METHOD OF FABRICATING THIN FORM FACTOR VIBRATION ISOLATORS WITH STABLE STORAGE MODULUS PROPERTIES OVER EXTENDED TEMPERATURE RANGES AS STANDALONE PARTS

Abstract

A liquid RTV material is calendared and cured to form a sheet of Silicone material. The de-gassing, pressing and curing steps are tailored to provide a low porosity Silicone sheet having a fine surface finish and consistent chemical properties. The sheet is stamped or cut to form standalone vibration isolators having a thin and dimensionally stable form factor of less than 1.25 mm that exhibit a stable storage modulus to temperature excursions below 30 C. and preferably over a range of 60 C. to 100 C.

Claims

1. A method of fabricating vibration isolators, comprising: providing a liquid room temperature vulcanizing (RTV) material having a viscosity of less than 100,000 centipose (cps); calendaring the liquid RTV material to press the liquid RTV material into a sheet; curing the sheet of liquid RTV material to form a sheet of solid Silicone material having a thickness of less than 1.25 mm; and forming one or more vibration isolators from the sheet of solid Silicone material, each said vibration isolator having a thickness of less than 1.25 mm and a storage modulus of between 2,000 KPa and 5,000 KPa at operating temperatures below 30 C.

2. The method of claim 1, wherein the liquid RTV material comprises a Silicone polymer.

3. The method of claim 2, further comprising: mixing the liquid RTV material with a tin catalyst.

4. The method of claim 3, wherein the viscosity of the liquid RTV material is between 30,000 and 100,000 cps.

5. The method of claim 1, wherein the storage modulus varies by less than 700 KPa at operating temperatures between 30 C. and 60 C.

6. The method of claim 1, wherein storage modulus varies by less than 700 KPa at operating temperatures between 60 C. and 100 C.

7. The method of claim 1, wherein the thickness of the sheet of solid Silicone material varies by less than +/0.127 mm.

8. The method of claim 1, wherein the sheet of solid Silicone material has a Shore A hardness of between 64-66 at room temperature.

9. The method of claim 1, wherein the step of calendaring the liquid RTV material comprises: adjusting a gap between a pair of rollers to a specified sheet thickness; providing a pair of calendaring plates joined at one end; adding a stiffening material to an outer surface of each said plate; inserting the calendaring plates joined end first between the pair of rollers; mixing the liquid RTV material with a catalyst; de-gassing the liquid RTV material; pouring the liquid RTV material between the calendaring plates; and running the calendaring process to press the liquid RTV material between the rollers into the sheet of liquid RTV material.

10. The method of claim 9, wherein the calendaring plates are Poly Tetra Fluoro Ethylene (PTFE) coated fiberglass plates and the stiffening material is a polyester film.

11. The method of claim 9, wherein the liquid RTV material is de-gassed in a vacuum pressure of less than 650 torr for at least 10 minutes.

12. The method of claim 9, wherein the step of curing the pressed liquid RTV material comprises: curing the sheet of liquid RTV material at room temperature and room humidity for at least 24 hours to cross-link the RTV material to provide dimensional stability to form the sheet of solid Silicone material; removing the sheet of solid Silicone material from the calendaring plates; curing the material at room temperature and elevated relative humidity to increase the cross-linking; and curing the material at an elevated temperature and at least 30% relative humidity to complete crosslinking and stabilize the Silicone material.

13. The method of claim 11, wherein the Silicone sheet is post cured at an elevated temperature of at least 110 C.

14. The method of claim 1, wherein the step of curing the liquid RTV material comprises: curing the sheet of liquid RTV material at room temperature and room relative humidity for at least 24 hours to cross-link the RTV material to provide dimensional stability to form the sheet of solid Silicone material; removing the sheet of solid Silicone material from the calendaring plates; curing the material at room temperature and elevated relative humidity to increase the cross-linking; and curing the material at an elevated temperature to complete crosslinking and stabilize the Silicone material.

15. A method of fabricating vibration isolator components, comprising: providing a liquid room temperature vulcanizing (RTV) material comprising a Silicone polymer and having a viscosity of less than 100,000 centipose (cps); calendaring the liquid RTV material to press the liquid RTV material into a sheet; curing the sheet of liquid RTV material to form a sheet of solid Silicone material having a thickness of less than 1.25 mm; and forming one or more vibration isolator components from the sheet of solid silicon material, each said vibration isolator component having a thickness of less than 1.25 mm that varies by less than +/0.127 mm and a storage modulus of between 2,000 KPa and 5,000 that varies less than 700 KPa between operating temperatures between 60 C. and 100 C.

