Tire

Abstract

A tire 10 has a decoration portion 15 using a paint on a surface of a side portion 12. The decoration portion 15 has a white paint layer 16 formed on at least a part of the decoration portion 15, a color paint layer 17 disposed by laminating on the white paint layer 16 and having a thickness less than the thickness of the white paint layer 16, and a protective layer 18 disposed by laminating on the color paint layer 17 and having the thickness less than the thickness of the white paint layer 16. The elastic modulus of the protective layer is larger than the elastic modulus of the white paint layer and the color paint layer. A thickness of the decoration portion 15 as a whole, including the white paint layer 15, the color paint layer 17 and the protective layer 18, is 150 m or less.

Claims

1. A tire comprising a decoration portion using a paint on a surface of a side portion, wherein: the decoration portion having a white paint layer disposed on at least a part of the decoration portion, a color paint layer having a thickness lower than a thickness of the white paint layer and being disposed by laminating on an outer side in the tire width direction of the white paint layer, and a protective layer having a thickness lower than the thickness of the white paint layer, an elastic modulus higher than both the white paint layer and the color paint layer and being disposed by laminating on at least an outer side in the tire width direction of the color paint layer, a thickness of the decoration portion, including the white paint layer, the color paint layer and the protective layer, being 150 m or less.

2. The tire according to claim 1, wherein: the thickness of the decoration portion as a whole is 95 m or less.

3. The tire according to claim 1, wherein: an elastic modulus of the protective layer is 110.sup.7 or more to 110.sup.8 Pa or less.

4. The tire according to claim 3, wherein: at least a part of the protective layer is disposed by laminating on the side portion without interposition of the white paint layer and the color paint layer, and the thickness of the protective layer is 10% or more of the thickness of the decoration portion as a whole.

5. The tire according to claim 3, wherein: the thickness of the protective layer is 20 m or less.

6. The tire according to claim 3, wherein: the thickness of the protective layer is 30% or less of a paint thickness in total of the white paint layer and the color paint layer.

7. The tire according to claim 3, wherein: the thickness of the decoration portion as a whole is 95 m or less.

8. The tire according to claim 1, wherein: at least a part of the protective layer is disposed by laminating on the side portion without interposition of the white paint layer and the color paint layer, and the thickness of the protective layer is 10% or more of the thickness of the decoration portion as a whole.

9. The tire according to claim 8, wherein: the thickness of the protective layer is 20 m or less.

10. The tire according to claim 8, wherein: the thickness of the protective layer is 30% or less of a paint thickness in total of the white paint layer and the color paint layer.

11. The tire according to claim 8, wherein: the thickness of the decoration portion as a whole is 95 m or less.

12. The tire according to claim 1, wherein: the thickness of the protective layer is 20 m or less.

13. The tire according to claim 12, wherein: the thickness of the protective layer is 30% or less of a paint thickness in total of the white paint layer and the color paint layer.

14. The tire according to claim 12, wherein: the thickness of the decoration portion as a whole is 95 m or less.

15. The tire according to claim 1, wherein: the thickness of the protective layer is 30% or less of a paint thickness in total of the white paint layer and the color paint layer.

16. The tire according to claim 15, wherein: the thickness of the decoration portion as a whole is 95 m or less.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) In the accompanying drawings:

(2) FIG. 1 is a cross-sectional diagram in the tire width direction of the tire according to this disclosure.

DETAILED DESCRIPTION

(3) Hereinafter, an embodiment of this disclosure will be described with reference to the drawing.

(4) First, a tire according to an embodiment of this disclosure is described. FIG. 1 is a cross-sectional diagram in the tire width direction of the tire according to this embodiment. As illustrated in FIG. 1, tire 10 includes a tread portion 11 and a side portion 12. The tread portion 11 contacts the road surface. The side portion 12 includes a sidewall portion 13 and a bead portion 14. More specifically, the side portion 12 is a portion within a range from an end edge of outer side in a tire width direction of the tread surface to a rim fitting portion of the bead portion 14.

(5) The tire 10 of this embodiment has a decoration portion 15 on the side portion 12. The decoration portion 15 displays a marking, a decoration and the like by using a paint of white color or other colors. The decoration portion 15 includes on at least a part thereof a white paint layer 16, a color paint layer 17 laminated thereon, and a further laminated protective layer 18. The decoration portion 15 may be in a manner of continuous or intermittent along a circumferential direction of the side portion 12, or in a manner partially formed on the side portion 12. Further, the decoration portion 15 may have a configuration either including only a part formed by laminating the white paint layer 16, the color paint layer 17 and the protective layer 18, or including such part in a part thereof. The thickness of the decoration portion 15 as a whole, including the white paint layer 16, the color paint layer 17 and the protective layer 18, is necessarily 150 m or less, preferably 95 m or less. Further, the thickness of the decoration portion 15 as a whole refers to a thickness at a maximum thickness position within the side portion 12. Further, in FIG. 1, for the sake of easiness to understand, illustrated is a mode in which the white paint layer 16, the color paint layer 17 and the protective layer 18 have exaggerated thicknesses.

