Prelubricated stock sheet and method and system for making the same

Abstract

A pre-lubricated stock sheet and a method and system for making the same are described. The pre-lubricated stock is generally in a coil wound form. The stock sheet can have opposing first and second sheet surfaces joined together by opposing side edges and opposing ends. Typically, the first and second sheet surfaces are substantially smooth and planar, wherein the sheet has 3 mg/foot.sup.2/side to about 200 mg/foot.sup.2/side of a solid lubricant having a melting temperature from about 80 to 212 degrees Fahrenheit. Moreover, the opposing side edges usually are substantially free of the solid lubricant. In some configurations, the stock sheet is an aluminum stock sheet, more particularly an aluminum can stock sheet. Furthermore, the lubricant can be in some configurations a food grade lubricant, that is qualifies a low volatile organic compound under one or more of municipal, state and federal governing authorities.

Claims

1. A method, comprising: heating a solid lubricant to form a liquid lubricant; flowing the liquid lubricant to one or more pairs of applicators contained in an enclosure comprising a sheet inlet and a sheet outlet, wherein the enclosure is one or more of heated and insulated and wherein the enclosure is maintained at a temperature of from about 80 to 212 degrees Fahrenheit; passing a stock sheet having opposing planar first and second stock sheet surfaces joined together by opposing stock sheet side edges and opposing stock sheet ends through the sheet inlet and the sheet outlet; contacting the first and second stock sheet surfaces with the one or more pairs of applicators to form a lubricated stock sheet, wherein each of the one or more pairs of applicators deposits the liquid lubricant on the first and second stock sheet surfaces, and wherein no more than a total of from about 3 mg/foot.sup.2/side to about 200 mg/foot.sup.2/side of the liquid lubricant is deposited on the first and second stock sheet surfaces by the one or more pairs of applicators; and winding the lubricated stock sheet into a coil.

2. The method of claim 1, wherein a melting temperature of the solid lubricant ranges from about 100 to about 200 degrees Fahrenheit, wherein no more than a total of from about 5 mg/foot.sup.2/side to about 110 mg/foot.sup.2/side of the liquid lubricant is deposited on the first and second stock sheet surfaces by the one or more pairs of applicators, and wherein the flowing and contacting further comprises: applying air pressure to a headspace of a lubricant-containing vessel to cause the liquid lubricant to flow pneumatically to the one or more pairs of applicators; flowing the liquid lubricant from the lubricant-containing vessel to a perforated applicator element having first and second perforated element surfaces, wherein the perforated applicator element is in fluid communication with a porous applicator element having first and second porous element surfaces, wherein the liquid lubricant flows from the first perforated element surface to the second porous element surface and from the second porous element surface to the first porous element surface, and wherein the contacting further comprises contacting the first porous element surface with the first and second stock sheet surfaces to deposit the liquid lubricant on the stock sheet.

3. The method of claim 2, wherein the first perforated element surface is in physical contact with the second porous element surface, wherein the melting temperature of the solid lubricant ranges from about 140 to about 195 degrees Fahrenheit, wherein the dispensed liquid lubricant forms a substantially continuous and substantially uniform lubricant layer on each of the first and second stock sheet surfaces of the lubricated stock sheet, wherein the perforated applicator element comprises a metallic material, a polymeric material, or a combination thereof, wherein the perforated applicator element comprises a plurality of apertures, a plurality of channels, or a combination thereof substantially uniformly distributed over the first and second perforated element surfaces, wherein the porous applicator element comprises a textile material, an organic polymeric material, an inorganic polymeric material, or a combination thereof, wherein the porous applicator element is permeable, porous, or both porous and permeable, wherein the enclosure is heated and further comprising: supplying thermal energy to the one or more pairs of applicators, wherein the thermal energy is supplied by one or more thermal heating elements contained within the enclosure and positioned between the one or more pairs of applicators and the enclosure; and controlling, in response to input from a pressure indicator and by a pressure-adjusting element, a pressure applied to the first and second stock sheet surfaces by the porous applicator element to deposit the liquid lubricant on the stock sheet, wherein the pressure-adjusting element comprises one of an electromechanical device, a solenoid, a pneumatic device, or a combination thereof.

4. The method of claim 1, wherein a melting temperature of the solid lubricant ranges from about 80 to about 212 degrees Fahrenheit, wherein the first and second stock sheet surfaces, respectively, have first and second sheet surface areas, and wherein the contacting further comprises depositing the liquid lubricant on from about 99 to about 100% of the first and second sheet surface areas.

5. The method of claim 1, wherein the contacting further comprises contacting the stock sheet with the one or more pairs of applicators while the stock sheet is moving at a rate of about 100 to about 2,000 feet/minute, and wherein each of the first and second sheet surfaces comprises from about 60 mg/foot.sup.2/side to about 90 mg/foot.sup.2/side of the liquid lubricant.

6. The method of claim 1, wherein the enclosure is heated and further comprising supplying thermal energy to the one or more pairs of applicators, wherein the thermal energy is supplied by plural thermal heating elements positioned within the enclosure, wherein the plural heating elements are positioned symmetrically about the one or more pairs of applicators, and wherein each of the first and second sheet surfaces has from about 60 mg/foot.sup.2/side to about 90 mg/foot.sup.2/side of the liquid lubricant.

7. The method of claim 1, wherein each of the first and second sheet surfaces has from about 90 to about 100 mg/foot.sup.2/side with a variation in thickness of about 10 mg/foot.sup.2/side of the liquid lubricant.

8. The method of claim 1, wherein one or more temperature sensing elements determine the enclosure temperature and a temperature controller maintains the enclosure temperature in the range of from about 80 to 212 degrees Fahrenheit and further comprising heating the enclosure using hot air produced from a heat exchanger fan subassembly comprising one or more fans and one or more heat exchanger elements.

9. The method of claim 1, wherein from about 3.7 to about 13.9 mg/square meter of the liquid lubricant is deposited on the stock sheet by the one or more pairs of applicators, wherein the one or more pairs of applicators contact the first and second sheet surfaces at a rate of from about 50 to about 6,000 feet/minute, wherein one or more of the following is true: (i) the solid lubricant is one or more of a NSF, Kosher or Halal approved food grade lubricant; (ii) the solid lubricant is one of dioctyl sulfosuccinate, 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, dioctyl sebacate, bis(2-ethylhexyl) sebacate, sebacic acid di(2-ethylhexyl) ester, hydrotreated heavy naphthenic petroleum distillates, alkenes having a carbon chain length greater than ten, and poly--olefin, petrolatum, and mixtures thereof; (iii) the solid lubricate is FDA approved per 21 CFR 178.3910 Paragraph (b); and (iv) the solid lubricant qualifies as a low volatile organic compound under one or more of municipal, state and federal governing authorities and wherein the heating comprises monitoring, by a temperature element, a temperature in a lubricant-heating vessel and heating, in response to input from a temperature controller in communication with the temperature element, the solid lubricant in the lubricant-heating vessel.

10. The method of claim 1, wherein the enclosure is heated and further comprising: supplying thermal energy to the one or more pairs of applicators, wherein the thermal energy is supplied by multiple thermal heating elements positioned within the enclosure, wherein the heating elements are positioned symmetrically about the one or more pairs of applicators, and wherein the stock sheet comprises one of steel, stainless steel, copper, tin, nickel, gold, platinum, rhodium, aluminum, an organic polymeric material, a metal, an alloyed metal, and a combination thereof.

11. The method of claim 2, wherein the heating comprises monitoring, by a first temperature element, a temperature in a lubricant-containing vessel and heating, in response to input from a temperature controller in communication with the first temperature element, the solid lubricant in the lubricant-containing vessel, wherein the heating comprises monitoring, by a second temperature element, a temperature in process piping transporting the liquid lubricant from the lubricant-containing vessel to the one or more pairs of applicators and heating, in response to input from the temperature controller in communication with the second temperature element, the lubricant in the process piping, and wherein, prior to the contacting, first and second side edges of the stock sheet are substantially free of the liquid and/or the solid lubricant.

