METHOD FOR DISASSEMBLING AND SEPARATING WASTE LITHIUM-ION BATTERY

Abstract

A method for disassembling and separating a waste lithium-ion battery comprises: directly tearing a battery pack or a cell of the waste lithium-ion battery with water and electricity without discharging after removing a housing, then performing first wet screening, directly performing wet degumming without drying after recovering an electrolyte and removing iron by magnetic separation, then performing first crushing with water, third wet screening and second crushing with water after performing second wet screening, and finally performing jigging separation to obtain copper powder, aluminum powder, positive and negative electrode materials, plastic powder and separator pulp.

Claims

1. A method for disassembling and separating a waste lithium-ion battery, comprising: putting a battery pack or a cell with a voltage within 36 V of the waste lithium-ion battery into a roller tearing machine to tear with electricity directly under protection of water with a mass ratio of 1 to 10 times or directly under a water spraying condition without lowering or eliminating the voltage by physical and chemical means after removing a housing, then performing first wet screening, directly performing wet degumming without drying after recovering an electrolyte and removing iron by two-stage magnetic separation, then performing first crushing with water, third wet screening and second crushing with water after performing second wet screening, and finally performing jigging separation to obtain copper powder, aluminum powder, positive and negative electrode materials, plastic powder and separator pulp.

2. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the battery pack or the cell is put into the roller tearing machine to tear with electricity directly under protection of water with a mass ratio of 2 to 9 times or directly under the water spraying condition, so as to be torn into pieces smaller than 15×15 mm.

3. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the first wet screening comprises: passing the torn mixture pieces through a 150-mesh drum screen under push of water to perform the wet screening, wherein undersize materials are the water, the electrolyte and the positive and negative electrode materials falling off in a tearing process; and an oversize material is a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

4. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the recovering the electrolyte comprises: performing oil-water separation on undersize materials of the wet screening, a light liquid being the electrolyte, and a heavy liquid and a precipitate being the water and rough positive and negative electrode materials 1, performing separation by a plate-and-frame filter press, a filter cake being the rough positive and negative electrode materials 1, and a filtrate returning to the section as tearing water, and packing the electrolyte by a closed iron drum to store in a warehouse and sent to a qualified unit for treatment as the electrolyte.

5. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the removing the iron by magnetic separation comprises: performing two-stage magnetic separation on an oversize material of the wet screening, and separating an iron sheet of the torn battery pack and cell to package and put in storage, wherein the two-stage magnetic separation is intended to allow other nonmagnetic substances carried by the iron sheet in first-stage magnetic separation to produce a shift under an action of the water when converting to second-stage magnetic separation, so that the nonmagnetic substances automatically break away from the carrying to be separated from the iron sheet.

6. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the wet degumming comprises: adding a degumming agent to the pieces of the torn battery according to a volume ratio of 5% to 15% in a degumming barrel to stir and soak for 5 minutes to 60 minutes, so that the positive and negative electrode materials are separated from a copper foil and an aluminum foil or adhesion thereof fails, thus being easy to peel off.

7. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the second wet screening comprises: passing materials subjected to wet degumming through the 150-mesh drum screen, wherein undersize materials are a sol solution and the separated positive and negative electrode materials, and performing filter-pressing by a plate-and-frame filter press, a filter cake being rough positive and negative electrode materials 3, and a filtrate being water containing a degumming agent and returning to supplement with a certain amount of degumming agent for recycling, wherein an oversize material is a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, plastic, separator paper, and the like, and is crushed and screened once.

8. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the third wet screening comprises: passing materials crushed with water for the first time through the 150-mesh drum screen, wherein undersize materials are the positive and negative electrode materials and the water, and performing filter-pressing by a plate-and-frame filter press, a filter cake being rough positive and negative electrode materials 2, and a filtrate being water and returning to crushing and screening procedures of the section for recycling, wherein oversize materials are the copper powder, the aluminum powder, the plastic powder, the separator pulp, and positive and negative electrode material powder.

