A-SITE HIGH-ENTROPY NANOMETER METAL OXIDE WITH HIGH CONDUCTIVITY, AND PREPARATION METHOD THEREOF

Abstract

The present disclosure relates to the field of new materials, and aims at providing an A-site high-entropy nanometer metal oxide with high conductivity, and a preparation method thereof. The metal oxide has molecular formula of Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 and is a powder, and has microstructure of the metal oxide as a square nanometer sheet with a side length of 4-12 nm and a thickness of 1-3 nm. Compared with an existing high-entropy oxide, the product in the present disclosure has high conductivity, and can be well applied to a conductive alloy, an electrical contact composite material, a conductive composite material, a multifunctional bio-based composite material, a conductive/antistatic composite coating and the like.

Claims

1. An A-site high-entropy nanometer metal oxide with high conductivity, wherein the metal oxide has a molecular formula of Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7; and is a powder, and has microstructure of a square nanometer sheet with a side length of 4-12 nm and a thickness of 1-3 nm.

Description

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0030] The present invention is described below in details in conjunction with the particular embodiments. The following embodiments facilitate those skilled in the art further understanding the present disclosure, but do not limit the present disclosure in any way. It should be noted that, for those skilled in the art, several alterations and modifications can be made without departing from the concept of the present invention, which fall within the protection scope of the present invention.

[0031] In the following embodiments, Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 are powder forms. Absolute ethyl alcohol, tetrahydrofuran, propyl alcohol, phenylenediamine, hydrogenated tallowamine, sorbitol and carbamyl ethyl acetate are commercial reagents.

Example 1

[0032] Provided is a preparation method for an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity, the method including the following steps.

[0033] (1) Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and

[0034] NH.sub.4VO.sub.3 were taken at a molar ratio of 0.4:0.3:0.4:0.5:0.4:0.7:0.8:0.5, added to a mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran at a mass ratio of 0.3:3:0.5, and stirred for five minutes to obtain a mixed liquid I. The ratio of the total mass of Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 to that of the mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran (0.3:3:0.5) is 12.6%.

[0035] (2) Para-phenylene diamine, hydrogenated tallowamine, sorbitol and carbamyl ethyl acetate at a mass ratio of 1:0.2:7:0.01 were taken, added to propyl alcohol, and stirred for one hour to obtain a mixed liquid II. The ratio of the total mass of the para-phenylene diamine, the hydrogenated tallowamine, the sorbitol and the carbamyl ethyl acetate to that of the propyl alcohol is 7.5%;

[0036] (3) The mixed liquid I obtained in step (1) was heated to 50 C., and the mixed liquid II obtained in step (2) was dripped at the speed of one drop per second, into the mixed liquid I obtained in step (1) with stirring and ultrasound, and heated to the temperature of 85 C. after the dripping is completed and the temperature was maintained for three hours while stopping stirring, and the temperature was decreased to the room temperature, so as to obtain a mixed liquid III. The mass ratio of the mixed liquid I to the mixed liquid II is 10:4.

[0037] (4) The mixed liquid III was added to an electrolytic cell with using a platinum electrode as an electrode and applying a voltage of 3 V to two ends of the electrode, and reacting for 13 minutes, to obtain a mixed liquid IV.

[0038] (5) The mixed liquid IV obtained in step (4) was heated with stirring, another mixed liquid II was taken and dripped into the mixed liquid IV obtained in step (4) at the speed of one drop per second. The mass ratio of the mixed liquid II to the mixed liquid IV is 1.05:1.25; and after the dripping is completed, the temperature was decreased to the room temperature under stirring, so as to obtain a mixed liquid V.

[0039] (6) A high-speed shearing treatment was performed on the mixed liquid V obtained in step (5) by using a high-speed shear mulser at the speed of 20000 revolutions per minute for one hour, so as to obtain a mixed liquid VI.

[0040] (7) Lyophilization treatment was performed on the mixed liquid VI to obtain a mixture I;

[0041] (8) The mixture I obtained in step (7) and absolute ethyl alcohol were mixed at a mass ratio of 1:2 and uniformly stirred, and were sealed at a temperature of 210 C. for performing solvent thermal treatment for 18 hours. The reaction was cooled to the room temperature, the obtained powder was collected by centrifugation, washed with deionized water and absolute ethyl alcohol eight times respectively, and dried to obtain a powder I.

[0042] (9) The powder I obtained in step (8) and ammonium persulfate was uniformly mixed at a mass ratio of 10:1, and sealed and heated to 165 C. The temperature was maintained for 13 hours. The reaction was cooled to the room temperature, the obtained mixed powder was washed with deionized water ten times, and dried to obtain a powder II.

[0043] (10) The powder II obtained in step (4) was placed into a crucible, heated to a temperature of 1500 C. at a speed of 3 C. per minute. The temperature was maintained for 7 hours. The reaction was cooled to the room temperature, to obtain an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity.

