FLAME-RETARDANT POLYMER; METHOD FOR PREPARING IT AND THERMOPLASTIC POLYMER COMPOSITION COMPRISING IT

Abstract

The invention relates to a polymer which is useful as flame-retardant polymer. The invention also relates to a method of preparing said polymer and to a thermoplastic polymer composition comprising said polymer. The thermoplastic polymer composition can be used for the production of molded articles or yarns having excellent flame-retardant properties in order to ensure adequate fire protection.

Claims

1. A polymer, obtainable by polycondensation of a) at least one phosphorous-containing monomer selected from adducts of: a1) 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and/or nuclear substituted DOPO derivatives, with a2) at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof; b) at least one secondary diamine; and c) optionally other monomers.

2. The polymer according to claim 1 having a phosphorous content of at least 4% by weight, each of the total weight of the polymer.

3. The polymer according to claim 1, wherein the phosphorous-containing monomer a) is selected from a compound represented by the following general formula (I): ##STR00012## wherein n and m are integers from 0 to 4; R.sub.1 and R.sub.2 are independently selected from the group consisting of alkyl, alkoxy, aryl, aryloxy and aralkyl, wherein, if more than one of R.sub.1 and/or R.sub.2 are present, each of these substituents can be identical or different to each other; and R.sub.3 denotes a residue derived from the unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof.

4. The polymer according to claim 1, wherein the unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof is a divalent carboxylic acid or ester or anhydride thereof which preferable is selected from the group consisting of itaconic acid, maleic acid, fumaric acid, endomethylene tetrahydrophthalic acid, citraconic acid, mesaconic acid, and tetrahydrophthalic acid and esters and anhydrides thereof.

5. The polymer according to claim 1, wherein the secondary diamine b) is a compound represented by the following general formula (II): ##STR00013## wherein R.sub.4, R.sub.5 and R.sub.6 independently represent hydrocarbon residues which optionally contain one or more heteroatoms and which optionally form one or more rings with themselves or any of each other of R.sub.4, R.sub.5 and/or R.sub.6.

6. The polymer according to claim 5, wherein R.sub.4, R.sub.5 and R.sub.6 independently represent aryl, heteroaryl or linear, branched and/or cyclic C.sub.1-30 alkyl residues, or any combination thereof, wherein the C.sub.1-30 alkyl residues are optionally substituted or interrupted by one or more heteroatoms and/or one or more aryl groups.

7. The polymer according to claim 5, wherein R.sub.4 is arylene or linear, branched and/or cyclic C.sub.1-20 alkylene, or any combination thereof, wherein the C.sub.1-20 alkylene are optionally interrupted by one or more heteroatoms.

8. The polymer according to claim 5, wherein R.sub.5 and R.sub.6 independently represent aryl, C.sub.1-3 alkylaryl, or linear, branched and/or cyclic C.sub.1-6 alkyl, or wherein R.sub.5 and R.sub.6 together have 1 to 3 carbon atoms and form a ring together with NH R.sub.4NH, or wherein R.sub.4 and/or R.sub.5 represent a C.sub.1-3 alkylene residue forming a ring together with R.sub.4.

9. The polymer according to claim 5, wherein the secondary diamine b) is selected from the group consisting of 4,4-bipiperidine, piperazine, 4,4-ethylenedipiperidine, N,N-dimethyl-1,6-hexanediamine, N,N-dimethyl-1,8-octanediamine, N,N-diethyl-1,3-propanediamine, N,N-dimethyl-1,3-propanediamine, N,N-diisopropyl-1,3-propanediamine, N,N-diethylethylenediamine, N,N-dimethylethylenediamine, N,N-diisopropylethylenediamine, N,N-diphenylethylenediamine, N,N-dibenzylethylenediamine, trans-N,N-dimethylcyclohexane-1,2-diamine, N,N-bis[3-(methylamino)propyl]methylamine, and 4,4-trimethylenedipiperidine, or salt thereof or mixture thereof.

10. The polymer according to claim 5 comprising repeating units represented by the following general formula (III): ##STR00014## wherein R.sub.4, R.sub.5 and R.sub.6 are defined as in claim 5.

11. A method of preparing a polymer according to claim 1, wherein the method comprises the steps of: a) reacting 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and/or nuclear substituted derivatives thereof with at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof to obtain a first phosphorous-containing monomer; b) reacting the first phosphorous-containing monomer obtained in step a) with at least one secondary diamine, and optionally other monomers; and c) optionally carrying out the reaction step b) in the presence of at least one monovalent carboxylic acid and/or monovalent secondary amine and/or reacting the polymer obtained in step b) with at least one monovalent carboxylic acid and/or monovalent secondary amine to obtain an end-capped polymer.

12. A thermoplastic polymer composition comprising a thermoplastic polymer and a polymer according to claim 1, wherein the thermoplastic polymer is selected from the group consisting of polyamides, polyphthalamides, polyesters including unsaturated polyester resins, polysulfones, polyimides, polyolefins, polyacrylates, polyether etherketones, acrylnitril butadiene styrenes (ABS), polyurethanes, polystyrenes, polycarbonates, polyphenylene oxides, phenolic resins and mixtures thereof.

13. The thermoplastic polymer composition according to claim 12, wherein the thermoplastic polymer is at least one polyamide selected from the group consisting of PA6.6, PA6, PA6.10, PA6.12, PA MXD.6, PA11, PA12, PA6.6/6, P6.6/6.T, and mixtures thereof.