(6) The white paint layer 16 is disposed on at least a part of the decoration portion 15 by, e.g., printing a white paint. The white paint layer 16 may be directly formed or may be formed via such as primer, on the surface of the side portion 12.

(7) The color paint layer 17 is disposed by laminating a color paint having a color different form the white paint by, e.g., printing, on at least a part of the outer side in tire width direction of the white paint layer 16. Moreover, as for the color paint layer 17, the thickness of the color paint layer 17 is necessarily less than the thickness of the white paint layer 16. Further, the thicknesses of the color paint layer 17 and the white paint layer 16 refer to each thickness at a maximum thickness position within the decoration portion 15. Further, for example, a marking, a decoration and the like are applied on the white paint layer 16 by using the color paint layer 17. Further, the white paint layer 17 may be directly formed or may be formed via such as other layer, on the surface of the side portion 16.

(8) In this embodiment, the white paint and the color paint are a UV ink which contain as primary components, e.g., a photopolymerization initiator, oligomer, monomer or coloring agent, and may be optionally compounded with ultraviolet absorber, antioxidant, photostabilizer, adhesion promoter, rheology adjusting agent, dispersant and the like.

(9) The protective layer 18 is disposed by laminating on at least an outer side in the tire width direction of the color paint layer 17, by using a transparent material such as OP varnish, aqueous urethane resin and the like. Further, it is preferable that at least a part of the protective layer 18 is disposed on the surface of the side portion 12 in a manner exceeding an outer edge where the white paint layer 16 is formed, without interposition of the white paint layer 16 and the color paint layer 17 (see the reference sign A). Moreover, the thickness of the protective layer 18 is necessarily less than the thickness of the white paint layer 16, and is preferably 10% or more of the thickness of the decoration portion 15 as a whole when disposed on the surface of the side portion 12 without interposition of the white paint layer 16 and the color paint layer 17, is preferably 20 m or less, and is preferably 30% or less of the paint thickness in total of the white paint layer 16 and the color paint layer 17. Further, the thickness of the protective layer 18 and the paint thickness refer to thicknesses at the maximum thickness position within the decoration portion 15. Moreover, the elastic modulus of the protective layer 18 is necessarily larger than the elastic modulus of either the white paint layer 16 or the color paint layer 17, and is preferably 110.sup.7 Pa or more to 110.sup.8 Pa or less. Further, the elastic modulus a value measured according to JIS K7244-4 (ISO 6721-4) Tensile Vibration.

(10) According to the tire of this embodiment having the aforementioned configuration, since the thickness of the decoration portion 15 as a whole is 150 m or less, it is possible that the decoration portion 15 as a whole obtains tracking to deformation of the side portion 12, and the decoration portion 15 obtains excellent resistance to crack with respect to assumed distortion of the side portion 12. Moreover, according to the tire of this embodiment, as mentioned above, since the thickness of the white paint layer 16 is larger than the thickness of the color paint layer 17 and the protective layer 18, it is possible to render the white paint layer 16 having an elastic modulus lower than the protective layer 18 distortion occurring in the side portion 12. Moreover, due to interposition of the color paint layer 17 between the white paint layer 16 and the protective layer 18, it is possible to greatly suppress the effect of distortion of the protective layer 18. Therefore, it is possible to use a material having the elastic modulus capable of achieving the required resistance to external damage to the protective layer 18, and simultaneously, the protective layer 18 is capable of obtaining the required resistance to crack with respect to assumed distortion of the side portion 12. According to the aforementioned combination of effects, the decoration portion 15 is capable of having both excellent resistance to external damage and excellent resistance to crack. Moreover, according to the tire of this embodiment, since the color paint layer 17 is disposed by laminating on the white paint layer 16, comparing to a configuration directly forming the color paint layer 17 on the side portion 12, it is possible to improve the coloring of the color paint layer 17.

(11) Moreover, by setting the thickness of the white paint layer 16 to be larger than the thickness of the white paint layer 17, it is possible to improve the coloring and the decorative property of the color paint layer 17.

(12) Moreover, by setting the elastic modulus the protective layer 18 to be 110.sup.7 Pa or more, it is possible to obtain sufficient resistance to external damage. Moreover, by setting the elastic modulus the protective layer 18 to be 110.sup.8 Pa or less, it is possible to obtain sufficient resistance to crack.

