Pressure-reducing and injection-enhancing anti scaling agent for low-permeability water-injection well and preparation method thereof

Abstract

The present disclosure provides a pressure-reducing and injection-enhancing anti-scaling agent for low-permeability water-injection wells and a preparation method thereof. The anti-scaling agent is prepared from starting materials comprising: 10 to 12 parts of non-ionic surfactant(s), 18 to 20 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 5 to 8 parts of anionic surfactant(s), 6 to 8 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 2 to 5 parts of a dispersant, 15 to 18 parts of a diluent, 8 to 10 parts of an organic amine salt, and 30 to 36 parts of water. The pressure-reducing and injection-enhancing agent according to the present disclosure is characterized by having multiple functions in one agent. When used in an amount being 0.5% of the water injected to a water injection well, it shows excellent anti-swelling property, shrinking property, anti-corrosive property, and calcium sulfate and barium (strontium) sulfate scale resistance.

Claims

1. A pressure-reducing and injection-enhancing anti-scaling agent for low-permeability water-injection wells, prepared from starting materials comprising the following components: 10 to 12 parts of non-ionic surfactant(s), 18 to 20 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 5 to 8 parts of anionic surfactant(s), 6 to 8 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 2 to 5 parts of a dispersant, 15 to 18 parts of a diluent, 8 to 10 parts of an organic amine salt, and 30 to 36 parts of water.

2. The anti-scaling agent according to claim 1, prepared from starting materials comprising the following components: 11 parts of non-ionic surfactant(s), 18 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 6 parts of anionic surfactant(s), 6 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 3 parts of a dispersant, 16 parts of a diluent, 8 parts of an organic amine salt, and 35 parts of water.

3. The anti-scaling agent according to claim 1, wherein the non-ionic surfactant is a polyoxyethylene non-ionic surfactant.

4. The anti-scaling agent according to claim 3, wherein the non-ionic surfactant is a fatty alcohol polyoxyethylene ether, a polyoxyethylene octylphenol ether, or a polyoxyethylene nonyl phenyl ether.

5. The anti-scaling agent according to claim 1, wherein the anionic surfactant is a water-soluble phosphate-based anionic fluorocarbon surfactant.

6. The anti-scaling agent according to claim 5, wherein the anionic surfactant is a water-soluble phosphate-based anionic fluorocarbon surfactant having a structural formula of (RfCH.sub.2CH.sub.2O)nPO(ONH.sub.4)m, wherein Rf=F(CF.sub.2CF.sub.2)x, n+m=3, and x=1 to 7, and having a molecular weight of 500 to 600.

7. The anti-scaling agent according to claim 1, wherein the organic phosphonic acid-carboxylic acid scale inhibitor is 2-phosphonobutane-1,2,4-tricarboxylic acid or sodium ethylenebis(nitrilobismethylene)tetraphosphonate.

8. The anti-scaling agent according to claim 1, wherein the dispersant is monobutyl ethylene glycol ether or dibutyl ethylene glycol ether.

9. The anti-scaling agent according to claim 1, wherein the diluent is methanol, ethanol, or ethylene glycol.

10. The anti-scaling agent according to claim 1, wherein the organic amine salt comprises monoethanolamine, triethanolamine, or diethylene diamine.

11. A method for preparing the pressure-reducing and injection-enhancing anti-scaling agent for low-permeability water-injection wells of claim 1, said method comprising the steps of: weighing the components; adding the organic phosphonic acid-carboxylic acid scale inhibitor, the anionic surfactant and the non-ionic surfactant to water; then adding the organic amine salt and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate under stirring, to allow a reaction to proceed, after the reaction is complete, adding the diluent and the dispersant; and collecting the product to obtain the anti-scaling agent.

12. The method according to claim 11, further comprising: after the reaction is complete, lowering the temperature to room temperature, before addition of the diluent and the dispersant.

