Welded joint

Abstract

A welded joint comprising an aluminum-based base material comprising an aluminum alloy or pure aluminum and a copper-based base material comprising a copper alloy or pure copper joined by a weld metal portion is provided. The weld metal portion contains copper in ranges of less than 75% by mass and silicon in ranges of less than 13% by mass and has a higher content of copper and silicon than the aluminum-based base material.

Claims

1. A welded joint comprising an aluminum-based base material comprising an aluminum alloy or pure aluminum and a copper-based base material comprising a copper alloy or pure copper joined by a weld metal portion, wherein the weld metal portion contains copper in ranges of less than 75% by mass and silicon in ranges of less than 13% by mass and has a higher content of copper and silicon than the aluminum-based base material.

2. The welded joint according to claim 1, wherein the weld metal portion further contains zinc in a range of 30% by mass or less and has a higher content of zinc than the aluminum-based base material.

3. The welded joint according to claim 2, wherein copper content of the weld metal portion is less than 75% by mass when the weld metal portion is measured at a position in the weld metal portion 300 m away from a boundary surface between the copper-based base material and the weld metal portion.

4. The welded joint according to claim 3, wherein the weld metal portion further contains iron, and the iron is present in a concentrated state at a surface of the weld metal portion.

5. The welded joint according to claim 2, wherein the weld metal portion further contains iron, and the iron is present in a concentrated state at a surface of the weld metal portion.

6. The welded joint according to claim 1, wherein copper content of the weld metal portion is less than 75% by mass when the weld metal portion is measured at a position in the weld metal portion 300 m away from a boundary surface between the copper-based base material and the weld metal portion.

7. The welded joint according to claim 6, wherein the weld metal portion further contains iron, and the iron is present in a concentrated state at a surface of the weld metal portion.

8. The welded joint according to claim 1, wherein the weld metal portion further contains iron, and the iron is present in a concentrated state at a surface of the weld metal portion.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic perspective view of a welded joint being an embodiment according to the present disclosure.

(2) FIG. 2 is a schematic perspective view showing a state before joining in which an end portion of a copper-based base material is only superimposed on an end portion of an aluminum-based base material.

(3) FIG. 3 is a schematic perspective view showing a state before joining when an end portion of a copper-based base material is superimposed on an end portion of an aluminum-based base material, and then a powder filler metal is placed so as to be in contact with the copper end face located on the aluminum-based base material.

(4) FIG. 4 is a schematic cross-sectional view when a welded joint comprising an aluminum-based base material and a copper-based base material joined by a weld metal portion is cut perpendicularly to the welding direction.

DETAILED DESCRIPTION

(5) Thereafter, embodiments of the welded joint according to the present disclosure will be described below with reference to the accompanying drawings.

(6) FIG. 1 shows a welded joint being an embodiment according to the present disclosure.

(7) The illustrated welded joint 1 comprises an aluminum-based base material 2 comprising an aluminum alloy or pure aluminum and a copper-based base material 3 comprising a copper alloy or pure copper joined by a weld metal portion 4.

(8) The aluminum alloy is not particularly limited, and examples of the aluminum alloy include AlMn-based alloys (JIS 3000-based alloys), AlMg-based alloys (JIS 5000-based alloys), and AlMgSi alloys (JIS 6000-based alloys), and examples of the pure aluminum include JIS 1000-based alloys. Specific examples are A1100, A1050, A3003, A3004, A5052, A5083, A6061, and the like.

(9) The copper alloy is not particularly limited, and examples of the copper alloy include CuZn-based alloys (brass) and CuSn-based alloys (bronze), and examples of the pure copper include oxygen-free copper, tough pitch copper, and phosphorus-deoxidized copper. Specific examples are C1020, C1100, C1201, C2600, C5191, C6191, and the like.