(13) Moreover, by setting the thickness of the protective layer 18 to be 10% or more of the thickness of the decoration portion 15 as a whole when the protective layer 18 is disposed on the surface of the side portion 12 without interposition of the white paint layer 16 and the color paint layer 17, it is possible to suppress occurrence of crack at the border position described in the following. Within the decoration portion 15, if the difference in thickness is too large between a region configured merely with the protective layer 18 and a region configured with other layers (the white paint layer 16 and the color paint layer 17) as well, the probability of occurrence of crack at a border position between the two regions is increased. For this reason, according to this embodiment, by setting an upper limit of the difference in thickness, it is possible to suppress the occurrence of crack at the border position. Moreover, by disposing the protective layer 18 on the surface of the side portion 12 without interposition of the white paint layer 16 and the color paint layer 17, it becomes possible to sufficiently protect the white paint layer 16 and the color paint layer 17.

(14) Moreover, by setting the thickness of the protective layer 18 to be 20 m or less, distortion to the protective layer 18 is further suppressed, and the deformation volume due to distortion of the protective layer 18 is suppressed. Accordingly, it is possible to obtain sufficient resistance to crack.

(15) Moreover, by setting the thickness of the protective layer 18 to be 30% or less of the paint thickness, it is possible to further suppress concentration of distortion to the protective layer 18. Therefore, the deformation volume of distortion of the protective layer 18 itself is further suppressed. Accordingly, it is possible to obtain sufficient resistance to crack.

(16) Moreover, by setting the thickness of the decoration portion 15 as a whole to be 95 m or less, the decoration portion 15 as a whole obtains tracking to deformation of the side portion 12, and a sufficient resistance to crack is obtained.

EXAMPLES

(17) Next, tires according to the present disclosure were produced, and the resistance to crack, the resistance to external damage and the coloring were evaluated, as described below. With the specifications as shown in Table 1, produced were tires having a tire size of 195/65R15 according to Comparative Examples 1 to 3 and Examples 1 to 11, in which a white paint layer 16 and a color paint layer 17 were disposed by using a white paint and a color paint of UV curable ink (made by Miyama Co., Ltd.), and a protective layer was disposed by using an aqueous urethane resin. With respect to the tires of Comparative Examples 1 to 3 and the tires of Examples 1 to 11, resistance to crack, resistance to external damage and coloring were evaluated with the following methods. The results are as shown in Table 1.

(18) (Resistance to Crack Evaluation Test)

(19) The tires of Comparative Examples 1 to 3 and Examples 1 to 11 were mounted to a rim of size 6JJ (a standard rim of JATMA standard), applied an air pressure of 240 kPa (a maximum air pressure of JATMA standard), and subjected to a drum test over 10000 km (10000 km test) at a drum speed of 60 km/h, loading a drum load of 615 kg (a JATMA maximum load). Moreover, a drum test over 30000 km (30000 km test) was performed at same conditions as the 10000 km test. After loading the drum load, the resistance to crack was evaluated by judging via visual observation, respectively for the 10000 km test and the 30000 km test, whether a crack exists in laminating parts of the white paint layer 16 and the color paint layer 17. The evaluation results are as shown in Table 1. Further, the required resistance to crack is a performance that no crack occurs in the 10000 km test.

(20) (Resistance to External Damage Evaluation Test)

(21) A resistance to external damage test (20-time coin test) was performed by scratching with a coin for 20 times the decoration portion 15 of the tires of Comparative Example 1 to 3 and Examples 1 to 11. Moreover, the resistance to external damage test (100-time coin test) was performed by scratching with a coin for 100 times. After scratching with a coin, the resistance to external damage was evaluated by judging via visual observation whether an external damage occurred in the decoration portion 15. The evaluation results are shown in Table 1. Further, the required resistance to external damage is a performance that no external damage occurs in the 20-time coin test.

(22) (Coloring Evaluation Test)

(23) The coloring was evaluated by observing the tires of Comparative Examples 1 to 3 and Examples 1 to 11 by 20 observers, and aggregating a questionnaire graded on 3 steps with respect to the coloring of the color paint layer 17. The evaluation results are as shown in Table 1. In Table 1, the coloring of the examples were evaluated as C if evaluated as excellent in the questionnaire graded on 3 steps by less than 10 observers among the 20, as B if by 10 or more and less than 15, and as A if by 15 or more. Further, the required coloring is a performance evaluated as A or B.