14. The thermoplastic polymer composition according to claim 12, which comprises at least 0.1% by weight, of the polymer according to claim 1, each based on the total weight of the thermoplastic polymer composition.

15. The polymer of claim 1, wherein the polymer is used as flame-retardant polymer.

16. The polymer according to claim 3, wherein R.sub.1 and R.sub.2 are independently selected from C.sub.1-8 alkyl and C.sub.1-8 alkoxy; and n and m are independently 0 or 1.

17. The polymer according to claim 4, wherein the unsaturated divalent carboxylic acid is selected from the group consisting of itaconic acid, maleic acid and anhydrides thereof.

18. The polymer according to claim 7, wherein the one or more heteroatoms is selected from the group consisting of N and O, and wherein, if the heteroatom is N, it forms a tertiary amine.

19. The polymer according to claim 7, wherein the one or more heteroatoms is selected from the group consisting of N and O, and wherein, if the heteroatom is N, it forms N(C.sub.1-6 ).

20. The polymer according to claim 2, wherein the phosphorous content ranges from about 4% to about 15% by weight, each of the total weight of the polymer.

Description

DETAILED DESCRIPTION

Definitions

[0018] In the present description, wherein an element or composition is said to be included in and/or selected from a list of recited elements or components, it should be understood that in related embodiments explicitly contemplated here, the element or component can also be any one of the individual recited elements or components, or can also be selected from a group consisting of any two or more of the explicitly listed elements or components.

[0019] Further, it should be understood that elements and/or features of an apparatus, a process or method described herein can be combined in a variety of ways without departing from the scope and disclosures of the present teachings, whether explicit or implicit herein.

[0020] The term thermoplastic polymer shall mean a polymer that becomes pliable or moldable above a specific temperature, so is capable of flow at high temperatures below the thermal decomposition temperature and returns to a solid state upon cooling. A polymer is a macromolecular compound prepared by reacting (i.e., polymerizing, condensation) monomers of the same or different type, including homo- and copolymers. Thermoplastic materials are made by chain polymerization, polyaddition and/or polycondensation.

[0021] The term comprising includes consisting essentially of and consisting of.

[0022] In the present specification, the description of a range of values for a variable, defined by a bottom limit, or a top limit, or by a bottom limit and a top limit, also comprises the embodiments in which the variable is chosen, respectively, within the value range: excluding the bottom limit, or excluding the top limit, or excluding the bottom limit and the top limit.

[0023] In the present specification, the description of several successive ranges of values for the same variable also comprises the description of embodiments where the variable is chosen in any other intermediate range included in the successive ranges. Thus, for example, when it is indicated that the magnitude X is generally at least 10, advantageously at least 15, the present description also describes the embodiment where: the magnitude X is at least 11, or also the embodiment where: the magnitude X is at least 13.74, etc.; 11 or 13.74 being values included between 10 and 15.

[0024] In the present specification, the choice of an element from a group of elements also explicitly describes: [0025] the choice of two or the choice of several elements from the group, [0026] the choice of an element from a subgroup of elements consisting of the group of elements from which one or more elements have been removed.

[0027] A plurality of elements includes two or more elements.

[0028] The phrase A and/or B refers to the following selections: element A; or element B; or combination of elements A and B (A+B). The phrase A and/or B is equivalent to at least one of A and B. The phrase A and/or B equates to at least one of A and B.

[0029] The phrase A1, A2, . . . and/or An with n 3 includes the following choices: any single element Ai (i=1, 2, . . . n); or any sub-combinations of from two to (n1) elements chosen from A1, A2, . . . , An; or combination of all elements Ai (i=1, 2, . . . n). For example, the phrase A1, A2, and/or A3 refers to the following choices: A1; A2; A3; A1+A2; A1+A3; A2+A3; or A1+A2+A3.

[0030] The use of the singular a or one herein includes the plural unless specifically stated otherwise. By way of example, a multivalent alcohol denotes one multivalent alcohol or more than one multivalent alcohol.

[0031] In addition, if the term about or ca. is used before a quantitative value, the present teachings also include the specific quantitative value itself, unless specifically stated otherwise. As used herein, the term about or ca. refers to a +10% variation from the nominal value unless specifically stated otherwise.

FLAME-RETARDANT POLYMER

[0032] One aspect of the present invention relates to a flame-retardant polymer, which is obtainable by polycondensation of

[0033] a) at least one phosphorous-containing monomer selected from adducts of [0034] a1) 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and/or nuclear substituted DOPO derivatives, with [0035] a2) at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof;

[0036] b) at least one secondary diamine; and

[0037] c) optionally other monomers.

[0038] In a preferred embodiment, the flame-retardant polymer is halogen-free.

[0039] It is preferred that the flame-retardant polymer of the invention has a high phosphorous content of at least 4.0% by weight. Throughout this description, the phosphorous content is given in % by weight based on the total weight of the polymer. In more preferred embodiments, the polymer has a phosphorous content of at least 5.0% by weight, more preferably at least 5.8% by weight, even more preferably at least 7.0% by weight, such as at least 7.5% by weight. The upper limit of the phosphorous content in the polymer of the invention is not particularly limited and depends on the monomers used. Generally, the phosphorous content should not be above 15% by weight, preferably at a maximum of 10% by weight, more preferably at a maximum of 9% by weight and even more preferably at a maximum of 8% by weight. The given lower and upper limits of the phosphorous content can be combined with each other. Suitable ranges are, for example, at least 4.0% to about 15% by weight and about 5.0% to about 9% by weight. Other combinations of lower and upper limits are possible as well. In preferred embodiments, the phosphorous content is about 5.0% to about 15% by weight, more preferably about 5.8% to about 10% by weight, even more preferably about 7.0% to about 9% by weight, and most preferably about 7.5% to about 8% by weight, each of the total weight of the polymer.