(10) In the welded joint 1 of the present disclosure, in the weld metal portion 4, copper is contained in the ranges of less than 75% by mass and silicon is contained in the range of less than 13% by mass, and the content of copper and silicon is made higher than in the aluminum-based base material 2. Thus, a welded joint having high joint strength and having excellent ductility can be provided. Hereinafter, the reason for the limitation of the content of copper and silicon in the weld metal portion 4 will be described.

(11) (I) Copper and silicon being contained in the ranges of less than 75% by mass and less than 13% by mass respectively, and the content of copper and silicon being made higher than in the aluminum-based base material 2

(12) During welding, the aluminum-based base material 2 having a lower melting point than the copper-based base material 3 melts in the vicinity of the joining portion, and the strength tends to decrease in a melted site and a site where structure change occurs due to heat input in the welding, compared with strength in the surrounding site with no change. The present inventors have made a study for compensating for strength decrease accompanying metal structure change due to welding, and the like, based on the finding that copper (Cu) and silicon (Si) can improve the strength of aluminum by the addition of proper amounts. As a result, the present inventors have succeeded in forming a welded joint having high joint strength and excellent ductility by arranging the weld metal portion 4 being the joining portion so that copper is contained in the range of less than 75% by mass and silicon is contained in the range of less than 13% by mass, and the content of copper and silicon is made higher, preferably 0.5% by mass or more higher, than in the aluminum-based base material 2. When at least one of the content of Cu and the content of Si in the weld metal portion 4 is higher than the above proper ranges, the ductility of the weld metal portion 4 decreases significantly.

(13) In the present disclosure, it may be preferred that the copper content when measured at a position in the weld metal portion (weld bead) 4 300 m away from a boundary surface B between the copper-based base material 3 and the weld metal portion 4 is less than 75% by mass. In the welding of the aluminum-based base material 2 and the copper-based base material 3, the boundary surface B and its vicinity region in the weld metal portion 4, more specifically the region R1 of the weld metal portion 4 divided by the boundary surface B between the copper-based base material 3 and the weld metal portion 4 and a line drawn at a position N 300 m away from this boundary surface B (shown by the dot-and-dash line in FIG. 4), as shown in FIG. 4, are a region close to the copper-based base material 3, and mixing with the aluminum-based base material 2 does not proceed, and therefore the Cu content is higher than in another region R2. Particularly when a region having a Cu content of 75% or more is present in a wide range in the weld metal portion 4, the ductility of the weld metal portion 4 tends to decrease. Thus, it is preferred that even if the region having a content of Cu of 75% or more is present in the weld metal portion 4, the region is only in the boundary surface B between the copper-based base material 3 and the weld metal portion 4 and the region R1 being its vicinity region, and the copper content when measured in the region R2 being at a position 300 m or more away from the boundary surface B is less than 75% by mass. For the quantitative analysis of the copper content in the weld metal portion, for example, the weld metal portion (weld bead portion) is cut from the obtained welded joint in the direction perpendicular to the welding direction, mirror finish is performed by polishing, then the region of the weld metal portion 4 is grasped from a composition image of a scanning electron microscope (SEM), and then point analysis is performed by an electron probe microanalyzer (EPMA), and in the analysis, by comparing with the analysis results of standard samples of elements, quantification can be performed.

(14) (II) In the present disclosure, proper amounts of copper and silicon are contained in the weld metal portion 4 as described above, and zinc (Zn), iron (Fe), manganese (Mn), magnesium (Mg), and phosphorus (P) can be further contained as needed.

(15) (i) Zinc (Zn) being further contained in the range of 30% by mass or less, and the content of zinc being made higher than in the aluminum-based base material 2

(16) It may be preferred that the weld metal portion 4 further contains zinc (Zn) in the range of 30% by mass or less, and the content of zinc is made higher than in the aluminum-based base material 2. Further adding zinc in the range of 30% by mass or less to the weld metal portion 4, in addition to the addition of proper amounts of Cu and Si described above, can effectively improve strength and is therefore preferred for compensating for a decrease in the strength of the joining portion accompanying metal structure change due to welding, and the like. The zinc content in the weld metal portion 4 is set at 30% by mass or less because when the zinc content is higher than 30% by mass, the ductility of the weld metal portion 4 tends to decrease. It is preferred that the zinc (Zn) content in the weld metal portion 4 is made 0.8% by mass or more higher, more preferably 1.0% by mass or more higher, than zinc content in the aluminum-based base material 2. Further, in order to exhibit the effect of compensating for a decrease in the strength of the joining portion accompanying metal structure change due to welding, and the like, it is preferred that the lower limit value of the zinc content in the weld metal portion 4 is set at 0.5% by mass.

