LEATHER-LIKE SHEET AND BACKPACK USING THE SAME AS A BACK SURFACE MATERIAL

Abstract

Disclosed is a leather-dike sheet including a fiber base material and a colored resin layer laminated on the fiber base material, wherein the colored resin layer includes an intermediate layer and a skin layer laminated on the intermediate layer, wherein the skin layer is a layer containing polyurethane and a black pigment of 3 g/m.sup.2 or more, and the intermediate layer is a layer containing polyurethane and a black pigment, and in the L*a*b* color system, a leather-like sheet having a lightness value of L*30 is used.

Claims

1: A leather-like sheet, comprising a fiber base material, and a colored resin layer laminated on the fiber base material, wherein the colored resin layer comprises an intermediate layer and a skin layer laminated on the intermediate layer, the skin layer is a layer containing polyurethane and 3 g/m.sup.2 or more of an infrared-reflective black pigment, the intermediate layer is a layer containing polyurethane and a black pigment, and the leather-like sheet has a surface having a lightness value of L*30 in the L*a*b* color system.

2: The leather-like sheet according to claim 1, wherein the reflectance with respect to a near-infrared ray of the wavelength of 905 nm is 10% or more, and a reflectance with respect to a near-infrared ray of the wavelength of 1550 nm is 10% or more.

3: The leather-like sheet according to claim 1, wherein the solar reflectance in the wavelength-range from 250 to 2500 nm is 10% or more on the average.

4: The leather-like sheet according to claim 1. wherein the infrared-reflective black pigment has a reflectance of 25% or more with respect to a near-infrared ray of the wavelength of 905 nm, a reflectance of 50% or more with respect to a near-infrared ray of the wavelength of 1550 nm, and a transmittance of less than 50% with respect to a near-infrared ray of the wavelength of 905 nm.

5: The leather-like sheet according to claim 1, wherein the infrared-reflective black pigment is a titanium-based black pigment that is a CaOTiO.sub.2MnO.sub.2 base.

6: The leather-like sheet according to claim 1, wherein the skin layer contains 0 to 0.5 g/m.sup.2 of carbon black.

7: The leather-like sheet according to claim 1, wherein a reflection intensity of the surface is 30 or more, measured at the wavelength of 905 nm and the measurement distance 10 m, using a HORIZON manufactured by Livox Technology Company Limited.

8: A backpack, comprising the leather-like sheet according to claim 1 as a back surface material.

9: The leather-like sheet according to claim 1, wherein the skin layer contains 0 to 0.5 g/m.sup.2 of carbon black.

10: The leather-like sheet according to claim 1, wherein the skin layer does not contain carbon black.

11: The leather-like sheet according to claim 1, wherein the intermediate layer contains carbon black as the black pigment.

12: The leather-like sheet according to claim 1, wherein the thickness of the skin layer is from 10 to 30 m.

13: The leather-like sheet according to claim 1, wherein the thickness of the intermediate layer is from 10 to 50 m.

14: The leather-like sheet according to claim 1, further comprising a porous layer mainly composed of polyurethane having the thickness of 100 to 600 m between the fiber base material and the colored resin layer.

15: A leather-like sheet, comprising: a fiber base material, and a colored resin layer laminated on the fiber base material, wherein the colored resin layer comprises an intermediate layer and a skin layer laminated on the intermediate layer, the skin layer is a layer containing poly urethane, 3 g/m.sup.2 or more of an infrared-reflective black pigment and 0 to 0.5 g/m.sup.2 of carbon black, the intermediate layer is a layer containing polyurethane and 0.2 g/m.sup.2 or more of carbon black, and the leather-like sheet has a surface having a lightness value of L*30 in the L*a*b* color system.

16: The leather-like sheet according to claim 15, wherein the infrared-reflective black pigment is a titanium-based black pigment that is a CaOTiO.sub.2MnO.sub.2 base.

17: The leather-like sheet according to claim 15, wherein the thickness of the skin layer is from 10 to 30 m and the thickness of the intermediate layer is from 10 to 50 m.

18: The leather-like sheet according to claim 15, wherein the skin layer does not contain carbon black.

Description

BRIEF DESCRIPTION OF DRAWING

[0022] FIG. 1 is a schematic cross-sectional view for explaining a layer structure of a grain-like artificial leather according to an embodiment.

[0023] FIG. 2 is a view for explaining a measuring method of LIDAR sensor reflectance of the leather-like sheet, used in the examples.

[0024] FIG. 3 is a view showing the results obtained when surface of leather-like sheets obtained in the examples are measured by a LIDAR sensor.