[0044] As observed via an electron microscope, the obtained A-site high-entropy nanometer metal oxide with high conductivity is a powder, and has microstructure of a square nanometer sheet with a side length of about 4 nm and a thickness of about 1 nm.

[0045] The product powder was taken and compressed by using a powder sheeter at a pressure of 550 MPa into a sheet. Conductivity of the sheet is measured by using the four-probe method, and the conductivity of the product is 2.110.sup.8 S/m.

Example 2

[0046] Provided is a preparation method for an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity, the method including the following steps.

[0047] (1) Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 were taken at a molar ratio of 0.4:0.3:0.4:0.5:0.4:0.7:0.8:0.5, added to a mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran at a mass ratio of 0.3:3:0.5, and stirred for ten minutes to obtain a mixed liquid I. The ratio of the total mass of Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 to that of the mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran (0.3:3:0.5) is 12.6%.

[0048] (2) Para-phenylene diamine, hydrogenated tallowamine, sorbitol and carbamyl ethyl acetate were taken at a mass ratio of 3:0.4:9:0.03, added to propyl alcohol, and stirred for three hours to obtain a mixed liquid II. The ratio of the total mass of the para-phenylene diamine, the hydrogenated tallowamine, the sorbitol and the carbamyl ethyl acetate to that of the propyl alcohol is 7.5%.

[0049] (3) The mixed liquid I obtained in step (1) was heated to 70 C., and the mixed liquid II obtained in step (2) was dripped at the speed of one drop per second into the mixed liquid I obtained in step (1) with stirring and ultrasound, was further heated to the temperature of 95 C. after the dripping is completed. The temperature was maintained for seven hours while stopping stirring, and deceased to the room temperature, so as to obtain a mixed liquid III. The mass ratio of the mixed liquid I to the mixed liquid II is 8:6.

[0050] (4) The mixed liquid III was added to an electrolytic cell with using a platinum electrode as an electrode and applying a voltage of 5 V to two ends of the electrode, and reacting for 17 minutes, to obtain a mixed liquid IV.

[0051] (5) The mixed liquid IV obtained in step (4) was heated to 65 C. with stirring, and the mixed liquid II obtained in step (2) was dripped into the mixed liquid IV obtained in step (4) at the speed of one drop per second. The mass ratio of the mixed liquid II to the mixed liquid IV is 1.05:1.25; and after the dripping is completed, the temperature was decreased to the room temperature under stirring, so as to obtain a mixed liquid V.

[0052] (6) High-speed shearing treatment was performed on the mixed liquid V obtained in step (5) by using a high-speed shear mulser at the speed of 40000 revolutions per minute for three hours, so as to obtain a mixed liquid VI.

[0053] (7) Lyophilization treatment was performed on the mixed liquid VI to obtain a mixture I.

[0054] (8) The mixture I obtained in step (7) and absolute ethyl alcohol was mixed at a mass ratio of 1:2 and uniformly stirred, and sealed at a temperature of 230 C. for performing solvent thermal treatment for 24 hours. The reaction was cooled to the room temperature, the obtained powder was collected by centrifugation, washed with deionized water and absolute ethyl alcohol eight times respectively, and dried to obtain a powder I.

[0055] (9) The powder I obtained in step (8) and ammonium persulfate were uniformly mixed at a mass ratio of 10:1, and sealed and heated to 175 C. The temperature was maintained for 15 hours and the reaction was cooled to the room temperature, the obtained mixed powder was washed with deionized water ten times, and dried to obtain a powder II.

[0056] (10) The powder II obtained in step (4) was placed into a crucible, heated to a temperature of 1700 C. at a speed of 3 C. per minute, and the temperature was maintained for 9 hours. The reaction was cooled to the room temperature to obtain an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity.

[0057] As observed via an electron microscope, the obtained A-site high-entropy nanometer metal oxide with high conductivity is a powder, and has microstructure of a square nanometer sheet with a side length of about 4 nm and a thickness of about 1 nm.

[0058] The product powder was taken and compressed by using a powder sheeter at a pressure of 550 MPa into a sheet. The conductivity of the sheet is measured by using the four-probe method, and the conductivity of the product is 2.110.sup.8 S/m.

Example 3

[0059] Provided is a preparation method for an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity, the method including the following steps.

[0060] (1) Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 were taken at a molar ratio of 0.4:0.3:0.4:0.5:0.4:0.7:0.8:0.5, added to a mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran at a mass ratio of 0.3:3:0.5, and stirred for 15 minutes to obtain a mixed liquid I. The ratio of the total mass of Gd(NO.sub.3).sub.3, Er(NO.sub.3).sub.3, La(NO.sub.3).sub.3, Nd(NO.sub.3).sub.3, Y(NO.sub.3).sub.3, ZrOSO.sub.4, SnC.sub.14 and NH.sub.4VO.sub.3 to that of the mixed solution of deionized water/absolute ethyl alcohol/tetrahydrofuran (0.3:3:0.5) is 12.6%.