(17) (ii) Iron (Fe) being further contained, and this iron being present in a concentrated state at the surface of the weld metal portion

(18) Further, in the present disclosure, it may be preferred that the weld metal portion 4 further contains iron (Fe), and this iron is present in a concentrated state at the surface of the weld metal portion 4 because by Fe being present in a concentrated state at the surface of the weld metal portion (weld bead) 4, deformation at the surface of the weld metal portion 4 is inhibited, and the effect of improving the strength is achieved. When a large amount of Fe is present to the central portion of the weld metal portion 4, the ductility of the weld metal portion 4 may decrease. It is preferred that the content of Fe present at the surface of the weld metal portion 4 is 3 times or more average Fe content when measured in the entire weld metal portion 4. It is preferred that the content of Fe present at the surface of the weld metal portion 4 is in the range of 0.5 to 2.0% by mass, and it is preferred that for Fe content when measured in the entire weld metal portion 4, the average value of the Fe content is 0.1 to 2.0% by mass. For the quantitative analysis of the content of Fe present at the surface (surface layer) of the weld metal portion, for example, the weld metal portion (weld bead portion) 4 is cut from the obtained welded joint in the direction perpendicular to the welding direction, mirror finish is performed by polishing, then the weld metal portion region is grasped from a composition image of a scanning electron microscope (SEM), and then point analysis is performed by an electron probe microanalyzer (EPMA) on a line drawn at a position M 50 m inside from the surface of the weld metal portion (shown by the broken line in FIG. 4), and in the analysis, by comparing with the analysis results of standard samples of elements, quantification can be performed.

(19) (iii) 2.0% by mass or less of manganese (Mn), 4.0% by mass or less of magnesium (Mg), and 1.0% by mass or less of phosphorus (P) being contained

(20) Mn is a component having the action of the improvement of the ductility of the weld metal portion and can therefore be added with an upper limit of 2.0% by mass. When the Mn content exceeds 2.0% by mass, coarse intermetallic compounds are formed, and the ductility may decrease.

(21) Mg is a component having the action of the improvement of the strength of the weld metal portion and can therefore be added with an upper limit of 4.0% by mass. When the Mg content exceeds 4.0% by mass, the corrosion resistance of the weld metal portion may decrease.

(22) P is a component having the action of the improvement of the ductility of the weld metal portion and can therefore be added with an upper limit of 1.0% by mass. When the P content exceeds 1.0% by mass, coarse intermetallic compounds are formed, and the ductility may decrease.

(23) [Manufacturing Method for Welded Joint]

(24) Thereafter, a method for manufacturing the welded joint of the present disclosure will be described while specifically illustrated below.

(25) In the present disclosure, a melt welding method such as arc welding, laser welding, or electron beam welding is applied. In order to adjust the components of the weld metal portion, a filler metal can be used as needed. When a filler metal is used, a filler metal in a rod form, a wire form, a foil form, a powder form, or the like is appropriately selected. Particularly, using a filler metal in a powder form is suitable for manufacturing a lap-welded joint or a lap fillet-welded joint because the influence of volume decrease in the melting and solidification process is reduced. When it is necessary to improve the filling rate of the powder, a dispersing material comprising polyethylene glycol, a polyether, or the like may be used.

