A METHOD OF MACHINING ARTICLES FROM A SUPERHARD DISC

Abstract

This disclosure relates to a method of machining articles from a disc comprising superhard material, such as polycrystalline diamond (PCD) or polycrystalline cubic boron nitride (PCBN). The method includes providing a disc having a diameter of no more than 100 mm and a thickness of no more than 10 mm, providing a nesting pattern, scanning the disc to identify and locate any flaws in the disc and subsequently creating a machining program that takes into account said flaws.

Claims

1. A method of machining articles from a disc comprising superhard material, the method comprising: Providing a disc to be machined, the disc having a diameter of no more than 100 mm and a thickness of no more than 10 mm; Providing a nesting pattern comprising one or more articles to be machined from a disc; Scanning the disc to identify non-defective and/or defective portions, said defective portions containing any one of more of the following: microstructural flaws, scratches, and compositional contaminants; Overlaying the nesting pattern onto defective and/or non-defective portions of the disc that were identified during scanning to create a machining program; Machining the one or more articles out of the disc according to the machining program.

2. The method as claimed in claim 1, wherein scanning the disc comprises ultrasonically scanning the disc to generate ultrasonic scan data.

3. The method as claimed in claim 2, comprising identifying non-defective portions of the disc using the ultrasonic scan data.

4. The method as claimed in claim 3, further comprising locating the non-defective portions of the disc using the ultrasonic scan data.

5. The method as claimed in claim 2, comprising identifying defective portions of the disc using the ultrasonic scan data.

6. The method as claimed in claim 5, further comprising locating the defective portions of the disc using the ultrasonic scan data.

7. The method as claimed in claim 1, wherein scanning the disc comprises visually scanning the disc to generate visual scan data.

8. The method as claimed in claim 7, comprising identifying non-defective portions of the disc using the visual scan data.

9. The method as claimed in claim 8, further comprising locating the non-defective portions of the disc using the visual scan data.

10. The method as claimed in claim 8, comprising identifying defective portions of the disc using the visual scan data.

11. The method as claimed in claim 10, further comprising locating the defective portions of the disc using the visual scan data.

12. The method as claimed in claim 1, further comprising reviewing the first said machining program file for defective portions and subsequently modifying the first said machining program to remove one or more articles that overlay any defective portions of the disc, thereby creating a second machining program file.

13. The method as claimed in claim 1, wherein the disc comprises polycrystalline diamond (PCD)

14. The method as claimed in claim 1, wherein the disc comprises polycrystalline cubic boron nitride (PCBN).

15. The method as claimed in claim 1, wherein the or each article is a cutting tip.

16. The method as claimed in claim 1, wherein machining comprises wire electro-discharge machining.

17. The method as claimed in claim 1, wherein machining comprises wire laser cutting.

18. A computer program comprising computer readable code which, when run on a computer apparatus, causes the computer apparatus to perform the method as claimed in claim 1.

19. A computer program product comprising a computer readable medium and a computer program according to claim 18, wherein the computer program is stored on the computer readable medium.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] The invention will now be more particularly described, by way of example only, with reference to the accompanying drawings, in which

[0021] FIG. 1 is a perspective view of a prior art tool module;

[0022] FIG. 2 is a perspective view of a prior art cutting tool;

[0023] FIG. 3 is a flow diagram indicating the method to machine articles from a superhard disc in accordance with the invention;

[0024] FIG. 4 is a perspective view of a superhard disc; and

[0025] FIG. 5 is an image in accordance with the invention, showing the combination of proposed, nested cutting tools juxtaposed onto the disc ahead of cutting tool removal therefrom, and in particular indicating defective portions of the disc.

DETAILED DESCRIPTION

[0026] Referring to FIG. 1, a prior art tool module is indicated generally at 10. The tool module 10 is connectable to a tool assembly (not shown) on, for example, a mill or a lathe. The tool module 10 comprises an elongate tool holder 12 and a removable cutting tool 14 detachably mounted at one end of the tool holder 12. This particular cutting tool 14 is square in plan view. The cutting tool 14 is held in place by a releasable clamp 16.

[0027] An alternative prior art cutting tool, indicated at 18, is shown in FIG. 2. The cutting tool 16 is triangular in plan view, with a central through-hole 20.

[0028] The cutting tools 10, 18 are typically removed from a disc shaped sintered body, which is circular in plan view. To maximise the allocation of tools obtainable from the disc, nesting software is commonly used.

[0029] FIG. 3 shows an exemplary method for machining articles from a superhard disc 22 in accordance with the invention. The following numbering corresponds to that of FIG. 3:

[0030] S1. Select the required disc 22. Only discs having a diameter of no more than 100 mm and a thickness of no more than 10 mm are suitable for use. The disc comprises sintered PCD. PCD is commonly consider an ultrahard material since it has a Vickers hardness over 80 GPa. Alternatively, may comprise sintered polycrystalline cubic boron nitride (PCBN) material. PCBN is commonly consider a superhard material since it has a Vickers hardness over 80 GPa.