12. The method of claim 1, wherein the heating comprises monitoring, by a first temperature element, a temperature in a lubricant-containing vessel and heating, in response to input from a temperature controller in communication with the first temperature element, the solid lubricant in the lubricant-containing vessel, wherein the heating comprises monitoring, by a second temperature element, a temperature in process piping transporting the liquid lubricant from the lubricant-containing vessel to the one or more pairs of applicators and heating, in response to input from the temperature controller in communication with the second temperature element, the lubricant in the process piping, and wherein opposing stock sheet side edges are substantially free of the liquid lubricant.

13. A method of claim 2, wherein the heating comprises: measuring, by a first temperature element, a first temperature in one or more lubricant heating vessels; heating, in response to commands from a temperature controller, the solid lubricant in the one or more lubricant heating vessels to form the liquid lubricant; transferring the liquid lubricant from the one or more lubricant heating vessels to the lubricant-containing vessel; measuring, by a second temperature element, a second temperature of one or more heated transfer lines; heating, in response to commands from the temperature controller, the one or more heated transfer lines; and flowing the liquid lubricant from the lubricant-containing vessel to the one or more pairs of applicators through the one or more heated transfer lines.

14. A method comprising: heating a solid lubricant to form a liquid lubricant; flowing pneumatically the liquid lubricant, under air pressure, from a heated lubricant-containing vessel through one or more heated transfer lines to one or more pairs of applicators comprising a perforated applicator element having first and second perforated element surfaces, wherein the perforated applicator element is in fluid communication with a porous applicator element having first and second porous element surfaces, wherein the liquid lubricant flows from the first perforated element surface to the second porous element surface and from the second porous element surface to the first porous element surface, and wherein the one or more pairs of applicators is contained in an enclosure comprising a sheet inlet to receive a stock sheet and a sheet outlet to output a lubricated stock sheet, wherein the enclosure is one or more of heated and insulated; contacting the first porous element surface with the stock sheet comprising opposing substantially planar first and second surfaces to deposit the liquid lubricant on the first and second surfaces and form the lubricated stock sheet, wherein the contacting occurs at a temperature from about 80 to 212 degrees Fahrenheit; and forming the lubricated stock sheet into a coil.

15. The method of claim 14, wherein a melting temperature of the solid lubricant ranges from about 100 to about 200 degrees Fahrenheit, wherein no more than a total of from about 5 mg/foot.sup.2/side to about 110 mg/foot.sup.2/side of the liquid lubricant is deposited on the stock sheet by the one or more pairs of applicators, and further comprising: applying air pressure to a headspace of the heated lubricant-containing vessel to cause pneumatically the liquid lubricant to flow under air pressure to the one or more pairs of applicators; passing the stock sheet through the sheet inlet of the thermally insulated and heated enclosure and the sheet outlet configured for the stock sheet to traverse the enclosure and wherein the contacting occurs within the enclosure, wherein one or more temperature sensing elements determines an enclosure temperature and a temperature controller maintains the enclosure temperature in the range of from about 80 to 212 degrees Fahrenheit; and controlling, in response to input from a pressure indicator, a pressure applied to the first and second stock sheet surfaces by the porous applicator element to deposit the liquid lubricant on the stock sheet, wherein the pressure adjusting element comprises one of an electromechanical device, a solenoid, a pneumatic device, or a combination thereof.

16. The method of claim 15, wherein the enclosure is heated, wherein the first perforated element surface is in contact with the second porous element surface, wherein the melting temperature of the solid lubricant ranges from about 140 to about 195 degrees Fahrenheit, wherein the dispensed liquid lubricant forms a substantially continuous and substantially uniform lubricant layer on the lubricated stock sheet, wherein the perforated applicator element comprises a metallic material, a polymeric material, or a combination thereof, wherein the perforated applicator element comprises a plurality of apertures, a plurality of channels, or a combination thereof substantially uniformly distributed over the first and second perforated element surfaces, wherein the porous applicator element comprises a textile material, an organic polymeric material, an inorganic polymeric material, or a combination thereof, and wherein the porous applicator element is permeable, porous, or both porous and permeable, and further comprising: supplying thermal energy to the one or more pairs of applicators, wherein the thermal energy is supplied by one or more heating elements, and wherein the one or more heating elements are contained within the enclosure in thermal proximity to the one or more pairs of applicators.

17. The method of claim 14, wherein from about 3.7 to about 13.9 mg/square meter of the liquid lubricant is deposited on the stock sheet by the one or more pairs of applicators, wherein the one or more pairs of applicators contact the first and second sheet surfaces at a rate of about 50 to about 6,000 feet/minute, wherein the heating step comprises monitoring, by a temperature element, a temperature in the heated lubricant-containing vessel and heating, in response to input from a temperature controller in communication with the temperature element, the solid lubricant in the heated lubricant-containing vessel, and wherein the contacting step further comprises one or more of the following: (i)depositing liquid lubricant on from about 99 to about 100% of the first and second sheet surfaces of the stock sheet; and (ii) depositing no more than a total of from about 3 mg/foot.sup.2/side to about 200 mg/foot.sup.2/side of the liquid lubricant on the stock sheet by the one or more pairs of applicators.

18. The method of claim 14, wherein the heating step comprises monitoring, by a first temperature element, a temperature in the heated lubricant-containing vessel and heating, in response to input from a temperature controller in communication with the first temperature element, the solid lubricant in the heated lubricant-containing vessel, wherein the heating step comprises monitoring, by a second temperature element, a temperature in process piping transporting the liquid lubricant from the heated lubricant-containing vessel to the one or more pairs of applicators and heating, in response to input from the temperature controller in communication with the second temperature element, the process piping, and wherein each of the first and second surfaces of the stock sheet has from about 90 to about 100 mg/foot.sup.2/side with a variation in thickness of about 10 mg/foot.sup.2/side of the liquid lubricant and wherein each of the first and second sheet surfaces has from about 60 mg/foot.sup.2/side to about 90 mg/foot.sup.2/side of the liquid lubricant.

19. A method, comprising: providing a stock sheet having opposing substantially planar first and second stock sheet surfaces joined together by opposing stock sheet side edges and opposing stock sheet ends; passing the stock sheet through an enclosure comprising a sheet inlet and a sheet outlet configured for the stock sheet to traverse the enclosure and to maintain a liquid lubricant in liquid form, wherein the enclosure is one or more of heated and insulated; contacting at least one of the first and second stock sheet surfaces with one or more pairs of applicators located within the enclosure to form a lubricated stock sheet, wherein each pair of applicators in the one or more pairs of applicators deposits the liquid lubricant to form a substantially continuous and substantially uniform lubricant layer on at least one of the first and second stock sheet surfaces, wherein the contacting occurs at a temperature of from about 80 to about 212 degrees Fahrenheit, wherein the liquid lubricant is a solid lubricant at ambient temperature, and wherein at least one of the following is true: (i)the contacting occurs while the stock sheet is moving at a rate of about 100 to about 2,000 feet/minute; and (ii) no more than a total of from about 3 mg/foot.sup.2/side to about 200 mg/foot.sup.2/side of the liquid lubricant is deposited on the stock sheet by the one or more pairs of applicators.

