Water-induced anti-counterfeiting paper and preparation method thereof

Abstract

The present invention discloses a water-induced anti-counterfeiting paper and a preparation method thereof, belonging to the field of anti-counterfeiting technology of paper. The water-induced anti-counterfeiting paper consists of a base paper layer and an anti-counterfeiting label thereon. The anti-counterfeiting label is a colorless, invisible pattern or character, and does not have any effect on the appearance of the base paper. When contacting with water, a transparency of a location where the paper has the anti-counterfeiting label increases, and thereby a character or a pattern appears. After drying, the character or the pattern disappears, and the paper reverted to normal. The water-induced anti-counterfeiting paper may be prepared by method of printing the anti-counterfeiting label at a surface of the base paper by processes such as printing, code-spurting and inkjet printing according to requirements. Compared with the existing anti-counterfeiting surface-printing technology and other anti-counterfeiting embedment technology, the water-induced anti-counterfeiting paper is low in cost, the process is simple, and is not easy to be imitated; and its identification method is simple, its anti-counterfeiting effect is remarkable, and detection is repeatable.

Claims

1. A water-induced anti-counterfeiting paper, consisting: a base paper layer; and an anti-counterfeiting label on the base paper layer, wherein the anti-counterfeiting label of the water-induced anti-counterfeiting paper is colorless and invisible, and does not have any effect on an intrinsic color of the base paper layer, wherein when the water-induced anti-counterfeiting paper contacts with water, a local transparency of the water-induced anti-counterfeiting paper where the anti-counterfeiting label is located increases, and thereby a character or a pattern of the anti-counterfeiting label appears; after drying, the character or the pattern disappears, the water-induced anti-counterfeiting paper reverted to normal, and a water-induced anti-counterfeiting feature detection of the water-induced anti-counterfeiting paper is repeatable, wherein a functional ink used for the anti-counterfeiting label comprises components as follows: a filler: 1 to 25 parts by weight; an adhesive: 3 to 50 parts by weight; a surfactant: 3 to 75 parts by weight; a vegetable oil: 5 to 20 parts by weight; an inorganic additive: 3 to 30 parts by weight; and a rheological agent: 1 to 15 parts by weight.

2. The water-induced anti-counterfeiting paper according to claim 1, wherein the base paper layer is writing paper, art paper, newsprint, printer paper, drawing paper, bond paper, cardboard paper, offset paper, paper for account books, bible paper or kraft paper that is made from plant fibers, having a basis weight of 20 g/m.sup.2 to 200 g/m.sup.2, and a Cobb60 value of 5 g/m.sup.2 to 100 g/m.sup.2.

3. The water-induced anti-counterfeiting paper according to claim 1, wherein the filler is calcium carbonate, magnesium carbonate, barium sulfate, calcium sulfate, kaolin, mica powder, montmorillonite, silicon dioxide, aluminium hydroxide, or aluminium oxide; the adhesive is epoxy resin, acrylic resin, polyvinyl alcohol, natural resin, guar gum, chitosan, cellulose derivative, starch, sodium alginate, styrene-butadiene latex, or styrene-acrylic emulsion; the surfactant is alkyl alcohol ether carboxylate, alkyl phosphate carboxylate, alkyl sulfonate, alkylbenzene sulfonate, sulfamate, higher fatty alcohol sulfate, fatty glyceride, polysorbate, fatty alcohol polyoxyethylene ether, alkylphenol ethoxylates, or alcohol compounds; the vegetable oil is tung oil, linseed oil, stillingia oil, soybean oil, rapeseed oil, castor oil, peanut oil, coconut oil, or cottonseed oil; the inorganic additive is sodium hydroxide, calcium hydroxide, hydrochloric acid, calcium chloride, nitrates, nitrites, or bicarbonates; and the rheological agent is organic bentonite, diatomite, cellulose derivative, polyurethane, polyether, or acrylic acid.

4. The water-induced anti-counterfeiting paper according to claim 1, wherein the functional ink has a solid content of 5% to 60%, and a viscosity of 1 mPa.Math.s to 10000 mPa.Math.s.

5. A method of preparing the water-induced anti-counterfeiting paper according to claim 1, comprising specific preparation steps as follows: 1) mixing, dispersing and stirring a filler, an adhesive, a surfactant, a vegetable oil, an inorganic additive, a rheological agent and a solvent, after diluting by adding water to have a desired solid content, rolling to form inks of various printing inks and inkjet inks; 2) printing a desired anti-counterfeiting label at a surface of a base paper using the inks obtained from step 1) by printing, code-spurting or inkjet printing, obtaining the water-induced anti-counterfeiting paper after drying.