13. The method according to claim 11, wherein the method comprises adding the organic amine salt and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate under stirring at 40 to 60 rpm.

14. The method according to claim 11, wherein the reaction is carried out at 80 to 90 C.

15. The method according to claim 11, wherein the reaction is carried out for 2 to 5 hours.

Description

DETAILED DESCRIPTION

(1) The embodiments and beneficial effects of the present disclosure will be described in detail in conjunction with Examples, in order to help readers better understand the nature and features of the present disclosure, but the Examples do not limit the implementable scope of the present disclosure.

Example 1

(2) The example provides a pressure-reducing and injection-enhancing anti-scaling agent for low-permeability water-injection wells, which consists of the following starting materials in parts by weight: 11 parts of non-ionic surfactant(s), 19 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 6 parts of anionic surfactant(s), 7 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 4 parts of a dispersant, 16 parts of a diluent, 9 parts of an organic amine salt, and 32 parts of water.

(3) Preparation method: to a dry enamel reaction kettle, water 320 kg, organic phosphonic acid-carboxylic acid scale inhibitor 70 kg, anionic fluorocarbon surfactant 60 kg, and non-ionic surfactant 110 kg were added in this order; a stirrer was initiated, and organic amine salt 90 kg and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate 190 kg were added under stirring; the mixture was heated to 80 C. to react for 2 hours, and then cooled to room temperature; diluent 160 kg and dispersant 40 kg were added; and the product was collected to give the high-performance pressure-reducing and injection-enhancing agent for low-permeability water-injection wells as a commercial product.

(4) In this Example, the non-ionic surfactant is a fatty alcohol polyoxyethylene ether AEO-9; hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate; the anionic surfactant is (RfCH.sub.2CH.sub.2O)nPO(ONH.sub.4)m, wherein Rf=F(CF.sub.2CF.sub.2)x, n+m=3, and x=1 to 7, having a molecular weight of 500 to 600; the organic phosphonic acid-carboxylic acid scale inhibitor is 2-phosphonobutane-1,2,4-tricarboxylic acid, the dispersant is monobutyl glycol ether; the diluent is methanol; and the organic amine salt is monoethanolamine.

(5) The present disclosure combines an organic phosphonic acid-carboxylic acid scale inhibitor with hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate to obtain an agent which has excellent anti-scaling and dispersing performance against calcium carbonate, calcium sulfate, barium sulfate, calcium fluoride and silicon-based scales in water, and very easily adsorbs microcrystalline sulfate scale on a surface physically and chemically to greatly improve the solubility of the sulfate scale. In practical production, since the surface of scales often has a layer of oily soil adhered thereon, washing with non-ionic and anionic surfactants and an organic amine salt ensures sufficient contact between the agent and the scales. The present disclosure uses methanol and monobutyl glycol ether as dispersant and diluent, to ensure that active components act on rock surfaces more rapidly.

Example 2

(6) The example provides a pressure-reducing and injection-enhancing anti-scaling agent for low permeability water injection wells, which consists of the following starting materials in parts by weight: 10 parts of non-ionic surfactant(s), 18 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 5 parts of anionic surfactant(s), 6 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 2 parts of a dispersant, 15 parts of a diluent, 8 parts of an organic amine salt, and 30 parts of water.

(7) Preparation method: to a dry enamel reaction kettle, water 300 kg, organic phosphonic acid-carboxylic acid scale inhibitor 60 kg, anionic fluorocarbon surfactant 50 kg, and non-ionic surfactant 100 kg were added in this order; a stirrer was started, and organic amine salt 80 kg and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate 180 kg were added under stirring; the mixture was heated to 80 C. to react for 3 hours, and then cooled to room temperature; diluent 150 kg and dispersant 20 kg were added; and the product was collected to give the high-performance pressure-reducing and injection-enhancing agent for low permeability water injection wells as a commercial product.

