ELECTROCHROMIC FILM MATERIAL AND ELECTROCHROMIC FILM DEVICE PREPARED THEREFROM

Abstract

The invention belongs to the technical field of electrochromic devices, particularly relates to a novel electrochromic film material, and further discloses an electrochromic film device prepared by the novel electrochromic film material. According to the electrochromic film device provided by the invention, the electrochromic film material is prepared by taking a high adhesive-property composition and a redox-type liquid-state electrochromic composition as raw materials for the first time, and the redox-type liquid-state electrochromic composition is dispersed and cured between conductive substrates by a curing reaction of the high adhesive-property composition. After a test, electrochromic response time of the electrochromic film device prepared by the invention is between 7-11 seconds, number of cycles is between 14-160,000 times, and color difference b value is between 20 and +30. It has a high color changing speed, long service life and stable performance, with a maximum cycle life reaching 160,000 times, and has good application performance.

Claims

1. An electrochromic film material, characterized in that its raw material components comprise a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the mass ratio of the high adhesive-property composition to the redox-type liquid-state electrochromic composition is 1:0.01-50; the high adhesive-property composition comprises following components in parts by weight: 1-60 parts by weight of a resin; 0.01-50 parts by weight of a monomer; 0.01-50 parts by weight of a crosslinking agent; 0.001-5 parts by weight of an initiator; and 0.001-0.01 parts by weight of a spacer.

2. (canceled)

3. The electrochromic film material according to claim 1, characterized in that: the resin comprises an acrylate resin, a polyurethane resin, a polyester resin or an epoxy resin; the monomer comprises an acrylic monomer, an acrylate monomer, a vinyl monomer, an epoxy monomer or an epoxy acrylate monomer; the crosslinking agent comprises a polyfunctional functional monomer; the initiator comprises a photoinitiator or a thermal initiator; and the spacer comprises rigid microbeads.

4. The electrochromic film material according to claims 1, characterized in that the redox-type liquid-state electrochromic composition comprises the following components in parts by weight: 0.01-10 parts by weight of an electrochromic material; 0.01-10 parts by weight of an ion storage material; 42 50.01-102.5 parts by weight of a liquid electrolyte material.

5. The electrochromic film material according to claim 4, characterized in that: the electrochromic material comprises an electrochromic material such as an organic high molecule, an organic small molecule, and a metal oxide or metal complex; the ion storage material comprises a compound such as vanadium pentoxide, tungsten oxide, cerium oxide, indium tin oxide, Prussian blue, polyaniline, triphenylamine, phenazine or viologen; the liquid electrolyte material consists of 50-99 parts by weight of a liquid conductive medium and 0.1-3.5 parts by weight of an electrolyte salt; the liquid conductive medium comprises a liquid organic solvent, an ionic liquid or a gel-like crosslinked polymer material; and the electrolyte salt is selected from at least one of lithium perchlorate, lithium hexafluorophosphate, lithium tetrafluorophosphate, lithium bis(oxalate)borate, lithium diimine, and lithium bis(trifluoromethylsulfonyl) imide.

6. The electrochromic film material according to claim 5, characterized in that: the organic high molecule electrochromic material is selected from at least one of polythiophene, polypyrrole, polyaniline, high-molecular polymers with electrochromic structures on side chains, and high-molecular metal complexes; the organic small-molecular electrochromic material is selected from one of viologen compounds, triphenylamine, triphenylamine derivatives, carbazole, carbazole derivatives, anthraquinone, anthraquinone derivatives, phenothiazine and phenothiazine derivatives; the metal oxide electrochromic material is a transition metal oxide selected from vanadium pentoxide, tungsten oxide, cerium oxide and indium tin oxide; the metal complex is selected from one of Prussian blue, Prussian black, Prussian white, Prussian green, and nitrosyl oxygen-containing molybdenum complexes.

7. A method for preparing the electrochromic film material according to claim 6, characterized by comprising uniformly mixing the components of the high adhesive-property composition and the redox-type liquid-state electrochromic composition according to a selected amount, and curing to obtain the electrochromic film material.

8. The method for preparing the electrochromic film material according to claim 7, characterized in that during the curing process, the initiator is a photoinitiator, the curing condition is ultraviolet light, the energy of the ultraviolet light is 0.5 mW/cm2 to 5.5 mW/cm2, and the curing time is 30 s to 5 min.

9. The method for preparing the electrochromic film material according to claim 7, characterized in that during the curing process, the initiator is a thermal initiator, the curing condition is oven heating, the heating temperature is 30-80 C., and the curing time is 10 s-30 min.

10. An electrochromic film device, characterized by comprising two layers of conductive substrates, and the electrochromic film material according to claim 6, wherein the electrochromic film material is cured between the two layers of conductive substrates.

11. The electrochromic film device according to claim 10, characterized in that the conductive substrate comprises an indium tin oxide conductive glass, an indium tin oxide conductive film, a silver nanowire conductive film, a fluorinated doped tin oxide glass, or a polymer conductive film.

