AIRBAG BASE FABRIC AND PRODUCTION METHOD THEREFOR

Abstract

The present disclosure describes using additional yarn having a boiling-water shrinkage rate less than that of the base yarn, thereby suppressing shrinkage at the sides in the width direction of the fabric and thus reducing the difference in the crimp ratio between the center in the width direction of the fabric and the sides in the width direction. This enables the production of a fabric for airbags with high uniformity in the width direction.

Claims

1. A fabric for airbags comprising unremoved fringe at both sides in the width direction of the fabric, the fabric comprising at least two additional yarns at each of the sides in the width direction, wherein the crimp ratio of warp yarn aligned in the center in the width direction of the fabric is within the range of 7 to 20%, the crimp ratio of warp yarn aligned at the sides in the width direction of the fabric is 3 to 15% or less, and the difference in the crimp ratio between the warp yarn aligned at the sides and the warp yarn aligned in the center is 5.0% or less.

2. The fabric for airbags according to claim 1, wherein the additional yarn has a boiling-water shrinkage rate less than that of a base yarn, which constitutes the fabric for airbags, and the difference in the boiling-water shrinkage rate between the additional yarn and the base yarn is 0.8% or more.

3. A method for producing the fabric for airbags of claim 1, comprising incorporating, at each side in the width direction of the fabric, at least two additional yarns in which the boiling-water shrinkage rate of a base yarn is greater than the boiling-water shrinkage rate of the additional yarn, and the difference in the boiling-water shrinkage rate between the base yarn and the additional yarn is 0.8% or more, and then performing scouring and shrinking.

Description

DESCRIPTION OF EMBODIMENTS

[0018] The fabric for airbags according to the present invention is a woven fabric formed from a synthetic-fiber multifilament. The synthetic-fiber multifilament that constitutes the fabric for airbags has a total fineness of preferably 200 to 600 dtex, and more preferably 300 to 550 dtex. A total fineness of 200 dtex or more, due to the elimination of the need for overly increasing the weaving density, reduces an excessive increase in binding force of the warp and weft yarn, thus making it easier for the packageability in an airbag module to fall within an appropriate range. A total fineness of 600 dtex or less makes it easier to reduce an excessive increase in rigidity of the yarn that constitute the woven fabric. A synthetic-fiber multifilament having a total fineness within the range of 200 dtex or more and 600 dtex or less is preferable because such a synthetic-fiber multifilament makes it easier to obtain a fabric for airbags that is moderately flexible and thus excellent in packageability in a module.

[0019] In the present invention, the total fineness of synthetic-fiber multifilament that constitutes the fabric for airbags is determined as follows. The warp and weft yarns of a fabric obtained through a dry-finishing process are each removed from the fabric, and measurement is performed in accordance with JIS L 1013 (2010), 8.3.1. Specifically, a sample with a length of cm is accurately taken with an initial tension applied. The absolute dry mass is measured, and the fineness based on corrected weight (dtex) is calculated using the following formula. The average of five measurements is determined to be the total fineness.

F0=10000m/0.9(100+R0)/100 [0020] F0: Fineness based on corrected weight (dtex) [0021] m: Absolute dry mass of sample (g) [0022] R0: Official moisture content (8)

[0023] The fabric for airbags according to the present invention is woven with base yarn (warp and weft yarns that constitute the fabric for airbags) and woven by further incorporating additional yarn having specific physical properties. The boiling-water shrinkage rate of the additional yarn is preferably less than the boiling-water shrinkage rate of the base yarn, which constitutes the airbag fabric. In particular, the boiling-water shrinkage rate of the additional yarn is preferably less than the boiling-water shrinkage rate of the base yarn (warp yarn).

[0024] In order to suppress flaring due to shrinkage at the sides in the width direction of the fabric during scouring and shrinking and during drying, the difference in the boiling-water shrinkage rate between the base yarn and the additional yarn is preferably 0.8 to 20%, more preferably 1.5 to 15%, and particularly preferably 4 to 12%. A difference in the boiling-water shrinkage rate between the base yarn and the additional yarn of below 0.8% reduces the effect of suppressing deformation due to shrinkage, whereas a difference in the boiling-water shrinkage rate between the base yarn and the additional yarn exceeding 20% adversely affects strength, air permeability, etc. since the base yarn shrinks too much, thereby damaging the weave structure.

