INTERMEDIARY RACE MEMBER OF ROLLING BEARING, RACE, ROLLING BEARING AND PRODUCTION METHOD THEREFOR

Abstract

A method for manufacturing a bearing ring of a rolling bearing includes a series of steps of cutting out an annular member from a material, forming a surface-hardened layer on the annular member, quenching and tempering the annular member, and polishing inner and outer diameter surfaces of the annular member. The method includes, after the quenching, rapidly cooling the ring member such that the ring member has a surface temperature of 50 C. or lower to form a bearing ring intermediate member, and after the tempering, polishing inner and outer diameter surfaces of the bearing ring intermediate member.

Claims

1-8. (canceled)

9. A method for manufacturing a bearing ring of a rolling bearing, the method comprising a series of steps of: cutting out an annular member from a material; forming a surface-hardened layer on the annular member; quenching and tempering the annular member; and polishing inner and outer diameter surfaces of the annular member, wherein the method comprises: after the quenching, rapidly cooling the ring member such that the ring member has a surface temperature of 50 C. or lower to form a bearing ring intermediate member; and after the tempering, polishing inner and outer diameter surfaces of the bearing ring intermediate member.

10. The method for manufacturing the bearing ring of the rolling bearing according to claim 9, wherein the rapid cooling is performed along with cleaning of the annular member with a cleaning liquid after the quenching.

11. (canceled)

12. The method for manufacturing the bearing ring of the rolling bearing according to claim 9, wherein an absolute value of an average residual stress of each part from a surface to a core portion in a radial direction is 0 to 191 MPa.

13. A method for manufacturing a rolling bearing comprising the method for manufacturing the bearing ring according to claim 9.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0053] FIG. 1 is a sectional view showing an example of a vehicle transmission.

[0054] FIG. 2 is a graph showing results of a preliminary test, and shows a relationship between a surface temperature of an annular member and a residual stress.

[0055] FIG. 3 is a graph showing a distribution of residual stress in a depth direction in Comparative Example 1.

[0056] FIG. 4 is a graph showing a distribution of residual stress in the depth direction in Example 1.

[0057] FIG. 5 is a graph showing a distribution of residual stress in the depth direction in Example 2.

[0058] FIGS. 6A, 6B and 6C are graphs each showing a roundness distribution of a polished specimen obtained in Example 1, Example 2, and Comparative Example 1.

DESCRIPTION OF EMBODIMENTS

[0059] Hereinafter, the present invention will be described in detail with reference to the drawings. In the following description, a bearing ring intermediate member of a rolling bearing is also simply referred to as race ring intermediate member.

[0060] In the present invention, there is no restriction on the type of the rolling bearing. As the rolling bearing, a tapered roller bearing, a ball bearing, a cylindrical roller bearing, a needle roller bearing, or the like are generally used, and in the present invention, these rolling bearings and also the bearing rings (inner ring or outer ring) are targeted. In addition, when the bearing ring is thinned, t/D (t: effective thickness of bearing ring, D: outer diameter of bearing ring) being 0.1 or less is particularly effective.

[0061] In the present invention, first, an annular member made of a material to be an inner ring or an outer ring is prepared. The material is preferably case-hardened steel such that a surface-hardened layer can be easily formed by carburizing treatment, nitriding treatment, and carbonitriding treatment. In order to improve hardenability, Cr, Mn, or the like are preferably added as alloy components.

[0062] Then, similar to a related art, the annular member is used to form a surface-hardened layer, heat treatment of quenching and tempering is performed to form a bearing ring intermediate member, and then an inner diameter surface and an outer diameter surface of the bearing ring intermediate member are polished to manufacture a bearing ring. The quenching may be performed once or twice. The obtained bearing ring is assembled together with a rolling element and a cage to form a rolling bearing. This sequence of steps is similar to that of the related art.