9. The method for disassembling and separating the waste lithium-ion battery according to claim 1, wherein the jigging separation comprises: feeding an oversize material crushed with water for the second time to a beneficiation jigger together with rough positive and negative electrode materials 1, rough positive and negative electrode materials 2 and rough positive and negative electrode materials 3, jigging with water to re-separate, separating the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp, and passing the positive and negative electrode materials, the plastic powder and the separator pulp through a plate-and-frame filter press respectively for filter-pressing, filter cakes being the positive and negative electrode materials, the plastic powder and the separator pulp, and being packaged and put in storage, and a filtrate being water and returning to a crushing procedure of the section as adding water for recycling.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

Description of the Drawings

[0024] FIG. 1 is a process flow chart of the present invention.

OPTIMAL EMBODIMENTS FOR IMPLEMENTING THE INVENTION

Optimal Implementations of the Invention

[0025] A method for disassembling and separating a waste lithium-ion battery comprises the following steps. In a, coding and registration are performed: a recycled waste lithium-ion battery is coded and registered.

[0026] In step b, tearing with electricity is performed: a waste lithium-ion battery with a model of 18650 and a weight of 20 kg is placed in water to be submerged, torn by a roller and cut into pieces of 15×15 mm.

[0027] In step c, screening with water is performed: wet screening is performed on the torn mixture pieces by a 150-mesh screen under push of water, wherein undersize materials are water, an electrolyte, and positive and negative electrode materials falling off in a tearing process; and an oversize material is a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0028] In step d, the electrolyte is recovered: oil-water separation is performed on the undersize materials obtained by screening with water in the step c, a light liquid is the electrolyte, with a volume of 1,150 mL measured by a measuring cylinder, and a heavy liquid and a precipitate are the water and rough positive and negative electrode materials 1, separation is performed by a suction filter, and dry power after drying is 325.1 g.

[0029] In step e, iron is removed by magnetic separation: iron in the piece mixture of the oversize material of the drum screen obtained by screening with water in the step c is separated with a magnet, and a waste iron sheet has a weight of 4,792.1 g.

[0030] In step f, wet degumming is performed: the material after iron removal by magnetic separation is a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and is put into a 0.2 m.sup.3 reaction barrel, added with 0.15 m.sup.3 of water, added with 0.01 m.sup.3 of tetrahydrofuran, and stirred for 15 minutes, and then there is an obvious foaming phenomenon on surfaces of the positive and negative electrode materials. Second wet screening is performed by a 150-mesh screen, wherein undersize materials are a sol solution and the separated positive and negative electrode materials, and suction filtration is performed by a suction filter, and a filter cake is rough positive and negative electrode materials 3, with a weight of 1,425.8 g, wherein an oversize material (containing 32.7% water) is a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and is crushed with water.

[0031] In step g, crushing and screening with water are performed: 14,833.3 g of the piece mixture of the copper foil and the aluminum foil adhered with the positive and negative electrode materials, the plastic, the separator paper, and the like (containing 16.2% water) after the second wet screening in the step f is added with 10 kg of water and crushed to be lower than 200 meshes in a crusher, and then wet screening is performed by a 150-mesh screen, wherein undersize materials are the positive and negative electrode materials and the water. Filter-pressing is performed by a suction filter, and a filter cake is rough positive and negative electrode materials 2, with a weight of 4,028.7 g (containing 25.65% water), wherein an oversize material is continuously added with water and crushed to be 200 meshes, in which the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp are separated by a vibrating jigger together with the rough positive and negative electrode materials 1, the rough positive and negative electrode materials 2 and the rough positive and negative electrode materials 3. Suction filtration is performed on the positive and negative electrode materials, the plastic powder and the separator pulp respectively by a suction filter, and filter cakes are dried, and comprise 1,612.4 g of copper powder, 3,004.9 g of aluminum powder, 6,412.1 g of positive and negative electrode materials, and 4,172.6 g of plastic powder and separator pulp respectively.

DETAILED DESCRIPTION

Implementations of the Invention

[0032] In order to understand the present invention more clearly, the present invention is further described in detail hereinafter by specific embodiments with reference to FIG. 1.

[0033] Implementation 1: A method for disassembling and separating a waste lithium-ion battery comprises: directly tearing a battery pack or a cell of the waste lithium-ion battery with water and electricity without discharging after removing a housing, then performing first wet screening, directly performing wet degumming without drying after recovering an electrolyte and removing iron by magnetic separation, then performing first crushing with water, third wet screening and second crushing with water after performing second wet screening, and finally performing jigging separation to obtain copper powder, aluminum powder, positive and negative electrode materials, plastic powder and separator pulp.