16. A method of fabricating vibration isolator components, comprising: providing a liquid room temperature vulcanizing (RTV) material having a viscosity of less than 100,000 centipose (cps); calendaring the liquid RTV material comprising the steps of: adjusting a gap between a pair of rollers to a specified sheet thickness of less than 1.25 mm; providing a pair of calendaring plates joined at one end; adding a stiffening material to the outside surface of each said plate; inserting the calendaring plates joined end first between the pair of rollers; mixing the liquid RTV material with a catalyst; de-gassing the liquid RTV material for at least 10 minutes; pouring the liquid RTV material between the plates; and running the calendaring process to press the liquid RTV material between the rollers into a sheet of liquid RTV material, and curing the sheet of liquid RTV material comprising the steps of: curing the sheet of liquid RTV material at room temperature and room humidity for at least 24 hours to cross-link the RTV material to provide dimensional stability to form the sheet of solid Silicone material; removing the sheet of solid Silicone material from the calendaring plates; curing the material at room temperature and an elevated relative humidity of at least 45% to increase the cross-linking; and curing the material at an elevated temperature of at least 110 C. to complete crosslinking and stabilize the Silicone material to form a sheet of solid Silicone material having a thickness of less than 1.25 mm; and forming one or more vibration isolator components from the sheet of solid silicon material, each said vibration isolator component having a thickness of less than 1.25 and a storage modulus of between 2,000 KPa and 5,000 at operating temperatures below 30 C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] FIGS. 1 and 2 are embodiments of a flow diagram and a process flow for fabricating vibration isolation components having a thin form factor and exhibiting stable storage modulus properties over extended temperature ranges; and

[0011] FIG. 3 is a diagram of an embodiment of an assembled vibration isolator.

DETAILED DESCRIPTION OF THE INVENTION

[0012] The present invention is directed to a method of fabricating a particular sub-class of passive vibration isolators having characteristics, which taken in combination pose unique challenges to the fabrication. First, the isolator must be fabricated as a standalone part. This part has a thin form factor <1.25 mm thick and must exhibit dimensional stability across the surface e.g. a variation of less than +/<0.127 mm. The part should exhibit stable mechanical properties including a Shore A hardness of between 64-66 at room temperature that remains stable over an operating temperature range. To provide the requisite dampening, the part must exhibit a storage modulus of 2,000 to 5,000 KPa over the operating temperature range including temperature excursions to less than 30 C. In typical applications, the part should exhibit less than a 700 Pa variation over an extended temperature range of 60 C. to 100 C. Providing the requisite storage modulus (damping properties) in a standalone part with such a thin form factor to temperatures below 30 C. was particularly challenging.

[0013] The known processes of casting-in-place a liquid RTV or rolling HRC into sheets and curing were not viable. A CIP RTV cannot provide a standalone part or satisfy the dimensional stability requirements. The HRC materials only exhibit stable storage modulus down to 20 C and are not viable in a form factor <1.25 mm.

[0014] We attempted to use an Injection Molding technique with the liquid RTV 560 to form the passive vibration isolators to these specifications. Injection Molding can provide standalone parts and in theory the liquid RTV can provide stable chemical properties (e.g., storage modulus) well below 60 C. Unfortunately this approach was not viable. Liquid RTV is humidity cured, which requires moisture to permeate throughout and material. Unlike cast-in-place, injection molding has a limited number of small vent holes, which did not allow sufficient moisture permeation. This resulted in highly porous material with greatly varying mechanical and chemical properties. We reached out to multiple suppliers of Silicone sheets to provide sheets to these specifications and no one bid the request. We then considered using liquid RTV with a standard calendaring process to form Silicon sheets. However, the liquid RTV runs during calendaring and the resultant Silicone sheet tends to wrinkle and is highly porous, and therefore is not suitable. The dimensional stability, mechanical and chemical properties of the sheet were all degraded.

[0015] To achieve the extended operating temperature range to below 30 C. and preferably to at least 60 C., we concluded that we needed to use a low viscosity RTV material such as RTV 560. To take advantage of the properties of RTV, a process for fabricating the liquid RTV into a solid Silicone sheet w/ the desired thin and uniform form factor and stable chemical properties (storage modulus and Shore A hardness) over the extended temperature range from which standalone parts could be stamped or cut had to be developed.