[0063] However, in the present invention, the annular member is rapidly cooled after being quenched to form the bearing ring intermediate member, and then tempering and polishing are performed. In addition, after the annular member is quenched with oil for cooling, the annular member may also be rapidly cooled along with cleaning of the oil adhering to the annular member. As a rapidly cooling method, the annular member may be immersed in a storage tank of water or a cleaning liquid, but the annular member is not suitable for continuous processing because the liquid temperature rises, and thus a method of spraying water or the cleaning liquid onto the annular member is preferable. A refrigerant for rapidly cooling is particularly preferably water in consideration of cooling capacity, cost, ease of post-processing, and the like, and water can also be used for cleaning. A cleaning liquid obtained by adding a surfactant to water is preferable, and a rust inhibitor may be added.

[0064] Although it is known that a compressive residual stress is generated on a surface of the annular member formed with the surface-hardened layer, the compressive residual stress depends on the order of generation of martensitic transformation associated with a gradient of the carbon, and is generated by the martensitic transformation occurring in the order from a core portion to the surface along with cooling. Since the hardness of martensite depends on the amount of carbon, a hardness distribution and a residual stress distribution corresponding to the gradient of carbon concentration are generated from the surface to the inside. The hardness depends almost only on the carbon concentration, but the residual stress depends on the occurrence time of the martensitic transformation. Therefore, by rapidly cooling the surface at which the occurrence of the martensite transformation is later than the occurrence of the martensite transformation at the core portion, the occurrence timing of the martensitic transformation is synchronized between the surface and the core portion, and the occurrence of the residual stress can be suppressed.

[0065] For this purpose, a cooling rate of the surface of the annular member is made relatively higher than a cooling rate of the core portion by rapid cooling the annular member after quenching or by rapid cooling the annular member along with the cleaning. Specifically, it has been found that it is effective to perform rapid cooling after quenching, and set the surface temperature of the annular member to 50 C. or lower, preferably 10 to 40 C. By the rapid cooling, the residual stress on the surface of the bearing ring intermediate member and the distribution of the residual stress are controlled, so that a change in the residual stress in the stock allowance corresponding to the surface, that is in the depth direction from the depth position of 50 m to the core portion is made gentle to an extent that the residual stress is almost not changed. More preferably, an absolute value of an average residual stress in the stock allowance is 0 to 191 MPa, and has a depth-residual stress distribution that gradually approaches 0 from the surface to the core portion. Further, the absolute value of the residual stress at the depth position of 50 m to 250 m corresponding to the inside of the stock allowance is set to 100 MPa or less. More preferably, the absolute value of the residual stress at the depth position of 50 m to 250 m corresponding to the inside of the stock allowance is set to 60 MPa or less. The cooling rate at the time of rapid cooling is 10 C./min or more, and more preferably 15 C./min or more.

[0066] Further, the residual stress distribution on the surface of the bearing ring intermediate member is preferably maintained as it is in the bearing ring which is a final product obtained by polishing. That is, even in the finally obtained bearing ring, the change in the residual stress from the depth position of 50 m to the core portion is gentle to an extent that the residual stress is almost not changed, the absolute value of the average residual stress in the stock allowance is 0 to 191 MPa, there is a depth-residual stress distribution that gradually approaches zero from the surface to the core portion, and the absolute value of the residual stress at the depth position of 50 m to 250 m is preferably 100 MPa or less, more preferably 60 MPa or less.

[0067] Then, after tempering by a related-art method, the inner diameter surface and the outer diameter surface are polished to complete the bearing ring, but the residual stress on the surface of the bearing ring intermediate member is reduced by the rapid cooling after quenching or the cleaning and the rapid cooling after quenching as described above, so that the reduction in roundness at the time of polishing can be suppressed.

[0068] The above-described bearing ring can be assembled together with the rolling element and the cage to form the rolling bearing.

[0069] Roundness is generally standardized by JIS B 1515, and is a difference between a maximum value and a minimum value of an outer diameter in one radial plane, and JIS B 1514 defines roundness for each bearing outer diameter and each grade. The accuracy of roundness required for the diameter of the bearing ring is about 0.01 to 0.03%. Here, a case where the maximum value at Grade 0 of a general product is set as a minimum target value, a preferable target value is set as within 0.015% of the outer diameter, and a more preferable target value is set as within 0.01% of the outer diameter will be described.

[0070] In addition, in the polishing, the stock allowance is defined in JIS B 0711 in consideration of the surface property or the like of a heat-treated product. In the rolling bearing for a transmission according to the present invention, the stock allowance of the outer diameter is set as 0.2 mm in diameter.