20. The method of claim 19, wherein one or more temperature sensing elements determine an enclosure temperature of the enclosure and a temperature controller maintains the enclosure temperature in the range of from about 80 to 212 degrees Fahrenheit and further comprising: applying air pressure to a headspace of a lubricant-containing vessel to pneumatically cause the liquid lubricant to flow, under air pressure, to the one or more pairs of applicators, wherein a temperature element monitors a temperature in the lubricant-containing vessel and, in response to input from the temperature element, a temperature controller in communication with the temperature element causes heating of a solid lubricant in the lubricant-containing vessel; flowing the liquid lubricant from the lubricant-containing vessel to a perforated applicator element having first and second perforated element surfaces, wherein the perforated applicator element is in fluid communication with a porous applicator element having first and second porous element surfaces, wherein the liquid lubricant flows from the first perforated element surface to the second porous element surface and from the second porous element surface to the first porous element surface, and wherein the contacting further comprises: contacting the first porous element surface with the stock sheet surface to deposit the liquid lubricant on the stock sheet; and controlling, in response to input from a pressure indicator, a pressure applied to the stock sheet by the first porous element surface.

21. The method of claim 19, wherein the first and second stock sheet surfaces respectively have first and second sheet surface areas, and wherein the contacting further comprises depositing liquid lubricant on more than about 99% of the first and/or second sheet surface areas.

22. The method of claim 19, wherein the amount of liquid lubricant deposited on the first and/or second stock sheet surfaces varies no more than about 10 mg/foot.sup.2 and further comprising: measuring, by a first temperature element, a first temperature in one or more lubricant heating vessels; heating, in response to commands from a temperature controller, a solid lubricant in the one or more lubricant heating vessels to form the liquid lubricant; measuring, by a second temperature element, a second temperature of one or more heated transfer lines; heating, in response to commands from the temperature controller, the one or more heated transfer lines; and transferring the liquid lubricant from the one or more lubricant heating vessels to the one or more pairs of applicators through the one or more heated transfer lines.re heated transfer lines.

23. The method of claim 19, wherein the passing and contacting steps comprise: monitoring, by a first temperature element, a temperature in a lubricant-containing vessel and heating, in response to input from a temperature controller in communication with the first temperature element, a solid lubricant in the lubricant-containing vessel to form the liquid lubricant; monitoring, by a second temperature element, a temperature in process piping transporting the liquid lubricant from the lubricant-containing vessel to the one or more pairs of applicators; and heating, in response to input from the temperature controller in communication with the second temperature element, the lubricant in the process piping, wherein prior to the contacting step, first and second side edges of the stock sheet are substantially free of the liquid and/or the solid lubricant, and further comprising winding the lubricated stock sheet to form a coil of the lubricated stock sheet.

24. A method, comprising: heating a solid lubricant in a lubricant heating vessel to form a liquid lubricant; transporting the liquid lubricant to a heated lubricant-containing vessel; applying pressure to a headspace of the lubricant-containing vessel to cause pneumatically the liquid lubricant to flow under air pressure through heated piping to an enclosure comprising one or more pairs of applicators, wherein the enclosure is one or more of heated and insulated; supplying thermal energy to the one or more pairs of applicators, wherein the thermal energy is supplied by one or more thermal heating elements contained within the enclosure and positioned near each of the one or more pairs of applicators; passing a stock sheet comprising opposing substantially planar first and second stock sheet surfaces joined together by opposing stock sheet side edges and opposing stock sheet ends through the sheet inlet and the sheet outlet; receiving, by a temperature controller, temperature measurements from temperature sensing elements in thermal communication with each of the lubricant heating vessel, heated lubricant-containing vessel, heated piping, and one or more thermal heating elements; in response to the temperature measurements, controlling an amount of thermal energy supplied to a plurality of the lubricant heating vessel, heated lubricant-containing vessel, heated piping, and one or more thermal heating elements to maintain a temperature of the liquid lubricant above a melting point of the solid lubricant; and winding the lubricated stock sheet into a coil.

25. The method of claim 24, wherein the melting temperature of the solid lubricant ranges from about 80 to 212 degrees Fahrenheit and further comprising: controlling, in response to input from a pressure indicator and by a pressure-adjusting element, a pressure applied to the first and second stock sheet surfaces by the one or more pairs of applicators to deposit the liquid lubricant on the stock sheet, wherein the pressure-adjusting element comprises an electromechanical device, a solenoid, a pneumatic device, or a combination thereof.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The accompanying drawings are incorporated into and form a part of the specification to illustrate several examples of the present disclosure. These drawings, together with the description, explain the principles of the disclosure. The drawings simply illustrate preferred and alternative examples of how the disclosure can be made and used and are not to be construed as limiting the disclosure to only the illustrated and described examples. Further features and advantages will become apparent from the following, more detailed, description of the various aspects, embodiments, and configurations of the disclosure, as illustrated by the drawings referenced below.

(2) FIG. 1 depicts a device according to some embodiments of the present disclosure;

(3) FIG. 2 depicts an exploded view of the component having reference number 101 in FIG. 1;

(4) FIG. 3 depicts a cross-sectional view of the component having reference number 108 in FIG. 1:

(5) FIG. 4 depicts a cross-sectional view of the component having reference number 104 in FIG. 1;

(6) FIG. 5 depicts a cross-sectional view of the component having reference number 106 in FIG. 1;

(7) FIG. 6 depicts a cross-sectional view of the component having reference number 102 in FIG. 1;

(8) FIG. 7 depicts a cross-sectional view of the component having reference number 131 in FIG. 1;

(9) FIG. 8 depicts a process according to some embodiments of the present disclosure;

(10) FIG. 9 depicts an exploded view of the component having reference number 194 in FIG. 1;

(11) FIG. 10 depicts an exploded view of the component having reference number 194 in FIG. 9;

(12) FIGS. 11A-11C depict three perspective views of the component having reference number 200 in FIG. 10;

(13) FIG. 12 is a diagram of the device according to some embodiments of the disclosure;

(14) FIG. 13 is a plot of the temperature of lubricant-containing vessel according to Example 2;

(15) FIG. 14 is a plot of the pressure of lubricant-containing vessel according to Example 2;

(16) FIG. 15 is a plot of the temperature of various device components contained with the enclosure according to Example 2;

(17) FIG. 16 is a plot of the applicator pressure according to Example 2;

(18) FIG. 17 is plot of the applicator pressure according to Example 3;

(19) FIG. 18 is a plot of the temperature of lubricant-containing vessel according to Example 3;

(20) FIG. 19 is a plot of the of the pressure of lubricant-containing vessel according to Example 3;

(21) FIG. 20 is a plot of the of the temperature of lubricant-containing vessel according to Example 4;

(22) FIG. 21 is a plot of the of the pressure of lubricant-containing vessel according to Example 4;

(23) FIG. 22 is a plot of the temperature of various device components contained with the enclosure according to Example 4;

(24) FIG. 23 is a plot of the of the temperature of lubricant-containing vessel according to Example 5;

(25) FIG. 24 is a plot of the of the pressure of lubricant-containing vessel according to Example 5;

(26) FIG. 25 is a plot of the of the pressure of applicators according to Example 5;

(27) FIG. 26 is a plot of the temperature of various device components contained with the enclosure according to Example 5;

(28) FIG. 27 is a plot of the of the temperature of lubricant-containing vessel according to Example 6;

(29) FIG. 28 is a plot of the of the pressure of lubricant-containing vessel according to Example 6;

(30) FIG. 29 is a plot of the temperature of various applicators contained with the enclosure according to Example 6;

(31) FIG. 30 is a plot of the applicator set temperature according to Example 6;

(32) FIG. 31 is a plot of the top prelubrication weights according to Example 6;

(33) FIG. 32 is a plot of the bottom prelubrication weights according to Example 6;

(34) FIG. 33 is a plot of the prelubrication viscosity according to Example 6;

(35) FIG. 34 is a plot of the of the temperature of lubricant-containing vessel according to Example 7;

(36) FIG. 35 is a plot of the of the pressure of lubricant-containing vessel according to Example 7;

(37) FIG. 36 is a plot of the temperature of various applicators contained with the enclosure according to Example 7;

(38) FIG. 37 is a plot of the applicator set pressure according to Example 7;

(39) FIG. 38 is a plot of the top prelubrication weights according to Example 7;

(40) FIG. 39 is a plot of the bottom prelubrication weights according to Example 7; and

(41) FIG. 40 is a plot of the prelubrication viscosity according to Example 7.

