RESISTIVE MEMORY DEVICES BASED ON METAL COORDINATED REDOX ACTIVE LIGANDS
20200312407 ยท 2020-10-01
Inventors
- Venkatesan Thirumalai (Singapore, SG)
- Sreetosh Goswami (Singapore, SG)
- Abhijeet Patra (Singapore, SG)
- Sreebrata Goswami (Kolkata, IN)
Cpc classification
H10N70/021
ELECTRICITY
International classification
G11C13/00
PHYSICS
C07F15/00
CHEMISTRY; METALLURGY
Abstract
Disclosed herein is a compound of formula (I):
[M(L).sub.n].sup.m+(A.sup.y).sub.z(I)
where A, M, L, n, m, y and z are as defined herein, which can be used in the formation of a resistive memory device. Also disclosed herein are methods of manufacturing such devices and their uses.
Claims
1. A compound of formula (I):
[M(L).sub.n].sup.m+(A.sup.y).sub.z(I) wherein: M represents Ru, Fe, Co, Rh, Ir, Ni, Os, Cr, Cu, Mn; A represents an anionic group having a charge y, where y represents from 1 to 4; in represents from 1 to 4; n represents from 2 to 6; z represents from 1 to 4; and L is a ligand selected from the ligand of formula (II) or one or more of the group consisting of ligands of formula (III) to (VII): ##STR00007## where: when L is the ligand (II), n is 2 and when L is a one or more of the group selected from (III) to (VII), n is 3; a and a each independently represent from 0 to 5; a, b and b to e each independently represent from 0 to 4; b represents from 0 to 3; R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 each independently represent, at each occurrence thereof, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, NR.sub.14R.sub.15, C(O)NR.sub.16R.sub.17, NR.sub.18C(O) R.sub.19, C(O)OR.sub.20, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, CN, alkyl, alkenyl, alkynyl (which latter three groups are unsubstituted or substituted by one or more substituents selected from OH, SH, C(O)OR.sub.22, or NR.sub.23R.sub.24), or, when present, any two instances of R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 together with the carbon atoms to which they are attached from a 5-12 membered cycloalkyl ring system, a 5-14 membered heterocycloalkyl ring system, a 6-10 membered aryl ring or a 5-14 membered heteroaryl ring system; and R.sub.4, R.sub.5 and R.sub.7 to R.sub.12 each independently represent, at each occurrence thereof, H, alkyl, alkenyl, alkynyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, or C(O)NR.sub.25R.sub.26; R.sub.14 to R.sub.26 each independently represent alkyl, alkenyl, alkynyl, cycloalkyl, aryl, heteroaryl, or aralkyl, provided that when M is Ir, Cr or Rh, L does not represent a ligand of formula (III).
2. The compound of claim 1, wherein L is the ligand of formula (II) or the ligand of formula (III).
3. The compound of claim 1, wherein R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 each independently represent, at each occurrence thereof, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, NR.sub.14R.sub.15, C(O)NR.sub.16R.sub.17, NR.sub.18C(O)R.sub.19, C(O)OR.sub.20, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, CN, alkyl, alkenyl, alkynyl (which latter three groups are unsubstituted or substituted by one or more substituents selected from OH, SH, C(O)OR.sub.22, or NR.sub.23R.sub.24), or, when present, any two instances of R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 together with the carbon atoms to which they are attached from a 5-7 membered cycloalkyl ring system, a 5-6 membered heterocycloalkyl ring system, a 6 membered aryl ring or a 5-6 membered heteroaryl ring system.
4. The compound of claim 3, wherein R.sub.1, R.sub.2, R.sub.1, and R.sub.2, each independently represent, at each occurrence thereof, alkyl, cycloalkyl, aryl, heteroaryl, NR.sub.14R.sub.15, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, or CN, optionally wherein R.sub.1, R.sub.2, R.sub.1, and R.sub.2, each independently represent, at each occurrence thereof, alkyl, halo, NO.sub.2, or CN (e.g. alkyl or halo).
5. The compound of claim 1, wherein: R.sub.4, R.sub.5 and R.sub.7 to R.sub.12 each independently represent, at each occurrence thereof, H or alkyl; and/or R.sub.14 to R.sub.26 each independently represent alkyl.
6. The compound of claim 1, wherein (A.sup.y) represents one or more anions selected from the group consisting of BF.sub.4.sup.l , ClO.sub.4.sup., PF.sub.6.sup., CF.sub.3SO.sub.3.sup., BPh.sub.4.sup., Cl.sup., Br.sup., and F.sup..
7. The compound of 6 claim 2, wherein a and a are 1, and b and b are 0, optionally wherein R.sub.1 and R.sub.1 are independently alkyl or halo.
8. The compound of claim 1, wherein L is selected from a ligand of formula (II) or formula (III): ##STR00008## wherein R.sub.1 and R.sub.1 are selected from H, alkyl or halo.
9. The compound of claim 1, wherein L is selected from the group consisting of: ##STR00009##
10. The compound of claim 1, wherein M represents Ru, Fe, Co, Ni, Os, optionally wherein M represents Ru; and/or (A.sup.y) represents (BF.sub.4.sup.) or (PF.sub.6.sup.) (e.g. (PF.sub.6.sup.)).
11. A resistive memory device comprising: a substrate material having a surface; and a compound of formula (I) as described in claim 1 coated onto at least a portion of the surface of the substrate material in the form of a film having a first surface and a second surface.
12. The device of claim 11, wherein the substrate material is YSZ.
13. The device of claim 11, wherein the device further comprises a first and second electrode, where the first electrode is sandwiched between the surface of the substrate and the first surface of the film of the compound of formula (I), and the second electrode is in direct contact with the second surface of the film of the compound of formula (I).
14. The device of claim 13, wherein the first electrode is ITO and/or the second electrode is gold or ITO.
15. The device of claim 14, wherein gold nanoparticles are deposited onto one of the first electrode and the film of the compound of formula (I).
16. The device of claim 14, wherein gold nanoparticles are deposited onto both of the first electrode and the film of the compound of formula (I), or are deposited therebetween.
17. A method of manufacturing a resistive memory device, the method comprising: a step of spin coating a solution comprising a solvent and a compound of formula (I), as described in claim 1, onto a substrate material.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045] .sup.)}(L.sup.2)]PF.sub.6.
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
[0056]
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068] .sup.)}(L.sup.2)]PF.sub.6 and [Ru(L.sup.2).sub.2](PF.sub.6).sub.2; and (c and d) planar and Au NDs devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2with full voltage scan and scan stopped at the intermediate plateau.
[0069]
[0070]
[0071]
[0072]
[0073]
[0074] .sup.)}(L.sup.2)]PF.sub.6: (a and c) pseudo colour plots of voltage-resolved Raman spectra for forward and backward sweep, respectively (1.8V.fwdarw.+2.9V and vice versa); (b and d) the top panel shows the J(V) response and the bottom panel shows the intensity of E.sub.0 (1301 cm.sup.1) and E.sub.1 (1259 cm.sup.1) modes for forward and backward sweep, respectively (1.8V.fwdarw.+2.9V and vice versa); and (e) UV-Vis spectra of the film and the solution of [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 at different states. Notations used: state-0=unreduced molecule; state-1=1-electron reduced state; and state-2=2-electron reduced state of the molecule.
DESCRIPTION
[0075] It has been surprisingly found that certain metallo-organic complexes are particularly useful in the formation of resistive memory devices. Said devices are generically described herein as a compound of formula (I):
[M(L).sub.n].sup.m+(A.sup.y).sub.z(I)
wherein:
[0076] M represents Ru, Fe, Co, Rh, Ir, Ni, Os, Cr, Cu, Mn;
[0077] A represents an anionic group having a charge y, where y represents from 1 to 4;
[0078] m represents from 1 to 4;
[0079] n represents from 2 to 6;
[0080] z represents from 1 to 4; and
[0081] L is a ligand selected from the ligand of formula (II) or one or more of the group consisting of ligands of formula (III) to (VII):
##STR00004##
where:
when L is the ligand (II), n is 2 and when L is a one or more of the group selected from (III) to (VII), n is 3;
a and a each independently represent from 0 to 5;
a, b and b to e each independently represent from 0 to 4;
b represents from 0 to 3;
[0082] R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 each independently represent, at each occurrence thereof, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, NR.sub.14R.sub.15, C(O)NR.sub.16R.sub.17, NR.sub.18C(O)R.sub.19, C(O)OR.sub.20, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, CN, alkyl, alkenyl, alkynyl (which latter three groups are unsubstituted or substituted by one or more substituents selected from OH, SH, C(O)OR.sub.22, or NR.sub.23R.sub.24), or, when present, any two instances of R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 together with the carbon atoms to which they are attached from a 5-12 membered cycloalkyl ring system, a 5-14 membered heterocycloalkyl ring system, a 6-10 membered aryl ring or a 5-14 membered heteroaryl ring system; and
[0083] R.sub.4, R.sub.5 and R.sub.7 to R.sub.12 each independently represent, at each occurrence thereof, H, alkyl, alkenyl, alkynyl, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, or C(O)NR.sub.25R.sub.26;
[0084] R.sub.14 to R.sub.26 each independently represent alkyl, alkenyl, alkynyl, cycloalkyl, aryl, heteroaryl, or aralkyl, provided that when M is Ir, Cr or Rh, L does not represent a ligand of formula (III).