DESCRIPTION OF EMBODIMENT

[0025] Hereinafter, an embodiment of the leather-like sheet according to the present invention will be described in detail. The leather-like sheet of the present embodiment is a leather-like sheet including a fiber base material and a colored resin layer laminated on the fiber base material, wherein the colored resin layer includes an intermediate layer and a skin layer laminated on the intermediate layer, the skin layer is a layer containing polyurethane and 3 g/m.sup.2 or more of an infrared-reflective black pigment, the intermediate laver is a layer containing polyurethane and a black pigment, and the leather-like sheet has a surface having a brightness value of L*30 in the L*a*b* color system.

[0026] FIG. 1 is a schematic cross-sectional Vie for explaining a layer structure of a leather-like sheet 10 which Is an example of the leather-like sheet of the present embodiment. The leather-like sheet 10 includes a fiber base material 1, a porous layer 2 mainly composed of polyurethane laminated on the fiber base material 1, a colored resin layer 5 including an intermediate layer 3 and a skin layer 4 adhered to the intermediate layer 3, and an adhesive layer 6 mainly composed of polyurethane adhering the porous layer 2 and the colored resin layer 5. The leather-like sheet is not limited to such a layer structure, and the layer structure is not particularly limited as long as it is a leather-like sheet including the fiber base material, and the colored resin layer laminated on the fiber base material and including the intermediate layer and the skin layer as described above. Additionally, as long as the effect of the present invention is not impaired, a clear layer having a thickness of about 1 to 5 m, which is a colorless transparent resin layer, may be further provided on the surface of the skin layer as necessary.

[0027] As the fiber base material, conventionally known artificial leather base materials used in the manufacture of artificial leathers or conventionally known synthetic leather base materials used in synthetic leathers, such as nonwoven fabrics, woven fabrics, knitted fabrics, or base materials: impregnated with an elastic polymer (polyurethane, etc.) therein, are used without any particular limitation. In addition, pigments may be blended in the elastic polymer as necessary. The thickness of the fiber base material is not particularly limited, but is preferably, for example, about 0.3 to 3 mm or further 0.5 to 1.5 mm. The type of the fiber forming the fiber base material is not particularly limited, and examples thereof include nylon-based fibers, polyester-based fibers, polyolefin-based fibers, and polyurethane-based fibers.

[0028] In addition, a fineness and a form of the fibers are not particularly limited. For example, the fineness may be a regular fiber such as more than 1 dtex, or an ultrafine fiber having a fineness less than 1 dtex. The form of the fibers may be s solid fiber or a fiber having voids such as a hollow fiber or a lotus-root-like fiber.

[0029] The skin layer is a polyurethane layer for coloring the surface of the leather-like sheet, containing 3 g/m.sup.2 or more of an infrared-reflective black pigment.

[0030] The skin layer is a polyurethane layer containing 3 g/m.sup.2 or more of an infrared-reflective black pigment, and thus becomes a colored polyurethane layer having a high reflectance with respect to near-infrared pulsed laser beams as will be described later.

[0031] The infrared-reflective black pigment is a black pigment having a reflectance of 25% or more with respect to a near-infrared ray of the wavelength of 905 nm, a reflectance of 50% or more with respect to a near-infrared ray of the wavelength of 1550 nm, and a transmittance of 50% or less with respect to a near-infrared ray of the wavelength of 905 nm. Further, it is preferable that the infrared-reflective black pigment has a reflectance of 30% or more with respect to a near-infrared ray of the wavelength of 905 nm, and a transmittance of 30% or less, more preferably 20% or less, and particularly preferably 0% or less with resect to a near-infrared ray of the wavelength of 905 nm. Specific examples of such infrared-reflective black pigments including titanium-based black pigments of a CaOTiO.sub.2MnO.sub.2 base (for example, TIPAQUE Black SG-103 manufactured by ISHIHARA SANGYO KAISHA, LTD.), titanium-based black pigments (Tilack Li manufactured by AKO KASEI Co., LTD. and complex oxide pigments of chromium oxide and iron oxide. The titanium-based black pigments of a CaOTiO.sub.2MnO.sub.2-base have a reflectance of 30% or more with respect to a near-infrared ray of the wavelength of 905 nm, a reflectance of 55% or more with respect. to a near-infrared ray of the wavelength of 1550 nm, and a transmittance of 10% or less with respect to a near-infrared ray of the wavelength of 905 nm.

[0032] For example, titanium-based black pigments of a CaOTiOMnO.sub.2 base are produced by mixing a calcium compound, a titanium compound, and a manganese compound by a wet grinding method and calcining the mixture at a temperature higher than 1110 C. Such titanium-based black pigments of a CaOTio.sub.2MnO.sub.2 base preferably have a perovskite phase as a main phase and a BET specific surface area of 1.0 m.sup.2/g or more and less than 3.0 m.sup.2/g.