[0034] The tearing without discharging refers to: tearing a battery pack or a cell with a voltage within 36 V without lowering or eliminating the voltage by physical and chemical means. That is to say, the battery needs to be discharged before disassembling in the prior art, but the battery can be directly disassembled without discharging in the present invention.

[0035] The directly tearing with water and electricity comprises: putting the battery pack or the cell of the waste lithium-ion battery into a roller tearing machine to tear with electricity directly under a water spraying condition without discharging after removing a housing, so as to be torn into pieces smaller than 15×15 mm. The piece is a mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, an iron sheet, a plastic sheet, a separator paper sheet, and the like with water.

[0036] The first wet screening comprises: passing the torn mixture pieces through a 150-mesh drum screen under push of water to perform the wet screening, wherein undersize materials are the water, the electrolyte and the positive and negative electrode materials falling off in a tearing process; and an oversize material is a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0037] The recovering the electrolyte comprises: performing oil-water separation on undersize materials of the wet screening, a light liquid being the electrolyte, and a heavy liquid and a precipitate being water and rough positive and negative electrode materials 1, performing separation by a plate-and-frame filter press, a filter cake being the rough positive and negative electrode materials 1, and a filtrate returning to the section as tearing water, and packing the electrolyte by a closed iron drum to store in a warehouse and sent to a qualified unit for treatment as the electrolyte.

[0038] The removing the iron by magnetic separation comprises: performing two-stage magnetic separation on an oversize material of the wet screening, and separating an iron sheet of the torn battery pack and cell to package and put in storage, wherein the two-stage magnetic separation is intended to allow other nonmagnetic substances carried by the iron sheet in first-stage magnetic separation to produce a shift under an action of the water when converting to second-stage magnetic separation, so that the nonmagnetic substances automatically break away from the carrying to be separated from the iron sheet.

[0039] The wet degumming comprises: soaking and stirring the pieces of the torn battery with a degumming agent in a degumming barrel for a certain time, so that the positive and negative electrode materials are separated from a copper foil and an aluminum foil or adhesion thereof fails, thus being easy to peel off.

[0040] Further, the wet degumming comprises: allowing a material after iron removal by magnetic separation, which is a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, to enter the degumming barrel, adding a certain concentration of degumming agent, soaking and stirring for a certain time, so that the positive and negative electrode materials are separated from the copper foil and the aluminum foil, or positive and negative electrode films are foamed and degummed.

[0041] The degumming agent is an organic solvent, such as one or a mixture of multiple of acetone, tetrahydrofuran, N-dimethylacetamide and dimethyl sulfoxide, preferably the tetrahydrofuran.

[0042] The certain concentration in the wet degumming step is a volume ratio of 1% to 20%, preferably 5% to 15%, and 10%.

[0043] The soaking and stirring for a certain time in the wet degumming step refers to soaking and stirring for 5 minutes to 60 minutes, preferably 10 minutes to 50 minutes, 20 minutes to 40 minutes, and 30 minutes, at a stirring speed of 15 rpm to 60 rpm, preferably 20 rpm to 55 rpm, 25 rpm to 50 rpm, and 35 rpm to 45 rpm.

[0044] The second wet screening comprises: passing materials subjected to wet degumming through the 150-mesh drum screen, wherein undersize materials are a sol solution and the separated positive and negative electrode materials, and performing filter-pressing by a plate-and-frame filter press, a filter cake being rough positive and negative electrode materials 3, and a filtrate being water containing a degumming agent and returning to supplement with a certain amount of degumming agent for recycling, wherein an oversize material is a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, plastic, separator paper, and the like, and is crushed and screened once.

[0045] The crushing with water for the first time comprises: adding water with a mass ratio of 3 to 5 times to the oversize material after the second wet screening, and crushing to be lower than 200 meshes.