DETAILED DESCRIPTION

(42) The method discussed herein can apply to stock sheet, with aluminum alloy sheet being illustrative.

(43) FIG. 1 depicts a device 100 according to some embodiments. The device 100 can have one or more pairs of applicators 101a and 101b, 101r and 101s, and so forth to 101y and 101z with each applicator 101 of the more of more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z. Each applicator 101 can include a porous applicator element 104, a perforated applicator element 108, and a liquid-dispensing element 118 (FIG. 2).

(44) Each applicator 101 of the one or more pair of applicators 101a and 101b, 101r and 101s, and so forth to 101y and 101z can have an applicator axis 126. The liquid-dispensing element 118 is generally positioned along the applicator axis 126.

(45) The perforated applicator element 108 can have first 122 and second 123 perforated element surfaces (FIG. 3). The porous applicator element 104 can have first 124 and second 125 porous element surfaces (FIG. 4). The first porous element surface 124 is generally the outer surface of each applicator 101 of the one or more applicators 101a and 101b, 101r and 101s, and 101y and 101z. Moreover, the second perforated element surface 123 is typically the inner surface of each of applicator 101 of the one the one or more pair applicators 101a and 101b, 101r and 101s, and 101y and 101z. The first perforated element surface 122 is usually in contact with the second porous element surface 125.

(46) The one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z can be configured consecutively. In some embodiments, the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z can include from about two to about three pairs of applicators 101. Moreover, the about two to about six pairs of applicators 101 can be configured consecutively. In some embodiments, the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z can include three pairs of applicators 101. Furthermore, the three pairs of applicators 101 can be configured consecutively.

(47) The perforated applicator element 108 can be one of a metallic material, a polymeric material, or a combination thereof. Generally, the perforated applicator element 108 can be one of steel, stainless steel, aluminum, stainless steel, or brass. More generally, the perforated applicator element 108 can be a metallic material. Furthermore, the perforated applicator element 108 can have a plurality of apertures, channels, or a combination thereof substantially uniformly distributed about most, if not all, of the perforated applicator element 108. Moreover, the perforated applicator element 108 can have a plurality of apertures, a plurality of channels, or a combination thereof substantially uniformly distributed over the perforated applicator element surface area. Furthermore, the plurality of apertures, the plurality of channels, or the combination thereof are sufficiently sized such that lubricant is uniformly distributed to the porous applicator element 104 and is not retrained by perforated applicator element 108.

(48) The porous applicator element 104 can comprise one of a textile material, an organic polymeric material, an inorganic polymeric material, or a combination thereof. Furthermore, the porous applicator element 104 can comprise one of a felt, a non-woven material, a solid foam material, a sponge material, or a fabric. Moreover, the porous applicator element 104 can be permeable, porous, or both porous and permeable. Usually, the porous applicator element 104 can have a wall thickness from about to about of an inch.

(49) Each pair of applicators 101 can have first 126a and second 126b applicator axes aligned in parallel. First 128 and second outer 129 surfaces of the applicators forming each pair of applicators (such as 101a and 101b, 101r and 101s, and 101y and 101z) are generally separated by a distance sufficient for accepting the stock sheet. The pressure-adjusting element 107 increases and/or decreases the distance such that the first 128 and second 129 outer surfaces of applicators 101 can apply a pressure on the stock sheet 102 positioned between the first and second applicators. It can be appreciated that in some embodiments, the pressure-adjusting element comprises one of an electromechanical device, a solenoid, a pneumatic device, or a combination thereof. Furthermore, the pressure-adjusting element 107 can be one of contained within the enclosure 121, external to the enclosure, or partially contained within the enclosure 121 and partially contained external to the enclosure 121.

(50) The liquid-dispensing element 118 generally dispenses a liquid lubricant. The dispensed liquid lubricant generally contacts the second perforated element surface 123.

(51) The device 100 can also have one or more pressure-adjusting elements 107. Typically, each of the applicators 101 has at least one pressure-adjusting element 107.

(52) The device 100 can also have one or more heating elements 105. The one or more heating elements 105 can be positioned between the enclosure 121 and the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z. The device 100 can include the one or more heating elements 105 being positioned symmetrically about the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z. Moreover, the one or more heating elements 105 can provide sufficient thermal energy to the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z to maintain a temperature within the enclosure 121 of from about 80 to 212 degrees Fahrenheit, more commonly, more commonly from about 100 to 200 degrees Fahrenheit, and even more commonly from about 140 to 195 degrees Fahrenheit. Generally, the one or more heating elements 105 can be one of an electrical resistance heating element, a hot water radiant heating element, a stream radiant heating element, a high-pressure steam radiant heating element, a super-critical steam radiant heating element, an infrared heating element, or a hot oil radiant heating element.

(53) The device 100 can also have an enclosure 121. The enclosure 121 can have a sheet stock inlet 111 and a sheet stock outlet 113. Moreover, the sheet stock inlet 111 and outlet 113 can be configured for a stock sheet 102 to traverse the enclosure 121. The stock sheet 102 can traverse midway between each pair of the one or more pairs of applicators 101a and 101b, 101r and 101s, and 101y and 101z. Typically, the enclosure 121 can be one of an insulated enclosure, a non-insulated enclosure, or a combination of insulated and non-insulated portions. The one or more pairs of applicators 101a and 101b, 101r and 101s, and so forth to 101y and 101z and the one or more heating elements 105 can be contained with the enclosure 121.

(54) The device 100 can also have a lubricant-containing vessel 103. The lubricant-containing vessel 103 is generally in fluid communication with each of the liquid-dispensing elements 118 of the applicators 101. The lubricant-containing vessel 103 is typically in fluid communication with each of the liquid-dispensing elements 118 through conduit 115.

(55) The device 100 can further include one or more temperature sensing elements 109. The enclosure 109 can have a void volume 130 having a void volume temperature. The one or more temperature sensing elements 109 can determine the void volume temperature. In some embodiments, the one or more temperature sensing elements 109 can be contained within the enclosure 121. In some embodiments, the one or more temperature sensing elements 109 can be configured external to the enclosure 121. In some embodiments, some of the one or more temperature sensing elements 109 can be configured external to the enclosure 121 and the others of the one or more temperature sensing elements 109 can be contained within the enclosure 121.

(56) The lubricant is typically a solid at ambient temperature. Generally, the lubricant-containing vessel 103 can be a heated to maintain the lubricant within the lubricant-containing vessel at a temperature greater than the ambient temperature. Commonly, the lubricant-containing vessel 103 contains lubricant in a liquefied form. The lubricant-containing vessel 103 is generally heated to a temperature greater than the ambient temperature to liquefy the lubricant.

(57) The device 100 can further have a pressurizing element (not depicted). The pressurizing element can convey the liquefied lubricant from the lubricant-containing vessel 103 to the liquid-dispensing elements 118 of each of the applicators 101.

(58) The device 100 can produce a coil wound sheet 106 (FIG. 5) having opposing first 110a and second 110b sheet surfaces joined together by opposing side edges 117a and 117b and opposing ends 119a and 119b (FIGS. 6 and 7). The first 110a and second 110b sheet surfaces are typically substantially smooth and planar. The lubricant 114 on the coil wound sheet 106 is generally in the solid form at ambient temperature. That is, the lubricant 114 on the coil wound sheet 106 is typically a solid lubricant. The solid lubricant is generally deposited on the first 110a and second 110b sheet surfaces. The opposing sheet side edges 117a and 117b are commonly substantially free of the solid lubricant 114. The lubricated stock sheet 131 generally has from about 3.7 to about 13.9 mg per square meter of a lubricant 114 deposited on the sheet 120.