[0071] Once the roundness and the stock allowance are determined, the residual stress required for obtaining the target roundness can be calculated within a range of the stock allowance.

[0072] The residual stress of the member can be determined from the curvature of the member, and in the present invention, the residual stress is determined based on a curvature method. That is, for the ring member made of case-hardened steel that is the material of the inner ring and outer ring, after the surface-hardened layer is formed, and the heat treatment of quenching and tempering are performed, dimensional changes of the outer and inner diameters are measured. From this amount of change, based on a definition expression of residual stress by the curvature method, the residual stress is calculated to achieve the target roundness for each outer diameter and thickness.

[0073] Tables 1 to 3 show results, and the average residual stress required to achieve the target roundness in the range of the stock allowance being 0.2 mm for each outer diameter and thickness of the annular member. Table 1 shows a case where the target roundness is within the maximum value of Grade 0 in JIS standard, Table 2 shows a case where the target roundness is within 0.015% of the outer diameter, and Table 3 shows a case where the target roundness is within 0.01% of the outer diameter. As shown in Tables 1 to 3, in any roundness, the residual stress decreases as the outer diameter increases when the thickness is the same; conversely, the residual stress increases as the thickness increases when the outer diameter is the same.

TABLE-US-00001 TABLE 1 Thickness Outer diameter of outer ring (mm) (mm) 50 60 70 80 90 100 120 3 76 53 39 34 27 22 15 4 181 125 92 81 64 51 36 5 331 230 168 148 117 95 66 6 366 268 237 187 151 105 7 392 346 274 222 154 8 477 377 305 212 9 496 402 280

TABLE-US-00002 TABLE 2 Thickness Outer diameter of outer ring (mm) (mm) 50 60 70 80 90 100 120 3 44 37 31 27 27 22 15 4 103 87 74 65 57 51 36 5 191 158 136 119 105 95 65 6 304 253 217 190 168 151 105 7 444 370 318 277 246 222 153 8 437 382 340 305 212 9 447 402 279

TABLE-US-00003 TABLE 3 Thickness Outer diameter of outer ring (mm) (mm) 50 60 70 80 90 100 120 3 29 25 21 18 16 15 12 4 69 58 50 43 38 35 29 5 127 105 91 79 70 63 53 6 202 168 145 126 112 100 84 7 296 246 211 185 164 147 123 8 407 340 291 254 225 203 169 9 447 383 335 297 268 223

[0074] Then, a relationship between the outer diameter and the residual stress was graphed for each thickness from the same table, an approximate straight line was determined by a least square method, and a slope and an intercept were determined. Table 4 shows a case where the roundness is within the maximum value of Grade 0 in JIS standard, Table 5 shows a case where the roundness is within 0.015% of the outer diameter, and Table 6 shows a case where the roundness is within 0.01% of the outer diameter.

TABLE-US-00004 TABLE 4 Thickness (mm) Slope Intercept 3 0.8 103 4 1.91 245 5 3.49 449 6 4.14 578 7 4.89 727 8 6.45 971 9 7.04 1120

TABLE-US-00005 TABLE 5 Thickness (mm) Slope Intercept 3 0.39 60 4 0.92 142 5 1.7 263 6 2.71 419 7 3.95 612 8 4.39 739 9 5.68 963

TABLE-US-00006 TABLE 6 Thickness (mm) Slope Intercept 3 0.24 38.9 4 0.56 91.55 5 1.03 167.6 6 1.64 267.7 7 2.4 391.5 8 3.31 539.6 9 3.66 642

[0075] Further, the relationship between the thickness and the slope and the relationship between the thickness and the intercept were graphed, and an approximate straight line was determined by the least square method. From the obtained approximate straight line and the outer diameter, the following Expressions (1) to (3) relating to the residual stress at the depth position of 50 m from the surface are obtained for each target roundness. In the Expressions, D is the outer diameter of the bearing ring, and t is the thickness of the bearing ring.

