Zeolite having specific ratio of divalent copper ions supported thereon, and preparation method therefor and catalyst composition comprising same

Abstract

The present invention relates to zeolite containing Cu2+ () and Cu2+ () having different NO adsorption capacities loaded at a specific ratio, wherein the zeolite is chabazite (CHA)-type zeolite, particularly chabazite (CHA)-type zeolite loaded with divalent copper ions in which the NO adsorption area ratio of Cu2+ ()/Cu2+ () after exposure to NO (nitrogen oxide) for 180 sec is 80% or more. In addition, the present invention relates to a method of preparing zeolite that is ion-exchanged in a slurry state and to a catalyst including the specified chabazite (CHA)-type zeolite.

Claims

1. An SCR catalyst composition, comprising a chabazite (CHA)-type zeolite and a binder, wherein the chabazite (CHA)-type zeolite is loaded with copper ions in which a NO adsorption area of Cu.sup.2+ () is 80% or more as compared to a NO adsorption area of Cu.sup.2+ () after exposure to NO for 180 sec in a NO DRIFTS spectrum.

2. The catalyst composition of claim 1, wherein the binder is zirconium acetate.

3. The catalyst composition of claim 1, further comprising an alkali metal and/or an alkaline earth metal.

4. The catalyst composition of claim 3, wherein the alkali metal is potassium and the alkaline earth metal is calcium.

5. A honeycomb SCR catalyst structure coated with the catalyst composition of claim 1.

6. A method of preparing the SCR catalyst composition of claim 1, the method comprising preparing a zeolite slurry by dispersing a copper precursor and chabazite (CHA)-type zeolite in a slurry state and drying and calcining the zeolite slurry.

7. The method of claim 6, wherein the copper precursor is copper oxide, copper nitrate, copper sulfate, or copper acetate.

Description

DESCRIPTION OF DRAWINGS

(1) FIG. 1 schematically shows the overall process of preparing a conventional catalyst structure;

(2) FIG. 2 schematically shows the overall process of preparing a catalyst structure according to the present invention;

(3) FIG. 3 shows scanning electron microscope (SEM) images of two zeolites obtained through ISIE according to the present invention and two zeolites obtained through conventional LPIE;

(4) FIG. 4 shows the XRD patterns of the two samples of FIG. 3;

(5) FIG. 5 shows the spectrum results obtained through NO DRIFTS, which is a spectroscopic process for measuring a NO adsorption rate, and a chabazite-type (CHA) zeolite structure;

(6) FIG. 6 shows peak changes depending on the NO exposure time (ranging from 15 sec to 537 sec) in NO DRIFTS;

(7) FIG. 7 shows the results of NO adsorption rates of the zeolite samples prepared through ISIE and LPIE;

(8) FIG. 8 is graphs showing the NOx conversion performance using Case-1 catalysts;

(9) FIG. 9 is graphs showing the NOx conversion performance using Case-2 catalysts; and

(10) FIG. 10 is graphs showing the results of comparison of activity before and after hydrothermal aging of Fe-zeolite catalysts prepared through ISIE and LPIE.

MODE FOR INVENTION

(11) As used herein, the term catalyst or catalyst structure refers to a structure configured such that a catalyst composition including zeolite is applied to the inside of a typical honeycomb carrier or support. As is apparent by those skilled in the art, the carrier or support may indicate a structure, which may be made of an inorganic material or a metal and in which multiple passages are defined by multiple inner walls and the catalyst composition is applied on some or all of the inner walls. The catalyst structure is distinguished from what is meant by the term catalyst composition, and the catalyst composition is also distinguished from zeolite, which is a component thereof. Herein, the catalyst composition should be understood to include zeolite and a binder or an additive, such as an alkali metal or an alkaline earth metal, required for application onto the catalyst structure. In the present invention, zeolite means a structure in which a tetrahedron of (Si,Al)O.sub.4 has a three-dimensional skeleton and cavities due to the presence of apical oxygen, as will be easily understood by those skilled in the art, but in particular, chabazite-type zeolite having a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 5 to 50 is described as an example.

(12) As copper-ion-exchanged chabazite-type zeolite, Cu-zeolite having a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 30 and an average particle diameter of 1.5 m or more is known in the art. Cu-zeolite available from a commercial source is prepared through known LPIE. By catalyst manufacturers, a catalyst structure is manufactured in a manner in which commercially available Cu-zeolite is purchased, mixed with deionized water (DI water), a binder such as alumina, silica or zirconia, and an additive, and dispersed, thus preparing a Cu-zeolite catalyst composition, which is then applied on a honeycomb carrier, followed by drying and calcination. Here, the additive includes an alkali metal, an alkaline earth metal, a sugar or the like, which is known in the art. The completed honeycomb catalyst structure is attached to a vehicle engine exhaust system to reduce nitrogen oxides discharged from the engine to harmless substances. FIG. 1 schematically illustrates the overall process of preparing a conventional catalyst structure. However, the amount of copper that is loaded needs to be varied in order for catalyst manufacturers to prepare various catalyst compositions, which are applied on the carrier, and moreover, and the preparation of a NOx reduction catalyst using Cu-zeolite that is obtained through conventional LPIE and is commercially available is problematic because NOx activity at high temperatures is low, and thus a novel method of preparing a catalyst composition, aiming at enabling variation in the amount of copper that is loaded, cost reduction and excellent high-temperature activity, is recognized as a challenging task.

