DOSAGE FORM FOR USE IN TREATING OR PREVENTING OF A DISEASE

Abstract

A dosage form contains a biologically active ingredient for treating or preventing a disease in the animal or human body, where treatment or prevention requires release of 50% or more of the biologically active ingredient in the small intestine within the pH range from 3 to 5.5. The dosage form contains: a) a core, containing the biologically active ingredient; b) an intermediate coating layer (ICL) onto or above the core, containing an alkaline agent; and c) an enteric coating layer (ECL) onto or above the ICL, containing an enteric polymer. The relation of alkaline agent to enteric polymer is 5 to 95% when calculated by the formula:

[00001]$\frac{\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}\times 100}{\begin{array}{c}(\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}+\\ \mathrm{quantity}\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL}).\\ \mathrm{The}\mathrm{ICL}\mathrm{has}a\mathrm{thickness}\mathrm{of}\mathrm{about}22\mu m\mathrm{or}\mathrm{more}.\end{array}}$

Claims

1: A dosage form, comprising a biologically active ingredient for treating or preventing of a disease in an animal or a human body, wherein the treatment or the prevention of the disease requires release of 50% or more of the biologically active ingredient in a small intestine within a pH range from 3 up to 5.5, wherein the dosage form comprises: a core, comprising the biologically active ingredient, an intermediate coating layer (ICL) onto or above the core, the ICL comprising an alkaline agent, and an enteric coating layer (ECL) onto or above the intermediate coating layer, the ECL comprising an enteric polymer, wherein a relation of the alkaline agent to the enteric polymer is 5 to 95% when calculated by the formula: $\frac{\mathrm{quantity}\mathrm{of}\underset{\_}{\mathrm{the}}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}\times 100}{\begin{array}{c}(\mathrm{quantity}\mathrm{of}\underset{\_}{\mathrm{the}}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}+\\ \mathrm{quantity}\mathrm{of}\underset{\_}{\mathrm{the}}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL}).\end{array}}$ and wherein the intermediate coating layer has a thickness of about 22 μm or more.

2. The dosage form according to claim 1, wherein the biologically active ingredient is released in an amount of 10% or less at a pH of 1.2 for 120 min, and in an amount of 50% or more within a pH range from 3 to 5.5 for 45 min.

3: The dosage form according to claim claim 1, wherein the disease and a class of the biologically active ingredient for treating or preventing the disease, respectively, are selected from the group consisting of gastrointestinal lavage and laxatives; an inflammatory bowel disease and corticosteroids; hypercholesterolemia or hypertriglyceridemia and statins; CHF and glycosides; arrhythmia and stereoisomers of quinidine; cancer and plant alkaloids; ulcer or gastroesophageal reflux disease (GERD) and proton pump inhibitors; a bacterial infection and antibiotics; HIV and nucleosides; pancreatic insufficiency and lipases; major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and norepinephrine/dopamine-reuptake inhibitors (NDRI); pain or inflammation and NSAIDs; rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and NSAIDs; Parkinson's disease and dopamine precursors; malaria and antimalarials; hypertension and beta-blockers; diabetes and biguanides edema or chronic renal insufficiency and benzoic-sulfonamide-furans mild to severe heart failure or left ventricular dysfunction after myocardial infarction with ventricular ejection fraction ≤40% hypertension and beta adrenoceptor blockers, a systemic fungal infection and antifungals; hyperlipoproteinemia or hypertriglyceridemia and fibrate antilipemics; heart failure and mineralocorticoid hormones; cancer and anthracycline antibiotics; hypertension, angina, or cluster headache prophylaxis and calcium channel blockers; and atrial fibrillation and beta blockers.

4: The dosage form according to claim 1, wherein the disease and the biologically active ingredient for treating or preventing the disease, respectively, are selected from the group consisting of gastrointestinal lavage and bisacodyl; an inflammatory bowel disease and budesonide; hypercholesterolemia or hypertriglyceridemia and fluvastatin; CHF and digoxin; arrhythmia and quinidine, cancer and etoposide; ulcer or gastroesophageal reflux disease (GERD) and omeprazole, lansoprazole, pantoprazole, or rabeprazole; a bacterial infection and erythromycin, penicillin G, ampicillin, streptomycin, clarithromycin, or azithromycin; HIV and dideoxyinosine (ddI or didanosine), dideoxyadenosine (ddA), or dideoxycytosine (ddC); pancreatic insufficiency and a lipase; major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and bupropion; pain and inflammation, rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and acetyl salicylic acid, diclofenac, or indomethacin; Parkinson's disease and levodopa; malaria and hydroxychloroquine sulphate; hypertension and atenolol; diabetes and metformin hydrochloride; edema or chronic renal insufficiency and benzoic-sulfonamide-furans; mild to severe heart failure or left ventricular dysfunction after myocardial infarction with ventricular ejection fraction ≤40% hypertension and furosemide; a systemic fungal infection and ketoconazole; hyperlipoproteinemia or hypertriglyceridemia and fenofibrate; heart failure and aldosteron; cancer and doxorubicin; hypertension, angina, or cluster headache prophylaxis and verapamil; and atrial fibrillation and sotalol.

5: The dosage form according to claim 1, wherein the disease is atrial fibrillation and the biologically active ingredient for treating or preventing the disease is sotalol.

6. The dosage form according to claim 1, wherein the disease is ulcer or gastroesophageal reflux disease (GERD) and the biologically active ingredient is pantoprazole.

7: The dosage form according to claim 1, wherein the core comprises the biologically active ingredient distributed in a matrix structure or bound in a binder in a coating on an inner core.

8: The dosage form according to claim 1, wherein the alkaline agent is an alkali or an earth alkali metal salt.

9: The dosage form according to claim 1, wherein the alkaline agent is selected from the group consisting of calcium oxide, calcium carbonate, magnesium carbonate, magnesium oxide, sodium carbonate, sodium bicarbonate, sodium hydroxide, and a combination thereof.

10: The dosage form according to claim 1, wherein the alkaline agent is magnesium carbonate or magnesium oxide.

11: The dosage form according to claim 1, wherein the intermediate coating layer further comprises a plasticizer and/or a polymeric binder.

12: The dosage form according to claim 1, wherein the enteric polymer in the enteric coating layer is selected from the group consisting of an anionic (meth)acrylate copolymer, an anionic cellulose, an anionic polysaccharide, a polyvinyl acetate phthalate, and a mixture thereof.

13: The dosage form according to claim 12, wherein the anionic (meth)acrylate copolymer is selected from the group consisting of a copolymer comprising polymerized units of methacrylic acid and ethyl acrylate, a copolymer comprising polymerized units of methacrylic acid and methyl methacrylate, a copolymer comprising polymerized units of methacrylic acid, methyl acrylate, and methyl methacrylate, and a mixture thereof.

14: The dosage form according to claim 12, wherein the anionic cellulose is selected from the group consisting of carboxymethyl ethyl cellulose, a salt of carboxymethyl ethyl cellulose, cellulose acetate phthalate, cellulose acetate succinate, cellulose acetate trimellitate, hydroxypropyl methyl cellulose phthalate, hydroxypropyl methyl cellulose acetate succinate, and a mixture thereof.

15. The dosage form according to claim 1, wherein the relation of the alkaline agent to the enteric polymer is 7 to 80%

Description

DETAILED DESCRIPTION

Dosage Form

[0012] The invention is concerned with a dosage form comprising a biologically active ingredient for use in treating or preventing of a disease in the animal or human body, which treatment or prevention provides the release of 50% or more of the biologically active ingredient in the small intestine within the pH range pH from 3 up to 5.5, wherein the dosage form comprises:

a) a core, comprising the biologically active ingredient,
b) an intermediate coating layer (ICL) onto to or above the core, comprising an alkaline agent and
c) an enteric coating layer (ECL) onto or above the intermediate coating layer, comprising an enteric polymer,
wherein the relation of the alkaline agent to enteric polymer in the dosage form is 5 to 95% when calculated by the formula:

[00002]$\frac{\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}\times 100}{\begin{array}{c}(\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}+\\ \mathrm{quantity}\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL})\end{array}}$

and wherein the intermediate coating layer (ICL) has a thickness of about 22 μm or more.

[0013] The dosage form may usually have the form of the core, however additionally coated with the intermediate coating layer and the enteric coating layer as disclosed, e.g. the form of a (coated) pellet (core). Furthermore, several single dosage forms may be contained in multiple as parts of a multi-unit dosage form, e.g. contained in a capsule or in a tablet in which a multiple of inventive dosage form are contained, e.g. in the form of (coated) pellet (cores).

[0014] The dosage form may have the form of, for instance, a tablet, a minitablet, a pellet, a pill, a granule, a sachet or a capsule. The dosage form may as well be contained, preferably in multi-units, for instance, in a tablet, in a sachet or in a capsule.

Release of the Biologically Active Ingredient

[0015] Preferably the release of the biologically active ingredient is 10% or less at pH 1.2 for 120 min and 50% or more (50-100%), preferably 60 to 100%, at a pH from 3 to 5.5, preferably at a pH from 3.2 to 5.0, for 45 min. The pH 1.2 test medium may be 0.1 N HCl according to USP, for instance USP 42, pH 3 to 5.5 media may be buffered media according to USP, for instance USP 42 (2019).

Core

[0016] The core of the dosage form comprises a biologically active ingredient.

[0017] The core of the dosage form may comprise the biologically active ingredient distributed in a matrix structure or bound in a binder in a coating on an inner core structure or enclosed in a capsule.

[0018] The core may be prepared by methods such as granulation, extrusion, spheronization or hot melt extrusion.

[0019] The core may be a pellet, a pill, a granule, a tablet or a capsule. The core may be an active ingredient-containing tablet, a pellet-containing compressed tablet, a mini-tablet or a capsule, which may be filled with active ingredient-containing pellets or granules, with a drug solution or dispersion, with mini-tablets or powder or combinations thereof.

[0020] The core may comprise for instance an uncoated pellet, a neutral carrier pellet, for instance a sugar sphere or non-pareilles, on top of which the biologically active ingredient is bound in a binder, such as lactose, polyvinyl pyrrolidone or a neutral cellulose-derivates such as HPC or HPMC. The binder-coating layer with the biologically active ingredient is considered herein as part of the core.

[0021] The binder-coating layer of the core has, in contrast to the intermediate coating layer and the enteric coating layer, essentially no influence on the controlled release of the biologically active ingredient. The core may as well comprise an uncoated pellet consisting of a crystallized biologically active ingredient.

[0022] The core may comprise 0.1 to 100, 1 to 100, 2 to 90, 5 to 85, 10 to 70, 15 to 50% by weight of the biologically active ingredient. The core may comprise 0 to 99, 10 to 98, 15 to 95, 30 to 90 or 50 to 85% by weight of pharmaceutical or nutraceutical acceptable excipients. The biologically active ingredient and the pharmaceutical or nutraceutical acceptable excipients may add up to 100%.

Disease(s) and Biologically Active Ingredient(s)

[0023] The biologically active ingredient(s) may comprise biologically active pharmaceutical ingredients and biologically active nutraceutical ingredients.