[0046] The third wet screening comprises: passing materials crushed with water for the first time through the 150-mesh drum screen, wherein undersize materials are the positive and negative electrode materials and the water, and performing filter-pressing by a plate-and-frame filter press, a filter cake being rough positive and negative electrode materials 2, and a filtrate being water and returning to crushing and screening procedures of the section for recycling, wherein oversize materials are the copper powder, the aluminum powder, the plastic powder, the separator pulp, positive and negative electrode material powder, and the like.

[0047] The crushing with water for the second time comprises: continuously adding water to the oversize material after the third wet screening, and crushing to be lower than 200 meshes.

[0048] The jigging separation comprises: feeding an oversize material crushed with water for the second time to a beneficiation jigger together with rough positive and negative electrode materials 1, rough positive and negative electrode materials 2 and rough positive and negative electrode materials 3, jigging with water to re-separate, separating the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp, and passing the positive and negative electrode materials, the plastic powder and the separator pulp through a plate-and-frame filter press respectively for filter-pressing, filter cakes being the positive and negative electrode materials, the plastic powder and the separator pulp, and being packaged and put in storage, and a filtrate being water and returning to a crushing procedure of the section as adding water for recycling.

[0049] Embodiment 1: A method for disassembling and separating a waste lithium-ion battery comprised the following steps. In a, coding and registration were performed: a recycled waste lithium-ion battery was coded and registered.

[0050] In step b, a housing was removed: a housing of a battery with a battery number of H-52201 was removed, and one of seven battery packs, with a weight of 1,958.0 g, was taken out.

[0051] In step c, tearing with water and electricity was performed: the battery was directly placed in water to be submerged without discharging, and cut with a blade into pieces smaller than 15×15 mm.

[0052] In step d, screening with water was performed: wet screening was performed on the torn mixture pieces by a 150-mesh screen, wherein undersize materials were water, an electrolyte, and positive and negative electrode materials falling off in a tearing process; and an oversize material was a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0053] In step e, the electrolyte was recovered: oil-water separation was performed on the undersize materials obtained by wet screening in the step d through a separating funnel, a light liquid was the electrolyte, with a volume of 120 mL measured by a measuring cylinder, and a heavy liquid and a precipitate were the water and rough positive and negative electrode materials 1, separation was performed by a suction filter, and dry power after drying was 47.46 g.

[0054] In step f, iron was removed by magnetic separation: iron in the piece mixture of the oversize material of the drum screen obtained by wet screening in the step d was separated with a magnet, which was 0.0 g.

[0055] In step g, wet degumming was performed: the material after iron removal by magnetic separation was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was put into a 5000 mL beaker, added with 3000 mL of water, added with 150 mL of tetrahydrofuran, and stirred for 30 minutes, and then the positive and negative electrode materials showed an obvious foaming phenomenon. Second wet screening was performed by a 150-mesh screen, wherein undersize materials were a sol solution and the separated positive and negative electrode materials, and suction filtration was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 3, with a weight of 324.25 g, wherein an oversize material (containing 41.4% water) was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was crushed with water.

[0056] In step h, crushing and screening with water were performed: 2,060.2 g of the piece mixture of the copper foil and the aluminum foil adhered with the positive and negative electrode materials, the plastic, the separator paper, and the like (containing 21% water) after the second wet screening in the step g was added with 10 kg of water and crushed to be lower than 200 meshes in a crusher, and then third wet screening was performed by a 150-mesh screen, wherein undersize materials were the positive and negative electrode materials and the water. Filter-pressing was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 2, with a weight of 536.91 g (containing 38.5% water), wherein 1,944.2 g of oversize material was continuously added with 10 kg of water and crushed to be 200 meshes, in which the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp were separated by a vibrating jigger together with the rough positive and negative electrode materials 1, the rough positive and negative electrode materials 2 and the rough positive and negative electrode materials 3. Suction filtration was performed on the positive and negative electrode materials, the plastic powder and the separator pulp respectively by a suction filter, and filter cakes were dried, and comprised 228.60 g of copper powder, 428.44 g of aluminum powder, 943.10 g of positive and negative electrode materials, and 251.40 g of plastic powder and separator pulp respectively.

[0057] Embodiment 2: A method for disassembling and separating a waste lithium-ion battery comprised the following steps. In a, coding and registration were performed: a recycled waste lithium-ion battery was coded and registered.