(59) The first 110a and second 110b sheet surfaces, respectively, can have first and second sheet surface areas. Typically, more than about 95% of the first and second sheet surface areas are in contact with the solid lubricant 114. More typically, more than about 98% of the first and second sheet surface areas are in contact with the solid lubricant 114. Even more typically, more than about 99% of the first and second sheet surface areas are in contact with the solid lubricant 114. Yet even more typically, more than about 99.8% of the first and second sheet surface areas are in contact with the solid lubricant 114.

(60) The solid lubricant 114 is generally deposited on the first 110a and second 110b sheet surfaces of the coil wound sheet 106. The lubricated stock sheet 131 commonly has a sum total of solid lubricant 114 deposited on first 110a and second 110b surfaces of the coil wound sheet 106 is from about 3.7 to about 13.9 mg per square meter, more commonly from about 5.6 to about 11.6 mg per square meter, and even more commonly from 4.6 to about 9.3 mg per square meter.

(61) The lubricant 114 can have a melting temperature from about 80 to 212 degrees Fahrenheit, more commonly, more commonly from about 100 to 200 degrees Fahrenheit, and even more commonly from about 140 to 195 degrees Fahrenheit.

(62) The lubricant 114 can be a food grade lubricant. The lubricant 114 can commonly be one or more of a NSF, Kosher or Halal approved food grade lubricant. Generally, the lubricant can be one of dioctyl sulfosuccinate, 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, dioctyl sebacate, bis(2-ethylhexyl) sebacate, sebacic acid di(2-ethylhexyl) ester, hydrotreated heavy naphthenic petroleum distillates, alkenes having a carbon chain length greater than ten, and poly--olefin, petrolatum, and mixtures thereof. The lubricate 114 is usually a FDA approved lubricant per 21 CFR 178.3910 Paragraph (b). Moreover, the lubricant 114 can qualify as a low volatile organic compound under one or more of municipal, state and federal governing authorities.

(63) The first 110a and second 110b sheet surfaces can have can commonly have from about 3 mg/foot.sup.2/side to about 200 mg/foot.sup.2/side of the lubricant, more commonly about 5 mg/foot.sup.2/side to about 110 mg/foot.sup.2/side of the lubricant or even more commonly about 60 mg/foot.sup.2/side to about 90 mg/foot.sup.2/side of the lubricant. In some embodiments, each of the upper and lower surfaces of the sheet can generally have about 15010 mg/foot.sup.2 of lubricant, more generally about 10010 mg/foot.sup.2 of lubricant, even more generally about 8010 mg/foot.sup.2 of lubricant, and even more generally about 9010 mg/foot.sup.2 of lubricant.

(64) The lubricated stock sheet 131 and/or coil wound sheet 106 can be one of steel, stainless steel, copper, tin, nickel, gold, platinum, rhodium, aluminum, an organic polymeric material, a metal, an alloyed metal, or a combination thereof. In some embodiments, the lubricated stock sheet 131 and/or coil wound sheet 106 can be selected from the group consisting essentially of steel, stainless steel, copper, tin, nickel, gold, platinum, rhodium, aluminum, an organic polymeric material, a metal, an alloyed metal, or a combination thereof.

(65) The lubricated stock sheet 131 and/or coil wound sheet 106 can be an automotive sheet stock.

(66) The lubricated stock sheet 131 and/or coil wound sheet 106 can be a can sheet body, tab or end stock. The can sheet stock can be one an AA 5182 series-based alloy, an AA5182ES, AA5182SP, AA5182FE, AA5182M8, an AA 3004 series-based alloy, AA3004, AA8011, AA3104, AA35182, AA3104, AA5052, and AA5006. In some embodiments, the can sheet stock can be one of steel and stainless steel.

(67) In accordance with some embodiments is a process 140 (FIG. 8).

(68) In step 142, a stock sheet 102 is provided. The stock sheet can have opposing first 110a and second 110b stock sheet surfaces joined together by opposing stock sheet side edges 117a and 117b and opposing stock sheet ends 119a and 119b.

(69) In step 144, the first 110a and second 110b stock sheet 102 surfaces are contacted with one or more pairs of applicators 101a and 101b, 101r and 101s, and so forth to 101y and 101z to form a lubricated stock sheet 131. Contacting step 144 can include a step of depositing, step 147, with each pair of applicators 110 depositing a liquefied lubricant 114 on the first 110a and second 110b stock sheet surfaces to form the lubricated stock sheet 131.

(70) The first 110a and second 110b sheet surfaces are typically substantially smooth and planar. The lubricant 114 on the coil wound sheet 106 is generally in the solid form at ambient temperature. That is, the lubricant 114 on the coil wound sheet 106 is typically a solid lubricant. The solid lubricant is generally deposited on the first 110a and second 110b sheet surfaces. The opposing sheet side edges 117a and 117b are commonly substantially free of the solid lubricant 114. The lubricated stock sheet 131 generally has from about 3.7 to about 13.9 mg per square meter of a lubricant 114 deposited on the sheet 120.

(71) The first 110a and second 110b sheet surfaces, respectively, can have first and second sheet surface areas. Typically, more than about 95%, more typically, more than about 98%, more typically, more than about 99%, and even more typically, more than about 99.8% of the first and second sheet surface areas are in contact with the solid lubricant 114.

(72) It can be appreciated that the liquefied lubricant is generally applied at a temperature greater than the ambient temperature. Moreover, the lubricant is commonly a solid lubricant at ambient temperature, and is usually deposited (on the stock sheet) in a liquefied state. Typically, the contacting step 144 occurs at a temperature from about 80 to 212 degrees Fahrenheit, more commonly, more commonly from about 100 to 200 degrees Fahrenheit, and even more commonly from about 140 to 195 degrees Fahrenheit. Commonly, the opposing stock sheet edges are substantially free of the liquefied lubricant.

(73) Some embodiments can include a step of supplying thermal energy, step 141, to the one or more pairs of applicators 101. Generally, the thermal energy can be supplied by one or more thermal heating elements 105. The one or more heating elements 105 and the one or more pairs of applicators 101a and 101b, 101r and 101s, and so forth to 101y and 101z can be contained with an enclosure 121. The one or more thermal heating elements 105 can supply sufficient thermal energy to maintain the one or pairs of applicators 101 at a temperature from about 80 to 212 degrees Fahrenheit, more commonly, more commonly from about 100 to 200 degrees Fahrenheit, and even more commonly from about 140 to 195 degrees Fahrenheit. The heating elements 105 can be one of an electrical resistance heating element, a hot water radiant heating element, a stream radiant heating element, a high-pressure steam radiant heating element, a super-critical steam radiant heating element, an infrared heating element, or a hot oil radiant heating element. The enclosure 121 can be one of an insulated enclosure, a non-insulated enclosure, or a combination of insulated and non-insulated portions.

(74) In step 146, the lubricated stock sheet 131 is coil wound to form a roll of the lubricated stock sheet 106.

(75) Some embodiments can include a step of flowing, step 143, the liquefied lubricant 114 from a lubricant-containing vessel 103 to a liquid-dispensing element 118. The step 143 can also include dispensing, from the liquid-dispending element 118, the liquefied lubricant 114 to a perforated applicator element 108 having first 122 and second 123 perforated element surfaces. Moreover, the perforated applicator element 108 can typically be in fluid communication with the porous applicator element 104 having first 124 and second 125 porous element surfaces. Furthermore, the liquefied lubricant can generally flow from the first perforated element surface 122 to the second porous element surface 125 and from the second porous element surface 125 to the first porous element surface 124.