[0024] The disease(s) and the class of biologically active ingredient(s) associated for treating or preventing the disease(s) may be selected from gastrointestinal lavage and a laxatives, inflammatory bowel diseases and corticosteroids, hypercholesterolemia or hypertriglyceridemia and statins, CHF and glycosides, arrhythmia and stereoisomers of quinidine, cancer and plant alkaloids, ulcer or gastroesophageal reflux disease (GERD) and proton pump inhibitors, bacterial infections and antibiotics, HIV and nucleosides, pancreatic insufficiency and lipases, major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and norepinephrine/dopamine-reuptake inhibitors (NDRI), pain and inflammation and NSAIDs, rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and NSAIDs, parkinson's disease and dopamine precursors, malaria and antimalarials, hypertension and beta-blockers, diabetes and biguanides, edema or chronic renal insufficiency and benzoic-sulfonamide-furans, mild to severe heart failure, left ventricular dysfunction after myocardial infarction with ventricular ejection fraction 540% hypertension and beta adrenoceptor blockers, systemic fungal infections and antifungals, hyperlipoproteinemia or hypertriglyceridemia and fibrate antilipemics, heart failure and mineralocorticoid hormones, cancer and Anthracycline antibiotics, hypertension, angina or cluster headache prophylaxis and calcium channel blockers, and atrial fibrillation and beta blockers.

[0025] The disease(s) and the biologically active ingredient(s) associated for treating or preventing the disease(s) may be selected from gastrointestinal lavage and bisacodyl, inflammatory bowel diseases and budesonide, hypercholesterolemia or hypertriglyceridemia and fluvastatin, CHF and digoxin, arrhythmia and quinidine, cancer and etoposide, ulcer and gastroesophageal reflux disease (GERD) and omeprazole, lansoprazole, pantoprazole or rabeprazole, bacterial infections and erythromycin, penicillin G, ampicillin, streptomycin, clarithromycin or azithromycin, HIV and dideoxyinosine (ddl or didanosine), dideoxyadenosine (ddA) or dideoxycytosine (ddC), pancreatic insufficiency and lipases, major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and bupropion, pain and inflammation, rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and acetyl salicylic acid (Aspirin®), diclofenac or indomethacin, parkinson's disease and levodopa, malaria and hydroxychloroquine sulphate, hypertension and atenolol, diabetes and metformin hydrochloride, edema or chronic renal insufficiency and benzoic-sulfonamide-furans, mild to severe heart failure, left ventricular dysfunction after myocardial infarction with ventricular ejection fraction 540% hypertension and furosemide, systemic fungal infections and ketoconazole, hyperlipoproteinemia or hypertriglyceridemia and fenofibrate, heart failure and aldosteron, cancer and doxorubicin, hypertension, angina or cluster headache prophylaxis and verapamil, and atrial fibrillation and sotalol.

[0026] Preferably the disease may be atrial fibrillation and the biologically active ingredient associated for treating or preventing the is sotalol.

[0027] Preferably the disease may be ulcer and gastroesophageal reflux disease (GERD) and the biologically active ingredient associated for treating or preventing the is pantoprazole.

[0028] Further biologically active ingredients according to the present application may be biotechnology derived products or microbiologically derived products and may be selected from, for instance, enzymes, hormones, liquid or solid natural extracts, oligonucleotides, DNA, RNA, mRNA, siRNA, Protacs (proteolysis targeting chimera), peptide hormones, therapeutic bacteria, prebiotics, probiotics, peptides, proteins, urology drugs, omega-3-fatty acids, anthocyanidines e.g. from bilberries, blueberries or black currants as antioxidants, vitamins and vaccines.

Intermediate Coating Layer

[0029] The intermediate coating layer (ICL) is onto to or above the inner core and is comprising an alkaline agent. The intermediate coating layer may comprise 5 to 75, preferably 10 to 50% by weight of the alkaline agent. The intermediate layer may comprise 25 to 95, preferably 90 to 50% by weight of further pharmaceutically or nutraceutically acceptable excipients, such as, for example, a polymeric binder, for instance a neutral water-soluble cellulose such as hydroxypropylmethylcellulose (HPMC) or hydroxypropylcellulose (HPC) or polyvinyl pyrrolidone (PVP), or a plasticizer or a anti tacking agent or combination thereof. The polymeric binder may also be a neutral or an anionic (meth)acrylate copolymer, the latter may optionally be partially or completely neutralized. Preferably the intermediate layer is onto the core with no other coating layers in between. The intermediate coating layer (ICL) is present in an amount of 5 to 100, preferably 7.5 to 50% by weight calculated on the weight of the core. The intermediate coating layer (ICL) has a thickness of about 22 μm or more, especially of 22 to 250 μm, preferably of 25 to 100 μm (mean average).

Measurement of the Intermediate Coating Layer (ICL) Thickness

[0030] The thickness of the intermediate coating layer (ICL) is determined via Scanning Electron Microscopy (SEM) investigation. The thickness is expressed as the mean average value of the measurement of a random sample in μm. The Scanning Electron Microscopy (SEM) investigation is based on the measurement of the visual intermediate coating layer (ICL) thickness of a random sample of units ((minimum) sample size) selected from a batch production of the dosage form at a statistical confidence level of 95%, a Z-value of 1.96, an error margin e of 0.1 and a standard of deviation of 0.5. The intermediate coating layer (ICL) becomes SEM-visible in its cross-section view, when the dosage form is separated (broken or cut) into two almost equal parts and its thickness can be measured in the SEM-view. When the production batch size N (production lot) of the dosage form exceeds 1.000 units, the measurement of a random sample of 100 units is usually sufficient. The measurement of layer thicknesses of coated dosage forms via Scanning Electron Microscopy (SEM) and the statistical methods applied are well known to skilled person in the field of pharmacy.

Sample Number Calculation Equation:

[0031] [00003]$\mathrm{sample}\mathrm{size}=\frac{\frac{z^2\times p\left(1-p\right)}{e^2}}{1+\left(\frac{z^z\times p\left(1-p\right)}{e^{2}N}\right)}$

N=Batch Size

[0032] e=Error Margin
z=Z-Value representing the confidence level
p=Standard of deviation

TABLE-US-00001 Confidence level Z-value 80% 1.28 85% 1.44 90% 1.65 95% 1.96 99% 2.58

Calculation for Example C3

[0033] N=457,200 [units]
e=0.1
z=1.96
p=0.5

[00004]$\mathrm{sample}\mathrm{size}=\frac{\frac{1.96^2\times 0,5\left(1-0.5\right)}{0.1^2}}{1+\left(\frac{1.96^2\times 0.5\left(1-0.5\right)}{{0.1}^{2}457,200}\right)}\mathrm{sample}\mathrm{size}=96.06$

Analytical Method

SEM Equipment Set-Up

Make: Thermo Fisher Scientific

Model: FEI Quanta 200

[0034] Pressure: Low Vacuum mode at 65 pascals

Magnification: Various

[0035] Voltage (HV) was kept at 20 KV
Detector used was Large Field Detector (LFD)

SEM Method Description:

[0036] Samples are to be randomly taken from the batch of coated dose units i.e. pellets or tablets. The taken samples were broken typically into two equally sized dose unit halves. The broken pieces were fixed in an upright position on the sample mounting disc. The samples are to be investigated at an adequate magnification which corresponds to the dose unit dimensions. The layer thickness will be determined in a 900 angle to the substrate. The single values are noted, and the mean average and standard deviation are calculated. The standard deviation in a representative batch production should not exceed +/−20% of the mean average value.

Alkaline Agent

[0037] The alkaline agent may be an alkali or an earth alkali metal salt. The alkaline agent may be, for instance, selected from calcium oxide, calcium carbonate, magnesium carbonate, magnesium oxide, sodium carbonate, sodium bicarbonate and sodium hydroxide or any mixtures thereof. Preferred alkaline agents are magnesium oxide or magnesium carbonate. The relation of the alkaline agent in the intermediate coating layer (ICL) to the enteric polymer in the enteric coating layer (ECL) is 5 to 95, preferably 7 to 80% when calculated by the formula:

[00005]$\frac{\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}\times 100}{\begin{array}{c}(\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}+\\ \mathrm{quantity}\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL})\end{array}}$

Plasticizers

[0038] Plasticizers may be defined in that they achieve through physical interaction with a polymer a reduction in the glass transition temperature and promote film formation, depending on the added amount. Suitable substances usually have a molecular weight of between 100 and 20,000 and comprise one or more hydrophilic groups in the molecule, e.g. hydroxy ester or amino groups.

[0039] The intermediate coating layer or the enteric coating layer may comprise a plasticizer, which may be selected from the groups of alkyl citrates, glycerol esters, alkyl phthalates, alkyl sebacates, sucrose esters, sorbitan esters and polyethylene glycols. The intermediate coating layer may comprise a plasticizer, preferably about 2 to 50, preferably 5 to 25% by weight, which may be selected from triethyl citrate (TEC), acetyl triethyl citrate (ATEC), diethyl sebacate and dibutyl sebacate (DBS), glycerol, propylene glycol, polyethylene glycols 200 to 12,000 and castor oil. A preferred plasticizer for the intermediate coating layer may be glycerine or triethyl citrate. A preferred plasticizer for the enteric coating layer may be triethyl citrate.

Enteric Coating Layer

[0040] The enteric coating layer is onto to or above the intermediate coating layer is comprising an enteric polymer and optionally pharmaceutically or nutraceutically acceptable excipients. The enteric coating layer may comprise 10 to 100, preferably 20 to 80% by weight of the enteric polymer. The enteric coating layer may comprise 90 to 0, preferably 80 to 20% by weight of pharmaceutically or nutraceutically acceptable excipients, such as, for example, a plasticizer. Preferably the enteric coating layer is onto the intermediate coating layer with no other coating layers in between. The enteric coating layer may be present in an amount of 5 to 50% by weight calculated on the weight of the core and the intermediate layer.

Enteric Polymer

[0041] The enteric polymer in the further coating layer onto or above the intermediate coating layer may be selected from anionic (meth)acrylate copolymers, anionic celluloses, anionic polysaccharides and polyvinyl acetate phthalates or any mixtures thereof. The enteric coating layer may be present in an amount of 10 to 50% by weight calculated on the weight of the core and the intermediate layer.

Anionic (Meth)Acrylate Copolymer(s)

[0042] The enteric coating layer may comprise a (meth)acrylate copolymer selected from copolymers comprising polymerized units of methacrylic acid and ethyl acrylate, of methacrylic acid and methyl methacrylate, of ethyl acrylate and methyl methacrylate or of methacrylic acid, methyl acrylate and methyl methacrylate, from a mixture of a copolymer comprising polymerized units of methacrylic acid and ethyl acrylate with a copolymer comprising polymerized units of methyl methacrylate and ethyl acrylate and a mixture of a copolymer comprising polymerized units of methacrylic acid, methyl acrylate and methyl methacrylate with a copolymer comprising polymerized units of methyl methacrylate and ethyl acrylate or any mixtures thereof.

[0043] The coating layer may comprise a (meth)acrylate copolymer comprising polymerized units of 40 to 60% by weight of methacrylic acid and 60 to 40% by weight of ethyl acrylate (type EUDRAGIT® L 100-55). A suitable second polymer is EUDRAGIT® L 100-55 (Evonik Nutrition & Care GmbH, Darmstadt, Germany), which is a copolymer comprising polymerized units of 50% by weight of methacrylic acid and 50% by weight of ethyl acrylate. EUDRAGIT® L 30 D-55 is a 30% by weight aqueous dispersion of EUDRAGIT® L 100-55. The glass transition temperature T.sub.gm of EUDRAGIT® L 100-55 is about 110° C.

