Cooking vessel and manufacturing method

Abstract

A cooking vessel includes a receptacle of a first material for receiving foodstuff, and a bottom section of a second material. The bottom section being attached to the receptacle for providing an induction heating capability for the cooking vessel. In order to provide a cooking vessel whose temperature can simply and reliably be determined during induction heating the second material is unalloyed or low-alloyed steel.

Claims

1. A cooking vessel comprising: a receptacle of a first material comprising at least one of aluminum and stainless Steel for receiving foodstuff, and a bottom section of a second material which is a solid unalloyed or low-alloyed steel containing carbon in a range of 0.1-5%, or containing carbon in a range of less than 0.005% and containing silicon, wherein the total share of alloying components which optionally include one or more of silicone, manganese, aluminum, and copper does not exceed 8 percent, the bottom section being attached to the receptacle for providing an induction heating capability for the cooking vessel, wherein the second material is coated with a coating layer of chromium, and the receptacle and the bottom section are attached to each other by the coating layer.

2. The cooking vessel according to claim 1, wherein the coating layer is of the chromium and the amount of the chromium is within a range between 50-180 mg/m.sup.2 inclusive.

3. The cooking vessel according to claim 1, wherein the coating is a thin layer of chromium having a thickness within a range between 0.2 nm-30 m inclusive.

4. The cooking vessel according to claim 1, wherein the first material is aluminum.

5. The cooking vessel according to claim 1, where the first material is stainless steel.

6. The cooking vessel according to claim 1, wherein the bottom section has a thickness of more than 0.1 mm, and less than or equal to 0.5 mm.

7. The cooking vessel according to claim 1 wherein outer surfaces of the bottom section are protected by a corrosion protection layer.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) In the following the present invention will be described in closer detail by way of example and with reference to the attached drawings, in which

(2) FIG. 1 illustrates a first embodiment of a cooking vessel,

(3) FIG. 2 illustrates a second embodiment of a cooking vessel,

(4) FIG. 3 illustrates a third embodiment of a cooking vessel, and

(5) FIG. 4 illustrates a fourth embodiment of a cooking vessel.

DESCRIPTION OF AT LEAST ONE EMBODIMENT

(6) FIG. 1 illustrates a first embodiment of a cooking vessel 1. FIG. 1 illustrates the cooking vessel in cross-section in order to show the various parts and layers included in the cooking vessel. The handle 2 of the cooking vessel is only partially illustrated by dotted lines.

(7) In FIG. 1 it is by way of example assumed that the cooking vessel 1 is a frying pan. However, this is only an example of one possible cooking vessel, and in praxis the cooking vessel may instead be a kettle, a pot or any other cooking vessel suitable for preparing foodstuff on an induction heater. In this connection the term foodstuff refers generally to any material which needs to be heated while preparing food.

(8) The illustrated cooking vessel 1 comprises a receptacle 3 of a first material. During use this receptacle 3 receives foodstuff. For this purpose the receptacle has a tight bottom 4 and edges 5 protruding upwards from the bottom 4 in order to ensure that the foodstuff does not leak out of the receptacle 1 during use. Additionally, though not illustrated, the receptacle may be provided with a lid, for instance. The first material used for manufacturing the receptacle 3 may be any material commonly used in cooking vessels. Consequently the first material may be aluminum or stainless steel, for instance. The material thickness of the bottom 4 and edges 5 may be about 3-6 mm, for instance. If necessary, a coating layer of a non-stick material may be provided to cover the inner surface of the receptacle 3 in order to prevent foodstuff from being stuck on the inner surface.

(9) The cooking vessel 1 additionally comprises a bottom section 6 of a second material. The thickness of the bottom section may be more than 0.1 mm, preferably about 0.5 mm, though it is possible to utilize bottom sections which are even thicker. The bottom section 6 provides an induction heating capability for the cooking vessel 1. Therefore, the receptacle 3 may be of aluminum for instance, as the bottom section 6 ensures that the cooking vessel 1 indeed can be heated with an induction heater even though aluminum is not suitable for heating with an induction heater. The second material used in the bottom section 6 is unalloyed or low-alloyed steel. Practical tests have shown that once unalloyed or low-alloyed steel is used in the bottom section 6, it becomes possible to accurately determine the temperature of the cooking vessel 1 on an induction heater based on the frequency both while the temperature of the cooking vessel 1 increases and while it decreases. According to practical tests the temperature of the cooking vessel can in this way be measured with an error of less than 5 C. Therefore, no similar hysteresis between heating and cooling is present as in prior art cooking vessels where the bottom section comprises ferritic stainless steel, for instance. Therefore it is possible to determine the temperature very accurately with a measuring resonant circuitry based on the measured frequency.

(10) In this connection the terms unalloyed steel and low-alloyed steel refer to a steel which contains carbon, but the steel has not been processed or provided with additives that prevent corrosion when exposed to air and moisture. One alternative is that this steel contains carbon in the range of 0.1-5% and where the total share of the alloying components, such as Si, Mn, Al, Ti and Cu, does not exceed 8%. Another alternative is that the steel is an unalloyed steel commonly referred to as an electrical steel, in other words a steel which contains less than 0.005% carbon but which contains silicon.

(11) In the illustrated example, the bottom section 6 is attached to the receptacle 3 by a coating layer 7. On alternative is to utilize a coating layer 7 of chromium, nickel, aluminum or copper. This makes it possible to attach the receptacle 3 to the bottom section 6 by means of the coating layer 7 alone. Consequently no additional mechanical or other attachment means are needed for this attachment. One alternative is to carry out the attachment by impact bonding. In impact bonding the bottom section 6 and the receptacle 3 are arranged on top of each other with the coating layer 7 between them. In this position a high pressure is utilized to press the parts together, such that friction between the parts leads to a situation where the parts are bonded together.