(26) Examples of the filler metal used include AlCuSi-based or AlCuSiZn-based alloys. By using a filler metal based on such an alloy, it is possible to adjust the alloy composition of the weld metal portion within the prescribed range. In the filler metal, it is necessary to appropriately change the composition according to the compositions of the aluminum-based base material and the Cu-based base material used, and, for example, it is desired to use a filler metal comprising an AlCuSi-based alloy of 30% by mass or less of Cu and 13% by mass or less of Si. Further, when Zn is also added to the weld metal portion, it is desired to use a filler metal comprising an AlCuSiZn-based alloy of 30% by mass or less of Cu, 13% by mass or less of Si, and 30% by mass or less of Zn.

(27) The above-described parts only show some embodiments of this disclosure, and various changes can be made in the claims. In FIG. 1, a case where the welded joint is a lap joint (fillet lap joint) is shown, but the present disclosure is not limited to only such a welded joint and can be various welded joints according to the application, such as a butt joint, a corner joint, and a T-joint.

EXAMPLES

(28) Hereinafter, a description will be given in more detail based on the Examples of the present disclosure, but the present disclosure is not limited to these.

Examples 1 to 51 and Comparative Examples 1 to 6

(29) A copper-based base material 3 of length 100 mmwidth 50 mmthickness 1 mm was placed on an aluminum-based base material 2 of length 100 mmwidth 50 mmthickness 1 mm so as to be superimposed in the range of length direction dimension 30 mmwidth direction dimension 50 mm as shown in FIG. 2. Thereafter, a powder filler metal 5 was placed so as to be in contact with the total length of the end face of the copper-based base material 3 located on the aluminum-based base material 2, as shown in FIG. 3. In some Examples, an iron powder was further placed on the powder filler metal 5. As the powder filler metal, eight types of powder filler metals Nos. 1 to 8 are shown in Table 1. The powder filler metals Nos. 1 to 8 all contain at least Al, Si, and Fe, and Nos. 2 to 4 and 6 to 8 contain Cu, and further, Nos. 3, 5, and 8 also contain Zn.

(30) The types of the aluminum-based base material 2 and the copper-based base material 3, the type of the powder filler metal (No. in Table 1), the amount of the powder filler metal added (g) per mm of weld length, whether or not the iron powder is placed on the powder filler metal, the amount of the iron powder added (g) per mm of weld length, and the welding method are shown in Table 2.

(31) Further, as the aluminum-based base material, any of A1050 (pure Al), A3003 (AlMn-based alloy), A5052 (AlMg-based alloy), A5083 (AlMg-based alloy), and A6061 (AlMgSi-based alloy) was used, and as the copper-based base material, any of C1100 (tough pitch copper), C1020 (oxygen-free copper), C1220 (phosphorus-deoxidized copper), and C2100 (brass) was used.

(32) The composition components of A1050, A3003, A5052, A5083, and A6061 used in the Examples and Comparative examples are as follows.

(33) [A1050]

(34) Cu: 0.01% by mass, Si: 0.15% by mass, Zn: 0.01% by mass, Fe: 0.20% by mass, balance Al

(35) [A3003]

(36) Cu: 0.10% by mass, Si: 0.25% by mass, Zn: 0.05% by mass, Fe: 0.30% by mass, Mn: 1.25% by mass, balance Al

(37) [A5052]

(38) Cu: 0.02% by mass, Si: 0.10% by mass, Zn: 0.01% by mass, Fe: 0.20% by mass, Mg: 2.50% by mass, Cr: 0.20% by mass, balance Al

(39) [A5083]

(40) Cu: 0.01% by mass, Si: 0.10% by mass, Zn: 0.05% by mass, Fe: 0.20% by mass, Mn: 0.70% by mass, Mg: 4.50% by mass, Cr: 0.10% by mass, balance Al

(41) [A6061]

(42) Cu: 0.25% by mass, Si: 0.50% by mass, Zn: 0.10% by mass, Fe: 0.40% by mass, Mg: 1.0% by mass, Cr: 0.10% by mass, balance Al

(43) The welding was carried out by laser welding or TIG welding. In the laser welding, laser light output from a fiber laser was passed through a collimator lens and an f lens and adjusted so that the spot diameter was a diameter of 600 m. The laser welding was performed at a welding output of 1000 W. The welding speed was set at 1000 mm/min, and the irradiation position of the laser was set at a position on the aluminum-based base material 2 side 500 m away from the end face of the copper-based base member 3. In the TIG welding, the powder filler metal 5 manually placed and the surrounding base material (aluminum-based base material 2) were melted and joined. The welding current was set at 150 A, and the welding was performed downward with a speed of 30 cm/min as a rough standard.