[0040] In the polycondensation reaction, which makes the polymer of the present invention obtainable, a first phosphorous-containing monomer a) is used. This monomer is an adduct of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and/or nuclear substituted DOPO derivatives with at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof. DOPO has the following chemical structure:

##STR00001##

[0041] Nuclear substituted DOPO derivatives denotes DOPO derivatives which bear one or more substituents on the aromatic rings of DOPO. Each ring may bear 0 to 4 substituents, which can for example be selected from alkyl, alkoxy, aryl, aryloxy and aralkyl. The alkyl moiety in alkyl, alkoxy and aralkyl may have, for example, 1 to 30 carbon atoms, which may be linear, branched or cyclic and which may be saturated or unsaturated, preferably saturated. The aryl in aryl, aryloxy and aralkyl may, for example, comprise 6 to 30 carbon atoms, such as phenyl and naphthyl. If the DOPO molecule bears more than one nuclear substituent, these substituents may be identical or different to each other.

[0042] To obtain the first phosphorous-containing monomer a), the DOPO and/or nuclear substituted DOPO derivatives are reacted with at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof to form an adduct. This adduct formation is shown in the following reaction scheme by way of example using DOPO and itaconic acid as unsaturated dicarboxylic acid. It is, however, to be understood that instead of DOPO, nuclear substituted DOPO derivatives and instead of itaconic acid, other di- or multivalent unsaturated carboxylic acids or esters or anhydrides thereof may be used.

##STR00002##

[0043] In one embodiment of the present invention, the unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof is a divalent carboxylic acid or ester or anhydride thereof. In a preferred embodiment, the divalent carboxylic acid or ester or anhydride thereof is selected from the group consisting of itaconic acid, maleic acid, fumaric acid, endomethylene tetrahydrophthalic acid, citraconic acid, mesaconic acid, and tetrahydrophthalic acid and esters and anhydrides thereof. Itaconic acid and maleic acid and anhydrides thereof being particularly preferred.

[0044] In one embodiment of the present invention, the phosphorous-containing monomer a) can be selected from a compound represented by the following general formula (I):

##STR00003##

wherein n and m are integers from 0 to 4;

[0045] R.sub.1 and R.sub.2 are independently selected from alkyl, alkoxy, aryl, aryloxy and aralkyl, wherein, if more than one of R.sub.1 and/or R.sub.2 are present, each of these substituents can be identical or different to each other; and

[0046] R.sub.3 denotes a residue derived from the unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof.

[0047] R.sub.1 and R.sub.2 are preferably defined as above with respect to the definition of the nuclear substituted DOPO derivatives. In a preferred embodiment, R.sub.1 and R.sub.2 are independently selected from C.sub.1-8 alkyl and C.sub.1-8 alkoxy; and n and m are independently 0 or 1.

[0048] In order to facilitate a high thermal stability of the final flame-retardant polymer, it is preferred that the first phosphorous-containing monomer a) does not contain any carbon carbon double or triple bonds except aromatic bonds.

[0049] Using the above described first phosphorous-containing monomer a), the flame-retardant polymer of the invention can be obtained by polycondensation with at least one secondary diamine. This polycondensation reaction results in a polyamide.

[0050] In one embodiment, the secondary diamine b) is a compound represented by the following general formula (II):

##STR00004##

[0051] 5

wherein R.sub.4, R.sub.5 and R.sub.6 independently represent hydrocarbon residues which may contain one or more heteroatoms and which may form one or more rings with themselves or any of each other of R.sub.4, R.sub.5 and/or R.sub.6.

[0052] The secondary diamine b) in a preferred embodiment does not contain any primary amine group. In a further embodiment, the secondary diamine b) may contain one or more tertiary amine groups.

[0053] In the above compound of general formula (II) R.sub.4, R.sub.5 and R.sub.6 may independently represent aryl, heteroaryl or linear, branched and/or cyclic C.sub.1-30 alkyl residues, or any combination thereof, wherein the C.sub.1-30 alkyl residues may be substituted or interrupted by one or more heteroatoms, such as O, N, S or P, and/or one or more aryl groups. Suitable aryl residues are for example phenyl and naphthyl. Suitable heteroaryl residues are for example pyrrolyl and isoquinolinyl. Suitable alkyl residues are in particular C.sub.1-20 alkyl residues and more preferably C.sub.1-18 alkyl residues. Combinations of these residues are for example benzyl, bisphenoxy, biphenyl and methylenebiphenyl.

[0054] In one embodiment, R.sub.4 may be arylene or linear, branched and/or cyclic C.sub.1-20 alkylene, or any combination thereof, wherein the C.sub.1-20 alkylene may be interrupted by one or more heteroatoms, preferably selected from N and O, wherein, if the heteroatom is N, it preferably forms a tertiary amine, more preferably N(C.sub.1-6 alkyl). Examples of R.sub.4 are linear C.sub.1-10 alkylene, cyclohexylene, in particular 1,2-cyclohexylene, and C.sub.1-3 alkylene-N(C.sub.1-6 alkyl)C.sub.1-3 alkylene.