[0085] The term halo, when used herein, includes references to fluoro, chloro, bromo and iodo.
[0086] Unless otherwise stated, the term aryl when used herein includes C.sub.6-14 (such as C.sub.6-10) aryl groups. Such groups may be monocyclic, bicyclic or tricyclic and have between 6 and 14 ring carbon atoms, in which at least one ring is aromatic. The point of attachment of aryl groups may be via any atom of the ring system. However, when aryl groups are bicyclic or tricyclic, they are linked to the rest of the molecule via an aromatic ring. C.sub.6-14 aryl groups include phenyl, naphthyl and the like, such as 1,2,3,4-tetrahydronaphthyl, indanyl, indenyl and fluorenyl. Embodiments of the invention that may be mentioned include those in which aryl is phenyl.
[0087] Unless otherwise stated, the term alkyl refers to an unbranched or branched, cyclic, saturated or unsaturated (so forming, for example, an alkenyl or alkynyl) hydrocarbyl radical, which may be substituted or unsubstituted (with, for example, one or more halo atoms). Where the term alkyl refers to an acyclic group, it is preferably C.sub.1-10 alkyl and, more preferably, C.sub.1-6 alkyl (such as ethyl, propyl, (e.g. n-propyl or isopropyl), butyl (e.g. branched or unbranched butyl), pentyl or, more preferably, methyl). Where the term alkyl is a cyclic group (which may be where the group cycloalkyl is specified), it is preferably C.sub.3-12 cycloalkyl and, more preferably, C.sub.5-10 (e.g. C.sub.5-7 ) cycloalkyl.
[0088] The term heteroaryl when used herein refers to an aromatic group containing one or more heteroatom(s) (e.g. one to four heteroatoms) preferably selected from N, O and S (so forming, for example, a mono-, bi-, or tricyclic heteroaromatic group). Heteroaryl groups include those which have between 5 and 14 (e.g. 10) members and may be monocyclic, bicyclic or tricyclic, provided that at least one of the rings is aromatic. However, when heteroaryl groups are bicyclic or tricyclic, they are linked to the rest of the molecule via an aromatic ring. Heterocyclic groups that may be mentioned include benzothiadiazolyl (including 2,1,3-benzothiadiazolyl), isothiochromanyl and, more preferably, acridinyl, benzimidazolyl, benzodioxanyl, benzodioxepinyl, benzodioxolyl (including 1,3-benzodioxolyl), benzofuranyl, benzofurazanyl, benzothiazolyl, benzoxadiazolyl (including 2,1,3-benzoxadiazolyl), benzoxazinyl (including 3,4-dihydro-2H-1,4-benzoxazinyl), benzoxazolyl, benzomorpholinyl, benzoselenadiazolyl (including 2,1,3-benzoselenadiazolyl), benzothienyl, carbazolyl, chromanyl, cinnolinyl, furanyl, imidazolyl, imidazo[1,2-a]pyridyl, indazolyl, indolinyl, indolyl, isobenzofuranyl, isochromanyl, isoindolinyl, isoindolyl, isoquinolinyl, isothiaziolyl, isoxazolyl, naphthyridinyl (including 1,6-naphthyridinyl or, preferably, 1,5-naphthyridinyl and 1,8-naphthyridinyl), oxadiazolyl (including 1,2,3-oxadiazolyl, 1,2,4-oxadiazolyl and 1,3,4-oxadiazolyl), oxazolyl, phenazinyl, phenothiazinyl, phthalazinyl, pteridinyl, purinyl, pyranyl, pyrazinyl, pyrazolyl, pyridazinyl, pyridyl, pyrimidinyl, pyrrolyl, quinazolinyl, quinolinyl, quinolizinyl, quinoxalinyl, tetrahydroisoquinolinyl (including 1,2,3,4-tetrahydroisoquinolinyl and 5,6,7,8-tetrahydroisoquinolinyl), tetrahydroquinolinyl (including 1,2,3,4-tetrahydroquinolinyl and 5,6,7,8-tetrahydroquinolinyl), tetrazolyl, thiadiazolyl (including 1,2,3-thiadiazolyl, 1,2,4-thiadiazolyl and 1,3,4-thiadiazolyl), thiazolyl, thiochromanyl, thiophenetyl, thienyl, triazolyl (including 1,2,3-triazolyl, 1,2,4-triazolyl and 1,3,4-triazolyl) and the like. Substituents on heteroaryl groups may, where appropriate, be located on any atom in the ring system including a heteroatom. The point of attachment of heteroaryl groups may be via any atom in the ring system including (where appropriate) a heteroatom (such as a nitrogen atom), or an atom on any fused carbocyclic ring that may be present as part of the ring system. Heteroaryl groups may also be in the N- or S-oxidised form. Particularly preferred heteroaryl groups include pyridyl, pyrrolyl, quinolinyl, furanyl, thienyl, oxadiazolyl, thiadiazolyl, thiazolyl, oxazolyl, pyrazolyl, triazolyl, tetrazolyl, isoxazolyl, isothiazolyl, imidazolyl, pyrimidinyl, indolyl, pyrazinyl, indazolyl, pyrimidinyl, thiophenetyl, thiophenyl, pyranyl, carbazolyl, acridinyl, quinolinyl, benzoimidazolyl, benzthiazolyl, purinyl, cinnolinyl and pterdinyl. Particularly preferred heteroaryl groups include monocylic heteroaryl groups. The term heterocycloalkyl is interpreted accordingly.
[0089] Embodiments of formula (I) that may be mentioned herein include those in which: [0090] (a) R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 may each independently represent, at each occurrence thereof, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, aralkyl, NR.sub.14R.sub.15, C(O)NR.sub.16R.sub.17, NR.sub.18C(O)R.sub.19, C(O)OR.sub.20, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, CN, alkyl, alkenyl, alkynyl (which latter three groups are unsubstituted or substituted by one or more substituents selected from OH, SH, C(O)OR.sub.22, or NR.sub.23R.sub.24), or, when present, any two instances of R.sub.1 to R.sub.3, R.sub.1, R.sub.2, R.sub.1, R.sub.2, R.sub.6 and R.sub.13 together with the carbon atoms to which they are attached from a 5-7 membered cycloalkyl ring system, a 5-6 membered heterocycloalkyl ring system, a 6 membered aryl ring or a 5-6 membered heteroaryl ring system. More particularly R.sub.1, R.sub.2, R.sub.1, and R.sub.2 may each independently represent, at each occurrence thereof, alkyl, cycloalkyl, aryl, heteroaryl, NR.sub.14R.sub.15, OR.sub.21, C(O)OH, OH, halo, NO.sub.2, or CN, optionally wherein R.sub.1, R.sub.2, R.sub.1, and R.sub.2, each independently represent, at each occurrence thereof, alkyl, halo, NO.sub.2, or CN (e.g. alkyl or halo); [0091] (b) R.sub.4, R.sub.5 and R.sub.7 to R.sub.12 each independently represent, at each occurrence thereof, H or alkyl; [0092] (c) R.sub.14 to R.sub.26 each independently represents alkyl; [0093] (d) a and a are 1, and b and b are 0, optionally wherein R.sub.1 and R, are independently alkyl or halo.
[0094] It will be appreciated that any of (a) to (d) may be used to replace the values provided above for formula (I), whether singly or in any technically sensible combination.
[0095] The complexes of formula (I) disclosed herein may display a number of stable conductive states. In addition, it is possible to use the ligands and metals described herein to provide resistive memory devices with a desired number of conductive states for a particular task. For example, if a bi-stable device is required (i.e. two stable conduction states for each polarity), then a ligand of formula (III) may be suitable for use in the desired devices. On the other hand, where three stable conduction states for each polarity are required, then the use of ligand (II) may be suitable. As such, ligands can be chosen to meet the required properties of the desired device.
