ABSORBABLE IRON-BASED IMPLANTABLE DEVICE

Abstract

An absorbable iron-based implantable device, including an iron-based substrate and an iron absorption promoter that is attached to the iron-based substrate. The iron absorption promoter is a polymer containing an antioxidant structural unit on the molecular chain thereof. The antioxidant is gradually released as the iron absorption promoter is gradually degraded or broken, and may promote the absorption of iron.

Claims

1-17. (canceled)

18. An absorbable iron-based implantable device, comprising: an iron-based substrate and an iron absorption promoter attached to the iron-based substrate, wherein the iron absorption promoter is a polymer, and an antioxidant structural unit is contained in the molecular chain of the iron absorption promoter.

19. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter is capable of being degraded to release an antioxidant.

20. The absorbable iron-based implantable device of claim 19, wherein the antioxidant is at least one selected from the group consisting of: ascorbic acid, procyanidin, vitamin E, glutathione, and lipoic acid.

21. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter has a weight-average molecular weight of 1,000 to 500,000.

22. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter is a procyanidin polymer.

23. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter further comprises at least one degradable polymeric structural unit.

24. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter further comprises at least one non-degradable polymeric structural unit.

25. The absorbable iron-based implantable device of claim 23, wherein the degradable polymer is at least one selected from the group consisting of: degradable polyester, polyamino acid, polyanhydride, and glucan.

26. The absorbable iron-based implantable device of claim 25, wherein the degradable polyester is at least one selected from the group consisting of: polylactic acid, polyglycolic acid, polysuccinate, poly(-hydroxybutyrate), polycaprolactone, and polyethylene adipate.

27. The absorbable iron-based implantable device of claim 25, wherein the polyamino acid is at least one selected from the group consisting of: polylysine, polyaspartic acid, polycysteine, polymethionine, polyornithine, and polyglutamic acid.

28. The absorbable iron-based implantable device of claim 25, wherein the polyanhydride is at least one selected from the group consisting of: polyoxalate anhydride, polybutanedioic anhydride, polyadipic anhydride, polysebacic anhydride, polydodecanoic anhydride, polycitric anhydride, polymalic anhydride, polysuccinic anhydride, polytartaric anhydride, polyitaconic anhydride, and polymaleic anhydride.

29. The absorbable implantable device of claim 24, wherein the non-degradable polymer is at least one selected from the group consisting of: polyethylene glycol, polyacrylate, polysuccinate, polycarbonate, polyethylene vinyl acetate, poly(n-butyl methacrylate), polystyrene, polyvinylidene fluoride, polyvinyl pyrrolidone, and polyhexafluoroethylene.

30. The absorbable iron-based implantable device of claim 18, wherein the mass ratio of the iron absorption promoter to iron in the iron-based substrate is 0.053:1.

31. The absorbable iron-based implantable device of claim 30, wherein the mass ratio of the iron absorption promoter to iron in the iron-based substrate is 0.151:1.

32. The absorbable iron-based implantable device of claim 18, wherein the iron absorption promoter is attached to a surface of the iron-based substrate or the iron absorption promoter is filled inside of the iron-based substrate.

33. The absorbable iron-based implantable device of claim 18, wherein the absorbable iron-based implantable device is a cardiovascular stent, a cerebrovascular stent, a peripheral vascular stent, a biliary stent, an esophageal stent, an airway stent, an occluding device, or an orthopedic implant.

34. The absorbable iron-based implantable device of claim 18, wherein the absorbable iron-based implantable device further comprises an active drug attached to the iron-based substrate, wherein the active drug is at least one selected from antiangiogenic drugs, antiplatelet drugs, antithrombotic drugs, anti-inflammatory drugs, and anti-sensitizing drugs.

Description

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0025] The foregoing objects, features and advantages of the embodiments will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings. In the following, numerous details are set forth to describe the embodiments. However, the embodiments may be implemented by many other manners different than those described herein and similar modifications may be made by those of ordinary skill in the art without departing from the spirit of the embodiments, thus the embodiments should not be construed as limiting.

[0026] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the present disclosure belongs. The terms used herein in the description of the present disclosure are for the purpose of describing particular embodiments only and not intended to be limiting of the present disclosure.

[0027] In one embodiment, an absorbable iron-based implantable device includes an iron-based substrate and an iron absorption promoter attached to the iron-based substrate, the iron absorption promoter being a polymer containing an antioxidant structural unit on the molecular chain thereof, and being capable of being degraded to release the antioxidant.