[0076] When the target roundness is within the maximum value of JIS Grade 0, in the present invention,

residual stress(1.04t2.2)D170.8t+425(1)

[0077] When the target roundness is within 0.015% of the outer diameter, in the present invention,

residual stress(0.90t2.6)D151.9t+454(2)

[0078] When the target roundness is within 0.01% of the outer diameter, in the present invention,

residual stress(0.61t1.8)D104.6t+322(3)

[0079] For example, in the case of an outer ring of a tapered roller bearing having an outer diameter of 73 mm and an effective thickness of 4.8 mm, in order to keep the roundness after polishing within the maximum value of JIS Grade 0, from Expression (1), the average residual stress at the depth position of 50 m to 250 m on a raceway surface of the intermediate member of the bearing ring serving as the outer ring may be about 191 MPa or higher. When the roundness is further increased, the residual stress may be set to 150 MPa or higher in order to make the roundness within 0.015% of the outer diameter from Expression (2); the residual stress may be set to 97 MPa or higher in order to make the roundness within 0.01% of the outer diameter from Expression (3).

[0080] In the surface hardening treatment by carburizing, nitriding, or carbonitriding, the residual stress on the surface is basically compressive, and the residual stress becomes a negative value.

[0081] Then, by polishing the bearing ring intermediate member whose residual stress is controlled so as to satisfy the expressions (1) to (3) in this way, even if some elliptical deformation occurs, it is possible to reduce the occurrence of stress resulting from non-uniform stock allowance, and to ensure the target roundness in the bearing ring.

[0082] As described above, since the surface property of the bearing ring intermediate member is reflected in the surface property of the obtained bearing ring, for example, assuming that the average residual stress value of the bearing ring intermediate member which is subjected to heat treatment so as to satisfy Expression (1) is 150 MPa, the residual stress on the surface of the bearing ring is lower than 150 MPa. When the residual stress value of the bearing ring is evaluated, it is necessary to remove the residual stress caused by the polishing processing. To achieve this, electrolytic polishing of about 50 m is necessary, and the surface residual stress of the bearing ring after polishing is a residual stress at a depth of 50 m.

EXAMPLES

[0083] The present invention is further specifically described below with reference to Examples, but the present invention is not limited to such Examples in any way.

[0084] (Preliminary Test)

[0085] A steel material containing 0.4% by mass of carbon and further added with an alloy element such as Cr or Mn in order to ensure hardenability in oil cooling was prepared. An annular member whose outer diameter is about 75 mm was cut out from this steel material, and was subjected to carbonitriding treatment for 3.5 hours. Next, after secondary heating, quenching is performed in oil of about 100 C., and water is quickly sprayed to perform cleaning and quenching, the surface temperature of the annular member was set to 20 to 50 C., and tempering was performed to obtain a test piece. Then, the circumferential surface of the test piece was electrolytically polished to a predetermined depth, and an operation of measuring a residual stress at that position was repeated, and the residual stress up to a depth of 250 m in the vicinity of stock allowance was obtained. As results of the measurement, an average residual stress up to a depth of 250 m was 37 MPa when a surface temperature was 20 C., 34 Mpa when the surface temperature was 30 C., and 138 Mpa when the surface temperature was 50 C.

[0086] The measurement results are graphed and shown in FIG. 2, and the average residual stress is constant at a small value when the surface temperature of the annular member is 40 C. or lower, and constant at a smaller value when the surface temperature of the annular member is 38 C. or lower. That is, it is understood that the surface temperature of the annular member may be 40 C. or lower, preferably 38 C. or lower by rapid cooling.

Example 1, Example 2, Comparative Example 1

[0087] Similar to the preliminary test, an annular member for an outer ring of the tapered roller bearing having an outer diameter of 73 mm and a thickness of 4.8 mm was cut out from the steel material containing 0.4% by mass of carbon and added with an alloy element such as Cr or Mn, and was subjected to the carbonitriding treatment for 3.5 hours. Next, after secondary heating, quenching was performed in oil of about 100 C., the annular member was rapidly cooled to 50 C. after the quenching in Example 1 while the annular member was rapidly cooled to room tempering (25 C.) after the quenching in Example 2, and then the tempering was performed at 180 C. to obtain a test piece. On the other hand, in Comparative Example 1, after the quenching, the annular member was not particularly cooled, and then the tempering was performed at 180 C. to obtain a test piece.