(44) For the welded joints fabricated above, the composition analysis of the weld metal portion and the aluminum-based base material, and a tensile shear test were carried out. The details of each evaluation will be described below.

(45) <Composition Analysis of Weld Metal Portion>

(46) The weld metal portion (weld bead portion) was cut from the obtained welded joint in the direction perpendicular to the welding direction, and mirror finish was performed by polishing. Then, the weld metal portion region was grasped from a composition image of an SEM, and then the composition was analyzed by point analysis by an EPMA. In the analysis, by comparing with the analysis results of standard samples of elements, quantification was performed. For measurement, a beam having a spot diameter of 50 m was used, and the entire weld metal portion was analyzed at intervals of 100 m in the thickness direction and width direction of the weld metal portion. The elements used as analysis targets were Cu, Si, Zn, Fe, Mn, Mg, and P. From the obtained analysis results, the average content (% by mass) of Cu, Si, Zn, Fe, Mn, Mg, and P in the entire weld metal portion, Cu content (% by mass) when measured on a line drawn at a position N in the weld metal portion 300 m away from the boundary surface B between the copper-based base material 3 and the weld metal portion 4 (shown by the dot-and-dash line in FIG. 4), and the content (% by mass) of Fe present at the surface (surface layer) of the weld metal portion were each calculated.

(47) <Tensile Shear Test>

(48) For each welded joint obtained, both width ends were each cut by 7.5 mm to fabricate a sample in a strip form having the width decreased to 35 mm. A tensile shear test was performed using this sample as a test piece, and the maximum load (N) being the tensile load when the test piece broke was obtained, and the ductility (%) was calculated. For the evaluation of the ductility, the total width of the weld metal portion before and after the test was measured, and the ductility was calculated by [(amount of change in weld metal portion width before and after test)/(width of weld metal portion before test)]100(%). In the present Examples, for joint strength, a case where the above maximum load was 400 N or more was evaluated as being at an acceptable level, and for the ductility, a case where the numerical value calculated by the above formula was 1.0% or more was evaluated as being at an acceptable level. Their evaluation results are shown in Table 3.

(49) TABLE-US-00001 TABLE 1 Component composition (% by mass) Filler metal No. Cu Si Zn Fe Al 1 0 15 0 0.2 Balance 2 40 15 0 0.2 Balance 3 40 15 20 0.2 Balance 4 75 7 0 0.2 Balance 5 0 7 40 0.2 Balance 6 40 15 0 3.5 Balance 7 40 0.2 0 0.2 Balance 8 40 15 40 0.2 Balance