(76) In some embodiments, the stock sheet can commonly be contacted with each pair of the one or more pairs of applicators at a rate of about 50 to about 6,000 feet per minute, more commonly at a rate of about 100 to about 2,000 feet per minute, or even more commonly at a rate of about 400 to about 700 feet per minute.

(77) FIG. 9 depicts in accordance with some embodiments, a sheet lubricant application system 190 in operating position to engage stock sheet 102 between an oiler 191 and a breakdown roll system 192. The oiler 191 can be without limitation a Peabody oiler. The breakdown roll system 192 generally includes a breakdown roller 193.

(78) As can be seen from FIGS. 9, 10 and 11A-11C, the system 190 includes a drawer assembly 194. The drawer assembly 194 is generally positioned within a system mounting 195 by first and second roll caster assemblies 196a and 196b. The drawer assembly 194 can be removed from the system mounting 195 by means of the first and second roll cast assemblies 196a and 196b.

(79) With reference to FIG. 10, the sheet lubricant application system 190 includes an application subassembly 200, valve stack 204, left and right lubricator supports 208a and 208b, bulk head plate 212, heat box bottom 216 of the drawer assembly 194, heat box top 220 of the drawer assembly 194, heat exchanger fan subassemblies 224a, 224b, 224c, and 224d, hex bolt flanges 228, and fasteners 232 and washers 236. The heat exchanger fan subassemblies 224a, 224b, 224c, and 224d with each comprising a fan and heat exchanger tubing (not depicted), whereby air blown by the fans is heated by hot water in the tubing to heat the application subassembly 200 and avoid solidification of the lubricant during application to the sheet. The valve stack comprises fluid flow meters to meter lubricant fluid flow to the application rollers.

(80) With reference to FIGS. 3 and 11A-C, the applicator subassembly 200 includes six roller subassemblies 304a-f, a male tee push fitting 308, a pressure regulator assembly 312, an upper roller carrier 316, a pivot replacement pin 320, a pivot bracket 324, an air cylinder assembly 330, a push-in swivel elbow 334, lower roller carrier 338, a dispenser assembly 342, a mounting bracket for the air cylinder 346, a stub shaft with a jam nut 350, a tube guard 354, a T-slot extrusion 358, and a double endplate with cut outs 362. The adjacent roller subassemblies 304 move up and down to adjustably engage the sheet. The pressure regulator assembly 312 measures the pressure applied by each adjacent pair of roller subassemblies to the sheet.

(81) With reference to FIG. 4, each roller subassembly 204 comprises a liquid-dispensing element 118, porous applicator element 104, perforated applicator element 108, roller end caps (which includes the bearing) 112a,b, bearing 116, and stub shaft 120. As can be seen from the assembled cutaway, the liquid-dispensing element 118 passes through the end cap1 112a and 112b and includes orifices 132 along its length to dispense heated liquid lubricant. 114 in liquefied form. The liquid lubricant 114 flows through the perforations in the perforated applicator element 108 to soak the porous applicator element 104, which contacts the stock sheet 102 and applies liquid lubricant 114 to the stock sheet 102 by roll coating techniques under controlled pressure, allowing precise control of the amount of lubricant 114 applied. The opposing pairs of roller subassemblies apply lubricant to opposing surfaces of the stock sheet 102. The porous applicator element 104 is commonly one or more of polyurethane foam, polyester felt, or wool felt.

(82) With reference to FIG. 12, the control circuitry and ancillary equipment for the lubricant application system 190 is depicted. The lubricant application system 190 comprises first and second lubricant heating vessels 400a,b, which heat and melt the solid lubricant by means of heating assemblies 404. The heated lubricant is mixed by impellers 408. The heated lubricant is transported to the lube dispensing vessel 416, which is also heated by a heating assembly 404. Under the pressure of air, the heated liquid lubricant passes pneumatically along heated lube process piping 412 to the lubricant injectors 300 for introduction into the roller subassemblies 204.

(83) The control circuitry includes the following components: electrical supply (ES), flow controller (FC), timer alarm high (KAH), pressure indicator (PI), (to indicate pressure in the pneumatic signal lines), pressure alarm high (PAH), pressure alarm low (PAL), pressure transmitter (PT), (to transmit pressure measurements in the pneumatic signal lines), solenoid valve (SOV), temperature element (TE), (in measure temperatures in each of the lube dispensing vessel 416, lube drum preheat station 400a and lube drum dispensing station 400b, the transfer piping, and the enclosure), temperature indicator (TI), (to transmit temperature measurements), temperature indicating controller (TIC), temperature controller (TC), (controlling the temperatures in the lube process piping, the lube dispensing vessel 416, lube drum preheat station 400a and lube drum dispensing station 400b), temperature alarm high (TAH), and temperature alarm low (TAL). Other component types in the lubricant application system 190 include lube process piping (connecting the lube dispensing vessel 416 with the lubricant injectors 300 to apply pressure), water supply, pneumatic signal (line), (connecting plant air with each of the lubricant injectors 300 and the lube dispensing vessel 416), electrical signal (line), ethernet connection, manual valve, solenoid valve, self-relieving pressure regulator (with manually adjustable set point) (to regulate pressure in the pneumatic signal lines), motor, heating element (to provide thermal energy in response to input from the temperature controller), manual pressure relief valve, fan (to heat the enclosure), filter, and visual alarm (showing alarm type designator and alarm set point value).

(84) Control subassemblies include for the first and second lubricant heating vessels 400a,b, and lube dispensing vessel 416 include a temperature controller and temperature element pairing to monitor the temperature of the lubricant.

(85) Control subassembly for the heated lube process piping 412 temperature controller and temperature element to monitor piping temperature (and avoid lubricant solidification in the piping during pneumatic transport.

(86) Control subassemblies for each of the roller subassemblies 204 include a proximity sensor (to detect roller subassembly speed or rotation rate to shut down automatically the device in the event of a rate above or below set thresholds) and solenoid valves to shut down the flow of liquid lubricant in the event of system malfunction or shut down. A temperature element and control can be engaged with the lubricant supply to or within each roller subassembly 204 to shut down automatically the device in the event a measured temperature between a first and second roller subassemblies exceeds a set threshold.

(87) The drawer assembly 194 is engaged with a proximity sensor to determine when the drawer assembly 194 is not in a proper (operative) position. When the proximity sensor detects that the drawer assembly 194 is in an improper position, the system is rendered inoperative.

(88) The lubricant typically has a melt point typically no more than about 250% above, more typically no more than about 200% above, more typically no more than about 150% above, and even more typically no more than about 100% above ambient temperature. In one application, the lubricant has a melt point at or slightly above (typically no more than about 35% above and more typically no more than about 25% above) ambient temperature. In one application, the melt point of the lubricant ranges from ambient temperature (or slightly above room temperature) commonly from about 80 to 212 degrees Fahrenheit, more commonly, more commonly from about 100 to 200 degrees Fahrenheit, and even more commonly from about 140 to 195 degrees Fahrenheit. Ambient temperature typically ranges from about 12 to about 3 and more typically from about 18 to about 27 degrees Celsius. The lubricant can be any oil, soluble oil, semisynthetic, and dry-film. In addition to having good lubricity, lubricants should be easily removable from the formed sheet, because the can body has to be completely oil-free for painting. Therefore, in selection/evaluation of stamping lubricants, one should consider advantages and disadvantages of lubricants not only for deep drawing but also for assembly and painting operations. Examples of suitable lubricants include AMCO5157, Quakerol Pre Lube, AMCO5357, and O4C-172.

(89) In one configuration, the sheet lubricant application system 190 can be set to apply, to each of the upper and lower surfaces of the sheet, about 15010 mg/foot.sup.2 of lubricant, more commonly about 10010 mg/foot.sup.2 of lubricant, even more commonly about 8010 mg/foot.sup.2 of lubricant, and even more commonly about 9010 mg/foot.sup.2 of lubricant.

