ATMOSPHERIC PLASMA REACTOR FOR THE LARGE-SCALE PRODUCTION OF CARBON NANOTUBES AND AMORPHOUS CARBON

Abstract

The present invention addresses to a plasma reactor for the thermal and/or plasmatic decomposition of hydrocarbon molecules aiming at the production of carbon nanotubes on a large scale, as well as amorphous carbon of superior quality in terms of purity. Because it is operated at pressures close to the atmospheric pressure and can operate in a continuous flow regime, said reactor has a superior capacity for the production of carbon nanotubes. The hydrocarbon pyrolysis by means of thermal plasma or the heat derived therefrom produces carbonaceous material that presents a higher purity content than those obtained by the methods most used in the production of solid carbon, which are based, generally, on the burning of part of the load hydrocarbon.

Claims

1. An atmospheric plasma reactor, characterized in that it comprises: at least one reaction chamber (C) made of stainless steel, consisting of one section (A) or two sections (A and B), with a plasma torch (T) having a injector (1), a coupling flange (2), an injection jacket (6), a cathode support (7), an electrode containing a piece of tungsten with 2% thoria (cathode) (19), an anode (4), a cathode cooling surface (8), a cathode jacket (9), an insulator (10) and an outer jacket (18).

2. The reactor according to claim 1, characterized in that it comprises catalysts inside the reaction chamber (C) to manufacture carbon nanotubes (E) and amorphous carbon, when catalysts are not used.

3. The reactor according to claim 1, characterized in that the electrical contact of the arc on the cathode (19) occurs entirely on the surface of the piece of tungsten with 2% thoria.

4. The reactor according to claim 1, characterized in that the reaction chamber (C) is downstream of the plasma torch (T).

5. The reactor according to claim 1, characterized in that it comprises an injector (1) for injecting the gas in the axial direction.

6. The reactor according to claim 5, characterized in that the injected gas is argon.

7. The reactor according to claim 5, characterized in that the injected gas is helium.

8. The reactor according to claim 6, characterized in that the gas is maintained at an electrical discharge of about 5 to 50 A and 22 to 32 V.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0021] The present invention will be described in more detail below, with reference to the attached figures which, in a schematic way and not limiting the inventive scope, represent examples of the same. In the drawings, there are:

[0022] FIG. 1 illustrating the reaction chamber;

[0023] FIG. 2 illustrating the fastening structure of the plasma pyrolysis equipment;

[0024] FIG. 3 illustrating the plasma torch;

[0025] FIG. 4 illustrating an electrode (cathode);

[0026] FIG. 5 illustrating the torch anodes in the straight (D1), conical (D2) and step (D3) shape;

[0027] FIG. 6 with SEM images of produced carbon nanotubes (E).

DETAILED DESCRIPTION OF THE INVENTION

[0028] The plasma reactor (T+C) for the thermal decomposition of hydrocarbon molecules, aiming at the production of carbon nanotubes (E) on a large scale and amorphous carbon of superior quality in terms of purity, has a reaction chamber (C) made of stainless steel, as shown in FIG. 1. The chamber (C) consists of two sections, called the upper section (A) and the lower section (B).

[0029] The fastening structure of the plasma pyrolysis equipment (FIG. 2) was built in carbon steel. Its base was designed to ensure the stability of the structure, preventing it from toppling over with the weight of the electrode set (FIG. 3) and the reaction chamber (C). The base also has enough space to accommodate the electrical source and the thermostatic bath for cooling the electrodes.

[0030] The upper section (A) of the reaction chamber (C) has a window to enable the visualization of the electric arc and visual monitoring of the process throughout the reaction tests.

[0031] The lower section of the chamber (B) consists of only of a temperature sensor input (i) and two larger diameter inputs (ii, iii) that can be used for QUENCHING, if necessary, or input for a pressure sensor or even temperature sensor.

[0032] The upper flange (F) was designed to ensure the coupling of the electrode system for generating the plasma torch (T). This section of the chamber (A) also contains two inputs for temperature sensors (I, II), equidistant from each other, and a third input with a larger diameter that can be used for QUENCHING (III) or for inserting a sensor for measuring the temperature at the boundary point between the two sections or even for monitoring the pressure downstream the reaction zone.

