SUPERHYDROPHOBIC COATINGS FOR THE TREATMENT OF TEXTILES

Abstract

The present invention relates to aqueous silane emulsions based on specific hydrolysable silanes anionic and non-ionic surfactants, a textile comprising a coating obtainable by impregnating the textile with the aqueous silane emulsion according to the present invention and the use of the aqueous silane emulsion according to the present invention for treating textiles. Moreover, the invention also encompasses a method of impregnating a textile with the aqueous silane emulsion according to the present invention as obtained via dilution from a concentrated system.

Claims

1. Aqueous silane emulsion, comprising a) at least one hydrolysable silane having the general formula (I):
R.sup.1Si(OR.sup.2).sub.3 (I), wherein R.sup.1 is an C.sub.4-C.sub.10, alkyl group which can be optionally substituted with one or more groups independently selected from F, CI, Br, I or OH; and R.sup.2 is independently selected from an C.sub.1-C.sub.4, alkyl group which can be optionally substituted with one or more groups independently selected from F, CI, Br, I or OH; b) at least one anionic surfactant, having an HLBd value of 18 to 40, which comprises or is sodium lauryl sulfate; c) optionally at least one non-ionic surfactant, having an HLBg value of 2 to 10; d) optionally at least one acid; e) optionally at least one additive; and f) the remainder being water; wherein the sum of a) to f) is 100 wt.-%.

2. The aqueous silane emulsion according to claim 1, wherein a) is present in 5 to 6 wt.-% based on the total weight of the aqueous silane emulsion and/or a) comprises octyltriethoxysilane.

3. The aqueous silane emulsion according to claim 1, wherein b) is present in 0.02 to 0.2 wt.-%, based on the total weight of the aqueous silane emulsion.

4. The aqueous silane emulsion according to claim 1, wherein the at least one acid d) is an organic acid, having a pKa of 1.3-5.0, selected from acetic acid, para-toluenesulfonic acid, benzenesulfonic acid, camphorsulfonic acid, malic acid, maleic acid, glyoxylic acid, citric acid, formic acid, pyruvic acid, tartaric acid, phthalic acid, acetylsalicylic acid, salicylic acid, lactic acid, dihydroxy fumaric acid, mandelic acid, malonic acid, glycolic acid and oxalic acid or combinations thereof, and is present in 1 to 1.5 wt.-%, based on the total weight of the aqueous silane emulsion.

5. The aqueous silane emulsion according to claim 1, wherein the at least one further additive e) is selected from defoamer, buffering agents like sodium bicarbonate, amino silicones, wetting agents, crosslinking agents, extenders or combinations thereof, and is present in 0.1 to 2 wt.-%, based on the total weight of the aqueous silane emulsion.

6. The aqueous silane emulsion according to claim 1, wherein 80 to 90 wt.-%, of water is present, based on the total weight of the aqueous silane emulsion.

7. The aqueous silane emulsion according to claim 1, wherein the average droplet size is 30 to 60 nm and the pH-value is from 3 to 5.8.

8. The aqueous silane emulsion according to claim 1, wherein c) is present in 0.02 to 0.5 wt. %, based on the total weight of the aqueous silane emulsion and is selected from sorbitan esters and polyethoxylated sorbitan esters. 9 (currently amended): The aqueous silane emulsion according to claim 1, wherein the aqueous silane emulsion is a concentrate, wherein (1) a) is present in 18 to 40 wt.-%, based on the total weight of the concentrate; (2) b) is present in 0.05 to 2.0 wt.-% based on the total weight of the concentrate; (3) c) is present in 0.35 to 2.8 wt.-%, based on the total weight of the concentrate; and/or (4) f) is present in at least 55 to 58 wt.-% based on the total weight of the concentrate; and (5) the concentrate emulsion has a pH-value of from 6 to 7.

10. A textile comprising a coating obtainable by impregnating a textile substrate with the aqueous silane emulsion according to claim 1.

11. The textile of claim 10, wherein the textile substrate is polyamide, polypropylene or polyester.

12. A method of impregnating a textile, with an aqueous silane emulsion according to claim 1, comprising the steps: i) applying the aqueous silane emulsion via pad application onto a textile substrate; and ii) curing the treated textile substrate obtained in step i).