[0058] In step b, tearing with electricity was performed: a housing of a waste lithium-ion battery with a serial number of H-52187 was removed, and seven battery packs were all taken out, with a weight of 13,867 g, placed in water to be submerged, torn by a hobbing cutter and cut into pieces smaller than 15×15 mm.

[0059] In step c, screening with water was performed: wet screening was performed on the torn mixture pieces by a 150-mesh screen under push of water, wherein undersize materials were water, an electrolyte, and positive and negative electrode materials falling off in a tearing process; and an oversize material was a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0060] In step d, the electrolyte was recovered: oil-water separation was performed on the undersize materials obtained by screening with water in the step c, a light liquid was the electrolyte, with a volume of 835 mL measured by a measuring cylinder, and a heavy liquid and a precipitate were the water and rough positive and negative electrode materials 1, separation was performed by a suction filter, and dry power after drying was 355.1 g.

[0061] In step e, iron was removed by magnetic separation: iron in the piece mixture of the oversize material of the drum screen obtained by wet screening in the step c was separated with a magnet, which was 0.0 g.

[0062] In step f, wet degumming was performed: the material after iron removal by magnetic separation was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was put into a 0.1 m.sup.3 reaction barrel, added with 0.5 m.sup.3 of water, added with 12.5 kg of tetrahydrofuran and 12.5 kg of N-dimethylacetamide, and stirred for 10 minutes, and then there was an obvious foaming phenomenon on surfaces of the positive and negative electrode materials. Second wet screening was performed by a 150-mesh screen, wherein undersize materials were a sol solution and the separated positive and negative electrode materials, and suction filtration was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 3, with a weight of 1,075.3 g, wherein an oversize material (containing 38.1% water) was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was crushed with water.

[0063] In step h, crushing and screening with water were performed: 21,150 g of the piece mixture of the copper foil and the aluminum foil adhered with the positive and negative electrode materials, the plastic, the separator paper, and the like (containing 15% water) after the second wet screening in the wet degumming step was added with 10 kg of water and crushed to be lower than 200 meshes in a crusher, and then wet screening was performed by a 150-mesh screen, wherein undersize materials were the positive and negative electrode materials and the water. Filter-pressing was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 2, with a weight of 2,701.8 g (containing 32.6% water), wherein 15, 840.1 g of oversize material (containing 15% water) was continuously added with 10 kg of water and crushed to be 200 meshes, in which the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp were separated by a vibrating jigger together with the rough positive and negative electrode materials 1, the rough positive and negative electrode materials 2 and the rough positive and negative electrode materials 3. Suction filtration was performed on the positive and negative electrode materials, the plastic powder and the separator pulp respectively by a suction filter, and separated substances were dried, and comprised 1,596.3 g of copper powder, 2,993.5 g of aluminum powder, 6,580.4 g of positive and negative electrode materials, and 1,861.5 g of plastic powder and separator pulp respectively.

[0064] Embodiment 3: A method for disassembling and separating a waste lithium-ion battery comprised the following steps. In a, coding and registration were performed: a recycled waste lithium-ion battery was coded and registered.

[0065] In step b, tearing with electricity was performed: a waste lithium-ion battery with serial numbers of H-50321 and H-57106 and a weight of 68.6 kg was placed in water together with a housing to be submerged, torn by a roller and cut into pieces smaller than 15×15 mm.

[0066] In step c, screening with water was performed: wet screening was performed on the torn mixture pieces by a 150-mesh screen under push of water, wherein undersize materials were water, an electrolyte, and positive and negative electrode materials falling off in a tearing process; and an oversize material was a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0067] In step d, the electrolyte was recovered: oil-water separation was performed on the undersize materials obtained by screening with water in the step c, a light liquid was the electrolyte, with a volume of 1,600 mL measured by a measuring cylinder, and a heavy liquid and a precipitate were the water and rough positive and negative electrode materials 1, separation was performed by a suction filter, and dry power after drying was 710.4 g.

[0068] In step e, iron was removed by magnetic separation: iron in the piece mixture of the oversize material of the drum screen obtained by wet screening in the step c was separated with a magnet, and a waste iron sheet had a weight of 41.88 kg.