6. A method of preparing the water-induced anti-counterfeiting paper according to claim 2, comprising specific preparation steps as follows: 1) mixing, dispersing and stirring a filler, an adhesive, a surfactant, a vegetable oil, an inorganic additive, a rheological agent and a solvent, after diluting by adding water to have a desired solid content, rolling to form inks of various printing inks and inkjet inks; 2) printing a desired anti-counterfeiting label at a surface of a base paper using the inks obtained from step 1) by printing, code-spurting or inkjet printing, obtaining the water-induced anti-counterfeiting paper after drying.

7. A method of preparing the water-induced anti-counterfeiting paper according to claim 3, comprising specific preparation steps as follows: 1) mixing, dispersing and stirring a filler, an adhesive, a surfactant, a vegetable oil, an inorganic additive, a rheological agent and a solvent, after diluting by adding water to have a desired solid content, rolling to form inks of various printing inks and inkjet inks; 2) printing a desired anti-counterfeiting label at a surface of a base paper using the inks obtained from step 1) by printing, code-spurting or inkjet printing, obtaining the water-induced anti-counterfeiting paper after drying.

8. A method of preparing the water-induced anti-counterfeiting paper according to claim 4, comprising specific preparation steps as follows: 1) mixing, dispersing and stirring a filler, an adhesive, a surfactant, a vegetable oil, an inorganic additive, a rheological agent and a solvent, after diluting by adding water to have a desired solid content, rolling to form inks of various printing inks and inkjet inks; 2) printing a desired anti-counterfeiting label at a surface of a base paper using the inks obtained from step 1) by printing, code-spurting or inkjet printing, obtaining the water-induced anti-counterfeiting paper after drying.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a structural schematic diagram of a water-induced anti-counterfeiting paper according to the present invention.

(2) FIG. 2 is a schematic diagram of an anti-counterfeit effect of a water-induced anti-counterfeiting paper according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

(3) Specific implementations of the present invention are further described below in combination with examples, but the implementations and the scope of protection of the present invention are not limited thereto.

(4) As shown in FIG. 1, a water-induced anti-counterfeiting paper according to the present invention is composed of a colorless and invisible anti-counterfeiting label 101 and a base paper layer 102. When contacting with water, a transparency of the paper at the location of anti-counterfeiting label 101 increases, and an anti-counterfeiting pattern or character 103 appears (as shown in FIG. 2).

Embodiment 1

(5) An advanced bible paper is used as the base paper, having a basis weight of 20 g/m.sup.2, and a Cobb60 value of 5 g/m.sup.2.

(6) 25 g of a filler, 50 g of an adhesive, 3 g of a surfactant, 3 g of an inorganic additive, 1 g of a rheological agent and 13 g of a solvent were mixed, dispersed and stirred; water was added for diluting to have a solid content of 60%; and then it was rolled to form a flatbed printing ink with a viscosity of 10000 mPa.Math.s. In particular, the filler is calcium carbonate, the adhesive is acrylic resin, the surfactant is sodium dodecyl benzene sulfonate, the inorganic additive is calcium chloride, the rheological agent is carboxymethylcellulose, and the solvent is ethanol. The desired anti-counterfeiting label was printed at a surface of the advance bible paper using the obtained flatbed printing ink by offset printing, and the water-induced anti-counterfeiting paper was obtained after drying.

(7) By observation, the anti-counterfeiting label of the water-induced anti-counterfeiting paper according to the present invention is in a colorless and invisible state at the surface of the dried paper. After wiping with water, a transparency of a location where the paper has the anti-counterfeiting ink label is increased, and specific character or pattern was observed, with an obvious visual effect and clear details. After water evaporated, the appeared character or pattern disappeared, and the paper reverted to normal.

Embodiment 2

(8) A cardboard paper is used as the base paper, having a basis weight of 200 g/m.sup.2, and a Cobb60 value of 100 g/m.sup.2.

(9) 1 g of a filler, 3 g of an adhesive, 75 g of a surfactant, 5 g of a vegetable oil, 5 g of an inorganic additive, 5 g of a rheological agent and 3 g of a solvent were mixed, dispersed and stirred; water was added for diluting to have a solid content of 5%; and then it was rolled to form a code-spurting ink with a viscosity of 100 mPa.Math.s. In particular, the filler is kaolin, the adhesive is polyvinyl alcohol, the surfactant is dioctyl sodium sulfosuccinate, the vegetable oil is linseed oil, the inorganic additive is sodium carbonate, the rheological agent is hydroxypropyl methyl cellulose, and the solvent is isopropanol. The desired anti-counterfeiting label was printed at a surface of the cardboard paper using the obtained code-spurting ink by continuously code-spurting, the water-induced anti-counterfeiting paper was obtained after drying.