(24) TABLE-US-00001 TABLE 1 Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 1 Example 2 Example 3 Example 4 Decoration portion thickness [m] 60 160 60 60 150 95 60 Protective layer thickness [m] 10 27 30 10 25 16 10 Protective layer thickness/decoration 17 17 50 17 17 17 17 portion thickness [%] Protective layer thickness/paint 20 20 100 20 20 20 20 thickness [%] Presence of white paint layer Absent Present Present Present Present Present Present Comparison of white paint layer Small Small Large Small Small Small Small thickness (*1) Protective layer elastic modulus [Pa] 5 10.sup.7 5 10.sup.7 5 10.sup.7 5 10.sup.7 5 10.sup.7 5 10.sup.7 9 10.sup.6 Presence of 10000-km test crack Absent Present Present Absent Absent Absent Absent Presence of 30000-km test crack Absent Present Present Absent Present Absent Absent 20-time coin test Absent Absent Absent Absent Absent Absent Absent 100-time coin test Absent Absent Absent Absent Absent Absent Present Coloring C A A A A A A Example Example Example 5 Example 6 Example 7 Example 8 Example 9 10 11 Decoration portion thickness [m] 60 60 60 60 60 60 60 Protective layer thickness [m] 10 10 10 20 25 6 5 Protective layer thickness/decoration 17 17 17 33 42 10 8 portion thickness [%] Protective layer thickness/paint 20 20 20 50 71 11 9 thickness [%] Presence of white paint layer Present Present Present Present Present Present Present Comparison of white paint layer Small Small Small Small Small Small Small thickness (*1) Protective layer elastic modulus [Pa] 5 10.sup.7 1 10.sup.8 2 10.sup.8 5 10.sup.7 5 10.sup.7 5 10.sup.7 5 10.sup.7 Presence of 10000-km test crack Absent Absent Absent Absent Absent Absent Absent Presence of 30000-km test crack Absent Absent Present Absent Present Absent Present 20-time coin test Absent Absent Absent Absent Absent Absent Absent 100-time coin test Absent Absent Absent Absent Absent Absent Absent Coloring A A A A A A A The *1 in Table 1 shows small when the thicknesses of both the color paint layer 17 and the protective layer 18 are less than the thickness of the white paint layer 16, and shows large when at least one is more than the thickness of the white paint layer 16.

(25) As shown in Table 1, in Examples 1 to 11, no crack occurred in the 10000 km test. On the other hand, in Comparative Examples 2 and 3, a crack occurred in the 10000 km test. Therefore, if the thicknesses of both the color paint layer 17 and the protective layer 18 are less than the thickness of the white paint layer 16 and the thickness of the decoration portion 15 as a whole is 150 m or less, it is understood that the resistance to crack is sufficient. Moreover, in Examples 1, 3 to 6, 8 and 10, no crack occurred in the 30000 km test. On the other hand, since a crack occurred in the 30000 km test in Example 7, it is understood that the resistance to crack is further improved by setting the elastic modulus of the protective layer 18 to be 110.sup.8 Pa or less. Moreover, on the other hand, since a crack occurred in the 30000 km test in Example 11, it is understood that the resistance to crack is further improved by setting the thickness of the protective layer 18 to be 10% of more of the thickness of the decoration portion 15 as a whole. Moreover, on the other hand, since a crack occurred in the 30000 km test in Examples 2 and 9, it is understood that the resistance to crack is further improved by setting the thickness of the protective layer 18 to be 20 m or less. Moreover, on the other hand, since a crack occurred in the 30000 km test in Example 9, it is understood that the resistance to crack is further improved by setting the thickness of the protective layer 18 to be 30% or less of the paint thickness. Moreover, on the other hand, since a crack occurred in the 30000 km test in Example 2, it is understood that the resistance to crack is further improved by setting the thickness of the decoration portion 15 as a whole to be 95 m or less.

(26) As shown in Table 1, in Examples 1 to 11, no external damage occurred in the 20-time coin test. Accordingly, it is understood that the decoration portion 15 has the required resistance to external damage by including a protective layer 18. Moreover, in Examples 1 to 3 and 5 to 11, no external damage occurred in the 100-time coin test. On the other hand, since an external damage occurred in the 100-time coin test in Example 4, it is understood that the resistance to external damage is further improved by setting the elastic modulus of the protective layer 18 to be 110.sup.7 Pa or more.

(27) Moreover, as shown in Table 1, it is understood that the coloring is improved in Examples 1 to 11, comparing to Comparative Example 1. Accordingly, it is understood that the decoration portion 15 has an improved coloring by including a white paint layer 16.

REFERENCE SIGNS LIST

(28) 10 tire 11 tread portion 12 side portion 13 sidewall portion 14 bead portion 15 decoration portion 16 white paint layer 17 color paint layer 18 protective layer