[0028] The iron-based substrate may be a pure iron substrate or an iron-based alloy substrate. For example, the material of iron-based alloy substrate is an iron-based alloy having a carbon content of not higher than 2.11 wt. %.

[0029] The iron absorption promoter may be attached to the surface of the iron-based substrate in a film forming manner. For example, the iron absorption promoter is attached to the outer surface, the inner surface or the side of the iron-based substrate. Alternatively, the iron absorption promoter is attached to the outer surface, the inner surface and the side surface of the iron-based substrate at the same time. Or the iron absorption promoter is attached to the outer and inner surfaces of the iron-based substrate, etc. That is, the position of the film formed by the iron absorption promoter on the iron-based substrate is not limited. Also, the distribution of the iron absorption promoter on the surface of the iron-based substrate may be either uniform or non-uniform.

[0030] In a further embodiment, the iron absorption promoter may be filled inside of the iron-based substrate. Gaps, pores, grooves, through-holes or inner cavities and the like can be formed on the iron-based substrate, so that the iron absorption promoter is filled into the corresponding gaps, pores, grooves, through-holes or inner cavities, so that the iron absorption promoter is filled inside of the iron-based substrate.

[0031] For example, the antioxidant is at least one selected from ascorbic acid, procyanidine, vitamin E, glutathione and lipoic acid. An antioxidant is polymerized to form an iron absorption promoter through a polymerization reaction, an antioxidant structural unit being a repeating unit on the molecular chain of the iron absorption promoter, and the antioxidant structural units being connected through chemical bonds. The antioxidant is released as the iron absorption promoter is degraded or broken.

[0032] The antioxidant released from the iron absorption promoter is at least one selected from ascorbic acid, procyanidin, vitamin E, glutathione and lipoic acid. The antioxidant released from the iron absorption promoter is a small molecule in the normal metabolic process of human tissue cells or a daily nutrient which can be safely untaken, such that the degraded or released product of the iron absorption promoter in vivo has a good biocompatibility with a human body, and harmful substance to the human body is not generated.

[0033] The antioxidant released during degradation of the above iron absorption promoter is an antioxidant showing a strong reduction effect, and when the iron absorption promoter is degraded or broken in vivo to release the antioxidant, oxygen in situ and near the absorbable iron-based implantable device can be consumed, to ensure that Fe.sup.2+ generated by corrosion is not immediately oxidized into Fe.sup.3+, but exists in the form of Fe.sup.2+ and precipitate thereof having a higher solubility, thereby facilitating diffusion and absorption of the iron corrosion product. Moreover, the iron absorption promoter can delay the conversion of Fe.sup.2+ to Fe.sup.3+, and free Fe.sup.2+ can diffuse out along with tissue fluid. The farther away from the iron-based substrate, the higher the concentration of oxygen ions in the tissue, until the level of oxygen concentration in normal tissues is recovered. The diffused Fe.sup.2+ ions are continuously oxidized to Fe.sup.3+ ions in oxygen-enriched tissues far away from the iron-based substrate, the Fe3+ ions are precipitated into dispersive Fe(OH).sub.3 solid corrosion products in surrounding tissues in which the iron-based substrate is implanted in situ. The more dispersive the Fe(OH).sub.3 solid corrosion product is, the more beneficial to improve the efficiency of phagocytosis and transportation and metabolism of ferric corrosion products by phagocytic cells, so that the absorption period of the absorbable iron-based implantable device in vivo is shortened.

[0034] In addition, in a physiological environment, after the absorbable iron-based implantable device is implanted into a body, the antioxidant is gradually released as the iron absorption promoter is gradually degraded or broken, so that the release rate of the antioxidant is delayed, the utilization rate of the antioxidant is improved, and the effect for promoting the long-acting iron absorption is achieved.

[0035] In a simulated physiological environment, such as in a saline solution, the iron absorption promoter may also be gradually degraded or broken to gradually release the antioxidant.

[0036] It can be appreciated that the antioxidant forming the iron absorption promoter may be any other antioxidant that shows antioxidant capacity and good biocompatibility with the human body.

[0037] If the molecular weight of the iron absorption promoter is too low, the release rate of the antioxidant will be too fast to facilitate improving the long-acting iron absorption promoting effect thereof, while if the molecular weight of the iron absorption promoter is too high, it will make the synthesis difficult and mechanical properties too poor to coat on the surface of the iron-based substrate. Thus, the weight-average molecular weight of the iron absorption promoter is from 1,000 to 500,000. For example, the weight-average molecular weight of the iron absorption promoter is from 3,000 to 300,000.