[0061] (2) Para-phenylene diamine, hydrogenated tallowamine, sorbitol and carbamyl ethyl acetate were mixed at a mass ratio of 2:0.3:8:0.02, added to propyl alcohol, and stirred for two hours to obtain a mixed liquid II. The ratio of the total mass of the para-phenylene diamine, the hydrogenated tallowamine, the sorbitol and the carbamyl ethyl acetate to that of the propyl alcohol is 7.5%.

[0062] (3) The mixed liquid I obtained in step (1) was heated to 60 C., and the mixed liquid II obtained in step (2) was dripped at the speed of one drop per second into the mixed liquid I obtained in step (1) with stirring and ultrasound, and further heated to the temperature of 90 C. after the dripping is completed and stopping stirring. The temperature was maintained for five hours, and decreased to the room temperature, so as to obtain a mixed liquid III. The mass ratio of the mixed liquid I to the mixed liquid II is 9:7.

[0063] (4) The mixed liquid III was added to an electrolytic cell with using a platinum electrode as an electrode and applying a voltage of 7 V to two ends of the electrode, and reacting for 15 minutes, to obtain a mixed liquid IV.

[0064] (5) The mixed liquid IV obtained in step (4) was heated to 60 C. with stirring, and the mixed liquid II obtained in step (2) was dripped into the mixed liquid IV obtained in step (4) at a speed of one drop per second. The mass ratio of the mixed liquid II to the mixed liquid IV is 1.05:1.25; and after the dripping is completed, the temperature was decreased to the room temperature under stirring, so as to obtain a mixed liquid V.

[0065] (6) A high-speed shearing treatment was performed on the mixed liquid V obtained in step (5) by using a high-speed shear mulser at the speed of 30000 revolutions per minute for two hours, so as to obtain a mixed liquid VI.

[0066] (7) Lyophilization treatment was performed on the mixed liquid VI to obtain a mixture I.

[0067] (8) The mixture I obtained in step (7) and absolute ethyl alcohol were mixed at a mass ratio of 1:2 and uniformly stirred, and sealed at the temperature of 220 C. for performing the solvent thermal treatment for 21 hours. The reaction was cooled to the room temperature, the obtained powder was collected by centrifugation, washed with deionized water and absolute ethyl alcohol eight times respectively, and dried to obtain a powder I.

[0068] (9) The powder I obtained in step (8) and ammonium persulfate were uniformly mixed at a mass ratio of 10:1, and sealed and heated to 170 C. The temperature was maintained for 14 hours. The reaction was cooled to the room temperature, the obtained mixed powder was washed with deionized water ten times, and dried to obtain a powder II; and

[0069] (10) The powder II obtained in step (4) was placed into a crucible, heated to a temperature of 1600 C. at the speed of 3 C. per minute, and the temperature was maintained for 8 hours. The reaction was cooled to the room temperature, to obtain an A-site high-entropy nanometer metal oxide (Gd.sub.0.4Er.sub.0.3La.sub.0.4Nd.sub.0.5Y.sub.0.4)(Zr.sub.0.7, Sn.sub.0.8, V.sub.0.5)O.sub.7 with high conductivity.

[0070] As observed via an electron microscope, the obtained A-site high-entropy nanometer metal oxide with high conductivity is a powder, and has microstructure of a square nanometer sheet with a side length of about 8 nm and a thickness of about 2 nm.

[0071] The product powder was taken and compressed by using a powder sheeter at a pressure of 550 MPa into a sheet. The conductivity of the sheet is measured by using the four-probe method, and the conductivity of the product is 4.110.sup.8 S/m.

Comparative Example 1

[0072] A commercially available ITO (indium tin oxide) powder is taken and compressed by using a powder sheeter at a pressure of 550 MPa into a sheet, and the conductivity of the sheet is measured by using the four-probe method.

[0073] As measured, the conductivity of the commercially available ITO (indium tin oxide) is 1.610.sup.6 S/m.

Comparative Example 2

[0074] A commercially available powder of a high-entropy oxide (CoCrFeMnZn).sub.3O.sub.4 is taken and compressed by using a powder sheeter at a pressure of 550 MPa into a sheet, and the conductivity of the sheet is measured by using the four-probe method.

[0075] As measured, the conductivity of the commercially available high-entropy oxide (CoCrFeMnZn).sub.3O.sub.4 is 1.610.sup.3 S/m.

[0076] The particular examples in the present disclosure are described above. It should be understood that the present invention is not limited to specific embodiments described above, and various alterations or modifications may be made by those skilled in the art within the scope of the claims, not affecting essential contents in the present disclosure.