METHOD FOR PREPARING SUPER-LUBRICATIVE MULTI-LAYER COMPOSITE FULLERENE-LIKE CARBON LAYER/GRAPHENE-LIKE BORON NITRIDE THIN FILM

Abstract

A method for preparing a super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film is provided. A substrate is ultrasonically cleaned in absolute ethyl alcohol and acetone sequentially for 15 min. The substrate is cleaned by argon plasma bombardment for 15 min. A fullerene-like carbon layer A having an onion-like structure is prepared by high-vacuum medium-frequency magnetron sputtering for 30 s. A graphene-like boron nitride layer B is prepared by high-vacuum medium-frequency magnetron sputtering and coating device to sputter the elemental boron target for 30 s. Steps (3) and (4) are repeated 80 times to overlay the fullerene-like carbon layer A and the graphene-like boron nitride layer B in an alternate way. The super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film has a large load capacity, and excellent wear resistance, high temperature resistance and super lubrication.

Claims

1. A method for preparing a super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film, comprising: 1) ultrasonically cleaning a substrate in absolute ethyl alcohol and acetone sequentially for 15-30 min; 2) cleaning the substrate by argon plasma bombardment for 15 min; 3) preparing a fullerene-like carbon layer A having an onion-like structure by high-vacuum medium-frequency magnetron sputtering; 4) preparing a graphene-like boron nitride layer B using a high-vacuum medium-frequency magnetron sputtering and coating device to sputter an elemental boron target; 5) repeating steps (3) and (4) 60-80 times to overlay the fullerene-like carbon layer A and the graphene-like boron nitride layer B in an alternate way to obtain the super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film with a first layer and a last layer being the fullerene-like carbon layer A.

2. The method of claim 1, wherein the substrate is made of metal or ceramic.

3. The method of claim 1, wherein the fullerene-like carbon layer A has a thickness of 6-12 nm, the graphene-like boron nitride layer B has a thickness of 2.1-3.5 nm, and the multilayer fullerene-like carbon layer/graphene-like boron nitride super-lubricative composite thin film has a total thickness of 2-3.5 m.

4. The method of claim 1, wherein the fullerene-like carbon layer A is prepared by high-vacuum medium-frequency magnetron sputtering using methane or acetylene under a pressure of 10-15 Pa, a negative bias pulsed voltage of 800-1000 V and a duty ratio of 60%-80% for 10-50 s.

5. The method of claim 1, wherein the graphene-like boron nitride layer B is prepared using the high-vacuum medium-frequency magnetron sputtering and coating device to sputter the elemental boron target in an atmosphere of nitrogen and argon under a pressure of 0.4-0.5 Pa, a negative bias pulsed voltage of 400-1000 V and a duty ratio of 60%-80% for 10-50 s; wherein the nitrogen has a purity of more than 99.99% and a flow rate of 55-95 sccm; and the argon has a purity of more than 99.99% and a flow rate of 60-120 sccm.

6. The method of claim 1, wherein the elemental boron target is rectangle, circular or a rotary column.

7. The preparation method of claim 1, wherein a purity of the elemental boron is more than 99.9% and is produced by hot forming; and the elemental boron target has a length of 60-90 cm, a width of 10-20 cm and a height of 1-5 cm.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0027] The FIGURE is a sectional view of a super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film according to the present disclosure, where A refers to a fullerene-like carbon layer and B refers to a graphene-like boron nitride layer.

DETAILED DESCRIPTION OF EMBODIMENTS

[0028] The disclosure will be further described with reference to the following embodiments and the accompany drawing.

[0029] Embodiment 1

[0030] The disclosure provides a method for preparing a super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film, including the following steps.

[0031] 1) A substrate is ultrasonically cleaned in absolute ethyl alcohol and acetone sequentially for 15 min, then is blown dry using nitrogen, and is placed in a chamber at a distance of 80 mm from a target. A vacuumizing is started. Specifically, the substrate can be a 304 stainless steel sheet.

[0032] 2) When the pressure of the chamber is less than 5 10.sup.5 Pa, argon enters the chamber at a flow rate of 120 sccm, the bias pulsed voltage is 1000 V, and the duty ratio is 70%, the substrate is cleaned by argon plasma bombardment for 15 min to remove oxide and other materials on the surface of the substrate.

[0033] 3) A first inflow valve for CH.sub.4 is opened to let CH.sub.4 in at a flow rate of 80 sccm; a second inflow valve for Ar is opened to let Ar in at a flow rate of 120 sccm; the pressure of the chamber is kept as 15 Pa; and the bias pulsed voltage is adjusted to 800 V. A fullerene-like carbon layer A is prepared by high-vacuum medium-frequency magnetron sputtering for 30 s.

[0034] 4) The first inflow valve for CH.sub.4 is closed; a third inflow valve for N.sub.2 is opened to let N.sub.2 in at a flow rate of 80 sccm; the second inflow valve for Ar is adjusted to let Ar in at a flow rate of 90 sccm; the pressure of the chamber is kept as 0.45 Pa; a baffle for an elemental boron target is opened; the elemental boron target is electrified to adjust the sputtering current to 1 A; the bias pulsed voltage is increased from 400 V to 600 V by 100 V every 5 s, and then keeps at 600 V for 10 s. A graphene-like boron nitride layer B is prepared using a high-vacuum medium-frequency magnetron sputtering and coating device to sputter the elemental boron target for 20 s.

[0035] 5) Steps (3) and (4) are repeated 80 times to overlay the fullerene-like carbon layer A and the graphene-like boron nitride layer B in an alternate way, as shown in the FIGURE, to obtain the super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film with a total thickness of 1.04 m.

[0036] 6) The super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film has a hardness of 25 GPa, a bonding force of 60 GPa and a friction coefficient of 0.004.

[0037] A BASALT-N2 friction wear testing machine is used to test the performance of the super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film in this embodiment. Table 1 indicated the conditions and results of a frictional wear experiment for the super-lubricative multi-layer composite fullerene-like carbon layer/graphene-like boron nitride thin film according to the present disclosure. As shown in Table 1, the test was carried out in a ball-disc reciprocating friction mode with a load of 20 N, a frequency of 5 Hz, a stroke of 5 mm, a temperature of 27 C. and a moisture content of 38%. The multilayer fullerene-like carbon layer/graphene-like boron nitride super-lubricative composite thin film is prepared on a stainless steel sheet, the dual balls are made of GCr15 bearing steel, and the dual balls have a diameter of 6 mm. The result showed that the friction coefficient was kept at 0.006, the wear rate was 3.410.sup.9 m.sup.3/Nm.

TABLE-US-00001 TABLE 1 Load 20N Frequency 5 Hz Stroke 5 mm Temperature 27 C. Moisture % 38% Dual balls GCr15 6 mm Friction coefficient 0.006 Wear rate 3.4 10.sup.9 m.sup.3/Nm