[0031] In this embodiment, and as best seen in FIG. 4, the disc 22 comprises a PCD layer 21 sinter joined to a tungsten carbide substrate 23. The disc 22 has a diameter of 76.5 mm, with an overall height of 1.6 mm. The PCD layer 21 is 0.5 mm thick.

[0032] Each disc 22 is assigned a unique number to identify it, and this identifier travels with the disc 22 throughout the process. Each disc 22 also has a reference point for disc orientation.

[0033] S2 & S3. The disc 22 is scanned in order to characterise the disc 22 and to determine its quality. Sometimes, the superhard disc 22 comprises non-defective portions 24 and also defective portions 26, best seen in FIG. 5. Defective portions 26 include a flaw or an unacceptable grade or quantity of flaw, whereas non-defective portions 24 include no flaws, or at worst an acceptable grade or quantity of flaw. The flaws can be variations in the layer with respect to the grade tolerance specification, scratches or polishing defects on the surface. Not all discs 22 comprise defective portions 26 but it is clearly beneficial to identify any flaws ahead of tool segments or blanks 28 removed from the disc. Machining tools made from defective tool segments are prone to premature failure in use, damaging the workpiece they are machining, and increasing spoilage.

[0034] Scanning may comprise visual scanning and/or ultra-sonic scanning.

[0035] Visual scanning comprises the automated scanning of around 12,000 points on each disc. Initially, surface defects are determined from a visual inspection under magnification. Then the visually defective portions are marked on the disc surface and a visual defect camera takes a contrast image of the surface and outputs all 12,000 points with high or low values representing painted areas of the disc.

[0036] Ultra-sonic scanning measures the thickness of the disc, scans around 96,000 points with a depth of each point. Ultra-sonic scanning is also automated.

[0037] Scan data from each individual disc is logged for traceability. Each point contains X and Y positions, together with Z layer depth for ultra-sonic scanning.

[0038] Steps 2 and 3 may take place in either order. Scanning may optionally consist of only S2 or only S3. Preferably, the scanning step comprises both visual scanning and ultra-sonic scanning.

[0039] S4. The scan data from visual scanning, ultrasonic scanning or both, is then compiled into a single scan results file. This is a digital file representing the scan data, for example, the file may be AutoCAD dxf file. The scan results file is unique to each disc and is not transferrable to or indicative of any other disc. The scan results file contains means to identify defects and to locate those defects. Alternatively, or additionally, the scan results file contains means to identify and optionally, to locate, non-defective portions of the disc.

[0040] Preferably, the scan data file(s) is(are) analysed automatically via macro and only locations indicating layer out of tolerance results and high contrast painted areas are plotted in dxf format.

[0041] S5. Select the nesting file. Each pre-configured nesting file is different for each set of tool segments, depending on the size and the shape of the individual tool segments. The nesting file indicates the outline of one or more proposed tool segments, arranged on the disc for maximum usage of the disc, regardless of the quality of the disc material. In FIG. 5, the proposed tool segments 28 are triangular.

[0042] S6. Combine scan results and nesting pattern to help create a machining file. As indicated in FIG. 5, the proposed layout of nested tool segments 28 is juxtaposed onto the scan results. If the disc were to be used with any further intervention, tool segments 28 originating in the defection portions 26 of the disc 20 would result.

[0043] S7. Thus, the machining file may then be adjusted at this point. This step is preferably automated through software with some manual manipulation required. The tool segments 28 that would have been machined from the defective portions are removed from the machining program. Only tool segments 28 that fall within the non-defective portions 24 of the disc remain. Alternatively, the machining file may be adjusted to filter out the non-defection 24 portions of the disc 22.

[0044] S8. Tool segments 18 are machined out of the disc in accordance with the revised machining program, using wire EDM or laser cutting.

[0045] Depending on the process, tool segments 18 are then required to be cleaned.

[0046] Subsequently, each tool segment 18 is visually inspected to determine conformity with the approved drawing, before shipment to the customer.

[0047] In most cases, the customer would braze the tool segment 18 onto a particular machining tool. Alternatively, the tool segment 18 may be clamped in place as described previously with respect to FIG. 1.

[0048] It is imperative that the disc orientation is identical for both the machining program and the actual disc ahead of machining.

[0049] In summary, the inventors have found that the new process is more efficient in cutting and processing, and importantly, it saves on manual labour. Users have better control over the materials. Significantly, this process supports ISO certification and is a selling point for the end-user.

[0050] While this invention has been particularly shown and described with reference to embodiments, it will be understood by those skilled in the art that various changes in form and detail may be made without departing from the scope of the invention as defined by the appended claims.