(10) By observation, the anti-counterfeiting label of the water-induced anti-counterfeiting paper according to the present invention is in a colorless and invisible state at the surface of the dried paper. After wiping with water, a transparency of a location where the paper has the anti-counterfeiting ink label is increased, and specific character or pattern was observed, with an obvious visual effect and clear details. After water evaporated, the appeared character or pattern disappeared, and the paper reverted to normal.

Embodiment 3

(11) A bond paper is used as the base paper, having a basis weight of 65 g/m.sup.2, and a Cobb60 value of 25 g/m.sup.2.

(12) 2 g of a filler, 5 g of an adhesive, 5 g of a surfactant, 20 g of a vegetable oil, 5 g of an inorganic additive, 15 g of a rheological agent and 45 g of a solvent were mixed, dispersed and stirred; water was added for diluting to have a solid content of 40%; and then it was rolled to form a code-spurting ink with a viscosity of 5 mPa.Math.s. In particular, the filler is calcium carbonate, the adhesive is styrene-acrylic emulsion, the surfactant is sodium dodecyl benzene sulfonate, the vegetable oil is soybean oil, the inorganic additive is sodium nitrite, the rheological agent is polyvinyl alcohol (PVA1788), and the solvent is acetone. The desired anti-counterfeiting label was printed at a surface of the bond paper using the obtained code-spurting ink by continuously code-spurting, and the water-induced anti-counterfeiting paper was obtained after drying.

(13) By observation, the anti-counterfeiting label of the water-induced anti-counterfeiting paper according to the present invention is in a colorless and invisible state at the surface of the dried paper. After wiping with water, a transparency of a location where the paper has the anti-counterfeiting ink label is increased, and specific character or pattern was observed, with an obvious visual effect and clear details. After water evaporated, the appeared character or pattern disappeared, and the paper reverted to normal.

Embodiment 4

(14) A writing paper is used as the base paper, having a basis weight of 70 g/m.sup.2, and a Cobb60 value of 40 g/m.sup.2.

(15) 12 g of a filler, 30 g of an adhesive, 3 g of a surfactant, 10 g of an inorganic additive, 5 g of a rheological agent and 15 g of a solvent were mixed, dispersed and stirred; water was added for diluting to have a solid content of 45%; and then it was rolled to form a letterpress printing ink with a viscosity of 2000 mPa.Math.s. In particular, the filler is kaolin, the adhesive is an oxidized starch gelatinized liquid, the surfactant is alkylphenol ethoxylates, the additive is ammonium nitrate, the rheological agent is guar gum, and the solvent is ethanol. The desired anti-counterfeiting label was printed at a surface of the writing paper using the obtained letterpress printing ink by flexography, and the water-induced anti-counterfeiting paper was obtained after drying.

(16) By observation, the anti-counterfeiting label of the water-induced anti-counterfeiting paper according to the present invention is in a colorless and invisible state at the surface of the dried paper. After wiping with water, a transparency of a location where the paper has the anti-counterfeiting ink label increased, and specific character or pattern was observed, with an obvious visual effect and clear details. After water evaporated, the appeared character or pattern disappeared, and the paper reverted to normal.

Embodiment 5

(17) A copy paper is used as the base paper, having a basis weight of 80 g/m.sup.2, and a Cobb60 value of 25 g/m.sup.2.

(18) 5 g of a filler, 8 g of an adhesive, 3 g of a surfactant, 30 g of an inorganic additive, 1 g of a rheological agent and 50 g of solvent were mixed, dispersed and stirred; water was added for diluting to have a solid content of 20%; and then it was rolled to form an inkjet ink with a viscosity of 1 mPa.Math.s. In particular, the filler is calcium carbonate, the adhesive is acrylic resin, the surfactant is fatty alcohol polyoxyethylene ether, the inorganic additive is calcium chloride, the rheological agent is modified carboxymethylcellulose, and the solvent is ethanol. The desired anti-counterfeiting label was printed at a surface of the copy paper using the obtained inkjet ink by inkjet printing, and the water-induced anti-counterfeiting paper was obtained after drying.

(19) By observation, the anti-counterfeiting label of the water-induced anti-counterfeiting paper according to the present invention is in a colorless and invisible state at the surface of the dried paper. After wiping with water, a transparency of a location where the paper has the anti-counterfeiting ink label is increased, and specific character or pattern was observed, with an obvious visual effect and clear details. After water evaporated, the appeared character or pattern disappeared, and the paper reverted to normal.

(20) The above embodiments are the preferred embodiments of the present invention. However, the embodiments of the present invention are not limited to the above embodiments. Any other changes, modifications, substitutions, combinations and simplification, without departing from the spirit and material of the present invention, should be equivalent replacement, and are included in the scope of the present invention.