[0033] The plasma torch (T) is provided with an induced magnetic field, responsible for rotating the arc at a predetermined speed, which is an important factor to ensure a homogeneous temperature for the plasma gas at a low consumption of the electrode. The plasma torch (T) supplies the energy necessary for the breakdown of the hydrocarbon load. The radiation therefrom, as well as the heat convection from the plasma gas, provides enough energy for the hydrocarbons in the load to reach the complete pyrolysis temperature of methane molecules (1000 C.). For the production of higher quality carbon materials, the process should preferably take place at temperatures above 2500 C.

[0034] In FIG. 3 (plasma torch), it is possible to observe the important components for the operation of the plasma torch (T), such as the injector (1), the coupling flange (2), the anode (4), the injection jacket (6), the cathode support (7), the cathode jacket (9) and the cathode (19), the cathode cooling (8), the insulator (10) and the outer jacket (18). Said injector (1) injects the gas in the axial direction.

[0035] After the two sections (A and B), there is a reduction from 4 (10.16 cm) to 2 (5.08 cm) with two more auxiliary inputs (j, jj), one for a temperature sensor and the other for a pressure sensor. This reduction converges to a horizontal tube (T) also of 2 (5.08 cm) with a gas injection nozzle (K) for QUENCHING. This tube section also contains two auxiliary inputs, one for monitoring the gas temperature (L), before entering the gas/solid separation system, and the other for measuring pressure (K).

[0036] FIG. 4 represents a cathode (19) and FIG. 5 the anodes (D1, D2, and D3), which, because they are metallic and due to the electrical contact of the cathode arc occur entirely in the piece of tungsten with 2% thoria, the electrodes have a service life at least three times longer than conventional carbon electrodes (U.S. Pat. No. 5,997,837) or another pair of metallic electrodes (PI0305309-1), even with temperatures inside the chamber at the same magnitude.

[0037] The new torch (T) features a superior design in terms of coupling between parts, more refined, where some parts are coupled through threads; the insert of tungsten with 2% thoria with forced adjustment in a copper piece forming what can be called a cathode (19), in addition to well-adjusted skirts for safe cooling of the electrodes. The new torch (T) also presents an improved design of the electrodes, which have a longer service life due to the precise thoriated tungsten insert in the cathode (19) (which forces the root of the electric arc to be located on the external surface of the insert of tungsten with 2% thoria, which works as a cathode19) and new geometries for three different types of anode. The reaction chamber (C) was tested with the new plasma torch (T), obtaining temperatures inside the chamber (C) in the same magnitude, despite a lower energy consumption compared to PI0305309-1, and producing carbon in solid state.

[0038] Part of the electrical-electronic system will be installed in the support column (FIG. 2-CL) and in the upper cabin (FIG. 2-CA), which, in addition to the structural function, will serve as a cabin for passing power cables and installation of electronic components.

[0039] The upper cabin (CA) will be used to support the set of electrodes and to install pressure and temperature indicators, mass flow controllers, switches in general, starting buttons, stopping the electrical source and control device of the current provided to the system.

[0040] Considering the cold start, that is, from room temperature, of the reactor (T+C) developed in the design, it is possible to obtain about 1 g of high purity carbonaceous material, providing the argon plasma with an energy less than 1.2 kWh. The carbonaceous material to be obtained may have a high content of carbon nanostructures, such as carbon nanotubes (E), depending mainly on the temperature in the bed zone containing catalysts. It is possible to manufacture carbon nanotubes (E), when catalysts are used inside the reaction chamber (C), and to manufacture amorphous carbon, when catalysts are not used.

[0041] Argon gas was used as plasma gas, being maintained at an electrical discharge of about 5 to 50 A and 22 to 32 V. In all tests, the cathode (19) was cooled with water at a temperature of about 22 to 26 C. Alternatively, helium gas can be used as plasma gas.

[0042] The heat from the plasma arc is low in the radial direction and the highest temperatures are possible in the region (A) of the chamber (C) downstream of the plasma arc, preferably in the axial axis of the chamber (C). Therefore, the thermal decomposition of methane will occur mainly due to the heat from the plasma torch (T) in the axial direction.

[0043] It should be noted that, although the present invention has been described in relation to the attached drawings, it may undergo modifications and adaptations by technicians skilled on the subject, depending on the specific situation, but provided that within the inventive scope defined by the claims.