[0055] In one embodiment, R.sub.5 and R.sub.6 independently represent aryl, C.sub.1-3 alkylaryl, or linear, branched and/or cyclic C.sub.1-6 alkyl, or R.sub.5 and R.sub.6 together have 1 to 3 carbon atoms and form a ring together with NHR.sub.4NH, or R.sub.4 and/or R.sub.5 represent a C.sub.1-3 alkylene residue forming a ring together with R.sub.4. Examples for aryl are phenyl and naphthyl. An example for C.sub.1-3 alkylaryl is benzyl. Examples for linear, branched and/or cyclic C.sub.1-.sub.6 alkyl are in particular methyl, ethyl, propyl, isopropyl, butyl, tert-butyl, and cyclohexyl. An example where R.sub.5 and R.sub.6 together have 1 to 3 carbon atoms and form a ring together with NHR.sub.4NHis piperazine. Examples where R.sub.4 and/or R.sub.5 represent a C.sub.1-3 alkylene residue forming a ring together with R.sub.4 are 4,4-trimethylenedipiperidine, 4,4-dimethylenedipiperidine and 4,4-dipiperidine.

[0056] In one embodiment, the secondary diamine b) is selected from the group consisting of 4,4-bipiperidine, piperazine, 4,4-ethylenedipiperidine, N,N-dimethyl-1,6-hexanediamine, N,N-dimethyl-1,8-octanediamine, N,N-diethyl-1,3-propanediamine, N,N-dimethyl-1,3-propanediamine, N,N-diisopropyl-1,3-propanediamine, N,N-diethylethylenediamine, N,N-dimethylethylenediamine, N,N-diisopropylethylenediamine, N,N-diphenylethylenediamine, N,N-dibenzylethylenediamine, trans-N,N-dimethylcyclohexane-1,2-diamine, N,N-bis[3-(methylamino)propyl]methylamine, and 4,4-trimethylenedipiperidine, or salt thereof or mixture thereof. 4,4-etyhelendipiperidine, 4,4-trimethylenedipiperidine and piperazine are particularly preferred. Piperazine is even more preferred.

[0057] In one embodiment of the present invention, the flame-retardant polymer is obtainable by reacting DOPO with itaconic acid to form the first phosphorous-containing monomer a), which is then reacted with a secondary diamine of above general formula (II) to form a polyamide having repeating units represented by the following general formula (III):

##STR00005##

wherein R.sub.4, R.sub.5 and R.sub.6 are defined as above.

[0058] In a preferred embodiment of the invention, the flame-retardant polymer having repeating units represented by the above general formula (III) is obtained using a secondary diamine or formula (II) being selected from the group consisting of 4,4-ethylenedipiperidine, 4,4-trimethylenedipiperidine and piperazine. Piperazine being even more preferred.

[0059] The above described flame-retardant polymer may optionally comprise other monomer residues in addition to the first phosphorous-containing monomer a) and the secondary diamine monomer b). These other monomers are not particularly limited as long as they can react with the first monomer a) and the second monomer b) to form a polymer. Preferably, the other monomer does not contain any carbon carbon double or triple bond except aromatic bonds in order to obtain a final flame-retardant polymer of high thermal stability.

[0060] The other monomers c) can be selected or example from di- and multivalent carboxylic acids and di- or multivalent amines, which may or may not comprise phosphorous atoms or other heteroatoms, such as oxygen, nitrogen and sulfur. Other monomers, which can for example form block copolymers with the polyamide units of monomers a) and b), may be used.

[0061] As a reasonably high phosphorous content of the flame-retardant polymer of the invention is desired, the amount of other monomers in the polymer should be low, in particular if the other monomers do not contain any phosphorous atoms. It can therefore be of advantage if, for example, less than 20%, preferably less than 10% and even more preferably less than 5% of the monomer residues of the polymer are residues of other monomers c). In a preferred embodiment, the flame-retardant polymer of the invention does not contain any other monomers c).

[0062] If present, other monomers c) can, for example, be selected from carboxyphosphinic acid derivatives, such as carboxyethyl-phenylphosphinic acid (CEPPA) and carboxyethyl-methylphosphinic acid (CEMPA), aminophosphinic acid derivatives making an amide bond by polycondensation, such as aminomethyl phosphinic acid (AMPA), biscarboxyphosphine oxide derivatives, such as bis(beta-carboxyethyl)methylphopsphine oxide (CEMPO), bisaminophosphine oxide derivatives making an amide bond by polycondensation, such as bis(3-aminopropyl)methylphosphine oxide (AMPO), multivalent carboxylic acids, such as terephthalic acid, isophthalic acid, phthalic acid, sebacic acid, adipic acid, glutaric acid and succinic acid.

[0063] To improve the compatibility with the thermoplastic polymers, the flame-retardant polymer according to the invention can be end-capped by reaction with a monovalent secondary amine and/or a monovalent carboxylic acid.

[0064] The chemical and physical properties of the polymer according to the invention can be influenced by selecting di- or multivalent monomers. If only divalent monomers are employed, no cross-linking between the polymer backbones occurs. If multivalent monomers are used, cross-linking could occur. By selecting a suitable ratio between di- and multivalent monomers, the degree of cross-linking and thus the properties of the polymer can be tailored.

[0065] The average molecular weight Mn of the polymer according to the invention can be above 1,000 g/mol, such as above 3,000 g/mol or even above 5,000 g/mol. The average degree of polymerization of the polyamide amounts to, for example, at least 5, preferably at least 15, even preferably at least 25.