[0033] The skin layer contains 3 g/m.sup.2 or More, preferably 3 to 5 g/m.sup.2 of the infrared-reflective black pigment. When the content of the infrared-reflective black pigment is less than 3 g/m.sup.2, the reflectance of the leather-like sheet with respect to near-infrared rays is low, and the detectability by LIDAR sensor is lowered. In addition, when the content of the infrared-reflective black pigment is too large, the blackness becomes low, and the cost-efficiency is also lowered.

[0034] The thickness of the skin layer is not particularly limited as long as the skin layer contains 3 g/m.sup.2 or more of an infrared-reflective black pigment, but is preferably 10 m or more, and more preferably from 20 to 30 m. When the skin layer is too thin, the infrared-reflective black pigment tends to be less likely to contain 3 g/m.sup.2 or more.

[0035] The content ratio of the infrared-reflective black pigment in the skin layer is not particularly limited as long as the skin layer contains 3 g/m.sup.2 or more of the infrared-reflective black pigment, but is preferably 10 mass % or more, more preferably 15 mass % or more, and particularly preferably 20 mass % or more. When the content ratio of the infrared-reflective black pigment is too low, the infrared-reflective black pigment is less likely to be contained in 3 g/m.sup.2 or more, and when the content ratio is too high, the blackness tends to be low and the cost-efficiency tends to be lowered.

[0036] The skin layer does not contain carbon black, or may contain carbon black in a range from 0 to 0.5 g/m.sup.2, or even from 0 to 0.1 g/m.sup.2 as long as the effect of the present invention is not impaired and depending on the type of carbon black. When the skin layer contains carbon black exceeding 0.5 g/m.sup.2, near-infrared rays irradiated on the surface of the obtained leather-like sheet is preferentially absorbed by carbon black, so that the reflectance of near-infrared rays becomes low and the detectability by LIDAR>sensors tends to decrease.

[0037] The skin layer may contain other pigments other than carbon black as long as the effect of the present invention is not impaired. The other pigments are not particularly limited as long as absorptance of near-infrared rays of the wavelength from 905 to 1600 nm is not too high, and specific examples thereof include anthraquinone-based pigments, Diketopyrrolopyrrole-based pigments, and perylene-based pigments such as perylene black.

[0038] Note that, for example, since perylene black has a transmittance of 60% or more with respect to a near-infrared ray of the wavelength of 905 nm, when used alone, the reflectance of near-infrared rays is low, so that the detectability by LIDAR sensors is low, and the color developability of dark colors is low.

[0039] The mean dispersion particle diameter of the infrared-reflective black pigment in the colored resin laver is not particularly limited, but is preferably from 1 to 10 m, more preferably from 1.5 to 8 m. When the mean dispersion particle diameter of the infrared-reflective black pigment is within such a range, irregular reflection of light on the surface of the particles of the infrared-reflective black pigment is easily suppressed, and the colored resin layer having a high blackness tends to be easily formed. When the mean dispersion particle diameter of the infrared-reflective black pigment is too small, light tends to be irregularly reflected on the surface of the particles of the infrared-reflective black pigment, so that the surface of the leather-like sheet tends to develop a reddish color. When the mean dispersion particle diameter of the infrared-reflective clack pigment is too large, the mechanical properties of the film of the colored resin layer deteriorate, and the abrasion resistance of the surface of the leather-like sheet tends to be deteriorated.

[0040] On the other hand, the intermediate layer is a layer containing polyurethane and a black pigment, and is colored dark.

[0041] The intermediate layer is a polyurethane layer which is colored in a dark color by containing a black pigment. The intermediate layer is a layer for adjusting the color visually recognized from the surface of the leather-like sheet to a dark color without blending a large amount of carbon black in the skin layer.

[0042] Examples of the black pigment contained in the intermediate layer include carbon black such as furnace black, channel black, and acetylene black; infrared-reflective black pigments; and composite oxide-based black pigments. Among these, carbon black is preferable from the viewpoint that the dark surface is easily obtained. In addition, the infrared-reflective black pigment. is preferable from the viewpoint of further increasing the reflectance of near-infrared ry.

[0043] Note that the intermediate layer may contain other pigments other than the black pigment for the purpose of arranging colors, as long as the effect of the present invention is not inhibited. Other pigments are not particularly limited, and specific examples thereof include anthraquinone-based pigments, diketopyrrolopyrrole-based pigments, and perylene-based pigments.

[0044] When the intermediate layer contains carbon black as a black pigment, it is preferable that the intermediate layer contains carbon black in an amount of 0.2 g/m.sup.2 or more, more preferably from 0.5 to 5 g/m.sup.2, from the viewpoint or easily obtaining the leather-like sheet having a dark surface of L*30. Further, when the intermediate layer contains an infrared-reflective black pigment as a black pigment, it is preferable that the intermediate layer contains an infrared-reflective black pigment in an amount of 2 g/m.sup.2 or more, more preferably from 2 to 5 g/m.sup.2, from the viewpoint of easily obtaining the leather-like sheet having a dark surface of a L*30.