(13) The present inventors have prepared Cu-zeolite having a novel structure through a novel process called ISIE and a catalyst composition using the same. Compared to conventional Cu-zeolite obtained through LPIE, zeolite prepared through ISIE is very similar in terms of structure (SEM image), crystal structure (XRD pattern) and other properties (H.sub.2-TPR and NH.sub.3-TPD), but is different in the oxidation state of the ion-exchanged metal and the position thereof in zeolite pores, and thus the high-temperature activity of the catalyst according to the present invention can be confirmed to increase based on these parameter differences. FIG. 2 schematically illustrates the overall process of preparing a catalyst structure according to the present invention.

(14) ISIE, which is a one-pot process used for the preparation of zeolite in the present invention, is different from conventional LPIE in that it obviates washing and filtration in the preparation of metal-impregnated zeolite. In LPIE, a soluble, especially water-soluble, Cu precursor, and ammonium zeolite are adjusted in temperature and acidity in a liquid phase, pretreated, washed and then filtered and thus copper-ion-exchanged, but in ISIE, a Cu precursor, preferably insoluble CuO, and H-zeolite are subjected to ion exchange through contact and milling in a slurry state, and thus ISIE is understood to be a process that obviates additional washing and filtration. Specifically, DI water is added with CuO, H-zeolite and a binder, for example, a Zr material, stirred at room temperature for 10 min or more, milled, further added with an additive, and dispersed to afford a Cu-zeolite catalyst composition, which is then applied on a honeycomb carrier, followed by drying and calcination, thereby preparing a catalyst structure. Although not particularly limited in theory, CuO is deemed to undergo slow copper ionization through slurry milling and to be transferred to the proper position in zeolite. The zeolite prepared through ISIE according to the present invention is compared with the conventional zeolite prepared through LPIE. FIG. 3 shows SEM images of two zeolite samples obtained through ISIE and two zeolite samples obtained through LPIE.

(15) The Case-1 sample is zeolite that has a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 30 and in which 3 wt % of CuO is loaded based on the total weight thereof, and the Case-2 sample is zeolite that has a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 5 and in which 2.5 wt % of CuO is loaded based on the total weight thereof and potassium and calcium oxides are contained as additives in amounts of 1 to 5 wt %. As shown in FIG. 3, the morphological structures of zeolites obtained through ISIE and LPIE are almost the same as each other.

(16) In the present invention, the crystal structures of zeolites obtained through ISIE and LPIE are compared. FIG. 4 shows the XRD patterns of the two samples of FIG. 3.

(17) As shown in FIG. 4, the crystal structures of zeolites obtained through ISIE and LPIE are almost the same as each other. In the present invention, various properties were measured in order to structurally distinguish the zeolites obtained through ISIE and LPIE, and specifically, the H.sub.2-TPR profiles and NH.sub.3-TPD profiles of the zeolites hydrothermally aged at 750 C. for 20 hr are almost the same as each other (profiles are not shown).

(18) However, as will be described below, the zeolite prepared in the present invention is different in terms of NOx reduction, in particular NOx reduction activity at high temperatures, from conventional zeolite, and thus the present inventors have sought to determine the parameters that distinguish them structurally.

(19) As disclosed in documents, two divalent copper ions are known to be present depending on the NO adsorption capacity. FIG. 5 shows spectrum results obtained through NO DRIFT spectroscopy for measuring the NO adsorption rate, and the chabazite (CHA)-type zeolite structure. With reference to the documents, CHA is configured such that the -type divalent copper ion Cu.sup.2+ () is exchanged in the double 6-ring region and the -type divalent copper ion Cu.sup.2+ () is present in large cavities. The present inventors have investigated whether the presence or content of such divalent copper ions may be utilized as a parameter to specify the zeolites produced through ISIE and LPIE. FIG. 6 shows peak changes depending on the NO exposure time (ranging from 15 sec to 537 sec) in NO DRIFTS, which may be implemented by those skilled in the art. The zeolite sample was calcined at 450 C. in a N.sub.2 atmosphere, cooled to 40 C., and exposed to a 5% NO/N.sub.2 atmosphere.

(20) As shown in FIG. 6, the NO adsorption rate of Cu.sup.2+ () is decreased and the NO adsorption rate of Cu.sup.2+ () is increased over time. Through such NO DRIFT measurement, the Cu-zeolite of the present invention was specified to have a ratio of ions having different states, as a parameter, to distinguish Cu-zeolite prepared through ISIE according to the present invention. As a new parameter, the present inventors adopted the adsorption ratio of Cu.sup.2+ ()/Cu.sup.2+ () of the catalyst composition after exposure to NO (nitrogen monoxide) for 180 sec. FIG. 7 shows the results of adsorption rates of the Case-1 and Case-2 zeolite samples.