[0038] Meanwhile, the above iron absorption promoter is a polymer containing antioxidant structural units and has the advantage of high stability comparing to most natural antioxidants. Under illumination, oxygen enrichment or a specific pH environment, the chemical property of the above iron absorption promoter is difficult to change, enabling a long-acting and stable existence. In addition, the iron absorption promoter has a poor solubility in water. Therefore, the iron absorption promoter can exist stably in a body, and after the absorbable iron-based implantable device is implanted into the body, the iron absorption promoter is difficult to dissolve in aqueous tissue fluid, resulting in a little lose and thereby promoting the absorption of iron in long term.

[0039] Moreover, the iron absorption promoter has good stability and low environmental requirement on product storage, so that the product failure caused by the failure of the iron absorption promoter during storage is avoided, and the shelf life is prolonged.

[0040] In one embodiment, the iron absorption promoter further includes at least one degradable polymeric structural unit. The iron absorption promoter is formed by polymerization of a degradable polymer monomer and the above antioxidant. On the molecular chain of the iron absorption promoter, the degradable polymer structural unit is connected with the antioxidant structural unit through a chemical bond. Here, the degradable polymer structural unit refers to the repeating unit in the degradable polymer molecular chain.

[0041] In one embodiment, the degradable polymer is selected from at least one forming degradable polyester, polyamino acid, polyanhydride and glucan.

[0042] In one embodiment, the degradable polyester is at least one selected from polylactic acid, polyglycolic acid, polysuccinate, poly(-hydroxybutyrate), polycaprolactone, and polyethylene adipate.

[0043] In one embodiment, polyamino acid is at least one selected from polylysine, polyaspartic acid, polycysteine, polymethionine, polyornithine, and polyglutamic acid.

[0044] In one embodiment, the polyanhydride is at least one selected from polyoxalate anhydride, polybutanedioic anhydride, polyadipic anhydride, polysebacic anhydride, polydodecanoic anhydride, polycitric anhydride, polymalic anhydride, polysuccinic anhydride, polytartaric anhydride, polyitaconic anhydride, and polymaleic anhydride.

[0045] Polymerization of the degradable polymer monomer and the antioxidant facilitates improving the stability of the antioxidant, further delaying the release rate of the antioxidant, such that after the absorbable iron-based implantable device is implanted into a body, the antioxidant is gradually and slowly released to keep consistent with the degradation period of the iron-based substrate as far as possible, enabling a long-acting effect on promoting the iron absorption to a maximum level, and the chain segment formed by the degradable polymer is gradually degraded and absorbed as the antioxidant is released.

[0046] It can be appreciated that in other embodiments, in addition to the degradable polymer monomers listed above, other degradable polymer monomers capable of polymerizing with an antioxidant to form an iron absorption promoter and having good biocompatibility with the human body can also be used in the absorbable iron-based implantable device to promote a long-lasting absorption of iron.

[0047] In a further embodiment, the iron absorption promoter further includes at least one non-degradable polymeric structural unit. The non-degradable polymeric structural unit is a repeating unit on the non-degradable polymer molecular chain. The iron absorption promoter is formed by polymerization of a non-degradable polymer monomer with an antioxidant. In one embodiment, the non-degradable polymer is at least one selected from polyethylene glycol, polyacrylate, polysuccinate, polycarbonate, polyethylene vinyl acetate, poly(n-butyl methacrylate), polystyrene, polyvinylidene fluoride, polyvinyl pyrrolidone, and polyhexafluoroethylene.

[0048] In one embodiment, the iron absorption promoter further includes at least one degradable polymeric structural unit and at least one non-degradable polymeric structural unit. For example, the varieties of degradable and non-degradable polymers are the same as the varieties of degradable and non-degradable polymers listed above, respectively.

[0049] The addition of non-degradable polymeric structural unit may improve hydrophilicity or hydrophobicity, or mechanical properties of the iron absorption promoter, or stability and the release rate of the antioxidant.

[0050] It can be appreciated that in other embodiments, in addition to the non-degradable polymeric monomers listed above, other non-degradable polymeric monomers which are capable of polymerizing with an antioxidant or an antioxidant together with a degradable polymeric monomer to form an iron absorption promoter and are biocompatible with the human body, may also be used in the absorbable iron-based implantable devices described above to improve hydrophilicity or hydrophobicity, or mechanical properties of the iron absorption promoter, or stability and the release rate of the antioxidant.