[0066] In one embodiment, the flame-retardant polymer according to the invention preferably has a viscosity close to the temperature of processing of the final thermoplastic polymer composition (such as for example 280 C.). At this viscosity, an optimum processibility of the polyamide of the invention in the melt-spinning process and other extrusion processes is obtained. The desired viscosity can be adjusted by an accurate monitoring of the average molecular weight Mn, the average degree of polymerization DPn and/or the degree of branching of the polyamide of the invention.

[0067] The chemical and physical properties of the flame-retardant polymer according to the invention can further be influenced by the temperature and time of polycondensation, the catalyst used and the addition of, for example, chain prolongation and chain branching monomers. Heat stabilizers may also be added. To improve the color of the flame-retardant polymer according to the invention, it is further possible to use known optical brightening agents.

[0068] A further embodiment of the present invention relates to a method of preparing the above described flame-retardant polymer. This method comprises the steps of

[0069] a) reacting 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and/or nuclear substituted derivatives thereof with at least one unsaturated di- or multivalent carboxylic acid or ester or anhydride thereof to obtain a first phosphorous-containing monomer;

[0070] b) reacting the first phosphorous-containing monomer obtained in step a) with at least one secondary diamine of formula (II); and

[0071] c) optionally carrying out the reaction in step b) in the presence of at least one monovalent carboxylic acid and/or monovalent secondary amine and /or reacting the polymer obtained in step b) with at least one monovalent carboxylic acid and/or monovalent secondary amine to obtain an end-capped polymer.

[0072] Suitable reaction conditions and in particular polycondensation conditions are known to the person skilled in the art. Useful specific parameters are exemplified in the examples below.

[0073] The flame-retardant polymer according to the invention is particularly suitable to impart flame-retardant properties to a thermoplastic polymer composition. Therefore, in a further embodiment, the present invention relates to a thermoplastic polymer composition comprising a thermoplastic polymer and a flame-retardant polymer as described above.

[0074] The thermoplastic polymer in the thermoplastic polymer composition can be selected from a broad variety of polymers, in particular synthetic polymers, including homopolymers, copolymers and block copolymers. Also mixtures of one or more thermoplastic polymers may be used. A list of suitable synthetic polymers is, for example, disclosed in WO 2008/119693 A1, the content of which is incorporated herein by reference. Specific examples of suitable thermoplastic polymers are, for example, polyamides, polyphthalamides, polyesters including unsaturated polyester resins, polysulfones, polyimides, polyolefins, polyacrylates, polyether etherketones, acrylnitril butadiene styrenes (ABS), polyurethanes, polystyrenes, polycarbonates, polyphenylene oxides, phenolic resins and mixtures thereof.

[0075] In a preferred embodiment, the thermoplastic polymer is a polyamide, such as a polyamide that is suitable for melt spinning or other molding processes. The polyamide can, for example, be selected from the group consisting of PA 6.6, PA 6, PA 6.10, PA 6.12, PA MXD.6, PA 11 and PA 12. Copolyamides, such as PA 6.6/6 and PA 6.6/6.T and blends of polyamides, such as PA 6.6/PA 6 and PA 6.6/PA 6.10 are suitable as well.

[0076] The amount of flame-retardant polymer in the thermoplastic polymer composition according to the invention is not particularly limited and can be selected by a person skilled in the art according to the requirements. In one embodiment, the thermoplastic polymer composition comprises at least 0.1% by weight, preferably at least 2% by weight of the flame-retardant polymer based on the total weight of the thermoplastic polymer composition. For example, the thermoplastic polymer composition can comprise from about 0.1% to about 30% by weight, preferably from about 2% to about 25% by weight, even more preferably from about 6% to about 20% by weight of the flame-retardant polymer, based on the total weight of the thermoplastic polymer composition.

[0077] In another embodiment, the thermoplastic polymer composition can comprise the flame-retardant polymer in an amount such that the final thermoplastic polymer composition has a phosphorous content of from about 0.1% to about 4% by weight, preferably of from about 0.1% to about 2% by weight, in particular of from about 0.5% to about 1% by weight, based on the total weight of the thermoplastic polymer composition.

[0078] It is also possible to first prepare a master batch of a thermoplastic polymer composition containing a higher phosphorous content of up to, for example, about 5% by weight of the total weight of the composition and then add this master batch to another thermoplastic polymer composition for tailoring its properties.

[0079] For example, to produce flame-retardant polymer fibers, the flame-retardant polymer according to the invention can physically be mixed with an appropriate polyamide in the melt, and the mixture is then either directly spun as a polymer mixture having a phosphorous content of between about 0.1% and about 1% by weight, so as to form filaments, or, the mixture is then tailored in terms of a master batch having a phosphorous content of between about 2% and about 5% by weight, and is then added to the same or a different type of polyamide and spun to filaments in a second process step.

[0080] Polymer fibers produced in a melt-spinning process from a thermoplastic polymer composition of the present invention preferably have a total phosphorous content of from about 0.1% to about 2% by weight, in particular of from about 0.5 to about 1% by weight, based on the total weight of the thermoplastic polymer composition, and they are therefore sufficiently flame-proof.

[0081] All aforementioned polyamides can be finished in an excellent manner to be flame-retarding with the aforementioned flame-retardant polymer by a simple physical mixing of the polymer melts under conditions as are usual in the melt-spinning process. When using the flame-retardant polymer according to the invention, important polymer properties, such as the melt viscosity, the melting point of the polymer composition obtained after mixing are changed only to an extent that a reliable processing, such as a melt spinning remains entirely ensured.

