METHOD FOR PRODUCING AT LEAST ONE DEVICE IN COMPRESSIVE STRAINED SEMICONDUCTOR

Abstract

Method for producing a semiconductor device, including: producing, on a first region of a surface layer comprising a first semiconductor and disposed on a buried dielectric layer, a layer of a second compressive strained semiconductor along a first direction; etching a trench through the layer of the second semiconductor forming an edge of a portion of the layer of the second semiconductor oriented perpendicularly to the first direction, and wherein the bottom wall is formed by the surface layer; thermal oxidation forming in the surface layer a semiconductor compressive strained portion along the first direction and forming in the trench an oxide portion; producing, through the surface layer and/or the oxide portion, and through the buried dielectric layer, dielectric isolation portions around an assembly formed of the compressive strained semiconductor portion and the oxide portion; and wherein the first semiconductor is silicon, the second semiconductor is SiGe, and said at least one compressive strained semiconductor portion includes SiGe.

Claims

1. Method for producing at least one semiconductor device, including the implementation of the following steps: producing, on at least a first region of a surface layer comprising a first semiconductor and disposed on a buried dielectric layer of a semiconductor-on-insulator type substrate, a layer of a second semiconductor which is compressive strained at least along a first direction; etching at least one trench through the layer of the second semiconductor forming at least one edge of at least one portion of the layer of the second semiconductor oriented perpendicularly to the first direction, and such that a bottom wall of said at least one trench is formed by the surface layer; thermal oxidation forming simultaneously in the surface layer at least one semiconductor portion which is compressive strained at least along the first direction, and in said at least one trench at least a first oxide portion; producing, at least through the surface layer and/or said at least a first oxide portion, and through the buried dielectric layer, dielectric isolation portions at least around an assembly formed of said at least one compressive strained semiconductor portion and said at least a first oxide portion. and wherein the first semiconductor is silicon, the second semiconductor is SiGe, and said at least one compressive strained semiconductor portion includes SiGe.

2. Method according to claim 1, wherein the steps of the method are implemented such that: several trenches are etched through the layer of the second semiconductor and form all the edges of several portions of the layer of the second semiconductor which are oriented perpendicularly to the first direction, the thermal oxidation forms in the surface layer several compressive strained semiconductor portions electrically isolated from one another by several first oxide portions, and the dielectric isolation portions are produced such that they surround an assembly formed of the compressive strained semiconductor portions and the first oxide portions.

3. Method according to claim 1, wherein the steps of the method are implemented such that: the dielectric isolation portions also surround at least a second region of the surface layer which is protected by a mask during the implementation of the steps of producing the layer of the second semiconductor, etching the trench(es), and of thermal oxidation, and at least one of the dielectric isolation portions electrically isolates the second region of the surface layer with respect to the compressive strained semiconductor portion(s).

4. Method according to claim 1, further including, between the thermal oxidation and producing the dielectric isolation portions: depositing an oxide layer covering at least the first oxide portion(s) and at least second oxide portion formed on the compressive strained semiconductor portion(s) in place of said at least one portion of the layer of the second semiconductor following the implementation of thermal oxidation, and wherein the thickness is greater than that of the compressive strained semiconductor portion(s); chemical mechanical planarization of the oxide layer; removing remaining parts of the oxide layer and the second oxide portion(s).

5. Method according to claim 4, wherein the steps of the method are implemented such that: the dielectric isolation portions also surround at least a second region of the surface layer which is protected by a mask during the implementation of the steps of producing the layer of the second semiconductor, etching the trench(es), and of thermal oxidation, and at least one of the dielectric isolation portions electrically isolates the second region of the surface layer with respect to the compressive strained semiconductor portion(s). and wherein: the oxide layer also covers the mask protecting the second region of the surface layer; the chemical mechanical planarization of the oxide layer is stopped on the mask; removing the remaining parts of the oxide layer and the second oxide portion(s) corresponds to a deoxidation which is controlled and stopped on the compressive strained semiconductor portion(s).