[0045] The thickness of the intermediate laver is not particularly limited as long as the surface of the leather-like sheet can be adjusted to a surface having a lightness value of L*30, but is preferably from 10 to 50 m, and more preferably from 20 to 30 m. If the intermediate layer is too thin, it tends to be difficult to adjust to a dark color such as L*30.

[0046] The content ratio of the black pigment in the intermediate layer is not particularly limited as long as the surface of the leather-like sheet, can be adjusted to a surface having a L*30. When the black pigment contains carbon black, the content of carbon black is preferably 2 masse or more, and more preferably from 2 to 10 mass % in the intermediate layer. When the black pigment contains the infrared-reflective black pigment, the intermediate layer preferably contains 10 mass' or more of the infrared-reflective black pigment, and more preferably from 10 to 20 mass %. When the content ratio of the black pigment is too small, it tends to be difficult to obtain a dark color such as

[0047] The polyurethane for forming the intermediate layer, the skin layer, and the porous layer is obtained by reacting urethane raw material containing a polymer polyol, an organic polyisocyanate, and a chain extender. Polyurethanes are prepared as melts; organic solvent solutions (e.g., solutions in organic solvents such as dimethylformamide, methyl ethyl ketone, acetone, toluene, etc.); aqueous dispersions; or emulsions in the manufacture of the leather-like sheet.

[0048] Specific examples of the polymer polyols include polyether-based polyols such as polyethylene glycol, polypropylene glycol, polytetramethylene glycol, and polymethyltatramethylene glycol; polycarbonate-based polyols such as polyhexamethylene carbonate diol, poly(3-methyl-1,5-pentylene carbonate diol, polypentamethylene carbonate diol, and polytetramethylene carbonate diol; polyester-based polyols such as polyethylene adipate diol, polybutylene adipate diol, polypropylene adipate diol, polybutylene sebacate diol, polyhexamethylene adipate diol, poly(3-methyl-1,5-pentylene adipate)diol, poly(3-methyl-1,5-pentylene sebacate)diol, and polycaprolactone diol; r copolymers thereof. These may be used singly or in combination of two or more thereof.

[0049] Specific: examples of the organic polyisocyanates include hardly yellowing diisocyanates including aromatic diisocyanates such as 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 4,4-diphenylmethane diisocyanate, and xylylene diisocyanate; and non-yellowing diisocyanates such as aliphatic or alicyclic diisocyanates such as hexamethylene diisocyanate, isophorone diisocyanate, norbornene diisocyanate, and 4,4-dicyclohexylmethane diisocyanate. Further, if necessary, multi-functional isocyanates such as 3-functional isocyanates and 4-functional isocyanates may be usec in combination. These may be used singly or in combination of two or more thereof.

[0050] Further, specific examples of the chain extenders include diamines such as hydrazine, ethylenediamine. propylenediamine, hexamethylenediamine, nonamethylenediamine, xylylenediamine, isophoronediamine, piperazine and derivatives thereof, adipic acid dihydrazide, and isophthalic acid dihydrazide; triamines such as diethylenetriamine; diols such as ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, 1,4-his (-hydroxyethoxy)benzene, and 1,4-cyclohexanediol; and triols such as trimethylolpropane; tetraols such as pentaerythritol; amino alcohols such as aminoethyl alcohol and aminopropyl alcohol; and the like. These may be used singly or in combination of two or more thereof. Further, in the chain extension reaction, monoamines such as ethylamine, propylamine, and butylamine; carboxyl group-containing monoamine compounds such as 4-aminobutanoic acid and 6-aminohexanoic acid; and monools such as methanol, ethanol, propanol, and butanol may be used in combination with the chain extender.

[0051] The polyurethane for forming the porous layer is formed, for example, by applying a solution of the polyurethane to be wet-solidified to the surface of the fiber base material, and then immersing them in an aqueous coagulation bath to solidify the porous polyurethane. In addition, the porous laver may be permeated inside the fiber base material for the purpose of imparting shape stability or the like of the fiber base material. In this case, the polyurethane solution is impregnated into the fiber base material in advance, and additional polyurethane solution is coated onto it, and then, the material is immersed in an aqueous coagulation bath to coagulate the polyurethane, whereby the porous polyurethane can also be imparted inside the fiber base material. The thickness of the porous layer is not particularly limited, but is preferably, for example, about 100 to 600 m, or more preferably from 200 to 400 m.

[0052] In order to form the intermediate layer and the skin layer on the surface of the porous layer, for example, a method using the following dry surface forming method is exemplified.

