GRADED PLANAR BUFFER FOR NANOWIRES

Abstract

A nanowire structure includes a substrate, a graded planar buffer layer, a patterned mask, and a nanowire. The graded planar buffer layer is on the substrate. The patterned mask is on the graded planar buffer layer and includes an opening through which the graded planar buffer layer is exposed. The nanowire is on the graded planar buffer layer in the opening of the patterned mask. A lattice constant of the graded planar buffer layer is between a lattice constant of the substrate and a lattice constant of the nanowire. By providing the graded planar buffer layer, lattice mismatch between the nanowire and the substrate can be reduced or eliminated, thereby improving the quality and performance of the nanowire structure.

Claims

1. A nanowire structure comprising: a substrate; a graded planar buffer layer on the substrate; a patterned mask on the graded planar buffer layer, the patterned mask comprising an opening through which the graded planar buffer layer is exposed; and a nanowire on the graded planar buffer layer in the opening of the patterned mask, wherein a lattice constant of the graded planar buffer layer is between a lattice constant of the substrate and a lattice constant of the nanowire.

2. The nanowire structure of claim 1 wherein the lattice constant of the graded planar buffer layer at least partially transitions between the lattice constant of the substrate and the lattice constant of the nanowire between a first surface of the graded planar buffer layer on the substrate and a second surface of the graded planar buffer layer on which the nanowire is provided.

3. The nanowire structure of claim 2 wherein the lattice constant of the graded planar buffer layer completely transitions between the lattice constant of the substrate and the lattice constant of the nanowire between the first surface of the graded planar buffer layer and the second surface of the graded planar buffer layer.

4. The nanowire structure of claim 1 wherein the graded planar buffer layer is a blanket layer on an entire surface of the substrate.

5. The nanowire structure of claim 1 wherein the graded planar buffer layer comprises a plurality of discrete layers, each having different properties.

6. The nanowire structure of claim 1 wherein the graded planar buffer layer is electrically insulating.

7. The nanowire structure of claim 1 wherein a thickness of the graded planar buffer layer is between 100 nm and 50000 nm.

8. The nanowire structure of claim 1 wherein: the substrate comprises one of indium phosphide, gallium antimonide, and gallium arsenide; the graded planar buffer layer comprises one or more layers each comprising one or more of indium aluminum arsenide, indium gallium arsenide, and aluminum gallium arsenide antimonide; and the nanowire comprises one of indium arsenide, indium antimonide, and indium arsenide antimonide.

9. The nanowire structure of claim 1 wherein the nanowire comprises a nanowire buffer layer and an active layer on the nanowire buffer layer.

10. The nanowire structure of claim 9 wherein a lattice constant of the nanowire buffer layer is between the lattice constant of the graded planar buffer layer and a lattice constant of the active layer.

11. A method for manufacturing a nanowire structure comprising: providing a substrate; providing a graded planar buffer layer on the substrate; providing a patterned mask on the graded planar buffer layer, the patterned mask comprising an opening through which the graded planar buffer layer is exposed; and providing a nanowire on the graded planar buffer layer in the opening of the patterned mask, wherein the graded planar buffer layer is provided such that a lattice constant of the graded planar buffer layer is between a lattice constant of the substrate and a lattice constant of the nanowire.

12. The method of claim 11 wherein the graded planar buffer layer is provided such that the lattice constant of the graded planar buffer layer at least partially transitions between the lattice constant of the substrate and the lattice constant of the nanowire between a first surface of the graded planar buffer layer on the substrate and a second surface of the graded planar buffer layer on which the nanowire is provided.

13. The method of claim 12 wherein the graded planar buffer layer is provided such that the lattice constant of the graded planar buffer layer completely transitions between the lattice constant of the substrate and the lattice constant of the nanowire between the first surface of the graded planar buffer layer and the second surface of the graded planar buffer layer.

14. The method of claim 11 wherein the graded planar buffer layer is provided as a blanket layer on an entire surface of the substrate.