6. Method according to claim 1, wherein the steps of the method are implemented such that: the trenches completely surround, in a plane parallel with the interface between the buried dielectric layer and the surface layer, the or each of the portions of the layer of the second semiconductor; the or each of the compressive strained semiconductor portions is surrounded completely, in said plane, by the first oxide portions.

7. Method according to claim 1, wherein the layer of the second compressive strained semiconductor is produced epitaxially.

8. Method according to claim 1, further including, after producing the dielectric isolation portions, producing at least one P-type FET transistor on and in the compressive strained semiconductor portion and, when the second region of the surface layer is protected by the mask when implementing the steps of producing the layer of the second semiconductor, etching, and of thermal oxidation, producing at least one N-type FET transistor on and in the second region of the surface layer.

9. Method according to claim 1, wherein the steps of the method are implemented successively.

10. Method according to claim 1, further including a step of producing a definitive gate of said at least one semiconductor device implemented after the other steps.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0056] The present invention will be understood more clearly on reading the description of embodiment examples given merely by way of indication and not limitation with reference to the appended drawings wherein:

[0057] FIGS. 1 to 13 represent the steps of a method for producing semiconductor devices according to a particular embodiment.

[0058] Identical, similar, or equivalent parts of the various figures described hereinafter bear the same reference numbers so as to facilitate the transition from one figure to another.

[0059] The various parts shown in the figures are not necessarily represented on a uniform scale, to render the figures more readable.

[0060] The various possibilities (alternative embodiments and embodiments) should be understood as not being mutually exclusive and may be combined with one another.

Detailed Description of Particular Embodiments

[0061] A method for producing semiconductor devices according to a particular embodiment is described hereinafter in relation to FIGS. 1 to 13.

[0062] The method is implemented using a semiconductor-on-insulator, for example SOI, type substrate, including: [0063] a base layer 102 serving as a mechanical base for implementing the different steps of the method, comprising for example silicon and the thickness whereof is for example equal to several hundred microns; [0064] a buried dielectric, or BOX, layer 104 comprising for example SiO.sub.2 and wherein the thickness is for example between about 15 nm and 200 nm; [0065] a surface layer 106 comprising a first semiconductor, for example silicon, and wherein the thickness is for example between about 5 nm and 30 nm.

[0066] The surface layer 106 corresponds to the layer whereon and wherein the semiconductor devices are to be produced. In the particular embodiment described herein, these semiconductor devices correspond to FET transistors, and more particularly MOSFET transistors. PMOS transistors are intended to be produced on and in one of more first regions of the surface layer 106, and the NMOS transistors are intended to be produced on and in one or more second regions of the surface layer 106.

[0067] As a general rule, the semiconductors may correspond to FET type transistors.

[0068] Advantageously, the thickness of the surface layer 106 is suitable for the FET transistors subsequently produced to be of the FDSOI type, and is for example between about 5 nm and 8 nm. The thickness of the surface layer 106 may particularly be selected such that this thickness, which will correspond to the thickness of the channel of the FET transistors, is less than or equal to about one third, or one quarter, of the smallest gate length Lg of the FET transistors. For example, for a gate length Lg=24 nm, the thickness of the surface layer 106 may be selected less than or equal to about 6 nm.

[0069] A hard mask 108 is produced on the surface layer 106. For this, the layer(s) intended to form the hard mask 108 are deposited on the surface layer 106. The hard mask 108 includes for example a stack of a layer of semiconductor oxide such as SiO.sub.2 and a layer of semiconductor nitride such as SiN. Lithography and etching steps are then implemented so as to form, through the hard mask 108, one or more openings 110 defining the pattern of the hard mask 108.

[0070] The structure obtained at this stage of the method is shown in FIG. 1. The opening(s) 110 are produced facing one or more first regions 112 of the surface layer 106 intended to produce the PMOS transistors. The portion(s) of the hard mask 108 cover one or more second regions 114 of the surface layer 106 intended to produce the NMOS transistors. In FIGS. 1 to 3, the first regions 112 are separated symbolically from the second regions 114 by dotted lines.