[0044] The coating layer may comprise a (meth)acrylate copolymer comprising polymerized units of 5 to 15% by weight methacrylic acid, 60 to 70% by weight of methyl acrylate and 20 to 30% by weight methyl methacrylate (type EUDRAGIT® FS). A suitable copolymer is EUDRAGIT® FS which is a copolymer polymerized from 25% by weight of methyl methacrylate, 65% by weight of methyl acrylate and 10% by weight of methacrylic acid. EUDRAGIT® FS 30 D is a dispersion comprising 30% by weight EUDRAGIT® FS. The glass transition temperature T.sub.gm of EUDRAGIT® FS is about 45° C.

[0045] The coating layer may comprise a (meth)acrylate copolymer comprising polymerized units of 40 to 60% by weight of methacrylic acid and 60 to 40% by weight of methyl methacrylate (type EUDRAGIT® L 100). EUDRAGIT® L 100 is a copolymer polymerized from 50% by weight of methyl methacrylate and 50% by weight of methacrylic acid. The glass transition temperature T.sub.gm of EUDRAGIT® L 100 is about or somewhat above 150° C.

[0046] The coating layer may comprise a (meth)acrylate copolymer comprising polymerized units of 20 to 40% by weight of methacrylic acid and 60 to 80% by weight of methyl methacrylate (type EUDRAGIT® S 100). EUDRAGIT® S 100 is a copolymer polymerized from 70% by weight methyl methacrylate and 30% by weight methacrylic acid. The glass transition temperature T.sub.gm of EUDRAGIT® S 100 is about or somewhat above 160° C.

[0047] The coating layer may also comprise an anionic (meth)acrylate copolymer(s) in the form of a core-shell polymer from two (meth)acrylate copolymer(s). The coating layer may comprise a (meth)acrylate copolymer which is a core-shell polymer, comprising 50 to 90, preferably 70 to 80% by weight of a core, comprising polymerized units of 60 to 80, preferably 65 to 75% by weight of ethyl acrylate and 40 to 20, preferably 35 to 25% by weight of methyl methacrylate, and 50 to 10, preferably 30 to 20% by weight of a shell, comprising polymerized units of 40 to 60, preferably 45 to 55% by weight of ethyl acrylate and 60 to 40, preferably 55 to 45% by weight of methacrylic acid.

[0048] A suitable core-shell polymer is EUDRAGIT® FL 30 D-55 (Evonik Nutrition & Care GmbH, Darmstadt, Germany), which is a commercially available 30% by weight aqueous dispersion of a copolymer from a two-stage emulsion polymerization process, with a core of about 75% by weight, comprising polymerized units of about 70% by weight of ethyl acrylate and 30% by weight of methyl methacrylate, and a shell of about 25% by weight, comprising polymerized units of 50% by weight ethyl acrylate and 50% by weight methacrylic acid. The glass transition temperature T.sub.gm of the polymer of EUDRAGIT® FL 30D-55 is about 8° C.

Anionic Celluloses

[0049] Anionic celluloses (chemically modified celluloses) may be selected from carboxymethyl ethyl cellulose and its salts, cellulose acetate phthalate, cellulose acetate succinate, cellulose acetate trimellitate, hydroxypropyl methyl cellulose phthalate and hydroxypropyl methyl cellulose acetate succinate or any mixtures thereof.

Anionic Polysaccharides

[0050] Anionic polysaccharides (not based on cellulose) with enteric properties may be selected from polymers such as shellac, chitosan, alginic acid and salts of alginic acid, e.g. sodium, potassium or ammonium alginate.

Pharmaceutically or Nutraceutically Acceptable Excipients

[0051] The core, in the intermediate layer or in the enteric coating layer may optionally comprise pharmaceutically or nutraceutically acceptable excipients. Such pharmaceutically or nutraceutically acceptable excipients may be selected from the group of antioxidants, brighteners, binding agents, such as lactose, polyvinyl pyrrolidone or neutral celluloses, flavoring agents, flow aids, glidants, penetration-promoting agents, pigments, plasticizers, further polymers, pore-forming agents and stabilizers or any combinations thereof.

Items

[0052] The invention may be characterized by the following items: [0053] 1. Dosage form, comprising a biologically active ingredient, for use in treating or preventing of a disease in the animal or human body, which treatment or prevention requires the release of 50% or more of the biologically active ingredient in the small intestine within the pH range from 3 up to 5.5, wherein the dosage form comprises: [0054] a) a core, comprising the biologically active ingredient, [0055] b) an intermediate coating layer (ICL) onto or above the core, comprising an alkaline agent and [0056] c) an enteric coating layer (ECL) onto or above the intermediate coating layer, comprising an enteric polymer, [0057] wherein the relation of the alkaline agent to the enteric polymer is 5 to 95% when calculated by the formula:

[00006]$\frac{\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}}{\begin{array}{c}100\\ \begin{array}{c}(\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{lCL}+\\ \mathrm{quantity}\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL})\end{array}\end{array}}\times$ [0058] and wherein the intermediate coating layer (ICL) has a thickness of about 22 μm or more. [0059] 2. Dosage form according to item 1, wherein the release of the biologically active ingredient is 10% or less at pH 1.2 for 120 min and 50% or more within the pH range from 3 to 5.5 for 45 min. [0060] 3. Dosage form, according to item 1 or 2, wherein the disease(s) and the class of biologically active ingredients for treating or preventing the disease(s) are selected from gastrointestinal lavage and laxatives, inflammatory bowel diseases and corticosteroids, hypercholesterolemia or hypertriglyceridemia and statins, CHF and glycosides, arrhythmia and stereoisomers of quinidine, cancer and plant alkaloids, ulcer or gastroesophageal reflux disease (GERD) and proton pump inhibitors, bacterial infections and antibiotics, HIV and nucleosides, pancreatic insufficiency and lipases, major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and norepinephrine/dopamine-reuptake inhibitors (NDRI), pain or inflammation and NSAIDs, rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and NSAIDs, Parkinson's disease and dopamine precursors, malaria and antimalarials, hypertension and beta-blockers, diabetes and biguanides, edema or chronic renal insufficiency and benzoic-sulfonamide-furans, mild to severe heart failure, left ventricular dysfunction after myocardial infarction with ventricular ejection fraction 540% hypertension and beta adrenoceptor blockers, systemic fungal infections and antifungals, hyperlipoproteinemia or hypertriglyceridemia and fibrate antilipemics, heart failure and mineralocorticoid hormones, cancer and anthracycline antibiotics, hypertension, angina or cluster headache prophylaxis and calcium channel blockers, and atrial fibrillation and beta blockers. [0061] 4. Dosage form, according to any of items 1 to 3, wherein the disease(s) and the biologically active ingredient associated for treating or preventing the disease(s) are selected from gastrointestinal lavage and bisacodyl, inflammatory bowel diseases and budesonide, hypercholesterolemia or hypertriglyceridemia and fluvastatin, CHF and digoxin, arrhythmia and quinidine, cancer and etoposide, ulcer or gastroesophageal reflux disease (GERD) and omeprazole, lansoprazole, pantoprazole or rabeprazole, bacterial infections and erythromycin, penicillin G, ampicillin, streptomycin, clarithromycin or azithromycin, HIV and dideoxyinosine (ddl or didanosine), dideoxyadenosine (ddA) or dideoxycytosine (ddC), pancreatic insufficiency and lipases, major depressive disorder (MDD) or seasonal affective disorder (SAD) or an aid for smoking cessation and bupropion, pain and inflammation, rheumatoid arthritis, osteoarthritis or ankylosing spondylitis and acetyl salicylic acid (Aspirin®), diclofenac or indomethacin, parkinson's disease and levodopa, malaria and hydroxychloroquine sulphate, hypertension and atenolol, diabetes and metformin hydrochloride, edema or chronic renal insufficiency and benzoic-sulfonamide-furans, mild to severe heart failure, left ventricular dysfunction after myocardial infarction with ventricular ejection fraction 540% hypertension and furosemide, systemic fungal infections and ketoconazole, hyperlipoproteinemia or hypertriglyceridemia and fenofibrate, heart failure and aldosteron, cancer and doxorubicin, hypertension, angina or cluster headache prophylaxis and verapamil, and atrial fibrillation and sotalol. [0062] 5. Dosage form according to any of items 1 to 4, wherein the disease is atrial fibrillation and the biologically active ingredient for treating or preventing the disease is sotalol. [0063] 6. Dosage form according to any of items 1 to 4, wherein the diseases is ulcer or gastroesophageal reflux disease (GERD) and the biologically active ingredient is pantoprazole. [0064] 7. Dosage form, according to one or more of items 1 to 6, wherein the core comprises the biologically active ingredient distributed in a matrix structure or bound in a binder in a coating on an inner core. [0065] 8. Dosage form, to one or more of items 1 to 7, wherein the alkaline agent is an alkali or an earth alkali metal salt. [0066] 9. Dosage form, according to one or more of items 1 to 8, wherein the alkaline agent is selected from calcium oxide, calcium carbonate, magnesium carbonate, magnesium oxide, sodium carbonate, sodium bicarbonate and sodium hydroxide or any combinations thereof. [0067] 10. Dosage form, according to one or more of items 1 to 9, wherein the alkaline agent is magnesium carbonate or magnesium oxide. [0068] 11. Dosage form, according to one or more of items 1 to 10, wherein the intermediate coating layer further comprises a plasticizer and/or a polymeric binder. [0069] 12. Dosage form, according to one or more of items 1 to 10, wherein the enteric polymer in the enteric coating layer is selected from anionic (meth)acrylate copolymers, anionic celluloses, anionic polysaccharides and polyvinyl acetate phthalates or any mixtures thereof. [0070] 13. Dosage form, according to one or more of items 1 to 12, wherein the anionic (meth)acrylate copolymers are selected from copolymers comprising polymerized units of methacrylic acid and ethyl acrylate, of methacrylic acid and methyl methacrylate and of methacrylic acid, methyl acrylate and methyl methacrylate or any mixtures thereof. [0071] 14. Dosage form, according to one or more of items 1 to 13, wherein the anionic celluloses are selected from carboxymethyl ethyl cellulose and its salts, cellulose acetate phthalate, cellulose acetate succinate, cellulose acetate trimellitate, hydroxypropyl methyl cellulose phthalate and hydroxypropyl methyl cellulose acetate succinate or any mixtures thereof. [0072] 15. Dosage form, according to one or more of items 1 to 14, wherein the relation of the alkaline agent to the enteric polymer is 7 to 80%. [0073] 16. Dosage form according to one or more of the preceding items, wherein the release of the biologically active ingredient is 10% or less at pH 1.2 for 120 min and 60 to 100% within the pH from 3.2 to 5.0 for 45 min. [0074] 17. Dosage form according to one or more of the preceding items, wherein core comprises 0.1 to 100, 1 to 100, 2 to 90, 5 to 85, 10 to 70 or 15 to 50% by weight of the biologically active ingredient. [0075] 18. Dosage form according to one or more of the preceding items, wherein the core comprises 0 to 99.9, 0 to 99, 10 to 98, 15 to 95, 30 to 90 or 50 to 85% by weight of pharmaceutical or nutraceutical acceptable excipients. [0076] 19. Dosage form according to one or more of the preceding items, wherein the biologically active ingredient is selected from enzymes, hormones, liquid or solid natural extracts, oligonucleotides, DNA, RNA, mRNA, siRNA, Protacs (proteolysis targeting chimera), peptide hormones, therapeutic bacteria, prebiotics, probiotics, peptides, proteins, urology drugs, omega-3-fatty acids and their salts, anthocyanines e.g. from bilberries, blueberries or black currants, vitamins and vaccines. [0077] 20. Dosage form according to one or more of the preceding items, wherein the intermediate coating layer (ICL) is present in an amount of 5 to 100% by weight calculated on the weight of the core. [0078] 21. Dosage form according to one or more of the preceding items, wherein the intermediate coating layer (ICL) is present in an amount of 7.5 to 50% by weight calculated on the weight of the core. [0079] 22. Dosage form according to one or more of the preceding items, wherein the intermediate coating layer (ICL) has a thickness of 22 to 250 μm, preferably of 25 to 100 μm (mean average). [0080] 23. Dosage form according to one or more of the preceding items, wherein the intermediate coating layer (ICL) comprises 5 to 75% by weight of the alkaline agent. [0081] 24. Dosage form according to one or more of the preceding items, wherein the intermediate coating layer (ICL) comprises 10 to 50% by weight of the alkaline agent. [0082] 25. Dosage form according to one or more of the preceding items, wherein the enteric coating layer (ECL) is present in an amount of 10 to 50% by weight calculated on the weight of the core and the intermediate layer. [0083] 26. Dosage form according to one or more of the preceding items, wherein the enteric coating layer (ECL) comprises 10 to 100% by weight of the enteric polymer. [0084] 27. Dosage form according to one or more of the preceding items, wherein the enteric coating layer (ECL) comprises 20 to 80% by weight of the enteric polymer. [0085] 28. Dosage form according to one or more of the preceding items, wherein the enteric polymer comprises a (meth)acrylate copolymer comprising polymerized units of 40 to 60% by weight of methacrylic acid and 60 to 40% by weight of ethyl acrylate.