[0051] For example, the antioxidant is copolymerized with the degradable polymer monomer and/or the non-degradable polymer monomer by random copolymerization, alternating copolymerization, block copolymerization or graft copolymerization. The iron absorption promoter formed by polymerization can be gradually release the antioxidant.

[0052] The lower mass of the iron absorption promoter has a novel effect on promoting the absorption of iron. The higher mass of the iron absorption promoter has a good effect on promoting the absorption of iron, but due to high mass and large volume thereof, physical properties of the absorbable iron-based implantable device are seriously affected. Therefore, the mass ratio of the iron absorption promoter to iron in the iron-based substrate is 0.053:1 in combination with the iron absorption effect and physical properties. In one embodiment, the mass ratio of the iron absorption promoter to iron in the iron-based substrate is 0.151:1.

[0053] In one embodiment, the absorbable iron-based implantable device further includes an active drug. The active drug may be coated directly on the iron-based substrate, or filled on the iron-based substrate, or dispersed in a film formed from the iron absorption promoter, or dispersed in the degradable polymer layer.

[0054] The active drug is at least one selected from antiangiogenic drugs, antiplatelet drugs, antithrombotic drugs, anti-inflammatory drugs, and anti-sensitizing drugs.

In particular, the antiangiogenic drug is at least one selected from taxol, rapamycin and rapamycin derivatives. The antiplatelet drug is cilostazol. The antithrombotic drug is heparin. The anti-inflammatory drug is dexamethasone. The anti-sensitizing drug is at least one selected from calcium gluconate, chlorpheniramine and cortisone.

[0055] An iron absorption promoter is attached to the iron-based substrate of the absorbable iron-based implantable device described above, the iron absorption promoter being a polymer containing an antioxidant structural unit. After the absorbable iron-based implantable device is implanted into a body, as the absorbable iron-based implantable device is gradually and slowly degraded, an antioxidant is gradually released, thereby enabling a long-acting effect and effectively delaying the release rate of the antioxidant, and the antioxidant which is released by the iron absorption promoter is interacted with an iron corrosion product more fully during the gradual corrosion process of the iron-based substrate, thereby promoting the absorption of the iron corrosion product.

[0056] The absorbable iron-based implantable device is a cardiovascular stent, a cerebrovascular stent, a peripheral vascular stent, a biliary tract stent, an esophageal stent, an airway stent, an occluding device, an orthopaedic implant and the like.

[0057] For preparation of the above-mentioned absorbable iron-based implantable device, first an iron-based substrate is prepared, and then an iron absorption promoter and/or a drug-containing degradable polymer layer and the like are formed on the iron-based substrate. For example, a lumen iron-based substrate may be formed by laser cutting, and then an iron absorption promoter and/or drug-containing degradable polymer layer may be formed on the iron-based substrate by plasma spraying, ultrasonic atomization spraying, and the like.

[0058] The above-mentioned iron absorption promoter is commercially available or is obtained by polymerization using a polymerization method. For instance, a melt polymerization process is used to copolymerize an antioxidant and a polymer monomer to form an iron absorption promoter, for example, the melt polymerization process is used to form a polylactic acid vitamin E copolymer. Alternatively, a ring-opening polymerization is used to form a copolymer of an antioxidant and a polymer monomer, for example, ascorbic acid is used as an initiator to initiate ring-opening polymerization of caprolactone to form ascorbic acid polycaprolactone copolymer. As another example, vitamin C (ascorbic acid), anhydrous potassium carbonate, and N, N-dimethylformamide are dissolved and mixed to react to form a benzyl-protected vitamin C precursor. After the benzyl protected vitamin C precursor is dissolved in dichloromethane, the solution of acrylamide is slowly added dropwise to form an acrylate-modified benzyl-protected vitamin C monomer. A polylactic acid homopolymer is formed by ring-opening polymerization of L-type lactide. The homopolymer and the vitamin C precursor are synthesized under the condition of copper bromide and anhydrous toluene to form a block compolyer which is then debenzylated by hydrogen to obtain polylactic acid-block-polyascorbic acid acrylate copolymer.

[0059] The absorbable iron-based implantable device described above are further illustrated by the following examples.