[0053] A polyurethane film for forming the skin layer is formed on a release paper. Then, by forming a polyurethane film for forming the intermediate layer on the polyurethane film of the skin layer, the colored resin layer including the intermediate laver and the skin layer laminated on the intermediate layer is formed. The colored resin layer may further include a layer other than the intermediate layer in a layer below the skin layer.

[0054] Then, an adhesive is applied to the colored resin layer, and the solvent is completely or incompletely removed and dried. Then, the adhesive laminated on the colored resin layer formed on the release pa-per is bonded to the surface of the porous layer and pressed, and then the porous layer and the colored resin layer are bonded to each other via the adhesive layer by curing the adhesive. Then, by peeling the release paper from the surface of the colored resin layer, a leather-like sheet including the fiber base material and the colored resin layer laminated on the fiber base material is obtained.

[0055] In the leather-like sheet of the present embodiment, the leather-like sheet is colored so as to nave a surface of a value of L*30 in L*a*b* color system by the colored resin layer including the skin layer containing the infrared-reflective back pigment and the intermediate layer containing the black pigment as described above.

[0056] In L/a*b* color system, colored so as to have a surface having a lightness value of L*30 means that a lightness value, calculated from a coordinate value of a L*a*b* color system obtained by measuring a dark colored surface, which is a design surface of a leather-like sheet, using a spectrophotometer, Is satisfied a value of L*30. The lightness of the dark colored surface is preferably L*30, and more preferably L*25.

[0057] The leather-like sheet of the present embodiment includes the skin layer containing an infrared-reflective black piment as described above, whereby a leather-like sheet having a high reflectance to near-infrared rays can be obtained. Accordingly, the leather-like sheet colored dark that is easily detectable by LIDAR sensor is obtained.

[0058] The reflectance of the surface having a lightness value of L*30 of the leather-like sheet with respect to near-infrared rays is preferably 10% or more, more preferably 15% or more, with respect to a near-infrared ray of the wavelength of 905 nm. Further, the reflectance of the surface is preferably 10% or more, more preferably 15% or Tore with respect to a near-infrared ray of the wavelength of 1550 nm.

[0059] The solar reflectance in the wavelength-range from 250 to 2500 nm of the surface of the leather-like sheet is preferably 10% or more, more preferably 15% or more. When the solar reflectance is within such a range, it is preferable from the viewpoint that a leather-like sheet with good color developability having a lightness value of L*30 is more easily obtained in addition to a high reflectance with respect to near-infrared rays

[0060] The leather-like sheet of the present embodiment described above is preferably used as a grain-like leather-like sheet imitating to natural leather, which can used as a skin material for bacs, clothing, shoes, and the like. In particular, when used, for example, as a backpack such as a Randoseru using the leather-like sheet as a back surface material, or as a material for clothing, that covers large areas of the wearer's body, it is preferably used as a grain-like leather-like sheet detected by LIDAR sensors with high accuracy even if large areas of the body are covered by the grain-like leather-like sheet.

[0061] In particular, when a child with a small body wears a Randoseru, most of the body may be hidden by the Randoseru. In such cases, a child wearing a Randoseru that is not easily detected by a LIDAR sensor is less likely to be noticed by a vehicle equipped with a LIDAR sensor. According to the backpack of the present embodiment, since the back surface material is easily detected in the vehicle provided with the LIDAR sensor, it is possible to reduce the possibility of traffic accidents of children during school commuting.

[0062] Such a leather-like sheet is preferable that the leather-like sheet has a reflection intensity of 40 or more, or even 50 or more, measured at the wavelength of 905 nm, the measurement distance 10 m and from the skin layer side using a LIDAR sensor, for example, HORIZON manufactured by Livox Technology Company Limited, from the viewpoint the leather-like sheet is easily detected by a L-DAR sensor mounted on a vehicle as a safety device.

EXAMPLES

[0063] Hereinafter, the present invention will be described in more detail with reference to Examples. The scope of the present invention is not limited to these examples.

Example 1

[0064] Island-in-the-sea composite fibers containing 45 parts by mass of 6-nylon (sea component) and 55 parts by mass of polystyrene (island component) were melt-spun, and they were drawn to 3 times, applied an oil agent for fiber, and then, after mechanical crimping, dried. The resulting crimped fibers were cut into 51 mm to form a staple of 3 dtex and a web was formed. Then, needle punching was performed alternately from both sides of the web in total about 500 punches/cm.sup.2 to obtain an entangled nonwoven fabric. The basis weight of this entangled nonwoven was 350 g/m.sup.2) and the apparent specific gravity was 0.17. The entangled nonwoven fabric was treated with a 4% aqueous solution of polyvinyl alcohol, compressed and fixed to a thickness of about 1.3 mm, and smoothed the surface thereof by buffing. Then, a 13% solution of polyurethane mainly composed of polyester-based polyurethane in dimethylformamide (hereinafter referred to as DMF) was impregnated into it. Then, after applying the same polyurethane solution to the surface at a solid content of 100 g/m.sup.2, the polyurethane was made porous by wet-solidification through immersion in a mixed liquid of DMF/water. Then, the island components were eluted and eliminated in hot toluene to convert the island-in-the-sa composite fibers into hollow fibers. In this way, a fiber base material on which the porous layer immersed into the surface of the entangled nonwoven fabric was laminated was obtained. The thickness of the porous layer was 300 m.