[0016] To accomplish this we modified a standard calendering process and the cure schedule specified in the RTV 560 TDS (Technical Data Sheet) by (a) adding a stiffening material to the calendaring plates to maintain the thickness uniform thickness and surface finish of the sheet (prevents wrinkling), (b) extending the degassing of the RTV far beyond that called for in the TDS to reduce the porosity, e.g., from a specified 2-3 minutes to at least 10 minutes and (c) implementing a 3-step curing process to provide dimensional stability by first curing the material at room temperature and relative humidity for at least 24 hours to cross-link the RTV to form a solid Silicone, removing the top calendering plate and curing the sheet at room temp and elevated humidity to increase cross-linking and finally post curing the sheet at an elevated temperature to stabilize the material and complete the cross-linking. The resulting Silicone sheet and passive vibration isolators satisfy the requirements for standalone parts, thin and stable form factor and stable storage modulus over an extended temperature range.

[0017] Referring now to FIGS. 1 and 2, an embodiment of the method of fabricating passive vibration isolators includes providing a low viscosity RTV material 10 (step 100) such as RTV 560. As described in the Momentive TDS for RTV 560, the material is a Silicone rubber compound comprising low temperature two-part Silicone elastomers. RTV 560 is designed for a room temperature cure and once cured has a continuous useful operating temperature range that spans115 C. to 260 C. with a Shore A hardness of 55. As stated, RTV is typically used for cast-in-place heat shielding and potting and encapsulation of electrical assemblies. The RTV acts as both a vibration and thermal isolator. The RTV material 10 is mixed with a catalyst 12 (step 102) suitably DBT (dibutyl tin dilaurate) as a curing agent. The mixture 14 is placed in a vacuum 16 and de-gassed for an extended period of time of at least 10 minutes (step 104). The vacuum pressure is suitably less than 650 torr. Extended degassing reduces the porosity of the material.

[0018] The gap between a pair of rollers 18 of a calendaring machine 20 is adjusted to a specified sheet thickness of less than 1.25 mm (step 106). A stiffening material 22 is added to the outside surface of each of a pair of calendaring plates 24 joined at one end 26 (step 108). In an embodiment, the calendaring plates are Poly Tetra Fluoro Ethylene (PTFE) coated fiberglass plates and the stiffening material is a polyester film. Stiffening improves dimensional stability of the material during processing to prevent, for example, wrinkling. The stiffened calendaring plates 24 are inserted joined end first between the pair of rollers 18 (step 110).

[0019] The liquid RTV material 14 is poured between calendaring plates 24 (step 112) and the calendaring process (rollers 18) is run (step 114) to press the liquid RTV material between the rollers into a sheet 28 of liquid RTV material. Stiffened calendaring plates 24 and sheet 28 are removed from the calendaring machine and placed on a flat surface.

[0020] The 24 hour room temperature cure specified in the TDS and typically employed to cure RTV 560 is replaced with a three-step process designed to form a dimensional stable sheet with the desired mechanical and chemical properties over the operating temperature range. The three-step cure produces a Silicone with a Shore A hardness of 64-66, for example. First, sheet 28 is cured at room temperature and room humidity for at least 24 hours to cross-link the RTV material to provide dimensional stability to form a sheet of solid Silicone material 29 (step 116). Room temperature is typically 23 C.+/2 C. and room relative humidity is typically between 15 and 40%. Both the top and bottom calendaring plates are removed (step 118) and the material is cured at room temperature and an elevated relative humidity of at least 45% to increase the cross-linking for a period of at least 18 hours (step 120). The material is post cured in an oven 30 at an elevated temperature of at least 110 C. for a period of at least 8 hours to complete crosslinking and stabilize the Silicone material to form the sheet of solid Silicone material. A specific humidity level is not a requirement for post cure. The chemistry at this point in the process does not require water (step 122). The Silicone sheet 29 is stamped with a die 32 or otherwise cut to form the passive vibration isolators 34 (step 124). One or more vibration isolators are assembled with an object to be isolated in a system (step 126).

[0021] Referring now to FIG. 3, in an embodiment a system 200 includes an object 202 that requires isolation from both mechanical and thermal inputs. In this system, one or more fasteners 204 secure the isolated object 202 to an upper level assembly 206. A washer 208 is used to distribute the load of the fastener 204 across the surface of a pair of passive vibration isolators 210 (of the type previously described), which are sandwiched between a mounting flange 212 of isolated object 202. A shim 214 may be inserted to adjust the height of the isolated object. In this system, the vibration isolators 210 must be standalone parts in order to be assembled with the fastener and washer in this manner and must have a thin form factor and dimensional stability. Furthermore, this particular system requires either continuous operation or excursions to temperatures less than 30 C.

[0022] While several illustrative embodiments of the invention have been shown and described, numerous variations and alternate embodiments will occur to those skilled in the art. Such variations and alternate embodiments are contemplated, and can be made without departing from the spirit and scope of the invention as defined in the appended claims.