[0025] The boiling-water shrinkage rate of the base yarn and the additional yarn used in the fabric for airbags according to the present invention may be such that boiling-water shrinkage rate of the base yarn>boiling-water shrinkage rate of the additional yarn, and it is effective that the difference between them is 0.8% or more. The additional yarn may be multifilament yarn, monofilament yarn, false-twisted yarn, or crimped yarn. The material thereof can be nylon 66 fiber, nylon 6 fiber, polyester fiber, etc. Typically, nylon 66 fiber is often used for the base yarn for the fabric for airbags. Since polyester fiber has a boiling-water shrinkage rate lower than that of nylon 66 fiber, it is preferable to use nylon 66 fiber for the base yarn and polyester fiber for the additional yarn.

[0026] In the present invention, the weaving density is measured in accordance with JIS L 1096 (2010), 8.6.1.

[0027] More specifically, a sample is placed on a flat table, and unnatural wrinkles and tension are removed. Then, the number of warp yarns and the number of weft yarns in a 2.54-cm section at five different points are counted, and the average of each of them in terms of the unit length is calculated to determine the weaving density.

[0028] In the present invention, the boiling-water shrinkage rate of the original yarn is measured in accordance with dimensional change rate by boiling water, filament dimensional change rate (method B), specified in JIS L 1013 (2010). Specifically, the boiling-water shrinkage rate is measured as follows. An initial tension is applied to a sample, and two points 500 mm apart are marked. The initial tension is then removed, and the sample is immersed in hot water at 100 C. for 30 minutes. The sample is then taken out, and water is gently wiped away with blotting paper or a cloth. The sample is air-dried, and then the initial tension is applied again. The length between the two points is measured, and the dimensional change rate by boiling water (%) is calculated using the following formula. The average of three measurements is determined to be the boiling-water shrinkage rate.

L=(L500)/500100 [0029] L: Boiling-water shrinkage rate (3) [0030] L: Length between two points (mm)

[0031] The material of the synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention is not particularly limited, and can be selected from a wide range of materials. To meet the characteristics described above, while taking economic efficiency into account, it is preferable to use a multifilament composed of a polyamide based-resin such as nylon 6, nylon 66, or nylon 46, or a multifilament composed of a polyester-based resin that contains mainly polyethylene terephthalate.

[0032] The synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention may contain various additives that are typically used for improving the productivity or characteristics in the production process for the original yarn or in the production process for the fabric. The synthetic-fiber multifilament that constitutes the fabric for airbags according to the present invention may contain, for example, at least one member selected from the group consisting of heat stabilizers, antioxidants, light stabilizers, lubricants, antistatic agents, plasticizers, thickening agents, pigments, and flame retardants.

[0033] The number of additional yarns in the fabric for airbags according to the present invention is not particularly limited. As the number increases, the effect is likely to increase. Considering the operability etc., the number of additional yarns is preferably 2 to 12. However, since each production facility varies, the number of additional yarns is not limited as long as the operability and quality are not impaired.

[0034] The width of the fabric for airbags according to the present invention is not particularly limited; however, the greater the width, the more likely that flaring will occur. The width of 160 cm or more is effective, and the width of 180 cm or more is particularly effective.

[0035] The flaring reduction technique of the present invention particularly effectively works for a high-density woven fabric. The fabric for airbags according to the present invention preferably has a cover factor of 1800 to 2600, and particularly preferably 2000 to 2500.

[0036] The CF is measured using the following formula:

CF=(A0.9).sup.1/2(W1)+(B0.9).sup.1/2(W2)

wherein A and B indicate the thickness of warp and weft yarn (dtex), and W1 and W2 indicate a warp weaving density and a weft weaving density (yarns/2.54 cm).

[0037] The structure of the woven fabric of the fabric for airbags according to the present invention is not particularly limited and can be a plain weave, a twill weave, a sateen weave, or a variation of these weaving patterns.

[0038] In the fabric for airbags according to the present invention, a plurality of additional yarns having a difference in the boiling-water shrinkage rate from that of the base yarn of 0.8% or more (boiling-water shrinkage rate of the base yarn>boiling-water shrinkage rate of the additional yarns) are incorporated into the selvages. Accordingly, in the fabric for airbags comprising unremoved fringe at both sides in the width direction of the fabric, the difference in the crimp ratio between the warp yarn aligned in the center in the width direction of the fabric and the warp yarn aligned at the sides in the width direction of the fabric is 5.0% or less, thereby suppressing flaring.