[0071] A layer 116 of a second compressive strained semiconductor is produced, for example epitaxially, on the first region(s) 112 of the surface layer 106, i.e. in the opening(s) 110 of the hard mask 108 (see FIG. 2). In the particular embodiment described herein, the second semiconductor corresponds to SiGe. Furthermore, due to the different between the lattice parameter of the silicon of the surface layer 106 and the lattice parameter of the SiGe of the layer 116, the SiGe of the layer 116 obtained epitaxially is compressive strained biaxially, i.e. with a compression strain oriented along two perpendicular directions with respect to one another and located in a plane parallel with the interface between the layer 116 and the surface layer 106 (parallel with the axes X and Y in FIG. 2). A first of these two directions, referred to as longitudinal direction, is intended to be parallel with the gate length, i.e. parallel with the direction of current flow in the channel, of the transistors to be produced at this or these first regions 112. In FIGS. 1 to 13, this first direction is parallel with the axis X. A second of these two directions, referred to as transversal direction, is perpendicular to the longitudinal direction. In FIGS. 1 to 13, this second direction is parallel with the axis Y.

[0072] Given that this layer 116 of the second compressive strained semiconductor is intended for the subsequent production of one or more compressive strained semiconductor portions in the surface layer 106 by implementing a thermal oxidation (and more specifically a germanium condensation in the particular embodiment described herein), the thickness of the layer 116 and the composition of the second semiconductor are selected according to the thickness of the surface layer 106, and the thickness and composition sought of the compressive strained semiconductor portion(s). In the particular embodiment described herein, the thickness of the layer 116 and the germanium concentration in the SiGe of the layer 116 are selected according to the thickness of the surface layer 106, as well as the germanium concentration and thickness sought of the compressive strained semiconductor portion(s) to be obtained after implementing thermal oxidation. According to the conservation law of the quantity of germanium atoms, the maximum germanium concentration X.sub.Ge,final that can be obtained in the compressive strained semiconductor portion(s) is:

[00001]$X_{\mathrm{Ge},\mathrm{final}}=X_{\mathrm{Ge},\mathrm{initial}}\frac{t_{\mathrm{SiGe},\mathrm{initial}}}{t_{\mathrm{SiGe},\mathrm{final}}},$

where X.sub.Ge,initial corresponds to the germanium concentration in the SiGe of the layer 116, t.sub.SiGe,initial the thickness of the layer 116, and t.sub.SiGe,final the sought thickness of the compressive strained semiconductor portions. For example, by producing a layer 116 comprising SiGe having a germanium concentration equal to 27% (Si.sub.0.73Ge.sub.0.27) and of thickness equal to 8 nm, on a surface layer 106 of silicon and of thickness equal to 8 nm, the compressive strained semiconductor portions obtained following the germanium condensation will have a thickness equal to 9 nm with a maximum germanium concentration of 24%. However, given that some of the germanium atoms are oxidized and lost, the final germanium concentration obtained is less than this maximum theoretical value. Considering the example described above, the germanium concentration obtained will be between about 22% and 23%.

[0073] As a general rule, the method is implemented such that the semiconductor of the layer 116 is compressive strained along at least a first direction in order to provide, in a p-doped channel of a transistor, a compressive strain which is oriented at least parallel with the longitudinal direction, in order to enhance the mobility of the charge carriers (holes) in the channel.

[0074] After producing the layer 116, this layer 116 is etched so as to form edges 124 of one or more distinct remaining portions 126, these edges 124 being parallel with the transversal direction. Trenches 118 etched through the layer 116 form these edges 124 (see FIG. 3).

[0075] To form these trenches 118, a resin mask 120 is produced on the layer 116 and on the hard mask 108. The mask 120 includes a pattern formed by openings 122 which pass through the entire thickness of the mask 120 and corresponding to the pattern of the trenches 118 to be produced in the layer 116. An etching of the layer 116, for example a dry RIE (reactive-ion etching) etching, is then implemented according to the pattern defined by the mask 120, with stoppage on the surface layer 106.

[0076] These trenches 118 are only etched through the layer 116 and do not pass through the surface layer 106. The bottom walls of the trenches 118 are therefore formed by the surface layer 106.