12. A method for preparing the electrochromic film device according to claim 11, characterized by comprising the steps of: uniformly mixing the components of the high adhesive-property composition and the redox-type liquid-state electrochromic composition according to a selected amount to obtain the electrochromic film material; and coating the electrochromic film material between two selected layers of conductive substrates, and carrying out a curing reaction to obtain a required electrochromic film device.

13. The method for preparing the electrochromic film device according to claim 12, characterized in that during the curing reaction, the initiator is a photoinitiator, the curing condition is ultraviolet light, the energy of the ultraviolet light is 0.5 mW/cm2 to 5.5 mW/cm2, and the curing time is 30 s to 5 min.

14. The method for preparing the electrochromic film device according to claim 12, characterized in that during the curing reaction, the initiator is a thermal initiator, the curing condition is oven heating, the heating temperature is 30-80 C., and the curing time is 10 s-30 min.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0041] Test conditions and methods for the performance of the obtained electrochromic film device in the following embodiments of the invention specifically comprise:

[0042] electrochromic properties: ultraviolet-visible-spectrophotometer (Jesco-V670) supplied by Japan Spectrometer Co., Ltd;

[0043] chromaticity change of the electrochromic device in different states: Philips 15-4460 colorimeter;

[0044] number of cycles: the cycling of the electrochromic device is realized by utilizing a multi-potential step method, and the cycling process of the electrochromic device is monitored in real time by combining V-670 so as to test the working performance of the electrochromic device;

[0045] driving voltage: CHI-660D electrochemical analyzer supplied by Shanghai Chenhua Instrument Co., Ltd.

EMBODIMENT 1

[0046] The electrochromic film device of the embodiment comprises two layers of indium tin oxide (ITO) conductive films as conductive substrates, wherein electrochromic film material is dispersed and cured between the two layers of ITO conductive films.

[0047] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0048] 10 kg of polyurethane acrylate resin;

[0049] 10 kg of methacrylate monomer;

[0050] 3 kg of trifunctional crosslinking agent PETA;

[0051] 0.003 kg of photoinitiator TPO;

[0052] 0.003 kg of 10 m spacer;

[0053] 1 kg of triphenylamine;

[0054] 1 kg of Prussian blue;

[0055] 74 kg of propylene carbonate; and

[0056] 0.5 kg of lithium perchlorate.

[0057] The preparation method of the electrochromic film device in the embodiment comprises taking each raw material component according to a selected amount, uniformly mixing the raw material components, coating the raw material components between two pieces of indium tin oxide (ITO) conductive films with a length of 3 meters and a width of 3 meters by using a roller coater, and curing for 2 minutes by using ultraviolet light with the energy of 2.5 mW/cm.sup.2 to obtain an electrochromic film device 1.

[0058] The resulting device was connected to a DC voltage of 5 V, the device turned yellow green from blue, the response time was 11 seconds, the light transmittance of the device was changed from 84.4 to 84.3, the color difference b value was changed from 20 to +30, and the number of cycles was 151154.

EMBODIMENT 2

[0059] The electrochromic film device of the embodiment comprises two layers of indium tin oxide (ITO) conductive films as conductive substrates, wherein electrochromic film material is dispersed and cured between the two layers of ITO conductive films.

[0060] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0061] 10 kg of polyurethane acrylate resin;

[0062] 8 kg of epoxy acrylate;

[0063] 3 kg of trifunctional crosslinking agent TMPTA;

[0064] 0.003 kg of photoinitiator TPO;

[0065] 0.003 kg of 10 m spacer;

[0066] 3 kg of polythiophene

[0067] 1 kg of Prussian blue;

[0068] 74 kg of propylene carbonate; and

[0069] 0.5 kg of lithium perchlorate.

[0070] The preparation method of the electrochromic film device in the embodiment comprises taking each raw material component according to a selected amount, uniformly mixing the raw material components, coating the raw material components between two pieces of indium tin oxide (ITO) conductive films with a length of 3 meters and a width of 3 meters by using a roller coater, and curing for 3 minutes by using ultraviolet light with the energy of 2.5 mW/cm.sup.2 to obtain an electrochromic film device 2.

[0071] The resulting device was connected to a DC voltage of 5.5 V, the device turned yellow green from blue, the response time was 10 seconds, the light transmittance of the device was changed from 84.4 to 84.1, the color difference b value was changed from 20 to +20, and the number of cycles was 148958.

EMBODIMENT 3

[0072] The electrochromic film device of the embodiment comprises two layers of indium tin oxide (ITO) conductive films as conductive substrates, wherein electrochromic film material is dispersed and cured between the two layers of ITO conductive films.

[0073] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0074] 10 kg of polyurethane acrylate resin;

[0075] 8 kg of epoxy acrylate;

[0076] 3 kg of trifunctional crosslinking agent TMPTA;

[0077] 0.003 kg of thermal initiator;

[0078] 0.003 kg of 10 m spacer;

[0079] 3 kg of polypyrrole;

[0080] 1 kg of Prussian blue;

[0081] 74 kg of propylene carbonate; and

[0082] 0.5 kg of lithium perchlorate.