[0065] Next, on a release paper (R-70 manufactured by LINTEC Corporation), 100 g/m.sup.2 of a polyurethane composition solution, which contains 100 parts by mass of a 22% DMF solution of a non-yellowing poly carbonate-based polyurethane, 30 parts by mass of a black vehicle containing 20 mass % of an infrared-reflective black pigment (titanium-based black pigment), and 30 parts by mass of DMF, is coated so as to be a thickness of about 20 m after drying, them, drying at 120 C. for 2 minutes, a skin layer colored black was formed. The titanium-based black pigment was the TIPAQUE Black SG 103 manufactured by ISHIHAPA SANGYO KAISHA, LTD., which is a CaOTiO.sub.2MnO.sub.2 based black pigment having a 30.1% of reflectance with respect to 905 nm, a 57.1% of reflectance with respect to 1550 nm, and a 10% or less of transmittance with respect to a near-infrared ray of the wavelength of 905 nm. The obtained skin layer did not contain carbon black, and the content of the titanium-based black pigment contained in the skin layer was 4.8 g/m.sup.2. The content. ratio of the titanium-based black pigment in the skin layer was 20 mass %.

[0066] Then, on the skin layer, 120 g/m.sup.2 Of a polyurethane composition solution containing 100 parts by mass of 30% DMF solution of a hardly yellowing polyether-based polyurethane, 20 parts by mass of a black vehicle containing 5% by mass of carbon black (furnace black), and 30 parts by mass of DMF and 30 parts by mass of MEK was coated so as to be a thickness of about 20 m after drying, and dried at 120 C. for 2 minutes to form an intermediate layer colored black. The furnace black has an about 5% of reflectance with respect to 905 nm, an about 6% of reflectance with respect to 1550 nm, and a 53 or less of transmittance with respect to the near-infrared ray of the wavelength of 905n m. The amounts of carbon black per unit area of the resulting intermediate layer were 0.6 g/me. The content ratio of carbon black in the intermediate layer was 3 mass %.

[0067] Then, a polyurethane-based adhesive solution was coated with 110 g/m.sup.2 on the intermediate layer formed on the release paper, and dried at 120 C. for 2 minutes to evaporate the solvent, thereby forming an adhesive layer. Then, the adhesive layer on the release paper was bonded to the porous layer laminated on the fiber base material to produce a laminated intermediate. Then, the laminated intermediate was pressed by pressing with a roll having a surface temperature of 75 C. with a clearance. Then, after an aging treatment at 50 C. for 3 days, the release caper was peeled off to obtain a leather-like sheet that was a grain-like artificial leather with a black surface.

[0068] The obtained leather-like sheet was evaluated as follows.

(Measurement of L* Value)

[0069] The coordinates of the L*a*b* color system on the surface of the leather-like sheet were measured with a spectrophotometer (CM-3700, manufactured by Minolta Co., Ltd.) to calculate the L* value. The number of samples was N=3, and the average value thereof was calculated.

(Reflectance, Transmittance)

[0070] The reflectance of the surface of the leather-like sheet was determined by measuring the reflectance spectrum of the wavelength-range from 250 nm to 2500 nm using a spectrophotometer (V-770 spectrophotometer, a type of ISN-923 integrating sphere manufactured by JASCO Co. Ltd.) and reading the reflectance of 905 nm and 1550 nm. The mean reflectance of all range up to the wavelength-range from 250 nm to 2500 nm was calculated as the solar reflectance. Further, the ca reflectance and transmittance of the titanium-based black pigment were measured using an ultraviolet-visible near-infrared spectrophotometer (V-670 manufactured by NIPPON DENSHOKU INDUSTRIES CO., LTD.) by placing the sample as a powder in a measuring cell and measuring the spectral reflectance and transmittance of in the range of from 300 nm to

(LIDAR Sensor Reflectance)

[0071] As shown in FIG. 2, a leather-like sheet of 26 cm26 cm was vertically placed in a frame surrounded by black cardboard. A HORIZON manufactured by Livox Technology Company Limited was installed at 10 m of the position as the measuring distance so that the emission light portion was at the height of 41 cm, and irradiated with laser having the wavelength of 905 nm. Then, the reflection intensity was measured by a method in which the energy when the laser beam was reflected from the object was expressed by a numerical value within a range of 0 (total absorption) to 255 (total reflection) FIG. 3 is a view showing the reflectance of the near-infrared ray on the surface of leather-like sheets measured by a LIDAR sensor. (A) is a view obtained by measuring the surface or the leather-like sheet of Example 1, (b) is: b measuring the surface of the leather-like sheet of Comparative Example 1.