[0096] In particular embodiments of the invention, L is selected from a ligand of formula (II) or formula (III):
##STR00005##
wherein R.sub.1 and R.sub.1 are selected from H, alkyl or halo. For example, L may be selected from the group consisting of:
##STR00006##
[0097] As will be appreciated, the anionic group A.sup.y may be selected from any anionic group that can act as a suitable stoichiometric counterion for the metal-ligand cation (i.e. the number of anionic groups provided matches the cationic charge of the metal-ligand cation). Examples of suitable A.sup.y groups include, but are not limited to BF.sub.4.sup., ClO.sub.4.sup., PF.sub.6.sup., CF.sub.3SO.sub.3.sup., BPh.sub.4.sup., Cl.sup., Br.sup., and F.sup.. More particular anions that may be selected include as the A.sup.y group are BF.sub.4.sup., PF.sub.6.sup. and Cl.sup. (e.g. PF.sub.6.sup.).
[0098] It is noted that the selected counterion is important in enabling the resulting devices to display hysteresis. Without wishing to be bound by theory, it is believed that the counterions can reside in several pockets around the metal-ligand cation and an applied electric field in the device can displace the anions from one pocket to another, travelling sub-nm distances. Given this, it is believed that when an electric field on the order of 100 MV/m is applied across a film of a compound of formula (I) in a device described herein below, the relative position of counterions with respect to the molecule is likely to change due to field-assisted reorientation. To move the counterions back to their original position, an electric field of opposite polarity would be required, resulting in J(V) hysteresis as displayed in the examples below. This suggests that one would expect to observe a steric effect of the counterions on the current hysteresis, which was verified by the preparation of devices using the counterions BF.sub.4.sup. (vdW-volume=187.7 .sup.3), PF.sub.6.sup. (vdW-1 volume=690.3 .sup.3) and Cl.sup. (vdW-volume=22.4 .sup.3) with the materials of Device A described in Example 4 below. Devices using BPh.sub.4.sup. as the counterion show a much less robust on-state when compared to PF.sub.6.sup., while Cl.sup. devices show slightly increased 2 hysteresis (results not shown). A similar result was obtained when the same counterions were used with the materials of Device B in Example 4 below. As such, larger switching voltages are needed when bulkier counterions are used. Thus selection of the counterion may be used to affect the properties of the resulting device, which may be accomplished through routine trial and error based on the results provided herein.
[0099] As noted above, various metals may be used in the complex of formula (I). It is expected that the use of different metals will provide the same basic functionality as that of Ru (which is used in embodiments of the invention below). Particular metals that may be mentioned in particular embodiments include Ru, Fe, Co, Ni, and Os.
[0100] As noted hereinbefore, the compound of formula (I) is particularly useful for providing a resistive memory device with improved properties as compared to metal-organic devices and provides advantages over fully inorganic systems (e.g. metal-oxide systems). Thus there is provided a resistive memory device comprising:
[0101] a substrate material having a surface; and
[0102] a compound of formula (I) as described above coated onto at least a portion of the surface of the substrate material in the form of a film having a first surface and a second surface.
[0103] It will also be understood that when a layer or element is referred to as being on another layer or substrate, it can be directly on the other layer or substrate, or intervening layers may also be present. Further, it will be understood that when a layer is referred to as being under another layer, it can be directly under, and one or more intervening layers may also be present. In addition, it will also be understood that when a layer is referred to as being between two layers, it can be the only layer between the two layers, or one or more intervening layers may also be present.
[0104] About, approximately, or substantially, as used herein is inclusive of the stated value and means within an acceptable range of deviation for the particular value as determined by one of ordinary skill in the art, considering the measurement in question and the error associated with measurement of the particular quantity (i.e., the limitations of the measurement system). For example, About, approximately, or substantially, may mean within one or more standard deviations, or within 30%, 20%, 10%, 5% of the stated value.
[0105] In order for the device to fully function, the device will also include a pair of electrodes. Thus, a first electrode may be sandwiched between the surface of the substrate and the first surface of the film of the compound of formula (I), and a second electrode may be in direct contact with the second surface of the film of the compound of formula (I). The material for the electrodes is not particularly limited and any suitable material may be used. Examples of suitable materials for the first electrode include, but are not limited to gold and, more particularly, ITO (indium tin oxide). Examples of suitable materials for the second electrode include ITO and, more particularly, gold. Such a device 100 is depicted in
[0106] The deposition of the electrodes may use any conventional technique that is known. The deposition of the molecular film may use any suitable technique. For example, the film may be laid using off-centered spin-coating onto the bottom or top electrode.
[0107] In certain embodiments, the inclusion of a layer of metal nanoparticles (e.g. gold, silver etc) at the interface between the first electrode and the first surface of the film formed from the material of formula (I). Such a device is shown in
[0108] The molecular film deposited on the substrate/electrodes may have any suitable thickness. For example, the thickness of the film may be from 10 to 100 nm, such as from 30 to 80 nm, such as from 30 to 50 nm or from 50 to 70 nm. Unless otherwise stated herein, all end points of related ranges may be combined to form new ranges, which are also explicitly disclosed (e.g. in the above example the ranges 30 to 100 and 50 to 80 nm are also disclosed).
[0109] Any suitable material may be used as the substrate. Examples of suitable substrates include, but are not limited to suitable ceramic materials and the like (e.g. Yttria-stabilized zirconia (YSZ)).
[0110] The devices obtained by the currently claimed invention may have any suitable size. For example, the size of the devices may range from 11 m to 100100 m and anything in between (e.g. 1100 m etc).
[0111] As will be noted, the current logic circuit and memory technology industry are looking for new devices with multiple states by which the storage density and computing power can be enhanced many-fold. The compounds disclosed herein can be easily turned into films and formed into suitable memory resistive devices, while also solving a number of issues normally associated with organic-metal devices, such as the ability to monitor the change in conductive states in situ, thereby allowing fine-tuning of the compounds/devices.
[0112] The devices described herein may also have the following advantages. [0113] 1. After optimization of the device fabrication process for each device (e.g. epitaxial ITO, shadow masking, low T evaporation of top electrode for the devices in the examples) it is possible to achieved a high yield and a high level of reproducibility. To make this point clear, more than 600 working devices have been fabricated. Yield and reproducibility are well known problems for organic devices and often go unresolved, but this is not the case for the devices disclosed herein. [0114] 2. In terms of stability, the disclosed devices outperform any other reported organic device significantly even at an elevated temperature of 350 K and in severe conditions of constant read-out. So far, the reported stabilities are only limited by measurement duration. Whereas other molecular-film devices show retention in the range of a few hours, the devices disclosed herein have demonstrated retention times of 60 days. This brings an improvement of almost 2 orders. [0115] 3. While other (metal)organic devices are either not rewritable: Write Once Read Many times memory (e.g. see Journal of the American Chemical Society 137, 4654-4657 (2015), Hong, E. Y.-H., et al. Journal of the American Chemical Society (2016), Gu, Q. F. et al. Adv Mater 27, 5968-5973, doi:10.1002/adma.201502274 (2015), and Adv Mater 24, 6210-6215, doi:10.100.sup.2/.sub.adma.201202319 (2012)). (WORM), or shows endurance values <10.sup.3 cycles, the devices disclosed herein have achieved an endurance of up to 10.sup.12 read-write cycles. This performance is comparable to the best values in oxide systems as reported by Lee et. al. (Nature materials 10, 625-630 (2011)). [0116] 4. The on/off value between any two states in the devices disclosed herein >10.sup.4 which is almost 4 orders of magnitude higher than the spread in the on and off state current values (see examples below). This ensures a low bit error rate. [0117] 5. With electrodes produced by shadow-masking, it was possible to scale down the devices to 1 m.sup.2. The uniformity of surface switching shown by the c-AFM scan
[0119] The devices disclosed herein may be used in as logic circuit elements, memory devices (especially in flexible portable devices) and in neuromorphic computing applications.
EXAMPLES
General Methods
[0120] NMR, ESI-MS Spectroscopy and Elemental Analysis: NMR spectra were obtained using a Bruker Avance 500 MHz spectrometer. A Perkin-Elmer 240C elemental analyzer was used to collect microanalytical data (C, H, N). ESI mass spectra were recorded on a Micromass Q-TOF mass spectrometer (Model No. YA263).