Examples

[0086] A. Core Preparation:

[0087] 1. Pantoprazole Matrix (Core) Pellets:

[0088] 1.1 Composition for Pantoprazole Matrix Pellets (Using Extrusion Method):

TABLE-US-00002 TABLE 1 Composition for Pantoprazole Matrix Pellets (Using extrusion method): Experiment ID I1 Composition Composition Ingredients (% w/w) (gm) # Pantoprazole Sodium 20.0 60.0 Mannitol 58.88 176.64 MCC PH-101 20.0 60.0 HPC LM 1.12 3.36 Water q.s.* q.s.* Total 100 300 Water uptake (% w/w) 25 25 *q.s. to get extrudable dough mass; Note: # Composition of Experiment I1 is also expressed in grams for demonstrating Percentage alkali on alkali and enteric polymer calculation. Quantities of ingredients in subsequent experiments can be calculated likewise. Abbreviations: HPC: Hydroxy propyl cellulose; MCC PH-101: Microcrystalline Cellulose PH101

[0089] 1.2 Process for Pantoprazole Matrix Pellets Preparation: [0090] I. All the ingredients were weighed in required quantity. [0091] II. Co-sifted mannitol, Pantoprazole Sodium, MCC PH-101, and HPC LM through 40#sieve. [0092] III. Dry mixed step II material for 10 minutes in planetary mixer. [0093] IV. Granulated dry mix of step III with purified water. [0094] V. Granulated wet mass was subjected for extrusion using 1.0 mm screen followed by Spheronization using 2.0 mm Chequered plate. [0095] VI. Wet pellets from Spheronizer were dried at 50° C. until LOD (Loss on drying) reached below 2% w/w. [0096] VII. Dried pellets were sized through 18# mesh followed by 20# mesh and fractions of pellets passed through 18# mesh and retained on 20# mesh were taken for coating purpose.

TABLE-US-00003 TABLE 2 General Process Parameters for Pantoprazole Sodium Matrix Pellets preparation: General Process Parameters Experiment I1 STEP 1: Preparation of Dough mass Equipment Planetary mixer Process data Dry mixing Time 10 minutes  Speed Minimum Binder addition Time 2 minutes Speed 1 Wet mixing Time 3 minutes Speed 2 STEP 2: Extrusion Equipment Extruder Equipment setup Extruder type Dome Extruder screw Single Screen diameter 1.0 mm Process data Screw speed 30 RPM Extrusion time 15 minutes STEP 2: Spheronization Equipment Spheronizer Equipment setup Spheronizer plate type Chequered plate Process parameter setup Spheronizer speed 1500 RPM Process data Spheronizer load 375.0 gm Spheronization time 1 Min

[0097] 2. Benazepril (Core) Tablets:

[0098] 2.1 Composition for Benazepril Tablets:

TABLE-US-00004 TABLE 3 Composition of Benazepril tablets: Experiment ID I2 & I3 Ingredients Composition (% w/w) Intra-granular materials Benazepril Hydrochloride 20 Microcrystalline Cellulose PH101 30 Lactose monohydrate 10 HPMC 6 cps 2.4 Water (q.s. to % w/w solids) q.s.* Extra-granular materials Microcrystalline Cellulose PH102 29.9 Aerosil ® 200 Pharma 1.1 Croscarmellose sodium 5.5 Magnesium stearate 1.1 Total 100 Solid content of binder solution 5.5% w/w  Water uptake 33% w/w *q.s. to acheive granulation end point Abbreviations: HPMC: Hydroxy propyl methyl cellulose

[0099] 2.2 Process for Benazepril Tablets: [0100] I. Weigh all the ingredients as specified in the formula. [0101] II. Benazepril hydrochloride and lactose monohydrate were mixed uniformly and sifted through #40 mesh. [0102] III. Microcrystalline cellulose PH101 and half quantity of HPMC 6cps was sifted through #40 mesh and added to the step II. [0103] IV. The powder blend of step III was added in to rapid mixture granulator and mixed for 5 min at slow speed. [0104] V. In a separate beaker, remaining half quantity of HPMC 6cps was added slowly in purified water under continuous stirring to get a clear binder solution. [0105] VI. Step V binder solution was then used to granulate dry mix of step IV. [0106] VII. After granulation, sift the wet material through 10# (2.0 mm) sieve. [0107] VIII. Granules were dried in tray dryer at 50° C. until LOD was achieved below 5% w/w. [0108] IX. Dried granules were passed through 30# (595 μm) sieve. [0109] X. Weighed all extra-granular materials accurately. [0110] XI. MCC PH 102, Croscarmellose sodium & Aerosil 200 were mixed in polybag and sifted through #40 mesh. [0111] XII. Benazepril granules of step IX & sifted material of step XI were mixed in a double cone blender for 15 min at 15 RPM. [0112] XIII. Sifted magnesium stearate (60#) was added to step XII for lubrication of the blend for 3 min at 15 RPM in double cone blender. [0113] XIV. Lubricated blend was used for tablet compression.

TABLE-US-00005 TABLE 4 General Process Parameters of for Benazepril Tablet preparation: General Process Parameters Experiment I2 & I3 Granulation Equipment Rapid mixer granulator Process data Dry mixing Time 10 minutes Impeller Speed Slow Chopper Speed Binder addition Time 3 minutes Impeller Speed Slow Chopper Speed Wet mixing Time 45 Seconds Impeller Speed Slow Chopper Speed Slow Compression Parle Elisabeth Tablet compression machine Equipment (ElizaPress-200) Equipment setup Shape of punch Circular, standard concave Size of punch 8.0 mm Upper punch Plain Lower punch Plain Process data Weight of tablet mg 200.0 Hardness N 70-90 Thickness Mm 3.90-4.10 Friability % 0. Disintegration time Minute 4-6

3. Sotalol (Core) Tablets:

[0114] 3.1 Composition of Sotalol Tablets:

TABLE-US-00006 TABLE 5 Composition of Sotalol tablets: Experiment ID I4 Ingredients Composition (% w/w) Intra-granular materials Sotalol Hydrochloride 40 Microcrystalline cellulose PH101 30 Ac-Di-Sol ® (Croscarmellose sodium) 2.5 HPMC 3 cps 1.5 Water (q.s. to % w/w solids) q.s.* Extra-granular materials Microcrystalline cellulose PH102 22.0 Aerosil ® 200 Pharma 1.0 Croscarmellose sodium 2.5 Magnesium stearate 0.5 Total 100 Solid content of binder solution 6.5% w/w  Water uptake 30% w/w *q.s. to achieve granulation end point

[0115] 3.2 Process for Sotalol Tablets: [0116] I. Weigh all the ingredients as specified in the formula. [0117] II. Sotalol hydrochloride, microcrystalline cellulose and Ac-Di-Sol© were mixed uniformly and sifted through #30 mesh. [0118] III. The powder blend of step II was added in to rapid mixture granulator and mixed for 3 min at slow speed. [0119] IV. In a separate beaker, HPMC 3 cps was added slowly in purified water under continuous stirring to get a clear solution. [0120] V. Step IV solution was then used to granulate dry mix of step III [0121] VI. Granules were dried in tray dryer at 60° C. for 2 hr then passed through 30# sieve and then further dried for 4 hr at 60° C. till LOD was achieved below 5% w/w. [0122] VII. Dried granules were passed through 30# (595 μm) sieve. [0123] VIII. Weighed all extra-granular materials accurately. [0124] IX. Microcrystalline cellulose PH101, Ac-Di-Sol® and Aerosil 200 were mixed in polybag and then sifted through #30 mesh. [0125] X. Sotalol granules of step VII & sifted material of step IX were mixed in a double cone blender for 15 min at 15 RPM. [0126] XI. Magnesium stearate (60# passed) was added to blend of step X and lubricated for 5 min at 15 RPM in double cone blender. [0127] XII. Lubricated blend was used for tablet compression.

TABLE-US-00007 TABLE 6 General Process Parameters for Sotalol Tablet preparation: General Process Parameters Experiment I4 Granulation Equipment Rapid mixer granulator Process data Dry mixing Time 15 minutes Impeller Speed Slow Chopper Speed Binder addition Time 5 minutes Impeller Speed Slow Chopper Speed Wet mixing Time 1 minute Impeller Speed Slow Chopper Speed Slow Compression Parle Elisabeth Tablet compression machine Equipment (ElizaPress-200) Equipment setup Shape of punch Circular, standard concave Size of punch 8.0 mm Upper punch Plain Lower punch Plain Process data Weight of tablet mg 200.0 Hardness N 60-90 Thickness Mm 4.10-4.30 Friability % 0.0-0.1 Disintegration time Minute 2-4

[0128] 4. Pantoprazole Sodium (Core) Tablets:

[0129] 4.1 Composition of Pantoprazole Sodium Tablets:

TABLE-US-00008 TABLE 7 Composition of Pantoprazole Sodium Tablets: Experiment ID I5 Ingredients Composition (% w/w) Pantoprazole Sodium 12.55 Pearlitol SD200 (Mannitol) 63.0 Aerosil 200 0.50 Microcrystalline Cellulose PH102 18.25 Crospovidone 2.0 HPMC 3 cps 2.0 Magnesium Stearate 1.7 Total 100

[0130] 4.2 Process for Pantoprazole Sodium Tablets Preparation: [0131] I. Weigh all the ingredients as specified in the formula. [0132] II. Co-sift Pantoprazole Sodium, Pearlitol SD200, Aerosil 200, MCC PH102, Crospovidone and HPMC 3cps through 40# sieve [0133] III. Mixed step II material in double cone blender for 15 minutes at 13 RPM. [0134] IV. Sifted Magnesium Stearate through 60# sieve. [0135] V. Lubricated step III blend with step IV magnesium stearate in double cone blender for 3 minutes at 13 RPM. [0136] VI. Compressed step V lubricated blend using 8.0 mm, Standard concave, plain punches.