EXPERIMENTAL

(90) The following examples are provided to illustrate certain aspects, embodiments, and configurations of the disclosure and are not to be construed as limitations on the disclosure, as set forth in the appended claims. All parts and percentages are by weight unless otherwise specified.

(91) Three different lubricants (I, II, and III) where applied to a standard aluminum can stock sheet according to the above methods and sample at ten different locations on the coil wound coil. Table 1 shows that the lubricant was substantially uniformly distributed on the stock sheet.

(92) TABLE-US-00001 TABLE 1 Cut (lubricant weights mg/ft.sup.2) Lubricant 1 2 3 4 5 6 7 8 9 10 I 63 60 65 58 55 60 61 67 69 65 II 67 61 59 62 49 47 55 66 70 64 IIIA 58 58 52 47 48 44 60 53 55 57 IIIB 59 68 66 70 61 60 60 65 56 62

Example 2

(93) Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 2. FIGS. 13-16 show that the lubricant-containing vessel temperature and pressure and the applicator temperature and pressure can be substantially controlled in the above-identified process.

Example 3

(94) Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 3. FIGS. 17-19 show that the lubricant-containing vessel temperature and pressure and the applicator pressure can be substantially controlled in the above-identified process.

Example 4

(95) Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 4. FIGS. 20-22 show that the lubricant-containing vessel temperature and pressure and the temperature within the enclosure can be substantially controlled in the above-identified process.

Example 5

(96) Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 5. FIGS. 23-26 show that the lubricant-containing vessel temperature and pressure and the applicator temperature at various locations and pressure can be substantially controlled in the above-identified process.

Example 6

(97) Lubricant was applied to a standard aluminum can stock sheet according to the Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 6. FIGS. 27-35 show that the lubricant-containing vessel temperature and pressure, the applicator temperature at various locations and pressure, lubricant viscosity, and amount of lubricant deposited on opposing sides of the stock sheet can all be substantially controlled in the above-identified process.

Example 7

(98) Lubricant was applied to a standard aluminum can stock sheet according to the Lubricant was applied to a standard aluminum can stock sheet according to the process parameters of Table 7. FIGS. 34-40 show that the lubricant-containing vessel temperature and pressure, the applicator temperature at various locations and pressure, lubricant viscosity, and amount of lubricant deposited on opposing sides of the stock sheet can all be substantially controlled in the above-identified process.

(99) A number of variations and modifications of the disclosure can be used. It would be possible to provide for some features of the disclosure without providing others.

(100) TABLE-US-00002 TABLE 2 Fractional Distance from Start to End of Process Spiral Wound Roll Conditions start end Lube Pot F. 146 145 144 144 143 142 141 140 146 Lube Pot PSI 50 50 50 50 50 50 50 50 50 Roller Assembly 194 192 193 193 193 192 193 192 194 OP F. Roller Assembly 180 179 179 179 179 179 179 180 180 Center F. Roller Assembly 187 186 187 185 186 186 185 186 187 Drive F. Roll Set PSI 30 30 30 30 30 30 30 30 30

(101) TABLE-US-00003 TABLE 3 Fractional Distance from Start to End of Spiral Wound Roll Process Conditions start end Lube Pot F. 141 141 140 142 142 142 142 141 141 Lube Pot PSI 50 50 50 50 50 50 50 50 50 Roller Assembly OP F. 192 191 191 191 191 191 191 191 192 Roller Assembly Center F. 178 178 177 178 178 178 178 178 178 Roller Assembly Drive F. 192 192 191 192 191 191 191 191 192 Roll Set PSI 30 30 30 30 30 30 30 30 30

(102) TABLE-US-00004 TABLE 4 Fractional Distance from Start to End of Spiral Wound Roll Process Conditions start end Lube Pot F. 141 143 143 141 140 141 142 142 141 Lube Pot PSI 50 50 50 50 50 50 50 50 50 Roller Assembly OP F. 191 191 191 191 191 191 191 191 191 Roller Assembly Center F. 176 175 175 175 175 175 175 174 175 Roller Assembly Drive F. 191 191 191 191 191 191 191 191 191 Roll Set PSI 30 30 30 30 30 30 30 30 30

(103) TABLE-US-00005 TABLE 5 Fractional Distance from Start to End of Spiral Wound Roll Process Conditions start end Lube Pot F. 144 140 140 143 142 140 142 141 144 Lube Pot PSI 50 50 50 50 50 50 50 50 50 Roller Assembly OP F. 191 190 190 190 190 190 190 190 191 Roller Assembly Center F. 178 176 175 175 176 175 176 177 178 Roller Assembly Drive F. 189 188 188 189 189 189 188 189 189 Roll Set PSI 30 30 30 30 30 30 30 30 30

(104) TABLE-US-00006 TABLE 6 Fractional Distance from Start to End of Spiral Wound Roll Process Conditions start end Lube Pot F. 141 141 143 141 141 143 142 144 141 Lube Pot PSI 50 50.5 50 50 50.5 50 50 50 50 Roller Assembly 195 194 195 193 194 194.5 194 194 195 OP F. Roller Assembly 181 181 179 178 179 180 179 180 180 Center F. Roller Assembly 195 194.5 195 195 194.5 195 195 195 194 Drive F. Roll Set PSI 30 30 30 30 30 30 30 30 30

(105) TABLE-US-00007 TABLE 7 Fractional Distance from Start to End of Spiral Wound Roll Process Conditions start end Lube Pot F. 139 140 142 141 141 142 142 142 143 Lube Pot PSI 50 50.0 50 50 50.0 50 50 50 50 Roller Assembly 197 196 195 195 195 195 196 195 195 OP F. Roller Assembly 180 178 178 176 176 177 177 177 177 Center F. Roller Assembly 195 194 194 194 195 195 195 194 195 Drive F. Roll Set PSI 30 30 30 30 30 30 30 30 30

(106) A number of variations and modifications of the disclosure can be used. It would be possible to provide for some features of the disclosure without providing others.

(107) In accordance with some embodiments, the step of providing the stock sheet can be providing an automotive sheet stock.

(108) In accordance with some embodiments, the step of providing the stock sheet can be providing a can body, end or tab sheet stock. Moreover, the can sheet stock is one of an AA 5182 series-based alloy, an AA5182ES, AA5182SP, AA5182FE, AA5182M8, an AA 3004 series-based alloy, AA3004, AA8011, AA3104, AA35182, AA3104, AA5052, and AA5006. Furthermore, the can sheet stock is one of steel and stainless steel.

(109) An AA 5182 series-based alloy (e.g., AA 5182ES and SP) is useful for producing end stock. The AA 5182 series-based alloy generally has the following composition:

(110) (i) from about 0.20 to about 0.50%, even more commonly from about 0.225 to about 0.45%, and even more commonly from about 0.250 to about 0.35% by weight manganese;

(111) (ii) from about 4.0 to about 4.95%, even more commonly from about 4.5 to about 5%, and even more commonly from about 4.7 to about 4.95% by weight magnesium;

(112) (iii) from about 0.001 to about 0.15%, even more commonly from about 0.005 to about 0.11%, and even more commonly from about 0.01 to about 0.08% by weight copper;

(113) (iv) from about 0.01 to about 0.35%, even more commonly from about 0.015 to about 0.30%, and even more commonly from about 0.020 to about 0.25% by weight iron; and

(114) (v) from about 0.01 to about 0.20%, even more commonly from about 0.015 to about 0.175%, and even more commonly from about 0.05 to about 0.15% by weight silicon;

(115) (vi) from about 0.01 to about 0.25%, even more commonly from about 0.025 to about 0.15%, and even more commonly from about 0.05 to about 0.1% by weight chromium;

(116) (vii) from about 0.01 to about 0.25%, even more commonly from about 0.051 to about 0.20%, and even more commonly from about 0.075 to about 0.175% by weight zinc;

(117) (vii) from about 0.001 to about 0.01% and even more commonly from about 0.001 to about 0.075% by weight nickel; and

(118) (viii) from about 0.001 to about 0.1%, even more commonly from about 0.005 to about 0.075%, and even more commonly from about 0.01 to about 0.07% by weight titanium.