13. The method of claim 12, wherein the application speed of step i) is 1 m/min to 30 m/min, and the pressure used to apply the aqueous silane emulsion is 1.5 to 3.5 bar.

14. The method of claim 12, wherein the curing temperature of step ii) is 150 to 160 C.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0038] In a preferred embodiment, the emulsion according to the present invention contains less than 0.5 wt.-%, preferably less than 0.1 wt.-%, more preferably 0.01 wt.-%, perfluorocarbons, based on the total weight of the emulsion. Most preferably, the emulsion according to the present invention is free from perfluorocarbons.

[0039] In a preferred embodiment, the aqueous silane emulsion of the present invention (as applied to textiles) comprises at least 70 wt.-%, preferably at least 80 wt.-%, more preferably at least 90 wt.-%, of water, based on the total weight of the emulsion. In a further preferred embodiment 70 to 90 wt.-%, more preferably 88 to 90 wt.-% of water is present, based on the total weight of the emulsion.

[0040] In a preferred embodiment, the emulsion according to the invention is an oil in water emulsion having an average droplet size of 10 to 150 nm, preferably 30 to 60 nm. The droplet size is determined via dynamic light scattering. It has been found that when a droplet size in this range is obtained the emulsions have longevity of stability over time.

[0041] In a preferred embodiment, the aqueous silane emulsion according to the invention has a pH-value of from 1 to 6.9, preferably 2 to 6, more preferably 3 to 5.8.

[0042] The emulsion contains at least one hydrolysable silane having the general formula (I)

R.sup.1Si(OR.sup.2).sub.3 (I), wherein [0043] R.sup.1 is an C.sub.2-C.sub.12, preferably C.sub.4-C.sub.10, more preferably C.sub.7-C.sub.9, most preferably C.sub.8, alkyl group which can be optionally substituted with one or more groups independently selected from F, Cl, Br, I or OH, preferably it is unsubstituted; and [0044] R.sup.2 is independently selected from an C.sub.1-C.sub.8, preferably C.sub.1-C.sub.4, more preferably C.sub.2, alkyl group which can be optionally substituted with one or more groups independently selected from F, Cl, Br, I or OH, preferably it is unsubstituted.

[0045] In a preferred embodiment, the hydrolysable silane according to the present invention has a molecular weight of 100 to 600 g/mol, preferably of 150 to 400 g/mol, more preferably 250 to 300 g/mol.

[0046] Specific examples of hydrolysable silanes useful according to the present invention include, but are not limited to, methyltrimethoxysilane, methyltriethoxysilane, methyltri-n-propoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, ethyltri-n-propoxysilane, propyltriethoxysilane, propyltri-n-propoxysilane, butyltrimethoxysilane, butyltriethoxysilane, isobutyltrimethoxysilane, isobutyltriethoxysilane, n-hexyltrimethoxysilane, 6-chloro-hexyltrimethoxysilane, 6,6,6-triflurohexyltrimethoxysilane, cyclohexyltrimethoxysilane, octyltrim ethoxysi lane, octyltriethoxysilane, octyltri isopropoxysi lane, 2-ethylhexyltrim ethoxysi lane, decyltrimethoxysilane, dodecyltrimethoxysilane, or mixtures thereof . In a more preferred embodiment the hydrolysable silane according to the present invention comprises octyltriethoxysilane, in an even more preferred embodiment it is octyltriethoxysilane.

[0047] In a preferred embodiment, at least one hydrolysable silane is present in 2 to 10 wt.-%, preferably 5 to 6 wt.-%, based on the total weight of the aqueous silane emulsion. In a further preferred embodiment, the at least one hydrolysable silane is present in 2 to 10 wt.-%, preferably 5 to 6 wt.-%, based on the total weight of the aqueous silane emulsion and comprises octyltriethoxysilane, more preferred is octyltriethoxysilane.

[0048] The emulsion comprises at least one anionic surfactant b), preferably having an HLBd value of 1 to 40, more preferably 18 to 40, most preferably 40. In general, the literature suggests nonionic surfactants having an HLBg value of from 1-20. However, it has been surprisingly found that emulsions comprising the specific hydrolizable silane compound a) according to the present invention show best stability with anionic surfactants having an HLBd values of at least 13, more preferably even higher.