TABLE-US-00009 TABLE 8 General Process Parameters for Pantoprazole Sodium tablet (core) preparation: Compression General Process Parameters Experiment I5 Parle Elisabeth Tablet compression Equipment machine (ElizaPress-200) Equipment setup Shape of punch Circular, standard concave Size of punch 8.0 mm Upper punch Plain Lower punch Plain Process data Weight of tablet mg 180.10 Hardness N 65-90 Thickness Mm 3.45-3.68 Friability % 0.2 Disintegration Minute 3 time

B. Coating:

[0137] 1. Coating composition for inventive experiments:

TABLE-US-00010 TABLE 9 Coating composition for Intermediate and enteric coating of inventive Experiment: Composition Composition (% w/w) (gram)* Experiment No. I1 I2 I3 I4 I5 I1 Core PP BT BT ST PT 85.0 Intermediate coating step HPMC (3 cps) 44.44 40.0 40.0 40.0 40.0 8.50 Glycerin 11.11 20.0 20.0 20.0 20.0 2.13 Magnesium 44.44 40.0 . . . 40.0 40.0 8.50 oxide Magnesium . . . . . . 40.0 . . . . . . . . . Carbonate Water q.s.to q.s.to q.s.to q.s.to q.s.to q.s. to (q.s to % w/w 10% 10% 10% 10% 10% 10% solid) Total 100 100 100 100 100 104.13 Polymer build 10% 3 3 15 2 10% up w.r.t. core w/w mg/cm.sup.2 mg/cm.sup.2 mg/cm.sup.2 mg/cm.sup.2 w/w pellets/tablets Enteric coating step EUDRAGIT 62.5 62.5 62.5 62.5 62.5 26.03 L30D-55 TEC 6.25 6.25 6.25 6.25 6.25 2.60 Talc 31.25 31.25 31.25 31.25 31.25 13.02 Water q.s.to q.s.to q.s.to q.s.to q.s.to q.s.to (q.s to % w/w 20% 20% 20% 20% 20% 20% solid) Total 100 100 100 100 100 145.78 Polymer build 25% 5 5 4 8 25% up w.r.t. w/w mg/cm.sup.2 mg/cm.sup.2 mg/cm.sup.2 mg/cm.sup.2 w/w intermediate coated pellets/tablets *Note: Composition of Experiment I1 is also expressed in grams for demonstrating Percentage alkali on alkali and enteric polymer calculation. Quantities of ingredients in subsequent experiments can be calculated likewise. Abbreviations: PP: Pantoprazole pellets; BT: Benazepril Tablets; ST: Sotalol Tablets; PT: Pantoprazole Tablets; HPMC: Hydrocy propyl methyl cellulose; TEC: Triethyl Citrate; w.r.t.: with respect to

[0138] 2. Coating Process for Inventive Experiments:

[0139] 2.1 Intermediate Coating:

[0140] 2.1.1 Intermediate Coating of Experiment I1, I2, I4 & I5: [0141] I. All ingredients were weighed in required quantity. [0142] II. HPMC [3 cps] was dissolved in water containing glycerin using overhead stirrer, until a clear solution is obtained. [0143] III. Magnesium oxide was added to above solution slowly while stirring and resulted suspension was then allowed to mix for 30 min. [0144] IV. Suspension was passed through 100# sieve and used for intermediate coating.

[0145] 2.1.2 Intermediate Coating of Experiment I3 [0146] I. All ingredients were weighed in required quantity. [0147] II. HPMC [3 cps] was dissolved in water containing glycerin using overhead stirrer, until a clear solution is obtained. [0148] III. Magnesium Carbonate was added to above solution slowly while stirring and resulted suspension then was allowed to mix for 30 min. [0149] IV. Suspension was passed through 40# sieve and used for intermediate coating.

TABLE-US-00011 TABLE 10(a) General Process Parameters for intermediate coating of inventive Experiment I1: General Process Parameters for intermediate coating Experiment I1 Equipment used Huttlin Mycrolab Equipment setup Silicone tube inner diameter mm 3.0 Nozzle bore mm 0.8 Process parameter setup Filter operation — Manual Filter shaking mode — Asynchronous Filter shaking sec 0.2 Filter shaking pause sec 1 Air flow mode — Auto Process data Air flow m.sup.3/hr 12-22 Atomization pressure bar 0.8-1.3 Microclimate bar 0.4-0.9 Inlet temperature ° C. 27-43 Product temperature ° C. 28-34 Pump RPM RPM 1-5

TABLE-US-00012 TABLE 10(b) General Process Parameters for intermediate coating of inventive Experiment I2 to I4 and I5: General Process Parameters for Experiment Experiment intermediate coating I2-I4 I5 Equipment used Neocota Neocota Equipment setup Silicone tube inner mm 3.0 3.0 diameter Pan size inch 14 14 Number of baffles No .Math. s 6 6 Process data Pan RPM RPM 2-8 2-8 Inlet temperature ° C. 70-73 60-65 Product ° C. 40-42 35-38 temperature Atomization bar 1.5 1.2-1.8 pressure Spray rate g/min 3-5 3-6

[0150] 2.2 Enteric Coating:

[0151] 2.2.1 Enteric Coating of Experiment I1-15: [0152] I. All the ingredients were weighed in required quantity. [0153] II. TEC and Talc were homogenized in water for 15 min then added slowly to the EUDRAGIT® L 30 D-55 dispersion while stirring, resulted suspension was mixed for 30 min using overhead stirrer. [0154] III. Suspension was passed through 40# sieve and used for enteric coating.

TABLE-US-00013 TABLE 11(a) General Process Parameters for enteric coating of Experiment I1: General Process Parameters for enteric coating Experiment I1 Equipment used Huttlin Mycrolab Equipment setup Silicone tube inner diameter mm 3.0 Nozzle bore mm 0.8 Process parameter setup Filter operation — Manual Filter shaking mode — Asynchronous Filter shaking sec 0.2 Filter shaking pause sec 1 Air flow mode — Auto Process data Air flow m.sup.3/hr 12-22 Atomization pressure bar 0.9-1.0 Microclimate bar 0.4-0.8 Inlet temperature ° C. 32-36 Product temperature ° C. 26-28 Pump RPM RPM 2-6

TABLE-US-00014 TABLE 11(b) General Process Parameters for enteric coating of inventive Experiment I2 to I4 & I5: General Process Parameters for Experiment Experiment enteric coating I2-I4 I5 Equipment used Neocota Neocota Equipment setup Silicone tube inner mm 3.0 3.0 diameter Pan size inch 14 14 Number of baffles No .Math. s 6 6 Process data Pan RPM RPM 8-9 8 Inlet temperature ° C. 45-50 46-48 Product temperature ° C. 28-32 30-32 Atomization pressure bar 1.2 1.5 Spray rate g/min 3-4 3-5

C. Analysis of Enteric Coated Pellets/Tablets:

[0155] Analytical Methodology

1. Benazepril Tablets

[0156] A) Dissolution Conditions [0157] 1) Dissolution Parameters [0158] Apparatus: USP Type II [0159] Dissolution Medium: Acid stage medium for 2 hrs followed by buffer stage medium (1 hr) [0160] Volume of Medium: 750 mL for acid stage, 1000 mL for buffer stage [0161] Speed: 50 rpm [0162] Temperature: 37° C.±0.5° C. [0163] Withdrawal Volume: 10 ml [0164] 2) Dissolution mediums [0165] I. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 5.5 buffer [0166] II. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 4.5 buffer [0167] III. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 3.0 buffer 3) Composition of dissolution mediums [0168] 1) Buffer pH 5.5— [0169] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 5.5 (±0.05) using ortho-phosphoric acid [0170] 2) Buffer pH 4.5— [0171] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 4.5 (±0.05) using ortho-phosphoric acid [0172] 3) Buffer pH 3.0— [0173] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 3.0 (±0.05) using ortho-phosphoric acid [0174] 4) Dissolution Procedure: [0175] Acid Stage: Benazepril hydrochloride tablets were transferred in different dissolution jars and then the dissolution test was performed as per parameters given in the method above (Acid Stage). After 2 hours 10 mL of aliquot was removed and analysed as acid stage sample solution. [0176] Buffer Stage: The tablets after acid stage were transferred to buffer stage medium. The dissolution test was continued as per parameters given in the method above (Buffer Stage). The aliquots of each interval ware filtered through 0.45 μm nylon membrane syringe filter discarding first few mL of the filtrate and analysed as buffer stage sample solution. [0177] B) Chromatographic Conditions [0178] Column: Agilent Zorbax Eclipse XDB C18 column, 150×4.6 mm, 5 μm or equivalent [0179] Mobile Phase: Buffer: MeOH (36:64) [0180] Wavelength: 240 nm [0181] Column Temp: 25° C. [0182] Injection Volume: 20 μL [0183] Flow rate: 1 mL/minute [0184] Preparation of Buffer for Mobile Phase: [0185] Accurately weighed 2.25 g of Tetra butyl ammonium bromide transferred in 500 mL water and dissolved. 0.55 mL of Glacial acetic acid added to it and volume was made up to 1000 mL with water. The buffer was filtered through 0.45 μm nylon membrane filter.

2. Sotalol Tablets

[0186] A) Dissolution Conditions [0187] 1) Dissolution Parameters [0188] Apparatus: USP Type II [0189] Dissolution Medium: Acid stage medium for 2 hrs followed by buffer stage medium (1 hr) [0190] Volume of Medium: 750 mL for acid stage, 1000 mL for buffer stage [0191] Speed 50 rpm [0192] Temperature 37° C.±0.5° C. [0193] Withdrawal Volume 10 ml [0194] 2) Dissolution mediums [0195] IV. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 5.5 buffer [0196] V. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 4.5 buffer [0197] VI. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 3.0 buffer [0198] 3) Composition of dissolution mediums [0199] 1) Buffer pH 5.5— [0200] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 5.5 (±0.05) using ortho-phosphoric acid [0201] 2) Buffer pH 4.5— [0202] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 4.5 (±0.05) using ortho-phosphoric acid [0203] 3) Buffer pH 3.0— [0204] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 3.0 (±0.05) using ortho-phosphoric acid [0205] 4) Dissolution Procedure: [0206] Acid Stage: Sotalol tablets were transferred in different dissolution jars and then the dissolution test was performed as per parameters given in the method above (Acid Stage). After 2 hours 10 mL of aliquot was removed and analyzed as acid stage sample solution. [0207] Buffer Stage: The tablets after acid stage were transferred to buffer stage medium. The dissolution test was continued as per parameters given in the method above (Buffer Stage). The aliquots of each interval ware filtered through 0.45 μm nylon membrane syringe filter discarding first few mL of the filtrate and analyzed as buffer stage sample solution. [0208] B) Chromatographic Conditions [0209] Column: Agilent Zorbax Eclipse XDB C 18 column, 150×4.6 mm, 5 μm or equivalent [0210] Mobile Phase: Buffer: ACN (90:10) [0211] Wavelength: 238 nm [0212] Column Temp: 25° C. [0213] Injection Volume: 20 μL [0214] Flow rate: 1.5 mL/minute [0215] Preparation of Buffer for Mobile Phase: [0216] Accurately weighed 6.8 g of potassium dihydrogen ortho-phosphate was dissolved in 1000 mL water. The buffer was filtered through 0.45 μm nylon membrane filter.