[0077] In the example in FIG. 3, this etching of the layer 116 forms two portions 126 separated from one another by one of the trenches 118 and each separated from the hard mask 108 by another of the trenches 118. FIG. 4 shows a partial top view of the structure produced after etching the trenches 118.

[0078] The width of each of the trenches 118, symbolized by an arrow in FIG. 3 and which corresponds to the dimension of the trench 118, in the plane parallel with the interface between the layer 116 and the surface layer 106, which is perpendicular with respect to the edge(s) 124 formed by said trench 118, is advantageously the smallest possible, but is limited by the capacity of the lithography equipment used. This width is for example equal to 35 nm.

[0079] In the particular configuration visible in FIGS. 3 and 4, three trenches 118 are etched to form two portions 126. According to an alternative embodiment, it is possible to etch a greater number of trenches 118 parallel with one another, in order to form a greater number of portions 126 from the layer 116.

[0080] Alternatively, it is also possible for the trenches 118 to be etched only between the portions 126 and not between the portions 126 and the hard mask 108.

[0081] According to a further alternative embodiment, it is also possible for a single portion 126 to be formed in the layer 116, with in this case at least one of the two edges 124 of the portion 126 being formed by a trench 118.

[0082] After this etching, the mask 120 is removed.

[0083] A thermal oxidation is then implemented (see FIG. 5).

[0084] This thermal oxidation makes it possible to carry out a condensation of the germanium present in the SiGe of the portions 126. The germanium atoms present in the portions 126 migrate into the parts of the first region(s) 112 of the surface layer 106 covered by the portions 126 and which become compressive strained semiconductor, herein SiGe, portions 128. In the particular embodiment described herein, the portions 128 include a compressive strain oriented parallel with the longitudinal direction and a compressive strain oriented parallel with the transversal direction. These portions 128 are herein intended for the production of PMOS transistor channels. At the end of this thermal oxidation, the portions 126 have been converted into portions 129 including the oxide of the semiconductor initially present in the portions 126.

[0085] Simultaneously with the formation of the portions 128, this thermal oxidation also makes it possible to form in the trenches 118 oxide portions 130 carrying out localized isolation of the portions 128 therebetween as well as with respect to the remainder of the surface layer 106 corresponding particularly to the second regions 114.

[0086] The thermal oxidation is for example implemented at a temperature of between 1100 C. and 1200 C., and for a duration of between 1 and 10 seconds. The temperature and duration of implementation of this thermal oxidation are selected according to the features sought for the portions 128, particularly the thickness of these portions 128, and also the thickness of the oxide portions 130 to be produced. The temperature and duration of implementation of this thermal oxidation must be sufficient for the material of the parts of the surface layer 106 covered by the portions 126 to be converted over the entire thickness of the surface layer 106, and for oxide portions 130 to each have a thickness at least equal to that of the portions 128.

[0087] Due to the thermal oxidation implemented, the dimensions of the portions 128 formed may be less than those of the portions 126 due to the oxide formed at the edges of the portions 128. For example, considering two portions 126 spaced from one another by a distance equal to 35 nm, the portions 128 obtained following the thermal oxidation may be spaced from one another by a distance equal to 55 nm.

[0088] An oxide layer 132 is then deposited onto the structure previously produced, thus covering the oxide portions 129 and 130 as well as the hard mask 108 (see FIG. 6).

[0089] A chemical mechanical planarization of the oxide layer 132 is then carried out, with stoppage on the hard mask 108 (see FIG. 7). The remaining parts of the oxide layer 132 and the portions 129 form, on the side of the layer 132 which is planarized, a substantially planar face aligned with the top face of the hard mask 108.

[0090] The remaining parts of the oxide layer 132 and the portions 129 are then removed, for example by implementing a deoxidation controlled and stopped on the portions 128 (see FIG. 8). This deoxidation may be obtained with a wet process such as HF diluted for example to 1%.

[0091] At this stage of the method, the portions 128 obtained are electrically isolated from one another as well as with respect to the second regions 114 of the surface layer 106. The strain present in the material of the portions 128 has not been altered by producing the oxide portions 130, particularly at the edges of these portions 128.