[0069] In step f, wet degumming was performed: the material after iron removal by magnetic separation was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was put into a 0.2 m.sup.3 reaction barrel, added with 0.15 m.sup.3 of water, added with 0.01 m.sup.3 of tetrahydrofuran, and stirred for 30 minutes, and then there was an obvious foaming phenomenon on surfaces of the positive and negative electrode materials. Second wet screening was performed by a 150-mesh screen, wherein undersize materials were a sol solution and the separated positive and negative electrode materials, and suction filtration was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 3, with a weight of 2,112.3 g, wherein an oversize material (containing 35.4% water) was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was crushed with water.

[0070] In step g, crushing and screening with water were performed: 40,915.4 g of the piece mixture of the copper foil and the aluminum foil adhered with the positive and negative electrode materials, the plastic, the separator paper, and the like (containing 14.1% water) after the second wet screening in the wet degumming step was added with 10 kg of water and crushed to be lower than 200 meshes in a crusher, and then wet screening was performed by a 150-mesh screen, wherein undersize materials were the positive and negative electrode materials and the water. Filter-pressing was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 2, with a weight of 8,287.6 g (containing 31.5% water), wherein an oversize material was continuously added with 10 kg of water and crushed to be 200 meshes, in which the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp were separated by a vibrating jigger together with the rough positive and negative electrode materials 1, the rough positive and negative electrode materials 2 and the rough positive and negative electrode materials 3. Suction filtration was performed on the positive and negative electrode materials, the plastic powder and the separator pulp respectively by a suction filter, and filter cakes were dried, and comprised 3,192.8 g of copper powder, 6,008.1 g of aluminum powder, 13,155.4 g of positive and negative electrode materials, and 3,720.9 g of plastic powder and separator pulp respectively.

[0071] Embodiment 4: A method for disassembling and separating a waste lithium-ion battery comprised the following steps. In a, coding and registration were performed: a recycled waste lithium-ion battery was coded and registered.

[0072] In step b, tearing with electricity was performed: a waste lithium-ion battery with a model of 18650 and a weight of 20 kg was placed in water to be submerged, torn by a roller and cut into pieces of 15×15 mm.

[0073] In step c, screening with water was performed: wet screening was performed on the torn mixture pieces by a 150-mesh screen under push of water, wherein undersize materials were water, an electrolyte, and positive and negative electrode materials falling off in a tearing process; and an oversize material was a piece mixture of a copper foil and an aluminum foil containing the positive and negative electrode materials, an iron shell, a plastic housing, separator paper, and the like.

[0074] In step d, the electrolyte was recovered: oil-water separation was performed on the undersize materials obtained by screening with water in the step c, a light liquid was the electrolyte, with a volume of 1,150 mL measured by a measuring cylinder, and a heavy liquid and a precipitate were the water and rough positive and negative electrode materials 1, separation was performed by a suction filter, and dry power after drying was 325.1 g.

[0075] In step e, iron was removed by magnetic separation: iron in the piece mixture of the oversize material of the drum screen obtained by screening with water in the step c was separated with a magnet, and a waste iron sheet had a weight of 4,792.1 g.

[0076] In step f, wet degumming was performed: the material after iron removal by magnetic separation was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was put into a 0.2 m.sup.3 reaction barrel, added with 0.15 m.sup.3 of water, added with 0.01 m.sup.3 of tetrahydrofuran, and stirred for 15 minutes, and then there was an obvious foaming phenomenon on surfaces of the positive and negative electrode materials. Second wet screening was performed by a 150-mesh screen, wherein undersize materials were a sol solution and the separated positive and negative electrode materials, and suction filtration was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 3, with a weight of 1,425.8 g, wherein an oversize material (containing 32.7% water) was a piece mixture of a copper foil and an aluminum foil adhered with the positive and negative electrode materials, plastic, separator paper, and the like, and was crushed with water.