3. Pantoprazole Pellets/Tablets

[0217] A) Dissolution Conditions [0218] 1) Dissolution Parameters [0219] Apparatus USP Type II [0220] Dissolution Medium Acid stage medium for 2 hrs. followed by buffer stage medium (1 hr) [0221] Volume of Medium 1000 mL for acid stage, 1000 mL for buffer stage [0222] Speed 50 rpm [0223] Temperature 37° C.±0.5° C. [0224] Withdrawal Volume 10 ml [0225] Sample Dilution Dilute 10 mL of Aliquot with 2 mL of 0.5 N Sodium Hydroxide Solution immediately. [0226] 2) Dissolution mediums [0227] I. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 5.5 buffer [0228] II. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 4.5 buffer [0229] 3) Composition of dissolution mediums [0230] 1) Buffer pH 5.5— [0231] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1-liter beaker. To this, 500 mL water was added, salts were dissolved, and volume was made up to 1000 mL with water. The pH was adjusted to 5.5 (±0.05) using ortho-phosphoric acid. [0232] 2) Buffer pH 4.5— [0233] Accurately weigh and transfer 2.99 g of Sodium acetate trihydrate to 1-liter beaker. To this add water to dissolve and make up volume to 1000 mL. Adjust the pH to 4.5 (±0.05) using glacial acetic acid. [0234] 3) Buffer pH 3.0— [0235] Accurately weigh and transfer 8.98 gram of citric acid anhydrous and 2.13 gram of Tri-sodium citrate dihydrate in 1000 ml of water. Sonicate to dissolve. Adjust it to pH 3.5 (±0.05) using dilute NaOH. [0236] 4) Dissolution Procedure: [0237] Acid Stage: Accurately weighed pellets of Pantoprazole or tablets were transferred in different dissolution jars and then the dissolution test was performed as per parameters given in the method above (Acid Stage). After 2 hours 10 mL of aliquot was removed, filtered through 0.45 μm PVDF membrane syringe filter. 1 mL was immediately diluted with 1 mL of 0.5 N sodium hydroxide solution and analyzed as acid stage sample solution. [0238] Buffer Stage: The pellets or tablets after acid stage were transferred to buffer stage medium. The dissolution test was continued as per parameters given in the method above (Buffer Stage). The aliquots of each interval ware filtered through 0.45 μm PVDF membrane syringe filter discarding first few mL of the filtrate. 1 mL was immediately diluted with 1 mL of 0.5 N sodium hydroxide solution and analyzed as buffer stage sample solution. [0239] B) Chromatographic Conditions [0240] Chromatographic Conditions [0241] Column: Agilent Zorbax XDB Eclipse C8 column, 150×4.6 mm, 5 μm [0242] Mobile Phase: Water: Acetonitrile: Triethylamine (60:40:1) pH adjusted to 7.0 (+0.05) with orthophosphoric acid [0243] Wavelength: 290 nm [0244] Column Temp: 30° C. [0245] Injection volume: 10 μL [0246] Flow rate: 1.0 mL/minute

D. Summarization:

[0247]

TABLE-US-00015 TABLE 12 Performance of inventive experiments: Experiment No. I1 I2 I3 I4 15 Objective Experiment Experiment with different Experiment Experiment with acid alkalis in intermediate with very with acid labile drug layer on acid stable drug & high labile drug & in matrix tablet dosage form concentration tablet dosage pellets dosage of alkali in form form intermediate layer Core PP BT BT ST PT Inner layer 10% w/w 3 mg/cm.sup.2 3 mg/cm.sup.2 15 mg/cm.sup.2 2 mg/cm.sup.2 (Intermediate coating of coating of coating of coating of coating of coat) HPMC 3 cps + HPMC 3 cps + HPMC 3 cps + HPMC 3cps + HPMC 3 cps + Glycerol Glycerol Glycerol Glycerol Glycerol (25%) + (50%) + (50%) + (50%) + MgO (50%) + MgO (100%) MgO(100%) MgCO3 (100%) MgO(100%) (100%) Outer layer 25% w/w 5 mg/cm.sup.2 5 mg/cm.sup.2 4 mg/cm.sup.2 8 mg/cm.sup.2 (Enteric coating of coating of coating of coating of coating of coat) EUDRAGIT EUDRAGIT EUDRAGIT EUDRAGIT EUDRAGIT L30D-55 + L30D-55 + L30D-55 + L30D-55 + L30D-55 + TEC (10%) + TEC (10%) + TEC (10%) + TEC (10%) + TEC (10%) Talc (50%) Talc (50%) Talc (50%) Talc (50%) Talc (50%) Dissolution testing in acid media Enteric Pass Pass Pass Pass Pass protection # Dissolution testing in buffer media of respective pH pH 5.5 83.06* 92.5@ 92.2@ 98.7@ 88.41* pH 4.5 @ . . . . . . 86.4 89.2 . . . pH 4.0 @ . . . 90.2 . . . . . . . . . pH 3.0 @ . . . 97.6 . . . 99.3 . . . % alkali in 25% w/w*** 37% w/w 37% w/w 77% w/w 19% w/w alkali + enteric polymer** Inference Enteric Enteric Enteric Higher Enteric resistance resistance resistance concentration resistance followed by followed by followed by of alkali can followed by release in release in release in be used release in pH 5.5 pH 3.0, 4.0 & pH 4.5 & 5.5 without pH 5.5 demonstrated 5.5 demonstrated affecting demonstrated with acid demonstrated with MgCO3 performance with acid labile drug with acid as alkali in labile drug for pellet stable drug intermediate for tablet dosage form for tablet layer dosage form dosage form # Enteric protection after 2 hrs exposure to 0.1N HCl; *Drug release after 60 mins; @: Drug release after 45 mins; [00007]$\frac{{ }^{**}\%\mathrm{alkali}\mathrm{in}\mathrm{alkali}+\mathrm{enteric}\mathrm{polymer}=\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}\times 100}{\left(\mathrm{qty}.\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}+\mathrm{qty}.\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL}\right)}$[00008]$\begin{array}{c}{ }^{***}\mathrm{Percent}\mathrm{in}\mathrm{alkali}+\mathrm{enteric}\mathrm{polymer}\mathrm{for}\mathrm{experiment}I1=\frac{8.5}{\left[8.5+26.03\right]}\times 100\\ =24.6\%w/w\end{array}$Abbreviation: PP: Pantoprazole pellets; BT: Benazepril Tablets; ST: Sotalol Tablets; PT: Pantoprazole Tablets; MgO: Magnesium Oxide; MgCO3: Magnesium Carbonate; TEC: Triethyl Citrate; cps: Centipoise; Qty.: Quantity; gm: Grams

E. Core Preparation:

[0248] 1. Sotalol Tablets: [0249] Composition and process for Sotalol Tablets for experiment C1 & C2: Refer core preparation of experiment I4 [0250] 2. Pantoprazole Pellets:

[0251] 2.1 Composition of Pantoprazole Pellets (Drug Layering Method):

TABLE-US-00016 TABLE 13 Composition of Pantoprazole Pellets: Experiment ID C3 Ingredients Composition (% w/w) NPS 20/25# (707-841 μm) 73.42 Pantoprazole Sodium Sesquihydrate 22.58 eq. to Pantoprazole 20% HPMC 6 cps 4.00 Water (q.s. for % w/w solids) q.s. for 20.0% Total 100

[0252] 2.2 Process for Pantoprazole Pellets: [0253] I. All the ingredients were weighed in required quantity. [0254] II. HPMC [6 cps] was dissolved in water using overhead stirrer, until a clear solution is obtained. [0255] III. Pantoprazole Sodium Sesquihydrate was sifted through 40 # (400 μm) sieve and added to solution of step II during continuous stirring. Continued stirring till clear solution is obtained. [0256] IV. Drug solution of step III was sifted through 40 # sieve and used for drug layering on NPS 20/25#.

TABLE-US-00017 TABLE 14 General Process Parameters for Pantoprazole Pellets drug Layering: General Process Parameters in GPCG 1.1, bottom spray for drug layering Experiment C3 Equipment setup Silicone tube inner diameter mm 3.0 Air distribution plate — C Column height mm 20 Nozzle bore mm 0.8 Process parameter setup Filter shaking mode — Asynchronous Filter shaking sec 5 Filter shaking pause sec 50 Air flow mode — Auto Process data Air flow CFM 30-90 Atomization pressure bar 1.0-1.4 Inlet temperature ° C. 45-50 Product temperature ° C. 32-38 Spray rate g/min 3-8

[0257] 3. Benazepril Pellets:

[0258] 3.1 Composition of Benazepril (Core) Pellets:

TABLE-US-00018 TABLE 15 Composition of Benazepril pellets for experiment C4 &C5: Formula for BENAZEPRIL BENAZEPRIL PELLETS PELLETS Experiment ID C4 C5 Composition Composition Ingredients (% w/w) (% w/w) NPS 18/20# (850-1000 μm) 64.05 NPS 20/25# (707-841 μm) 64.78 Benazepril 20.52 20.11 HPMC [3 cps] 10.33 10.12 Lactose 2.55 2.50 Aerosil 200 2.55 2.50 Water (q.s. to % w/w solids) q.s. to 20% q.s. to 25% Total 100 100 Abbreviations: NPS: Non-pareil seeds, HPMC: Hydroxy propyl methyl cellulose, cps: centipoise cps: centipoise

[0259] 3.2 Process for Benazepril Pellets Preparation for Experiment C4 &C5: [0260] I. All ingredients were weighed accurately. [0261] II. Benazepril hydrochloride and lactose monohydrate were dissolved in sufficient quantity of purified water under continuous string. [0262] II. In a separator beaker, HPMC 3 cps was dissolved in purified water under stirring. [0263] IV. Aerosil® 200 was homogenized in purified water for 15 minutes. [0264] V. Step II solution was added to step Ill under stirring. [0265] VI. Step IV dispersion was then added to step V under stirring. [0266] VII. Step VI suspension was then filtered through #60 mesh and used it for drug layering on NPS.

