Cable wrapping tape

Abstract

The present disclosure relates to a cable wrapping tape, including a band-shaped support (1) made of a textile fabric with warp threads (2) and weft threads (3) made of a PET plastic. The warp and weft threads (2, 3) are made of filament yarns, the size of the weft threads (3) being larger than the size of the warp threads (2). An adhesive coating is applied to the support (1). The size of the warp threads (2) is larger than/equal to 20 dtex and smaller than/equal to 40 dtex.

Claims

1. A cable wrapping tape, comprising a support (1) made of a textile fabric consisting of warp threads (2) and weft threads (3), the warp and weft threads (2, 3) being made of filament yarns made of PET plastic, the weft threads (3) being larger than the size of the warp threads (2), and an adhesive layer (4) applied to the support (1), wherein the size of the warp threads (2) is at least 20 dtex and at most 40 dtex, wherein the size of the weft threads (3) is between 155 dtex and 200 dtex, wherein the warp threads (2) have a thread count of at least 20 per cm and at most 30 per cm and a filament count in a range from 24 through 96 per warp thread (2), wherein the weft threads (3) have a thread count of at least 28 per cm and at most 40 per cm and a filament count in a range from 24 through 36 filaments per weft thread (3), wherein the grammage of the support (1) is at least 40 g/m.sup.2 and at most 100 g/m.sup.2, wherein the coated adhesion tape has a thickness of at least 0.08 mm and at most 0.12 mm, wherein the warp and weft thread are spun dyed, and wherein the support has a tear resistance in a range of 2500 mN through 8000 mN, measured according to DIN EN ISO 1974:2012-09.

2. The cable wrapping tape according to claim 1, wherein the adhesive layer (4) is made of an acrylate adhesive or of synthetic rubber.

3. The cable wrapping tape according to claim 1, wherein the grammage of the support (1) is between 80 g/m.sup.2 and 100 g/m.sup.2.

4. The cable wrapping tape according to claim 1, wherein the warp threads and the weft threads are selected from the group consisting of pre-oriented yarns, fully drawn yarns, and draw-textured yarns.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) In the drawings,

(2) FIG. 1 shows a top view of an adhesive tape according to the present invention and

(3) FIG. 2 shows a cross section along II-II in FIG. 1.

DETAILED DESCRIPTION OF THE DRAWINGS

(4) As is apparent from FIG. 1, a cable wrapping tape according to the present invention consists of a band-shaped support 1 made of a textile fabric, which is formed by warp threads 2 and weft threads 3. The material of the warp threads 2 and of the weft threads 3 is a PET plastic, wherein polyester is particularly preferred. The warp and weft threads 2, 3 are made of filament yarns. Filament yarns theoretically consist of threads having an infinite length, the so-called filaments. As a rule, filament yarns are not twisted, that is, the filaments are basically parallel to one another because they also stay together without twisting. A distinction is made between monofilaments, where only one fiber, that is one filament, forms the thread, and multifilaments, which consist of more than two individual fibers. Filament yarns of the following qualities are available on the market:

(5) 1. POY Thread

(6) So-called pre-oriented yarns which are pre-oriented filament yarns, made of a thermoplastic material like polyester or polyamide which was spun at high speed and partially drawn.

(7) 2. FDY Thread (Fully Drawn Thread)

(8) A smooth, thermoplastic filament yarn which is fully drawn and wound between two godets after having been spun and cooled by an air jet in the cooling duct.

(9) 3. DTY Yarn (DTY, Draw-Textured Yarns)

(10) Draw-textured threads, which are mostly manufactured by false twist draw texturing with integrated drawing.

(11) An adhesive coating 4 made preferentially of an acrylate adhesive or synthetic rubber is applied to one side of the support 1, its underside in the shown example. It is fundamental to the invention that the size of the warp threads 2 is larger than/equal to 20 dtex and smaller than/equal to 40 dtex, the size of the weft threads 3 being smaller than the size of the warp threads 2. In this case, it is particularly advantageous if the count of the warp threads 2 is smaller than/equal to 20 per cm and smaller than/equal to 30 per cm. Advantageously, the filament count, that is, the count of fibers per warp thread 2 is 24 to 96 filaments, preferentially 34 to 36 filaments. It is also conceivable that the count of warp threads 2 and weft threads 3 have a filament count of 36, 48 and 96 filaments. Furthermore, it is an advantage according to the present invention, if the count of weft threads 3 is smaller than/equal to 28 per cm and smaller than/equal to 40 per cm. It is also an advantage if the size of the weft threads 3 is between 155 dtex and 200 dtex, preferentially 167 dtex. The support fabric advantageously has weft threads 3, which have from 24 to 96 filaments per weft thread 3, preferentially 36 filaments (fibers). It is a further advantage if the grammage of the support 1 is larger than/equal to 40 g/m.sup.2 and smaller than/equal to 120 g/m.sup.2, in particular the grammage of the support 1 can be larger than/equal to 80 g/m.sup.2 and smaller than/equal to 100 g/m.sup.2. Furthermore, it is advantageous according to the present invention, if the warp threads 2 and/or the weft threads 3 are intermingled and/or texturized. It can also be provided according to the present invention, that the warp threads 2 and/or the weft threads 3 are spun dyed. In this context, spin dyeing is to be understood such that the threads are dyed during the extrusion process of the filaments that form the threads. Advantageous embodiments of an adhesive tape according to the present invention are shown in Table 1 below.