(8) In this Example, the non-ionic surfactant is a polyoxyethylene octylphenol ether OP-10; hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate; the anionic surfactant is (RfCH.sub.2CH.sub.2O)nPO(ONH.sub.4)m, wherein Rf=F(CF.sub.2CF.sub.2)x, n+m=3, and x=1 to 7, having a molecular weight of 500 to 600; the organic phosphonic acid-carboxylic acid scale inhibitor is sodium ethylenebis(nitrilobismethylene)tetraphosphonate, the dispersant is dibutyl glycol ether; the diluent is ethanol; and the organic amine salt is triethanolamine.

Example 3

(9) The example provides a pressure-reducing and injection-enhancing anti-scaling agent for low permeability water injection wells, which consists of the following starting materials in parts by weight: 12 parts of non-ionic surfactant(s), 20 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 8 parts of anionic surfactant(s), 8 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 5 parts of a dispersant, 15-18 parts of a diluent, 10 parts of an organic amine salt, and 36 parts of water.

(10) Preparation method: to a dry enamel reaction kettle, water 360 kg, organic phosphonic acid-carboxylic acid scale inhibitor 80 kg, anionic fluorocarbon surfactant 80 kg, and non-ionic surfactant 120 kg were added in this order; a stirrer was started, and organic amine salt 100 kg and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate 200 kg were added under stirring; the mixture was heated to 80 C. to react for 4 hours, and then cooled to room temperature; diluent 180 kg and dispersant 50 kg were added; and the product was collected to give the high-performance pressure-reducing and injection-enhancing agent for low permeability water injection wells as a commercial product.

(11) In this Example, the non-ionic surfactant is a polyoxyethylene nonyl phenyl ether TX-10; hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate; the anionic surfactant is (RfCH.sub.2CH.sub.2O)nPO(ONH.sub.4)m, wherein Rf=F(CF.sub.2CF.sub.2)x, n+m=3, and x=1 to 7, having a molecular weight of 500 to 600; the organic phosphonic acid-carboxylic acid scale inhibitor is sodium ethylenebis(nitrilobismethylene)tetraphosphonate, the dispersant is dibutyl glycol ether; the diluent is ethylene glycol; and the organic amine salt is diethylene diamine.

Example 4

(12) The example provides a pressure-reducing and injection-enhancing anti-scaling agent for low permeability water injection wells, which consists of the following starting materials in parts by weight: 11 parts of non-ionic surfactant(s), 18 parts of hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, 6 parts of anionic surfactant(s), 6 parts of an organic phosphonic acid-carboxylic acid scale inhibitor, 3 parts of a dispersant, 16 parts of a diluent, 8 parts of an organic amine salt, and 35 parts of water.

(13) Preparation method: to a dry enamel reaction kettle, water 350 kg, organic phosphonic acid-carboxylic acid scale inhibitor 60 kg, anionic fluorocarbon surfactant 60 kg, and non-ionic surfactant 110 kg were added in this order; a stirrer was started, and organic amine salt 80 kg and hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate 180 kg were added under stirring; the mixture was heated to 80 C. to react for 5 hours, and then cooled to room temperature; diluent 160 kg and dispersant 30 kg were added; and the product was collected to give the high-performance pressure-reducing and injection-enhancing agent for low permeability water injection wells as a commercial product.

(14) In this Example, the non-ionic surfactant is a polyoxyethylene nonyl phenyl ether TX-10; hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate; the anionic surfactant is (RfCH.sub.2CH.sub.2O)nPO(ONH.sub.4)m, wherein Rf=F(CF.sub.2CF.sub.2)x, n+m=3, and x=1 to 7, having a molecular weight of 500 to 600; the organic phosphonic acid-carboxylic acid scale inhibitor is 2-phosphonobutane-1,2,4-tricarboxylic acid, the dispersant is monobutyl glycol ether; the diluent is ethanol; and the organic amine salt is monoethanolamine.