[0049] Exemplary suitable anionic surfactants are alkali metal sulfosuccinates; sulfonated glyceryl esters of fatty acids such as sulfonated monoglycerides of coconut oil acids; salts of sulfonated monovalent alcohol esters such as sodium oleyl isothionate; amides of amino sulfonic acids such as the sodium salt of oleyl isothionate; amides of amino sulfonic acids such as the sodium salt of oleyl methyl tauride; sulfonated products of fatty acid nitriles such as palm itonitrile sulfonate; sulfonated aromatic hydrocarbons such as sodium alpha-naphthalene monosulfonate; condensation products of naphthalene sulfonic acids with formaldehyde, sodium octahydro anthracene sulfonate; alkali metal alkyl sulfates having alkyl groups of 8 to 30, preferably 8 to 18 carbon atoms; ether sulfates having alkyl groups of 8 to 30, preferably 8 to 18 carbon atoms; and alkylaryl sulfonates having one or more alkyl groups of 8 to 30 carbon atoms. In a preferred embodiment said at least one anionic surfactant comprises a sulfate group, more preferably is selected from alkali metal alkyl sulfates having alkyl groups of 8 to 30, preferably 8 to 18 carbon atoms; most preferably is an alkali metal alkyl sulfate having an alkyl group with 8 to 16 carbon atoms. In a further preferred embodiment, the at least one anionic surfactant comprises, more preferably consists of sodium lauryl sulfate.

[0050] In a preferred embodiment, the at least one anionic surfactant is present in 0.01 to 0.2 wt.-%, preferably 0.02 to 0.2 wt.-%, more preferably 0.025 to 0.2 wt.-%, based on the total weight of the aqueous silane emulsion. In a further preferred embodiment, the anionic surfactant is present in 0.01 to 0.2 wt.-%, preferably 0.02 to 0.2 wt.-%, more preferably 0.025 to 0.2 wt.-%, based on the total weight of the aqueous silane emulsion and comprises sodium lauryl sulfate, more preferred is sodium lauryl sulfate. In most preferred embodiments, the amount of anionic surfactant, preferably sodium lauryl sulfate, is 0.2 wt.-% or less, preferably between >0.01 and 0.2 wt.-% or 0.025 and 0.2 wt.-%, based on the total weight of the aqueous silane emulsion.

[0051] The emulsion of the present invention can further comprise at least one non-ionic surfactant c), preferably having an HLBg value of 1-20, more preferably 2-10. It has been found that a combination of the specific anionic and nonionic surfactant of the present invention facilitates the creation of a stable emulsified system that allows performance directly after coating application.

[0052] Exemplary suitable non-ionic surfactants are alkoxylated fatty alcohols, alkyl glycosides, alkoxylated fatty acid alkyl esters, fatty acid alkanol amides, hydroxyl mixed ethers, polyhydroxy fatty acid amides, triglycerides, sorbitan esters, sorbitan mono-, di- and triglycerides and alkoxylated sorbitol esters. In a preferred embodiment the at least one nonionic surfactant is selected from sorbitan esters, mono-, di- and triglycerides, and polyoxyethylene sorbitan esters, such as, without limitation, sorbitan monostearate, sorbitan distearate, sorbitan tristearate, sorbitan monolaurate, sorbitan dilaurate, sorbitan trilaurate, sorbitan monopalmitate, sorbitan dipalmitate, sorbitan tripalmitate, sorbitan monomyristate, sorbitan dimyristate, sorbitan trimyristate, sorbitan monooleate, sorbitan dioleate, sorbitan trioleate, sorbitan esters with mixed C.sub.12-18 fatty acids and polyoxyethylene variants of the afore-mentioned sorbitan esters. Preferred is, inter alia, sorbitan tristearate. Commercially available compounds include, without limitation, Span 60, Span 65, Span 20 and Tween 60 available from Croda.

[0053] In a preferred embodiment the at least one nonionic surfactant is present in 0.01 to 1.0 wt.-%, preferably 0.02 to 0.5 wt.-%, more preferably 0.1 to 0.5 wt.-%, based on the total weight of the aqueous silane emulsion.