Spectroscopic Characterization
[0121] The films were characterized with a number of spectral techniques to gain structural information, as well as data on the vibrational and electronic states of the film molecules.
[0122] Rutherford Backscattering Spectroscopy of the film (RBS): Rutherford backscattering spectroscopy was used to measure the ruthenium areal density. A silicon surface barrier detector (energy resolution of 15 keV was used in a 160 degree scattering angle geometry to collect the RBS spectra by probing with 2 MeV He.sup.+ ions. Beryllium was chosen as the substrate to quantify the lighter elements in the molecule. The SIMNRA (Mayer, M. in The fifteenth international conference on the application of accelerators in research and industry. 541-544 (AIP Publishing)) software was used to fit the experimental data. The ruthenium areal density was found to be 310.sup.14 atoms/cm.sup.2 for a film thickness of 80 nm, resulting in a volumetric density of ruthenium (and hence the molecule) of 3.7510.sup.19 cm.sup.3. Notably, the molecular stoichiometry is not retained in the RBS data since elements of low atomic weight are likely to escape due to high energy ion radiation (Maye, L. C. F. a. J. W. Fundamentals of Surface and Thin Film Analysis (North-Holland, New York, 1986).). For this film, Ru is the heaviest element and since it is too heavy to be evaporated via irradiation, the ruthenium count is taken as a reliable measure of the molecular density (each molecule contains one Ru-atom so the Ru-count represents the molecular density).
[0123] J(V) measurements: The devices were characterised using a standard Keithley and Agilent Measurement Systems. The characterisations were performed in probe stations and a Physical Property Measurement System (PPMS, Quantum Design). The measurement performed in air and in vacuum shows almost similar characteristics eliminating any possibility of effect of moisture in the device response.
[0124] ITO/film/ITO devices displayed very similar J(V) values to ITO/film/Au devices. Notably, even in the ITO/film/ITO configuration, the bottom electrode-film interface was different from the film-top electrode interface owing to the preparation methods of the two electrodes. The fact that the work function of the top electrode does not change the J(V) excludes a Schottky barrier.
[0125] Devices without a bonding pad for the top electrode were measured with a micro-manipulated probe station where the contact between the spring-loaded probes and the electrode is controlled by an automated sensor ensuring minimum mechanical damage to the devices.
[0126] In-situ Raman Spectroscopy: A JY Horiba LabRAM Evolution Raman spectrometer with an air cooled CCD detector was used for all measurements. A Lexel SHG 95 Argon Ion laser was used for the excitation. Excitation wavelengths of 514.5 nm, 488 nm and 633 nm were used to identify the Raman modes. However, for all voltage-resolved measurements we used the 514.5 nm laser excitation. The measurements were performed in reflection geometry. Since we needed to probe the signal from the film, we used transparent ITO as the top electrode while the rest of the device geometry was the same as described in
[0127] For low temperature measurements an Advanced Research Systems Inc. compressed helium-based closed cycle refrigerator was used, coupled to the above spectrometer.
[0128] In-situ UV-Visible-NIR Spectroscopy: We used a Shimadzu (Japan) Solidspec-3700 spectrophotometer for this in-situ measurement. The device structure was ITO/film/ITO/YSZ. We measured the spectra in transmission mode where the sample was mounted between the lamp and the detector as shown in
[0129] Computational Methods: Density functional theory (DFT) calculations were performed using the hybrid B3LYP (Becke, A. D. Density-functional exchange-energy approximation with correct asymptotic behavior. Physical review A 38, 3098 (1988)) exchange-correlation functional and def2svp (Weigend, F. & Ahlrichs, R. Balanced basis sets of split valence, triple zeta valence and quadruple zeta valence quality for H to Rn: design and assessment of accuracy. Physical Chemistry Chemical Physics 7, 3297-3305 (2005)) basis set with unrestricted Kohn-Sham wave functions as implemented in Gaussian 09 package (Frisch, M. J. et al. Gaussian 09, revision A. 1. Gaussian Inc., Wallingford, Conn. (2009)).
[0130] Calculated vibrational frequencies were scaled by 0.96, a scaling factor for the B3LYP functional with this basis set as calculated by the Computational Chemistry Comparison and Benchmark Database. Ab initio calculations of vibrational frequencies need to be scaled to match experimental frequencies to accommodate for two factors, the fact that the electronic structure calculation is approximate (no full configuration interaction, no relativity, etc.) and because the potential energy surface is assumed to be harmonic. Since the calculated frequencies stem from the second derivative of the potential energy surface, treating the PES 1 as harmonic rather than a Morse potential results in energy level spacing which are further apart than in reality.
[0131] Atomic Force Microscopy (including c-AFM) measurement: A JEOL JSPM 5200 AFM set up was used for all measurements. A CSC17/Ti-Pt tip (tip radius of curvature <30 nm, tip height: 20-25 m, tip cone angle <30, resonant 1 frequency 12 kHz, Force constant 0.15 N/m) was used for conducting-AFM characterisation. The c-AFM measurements were performed in contact mode in vacuum (at a pressure of 10.sup.5 mbar). The cantilever probe was approached to the sample with a set point voltage, +2 V. J(V) measurements were performed in contact mode and the resultant current was measured using a pre-amplifier which can detect currents up to 5 A with a 10 fA detection sensitivity. After each set of measurements, the first measurement was repeated to ensure retention of tip quality.
[0132] Estimation of contact area between the tip and the sample:
[0133] The area of contact between an AFM tip and a sample can be estimated from several models among which Johnson, Kendall and Roberts (JKR) and the Derjaguin-Muller-Toporov (DMT) model can be taken as the respective upper and lower limits as indicated in the literature.
JKR Model
[0134] According to JKR model, the relationship between the radius of contact (a) and the load force (F) is given by the Hertz equation,
[0135] In order to calculate the radius of contact a, we need to estimate [0136] 1. The load forceF.sub.l [0137] 2. Work of adhesion W.sub.2 between the tip and the surface [0138] 3. The effective elastic modulus between the probe tip and the sampleE.sub.eff [0139] 4. Radius of the probe tipR (<35 nm from tip data sheet)
1. Load ForceF.SUB.l
[0140] We estimate the load force from the set point value (+2V) used during our measurement:
F.sub.l=kS(2)
where k is the spring constant of the cantilever (=0.18 N/m), S is the deflection sensitivity of the 5 cantilever and 5 is the cantilever deflection (=2V).
[0141] The deflection sensitivity (S=62.5 nm/V) is extracted from the slope of the linear portion of the attract part of the force curve obtained on a hard substrate viz. SrTiO.sub.3 (STO) as shown in
2. Work of adhesion W.SUB.12
[0142] JKR model for pull-off force is expressed as
F.sub.pull-off=cRW.sub.12(3)
[0143] Where c is 1.5 for JKR model, R is the radius of the probe tip and W.sub.12 is the work of adhesion F.sub.pull-off is estimated using Eqn. 2 with same values of k and S used to estimate the load force (F) 15 value. The =1.5V is estimated from the F-d curve measured on the film surface of Device A (
[0144] By substituting the values of c, R and F.sub.pull-off in Eqn. 3, W.sub.12=0.1023 N/m
3. The Effective Elastic Modulus Between the Probe Tip and the SampleE.SUB.eff
[0145] E.sub.eff is calculated from the effective elastic modulus between two contacting bodies as shown in Eqn. 4.
.sub.tip, .sub.sample, E.sub.tip and E.sub.sample are the Poisson's ratios and Young's moduli of the probe tip and sample, respectively. Substituting the values of Poisson's ratio and Young's modulus of the SiN tip (E.sub.tip=166 GPa, .sub.tip=0.23) and sample (E.sub.sample=25 GPa, .sub.sample=0.4), we obtain, E.sub.eff=34.039 GPa. We substituted these values in JKR model as shown in Eqn. 1 to get a=4.41 nm. Therefore, the contact area a.sup.2=60 nm.sup.2
DMT Model
[0146] The expression for pull-off force as in Eqn. 3 is valid for the DMT model as well. The DMT model is an alternative model for contact mechanics and the contact profile is similar to the Hertzian contact but it takes in to account additional attractive interactions outside the contact. The area of contact by DMT model is given by,
[0147] By substituting the values in Eqn. 5, we get a=3.32 nm and contact area=34.66 nm.sup.2 Although DMT predicts a lower value for the contact area, as a conservative choice we assume an area of 60 nm.sup.2.
