Polyhalite granulation process

Abstract

There is provided herein a process for the production of polyhalite granules from fine dry polyhalite powder comprising preparing a binder-water mix and mixing the binder-water mix with the polyhalite powder in a mixer, continuously adding water to the mixer to provide a polyhalite material, discharging the polyhalite material from the mixer and introducing the material into a fluid bed, drying the material and screening the material to receive granules ranging in size between 1.4 mm to 4.75 mm.

Claims

1. A process for the production of polyhalite granules from fine dry polyhalite powder comprising: preparing a binder-water mix and mixing the binder-water mix with the polyhalite powder in a mixer; continuously adding water to the mixer to provide a polyhalite material; Discharging the polyhalite material from the mixer and introducing the material into a fluid bed; Drying the material; and Screening the material to receive granules ranging in size between 1.4 mm to 4.75 mm.

2. The process of claim 1, wherein preparing a binder-water mix comprises mixing a binder in a concentration of between 2.5-10% of the feed weight with water in a concentration of between 3-9% of the feed weight.

3. The process of claim 1, wherein the binder-water mix is mixed with the polyhalite powder in a mixer for 5-15 minutes.

4. The process of claim 1, wherein continuously adding water to the mixer to provide a polyhalite material comprises continuously adding water for at least two more minutes.

5. The process of claim 1, wherein discharging the material from the mixer and introducing the material into a fluid bed is performed for one minute at 20 degrees.

6. The process of claim 1, wherein drying the material is performed at 150 degrees.

7. The process of claim 6, wherein said drying is performed in a fluid bed or drum dryer.

Description

DETAILED DESCRIPTION OF THE INVENTION

(1) According to some demonstrative embodiments, there is provided a process for the granulation of polyhalite.

(2) According to some demonstrative embodiments, granules of polyhalite may provide superior characteristics, including for example, a sustained and/or controlled released of the fertilizer to the ground, for example, due to the substantially similar size and/or diameter of the granules.

(3) According to some demonstrative embodiments, the term fertilizer: may include any material of natural or synthetic origin that is applied to soils or to plant tissues to supply one or more plant nutrients essential to the growth of plants, including, for example, Single nutrient (straight) fertilizers such as Ammonium nitrate, Urea, calcium ammonium nitrate, superphosphate, e.g., Single superphosphate (SSP), phosphogypsum,

(4) Triple superphosphate (TSP) or a mixture thereof; Multinutrient fertilizers such as Binary (NP, NK, PK) fertilizers, e.g., monoammonium phosphate (MAP) and/or diammonium phosphate (DAP), NPK fertilizers which are three-component fertilizers providing nitrogen, phosphorus, and potassium; fertilizers which include one or more of the main micronutrients sources of iron, manganese, boron, molybdenum, zinc, and copper and the like; Compound fertilizers, e.g., which contain N, P, and K; Organic fertilizers such as peat, animal wastes, plant wastes from agriculture, and sewage sludge; and/or Other elements such as calcium, magnesium, and sulfur.

(5) According to some embodiments, use of polyhalite in granules is also beneficial to prevent the segregation of the polyhalite in a powder mix. Segregation often occurs due to differences in the size or density of the component of the mix. Normally, the smaller and/or denser particles tend to concentrate at the base of the container with the larger and/or less dense ones on the top. An ideal granulation will contain all the polyhalite of the mix in a correct proportion in each granule and segregation of granules will not occur.

(6) According to some demonstrative embodiments, the polyhalite granules are produced from fine material, e.g., powder, having a Particle Size Distribution (PSD) which is too small to be used by other conventional methods, e.g., bulk blending.

(7) According to some embodiments, the fine material (also referred to herein as fine dry polyhalite powder has a PSD of between 0.01 mm-1 mm, preferably between 0.03 mm-0.08 mm.

(8) According to some embodiments, the polyhalite granules of the present invention may have a spherical shape and accordingly blending with other nutrients (via for example bulk blending) may provide a more homogenous composition, the granules may also possess a low tendency of segregation, the granules may also exhibit low tendency to brake into small particles, the granules may also exhibit easy dissolution velocity, the granules may be easily coated and exhibit a low tendency to produce dust, thus diminishing environmental pollution (no dust liberation).

(9) The process can be changed according with the market needs and development, new line of products with different chemically and physically behaviors can be produced.

(10) According to some embodiments, the granules of the present invention may be coated with various coating materials, e.g., for anti-dusting and anticaking purposes, slow release and for the addition of microelements and/or macro-elements.

(11) According to some demonstrative embodiments, the granules of the present invention may also include one or more binders which include any suitable material or compound that may mechanically and/or chemically hold or draw other materials together to form a cohesive whole including, for example, organic or inorganic binders, such as, sodium silicate, potassium silicate, flyash, geopolymers, starch, bentonite, lignosulfonates, molasses, hydrated lime, bitumen, Portland cement, clay, acids (nitric, hydrochloric, phosphoric, sulphuric), cellulose gum, sucrose, water, water glass, cements, or combinations thereof.