[0054] The emulsion of the present invention can optionally further comprise at least one acid d), preferably the at least one acid is an organic acid, more preferably having a pKa of 1.3-5.0. Suitable exemplarily acids are preferably selected from acetic acid, para-toluenesulfonic acid, benzenesulfonic acid, camphorsulfonic acid, malic acid, maleic acid, glyoxylic acid, citric acid, formic acid, pyruvic acid, tartaric acid, phthalic acid, acetylsalicylic acid, salicylic acid, lactic acid, dihydroxy fumaric acid, mandelic acid, malonic acid, glycolic acid and oxalic acid or combinations thereof, more preferably the at least one organic acid comprises malic acid or acetic acid or a combination thereof, more preferred is acetic acid.

[0055] In a preferred embodiment, the at least one acid is present in 0.5 to 1.5 wt.-%, preferably 1 to 1.5 wt.-%, most preferably 1 wt.-%, based on the total weight of the aqueous silane emulsion. In a further preferred embodiment, the at least one organic acid is present in 0.5 to 1.5 wt.-%, preferably 1 to 1.5 wt.-%, most preferably 1 wt.-%, based on the total weight of the aqueous silane emulsion, more preferably the at least one organic acid comprises malic acid or acetic acid or a combination thereof, more preferred is acetic acid.

[0056] In a preferred embodiment, the emulsion according to the present invention can optionally comprise at least one further additive e). In a more preferred embodiment the at least one further additive is selected from defoamers, buffering agents like sodium bicarbonate; amino silicones, wetting agents, crosslinking agents, extenders or combinations thereof. In a preferred embodiment the at least one additive is present in 0.1 to 2.5 wt.-%, preferably 0.1 to 2 wt.-%, more preferably in 0.1 to 1.8 wt.-%, based on the total weight of the aqueous silane emulsion. In a more preferred embodiment the emulsion according to the present invention comprises at least one defoamer, preferably in 0.01 to 0.5 wt.-% based on the total weight of the aqueous silane emulsion. Defoamers are known to the skilled person and any kind can be employed as long as they do not detrimentally influence the emulsion. Particularly suitable defoamers are based on vegetable oil, for example Tego Antifoam KS53 which is commercially available from Evonik. In a further preferred embodiment, the emulsion according to the present invention comprises at least one crosslinking agent or extender, preferably in 1.0 to 2.0 wt.-%, more preferably 1.5 wt.-%. Crosslinking agents are known to the skilled person and any kind can be employed as long as they do not detrimentally influence the emulsion. Particularly suitable crosslinking agents are condensation products of fatty acid/melamine commercially available from Tanatex under the tradename Baygard, Edolan also provided by Tanatex and the Tegomer range as offered by Evonik. In a preferred embodiment, the emulsion comprises at least one wetting agent.

[0057] The emulsions of the present invention can be prepared as concentrates and diluted with water before use. The respective concentrates can be at least 2-fold, preferably at least 3 or 4-fold, for example 8-fold or up to 10-fold concentrated. This means that the concentrations of the active components are at least twice or more of those indicated above and the amount of water is decreased accordingly. In such concentrates the concentration of the silane component can thus be 2- to 10-fold higher than indicated above, typically between 10 and 40 wt.-%, preferably between 18 and 40 wt.-%, relative to the total weight of the concentrate. The same applies to all other components, for example the anionic and the non-ionic surfactants. For example, the anionic surfactant can be present in 0.02 to 2.0 wt.-%, preferably 0.04 to 2.0 wt.-%, more preferably 0.05 to 2.0 wt.-% based on the total weight of the concentrate. In a preferred embodiment, a concentrate emulsion of the present invention comprises at least 40 wt.-%, preferably at least 60 wt.-%, of water, based on the total weight of the emulsion. In a further preferred embodiment 50 to 70 wt.-%, more preferably 55 to 58 wt.-% of water is present, based on the total weight of the concentrate emulsion. In a preferred embodiment the concentrate emulsion according to the invention has a pH-value of from 1 to 7.5, preferably 2 to 7, more preferably 6 to 7. In a preferred embodiment the non-ionic surfactant is present in the concentrate in amounts of 0.2 to 2.8 wt.-%, preferably 0.3 to 2.8 wt.-%, more preferably 0.35 to 2.8 wt.-%, based on the total weight of the concentrate emulsion.

[0058] The emulsions of the present invention can be employed to impregnate textiles, especially under industry standards pad application more commonly known as Foulard application, in order to obtain coatings which, confer water repellent characteristics to the treated fabrics. The emulsion according to the present invention is used for treating textiles, preferably polyamide, polypropylene or polyester textiles, more preferably polyester textiles, to obtain a water repellent coating on the textiles.