[0148] We would like to highlight that as claimed in several reports.sup.6 the electrical area of contact is estimated to be 10% of the physical contact. However, still to be on the conservative side, we have used the area of 60 nm.sup.2 for the estimation of the current densities.
Precautions and Control Experiments
[0149] Notably, as further precautions, [0150] a. We measured the film topography before and after the I(V) measurements as presented in
[0152] Energy Calculation in a c-AFM device: We calculated the switching energy using E.sub.s=I.sub.sV.sub.st.sub.s where I.sub.s=on state current at switching voltage, V.sub.s=switching voltage and t.sub.s=switching time (we have taken 30 ns which is the fastest we could demonstrate). For a 60 nm.sup.2 device, I.sub.s=510.sup.7 A, V.sub.s=0.1V, t.sub.s=30 ns. Hence E.sub.s=(510.sup.70.13010.sup.9)=1.510.sup.15 J=1.5 fJ.
Device Yield Calculation
[0153] The device-yield reported here represents the number of successful devices obtained amongst those measured. However, the devices measured underwent a pre-screening process:
[0154] It is well-known that in spin coating process, the film near the substrate edge becomes non uniform. This is particularly true for substrates of 1 cm1 cm. Hence, it is a common practice to exclude those parts during device fabrication (Franssila, S. Introduction to microfabrication. (John Wiley & Sons, 2010)). As such, devices within about a 200-micron perimeter of the edges of the film were excluded.
[0155] For the devices obtained in the resulting central zone, an optical screening was conducted and the following devices were excluded: [0156] (a) where the top Au-electrode partially peeled off [0157] (b) where the shape of Au-electrode was not well defined and deviated from dimensions of the shadow mask.
[0158] The above pre-screening steps excluded about 5% of the devices. Thus, only those devices that passed the above steps were analyzed further.
[0159] Among the measured devices, the most common failure mode observed was that some devices were found to be shorted between top and bottom electrodes (approx. 80% of failure among measured devices); and the remaining devices did not show hysteretic IV characteristics and therefore no memory response (approx. 20% of failures).
Preparation of Ligands
[0160] 2-(Phenylazo)pyridine (L.sup.1) and 2,6-bis(phenylazo)pyridine (L.sup.2) were synthesized as reported in Campbell, N., Henderson, A. W. & Taylor, D. Journal of the Chemical Society (Resumed), 1281-1285 (1953) and Ghosh, P.; Samanta, S.; Roy, S. K.; Demeshko, S.; Meyer, F.; Goswami, S. Inorg. Chem., 53, 4678-4686 (2014).
General Preparation 1
Preparation of Devices
[0161] Indium tin oxide (ITO) grown on annealed yttria-stabilized zirconia (YSZ) was used as the bottom electrode for all the devices. Freshly grown ITO electrodes were used for device preparation, which ensures a much better surface coverage and reproducibility. Treatment of the electrode with oxygen plasma just before film preparation was also found to be favourable to device performance.
[0162] When included, gold nanoparticles (NPs) on the bottom electrode were obtained by annealing ultrathin Au-film sputtered on ITO substrate following the well-established methods (e.g. see Lin J. C., et al., Advanced Materials 2016, 28(4): 764-770). The solution of precursor molecules (i.e. the complexes of Examples 1 and 2) in acetonitrile were deposited on ITO by off-centered spin coating (OCSC) (Yuan, Y. et al. Nature communications 5, 3005 (2014)). The solution concentration and substrate position in the spin coater with respect to the center and the rotor speed can both be varied to get various film thicknesses. After deposition, the samples were stored in a vacuum chamber with a pressure of 10.sup.8 Torr for 12 hours. Subsequently, the Au/ITO electrode was deposited using shadow masks of various sizes. Au top electrodes were fabricated using electron beam evaporation. ITO top electrodes were deposited by the pulsed laser deposition (PLD) technique.
[0163] For devices for in situ characterization, amorphous ITO was used as the top electrode. A gold pad was used at the corner of the ITO for making contacts on the top electrode via the standard wire bonding method.
Example 1
Synthesis of mer-[Ru(L.SUP.1.).SUB.3.](PF.SUB.6.).SUB.2
[0164] The precursor complex [Ru(L.sup.1).sub.2(OH2).sub.2](ClO.sub.4).sub.2.H.sub.2O was synthesized as previously reported (Goswami, S.; Chakravarty, A. R.; Chakravorty, Inorg. Chem. 22, 602-609 (1983)).
[0165] In a round bottom flask equipped with a condenser, 100 mg (0.55 mmol) of L.sup.1, dissolved in 5 mL methanol, was added to a methanolic solution (20 mL) of 360 mg (0.50 mmol) [Ru(L.sup.1).sub.2(OH.sub.2).sub.2](ClO.sub.4).sub.2.H20. The mixture was then refluxed for 3 h. The blue-violet solution gradually turned orange and the resultant solution was then evaporated to dryness and washed thoroughly with hexane. The product thus obtained was dissolved in 5 mL of methanol and to it a saturated aqueous solution of NH.sub.4PF.sub.6 (1 mL) was added. The mixture was kept in a refrigerator for 1 h and the brown precipitate was collected by filtration and washed thoroughly with water. The product was finally crystallized by slow diffusion of its acetonitrile solution into toluene. Yield: 385 mg (82%).
[0166] The calculated elemental analysis percentages for C.sub.33H.sub.27F.sub.12N.sub.9P.sub.2Ru were C, 42.14; H, 2.89; N, 13.40 while the experimentally measured numbers were C, 42.28; H, 2.93; N, 13.32.
Example 2
Synthesis of [Ru(L.SUP.2.).SUB.2.](PF.SUB.6.).SUB.2
[0167] The complex [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 was synthesized from Ru(L.sup.2)(CH.sub.3CN)Cl.sub.2 via a three-step synthetic protocol.
[0168] In the first step an intermediate complex, [Ru(L.sup.2)Cl.sub.2(CH.sub.3CN)] was synthesized from the reaction between hydrated RuCl.sub.3 and L.sup.2. Its crystallization from CH.sub.3CN produced a dark crystalline compound. Substitution of 2Cl.sup. and CH.sub.3CN by L.sup.2 produced the monocationic complex, [Ru{(L.sup.2).sup.(.sup.)}(L.sup.2)]PF.sub.6 {(L.sup.2).sup.(
.sup.)=one electron reduced form of L.sup.2}. Chemical oxidation of [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 by Br.sub.2 in the presence of NH.sub.4PF.sub.6 produced the desired compound, [Ru(L.sup.2).sub.2](PF.sub.6).sub.2. The molecular structures of the Ru-complexes isolated in two redox states: di-cationic [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 with two counter-anions and mono-cationic [RuL.sup.2.sup.(
.sup.)L.sup.2]PF.sub.6 with one anion were deposited with the Cambridge Crystallographic Data Centre (CCDC deposition codes 1839995 and 1840074). Synthetic details of each step are elaborated below.
[0169] (i) Synthesis of [Ru(L.sup.2)Cl.sub.2(CH.sub.3CN)]: In a round bottom flask equipped with a condenser, a mixture of 170 mg (0.59 mmol) of L.sup.2 and 150 mg (0.57 mmol) RuCl.sub.3.3H.sub.2O in 20 mL ethanol was refluxed for 3 h. During this time the color of the reaction mixture slowly changed from red to green. The crude mass, obtained by the evaporation of the above solution, was washed thoroughly with hexane to remove unreacted L.sup.2. Finally, the product was crystallized by the slow evaporation of its acetonitrile solution. Yield: 215 mg (75%).
[0170] ESI-MS (m/z): 459.85 amu [C.sub.17H.sub.14Cl.sub.2N.sub.5Ru].sup.+ (z=1) i.e. ([RuLCl.sub.2(CH.sub.3CN)](CH.sub.3CN)+H).sup.+. The calculated elemental analysis percentages for C.sub.19H.sub.17Cl.sub.2N.sub.6Ru were C, 45.61; H, 3.22; N, 16.80, while the experimentally measured numbers were C, 45.78; H, 3.34; N, 16.71. .sup.1H NMR (400 MHz, CDCl.sub.3) 8.59 (d, J=8Hz, 2H), 8.30 (d, J=8Hz, 4H), 8.08 (t, J=8Hz, 1H), 7.60 (t, J=7Hz, 2H), 7.52 (t, J=8Hz, 4H), 2.70 (s, 3H).