[0092] The hard mask 108 is then removed (see FIG. 9).

[0093] Dielectric isolation portions 134, for example of STI type, are then produced through the surface layer 106, the buried dielectric layer 104 and a part of the thickness of the base layer 102 (see FIG. 10). These dielectric isolation portions 134 are produced around one or more assemblies formed of the portions 128 and 130 intended to serve to produce the PMOS transistors, and herein also around the second region(s) 114 intended to serve to produce the NMOS transistors. These dielectric isolation portions 134 may also serve to divide the or each of the second regions 114 into several parts. Given that the dielectric isolation portions 134 are not produced directly against the edges of the portions 128, the compressive strain present in the semiconductor of the portions 128 is maintained thanks to the oxide portions 130 which have been produced without impacting this compressive strain.

[0094] The dielectric isolation portions 134 are for example produced by etching first of all trenches through the surface layer 106 and/or the oxide portions 130, and through the buried dielectric layer 104 and a part of the thickness of the base layer 102 up to the sought depth, then filling these trenches with a dielectric material, for example SiO.sub.2.

[0095] Dielectric isolation portions 134 are also produced around the second regions 114. Given that producing these portions 134 includes producing trenches through the entire thickness of the surface layer 106 and the buried dielectric layer 104, this may create tensile strains in the second regions 114, which will be beneficial for the subsequent production of the NMOS transistors in the second regions 114.

[0096] FIG. 11 shows a top view of the structure obtained following the steps described above, according to a first particular configuration. In this figure, the oxide portions 130 are produced at the edges of the portions 128 which are oriented, or which extend, perpendicularly to the longitudinal direction, or perpendicularly to the length of the channels (direction from the source to the drain) of the PMOS transistors which will be subsequently produced on and in the portions 128. The dielectric isolation portions 134 surround the assembly formed of the portions 128 and the oxide portions 130. In this figure, the dielectric isolation portions 134 are also produced to electrically isolate therebetween different parts 136 of the second region 114.

[0097] The arrows seen in FIG. 11 represent the strains in the semiconductor material of the portions 128. These arrows show that the compressive strain is indeed retained in the semiconductor of the portions 128 in the longitudinal direction, and that a strain tending toward more tensile strain is present in these portions 128 in the transversal direction, particularly due to the small dimensions (width of each of the portions 128 of less than 500 nm) of these portions 128 in the transversal direction. This progression of the strain toward more tensile strain (i.e. the relaxation of the initial compressive strain) is obtained in that, when producing the trenches intended to serve to produce dielectric isolation portions 134, these trenches etched against the edges of the portions 128 which are oriented parallel with the longitudinal direction induce a relaxation of the compressive strain along the transversal direction.

[0098] When the initial semiconductor of the layer 106 is tensile strained, for example when the initial substrate used is for example of the sSOI (strained silicon on insulator) type with a tensile strain present in the silicon, this tensile strain may be found in the semiconductor of the portions 136, in the longitudinal direction and in the transversal direction.

[0099] FIG. 12 shows a top view of the structure obtained following the steps described above, according to a second particular configuration. Unlike the first configuration described above, the oxide portions 130 are produced at all the edges of the portions 128, i.e. not only those which are oriented perpendicularly to the longitudinal direction, but also those oriented parallel with this longitudinal direction. Thus, the biaxial compressive strain initially present in the semiconductor of the portions 128 is retained even after producing the dielectric isolation portions 134 which does not impact this strain. As for FIG. 11, the arrows seen in FIG. 12 represent the strains present in the semiconductor of the portions 128. As above, when the initial semiconductor of the layer 106 is tensile strained, this tensile strain may be found in the semiconductor of the portions 136, in the longitudinal direction and in the transversal direction.

[0100] Finally, the method is completed by producing PMOS transistors 138 on and in the portions 128, and NMOS transistors 140 on and in the parts 136 of the second region 114 (see FIG. 13). The definitive gates of these transistors are particularly produced after the steps described above.

[0101] Other types of semiconductor devices may be produced in the portions 128 and 136 obtained, such as for example MOSFET-based memories, or indeed devices of the field of optics or photonics.