(12) The thickness of the coating layer 7 may vary depending on the implementation. In case a receptacle 3 of aluminum is used, this receptacle may be attached to a bottom section 6 of unalloyed or low-alloyed steel by impact bonding when a coating layer 7 of chromium, nickel, aluminum or copper is arranged between the receptacle 3 and bottom part 6. In that case the amount of chromium, nickel, aluminum or copper may be about 50-180 mg/m.sup.2, which in practical implementation will result in a coating layer 7 which may be very thin, in praxis about 0.2 nm-30 m. However, coating layers of other thicknesses may be used in other implementations.

(13) FIG. 2 illustrates a second embodiment of a cooking vessel. The embodiment of FIG. 2 is very similar as the embodiment of FIG. 1. Therefore in the following the embodiment of FIG. 2 will be explained mainly by pointing out the differences between these embodiments.

(14) In FIG. 2 the receptacle 3 is implemented as explained in connection with FIG. 1. However, the bottom section 6 is manufactured of an ECCS (Electrically Chromium Coated Steel) plate. Such ECCS plates of unalloyed steel or low-alloyed steel where the upper and lower surfaces are coated by a coating layer 7 are commercially available.

(15) An advantage of utilizing an ECCS plate for manufacturing the bottom section 6 is that the manufacturing process becomes very simple. It is sufficient to cut a bottom section 6 of a suitable size and to attach this bottom section 6 to the receptacle 3 by impact bonding.

(16) FIG. 3 illustrates a third embodiment of a cooking vessel. The embodiment of FIG. 3 is very similar as the embodiment of FIG. 1. Therefore in the following the embodiment of FIG. 3 will be explained mainly by pointing out the differences between these embodiments.

(17) In FIG. 3 the receptacle 3 and the bottom section 6 are implemented and attached to each other with the coating layer 7 as explained in connection with FIG. 1. Alternatively it is possible to utilize a bottom section 6 as explained in connection with FIG. 2.

(18) In FIG. 3 an additional corrosion protection layer 8 is included in the cooking vessel. In the illustrated example the corrosion protection layer is added as a continuous layer extending along the entire outer surface of the receptacle 3 and also along the entire outer surface of the bottom section 6. The corrosion protection layer 8 may be implemented as a layer of silicone polyester or as a ceramic sol-gel coating, for instance. Silicone polyester is a polyester coating which includes silicone. A ceramic sol-gel coating is a siloxane based non-organic compound, in praxis a silicone glass.

(19) The illustrated cooking vessel may be manufactured by initially providing a receptacle 4 of a first material for receiving foodstuff, as illustrated in FIG. 2, for instance. The first material may be stainless steel or aluminum, for instance. A bottom section 6 or 6 (as illustrated in FIG. 1 or 2) of a second material dimensioned to fit to the bottom of the receptacle is taken into use. The second material is an unalloyed or low-alloyed steel. The bottom section and the receptacle are arranged on top of each other with a coating layer between them.

(20) A coating layer refers to a material layer which is applied by a suitable coating process, such as spraying or electrolytic coating, on top of a surface of an object, such as on the bottom of the receptacle or on a surface of the bottom section. Consequently, the raw material is a compound consisting practically of chromium, nickel, aluminum or copper alone. In praxis the amount of chromium, nickel, aluminum or copper in the coating layer in most cases exceeds 50%.

(21) Once the bottom section and the receptacle are arranged on top of each other with a coating layer between them, the bottom section and the receptacle are attached to each other. This may be implemented by impact bonding, such that the coating layer attaches the receptacle to the bottom section without any additional attachment means.

(22) FIG. 4 illustrates a fourth embodiment of a cooking vessel 1. The embodiment of FIG. 4 is very similar as the embodiment of FIG. 2. Therefore in the following the embodiment of FIG. 4 will be explained mainly by pointing out the differences between these embodiments.

(23) In FIG. 4 the cooking vessel 1 comprises a receptacle 3 of aluminum in combination with two layers of an ECCS plate, in other words a plate of unalloyed steel or low-alloyed steel where the upper and lower surfaces are coated by a coating layer.

(24) On the inner side of the receptacle a first ECCS plate 9 is arranged to cover the inner bottom surface of the receptacle 4. This plate may have upper and lower coating layers of chromium. In that case it is not necessary to provide any additional coating layers within the receptacle, but instead the foodstuff may be allowed to directly contact the upper surface of the ECCS plate 9. Naturally, if desired, an additional coating layer may be arranged to cover the upper surface of the ECCS plate 9.

(25) The outer bottom surface of the receptacle 4 is covered by second ECCS plate which provides the bottom section 6 and the coating layers 7, as has previously been explained in connection with FIG. 2. Also in this case the bottom section 6 may be of unalloyed steel or low-alloyed steel with the upper and lower surfaces are coated by a coating layer 7 of chromium.

(26) Similarly as has been explained in connection with the previous embodiments, the cooking vessel 1 may be manufactured by arranging the ECCS plates and the receptacle in the positions illustrated in FIG. 4, after which the attachment is carried out by impact bonding without utilizing other attachment means.

(27) It is to be understood that the above description and the accompanying figures are only intended to illustrate the present invention. It will be obvious to a person skilled in the art that the invention can be varied and modified without departing from the scope of the invention.