[0082] The thermoplastic polymer composition of the present invention may additionally comprise other flame retardants or additives known to a person skilled in the art, in particular those flame retardants and additives which are used in the preparation of fibers. Suitable other flame-retardants are, for example, melamine cyanurate, melamine polyphosphate, ammonium polyphosphate and metal stannates, preferably zinc stannate, metal borates such as zinc borate, polyhedral oligomeric silsesquioxanes (for example trade name POSS of Hybrid Plastics), and so-called nanoclays based on the exfoliated phyllosilicates montmorillonite and bentonite, such as, e.g., the products Nanomer of Nanocor, or Nanofil of Sdchemie, and inorganic metal hydroxides such as the products Magnifin or Martinal of Martinswerk. Due to the use of these additives, parameters that are important to the flame-retarding properties can be modified, for example the characteristic cone calorimetric numbers TTI (time to ignition) can be increased, PHRR (peak of heat release rate) can be reduced and/or a desired suppression of the smoke gas generation can be improved.

[0083] Both, the flame-retardant polymer as well as the thermoplastic polymer composition according to the invention may comprise additional components, such as anti-dripping agents, polymer stabilizers, anti-oxidants, light stabilizers, peroxide scavengers, nucleating agents, fillers and reinforcing agents, and other additives, such as blend compatibilizing agents, plasticizers, lubricants, emulsifiers, pigments, rheology additives, catalysts, flow-control agents, optical brighteners, flame-proving agents, antistatic agents and blowing agents. Specific examples of these additives are disclosed in WO 2008/119693 A1, the content of which is incorporated herein by reference.

[0084] The invention will now be further described by the following examples, which are, however, not to be understood in a limiting sense.

EXAMPLES

[0085] The following starting materials were used for production:

[0086] PA66 (Stabamid 26AE1)

[0087] Flame retardant: Ukanol FR 80 PU 30 (Schill+Seilacher), containing 8.0% w of phosphorus according to technical data sheet. Ukanol FR 80 is used in US 2013/0136911 A1 as flame retardant. It has the following chemical structure:

##STR00006##

[0088] Lunastab DDP, (6-oxide-6H-dibenzo (c,e) (1,2) oxa-phosphorin-6-yl) butanedioic acid, CAS [63562-33-4].

[0089] Piperazine, 99%, from Sigma-Aldrich.

[0090] 4,4-Trimethylenedipiperidine, 97%, from Sigma-Aldrich.

[0091] The following measuring methods were used:

[0092] Melting, crystallization and glass transition temperatures determined by DSC, at 10 C./min.

[0093] Onset of thermal degradation temperature determined by TGA, at 10 C./min under nitrogen flow.

[0094] Phosphorus content by ICP/OES after sulfonitric mineralization.

[0095] Viscosity number in formic acid 90%, according to ISO 307.

[0096] Carboxylic acid End-Groups (CEG) concentration and Amine End-Groups

[0097] (AEG) concentration were determined by potentiometric titration (unit: meq/kg).

[0098] Melt viscosity is measured by a rheometer with a cone-plate geometry, at 280 C. (with the exception of example 5, measured at 275 C.).

[0099] UL 94-V with 125133 mm samples.

Phosphorous Containing Polyamide

Example 1

Production of a Phosphorous Containing Polyamide According to the Invention 113.6 g (0.33 mol) of Lunastab DDP represented by the following formula:

[0100] ##STR00007##

and 29.4 g (0.34 mol) of Piperazine represented by the following formula:

##STR00008##

[0101] were poured with 60.0 g of demineralized water, 0.015 g of phosphoric acid 85% and antifoam in a stainless steel clave equipped with a mechanical stirrer with an internal thermometer. The clave atmosphere was purged with nitrogen, and the temperature was increased progressively to 220 C., with continuous stirring, letting pressure increase up to about 17.5 bar. The temperature was increased progressively up to 250 C., while maintaining the same level of pressure. The pressure was then progressively released while the temperature was increased to about 272 C. Vacuum was then applied to reach 300 mbar and kept for 30 min at the same temperature under continuous stirring. The vacuum was broken with nitrogen and the polymer was extruded in a strand. A glassy polymer was obtained which contained polyamide chains represented by the following formula:

##STR00009##

wherein n denotes the mole fraction of the polyamide repeating unit. The polymer thus obtained had the following analytical data:

[0102] The amorphous polyamide had a glass transition temperature of 189 C., and a thermal degradation onset of 381 C., and a char at 500 C. of 35%.

[0103] The phosphorous content was 7.8% w.

[0104] End-groups titrations were as follow: CEG=197 meq/kg, AEG=112 meq/kg, corresponding to an estimated Mn of 6500 g/mol, i.e. a DPn of 33.

Example 2

Production of a Phosphorous Containing Polyamide According to the Invention

[0105] Similarly to example 1, 93.31 g (0.27 mol) of Lunastab DDP and 56.7 g (0.27 mol) of 4,4-Trimethylenedipiperidine represented by the following formula:

##STR00010##

were polycondensed and the resulting polymer was extruded in a strand. A glassy polymer was obtained which contained polyamide chains represented by the following formula:

##STR00011##

wherein n denotes the mole fraction of the polyamide repeating unit. The polymer thus obtained had the following analytical data:

[0106] The amorphous polyamide had a glass transition temperature of 145 C., and a thermal degradation onset of 398 C., and a char at 500 C. of 19%. The phosphorous content was 5.7% w.