[0077] In step g, crushing and screening with water were performed: 14,833.3 g of the piece mixture of the copper foil and the aluminum foil adhered with the positive and negative electrode materials, the plastic, the separator paper, and the like (containing 16.2% water) after the second wet screening in the step f was added with 10 kg of water and crushed to be lower than 200 meshes in a crusher, and then wet screening was performed by a 150-mesh screen, wherein undersize materials were the positive and negative electrode materials and the water. Filter-pressing was performed by a suction filter, and a filter cake was rough positive and negative electrode materials 2, with a weight of 4,028.7 g (containing 25.65% water), wherein an oversize material was continuously added with water and crushed to be 200 meshes, in which the copper powder, the aluminum powder, the positive and negative electrode materials, the plastic powder and the separator pulp were separated by a vibrating jigger together with the rough positive and negative electrode materials 1, the rough positive and negative electrode materials 2 and the rough positive and negative electrode materials 3. Suction filtration was performed on the positive and negative electrode materials, the plastic powder and the separator pulp respectively by a suction filter, and filter cakes were dried, and comprised 1,612.4 g of copper powder, 3,004.9 g of aluminum powder, 6,412.1 g of positive and negative electrode materials, and 4,172.6 g of plastic powder and separator pulp respectively.

[0078] The roller and the drum screen used in the embodiments of the present invention are both market products produced by Henan Zhengzhou Mining Machinery Co., Ltd., a model number of the roller is 2PG0425 and a model number of the drum screen is GTS-0608.

TABLE-US-00001 TABLE 1 Inspection data sheet of disassembled components of the present invention. Embodiment Embodiment Embodiment Embodiment Weight of component (g) 1 2 3 4 Remark Before disassembling 1,958 13,867 68,600 20,000 After disassembling Electrolyte (mL) 120 835 1,600 1,150 Rough positive and negative 47.46 355.1 710.4 325.1 Drying electrode materials 1 Falling-off rate of positive and 5.03 5.4 5.4 5.07 negative electrode materials % Iron 0.0 0.0 41,880 4,792.1 Converting Rough positive and negative 330.2 1821.0 5,745.5 2,995.29 to dry basis electrode materials 2 Falling-off rate of positive and 35.01 26.67 43.67 46.71 negative electrode materials % Rough positive and negative 190.0 665.61 1,364.55 959.56 electrode materials 3 Falling-off rate of positive and 20.14 10.11 10.37 14.96 negative electrode materials % Copper powder 228.60 1,596.3 3,192.8 1,612.4 Aluminum powder 428.44 2,993.5 6,008.1 3,004.9 Positive and negative electrode 943.10 6,580.4 13,155.4 6,412.1g material powder Plastic powder and separator 251.40 1,861.5 3,720.9 4,172.6 pulp Total falling-off rate of positive 60.18 42.18 59.44 66.74 and negative electrode materials % (from tearing to first crushing)

TABLE-US-00002 TABLE 2 Inspection data sheet of ingredients of components in Embodiment 4 of the present invention. Inspection data Positive and Plastic negative and Copper Aluminum electrode separator Name (%) (%) Iron (%) materials (%) (%) Remark Copper powder 97.14 1.81 0.15 0.5 0.5 1. Copper, Aluminum powder 1.45 98.11 0.12 1.0 1.0 aluminum and iron Iron 0.21 0.16 98.15 0.2 1.5 elements are Rough positive and 4.05 5.12 0.6 / / measured by an negative electrode AAS method; and materials 1 2. other elements Rough positive and 6.14 7.21 0.11 / / except copper, negative electrode iron and aluminum materials 2 in the positive and Rough positive and 2.10 2.44 0.09 / / negative electrode negative electrode material powder materials 3 are not measured; Positive and negative 0.56 0.81 0.04 / / electrode material powder Plastic powder and 0.15 0.04 0.08 0.5 / separator pulp

[0079] The above are only the illustrative embodiments of the present invention, and are not intended to limit the present invention in form and in essence. It should be pointed out that, for those of ordinary skills in the technical field, several improvements and supplementations made without departing from the method of the present invention should also be regarded as falling within the scope of protection of the present invention. Those skilled in the art may make some alterations, modifications and equivalent changes by using the above-mentioned technical contents without departing from the spirit and scope of the present invention, which are all equivalent embodiments of the present invention. Meanwhile, any alterations, modifications and evolutions of equivalent changes made to the above embodiments according to the essential technology of the present invention still belong to the scope of protection of the present invention.

INDUSTRIAL APPLICABILITY

[0080] The technology of the present invention has passed the plant trial.