15. The method of claim 11 wherein providing the graded planar buffer layer comprises providing a plurality of discrete layers, each having different physical properties.

16. The method of claim 11 wherein the graded planar buffer layer is provided such that the graded planar buffer layer is electrically insulating.

17. The method of claim 11 wherein the graded planar buffer layer is provided such that a thickness of the graded planar buffer layer is between 100 nm and 50000 nm.

18. The method of claim 11 wherein: the substrate comprises one of indium phosphide, gallium antimonide, and gallium arsenide; the graded planar buffer layer comprises one or more layers each comprising one or more of indium aluminum arsenide, indium gallium arsenide, and aluminum gallium arsenide antimonide; and the nanowire comprises one of indium arsenide, indium antimonide, and indium arsenide antimonide.

19. The method of claim 11 wherein providing the nanowire comprises providing a nanowire buffer layer and providing an active layer on the nanowire buffer layer such that a lattice constant of the nanowire buffer layer is between the lattice constant of the graded planar buffer layer and a lattice constant of the active layer.

20. The method of claim 11 further comprising providing a superconductor layer on the nanowire.

Description

BRIEF DESCRIPTION OF THE DRAWING FIGURES

[0009] The accompanying drawing figures incorporated in and forming a part of this specification illustrate several aspects of the disclosure, and together with the description serve to explain the principles of the disclosure.

[0010] FIG. 1 illustrates a nanowire structure according to one embodiment of the present disclosure.

[0011] FIG. 2 illustrates a nanowire structure according to one embodiment of the present disclosure.

[0012] FIG. 3 is a flow chart illustrating a method for manufacturing a nanowire structure according to one embodiment of the present disclosure.

DETAILED DESCRIPTION

[0013] The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the embodiments and illustrate the best mode of practicing the embodiments. Upon reading the following description in light of the accompanying drawing figures, those skilled in the art will understand the concepts of the disclosure and will recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and the accompanying claims.

[0014] It will be understood that, although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of the present disclosure. As used herein, the term and/or includes any and all combinations of one or more of the associated listed items.

[0015] It will be understood that when an element such as a layer, region, or substrate is referred to as being on or extending onto another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being directly on or extending directly onto another element, there are no intervening elements present. Likewise, it will be understood that when an element such as a layer, region, or substrate is referred to as being over or extending over another element, it can be directly over or extend directly over the other element or intervening elements may also be present. In contrast, when an element is referred to as being directly over or extending directly over another element, there are no intervening elements present. It will also be understood that when an element is referred to as being connected or coupled to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being directly connected or directly coupled to another element, there are no intervening elements present.

[0016] Relative terms such as below or above or upper or lower or horizontal or vertical may be used herein to describe a relationship of one element, layer, or region to another element, layer, or region as illustrated in the Figures. It will be understood that these terms and those discussed above are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures.

[0017] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms a, an, and the are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms comprises, comprising, includes, and/or including when used herein specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.

[0018] Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms used herein should be interpreted as having a meaning that is consistent with their meaning in the context of this specification and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

[0019] FIG. 1 shows a nanowire structure 10 according to one embodiment of the present disclosure. The nanowire structure 10 includes a substrate 12, a graded planar buffer layer 14 on the substrate 12, a patterned mask 16 on the buffer layer 14, the patterned mask 16 including an opening through which a surface of the graded planar buffer layer 14 is exposed, a nanowire 18 on the graded planar buffer layer 14 in the opening of the patterned mask 16, and a superconductor 20 on the nanowire 18 and a portion of the patterned mask 16. As discussed above, conventionally the nanowire 18 would be provided directly on the substrate 12. For the nanowire 18 to be functional, it must comprise a conductive semiconductor such as indium arsenide, indium antimonide, and indium arsenide antimonide. Further, the substrate 12 must be an insulator such as gallium arsenide, gallium antimonide, and indium phosphide. Conducting semiconductors and insulators generally have very different lattice constants, resulting in a high lattice mismatch between the nanowire 18 and the substrate 12 in conventional nanowire structures 10.