[0083] The preparation method of the electrochromic film device in the embodiment comprises the following steps: and taking the raw material components according to a selected amount, uniformly mixing the raw material components, coating the raw material components between two pieces of indium tin oxide (ITO) conductive films with a length of 3 meters and a width of 3 meters by using a roller coater, and curing at 60 C. for 5 minutes by using an oven to obtain an electrochromic film device 3.

[0084] The resulting device was connected to a DC voltage of 5.5 V, the device turned yellow green from blue, the response time was 8 seconds, the light transmittance of the device was changed from 84.4 to 81.5, the color difference b value was changed from 18 to +11, and the number of cycles was 144650.

EMBODIMENT 4

[0085] The electrochromic film device of the embodiment comprises two layers of silver nanowire conductive films as conductive substrates, wherein electrochromic film material is dispersed and cured between the two layers of silver nanowire conductive films.

[0086] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0087] 10 kg of polyurethane acrylate resin;

[0088] 8 kg of epoxy acrylate;

[0089] 3 kg of trifunctional crosslinking agent TMPTA;

[0090] 0.003 kg of thermal initiator;

[0091] 0.003 kg of 10 m spacer;

[0092] 3 kg of polypyrrole;

[0093] 1 kg of ferrocene;

[0094] 95 kg of ethylene glycol carbonate; and

[0095] 0.5 kg of lithium perchlorate.

[0096] The preparation method of the electrochromic film device in the embodiment comprises taking the raw material components according to a selected amount, uniformly mixing the raw material components, coating the raw material components between two pieces of silver nanowire conductive films with a length of 3 meters and a width of 3 meters by using a roller coater, and curing for 5 minutes at 60 C. by using an oven to obtain an electrochromic film device 4.

[0097] The device was connected to a DC voltage of 5.0 V, the device turned yellow green from blue, the response time was 9 seconds, the light transmittance of the device was changed from 84.6 to 82.9, the color difference b value was changed from 17 to +11, and the number of cycles was 144920.

EMBODIMENT 5

[0098] The electrochromic film device comprises two layers of fluorinated doped tin oxide glasses as conductive substrates, and the electrochromic film material is dispersed and cured between the two layers of fluorinated doped tin oxide glasses.

[0099] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0100] 1 kg of epoxy resin;

[0101] 0.01 kg of epoxy acrylate monomer;

[0102] 0.01 kg of difunctional crosslinking monomer HDDA;

[0103] 0.001 kg of photoinitiator EDB;

[0104] 0.001 kg of 20 m spacer;

[0105] 0.01 kg of polyaniline;

[0106] 0.01 kg of vanadium pentoxide;

[0107] 50 kg of ethylene glycol carbonate; and

[0108] 0.1 kg of lithium hexafluorophosphate.

[0109] The electrochromic film device described in this embodiment is prepared in the same method as in Embodiment 1.

EMBODIMENT 6

[0110] The electrochromic film device of the embodiment comprises two layers of indium tin oxide (ITO) conductive films as conductive substrates, wherein electrochromic film material is dispersed and cured between the two layers of ITO conductive films.

[0111] According to the embodiment, the electrochromic film material comprises a high adhesive-property composition and a redox-type liquid-state electrochromic composition, and the electrochromic film material specifically comprises the following raw materials:

[0112] 60 kg of polyurethane acrylate resin CN966J75NS;

[0113] 50 kg of vinyl monomer;

[0114] 50 kg of difunctional crosslinking monomer TEGDA;

[0115] 5 kg of thermal initiator AIBN;

[0116] 0.01 kg of 30 m spacer;

[0117] 10 kg of phenothiazine;

[0118] 10 kg of polyaniline;

[0119] 99 kg of propylene carbonate; and

[0120] 3.5 kg of lithium bis(oxalate)borate.

[0121] The electrochromic film device described in this embodiment is prepared in the same method as in Embodiment 3.

[0122] According to the test data, the electrochromic response time of the electrochromic film device provided by the invention is 7-11 seconds, the number of cycles is 14-160,000 times, the color difference b value is 20 to +30, and the electrochromic film device has good performance.

[0123] According to the electrochromic film device disclosed by the invention, the production process is simple, the light transmittance of an original conductive base material is basically not changed before and after the curing, and the light transmittance of the electrochromic film device is over 80, which can meet the requirements of a user on chromaticity and light transmittance adjustment. Meanwhile, compared with an existing light regulating device on the market, the device provided by the invention has the advantages that the technology of dispersing and fixing an electrochromic solution by using the high adhesive-property composition effectively reduces the production cost, and has good economic benefit.

[0124] It is obvious that the above-described embodiments are merely illustrative for clarity of description and are not restrictive of the embodiments. For those skilled in the art, other variations and modifications in different forms can be made on the basis of the above description. All implementations are not required to be exhaustive. However, obvious changes and alterations derived therefrom are still within the scope of the invention.