(50) TABLE-US-00002 TABLE 2 Filler metal Amount of filler Whether or Amount of Al-based base Copper-based Filler metal added not iron powder iron powder material base material metal (g) per mm of is placed on added (g) per mm Welding Type Type No. weld length filler metal of weld length method Example 1 A1050 C1100 1 1 Not placed 0 Laser welding Example 2 A1050 C1100 1 3 Not placed 0 Laser welding Example 3 A1050 C1100 2 1 Not placed 0 Laser welding Example 4 A1050 C1100 2 3 Not placed 0 Laser welding Example 5 A1050 C1100 3 1 Not placed 0 Laser welding Example 6 A1050 C1100 3 3 Not placed 0 Laser welding Example 7 A1050 C1100 4 1 Not placed 0 Laser welding Example 8 A1050 C1100 5 1 Not placed 0 Laser welding Example 9 A1050 C1100 1 1 Placed 0.01 Laser welding Example 10 A1050 C1100 2 1 Placed 0.01 Laser welding Example 11 A1050 C1100 3 1 Placed 0.01 Laser welding Example 12 A3003 C1100 1 1 Not placed 0 Laser welding Example 13 A3003 C1100 2 1 Not placed 0 Laser welding Example 14 A3003 C1100 3 1 Not placed 0 Laser welding Example 15 A3003 C1100 3 3 Not placed 0 Laser welding Example 16 A3003 C1100 3 1 Placed 0.01 Laser welding Example 17 A5052 C1100 2 1 Not placed 0 Laser welding Example 18 A5052 C1100 3 1 Not placed 0 Laser welding Example 19 A5052 C1100 4 1 Not placed 0 Laser welding Example 20 A5052 C1100 1 1 Placed 0.01 Laser welding Example 21 A5052 C1100 2 1 Placed 0.01 Laser welding Example 22 A5083 C1100 1 3 Not placed 0 Laser welding Example 23 A5083 C1100 4 1 Not placed 0 Laser welding Example 24 A5083 C1100 5 1 Not Placed 0 Laser welding Example 25 A5083 C1100 1 1 Placed 0.01 Laser welding Example 26 A5083 C1100 2 1 Placed 0.01 Laser welding Example 27 A6061 C1100 1 1 Not placed 0 Laser welding Example 28 A6061 C1100 2 3 Not placed 0 Laser welding Example 29 A6061 C1100 3 1 Not placed 0 Laser welding Example 30 A6061 C1100 3 3 Not placed 0 Laser welding Example 31 A6061 C1100 5 1 Not placed 0 Laser welding Example 32 A1050 C1020 1 1 Not placed 0 Laser welding Example 33 A1050 C1020 2 3 Not placed 0 Laser welding Example 34 A1050 C1020 3 1 Not placed 0 Laser welding_ Example 35 A1050 C1020 3 3 Not placed 0 Laser welding Example 36 A1050 C1020 2 1 Placed 0.01 Laser welding Example 37 A1050 C1220 1 3 Not placed 0 Laser welding Example 38 A1050 C1220 2 3 Not placed 0 Laser welding Example 39 A1050 C1220 3 1 Not placed 0 Laser welding Example 40 A1050 C1220 4 1 Not placed 0 Laser welding Example 41 A1050 C1220 5 1 Not placed 0 Laser welding Example 42 A1050 C2100 1 3 Not placed 0 Laser welding Example 43 A1050 C2100 2 1 Not placed 0 Laser welding Example 44 A1050 C2100 2 3 Not placed 0 Laser welding Example 45 A1050 C2100 1 1 Placed 0.01 Laser welding Example 46 A1050 C2100 2 1 Placed 0.01 Laser welding Example 47 A1050 C1100 6 1 Not placed 0 Laser welding Example 48 A1050 C1100 8 3 Not placed 0 Laser welding Example 49 A1050 C1100 8 3 Placed 0.01 Laser welding Example 50 A1050 C1100 2 1 Not placed 0 TIG welding Example 51 A1050 C1100 3 1 Not placed 0 TIG welding Comparative Example 1 A1050 C1100 1 3 Not placed 0 Laser welding Comparative Example 2 A1050 C1100 7 1 Not placed 0 Laser welding Comparative Example 3 A1050 C1100 2 3 Not placed 0 Laser welding Comparative Example 4 A1050 C1100 1 3 Placed 0.01 Laser welding Comparative Example 5 A1050 C1100 7 1 Placed 0.01 Laser welding Comparative Example 6 A1050 C1100 7 3 Placed 0.01 Laser welding