[0020] To solve this problem, the graded planar buffer layer 14 is provided between the substrate 12 and the nanowire 18. The graded planar buffer layer 14 has a lattice constant that is between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18. In some embodiments, the graded planar buffer layer 14 provides a transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18 over a thickness of the graded planar buffer layer 14 such that the transition occurs from a first surface of the graded planar buffer layer 14 on the substrate 12 to a second surface of the graded planar buffer layer 14 on which the nanowire 18 is provided. The graded planar buffer layer 14 may provide a partial transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18 or a complete transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18. The graded planar buffer layer 14 may comprise multiple discrete layers, each of which has different physical properties. For example, the graded planar buffer layer 14 may comprise multiple layers, each of which has a different lattice constant in order to provide the transition in lattice constant from the lattice constant of the substrate 12 to the lattice constant of the nanowire 18 as discussed above. In various embodiments, the graded planar buffer layer 14 may comprise one or more layers of indium aluminum arsenide, indium aluminum antimonide, indium gallium arsenide, indium gallium phosphide, indium aluminum arsenide antimonide, indium gallium aluminum antimonide, aluminum gallium arsenide antimonide, and indium gallium arsenide antimonide. Providing the graded planar buffer layer 14 provides a much better lattice match for the nanowire 18 than the substrate 12. Accordingly, defects such as misfit dislocations, slip planes, and stacking faults can be reduced or eliminated. Further, other desirable properties, such as electrical confinement and insulation, can be maintained by selecting the appropriate material for the graded planar buffer layer 14.

[0021] The substrate 12 may comprise one of silicon, indium phosphide, gallium phosphide, gallium antimonide, and gallium arsenide. The substrate 12 may have a thickness between 50 m and 1000 m. The graded planar buffer layer 14 may have a thickness between 100 nm and 50000 nm. The patterned mask 16 may comprise a dielectric material such as silicon dioxide. The nanowire 18 may have a thickness between 20 nm and 300 nm. The nanowire 18 may further have a diameter of the order of a nanometer (10-9 meters) and up to 1000 nm, or a ratio of length to width greater than 1000. The superconductor may comprise one of aluminum, lead, niobium indium, tin, and vanadium. The superconductor 20 may have a thickness between 3 nm and 30 nm. The present disclosure contemplates any and all permutations and combinations of the above materials and thicknesses for the substrate 12, the graded planar buffer layer 14, the patterned mask 16, and the nanowire 18.

[0022] FIG. 2 shows the nanowire structure 10 according to an additional embodiment of the present disclosure. The nanowire structure 10 shown in FIG. 2 is substantially similar to that shown in FIG. 1, except that the nanowire 18 includes a nanowire buffer layer 18A and an active layer 18B. The nanowire buffer layer 18A may be provided to provide additional lattice matching between the graded planar buffer layer 14 and the active layer 18B. Accordingly, the nanowire buffer layer 18A may have a lattice constant that is between a lattice constant of the graded planar buffer layer 14 and the active layer 18B. Further, the nanowire buffer layer 18A may provide a transition in lattice constant from a lattice constant of the graded planar buffer layer 14 and the lattice constant of the active layer 18B. Nanowire buffer layers 18A have been used in the past to provide lattice matching, but are limited in their ability to do so because of constraints on the thickness thereof, as providing the nanowire buffer layer 18A above a certain thickness limits the available area for the active layer 18B of the nanowire 18, which provides the functionality thereof. The graded planar buffer layer 14 is not limited in its thickness, and thus can provide a much larger transition in lattice constant while maintaining other desirable characteristics of the substrate 12 such as electrical insulation. In contrast to the nanowire buffer layer 18A, which is provided only in the opening of the patterned mask 16 and forms part of the nanowire 18, the graded planar buffer layer 14 is provided as a blanket layer over an entire surface of the substrate 12 such that the patterned mask 16 is provided on the graded planar buffer layer 16.