[0059] In a preferred embodiment, the coating obtained on the textile endures longer than 10, preferably 20 laundry cycles, preferably having a spraying rate of at least 70 (ISO 2), preferably 80 (ISO 3), more preferably 90 (ISO 4) after the last cycle. The spraying rate is determined according to DIN EN ISO 4920:2012-12. For this test three samples of the finished textiles sized minimum 180 mm180 mm are tested using a spray tester and a water volume of 250 mL de-ionised water. After spraying, the residual water is tapped off the surface and the sample is scored using the spray test rating standard.

[0060] Commonly known impregnation techniques can be employed in order to achieve the coating of the textile.

[0061] In particular the present invention provides a method of impregnating a textile, preferably a polyamide, polypropylene or polyester textile, more preferably a polyester textile, with an aqueous silane emulsion according to the present invention, comprising the steps: [0062] i) applying the aqueous silane emulsion via pad application onto the textile; [0063] ii) curing the treated textile obtained in step i).

[0064] In a preferred embodiment, the application speed of step i) is 0.5 m/min to 40 m/min, preferably 1m/min to 30m/min, in commercial applications typically 20-30 m/min, and/or the pressure used to apply the aqueous silane emulsion is 1 to 6 bar, preferably 1.5 to 3.5 bar.

[0065] In a further preferred embodiment, the curing temperature of step ii) is 130 to 170 C., preferably 150 to 160 C.

[0066] In the following examples are presented to illustrate the present invention. However, the present invention is not limited to those examples.

EXAMPLES

[0067] C8=Octyltriethoxysilane

[0068] SLS=Sodium lauryl sulfate

[0069] Water=Deionized water

[0070] Table 1 shows stable exemplarily compositions according to the present invention. The emulsions can be obtained by mixing the components with a homogenizer. The samples were aged over a period of 6 months at room temperature and exhibited little evidence of phase separation.

TABLE-US-00001 TABLE 1 Amounts are in wt.-%, wherein the sum is 100 wt.-% Example Water C8 SLS Observation 1 89.5 10 0.5 Milky while emulsion 2 89 10 1 Milky while emulsion 3 89.9 10 0.1 Milky while emulsion 4 89.95 10 0.05 Milky while emulsion

[0071] Table 2 shows a series of formulations that were prepared to investigate the influence of surfactant levels on stability and droplet size with increasing C.sub.8 levels. The droplet size of the formulations was measured by DLS (dynamic light scattering) at 90

TABLE-US-00002 TABLE 2 Amounts are wt.-%, wherein the sum is 100 wt.-% Example C8 SLS Water DLS 90 pH Observation 5 0 0.05 95.95 207.4 5.4 unstable 6 5 0.12 94.88 88.7 4.2 Stable 7 7 0.07 92.93 70.2 3.5 Stable 8 7 0.10 92.9 53.7 3.2 Stable 9 20 0.05 79.95 23 4.5 Slight layering 10 20 0.5 79.5 13.7 4.0 Stable Example 5 is a Comparative Example

[0072] The data displayed in Table 2 shows the appropriate balance of surfactant to organosilane to ensure a stabilized emulsified system. As the level of C.sub.8 increases, it can be seen that the level of surfactant also need to increase to ensure stability is possible. Moreover, the droplet size correlating to stability is within the range of 10-150 nm.

[0073] Below Table 3 shows performance tests with emulsified systems according to the present invention comprising organic acids which were applied via Pad application to two types of polyester.

[0074] Blue=woven polyester (120 gsm)

[0075] White=knitted polyester

[0076] Testing Conditions:

TABLE-US-00003 Pad coating speed 0.6 m/min and emulsion pressure 3.5 bar White Polyester Pad coating speed 5 m/min and 1.5 bar Rotofil 51 Stent curing of 5 mins @ 150 C.

[0077] Samples were then allowed to equilibrate at room temperature for a period of 24 hours before performance testing was conducted. Performance testing was conducted in accordance the Spray test as above-mentioned according to DIN EN ISO 4920:2012-12.