(21) With reference to FIG. 7, the chabazite (CHA)-type zeolite according to the present invention is chabazite (CHA)-type zeolite loaded with copper ions in which the adsorption rate or adsorption area ratio of Cu.sup.2+ ()/Cu.sup.2+ () after exposure to NO for 180 sec is 80% or more. This is structurally and functionally differentiated from chabazite (CHA)-type zeolite prepared by LPIE, loaded with divalent copper ions in which the adsorption area ratio of Cu.sup.2+ ()/Cu.sup.2+ () is less than 80%.

(22) Below is a description of the method of preparing the catalyst composition schematically shown in FIG. 2. Specifically, H-zeolite may be purchased or synthesized. As understood by those skilled in the art, H-zeolite, especially chabazite-type zeolite, may be prepared using a material composition comprising a silica material, an alumina material, and water. Also, the material composition may be added with a component that is able to promote the crystallization of seed crystals. Examples of the silica material preferably include colloidal silica, amorphous silica, sodium silicate, tetraethyl ortho-silicate, and aluminosilicate gel. Examples of the alumina material preferably include aluminum sulfate, sodium aluminate, aluminum hydroxide, aluminum chloride, aluminosilicate gel, and metal aluminum. As a structure-directing agent, N,N,N-trialkyl adamantane ammonium hydroxide is used.

(23) It is preferred that these materials be mixed to afford the material composition for chabazite-type zeolite. In the material composition, the SiO.sub.2/Al.sub.2O.sub.3 molar ratio preferably falls in the range of 16 to 100. Given the molar ratio of the material composition ranging from 16 to 100, it is easy to obtain chabazite-type zeolite having a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 5 to 50. The material composition comprising water, the silica material, the alumina material, and the structure-directing agent is preferably crystallized in a sealed pressure vessel at a temperature between 100 and 200 C. for a sufficient period of time, thus obtaining chabazite-type zeolite. The chabazite-type zeolite thus obtained is configured such that one or both of the structure-directing agent and the alkali metal may be contained in the pores thereof. Hence, these are preferably removed as necessary. The removal of alkali metal, etc. may be performed through exchange treatment using an acidic solution, pyrolysis or appropriate combination thereof, thereby preparing H-zeolite. In the preparation method, chabazite-type zeolite is provided by way of example, and 8-membered oxygen-ring small-pore zeolite, for example, LTA, AEI, AFT, AFV, AFX, KFI, SAV, SFW, TSC, FAU, MFI, BEA, FER, or MOR, may be applied.

(24) The H-zeolite synthesized above or commercially purchased is mixed with a Cu precursor such as CuO, a binder such as Zr acetate, and an additive, and is dispersed, thus preparing a Cu-zeolite catalyst composition. As the Cu precursor, copper acetate, copper nitrate, or copper sulfate may be used. CuO is understood to be ion-exchanged through contact and milling in a slurry state with the H-zeolite. DI water is added with CuO, H-zeolite and Zr acetate, stirred at room temperature for 10 min or more, and then milled. Also, the additive is added thereto and dispersed, thus preparing a Cu-zeolite catalyst composition in a slurry state, which is then applied on the inner walls of a honeycomb carrier, understood by those skilled in the art, dried and calcined at 450 C., resulting in a catalyst structure. In the present invention, the additive may include an alkali metal, an alkaline earth metal, a sugar or the like, which is known in the art. In an embodiment of the present invention, as described above, the Case-1 sample is a catalyst composition including zeolite having a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 30 and loaded with 3 wt % of CuO based on the total weight thereof, and the Case-2 sample is a catalyst composition including zeolite having a SiO.sub.2/Al.sub.2O.sub.3 molar ratio of 5 and loaded with 2.6 wt % of CuO based on the total weight thereof and added with 1 to 5 wt % of potassium and calcium oxides as additives. The completed honeycomb catalyst structure is attached to a vehicle engine exhaust system to reduce nitrogen oxides into harmless substances. FIG. 8 is graphs showing the performance using the Case-1 catalysts. As shown in FIG. 8, compared to the conventional catalyst including zeolite prepared through LPIE, the catalyst prepared according to the present invention is characterized in that a high NOx conversion rate is maintained at high temperatures and N.sub.2O is formed in a small amount in the overall temperature range. Also, FIG. 9 is graphs showing the performance using the Case-2 catalysts. As shown in FIG. 9, compared to the conventional catalyst including zeolite prepared through LPIE, the catalyst having a low SiO.sub.2/Al.sub.2O.sub.3 ratio prepared according to the present invention is characterized in that a high NOx conversion rate is maintained in the overall temperature range and in that N.sub.2O formation is low at 250 to 550 C.

(25) Moreover, an embodiment in which Fe is exchanged in lieu of Cu was performed in the same manner as above. The results are shown in FIG. 10. As shown in this drawing, the activities before and after hydrothermal aging of the Fe-zeolite catalysts prepared through ISIE and LPIE were similar to each other, from which the ISIE process can be confirmed to be applicable even upon Fe ion exchange.