(119) An AA 5182 series-based alloy (e.g., AA 5182SP and FE) can be useful for producing tab stock. The AA 5182 series-based alloy typically has the following composition:

(120) (i) from about 0.20 to about 0.50%, even more commonly from about 0.225 to about 0.45%, and even more commonly from about 0.250 to about 0.35% by weight manganese;

(121) (ii) from about 4.0 to about 5%, even more commonly from about 4.2 to about 4.8%, and even more commonly from about 4.3 to about 4.6% by weight magnesium or in an alternative formulation even more commonly from about 4.8 to about 4.95% by weight magnesium;

(122) (iii) from about 0.001 to about 0.1%, even more commonly from about 0.005 to about 0.09%, and even more commonly from about 0.01 to about 0.08% by weight copper;

(123) (iv) from about 0.01 to about 0.35%, even more commonly from about 0.015 to about 0.30%, and even more commonly from about 0.020 to about 0.29% by weight iron; and

(124) (v) from about 0.01 to about 0.20%, even more commonly from about 0.015 to about 0.175%, and even more commonly from about 0.05 to about 0.15% by weight silicon;

(125) (vi) from about 0.01 to about 0.25%, even more commonly from about 0.025 to about 0.15%, and even more commonly from about 0.05 to about 0.1% by weight chromium;

(126) (vii) from about 0.01 to about 0.25%, even more commonly from about 0.051 to about 0.20%, and even more commonly from about 0.075 to about 0.175% by weight zinc;

(127) (vii) from about 0.001 to about 0.01% and even more commonly from about 0.001 to about 0.075% by weight nickel; and

(128) (viii) from about 0.001 to about 0.1%, even more commonly from about 0.005 to about 0.075%, and even more commonly from about 0.01 to about 0.07% by weight titanium.

(129) An AA 5182M8 series-based alloy useful for producing tab stock. The AA 5182M8 series-based alloy generally has the following composition:

(130) (i) from about 0.20 to about 0.50%, even more commonly from about 0.25 to about 0.45%, and even more commonly from about 0.275 to about 0.425% by weight manganese;

(131) (ii) from about 4 to about 5%, even more commonly from about 4.1 to about 4.7%, and even more commonly from about 4.15 to about 4.5% by weight magnesium;

(132) (iii) from about 0.001 to about 0.1%, even more commonly from about 0.01 to about 0.09%, and even more commonly from about 0.015 to about 0.08% by weight copper;

(133) (iv) from about 0.01 to about 0.35%, even more commonly from about 0.050 to about 0.30%, and even more commonly from about 0.075 to about 0.25% by weight iron; and

(134) (v) from about 0.001 to about 0.20%, even more commonly from about 0.01 to about 0.175%, and even more commonly from about 0.05 to about 0.15% by weight silicon;

(135) (vi) from about 0.001 to about 0.1%, even more commonly from about 0.01 to about 0.075%, and even more commonly from about 0.025 to about 0.050% by weight chromium;

(136) (vii) from about 0.001 to about 0.01% by weight nickel;

(137) (viii) from about 0.001 to about 0.1%, even more commonly from about 0.01 to about 0.09%, and even more commonly from about 0.015 to about 0.08% by weight titanium; and

(138) (ix) from about 0.01 to about 0.25%, even more commonly from about 0.015 to about 0.20%, and even more commonly from about 0.025 to about 0.15% by weight zinc.

(139) An AA 3004 series-based aluminum alloy (e.g., AA 5182ES and SP) is useful for producing body stock. The AA 3304 series-based aluminum alloy can have the following composition:

(140) (i) from about 0.75 to about 2.00%, even more commonly from about 0.85 to about 1.85%, and even more commonly from about 1 to about 1.5% by weight manganese;

(141) (ii) from about 0.5 to about 1.5%, even more commonly from about 0.65 to about 1.4%, and even more commonly from about 0.8 to about 1.3% by weight magnesium;

(142) (iii) from about 0.001 to about 0.35%, even more commonly from about 0.005 to about 0.30%, and even more commonly from about 0.01 to about 0.25% by weight copper;

(143) (iv) from about 0.001 to about 0.9%, even more commonly from about 0.005 to about 0.8%, and even more commonly from about 0.001 to about 0.7% by weight iron; and

(144) (v) from about 0.01 to about 0.40%, even more commonly from about 0.015 to about 0.35%, and even more commonly from about 0.05 to about 0.3% by weight silicon;

(145) (vi) from about 0.01 to about 0.25%, even more commonly from about 0.025 to about 0.15%, and even more commonly from about 0.05 to about 0.1% by weight chromium;

(146) (vii) from about 0.01 to about 0.25%, even more commonly from about 0.051 to about 0.20%, and even more commonly from about 0.075 to about 0.175% by weight zinc;

(147) (vii) from about 0.001 to about 0.01% and even more commonly from about 0.001 to about 0.075% by weight nickel; and

(148) (viii) from about 0.001 to about 0.1%, even more commonly from about 0.005 to about 0.075%, and even more commonly from about 0.01 to about 0.07% by weight titanium.

(149) It can be appreciated that any of above-identified alloy alloys can contain other elements. Typically, the elements other than those indicated in the above-identified aluminum alloys (AA 5182, AA51892M8, and AA3004 series-based) constitute no more than about 0.15% by weight of the composition.

(150) In some embodiments, the metal sheet is aluminum sheet having AA 5182 specifications and that is used for end or tab stock manufacture. AA 3004 commonly includes 0.9 to 1.1 wt. % magnesium and 0.9 to 1 wt. % manganese, while AA 5182 commonly includes from 4.6 to 4.9 wt. % magnesium and from 0.20 to 0.50 wt. % and more commonly no more than 0.35 wt. % manganese.

(151) The present disclosure, in various aspects, embodiments, and configurations, includes components, methods, processes, systems and/or apparatus substantially as depicted and described herein, including various aspects, embodiments, configurations, subcombinations, and subsets thereof. Those of skill in the art will understand how to make and use the various aspects, aspects, embodiments, and configurations, after understanding the present disclosure. The present disclosure, in various aspects, embodiments, and configurations, includes providing devices and processes in the absence of items not depicted and/or described herein or in various aspects, embodiments, and configurations hereof, including in the absence of such items as may have been used in previous devices or processes, e.g., for improving performance, achieving ease and\or reducing cost of implementation.

(152) The foregoing discussion of the disclosure has been presented for purposes of illustration and description. The foregoing is not intended to limit the disclosure to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the disclosure are grouped together in one or more, aspects, embodiments, and configurations for the purpose of streamlining the disclosure. The features of the aspects, embodiments, and configurations of the disclosure may be combined in alternate aspects, embodiments, and configurations other than those discussed above. This method of disclosure is not to be interpreted as reflecting an intention that the claimed disclosure requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed aspects, embodiments, and configurations. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate preferred embodiment of the disclosure.

(153) Moreover, though the description of the disclosure has included description of one or more aspects, embodiments, or configurations and certain variations and modifications, other variations, combinations, and modifications are within the scope of the disclosure, e.g., as may be within the skill and knowledge of those in the art, after understanding the present disclosure. It is intended to obtain rights which include alternative aspects, embodiments, and configurations to the extent permitted, including alternate, interchangeable and/or equivalent structures, functions, ranges or steps to those claimed, whether or not such alternate, interchangeable and/or equivalent structures, functions, ranges or steps are disclosed herein, and without intending to publicly dedicate any patentable subject matter.