[0060] The following characterization and test methods are employed in the following embodiments:

[0061] 1. Characterization of the effect of promoting the iron absorption

[0062] Taking an iron-based alloy vascular stent containing an iron absorption promoter as an example, a test that an iron-based alloy stent containing the iron absorption promoter was implanted into a healthy mini porcine coronary artery model was performed to detect the absorption/metabolism percentage of iron in a blood vessel where the iron-based alloy vascular stent was positioned, and the effect of promoting the iron absorption by the iron absorption promoter in vivo is evaluated by the absorption/metabolism percentage of iron. The method was as follows: measuring the mass of iron in the implanted iron-based alloy vascular stent as M.sub.0, then implanting iron-based alloy vascular stent containing the iron absorption promoter in the same batch and same specification into a porcine coronary artery, taking out the iron-based alloy vascular stent and a blood vessel segment where the iron-based alloy vascular stent was positioned after 36 months, carefully trimming redundant matters such as adipose tissue and myocardial tissue surrounding the outer membrane of the blood vessel to ensure the length of the blood vessel equivalent to that of the iron-based alloy vascular stent implanted therein, measuring the iron content in the iron-based alloy vascular stent as well as the blood vessel segment where the iron-based alloy vascular stent was positioned as M.sub.1, and the iron ion content in the blank blood vessel was too low and can be ignored herein. Thus during the implantation period, the iron absorption/metabolism percentage was W, W=(M.sub.0M.sub.1)/M.sub.0*100%.

[0063] Here, the method for testing the iron content was as follows: digesting the stent or the stent together with the blood vessel in a microwave digestion instrument by using concentrated nitric acid, then testing the concentration of iron ion in the solution by using an Agilent 240FS atomic absorption spectrometer under the conditions of a wavelength of 248.3 nm, a slit of 0.2 nm, acetylene as combustion-supporting gas and a flow rate of 2.0 L/min, and further calculating the mass of iron in the sample.

[0064] The better the effect of promoting iron absorption by the iron absorption promoter, the higher the percentage of iron absorption/metabolism. For an iron-based alloy implantable device without an antioxidant or an iron-based alloy implantable device containing a small molecular antioxidant, the iron absorption/metabolism percentage was generally within 15% after implantation into a porcine coronary artery for 36 months, while after adding a high molecular iron absorption promoter, the iron absorption/metabolism percentage was more than 15%, and the most desirable effect of promoting iron absorption was that the iron absorption/metabolism percentage equaled to 100%.

[0065] 2. The method for detecting the weight-average molecular weight of the polymer:

[0066] The weight-average molecular weight of the polymer was detected using a GPC-multi-angle light scattering detector from Wyatt, USA, combined with a molecular weight test system. The test system included a liquid phase pump and a sample injector from Agilent, USA, an Agilent PL MIXED-C type GPC column (size: 7.5300 mm, 5 microns) from Agilent, USA, and a multi-angle light scattering detector and a differential detector from Wyatt, USA. the detection condition was as follows: fluid phase: tetrahydrofuran; pump rate: 1 mL/min; loading volume of sample: 100 L; laser wavelength: 663.9 nm; test temperature: 35 C.

Embodiment 1

[0067] Proanthocyanidin polymer having a weight-average molecular weight of 1000 was dissolved in ethyl acetate to formulate a solution having the concentration of the proanthocyanidin polymer of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 4.0 mm and a wall thickness of 60 microns to form an iron absorption promoter coating having a thickness of 5 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.05:1. A polylactic acid (having a weight-average molecular weight of 20,000) rapamycin-loaded coating having a thickness of 3 microns was continuously sprayed on the surface of the iron absorption promoter coating to obtain the iron-based alloy coronary stent. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 20%.

Embodiment 2

[0068] Tocopherol polyethylene glycol maleate having a weight-average molecular weight of 5000 was dissolved in ethyl acetate to formulate a solution having the concentration of tocopherol polyethylene glycol maleate of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 3.0 mm and a wall thickness of 50 microns to form an iron absorption promoter coating having a thickness of 10 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.15:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 26%.

Embodiment 3

[0069] Polylactic acid block polycysteine coupled glutathione having a weight-average molecular weight of 10,000 was dissolved in ethyl acetate to formulate a solution having a concentration of 5 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 3 mm and a wall thickness of 50 microns to form an iron absorption promoter coating having a thickness of 15 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.25:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overspread ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 30%.