[0023] In one exemplary embodiment, the substrate 12 is indium phosphide, and has a thickness of 350 m. The graded planar buffer layer 14 includes several layers, including a first layer of In.sub.0.52Al.sub.0.48As having a thickness of 100 nm on the substrate 12, a second layer of In.sub.0.53Ga.sub.0.47As having a thickness of 2.5 nm on the first layer, a third layer of In.sub.0.52Al.sub.0.48As having a thickness of 2.5 nm on the second layer, a fourth layer on the third layer, the fourth layer transitioning from In.sub.0.52Al.sub.0.48As to In.sub.0.89Al.sub.0.11As over a thickness of 1000 nm, for example, as 20 discrete layers having a thickness of 50 nm, a fifth layer of InAl.sub.0.20As having a thickness of 33 nm on the fourth layer, a sixth layer of InAl.sub.0.20As having a thickness of 25 nm on the fifth layer, and a seventh layer of InGa.sub.0.20As having a thickness of 4 nm on the sixth layer. The nanowire 18 may include a first layer of InGa.sub.0.30As on the graded planar buffer layer 14 having a thickness of 60 nm, a second layer of InAs having a thickness of 10 nm on the first layer, and a third layer of InGa.sub.0.30As having a thickness of 60 nm on the second layer. The various layers of the graded planar buffer layer 14 provide a transition in lattice constant between the substrate 12 and the nanowire 18. Notably, the particular configuration of the graded planar buffer layer 14 and the nanowire 18, including the number of layers, the thickness of the layers, and the material composition of each layer shown in FIG. 3 are merely exemplary and are not intended to limit the scope of the present disclosure in any way.

[0024] In another exemplary embodiment, the substrate 12 is gallium antimonide and has a thickness of 350 m. The graded planar buffer layer 14 includes a first layer of gallium antimonide having a thickness of 500 nm, a second layer of Al.sub.0.8Ga.sub.0.2AsSb having a thickness of 50 nm on the first layer, and a third layer of indium arsenide having a thickness of 2 monolayers (ML) on the second layer. The nanowire 18 may comprise a single layer of indium arsenide having a thickness of 150 nm. Those skilled in the art will appreciate that gallium antimonide has a lattice constant that is relatively close to that of indium arsenide. However, other properties (e.g., electrical confinement and isolation) of gallium antimonide may not be ideal as a platform for the nanowire 18. The graded planar buffer layer 14 may thus primarily be provided in this embodiment to provide one or more other desirable properties (e.g., electrical confinement and isolation), rather than for lattice matching.

[0025] FIG. 3 is a flow diagram illustrating a method for manufacturing the nanowire structure 10 according to one embodiment of the present disclosure. The method begins by providing the substrate 12 (block 100). The graded planar buffer layer 14 is provided on the substrate 12 (block 102). The graded planar buffer layer 14 may be provided by any suitable manufacturing process. As discussed above, the graded planar buffer layer 14 may comprise multiple layers, each having different properties, and thus providing the graded planar buffer layer 14 may comprise providing several layers one on top of the other. Further as discussed above, the graded planar buffer layer 14 is provided as a blanket layer over an entire surface of the substrate. The patterned mask 16 is provided on the graded planar buffer layer 14 (block 104). Providing the patterned mask 16 on the graded planar buffer layer 14 may comprise providing a blanket mask layer on an entire surface of the graded planar buffer layer 14 then patterning the blanket mask layer by any suitable process to provide the patterned mask 16. The nanowire 18 is provided on the graded planar buffer layer 14 through one or more openings in the patterned mask 16 (block 106). Providing the nanowire 18 may comprise performing a selective-area-growth (SAG) process, or any other suitable manufacturing process. As discussed above, the nanowire 18 may include multiple layers such as the nanowire buffer layer 18A and the active layer 18B and thus providing the nanowire 18 may comprise providing more than one layer. The superconductor 20 is provided on the nanowire 18 (block 108) and, optionally, on a portion of the patterned mask 16.

[0026] Those skilled in the art will recognize improvements and modifications to the preferred embodiments of the present disclosure. All such improvements and modifications are considered within the scope of the concepts disclosed herein and the claims that follow.