(51) TABLE-US-00003 TABLE 3 Aluminum-based Weld metal portion Performance base material Cu content (% by evaluation Component mass) at position Fe content Maximum composition Average component composition N 300 m away (% by mass) load (N) Duc- (% by mass) (% by mass) from boundary in surface in tensile tility Cu Si Zn Cu Si Zn Fe Mn Mg P position B layer shear (%) Example 1 0.01 0.15 0.01 15 8 0.02 0.2 0 0 0 62 0.2 474 1.2 Example 2 0.01 0.15 0.01 14 12 0.02 0.2 0 0 0 56 0.2 440 1.1 Example 3 0.01 0.15 0.01 27 5 0.02 0.2 0 0 0 65 0.2 403 1.4 Example 4 0.01 0.15 0.01 45 12 0.02 0.2 0 0 0 62 0.2 519 1.3 Example 5 0.01 0.15 0.01 27 5 5.00 0.2 0 0 0 52 0.2 594 2.2 Example 6 0.01 0.15 0.01 45 12 15.00 0.2 0 0 0 60 0.2 469 2.8 Example 7 0.01 0.15 0.01 74 5 0.02 0.2 0 0 0 75 0.2 540 1.3 Example 8 0.01 0.15 0.01 15 5 30.00 0.2 0 0 0 60 0.2 428 2.5 Example 9 0.01 0.15 0.01 15 8 0.02 0.3 0 0 0 53 1.0 703 1.2 Example 10 0.01 0.15 0.01 27 5 0.02 0.3 0 0 0 60 1.0 730 1.2 Example 11 0.01 0.15 0.01 27 5 5.00 0.3 0 0 0 61 1.0 639 2.4 Example 12 0.10 0.25 0.05 15 8 0.02 0.2 0.25 0 0 59 0.2 502 1.4 Example 13 0.10 0.25 0.05 27 5 0.02 0.2 0.25 0 0 62 0.2 424 1.3 Example 14 0.10 0.25 0.05 27 5 5.00 0.2 0.25 0 0 65 0.2 546 2.1 Example 15 0.10 0.25 0.05 45 12 15.00 0.2 0.25 0 0 57 0.2 418 2.5 Example 16 0.10 0.25 0.05 27 5 5.00 0.3 0.25 0 0 66 1.0 607 2.5 Example 17 0.02 0.10 0.01 27 5 0.02 0.2 0 0.3 0 65 0.2 509 1.2 Example 18 0.02 0.10 0.01 27 5 5.00 0.2 0 0.3 0 55 0.2 436 2.1 Example 19 0.02 0.10 0.01 74 5 0.02 0.2 0 0.3 0 75 0.2 591 1.3 Example 20 0.02 0.10 0.01 15 8 0.02 0.3 0 0.3 0 53 1.0 788 1.3 Example 21 0.02 0.10 0.01 27 5 0.02 0.3 0 0.3 0 53 1.0 709 1.7 Example 22 0.01 0.10 0.05 14 12 0.02 0.2 0.10 1.8 0 63 0.2 532 1.4 Example 23 0.01 0.10 0.05 74 5 0.02 0.2 0.10 1.8 0 75 0.2 509 1.4 Example 24 0.01 0.10 0.05 15 5 30.00 0.2 0.10 1.8 0 73 0.2 525 2.7 Example 25 0.01 0.10 0.05 15 8 0.02 0.3 0.10 1.8 0 63 1.0 745 1.5 Example 26 0.01 0.10 0.05 27 5 0.02 0.3 0.10 1.8 0 68 1.0 782 1.4 Example 27 0.25 0.50 0.10 15 8 0.02 0.2 0 0.3 0 74 0.2 425 1.4 Example 28 0.25 0.50 0.10 45 12 0.02 0.2 0 0.3 0 54 0.2 429 1.5 Example 29 0.25 0.50 0.10 27 5 5.00 0.2 0 0.3 0 59 0.2 474 2.6 Example 30 0.25 0.50 0.10 45 12 15.00 0.2 0 0.3 0 70 0.2 454 2.4 Example 31 0.25 0.50 0.10 15 5 30.00 0.2 0 0.3 0 67 0.2 423 2.5 Example 32 0.01 0.15 0.01 15 8 0.02 0.2 0 0 0 61 0.2 505 1.8 Example 33 0.01 0.15 0.01 45 12 0.02 0.2 0 0 0 74 0.2 412 1.2 Example 34 0.01 0.15 0.01 27 5 5.00 0.2 0 0 0 50 0.2 411 2.3 Example 35 0.01 0.15 0.01 45 12 15.00 0.2 0 0 0 54 0.2 583 2.4 Example 36 0.01 0.15 0.01 27 5 0.02 0.3 