TABLE-US-00019 TABLE 16 General Process Parameters for Benazepril pellets (core) preparation of comparative experiments C4 & C5: General Process Parameters in GPCG 1.1, bottom spray C4 C5 Equipment setup Silicone tube inner diameter mm 3.0 3.0 Air distribution plat — B B Column height mm 20 20 Nozzle bore mm 0.8 0.8 Process parameter setup Filter shaking mode — Asynchronous Asynchronous Filter shaking sec 5 5 Filter shaking pause sec 100 100 Air flow mode — Auto Auto Process data Air flow CFM 50-75 60-80 Atomization pressure bar 1.0-1.1 1.2 Inlet temperature ° C. 25-35 50-60 Product temperature ° C. 20-25 40-44 Spray rate g/min 2-8 3-13

F. Coating:

[0267] 1. Coating composition for seal, intermediate and enteric coating of comparative experiments:

TABLE-US-00020 TABLE 17 Coating composition for seal coating, intermediate coating and enteric coating for experiment C1 to C5: Composition (% w/w) Experiment No. C1 C2 C3 C4 C5 Core ST ST PP BP BP Seal coating HPMC (6 cps) 40.61 Talc 59.39 Water (q.s NA NA q.s.to 15% NA NA to % w/w solid) Total 100 Polymer build up 1.7% w/w w.r.t. core pellets Intermediate coating HPMC 3 cps 74.07 EUDRAGIT ® 56.50 L30D-55 Pharmacoat 606 40.0 Triethyl citrate 2.82 Glycerin 18.52 Tween 80 1.13 Talc 28.25 Citric acid 11.30 Sodium Hydroxide NA q.s.* NA Magnesium Oxide 7.41 Magnesium 60.0 Carbonate Water (q.s q.s.to 10% q.s.to 10% q.s.to 10% to % w/w solid) Total 100 100 100 Polymer build up 5 mg/cm.sup.2 3.16% w/w 10% w/w w.r.t. core w.r.t. seal w.r.t. core pellets coated pellets pellets Enteric coating EUDRAGIT L30D- 62.5 62.5 64.0 62.5 62.5 55 TEC 6.25 6.25 6.08 6.25 6.25 Talc 31.25 31.25 26.88 31.25 31.25 Titanium Dioxide 3.04 Sodium Hydroxide q.s. #@ Water (q.s q.s. to 20% q.s. to 10% q.s. to 20% q.s. to 20% q.s. to 20% to % w/w solid) Total 100 100 100 100 100 Polymer build up 5 mg/cm.sup.2 5 mg/cm.sup.2 20% w/w 15% w/w 20% w/w w.r.t. core w.r.t. w.r.t. w.r.t. core w.r.t. tablets intermediate intermediate pellets intermediate coated coated coated pellets pellets pellets # for 30% Neutralization; @ Used in the form of 1N NaOH solution Abbreviations: ST: Sotalol Tablets; PP: Pantoprazole Pellets; BP: Benazepril Pellets; NA: Not applicable; w.r.t.: with respect to

2. Process of Seal, Intermediate and Enteric Coating:

[0268] 2.1 Seal Coating:

[0269] 2.1.1 Process of Seal Coating of Experiment C3: [0270] I. All the ingredients were weighed in required quantity. [0271] II. HPMC [6 cps] was dissolved in water using overhead stirrer, till a clear solution is obtained. [0272] III. Talc was added to step II solution slowly while stirring and resulted suspension was allowed to mix for 30 min. [0273] IV. Suspension was passed through 40# sieve and used for seal coating.

TABLE-US-00021 TABLE 18 General Process Parameters for seal coating of comparative experiment C3: General Process Parameters in GPCG 1.1, bottom spray for seal coating Experiment C3 Equipment setup Silicone tube inner diameter mm 3.0 Air distribution plate — C Column height mm 15 Nozzle bore mm 0.8 Process parameter setup Filter shaking mode — Asynchronous Filter shaking sec 5 Filter shaking pause sec 250 Air flow mode — Auto Process data Air flow CFM 50-70 Atomization pressure bar 1.0-1.4 Inlet temperature ° C. 45-50 Product temperature ° C. 33-37 Spray rate g/min 3-8

[0274] 2.2 Intermediate Coating:

[0275] 2.2.1 Process of Intermediate Coating of Experiment C2: [0276] I. Weighed all ingredients accurately. [0277] II. Weighed quantity of talc was dispersed in purified water under homogenizer for 30 min. [0278] III. Separately prepared citric acid solution was added in step II. [0279] IV. 1 N NaOH solution required for neutralization of EUDRAGIT® L30D-55 was prepared. [0280] V. In a separate glass beaker, TEC and Tween 80 were added in warmed purified water till to forms a clear solution. [0281] VI. The step V solution was then added to the step II dispersion under overhead stirrer for 10 to 15 min. [0282] VII. The required quantity EUDRAGIT© L30D-55 was added to step II dispersion and mixed. [0283] VIII. The step VII dispersion was neutralized with step IV solution under continuous stirring to form a clear dispersion with required pH. [0284] IX. Suspension was passed through 40# sieve and used for intermediate coating.

TABLE-US-00022 TABLE 19 General Process Parameters for intermediate coating of comparative experiment C2: General Process Parameters for intermediate coating Experiment C2 Equipment used Neocota Equipment setup Silicone tube inner diameter mm 3.0 Pan size inch 14 Number of baffles No.s 6 Process data Pan RPM RPM  2-10 Inlet temperature ° C. 55-65 Product temperature ° C. 30 Atomization pressure bar 1.5 Spray rate g/min 1-6

[0285] 2.2.2 Process of Intermediate Coating of Experiment C3: [0286] I. All the ingredients were weighed in required quantity. [0287] II. Pharmacoat 606 was dissolved in purified water using overhead stirrer. [0288] III. Magnesium Carbonate was added to above solution slowly while stirring and resulted suspension was then allowed to mix for 30 min. [0289] IV. Suspension was passed through 40# sieve and used for intermediate coating.

TABLE-US-00023 TABLE 20 General Process Parameters for intermediate coating of comparative experiment C3: General Process Parameters in GPCG 1.1, bottom spray for intermediate coating Experiment C3 Equipment setup Silicone tube inner mm 3.0 diameter Air distribution plate — C Column height mm 20 Nozzle bore mm 0.8 Process parameter setup Filter shaking mode — Asynchronous Filter shaking sec 5 Filter shaking pause sec 250 Air flow mode — Auto Process data Air flow CFM 50-70 Atomization pressure bar 1.0-1.4 Inlet temperature ° C. 41-45 Product temperature ° C. 33-37 Spray rate g/min 3-8

[0290] 2.2.3 Process for Experiment C5 Intermediate Coating: [0291] I. All the ingredients were weighed in required quantity. [0292] II. Glycerin was dissolved in purified water. [0293] III. HPMC (3 cps) was dissolved step II using overhead stirrer, till a clear solution is obtained. [0294] IV. Magnesium oxide was added to above solution slowly while stirring and resulted suspension was allowed to mix for 30 min. [0295] V. Suspension was passed through 40# sieve and used for intermediate coating on drug layered pellets.

[0296] 2.3 Enteric Coating:

[0297] 2.3.1 Process of Enteric Coating of Experiment C1& C2: [0298] I. Weigh all ingredients as specified in the formula. [0299] II. Weighed quantity of talc was dispersed in purified water under homogenizer for 30 min. [0300] III. In a separate glass beaker, TEC was added in warmed purified water till to forms a clear solution. [0301] IV. The step III solution was added to the step II dispersion under overhead stirrer for 15 min. [0302] V. Weighed quantity EUDRAGIT® L30D-55 dispersion was added in to step IV dispersion and mixed. [0303] V. The prepared dispersion was passed through 40# sieve and used for enteric coating.

[0304] 2.3.2 Process of Enteric Coating of Experiment C3: [0305] I. All the ingredients were weighed in required quantity. [0306] II. TEC and Talc were homogenized in water for 15 min then added slowly to the EUDRAGIT® L 30 D-55 dispersion while stirring, resulted suspension was mixed for 30 min using overhead stirrer. [0307] III. Suspension was passed through 40# sieve and used for enteric coating.

[0308] 2.3.3 Process of Enteric Coating of Experiment C4: [0309] I. All the ingredients were weighed in required quantity. [0310] II. Add EUDRAGIT® L30D-55 in 60% quantity of water under stirring. [0311] III. Prepare 1N sodium hydroxide solution using part of remaining quantity of water. [0312] IV. Add step III to step II slowly under stirring. [0313] V. Add TEC & talc in remaining quantity of water and homogenize it for 30 minutes [0314] VI. Add step V to step IV under stirring and continue stirring for 20 minutes. [0315] VII. Suspension was passed through 40# sieve and used for enteric coating on intermediate coated pellets.

[0316] 2.3.4 Process of Enteric Coating of Experiment C5: [0317] I. All the ingredients were weighed in required quantity. [0318] II. TEC and Talc were homogenized in water for 15 m then added slowly to the EUDRAGIT® L 30 D-55 dispersion while stirring, resulted suspension was mixed for 30 min using overhead stirrer. [0319] III. Suspension was passed through 40# sieve and used for enteric coating on intermediate coated pellets.

TABLE-US-00024 TABLE 21(a) General Process Parameters for enteric coating of comparative experiment C1& C2: General Process Parameters for Experiment enteric coating C1 - C2 Equipment used Neocota Equipment setup Silicone tube inner diameter mm 3.0 Pan size inch 14 Number of baffles No .Math. s 6 Process data Pan RPM RPM  6-14 Inlet temperature ° C. 55-65 Product temperature ° C. 28-32 Atomization pressure bar 1.5 Spray rate g/min 1-8

TABLE-US-00025 TABLE 21(b) General Process Parameters for enteric coating of comparative experiment C3 & C4: General Process Parameters in GPCG 1.1, bottom spray Experiment Experiment Experiment for enteric coating C3 C4 C5 Equipment setup Silicone tube inner mm 3.0 3.0 3.0 diameter Air distribution plate — B B B Column height mm 15 15 15-20 Nozzle bore mm 0.8 0.8 0.8 Process parameter setup Filter shaking mode — Asynchronous Asynchronous Asynchronous Filter shaking sec 5 5 5 Filter shaking pause sec 250 100 250 Air flow mode — Auto Auto Auto Process data Air flow CFM 40-70 63-76 70-80 Atomization pressure bar 1.0-1.4 1.5 1.0 Inlet temperature ° C. 35-39 52-55 38-41 Product temperature ° C. 29-32 39-44 29-31 Spray rate g/min 3-8 1-7 3-9