[0171] (ii) Synthesis of [Ru{(L.sup.2).sup.(.sup.)}(L.sup.2)]PF.sub.6 from [Ru(L.sup.2)Cl.sub.2(CH.sub.3CN)]: A mixture of 100 mg (0.20 mmol) of [Ru(L.sup.2)Cl.sub.2(CH.sub.3CN)] and 87 mg (0.42 mmol) of AgClO.sub.4 in 20 mL methanol was refluxed for 2 h. The color of the solution turned light brown and a white precipitate of AgCl appeared. The reaction mixture was then allowed to cool to room temperature and filtered through a G4 sintered-glass funnel to remove the precipitate. To the filtrate, 60 mg (0.21 mmol) of L.sup.2 was added and the mixture was refluxed for 3 h. The resulting dark brown solution was subsequently concentrated to 5 mL. To the above solution, 1 mL of saturated aqueous solution of NH.sub.4PF.sub.6 was added. The mixture was then kept in a refrigerator for 1 h. The resulting precipitate was filtered and washed thoroughly with water to remove excess NH.sub.4PF.sub.6 and dried in vacuum. The crude product was then purified on a preparative silica gel TLC plate using 1:10 acetonitrile-dichloromethane mixture as the eluent; a dark brown band was collected. The collected solution was evaporated to dryness and the product, was crystallized by slow diffusion of its dichloromethane solution into hexane. Yield: 102 mg (62%).
[0172] ESI-MS (m/z): 676.40 amu [C.sub.34H.sub.26N.sub.10Ru].sup.+ (z=1) i.e. ([RuL.sup.()L]PF.sub.6PF.sub.6).sup.+. The calculated elemental analysis percentages for C.sub.34H.sub.26F.sub.6N.sub.10PRu were C, 49.76; H, 3.19; N, 17.07 while the experimentally measured numbers were C, 49.69; H, 3.16; N, 16.94. This compound is paramagnetic with .sub.eff=1.81 BM, it displayed a nearly isotropic EPR signal at g=1.965 (298K).
[0173] (iii) Synthesis of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 from [Ru{(L.sup.2).sup.(.sup.)}(L.sup.2)]PF.sub.6: To a stirring acetonitrile solution of 100 mg (0.12 mmol) of the complex [Ru{(L.sup.2).sup.()}(L.sup.2)]PF.sub.6, excess Br.sub.2 (0.25 mL in 5 mL of acetonitrile) was added drop-wise over a period of 5 min. The mixture was then allowed to stir for 30 min in a fume hood. It was then evaporated and the resultant mass was washed thoroughly with hexane. The product, thus obtained, was dissolved in 5 mL of methanol and to it a saturated aqueous solution of NH.sub.4PF.sub.6 (1 mL) was added. The mixture was then kept in a refrigerator for 1 h, during which dark crystalline precipitate deposited. The precipitate was collected by filtration and washed thoroughly with water. The product was finally crystallized by slow diffusion of its acetonitrile solution into toluene. Yield: 95 mg (83%).
[0174] ESI-MS (m/z): 338.18 amu [C.sub.34H.sub.26N.sub.10Ru].sup.2+ (z=2) i.e. ([Ru(L.sup.2).sub.2](PF.sub.6).sub.22(PF.sub.6)).sup.2+. The calculated elemental analysis percentages for C.sub.34H.sub.26F.sub.12N.sub.10P.sub.2Ru were C, 42.29; H, 2.71; N, 14.51 while the experimentally measured numbers were C, 42.48; H, 2.74; N, 14.39, on an initial batch of materials. The experimentally measured numbers on a subsequent batch of materials made using the protocol above were C, 42.37; H, 2.69; N, 14.54. .sup.1H NMR (CD.sub.3CN, 500 MHz): 8.97 (d, J=8Hz, 1H), 8.60 (t, J=8Hz, 1H), 7.97 (d, J=8Hz, 1 H), 7.85 (d, J=8 Hz, 2H), 7.78-7.71 (m, 3H), 7.45 (t, J=8Hz, 1 H), 7.27 (t, J=8Hz, 2H), 7.13 (d, J=8 Hz, 2H).
Example 3
Electrochemical Characterization of the Compounds of Example 1 and 2
[0175] Cyclic voltammetric experiments of the two Ru complexes, mer-[Ru(L.sup.1).sub.3](PF.sub.6).sub.2 and [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 (2 mM) of Examples 1 and 2, respectively were carried out in a three-electrode cell where the working electrode was glassy carbon (area=3.14 mm.sup.2), the counter electrode was Pt-wire (area=220.69 mm.sup.2) and the reference electrode was Ag/AgNO.sub.3 (all reported potentials were referenced to the Ag/AgNO.sub.3 electrode). The electrodes were all dipped acetonitrile containing 0.1 M [Et.sub.4N]PF.sub.6, with the counter electrode separated from the main solution by a vycor glass frit. The electrochemical measurements were performed using a PC-controlled PAR model 273A electrochemistry system. The CV cell assembly was set up inside a glove box that has an O.sub.2 and moisture level of <1 ppm. The voltammetric data are provided in Table 1. The complexes displayed multiple waves as shown
TABLE-US-00001 TABLE 1 Compound Cyclic Voltammetry E.sub.1/2, V * mer-[Ru(L.sup.1).sub.3](PF.sub.6).sub.2 0.35, 0.66, 1.14, 1.42, 1.78, 2.09** [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 Optimized results: 0.40, 1.00, 1.53, 2.03** Initial results: 0.42, 1.025, 1.55, 1.76** * E.sub.1/2 = 0.5(E.sub.pa + E.sub.pc), where E.sub.pa and E.sub.pc are anodic and cathodic peak potentials, respectively, under a scan rate of 50 mV s.sup.1. **Quasi-reversible
Example 4
Preparation and Analysis of Devices A and B Using the Complex of Example 1
[0176] Using General Procedure 1, devices with a planar ITO bottom electrode were manufactured having an area of from 11 m (film thickness from 56-67 nm), 1010 m (film thickness from 54-69 nm), 2020 m (film thickness from 54-64 nm), 4040 m (film thickness from 53-64 nm), 6060 m (film thickness from 55-69 nm), 8080 m (film thickness from 56-62 nm) and 100100 m (film thickness from 58-67 nm) and are referred to herein as Device A.
[0177] Using General procedure 1, devices with Au-nanoparticle sputtered ITO bottom electrodes were manufactured having sizes of 11 m(film thickness from 34-42 nm), 22 m (film thickness from 37-46 nm) and 33 m (film thickness from 41-47 nm) and are herein referred to as Device B.
[0178] The devices were characterised using a Keithley source meter. The characterisations were performed in probe stations and a Physical property Measurement System (PPMS, Quantum Design). For devices to be used for in situ characterisation, we used amorphous ITO as the top electrode, deposited by the Pulsed Laser Deposition (PLD) technique. A gold pad was used at the corner of ITO for making contacts on the top electrode via the standard wire bonding method.
Device A Characterisation
Device Yield Calculation
[0179] A total of 350 Device A devices underwent electrical transport measurements, of which 91.7% were successful. Details of the device yield calculation mention are provided hereinabove.
AFM Image
[0180] An atomic force microscopy (AFM) image for Device A is shown in
On-off Switching of Device A
[0181]
[0182] As shown in
[0183] These devices, though robust and reproducible, suffer from high switching voltage values compared to the ITRS specifications for ReRAM devices. Additionally, the low current density values constrain their scaling to smaller dimensions. This led to the development of Device-B, discussed below.
TABLE-US-00002 TABLE 2 Device - A On-state Off-state Molecular current current film Switch-on Switch-off density @ density @ On-off Size # thickness voltage voltage V.sub.read = 2 V V.sub.read = 2 V ratio @ [m] devices [nm] [V] [V] [A/cm.sup.2] [A/cm.sup.2] 2 V 100 100 122 58-67 3.95 0.21 4.14 0.19 3.9 1.2 (6 1) 10.sup.4 (8.8 1) 10.sup.4 80 80 47 56-62 60 60 38 55-69 40 40 29 53-64 20 20 31 54-64 10 10 26 64-69 1 1 28 56-67
Device Statistics
[0184] With respect to device-to-device reproducibility, we analyzed the distribution of currents and switching voltages obtained by measuring 321 samples of device-A.