0 0 0 70 1.0 621 1.2 Example 37 0.01 0.15 0.01 14 12 0.02 0.2 0 0 0.01 80 0.2 582 1.3 Example 38 0.01 0.15 0.01 45 12 0.02 0.2 0 0 0.01 74 0.2 545 1.2 Example 39 0.01 0.15 0.01 27 5 5.00 0.2 0 0 0.01 57 0.2 474 2.5 Example 40 0.01 0.15 0.01 74 5 0.02 0.2 0 0 0.01 75 0.2 591 1.4 Example 41 0.01 0.15 0.01 15 5 30.00 0.2 0 0 0.01 61 0.2 510 2.4 Example 42 0.01 0.15 0.01 14 12 0.02 0.2 0 0 0 55 0.2 499 1.2 Example 43 0.01 0.15 0.01 27 5 0.02 0.2 0 0 0 71 0.2 561 1.9 Example 44 0.01 0.15 0.01 45 12 0.02 0.2 0 0 0 69 0.2 599 1.3 Example 45 0.01 0.15 0.01 15 8 0.02 0.3 0 0 0 50 1.0 615 1.4 Example 46 0.01 0.15 0.01 27 5 0.02 0.3 0 0 0 74 1.0 742 1.9 Example 47 0.01 0.15 0.01 27 5 0.02 1.0 0 0 0 73 1.0 497 1.5 Example 48 0.01 0.15 0.01 30 5 31.00 0.2 0 0 0 60 0.2 489 1.0 Example 49 0.01 0.15 0.01 30 5 31.00 0.3 0 0 0 60 1.0 481 1.0 Example 50 0.01 0.15 0.01 27 5 0.02 0.2 0 0 0 77 0.2 588 1.1 Example 51 0.01 0.15 0.01 27 5 5.00 0.2 0 0 0 78 0.2 580 1.0 Comparative 0.01 0.15 0.01 14 14 0.02 0.2 0 0 0 57 0.2 713 0.2 Example 1 Comparative 0.01 0.15 0.01 40 0.1 0.02 0.2 0 0 0 65 0.2 376 2.4 Example 2 Comparative 0.01 0.15 0.01 75 8 0.02 0.2 0 0 0 75 0.2 768 0.2 Example 3 Comparative 0.01 0.15 0.01 14 14 0.02 0.3 0 0 0 57 1.0 607 0.2 Example 4 Comparative 0.01 0.15 0.01 40 0.1 0.02 0.3 0 0 0 65 1.0 264 2.4 Example 5 Comparative 0.01 0.15 0.01 75 8 0.02 0.3 0 0 0 75 1.0 682 0.2 Example 6 (Note) The underlined bold characters in the table 3 mean being outside propriety in the present disclosure or that the performance is not at an acceptable level.

(52) From the results in Table 3, Examples 1 to 51 all had a tensile shear load in the range of 403 to 788 N and had a joint strength at an acceptable level, and also for the ductility, the calculated numerical value was in the range of 1.0 to 2.8% and at an acceptable level. On the other hand, in all of Comparative Examples 1 to 6, either the joint strength or the ductility was not at an acceptable level.

(53) According to the present disclosure, a welded joint having high joint strength and having excellent ductility can be provided. This welded joint being able to be applied to, for example, electrodes and bus bars for Li ion batteries, and electrodes, terminals, and wiring for electronic devices and wire harnesses. In addition, application is particularly expected in such wide-ranging fields that the use of a welded joint formed by the joining of different types of metal materials, an aluminum-based base material and a copper-based base material to each other is needed, for the purpose of promoting weight reduction and the like.