[0107] End-groups titrations were as follow: CEG=148 meq/kg, AEG=19 meq/kg, corresponding to an estimated Mn of 12 000 g/mol, i.e. a DPn of 46.

[0108] The melt viscosity at 280 C. under 100s-1 was 55 Pa.Math.s.

Example 3

Production of a Phosphorous Containing Polyamide According to the Invention

[0109] Similarly to example 1, 113.6 g (0.33 mol) of Lunastab DDP and 28.2 g (0.33 mol) of Piperazine were polycondensed and the resulting polymer was extruded in a strand. A glassy polymer was obtained. The amorphous polyamide had a glass transition temperature of 190 C., and a thermal degradation onset of 381 C., and a char at 500 C. of 38%.

[0110] The phosphorous content was 7.2% w.

[0111] End-groups titrations were as follow: CEG=303 meq/kg, AEG=76 meq/kg, corresponding to an estimated Mn of 5300 g/mol, i.e. a DPn of 27.

[0112] The melt viscosity at 280 C. under 100s-1 was 104 Pa.Math.s.

Example 4

Production of a Phosphorous Containing Polyamide According to the Invention

[0113] Similarly to example 1, 113.6 g (0.33 mol) of Lunastab DDP and 29.4 g (0.34 mol) of Piperazine were polycondensed with 0.049 g of phosphoric acid 85%, up to 282 C. and the resulting polymer was extruded in a strand. A glassy polymer was obtained. The amorphous polyamide had a glass transition temperature of 190 C., and a thermal degradation onset of 387 C., and a char at 500 C. of 36%.

[0114] End-groups titrations were as follow: CEG=181 meq/kg, AEG=97 meq/kg, corresponding to an estimated Mn of 7200 g/mol, i.e. a DPn of 36.

[0115] The melt viscosity at 280 C. under 100s-1 was 72 Pa.Math.s.

Example 5

Production of a Phosphorous Containing Polyamide According to the Invention

[0116] Similarly to example 1, 113.6 g (0.33 mol) of Lunastab DDP and 29.4 g (0.34 mol) of Piperazine were polycondensed without phosphoric acid, under pressure. The pressure was then progressively released while the temperature was increased to about 276 C. The finishing step was lead for 30 min, under continuous stirring and vacuum to reach about 30 mbar. The vacuum was then broken with nitrogen and the polymer was extruded in a strand. A glassy polymer was obtained. The amorphous polyamide had a glass transition temperature of 190 C.

[0117] End-groups titrations were as follow: CEG=152 meq/kg, AEG=90 meq/kg, corresponding to an estimated Mn of 8200 g/mol, i.e. a DPn of 41.

[0118] The melt viscosity at 275 C. under 100s-1 was 300 Pa.Math.s.

Comparative Example 1

Production of a PA6.6

[0119] 150.0 g (0.57 mol) of hexamethylenediammonium adipate salt were poured with 138.0 g of demineralized water and antifoam in a stainless steel clave equipped with a mechanical stirrer with an internal thermometer. The clave atmosphere was purged with nitrogen, and the temperature was increased progressively to 220 C., with continuous stirring, letting pressure increase up to about 17.5 bar. The temperature was increased progressively up to 250 C., while maintaining the same level of pressure. The pressure was then progressively released while the temperature was increased to about 272 C. and kept for 30 min at the same temperature under continuous stiffing. The polymer was extruded in a strand, cooled in a water bath, and then pelletized. A semicristalline polymer was obtained with the following analytical data:

[0120] The polyamide had a melting point of 261 C., a crystallization temperature of 225 C., and a thermal degradation onset of 423 C., and a char at 500 C. of 7%. The viscosity number was 131 mL/g.

[0121] The melt viscosity at 280 C. under 100s-1 was 180 Pa.Math.s.

Comparative Example 2

Production of a Phosphorous Containing PA6.6 Copolymer.

[0122] Similarly to Comparative Example 1, 132.0 g (0.50 mol) of hexamethylenediammonium adipate salt, 14.6 g (0.04 mol) of Lunastab DDP and 15.3 g (0.04 mol) of hexamethylenediamine 32.2% aqueous solution were poured with 129.0 g of demineralized water and antifoam in a stainless steel clave and polycondensated up to 272 C. and kept for 30 min at the same temperature under continuous stiffing. The polymer was too fluid to be extruded in a strand and could not be pelletized. A semicristalline polymer was obtained with the following analytical data:

[0123] The polyamide had a melting point of 257 C., a crystallization temperature of 221 C., and a thermal degradation onset of 374 C., and a char at 500 C. of 10%.

[0124] The viscosity number was 37 mL/g.

[0125] The melt viscosity at 280 C. under 100s-1 was 1 Pa.Math.s.

[0126] The phosphorous content was 0.9% w.

Production of PA6.6 Based Compounds

Example 6

Production of Flame-Retardant PA6.6 Compound

[0127] The PA6.6 pellets (Stabamid 26AE1) were cryogenic grinded below 1.5 mm and the powder was then dried at 90 C. in a vacuum oven for one night. The polyamide from example 1 was roughly dry grinded.

[0128] Dry blend was then prepared with the powders of PA6.6 and polyamide according to Example 1 with the corresponding ratio 87.2%/12.8% by weight, for 1% by weight end concentration of phosphorous.

[0129] The production of the compound was effected by melt blending with a twin-screw extruder of diameter D=11 mm (L/D =40) equipped by a water cooling bath and a pelletizer. The melt temperature was 260-290 C.