[0185] The (J(2)/Jmean) values for on and off states are about 31% and 16% for device-A (see
Endurance, Stability and Uniformity of Device A
[0186] The read-write sequences for device-A is shown in
[0187] The endurance of the device is demonstrated in
[0188] To estimate stability, two devices of type-A were placed into on and off states at time zero and current was sampled at 350K which is the typical semiconductor-device test temperature. During measurement, the read-out voltage (indicated in
[0189]
[0190] To confirm the uniformity of film conductance, we recorded spatial distribution maps of conductance with a c-AFM tip (see methods for tip details and
Raman and US-Vis-NIR Spectroscopy Analysis of Device A
[0191] To relate these transport phenomena to the geometric and electronic structure of the molecules, in operando Raman and UV-Vis-NIR spectroscopy for the thin film devices was performed (device configuration is ITO/film/ITO, details above in the Methods section). Further, we employed spectroelectrochemistry to record UV-Vis-NIR absorption spectra while simultaneously measuring cyclic voltammograms (CVs) of the molecules in 0.1M electrolyte solution.
[0192] The UV-Vis-NIR spectroelectrochemistry of the constituent [Ru(L.sup.1).sub.3].sup.2+ complexes in solution, during the first four redox events are shown in
[0193] This inference is further corroborated by Raman spectra of the film, measured as a function of applied voltage.
[0194] DFT calculations indicate that these modes correspond to the azo (NN) stretching mode for different redox states. The Raman peak at 1363 cm.sup.1 (E1) corresponds to the neutral azo-group. After single electron reduction it produces an azo-anion and the corresponding Raman peak shifts to 1313 cm.sup.1 (E2). The peak at 1275 cm.sup.1 (E3) corresponds to a doubly reduced hydrazido di-anion. The spectral weight of each peak is 1 a measure of the amount of a particular ligand redox state in the molecular thin film (details in Methods). Since the total number of molecules does not change, the summation of spectral weights of the three peaks is expected to be constant to first order.
[0195]
[0196] While this ligand redox state model explains the conductance jumps, it does not account for the memory effect or hysteresis and this is where the counter ions play a vital role.
[0197] DFT calculations show that different positions of counter-ions (PF.sub.6.sup.-) can significantly affect the molecular energy levels (300meV), as well as the dipole moment (18.8 to 22.4 D). When an electric field on the order of 1 GV/m is applied across the film, the relative position of counter ions with respect to the molecule will change due to field-assisted migration. To move the counter ions back to their original position, an electric field of opposite polarity would be required. Hence, the redox state transitions might not follow a reversible path in forward and reverse voltage sweep and instead exhibit hysteresis. To verify the effect of counter ions on the current response we prepared additional devices with counter ions of various van der Waals (vdW)-volumes since migration rates decrease with increasing vdW radii30. While BPh.sub.4.sup. (vdW-volume=187.7 .sup.3) devices show a much less robust on-state with 26% hysteresis area compared to the PF.sub.6.sup. (vdW13 volume=690.3 .sup.3) devices, those with Cl.sup. (vdW-volume=22.4 3) show 3% increased area (
RBS Spectra
[0198] An RBS spectrum of the [Ru(L.sup.1).sub.3](PF.sub.6).sub.2 film in device A is provided in
Device B Characterisation
[0199] Device B where Au nanoparticles (NPs) are sputtered at the ITO-organic layer interface. NPs are used for interface engineering to reduce the charge injection barrier (and/or the potential drop at the interface) via several mechanisms including local electric field enhancement, provision of mid-gap states, charge trapping and domain de-pinning (e.g. ferroelectrics).
AFM Image
[0200] The atomic force microscopy (AFM) image of the type-B device is shown in
On-Off Switching of Device B
[0201]
[0202] To address the issues noted above for Device-A, we use a modified device structure (device-B) with nanoparticles (NPs) sputtered at the ITO/film interface. The presence of NPs in device-B improves the following two device characteristics substantially: the switching bias window reduces by 90% enabling switching on and off at (51930)mV and (54737)mV respectively, and the current densities increase 4 orders of magnitude compared to device-A. To demonstrate scalability of device-B, we created a nano-scale test-device using a conductive-AFM (c-AFM) tip as the top electrode and a NP on ITO as bottom electrode, as described above. The contact area to the c-AFM-tip is estimated to be 60 nm.sup.2. The I(V) (and J(V)) characteristics of this device are shown in
TABLE-US-00003 TABLE 3 Device - B On-state Off-state Molecular current current film Switch-on Switch-off density @ density @ On-off Size # thickness voltage voltage V.sub.read = 0.3 V V.sub.read = 0.3 V ratio @ [m] devices [nm] [V] [V] [A/cm2] [A/cm.sup.2] 2 V 3 3 34 41-47 0.52 0.03 0.55 0.04 (11 4) 10.sup.2 (1 0.6) 10.sup.2 (1.2 5) 10.sup.5 2 2 20 37-46 1 1 6 34-42
Device Statistics
[0203] With respect to device-to-device reproducibility, we analyzed the distribution of currents and switching voltages obtained by measuring 50 samples of device-B (10 measurements per sample) and 50 measurements on 5 distinct locations with the c-AFM top electrode on the nanoparticles.
[0204] The (J(2)/Jmean) values for on and off states are about around 46% and 50% for device B (see
Device Performance
[0205] The read-write sequences for device-B is shown in
[0206] The endurance (cycles) of device-B is demonstrated in
[0207] To estimate stability, two devices of type-B was placed into on and off states at time zero and current was sampled at 350K which is the test temperature for typical semiconductor-devices. During measurement, the read-out voltage (indicated in
Raman and US-Vis-NIR Spectroscopy Analysis of Device B
[0208]
Example 5
Initial Studies Involving the Preparation and Analysis of the Multistate Device Prepared Using the [Ru(L.SUP.2.).SUB.2.](PF.SUB.6.).SUB.2 .Complex of Example 2
[0209] In these initial studies, the multistate device was made using the same method used in Example 4, but using the complex of Example 2 instead of Example 1. Both the planar and the gold nanoparticles devices were manufactured, but only the planar devices are discussed in this example.
[0210] Based on our understanding of the crucial role of the oxidation states of the azo (NN) functional groups with respect to the observed conductance states, we made devices of the same geometry but with complexes having four azo groups rather than three. We replaced the three bidendate ligands of [Ru(L.sup.1).sub.3] with two pincer-type ligands (L.sup.2=2,6-bis(phenylazo)pyridine), each with two conjugated azo groups, to obtain [Ru(L.sup.2).sub.2].sup.2+. The number of N=N bonds increases from three for [Ru(L.sup.1).sub.3].sup.2+ to four for ([Ru(L.sup.2).sub.2].sup.2+ (see
[0211] From the initial studies,
TABLE-US-00004 TABLE 4 Size [m.sup.2] # Devices Thickness range [nm] 100 100 117 ~60 80 80 39 ~60 60 60 34 ~60 40 40 29 ~60 20 20 31 ~60 10 10 22 ~60 1 1 23 ~60
Device Yield Calculation
[0212] A total of 350 multistate devices underwent electrical transport measurements, of which 84.2% were successful. Details of the device yield calculation mention are provided hereinabove.
Example 6
Optimized Studies Involving the Preparation, Characterizations and Performance of Devices Prepared Using the [Ru(L.SUP.2.).SUB.2.](PF.SUB.6.).SUB.2 .Complex of Example 2
[0213] In further optimized studies of the device of Example 5, planar and gold nanodiscs (Au NDs) [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 devices were prepared as equivalents to Devices A and B in Example 4, respectively. The devices were made using similar methods to those described in Example 4, but using the [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 complex of Example 2.
[0214] For the Au NDs device, gold nanodiscs were lithographically patterened on ITO, followed by spin coating of the film of ruthenium complexes. A c-AFM tip was used as a top electrode in this configuration. The ITO electrode was grounded during the measurement and the bias was applied on the tip, with the measurements performed in contact mode.
Characterization and Performance of Planar Device of [Ru(L.SUP.2.).SUB.2.](PF.SUB.6.).SUB.2
Film Characterization
[0215] The topography of the thin films of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2on the substrate of the planar devices were characterized by AFM and are shown in
Device Characterization
[0216] .sup.)}(L.sup.2)]PF.sub.6. In both geometries, the devices fabricated using the mono-cationic complex [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 have two conductance plateaus (binary memory), but devices with di-cationic complex [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 display three plateau, exhibiting ternary memory. Therefore, the devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 can be referred to as ternary devices in this example.