(12) According to some embodiments, preferably, the binders are sodium silicate, potassium silicate and/or flyash.

(13) According to some demonstrative embodiments, there is provided a process for the production of polyhalite granules which includes:

(14) Filling a mixer with dry polyhalite and mixing for one minute Mixing a binder, for example, in a concentration of between 2.5-10% of the feed weight, preferably 5%, with water for example, in a concentration of between 3-9% of the feed weight, preferably 6%, in a separate vessel, to provide for a binder-water mix;

(15) Adding the binder-water mix to the mixer including the polyhalite and mixing for 5-15 minutes;

(16) Adding 0.5% water without stopping the mixer and mixing for at least two more minutes;

(17) Discharging the material from the mixer and introducing the material into fluid bed for one minute at 20 degrees Celsius;

(18) Drying the material at 150 degrees Celsius in fluid bed or drum dryer; and Screening the material to receive granules ranging in size between 1.4 mm to 4.75 mm

EXAMPLES

Example-1

(19) Mixer velocity: 350 rpm (7.3 M/sec linear velocity)

(20) Choper velocity: 1500 rpm

(21) Residence time 710 min,

(22) The yield is approximately 50-70%. The sequence of the process:

(23) 1Fill the mixer and mix one minute and stop.

(24) 2Mix the binder (5% of the feed weight) with the water (6% of the feed weight) in a small vessel (the mix).

(25) 3Add the mix (binder+water) to the mixer and start it and the chopper during 5 minutes.

(26) 4Add water to the mixer in an amount equal to 0.5% of the feed weight without stopping and after the water addition stop the chopper.

(27) 5Continue to mixing two additional minutes

(28) 6Discharge the material

(29) 7Introduce the material into fluid bed one minute at 20 degrees

(30) 8Dry the material at 150 degrees five minutes.

(31) 9Screen the material 1.4 mm to 4.75 mm

(32) Drum Trials

(33) Drum trials were conducted in drum that have 80 cm diameter. Rotation velocity 20 rpm. Water were added by spray by nozzle at 4 atm. 20 Kg of Polyhalite were mixed with weighted binders for 1 minute at 300 rpm. Water was added on the materials and rotated for additional time.

(34) The granules were dried at 150 degree for 20 minutes.

Example-2

(35) Binder quantity 3-5% fly ash. Added water 5-7.5%, granulation time 7-8 minutes.

(36) Granules strength before humidity 1.7-2.9 Kg/granule and after humidity at 77% for 24 hours 0.7-1.6 Kg/granule. the yields were 60-67%.

Example 3

(37) As example 2 with 4% of fly ash+1% of Calcium Hydroxide. Granulation time 7 minutes. Strength of granule before humidity 2.6-3.5 Kg/granule and 1.6-1.8 Kg/granule after humidity. the yields were between 52-74%.

Example 4

(38) As example 2. 2% of fly ash+1% of Calcium Hydroxide. Strength of granule before humidity 2.6 Kg/granule and 1.5 Kg/granule after humidity. The yield was 43%.

(39) Plow Share Trials

(40) The plow share has volume of 1000 Lit. Filling materials at 15%. The Velocity was 300 rpm and Chopper velocity was 1500 rpm.

(41) 10-15 Kg of Polyhalite mixed with weighted binders for 1 minute at 300 rpm. Water were added and continue to mixed foe additional time, then the granules were dried at 150 degree for 20 minutes.

Example 5

(42) 10 kg of Polyhalite, was mixed with 7% of fly ash+5% of Calcium Hydroxide for 1 minute Water was added and mixed 5 minutes. The product was dried. The Strength of the granules before humidity 4 Kg/granule. and 1.9-2.1 after humidity at 77% for 24 hours and 1.7 Kg/granule after 72 hours at 77% humidity.

Example 6

(43) 15 kg of Polyhalite, was mixed with 6.5% of fly ash+2.-4% of Calcium Hydroxide for 1 minute Water was added and mixed 5 minutes. The product was dried. The Strength of the granules before humidity 2.2-2.9 Kg/granule. and 0.4-0.8 after humidity at 77% for 24 hours and 1.7 Kg/granule after 72 hours at 77% humidity.

Example 7

(44) 150 Lit plow share. Filling with materials to 40%. velocity 300 rpm. Chopper velocity 1500 rpm. The Polyhalite mixed with weighted binders 4% fly ash and 1% Calcium hydroxide for 1 minute at 300 rpm. Water were added and mixed for 5 minutes. The product was dried for 10 minutes at 140 degrees and screened.

(45) The average PSD was 1.4-4.75 mm. The single strength of the granules were 3.6-4.3 Kg/granules before humidity and 1.4-1.5 KG/granule after humidity at 77 and 86% for 24 hours. Collective strength 77-78%. Caking 0.3 Kg, and the yield 62-73%. After 180 days the single strength of the granules was 2.8-2.9 Kg/granules collective 68-71%, and caking 2.7 Kg. While this invention has been described in terms of some specific examples, many modifications and variations are possible. It is therefore understood that within the scope of the appended claims, the invention may be realized otherwise than as specifically described.