[0130] The compound thus obtained had the following analytical data:

[0131] The melting and crystallization temperatures were respectively 261 C. and 227 C.

[0132] The viscosity number was 107 mL/g.

[0133] The char content at 500 C. was 9% w.

[0134] The phosphorus content was 1% w.

[0135] The melt viscosity at 280 C. under 100s-1 was 82 Pa.Math.s.

Example 7

Production of Flame-Retardant PA6.6 Compound

[0136] Similarly to example 6, dry blend was prepared with the powders of PA6.6 (Stabamid 26AE1) and polyamide according to Example 2 with the corresponding ratio 83.1%/16.9% by weight, for 1% by weight end concentration of phosphorous.

[0137] The compound thus obtained had the following analytical data:

[0138] The melting and crystallization temperatures were respectively 260 C. and 227 C.

[0139] The viscosity number was 88 mL/g.

[0140] The char content at 500 C. was 12% w.

[0141] The phosphorus content was 1% w.

[0142] The melt viscosity at 280 C. under 100s-1 is 31 Pa.Math.s.

Comparative Example 3

Production of a PA6.6 Compound

[0143] Done similarly to Example 6 with 100% by weight of PA6.6 (Stabamid 26AE1).

[0144] The compound thus obtained had the following analytical data:

[0145] The melting and crystallization temperatures were respectively 263 C. and 234 C.

[0146] The viscosity number was 131 mL/g.

[0147] The melt viscosity at 280 C. under 100s-1 is 180 Pa.Math.s.

Comparative Example 4

Production of a Phosphorous Containing PA6.6 Compound

[0148] Done similarly to Example 6 with the component ratio PA6.6 (Stabamid 26AE1)/Ukanol FR 80 as follow 87.5%/12.5% by weight, for 1% by weight end concentration of phosphorous. The Ukanol FR 80, already in powder, was used as such.

[0149] The compound thus obtained had the following analytical data:

[0150] The melting and crystallization temperatures were respectively 259 C. and 233 C.

[0151] The phosphorus content was 1% w.

[0152] The viscosity number was 112 mL/g.

[0153] The melt viscosity at 280 C. under 100s-1 is 60 Pa.Math.s.

Flame-Retardancy Test

[0154] Prior to flame-retardancy test, the compounds were shaped by melt compression. The comparative examples were selected such that a pure PA6.6 system (Comp. ex. 3) and a phosphorous containing PA6.6 system (Comp. ex. 4) were tested. At the same time, examples 6 and 7 according to the invention were tested, which comprised both PA6.6 and the flame retardant polyamide of the invention (respectively Ex. 1 and Ex. 2).

[0155] The experimental data which verify the positive properties of the described compounds are compiled in Table 1.

TABLE-US-00001 TABLE 1 Composition Comp. Ex. 3 Comp. Ex. 4 Ex. 6 Ex. 7 PA6.6 (% by weight) 100.0% 87.5% 87.2% 83.1% FR80 (% by weight) 12.5% Example 1 (% by weight) 12.8% Example 2 (% by weight) 16.9% Properties VN (mL/g) 131 112 107 88 Tm ( C.) 263 259 261 260 Tc ( C.) 234 233 227 227 Melt viscosity at 280 C./100s1 (Pa .Math. s) 180 60 82 31 P-content (% by weight) 0 1 1 1 UL 94-V rating V2 V2 V0 V0 t1 (s) .sup.a) 2 2 0 2 t2 (s) .sup.b) 1 2 2 1 tf (s) .sup.c) 16 19 8 15 Cotton ignition Yes Yes No No Burn up to the No No No No holding clamp .sup.a) flaming combustion time after first application of the test flame. .sup.b) flaming combustion time after the second removal of the test flame. .sup.c) total flaming combustion time for the 10 flame applications for each set of 5 specimens.

[0156] It can be concluded from comparative example 1 and 2 that phosphorous containing PA6.6 of Comp. Ex. 2 leads to a dramatic loss of melt viscosity preventing any processability or applicability for such a polyamide.

[0157] Correspondingly to Table 1, only examples 6 and 7, containing the halogen-free flame-retardant polyamides according to the invention, have flame-retardant properties which fulfill V0 requirement, the best flame test rating according to UL 94-V, for 3 mm thick samples. In particular the specimens do not drip flaming particles that ignite the dry absorbent surgical cotton located 300 mm below the test specimen.

[0158] It can be deduced from comparative example 4 in the table that using Ukanol FR 80 which is known as halogen-free polyester flame retardant in the prior art leads to insufficient flame-retardant properties, since the specimens drip flaming particles that ignite the dry absorbent surgical cotton located 300 mm below the test specimen. Comparative example 3 with virgin PA6.6 behaves similarly. Moreover they both show increased total flaming combustion time compared to the examples according to the invention.

[0159] It can be concluded from these comparative tests that only with the halogen-free flame-retardant polyamide of the invention is the flame test according to UL 94-V V0 rated, while thermal characteristics of PA6.6 are maintained.

Washing Resistance Test

[0160] For the resistance to washing, 2 g of pellets obtained in Example 6 or in Comparative example 4 were mixed in 75 g of demineralized water, for 3 h at 95 C., under reflux. Then the pellets were filtered and dried for 2 nights at 90 C., under vacuum. Finally, the remaining phosphorous content was measured. In both cases the phosphorous relative variation was about +/1% w, which is below the incertitude of the measure itself. Thus no phosphorous content extraction was noticed during the washing resistance test in both cases.