G. Analysis of Enteric Coated Tablets/Pellets:

[0320] Analytical Methodology [0321] 1. Sotalol Tablets: Refer analytical methodology of step 0(2). [0322] 2. Pantoprazole Pellets: Refer analytical methodology of step 0(3). [0323] 3. Benazepril Pellets: [0324] A) Dissolution Conditions [0325] 1) Dissolution Parameters [0326] Apparatus: USP Type II [0327] Dissolution Medium: Acid stage medium for 2 hrs followed by buffer stage medium (1 hr) [0328] Volume of Medium: 750 mL for acid stage, 1000 mL for buffer stage [0329] Speed: 50 rpm [0330] Temperature: 37° C.±0.5° C. [0331] Withdrawal Volume: 10 ml [0332] 2) Dissolution mediums [0333] I. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 5.5 buffer [0334] II. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 4.5 buffer [0335] III. Acid stage medium-0.1 N HCl; Buffer stage medium-pH 3.0 buffer [0336] 3) Composition of dissolution mediums [0337] 1) Buffer pH 5.5— [0338] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved and volume was made up to 1000 mL with water. The pH was adjusted to 5.5 (±0.05) using ortho-phosphoric acid [0339] 2) Buffer pH 4.5— [0340] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1 liter beaker. To this, 500 mL water was added, salts were dissolved, and volume was made up to 1000 mL with water. The pH was adjusted to 4.5 (±0.05) using ortho-phosphoric acid [0341] 3) Buffer pH 3.0— [0342] 1 g of Potassium dihydrogen phosphate, 2 g of Di-potassium hydrogen phosphate and 8.5 g of Sodium chloride was weighed and transferred to 1-liter beaker. To this, 500 mL water was added, salts were dissolved, and volume was made up to 1000 mL with water. The pH was adjusted to 3.0 (±0.05) using ortho-phosphoric acid [0343] 4) Dissolution Procedure: [0344] Acid Stage: Accurately weighed pellets of Benazepril hydrochloride were transferred in different dissolution jars and then the dissolution test was performed as per parameters given in the method above (Acid Stage). After 2 hours 10 mL of aliquot was removed and analysed as acid stage sample solution. [0345] Buffer Stage: The pellets after acid stage were transferred to buffer stage medium. The dissolution test was continued as per parameters given in the method above (Buffer Stage). The aliquots of each interval ware filtered through 0.45 μm nylon membrane syringe filter discarding first few mL of the filtrate and analysed as buffer stage sample solution. [0346] B) Chromatographic Conditions [0347] Column: Agilent Zorbax Eclipse XDB C18 column, 150×4.6 mm, 5 μm or equivalent [0348] Mobile Phase: Buffer: MeOH (36:64) [0349] Wavelength: 240 nm [0350] Column Temp: 25° C. [0351] Injection Volume: 20 μL [0352] Flow rate: 1 mL/minute [0353] Preparation of Buffer for Mobile Phase: [0354] Accurately weighed 2.25 g of Tetra butyl ammonium bromide transferred in 500 mL water and dissolved. 0.55 mL of Glacial acetic acid added to it and volume was made up to 1000 mL with water. The buffer was filtered through 0.45 μm nylon membrane filter.

H. Summarization:

[0355]

TABLE-US-00026 TABLE 22(a) Performance of comparative experiment C1-C3: Experiment No. C1 C2 C3 Objective Standard “Duocoat Comparative example EUDRAGIT Technology” similar to example 1 of L30D-55 according to US 2005214371A1 coating WO2008/135090 using pantoprazole as A1 API instead of lansoprazole Core ST ST PP Inner layer (Seal . . . . . . 1.7% w/w HPMC 6 cps + coat) Talc (146.25%) Inner layer . . . 5 mg/cm.sup.2 coating 3.16% w/w HPMC 6 cps+ (Intermediate of EUDRAGIT Magnesium Carbonate coat) L30D-55 (150%) Neutralized at pH6.0 with 20% Citric acid + TEC (5%) + Talc (50%) Outer layer 5 mg/cm.sup.2 5 mg/cm.sup.2 coating 20% w/w EUDRAGIT (Enteric coat) coating of of EUDRAGIT L30D-55 + TEC (9.5%) + EUDRAGIT L30D-55 + TEC Talc (42%) + TiO.sub.2 L30D-55 + (10%) + Talc (4.75%) TEC (10%) + (50%) Talc (50%) Dissolution testing in acid media Enteric protection # Pass# Pass# Pass! Dissolution testing in buffer media of respective pH pH 5.5 4.4@ 9.4@ 26.29* pH 5.8@ 8.2 83.5 . . . pH 6.2@ 85.5 93 . . . % alkali in alkali + NA NA 18% w/w enteric polymer** Inference Very slow Very slow and Slow and incomplete and incomplete drug release is obtained incomplete release was with comparative release was observed at pH example similar to observed at 5.5 & below example 1 of pH 5.8, 5.5 US2005214371A1 using & below pantoprazole as API instead of lansoprazole #Enteric protection after 2 hrs exposure to 0.1N HCl; * Drug release after 45 mins; @ Drug release after 30 mins [00009]$\frac{{ }^{**}\%\mathrm{alkali}\mathrm{in}\mathrm{alkali}+\mathrm{enteric}\mathrm{polymer}=\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}\times 100}{\left(\mathrm{qty}.\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}+\mathrm{qty}.\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL}\right)}$Due to rapid degradation of Lansoprazole at lower pH conditions like pH 5.5, 4.5 and 3.0, Pantoprazole was used as API in example. !At enteric polymer build up 11.85% (Similar build up as US 2005214371 example 1), enteric protection for 2 hours was not obtained (degradation observed after 2 hr exposure to acid media-evaluated using back assay method) so further enteric coating done to get 20% enteric polymer build up which passed in enteric protection after 2 hour acid exposure. Abbreviation: ST: Sotalol Tablets; PP: Pantoprazole Pellets; HPMC: Hydroxy propyl methyl cellulose; TEC: Triethyl Citrate; TiO.sub.2: Titanium Dioxide; Qty.: Quantity; gm: Grams

TABLE-US-00027 TABLE 22(b) Performance of comparative experiment C4 & C5: Experiment No. C4 C5 Objective 30% Neutralized EUDRAGIT Experiment with very low L30D-55 coating alkali concentration in inner (according to US7932258B2) layer keeping intermediate layer thickness constant Core BP BP Inner layer 10% w/w HPMC + Glycerol (Intermediate coat) (25%) + MgO (10%) Outer layer 15% w/w EUDRAGIT L 30D55 20% w/w EUDRAGIT L30D-55 + (Enteric coat) (30% neutralized with NaOH) + TEC (10%) + Talc (50%) TEC (10%) + Talc (50%) Dissolution testing in acid media Enteric protection # Pass Pass Dissolution testing in buffer media of respective pH pH 5.5* 22.1 7.1 pH 4.5* 6.8 pH 3.0* 7.8 % alkali in alkali + NA 4.22% w/w** enteric polymer** Inference Enteric resistance followed by Use of 10% Magnesium oxide slow and incomplete release in (w.r.t. dry binder quantity in buffer pH 5.5 was observed intermediate coat) shows enteric resistance followed by less than 10% release in pH buffer 5.5 and lower pH # Enteric protection after 2 hrs exposure to 0.1N HCl; * Drug release after 45 mins; [00010]$\frac{{ }^{**}\%\mathrm{alkali}\mathrm{in}\mathrm{alkali}+\mathrm{enteric}\mathrm{polymer}=\mathrm{quantity}\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}\times 100}{\left(\mathrm{qty}.\mathrm{of}\mathrm{alkaline}\mathrm{agent}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ICL}+\mathrm{qty}.\mathrm{of}\mathrm{enteric}\mathrm{polymer}\mathrm{in}\mathrm{grams}\mathrm{in}\mathrm{the}\mathrm{ECL}\right)}$Abbreviation: BP: Benazepril pellets; TEC: Triethyl Citrate; NA: Not applicable; Qty.: Quantity; gm: Grams

[0356] Intermediate Coating Layer (ICL) Thickness Determination Via Scanning Electron Microscopy (SEM) Investigation

[0357] In order to perform an inner layer thickness evaluation, which is important in order to evaluate the functionality of the double layer dosage form, the following procedures are applied consisting of a suitable sample size calculation, random sampling of the number of samples, preparation of sample, determination of layer thickness and result evaluation.

[0358] Sample Number Calculation Equation:

[00011]$\mathrm{sample}\mathrm{size}=\frac{\frac{z^2\times p\left(1-p\right)}{e^2}}{1+\left(\frac{z^2\times p\left(1-p\right)}{e^{2}N}\right)}$

N=Batch Size

[0359] e=Error Margin
z=Z-Value representing the confidence level
p=Standard of deviation

TABLE-US-00028 TABLE 23 Confidence level Z-value 80% 1.28 85% 1.44 90% 1.65 95% 1.96 99% 2.58

[0360] Example of Calculation for C3

N=457,200 [units]
e=0.1
z=1.96
p=0.5

[00012]$\mathrm{sample}\mathrm{size}=\frac{\frac{1.96^2\times 0,5\left(1-0.5\right)}{{0.1}^2}}{1+\left(\frac{1.96^2\times 0.5\left(1-0.5\right)}{0.Math.1^{2}457,200}\right)}\mathrm{sample}\mathrm{size}=96.06$

Analytical Method

SEM Equipment Set-Up

[0361] Make: Thermo Fisher Scientific

[0362] Model: FEI Quanta 200

[0363] Pressure: Low Vacuum mode at 65 pascals

[0364] Magnification: Various

[0365] Voltage (HV) was kept at 20 KV

[0366] Detector used was Large Field Detector (LFD)

SEM Method Description:

[0367] Samples are to be randomly taken from the batch of coated dosage form units, i.e. pellets or tablets. The taken samples were broken typically into two equally sized dose unit halves. The broken pieces were fixed in an upright position on the sample mounting disc. The samples are to be investigated at an adequate magnification which corresponds to the dose unit dimensions. The layer thickness will be determined in a 900 angle to the substrate (core of the dosage form). The single values are noted, and the mean average and standard deviation is calculated. The results of the SEM analysis are shown in table 24. FIG. 1 shows a schematic cross-section through a spherical dosage form (e.g. a pellet or a tablet) with indication of the Inner coating Layer (ICL) thickness measurement principles as mentioned above.

TABLE-US-00029 TABLE 24 SEM Results Example/Experiment No. C3 I1 I2 I3 I4 I5 Core PP PP BT BT ST PT Inner layer 3.16% w/w 10% 3 mg/cm2 3 mg/ 15 mg/cm2 2 mg/cm2 (Intermediate coat) HPMC w/w coating of cm2 coating coating of 6cps + coating HPMC 3 coating of HPMC HPMC 3 Magnesium of cps + of 3cps + cps + Carbonate HPMC Glycerol HPMC Glycerol Glycerol (150%) 3cps + (50%) + 3cps + (50%) + (50%) + Glycerol MgO Glycerol MgO MgO (25%) + (100%) (50%) + (100%) (100%) MgO MgCO3 (100%) (100%) Units per batch 457,200 457,200 1,625 1,625 1,625 1,625 e 0.1 0.1 0.1 0.1 0.1 0.1 z 95% 95% 95% 95% 95% 95% p 0.5 0.5 0.5 0.5 0.5 0.5 Calculated Sample 96.0 96.0 90.7 90.7 90.7 90.7 Size (=minimum) Detected Values 100 100 100 100 100 100 Inner Layer 15.7 29.4 31.8 — 206.9 37.7 Thickness [μm] Standard Deviation [μm] ±2.7 ±3.9 ±3.3 — ±10.2 ±4.3

Conclusion:

[0368] It was found that the inner layer (intermediate coat) thickness of the comparative example C3 (15.7 μm with a standard deviation of ±2.7 μm) is significantly lower than the inner layer (intermediate coat) thickness of the inventive examples 11-5 (29.4-206.7 μm with a standard deviation of 13.9-10.2 μm, respectively). Thus, the inner layer thickness can be correlated to the incomplete release of 26.29% after 45 minutes incubation to a buffer media at pH 5.5 as reported above.