(Mean Dispersion Particle Diameter)

[0072] Using a scanning electron microscope (JSM-IT500 manufactured by JEOL Ltd.), SEM photographs of 2000 times the thickness cross section of the colored resin-layer of the test piece cut out from the leather-like sheet was taken. Then, the particle diameters Rn of n particles of all infrared-reflective black pigments observed in any 2500 m.sup.2 area were measured. Note that the longest portion of the observed infrared-reflective black pigment was defined as the particle diameter. In the case where a plurality of particles aggregates to form secondary particles, the longest portion as the secondary particles was defined as the particle diameter. In addition, when a plurality of types of black pigment particles are present in SEM photographing area, qualitative analyses by EDS elemental analyses were performed in advance in SEM photographing area to determine the infrared-reflective black pigment to be measured for the particle diameter.

[0073] Then, the respective volume Vn were calculated from the obtained particle diameters Rn of n particles by the following equation. Note that the respective volume Vn are calculated as spherical shapes.

[0074] Volume of the particles of the infrared-reflective black pigment: Vn=4/3(Rn/2).sup.3

[0075] Then, the obtained volumes Vn of n particles were arranged in ascending order of the particle diameter Rn to calculate a cumulative sum to obtain a volume cumulative frequency. The cumulative volume frequency was plotted against the particle diameter Rn, and the particle diameter when the cumulative volume frequency was 50% was defined as the dispersed particle diameter (D50). The above measurement was performed at any five points of the leather-like sheet, and the mean of the dispersed particle diameters (D50) at the five points was defined as the mean dispersed particle diameter.

[0076] The above results are shown in Table 1 below.

TABLE-US-00001 TABLE 1 Com. Com. Com. Com. Com. Com. Com Com. Example No. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Skin layer Content amount of 4.8 3.4 4.8 4.8 0 4.8 1.9 2.9 4.8 0 0 0 Infrared-reflective black pigment (g/m.sup.2) Content amount of 0 0 0 0 0 0 0 0 0 0 4.8 4.8 Perylene-based black pigment (g/m.sup.2) Content amount of 0 0 0 0.5 3.4 0 0 1.9 0.6 0.6 0 0 Carbon black (g/m.sup.2) Content ratio of 20 14 20 20 0 20 8 12 20 0 0 0 Infrared-reflective black pigment (mass %) Content ratio of 0 0 0 0 0 0 0 0 0 0 20 20 Perylene-based black pigment (mass %) Content ratio of 0 0 0 2 14 0 0 8 3 3 0 0 Carbon black (mass %) thickness (m) 20 20 20 20 20 20 20 20 20 20 20 20 Intermediate Content amount of 0.6 0.6 0 0 0.6 0 0.6 0.6 0 0 0.6 0 layer Carbon black (g/m.sup.2) Content amount of 0 0 3.4 3.4 0 0 0 1.8 0 4.8 0 3.4 Infrared-reflective black pigment (g/m.sup.2) Content ratio of 3 3 0 0 3 0 3 3 0 0 3 0 Carbon black (mass %) Content ratio of 0 0 14 14 0 0 0 9 0 20 0 14 Infrared reflective black pigment (mass %) thickness (m) 20 20 20 20 20 20 20 20 20 20 20 20 Total content amount of Infrared 4.8 3.4 8.2 8.2 0.0 4.8 1.9 4.7 4.8 4.8 0 3.4 reflective black pigment (g/m.sup.2) Total content amount of Perylene- 0 0 0 0 0 0 0 0 0 0 4.8 4.8 based black pigment (g/m.sup.2) Total content amount of Carbon 0.6 0.6 0 0.0 4.0 0 0.6 2.5 0.6 0.6 0.6 0.0 black (g/m.sup.2) Mean Dispersion Particle Diameter 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 of Infrared reflective black pigment (m) Value of L* 24.0 24.3 24.7 23.5 22.1 34.0 24.0 22.3 23.0 24.8 28.6 35.0 Reflectance 905 nm 18 14 25 10 4 23 10 5 7 4 4 20 (%) 1550 nm 22 18 44 11 4 40 10 5 7 4 4 35 250 to 2500 nm 16 12 30 11 4 30 8 5 7 4 4 28 (Solar reflectance) LIDAR sensor reflectance 60 50 100 40 10 100 30 10 10 10 10 80 (No unit)

Example 2

[0077] In Example 1, artificial leather was obtained and evaluated in the same manner as in Example 1, except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black piment was changed to the skin lacer containing 3.4 g/m.sup.2 of the infrared-reflective black pigment. The results are shown in Table.