(15) The technical parameters of quality of the high-performance pressure-reducing and injection-enhancing agent for low-permeability water-injection wells prepared in Examples 1-4 of the present disclosure are as follows: Appearance: colorless transparent liquid at room temperature; pH: 9 to 12; Anti-swelling ratio: 60% or higher, tested according to SY/T 5971 Method for evaluating the performance of clay stabilizer for water injection; Shrinkage ratio: 30% or higher; Anti-scaling ratio: 95% or higher against calcium sulfate; 90% or higher against barium (strontium) sulfate; tested according to Q/SY 126-2014 Technical requirements for anti-corrosion scale inhibitor for water treatment of oil fields; Corrosion rate: 0.021 mm/a or lower; according to SY/T 5273-2014 Criteria and evaluation method for performance of anti-corrosion agent for water treatment of oil field products; Solubility of barium sulfate at 60 C.: 0.8 g/100 g or higher.

(16) When used in an amount being 0.5% of the water injected to a water injection well, it shows excellent anti-swelling property, shrinking property, anti-corrosive property, and calcium sulfate and barium (strontium) sulfate scale resistance. At 60 C., the solubility of barium sulfate is increased by 3125 times.

(17) An on-site test using the high-performance pressure-reducing and injection-enhancing agent for low-permeability water-injection wells prepared in Example 4 was performed as follows.

(18) The high-performance pressure-reducing and injection-enhancing agent for low permeability water injection wells was tested on site in the No. x-xx well of the X oil exploitation plant in Changqing oil field. The average permeability is 3 MD, sensitive to weak acids. Over the first 10 months of injection, the water absorbing index dropped from 3.1 m.sup.3/d.Math.MPa to 1.1 m.sup.3/d.Math.MPa, and the corrosion rate dropped from 0.082 mm/a to 0.036 mm/a. The formation water of the oil field contained approximately 3,000 mg/L barium (strontium) ions, and the water for injection is of a sodium sulfate type, which are very incompatible to each other and easily produce carbonate or sulfate precipitates in formation layers, which is one of the major reasons responsible for reservoir plugging. An unplugging process using the high-performance pressure-reducing and injection-enhancing agent for low-permeability water-injection wells was applied. After the unplugging process, the water absorbing index started to increase and stabilized at the level of 3.3 m.sup.3/d.Math.MPa, and the daily injection amount of water was increased from 18 m.sup.3 to 39 m.sup.3, which remained effective for over 2.1 years without a pump checking operation due to scaling.

(19) In summary, the high-performance pressure-reducing and injection-enhancing agent for low-permeability water-injection wells according to the present disclosure is characterized by having multiple functions in one agent. As compared to the anti-scaling agents in the prior art, the present agent combines the product of the reaction between an organic phosphonic acid-carboxylic acid scale inhibitor and an organic amine with hexasodium triethylenetetramine-N,N,N,N,N,N-hexaacetate, which results in excellent anti-scaling and anti-corrosive performance, and makes the agent very easily adsorb microcrystalline sulfate scale on a surface physically and chemically to greatly improve the solubility of the sulfate scale. In practical production, since the surface of scales often has a layer of oily soil adhered thereon, washing with non-ionic and anionic surfactants and an organic amine salt ensures sufficient contact between the agent and the scales, while the dispersant and diluent can ensure that active components act on rock surfaces more rapidly. When used in an amount of 0.5%, it shows excellent anti-swelling property, shrinking property, anti-corrosive property, and calcium sulfate and barium (strontium) sulfate scale resistance. At 60 C., the solubility of barium sulfate is increased by 3125 times. The agent prevents and suppresses corrosion and scaling in the water injection system for oil fields to a greater extent, extends the lifetime of equipment and pipes, ensures effective operation of prior production, and increases the recovery ratio from oil reservoirs.

(20) Those test methods not described in detail in the above Examples are common knowledge in the art, and specified description thereof is omitted here.