Embodiment 4

[0070] Polylactic acid vitamin E copolymer having a weight-average molecular weight of 50,000 was dissolved in dichloromethane to formulate a solution having the concentration of 5 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 3.0 mm and a wall thickness of 50 microns to form an iron absorption promoter coating having a thickness of 15 microns, a polylactic acid (having a weight-average molecular weight of 20,000) paclitaxel-loaded drug layer having a thickness of 3 microns was continuously sprayed on the surface of the iron absorption promoter coating to obtain an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.25:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 35%.

Embodiment 5

[0071] Lipoic acid polylysine polyethylene glycol copolymer having a weight-average molecular weight of 100,000 was dissolved in ethyl acetate to formulate a solution having the concentration of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 3.0 mm and a wall thickness of 50 microns to form an iron absorption promoter coating having a thickness of 25 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.5:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 40%.

Embodiment 6

[0072] Ascorbic acid polycaprolactone copolymer having a weight-average molecular weight of 300,000, polylactic acid having a weight-average molecular weight of 100,000 and dexamethasone were dissolved in ethyl acetate based on a blending ratio of 1:1:1 by mass to formulate a solution having a total concentration of 6 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 3.0 mm and a wall thickness of 50 microns to form a blended coating containing an iron absorption promoter with a thickness of 25 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 0.5:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 45%.

Embodiment 7

[0073] Polylactic acid block polyascorbic acid acrylate having a weight-average molecular weight of 500,000 was dissolved into trichloromethane to formulate a solution having a concentration of 1.5 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 2.5 mm and a wall thickness of 40 microns to form an iron absorption promoter coating having a thickness of 33 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 1:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 55%.

Embodiment 8

[0074] Lipoic acid glucan copolymer having a weight-average molecular weight of 500,000 was dissolved in ethyl acetate to formulate a solution having the concentration of the lipoic acid glucan copolymer of 2 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 2.5 mm and a wall thickness of 40 microns to form an iron absorption promoter coating having a thickness of 50 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 2:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 60%.

Embodiment 9

[0075] Lipoic acid polyaspartic acid polyethylene glycol copolymer having a weight-average molecular weight of 100,000 (the preparation method is performed according to the method disclosed in CN1055242722 A) is dissolved in ethyl acetate to formulate a solution having the concentration of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 2.5 mm and a wall thickness of 30 microns to form an iron absorption promoter coating having a thickness of 50 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of the iron absorption promoter to iron in the iron-based alloy coronary stent substrate was 3:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 60%.

Comparative Example 1

[0076] Proanthocyanidin having a molecular weight of 594 was dissolved in ethanol to formulate a solution having a concentration of the proanthocyanidin of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 4.0 mm and a wall thickness of 60 microns to form an iron absorption promoter coating having a thickness of 5 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of proanthocyanidin to iron in the iron-based alloy coronary stent substrate was 0.05:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed, and the percentage of iron metabolized by the tissue tested as described above was 10%.

Comparative Example 2

[0077] Vitamin C was dissolved in purified water to formulate a solution having a concentration of vitamin C of 10 mg/mL, the formulated solution was then uniformly sprayed on the inner surface and the outer surface of an iron-based alloy coronary stent substrate having a nominal diameter of 2.5 mm and a wall thickness of 40 microns to form an iron absorption promoter coating having a thickness of 33 microns, thus obtaining an iron-based alloy coronary stent. Here, the mass ratio of vitamin C to iron in the iron-based alloy coronary stent substrate was 1:1. The prepared iron-based alloy coronary stent was implanted into a mini porcine coronary artery, maintaining an overdilation ratio in the range of 1.1:1 to 1.2:1 in the implantation process. A follow-up was performed 36 months after implantation, the remaining iron-based alloy coronary stent and surrounding vascular tissue thereof were removed and the percentage of iron metabolized by the tissue tested as described above was 15%.

[0078] It can be seen that after implantation of the iron-based alloy coronary stents of Embodiments 1-9, the percentage of iron metabolized by the tissue is higher than that of Comparative Example 1 and Comparative Example 2, indicating that the iron absorption promoter of Embodiments 1-9 does promote a long-acting iron absorption.

[0079] The various features of the above-mentioned embodiments may be combined in any way, and in order to simplify the description, not all possible combinations of the features of the above-mentioned embodiments are described, however, as long as there is no conflict between these features, they should be considered to be within the scope of the description.

[0080] The embodiments described above represent only a few embodiments of the present disclosure, the description of which is specific and detailed, but should not be construed to limit the scope of the present disclosure. It should be noted that several variations and modifications may be made by those of ordinary skill in the art without departing from the spirit of the present disclosure, which all fall within the scope of the present disclosure.