the present embodiment, the sizes of the part are 3 mm in height and 3 mm in width.

[0062] Step 6: clamping the metal sheets and the tooling encapsulated in step 4 to a wire cutting device, determining a wire path according to the geometry and sizes of the sheet in-plane metal microneedles designed in step 5 by the wire cutting device, conducting wire cutting on the tooling and the metal sheets 5 as a whole according to the wire path shown in FIG. 6, and processing the metal sheets 5 into the substrates 6 and the microneedle bodies 7. In the wire cutting process, the tips of the microneedle bodies 7 are cut with an 8-shaped path to ensure the sharpness of microneedle tips. In addition, during processing, a small amount of material is reserved on both sides of a single microneedle substrate as shown by the reference number 10 in FIG. 6 or FIG. 7 and is not cut. In the present embodiment, the height of the uncut part is 2 mm and the width is 2 mm. A schematic diagram (top view) when the metal sheets and the tooling after cut are not disassembled is shown in FIG. 7.

[0063] Step 7: taking off the fastening bolts 4 on the tooling, and taking out and washing the processed metal sheets 5 to obtain microneedle substrates which are not cut as shown in FIG. 8.

[0064] Step 8: cutting the microneedle substrates obtained in step 7, and removing the material on regions reserved on both sides of the substrates 6 to separate the sheet in-plane metal microneedles from the metal sheets 5 to obtain a sheet in-plane microneedle array as shown in FIG. 5.

[0065] An assembling and clamping device of a high aspect ratio in-plane metal microneedle array is disclosed. A special microneedle sheet assembling and clamping device comprises a main body 11 and a partition board 15; and the main body 11 and the partition board 15 are made of aluminum alloy material. The whole clamping device is a box-shaped cuboid with one side open, and the bottom of an inner cavity is provided with a slide rail 12 matched with the groove at the bottom of each microneedle substrate of S9. As shown by the reference number 12 in FIGS. 9, 10 and 11, the sizes of the inner cavity are 25 mm in length, 20 mm in width, 10 mm in height and 5 mm in wall thickness. Threaded holes 13 for installing the hand-held handle are processed on the bottom of an assembling body, and threaded holes 14 are processed on the end surfaces of both sides of the assembling body for pressing the partition board 15 by bolts 16. Three views of the whole clamping device are shown in FIGS. 9, 10, and 11. In the present embodiment, the partition board 15 used for positioning is made of aluminum alloy material. The height of the partition board 15 is 10 mm, and the length of the partition board 15 needs to be consistent with the width of the cavity of the main body 11, i.e., 20 mm. The width of the partition board 15 is set as required, and is 3.5 mm in the present embodiment; and the number of the partition boards is 7. The bottom of each partition board 15 is provided with a groove consistent with the size of the groove at the bottom of each microneedle substrate.

[0066] The sheet in-plane microneedle array and the partition board 15 as shown in FIG. 5 are arranged in sequence and placed in the main body 11 of the clamping device. The threaded through holes 14 as shown in FIGS. 9, 10, and 11 on the end surface of any side of the bolt clamping device are used to compact and fix the microneedle substrates and the partition board. The hand-held handle 17 is installed in the threaded hole 13 at the bottom of the clamping device, and finally the organized microneedle array shown in FIGS. 13, 14 and 15 is obtained.

[0067] An inserting auxiliary device of a high aspect ratio in-plane metal microneedle array is disclosed. The inserting auxiliary device comprises a rectangular frame main body 18, a positioning partition board 20, and positioning small spacers 21, as shown in FIGS. 16, 17 and 18. The rectangular frame main body 18 and the positioning partition board 20 are made of aluminum alloy material. The positioning small spacers 21 and the microneedle substrates 6 are made of the same material.

[0068] The rectangular frame main body 18 is a frame-shaped cuboid which is open up and down, and is arranged above the assembling and clamping device. The length and the width of an inner frame are consistent with the length and the width of the cavity of the main body 11 of the clamping device. The height of the rectangular frame main body 18 needs to be matched with the sizes of the positioning shoulders 8 shown in FIG. 5. In the present embodiment, the sizes of the part are 3 mm in height and 3 mm in width. The height needs to be consistent with the size of the microneedle substrate above the partition board. Both sides of the rectangular frame main body 18 are provided with threaded through holes 19 through which capless bolts 22 pass, for subsequent tightening.

[0069] The positioning partition board 20 is specifically shown in FIG. 19. The height of the positioning partition board 20 is consistent with the height of the rectangular frame main body 18, which is 3 mm. The length of the positioning partition board 20 is consistent with the length of the partition board 15 of the clamping device, which is 20 mm. The thickness of the positioning partition board 20 is consistent with the thickness of the partition board 15 of the clamping device, and the corresponding positions of the positioning partition board 20 and the microneedle bodies are lightly sanded with fine sandpaper. Every two positioning partition boards 20 are separated by the positioning small spacer 21, and a gap 23 between the two positioning partition boards 20 is used for the microneedle bodies 7 to pass. The height of the positioning small spacers 21 is consistent with the height of the positioning partition board 20, which is 3 mm. The width of the spacers should be slightly smaller than the width of the positioning shoulders 8 as shown in FIG. 5 in S9, and in the present embodiment, the width is 2.8 mm. The thickness is consistent with the thickness of the microneedle substrates. A positioning frame, the partition board and the spacers in S24 are assembled, and the inserting auxiliary device of the microneedle array as shown in FIG. 20 is finally obtained.

[0070] The positioning partition board 20 is assembled into the rectangular frame main body 18; the positioning small spacers 21 are placed at both ends of each positioning partition board 20 to make the distance of the positioning partition boards 20 consistent with the thickness of the microneedles. The capless bolts are used for compacting and encapsulating from one side of the rectangular frame main body 18 to compact the positioning partition board 20 and the positioning small spacers 21 to obtain the inserting auxiliary device of the microneedle array as shown in FIG. 20. 502 glue is used at both ends of the positioning partition boards 20 to reinforce the connection among the partition boards 20, the positioning small spacers 21 and the rectangular frame main body 18. The finally assembled inserting auxiliary device is shown in FIG. 20. A skin region to be applied with drugs is sterilized; the assembled inserting auxiliary device as shown in FIG. 20 is placed on the skin; and the assembled microneedle array as shown in FIGS. 13, 14 and 15 is inserted into the skin through the gap 23 of the positioning partition boards 20 in the auxiliary device.

[0071] The embodiments of the present invention are only used for describing and explaining the technical solution of the present invention rather than limitation. Although the present invention is described in detail with reference to the preferred embodiments, those ordinary skilled in the art shall understand that the technical solution of the present invention can be amended or equivalently replaced without departing from the spirit and the scope of the technical solution of the present invention. The amendment or equivalent replacement shall be covered within the scope of the claims of the present invention.