Example 3

[0078] In Example 1, an artificial leather was obtained and evacuated in the same manner as in Example 1, except that the intermediate layer containing 0.6 g/m.sup.2 of carbon black was changed to the intermediate layer containing 3.4 g/m.sup.2 of the infrared-reflective black pigment. The results are shown in Table 1.

Example 4

[0079] In Example 3, an artificial leather was obtained and evacuated in the same manner as in Example 1, except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black pigment were changed to the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black piment and 0.5 g/m.sup.2 of carbon black. The results are shown in Table 1.

Comparative Example 1

[0080] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example 1, except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black pigment was changed to the skin layer containing 3.4 g/m.sup.2 of carbon black to adjust the similar lightness of: the black. The results are shown in Table 1.

Comparative Example 2

[0081] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example 1, except that the intermediate layer containing 0.6 g/m.sup.2 of carbon black was changed to the intermediate layer containing no pigments. The results are shown in Table 1

Comparative Example 3

[0082] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example 1, except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black piment was changed to the skin layer containing 1.9 g/m.sup.2 of the infrared-reflective black pigment and 9 g/m.sup.2 of carbon black. The results are shown in Table 1.

Comparative Example 4

[0083] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example , except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black pigment was changed to the skin layer containing 2.9 g/m.sup.2 of the infrared-reflective black pigment and 1.9 g/m.sup.2 of carbon black. The results are shown in Table 1.

Comparative Example 5

[0084] In Example 1, an artificial leather was obtained and evaluated in the same manner as, in Example 1, except skin layer containing 4.8 g/m.sup.2 of the infrared reflective black piment was changed to the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black pigment and 0.6 g/m.sup.2 of carbon black, and the intermediate layer containing 0.6 g/m.sup.2 of carbon black was chanced to the intermediate layer containing no pigment. The results are shown in Table 1.

Comparative Example 6

[0085] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example 1 except that a change was made to replace the skin layer and the intermediate layer. The results are shown in Table 1.

Comparative Example 7

[0086] In Example 1, an artificial leather was obtained and evaluated in the same manner as in Example 1, except that the skin layer containing 41.8 g/m.sup.2 of the infrared-reflective black piment was changed to the skin layer containing 4.8 g/m.sup.2 of perylene-based black piment. As the perylene-based black pigment, perylene black (Paliogen Black L0084) having a transmittance of 65% or more with respect to a near-infrared ray of the wavelength of 905 nm was used. The results are shown in Table 1.

Comparative Example 8

[0087] In Example 3, an artificial leather was obtained and evaluated in the same manner as in Example 1, except that the skin layer containing 4.8 g/m.sup.2 of the infrared-reflective black pigment was changed to the skin layer containing 4.8 g/m.sup.2 of perylene black (Paliogen Black L0084). The results are shown in Table 1.

[0088] Referring to Table 1, each of the leather-like sheets, which is the artificial leather in Examples 1 to 4, in which the skin layer contains 3 g/m.sup.2 or more of an infrared-reflective black pigment and the intermediate layer contains a black pigment, was a leather-like sheet having a dark colored surface having the value of L*30 and was highly detectable by a LIDAR sensor. On the other hand, each of the leather-like sheets in Comparative Examples 1, 3, 4, and 6, which did not contain 3 gc/n or more of an infrared-reflective black pigment in the skin layer, had insufficient detectability by a LIDAR sensor. in addition, the leather-like sheet, which is the artificial leather in Comparative Example 2, in which the skin layer contains 3 g/m.sup.2 or more of an infrared-reflective black piment but the intermediate layer does not contain a crack pigment, was not able to obtain a dark-colored surface having the value of L*130. Further, the leather-like sheet, which is the artificial leather in comparative Example 5, in which the skin layer contains carbon black together with 3 g/m.sup.2 or more of an infrared-reflective black pigment and the intermediate layer contains no black pigments, was obtained with a dark color having the value L* of =30, but the detectability by a LIDAR sensor was insufficient because carbon black absorbed near-infrared rays. Further, the leather-like sheet in Comparative Example 7, which is an artificial leather in which the skin layer contains a perylene-based black pigment and the intermediate layer contains a black pigment, was obtained with a dark color having the value of L*30, but since the skin layer easily transmits near-infrared rays, the detectability by LIDAR sensors were insufficient. Further, the leather-like sheet in Comparative Example 8, in which the skin layer contained a perylene-based black pigment and the intermediate layer contained an infrared-reflective black pigment, had good detectability by a LIDAR sensor, but a dark-colored surface having the value of L*30 could not be obtained.

REFERENCE SIGNS LIST