[0217] In addition, the current density profile J(V) for the planar devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2, in
Device Performance
[0218] Despite being reproducible and thermally stable (up to 500 C. in vacuum, see
Device Statistics
[0219] A total of 295 different planar devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 was prepared in 20 different batches of preparation (
TABLE-US-00005 TABLE 5 Film Switch-on Switch-off Size # thickness voltage voltage Current density (A/cm.sup.2) V.sub.read = 2 V (m m) devices (nm) (V) (V) On Int1* Int2* Off Ratio 100 100 117 58 4 Sw 1: Sw 1: (6.6 0.5) 10.sup.1 (7.8 1.2) 10.sup.2 (8.8 0.7) 10.sup.3 (2.9 0.5) 10.sup.6 On/ 80 80 39 4.3 0.2 3.5 0.2 Int ~10.sup.3 60 60 34 Sw 2: Sw 2: Int1/ 40 40 29 6.2 0.2 5.1 0.2 Int2 ~10 20 20 31 Int2/ 10 10 22 Off ~10.sup.3 1 1 23 *Int-1 and -2 represent the positive and negative intermediate states respectively.
In Situ Raman and UV-Vis Spectroscopy
[0220] To correlate film conductance to molecular electronic states, in situ Raman and UV-Vis spectroscopy were carried out on planar devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2. It was observed that the results and mechanisms are similar in the planar and Au NDs devices. Major changes in voltage resolved Raman spectra were observed only during switching events in the modes at 1301 cm.sup.1 (E.sub.0), 1259 cm.sup.1 (E.sub.1), and at 1185 cm.sup.1 (E.sub.2) for the ternary device in the lowest conductance state. These modes (E.sub.0, E.sub.1 and E.sub.2) were assigned to azo NN stretching modes in different redox states.
[0221] The assignment of the Raman spectra to molecular redox-states is supported by comparison of voltage dependent UV-Vis and spectroelectrochemistry (
[0222] In the highest conductance state, only one dominant mode E.sub.0 was observed (
[0223] In contrast, at the lowest conductance (off) state of the ternary device, a third azo-mode E.sub.2 results in co-existence of three distinct redox states of the azo moiety whereas DFT predict that only two distinct azo-redox states are possible for a single molecule in any given redox state. The off-state UV-Vis spectrum also does not overlap with spectroelectrochemistry of any single redox state and the highly unusual non-monotonic dependence of E.sub.0-Raman mode on bias (
Charge Disproportionation (CD) at the Lowest Conductance (Off) State
[0224] It was proposed that the lowest conductance (off) state is formed via charge disproportionation (CD) resulting in pairs of singly- and triply-reduced molecules instead of all being doubly-reduced. The UV-Vis spectrum of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 in the off-state comprises of the solution-spectra of the singly- and triply-reduced molecules in 1:1 intensity ratio (
[0225] In addition, the off-state Raman spectra of the planar device (as shown in
[0226] Additionally, permittivity measurements were conducted, where the device capacitance was measured using a Keysight E4980A/AL Precision LCR Meter, with different applied DC bias voltage. For each value of DC-bias, an AC-voltage of 100 mV with frequencies ranging from 1 kHz to 1 MHz were used to measure the capacitance value of the film from which permittivity is calculated.
[0227] An abrupt doubling of dielectric constant during switch-off process in the ternary planar device was observed as shown in
Characterization and Performance of Au NDs device of [Ru(L.SUP.2.).SUB.2.](PF.SUB.6.).SUB.2
Film Characterization
[0228] The topography of the thin films of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 on the substrate of the Au NDs devices were characterized by AFM and are shown in
Device Characterization
[0229] .sup.)}(L.sup.2)]PF.sub.6. Similar to that of the planar device, the Au NDs device fabricated using the mono-cationic complex [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 have two conductance plateaus (binary memory), but the device with [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 displays three plateaus, exhibiting ternary memory. Therefore, the devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 can be referred to as ternary devices in this example.
[0230] Similarly, the current density profile J(V) for the Au NDs devices of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 (in
Device Performance
[0231] As mentioned above, voltages switching and current densities were optimized using the Au NDs devices. Local field enhancement at the nano-structures reduced the interfacial charge injection barrier, which lowered the switching voltages down to 151 and 215 mV and increased the current density by about four orders as compared to the planar devices. This gave reading current values of 5 A and 40 nA in the on and intermediate state respectively for the Au NDs devices (50 nm.sup.2 area,
[0232] The devices also endured 1010 pulses (four orders higher than flash memories, see Zhao, C. et al., Materials, 7, 5117-5145 (2014)) with 30 ns rise time (limited only by our measurement system, see
[0233] Further, pulse tests relating to the reading operations performed after 1 h, 2 h and 2 days after the writing operation showed retention of the current and voltage, therefore confirming the robustness of the conductance states (
In Situ Raman and UV-vis Spectroscopy
[0234] It was observed that the results and mechanisms for the Au NDs devices are similar to that of the planar devices (as discussed above).
Device Statistics
[0235] For the Au NDs device, multiple measurements were performed on 14 different nanodiscs in three different samples which were lithographically patterned in different batches (
TABLE-US-00006 TABLE 6 No. of Estimated Switch-on Switch-off measured Device Thickness voltage voltage Current density (A/cm.sup.2) V.sub.read = 75 mV points area (nm) (mV) (mV) On Int1* Int2* Off Ratio 14 50 nm.sup.2 42 4 151 6 135 6 (2.7 1.2) 10.sup.6 (3.1 0.7) 10.sup.3 (6.6 0.8) 10.sup.2 (7.1 1.2) 10.sup.1 On/ 215 7 186 5 Int ~10.sup.3 Int1/ Int2 ~5 Int2/ Off ~10.sup.3 *Int-1 and -2 represent the positive and negative intermediate states respectively.
Example 7
Characterizations and Performance of Devices Prepared Using the [Ru{(L.SUP.2.).SUP.(..SUP.).}(L.SUP.2.)]PF.SUB.6 .Complex of Example 2
[0236] The mono-cationic complex [Ru{(L.sup.2).sup.(.sup.)}(L.sup.2)]PF.sub.6 of Example 2 was also used to fabricate the planar and gold nanodiscs (Au NDs) devices as described in Example 6.
Device Characterization (for Both Planar and Au NDs Devices)
[0237] .sup.)}(L.sup.2)]PF.sub.6 complex, in comparison to that of the [Ru(L.sup.2).sub.2](PF.sub.6).sub.2. In both geometries, the devices fabricated using the mono-cationic complex [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 have two conductance plateaus (binary memory), therefore, such devices can be referred to as binary devices in this example.
[0238] The permittivity measurements were carried out as described in Example 6 and the relative permittivity and the current density of the film in the binary device were as shown in
In Situ Raman and UV-vis Spectroscopy
[0239] In situ Raman and UV-Vis spectroscopy were also carried out on the planar devices of [Ru{(L.sup.2).sup.(.sup.)}(L.sup.2)]PF.sub.6. Spectral signatures in the on- and off-states in the binary planar device of [Ru{(L.sup.2).sup.(
.sup.)}(L.sup.2)]PF.sub.6 are very similar to the on- and intermediate-states in the ternary planar device of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 (
[0240] Similar to the ternary planar device of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 in Example 6, in the highest conductance state, only one dominant mode E.sub.0 was observed (
[0241] The assignment of Raman spectra to molecular redox-states is also supported by comparison of voltage dependent UV-Vis and spectroelectrochemistry (
Example 8
Comparison of the Devices of the Current Invention With the Projected Values of the International Technology Roadmap for Semiconductors (ITRS, 2015)
[0242] The devices of the current invention were compared to the projected values by the International Technology Roadmap for Semiconductors (ITRS, 2015) for resistive random access memory (RRAM) devices. As shown in Table 7, the devices of current invention satisfy the parameters as set in the ITRS projections.
TABLE-US-00007 TABLE 7 ITRS Projection Achieved Values Achieved Values for (adopted from for Device-B the ternary Au NDs Table ERD 4b, (i.e. the NP device) device of [Ru(L.sup.2).sub.2](PF.sub.6).sub.2 Next best Parameter ITRS-2015) in example-2 in Example 6 Organic Device Read Current >10 nA/100 pA ~1 A 5 A (on), 200 fA at 400 nm.sup.2 (bipolar) 40 nA (intermediate), at 0.1 V W/E time ~ns <30 ns ~30 ns ms Write Cycles >10.sup.10 >10.sup.12 >10.sup.10 10.sup.4 Write Voltage <0.6 V 0.15 V 0.15 V, 0.22 V 1.5 V Read Voltage <0.2 V <0.05 V <0.1 V 0.1 V Write energy <1 pJ 450 aJ (area 50 nm.sup.2) 30 aJ, 30 fJ (area 50 nm.sup.2) Not reported Assuming 30 ns (switching time), 1 mA (switch-on current)