[0039] Furthermore, the fabric for airbags according to the present invention can be further coated, as necessary, with silicone resin or the like, which can further improve low air permeability. Such a fabric can be effectively used as a fabric for coated airbags.

EXAMPLES

[0040] The structure and effect of the present invention are described below in detail with reference to Examples.

Measurement of Crimp Ratio

[0041] The crimp ratio was measured in accordance with the method specified in JIS L 1096, 8.7, method B.

[0042] As samples, ten yarns were taken from the center in the width direction of the fabric. Additionally, from the sides in the width direction of the fabric, ten base yarns, excluding the additional yarn, were taken from each of the left and right sides at the endmost in the width direction. Then, the average of the center in the width direction of the fabric and the average of the sides in the width direction of the fabric were determined. The crimp ratio was compared between the right side in the width direction of the fabric and the center in the width direction of the fabric, and between the left side in the width direction of the fabric and the center in the width direction of the fabric, and the greater difference was determined to be the difference in the crimp ratio.

Weaving Density of Fabric

[0043] The measurement was performed in accordance with JIS L 1096 (2010), 8.6.1. More specifically, a sample was placed on a flat table, and unnatural wrinkles and tension were removed. The number of warp and weft yarns in a 2.54-cm section was counted and determined to be the density. The number of measurements was at least n=35 at 5-cm intervals from the base of the fringe, and both vertical and horizontal densities were measured. The difference therebetween was calculated at each measurement point.

Example 1

[0044] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144f and a boiling-water shrinkage rate of 8.4% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern by incorporating two additional yarns having a boiling-water shrinkage rate of 0.3% into each side (four additional yarns in total) with a water-jet loom so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98 C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130 C., and the second step was adjusted to have a temperature T2 of 135 C.

Example 2

[0045] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144f and a boiling-water shrinkage rate of 8.4% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern by incorporating 10 additional yarns having a boiling-water shrinkage rate of 0.3% into each side (20 additional yarns in total) with a water-jet loom so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98 C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130 C., and the second step was adjusted to have a temperature T2 of 135 C.

Example 3

[0046] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144f and a boiling-water shrinkage rate of 8.4% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern by incorporating 10 additional yarns having a boiling-water shrinkage rate of 6.8% into each side (20 additional yarns in total) with a water-jet loom so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98 C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130 C., and the second step was adjusted to have a temperature T2 of 135 C.

Comparative Example 1

[0047] Using a nylon 66 filament original yarn having a fineness of 470 dtex/144f and a boiling-water shrinkage rate of 8.4% (the monofilament cross-section was round) in the weft and warp direction of the base yarn, weaving was performed in a plain weave pattern with a water-jet loom so that the weft and warp both had a weaving density of 53.0 yarns/2.54 cm. Thereafter, the fabric was passed through a hot-water shrinkage tank at 98 C. without drying and then continuously passed through a dry-finishing process using a two-step suction drum dryer in which the first step was adjusted to have a temperature T1 of 130 C., and the second step was adjusted to have a temperature T2 of 135 C.

TABLE-US-00001 TABLE 1 Total Boiling-water Boiling-water Difference in warp crimp ratio number of shrinkage shrinkage of Between Between additional rate of additional Warp crimp ratio (%) center and center and yarns base yarn yarn Left side Right side left side of right side (yarns) (%) (%) of fabric Center of fabric fabric of fabric Ex. 1 4 8.4 0.3 5.5 9.9 5.9 4.3 3.9 Ex. 2 20 8.4 0.3 7.1 10.4 7.6 3.3 2.8 Ex. 3 20 8.4 6.8 6.3 10.1 6.0 3.8 3.7 Comp. Ex. 1 0 8.4 4.2 9.7 4.3 5.5 5.4

INDUSTRIAL APPLICABILITY

[0048] The present invention can improve the quality of fabric for airbags by reducing the difference in the crimp ratio between the center in the width direction of the fabric and the sides in the width direction of the fabric, and contributes to reduction in costs in the airbag manufacturing industry.