[0088] For some parts of these test pieces, a circumferential surface corresponding to the raceway surface was electrolytically polished to a predetermined depth, and an operation of measuring the residual stress at that position was repeated to determine a residual stress distribution in the depth direction. However, the maximum measurement depth was 250 which was the stock allowance for grinding the workpiece. Table 7 shows values of the residual stress of each test piece.

TABLE-US-00007 TABLE 7 Comparative Depth Example 1 Example 1 Example 2 (mm) (MPa) (MPa) (MPa) 0.05 330 90 59 0.1 289 135 62 0.15 235 106 11 0.2 263 114 5 0.25 266 108 8 average 277 111 29 value

[0089] FIGS. 3 to 5 are graphs showing the residual stress distribution in the depth direction of each test piece using the results of Table 7. As mentioned above, since the residual stress of the core portion is estimated to be almost zero, while the residual stress clearly decreases toward the core portion in Comparative Example 1, since the residual stress value at a depth of 50 to 250 m in the stock allowance is kept low in Examples 1 and 2, it can be seen that the residual stress gently decreases toward the core portion.

[0090] Subsequently, the change in roundness due to grinding in each case was evaluated.

[0091] The roundness of each test piece after the heat treatment was almost the same. For 50 test pieces in each case, the outer diameter side and the inner diameter side were polished once each, and the roundness was measured. The results are shown in FIGS. 6A to 6C. In Comparative Example 1, the roundness is 3 to 32 m, and there is a large variation. In contrast, in Example 1, the roundness of all the test pieces is 8 m or less; in Example 2, the roundness of all the test pieces is 4 m or less, and the roundness is smaller and uniform.

[0092] In the outer ring of a tapered roller bearing having the outer diameter of 73 mm and the effective thickness of 4.8 mm, the residual stress may be set to 191 MPa or more in order to keep the roundness within the maximum value of JIS Grade 0 according to Expression (1), the residual stress may be set to 150 MPa or more in order to keep the roundness within 0.015% of the outer diameter according to Expression (2), and the residual stress may be set to 97 MPa or more in order to keep the roundness within 0.01% of the outer diameter according to Expression (3). In Example 1, the average residual stress is 111 MPa, and the above-described residual stress (150 Mpa or more) for suppressing the roundness within 0.015% (=11 m) of the outer diameter is satisfied, and the roundness is 8 m or less and also satisfies within 11 m. Similarly, in Example 2, the average residual stress is 29 MPa, and the above-described residual stress (97 Mpa or more) for suppressing the roundness within 0.01% (=7.3 m) of the outer diameter is satisfied, and the roundness is 4 m or less and also satisfies within 7.3 m. In contrast, in Comparative Example 1, since the average residual stress is 277 MPa, the residual stress (191 MPa or more) for keeping the roundness within the maximum value of JIS Grade 0 is not satisfied, and the maximum of roundness is 32 m and does not satisfy the roundness of JIS Grade 0.

[0093] Thus, it can be seen from Comparative Example 1, Example 1, and Example 2 that the target roundness and Expressions (1) to (3) have a correlation.

[0094] Although the invention has been described in detail with reference to the specific embodiments, it will be apparent to those skilled in the art that various changes and modifications can be made without departing from the spirit and scope of the invention.

[0095] This application is based on Japanese Patent Application (No. 2018-070943) filed on Apr. 2, 2018 and Japanese Patent Application (No. 2018-077598) filed on Apr. 13, 2018, contents of which are incorporated herein by reference.

INDUSTRIAL APPLICABILITY

[0096] According to the present invention, in various rolling bearings, a bearing ring having a high roundness can be obtained, and a highly accurate rolling bearing can be obtained. For example, the rolling bearings are useful as rolling bearings used in an automobile transmission, a computer tomography machine (CT scanner) or the like.

REFERENCE SIGNS LIST

[0097] 1 housing [0098] 2 input shaft [0099] 3 output shaft [0100] 4 pilot shaft [0101] 5 counter shaft [0102] 6 reverse shaft [0103] 7 cylindrical roller bearing [0104] 8 needle roller bearing [0105] 9 gear group [0106] 9a, 9b gear [0107] 10 gear member [0108] 11 clutch hub