(12) TABLE-US-00001 TABLE 1 Support Material Without Adhesive coating Construction Construction Construction Unit 1 2 3 Support material Polyester Polyester Polyester without adhesive coating Grammage g/m.sup.2 40-70 70-100 70-100 Type of fiber 100% 100% 100% polyester polyester polyester Type of yarn Filament Filament Filament Warp threads/weft intermingled/ intermingled/ intermingled/ threads textured and textured and textured and spun dyed spun dyed spun dyed Count of warp 1/cm 20 30 30 threads Filament count unit 24 24 24 warp threads Size of the warp dtex 40 33 20 threads Count of weft threads 1/cm 30 35 35 Size of the weft dtex 167 167 167 threads Filament count unit 36 36 36 warp [sic, weft] threads

(13) Table 2 provides an overview of the mechanical properties of the individual embodiments according to Table 1. Table 3 includes technical data of the adhesive tape according to the present invention as per Table 1 compared to prior art adhesive tapes.

(14) TABLE-US-00002 TABLE 2 Support Material Constructions 1 to 3 Without Adhesive coating Patent EP Construction Construction Construction Patent EP 1990393 Test Unit 1 2 3 1074595 A1 Support material polyester polyester polyester polyester polyester without adhesive coating Grammage g/m.sup.2 40-70 70-100 70-100 65-70 70-75 Thickness mm 0.10 0.10 0.08 0.10 0.12 Elongation at % 8-10 8-20 8-20 23-30 25-28 break Breaking force N/cm 60-70 50-60 40-55 60-70 65-85 Air permeability l/m.sup.2s 60-100 80-200 100-300 60-200 60-200 Tear resistance mN 5,000- 4,000- 2,500- 6,000- 9,000- 8,000 7,000 6,000 9,000 13,000

(15) TABLE-US-00003 TABLE 3 This Table Refers to the Coated Adhesive Tape Con- structions Patent EP Patent EP Test Unit 1-3 1074595 1990393 Thickness mm 0.08-0.12 0.15 0.15 Elongation at break % 10-20 28-35 20-30 Tear resistance N/cm 40-80 60-70 65-85 Adhesive force steel N/cm 2.0-5.5 4.0-5.0 4.0-8.0 Adhesive strength N/cm 2.0-6.0 2.0-3.0 2.0-6.0 tape back Unwind adhesion N 2-9 2-9 2-9 Flagging (30 min.) mm 0-1 0-1 0-1 Flagging (24 h) mm 0-1 0-1 0-1 Abrasion 5 mm- strokes 20-75 35-70 130-150 mandrel (Class A) (Class A) (Class B) Noise damping dB (A) 1-1.5 1-1.6 1-1.6 (Class A) (Class A) (Class A) Hand tearability ./. Transversely Transversely Transversely as per LV312 tearable tearable tearable

(16) An adhesive tape according to the present invention is characterized by a very good temperature stability according to LV 312 within a range of 105 C. to 150 C., can be processed manually or mechanically, has a low strip thickness, is pliant and flexible, and consists of a rot resistant backing. By using the embodiment according to the present invention, it is possible to dispense with finishing steps, such as dressing or rewashing, which is required by prior art adhesive tapes. The basic data of the backing 1 and of the adhesive tape according to the present invention, and the shown parameters contained in the tables mentioned above are determined according to the following standards:

(17) TABLE-US-00004 TABLE 4 Date of the New currently DIN Standards designation valid version EN ISO 2286-2 1998-07 weight per unit area DIN 53830-3 1981-05 determination of linear density of yarns DIN EN 1049-2 1994-02 determination of threads per unit length DIN EN 1942 2008-06 thickness DIN EN 14410 2003-06 breaking strength/ elongation DIN EN 1939 2003-12 peel adhesion DIN EN 1944 1996-04 unwinding force DIN EN 21974 DIN EN ISO 2012-09 tear resistance 1974:2012-09 DIN EN ISO 1995-12 permeability of fabrics 9237 to air DIN 53 362 2003-10 flexural strength flagging according to LV 312, version: 2009/10 LV 312 LV 312-1 2009-10 protection systems for cable harnesses in motor vehicles, adhesive tapes; test guideline

(18) The manual tearability was determined according to LV 312.

(19) The abrasion test was carried out with an abrasion tester according to the joint test guideline of AUDI, BMW, DC and VW Adhesive Tapes for Cable Sets in Motor Vehicles, LV 312, on a 5-mm mandrel, and included checks every 10 strokes. The final value was achieved as soon as the adhesive coating on the back side (adhesive coating 4) was abraded from the support 1.

(20) The invention is not restricted to the exemplary embodiments, but also includes all equivalent embodiments within the scope of the invention. It is expressly pointed out that the exemplary embodiments are not restricted to all combined features, but each individual partial feature as such can also be fundamental to the present invention independently of all other partial features. As a person skilled in the art will readily appreciate, the above description is meant as an illustration of the principles of this invention. This description is not intended to limit the scope or application of this invention in that the invention is susceptible to modification, variation and change, without departing from spirit of this invention, as defined in the following claims.