TABLE-US-00004 TABLE 3 Amounts are in wt.-%, wherein the sum is 100 wt.-%, except for values of the spray test. Spray Test Results after Malic Acetic Laundry Cycles @ 40 C. Example C8 SLS Water Acid Acid pH Fabric 0 1 5 10 20 11 2 0.05 95.44 2.5 1.6 White 0 80 80 80 80 12 5 0.05 91.45 3.5 1.9 White 80 80 80 80 80 5 0.05 91.45 3.5 1.9 Blue 70 70 70 70 50 13 5 0.05 94.7 0.25 2.2 White 80 80 90 80 80 5 0.05 94.7 0.25 2.2 Blue 0 80 70 70 70 14 7 0.05 92.7 0.25 2.2 White 80 90 80 90 80 7 0.05 92.7 0.25 2.2 Blue 0 70 70 70 70 Huntsman Phobol CP-C White 100 100 100 100 75 Blue 100 100 90 90 70 Archroma SmartRepel Hydro PM White 100 100 100 100 90 Blue 80 90 100 90 90

[0078] Huntsman Phobol CP-C is comprised of a fluorinated acrylate polymer, i.e. is PFC based. Archroma SmartRepel Hydro PM is a fluorine free composition and is similar in composition to the formulas claimed in WO 2016/000829 A1.

[0079] Compositions of the present invention were scaled up and manufactured at a Pilot level to ensure that stability could be achieved when moving from lab to larger scale.

[0080] An emulsion was prepared on a batch scale as a concentrate having the following composition

TABLE-US-00005 TABLE 4 Exemplary composition Components Wt.-% C8 20 SLS 1 Deionised Water 78.2 Defoamer 0.3 Sodium Bicarbonate 0.5 100

[0081] Preparation:

[0082] Vessel was charged with the deionized water, followed by the SLS, (C.sub.8) octyltriethoxysilane, defoamer and sodium bicarbonate. This was pre-homogenized for 30 minutes at room temperature. The pre-mix was added to the Ystral mixer and mixed for 10 minutes at 8000 rpm. The composition displayed in Table 4 was subsequently tested on a range of fabric types using various application conditions including Pad Speed, Pressure and curing temperatures.

[0083] Up-Formulation for Coating Application:

[0084] The concentrate, as displayed in Table 4, was further up-formulated prior to application. Table 5 shows the formulation set that was prepared and subsequently coated and tested on Polypropylene (Table 6), Polyamide (Table 7) and polyester (Table 8).

TABLE-US-00006 TABLE 5 Components Wt.-% Concentrate Table 4 25 Extender 1.5 Acetic Acid 1.0 Deionised Water 72.5

[0085] Table 6 shows performance tests with emulsions according, as formulated in Table 5, to the present invention comprising organic acids and Baygard 40178, the extender, which were applied via Pad Application on polypropylene. The cure time was always 300 seconds, the cure temperature 110 C., pad application speed of 5 m/m in and a pad application pressure of 1.5 bar. It can be clearly seen that the performance was exceptional after 20 laundry cycles.

[0086] Table 6 showing the performance rating on polypropylene

TABLE-US-00007 Spray Test Results after Laundry Cycles @ 40 C. Example 0 1 5 10 20 15 0 100 95 100 100 16 0 100 100 90 100 Archroma Smart Repel 0 90 100 90 80 Hydro PM

[0087] Example 15 employs the composition of Table 5 and Example 16 additionally contains wetting agent (0.1%).

[0088] Table 7 shows performance tests with emulsions according to the present invention comprising organic acids which were applied via pad Application on polyester. The cure time was 300 seconds at 150 C. and 180 seconds at 160 C., the cure temperature 150 C. (unless otherwise specified), pad application speed of 5 m/min and a pad application pressure of 1.5 bar. It can be seen that a higher application temperature of 160 C. and the presence of wetting agent has no impact on overall durability.

[0089] Table 7 showing the performance rating on polyester samples

TABLE-US-00008 Spray Test Results after Laundry Cycles @ 40 C. Example 0 1 5 10 20 17 0 100 100 100 100 18 0 90 100 100 100 19 (coated at 160 C.) 0 100 100 100 100 20 (coated at 160 C.) 0 100 100 100 90 Archroma Smart Repel 100 100 100 100 90 Hydro PM

[0090] Examples 17 and 19 employ the composition of Table 5 and Examples 18 and 20 additionally contain wetting agent (0.1%).

[0091] Comparative Example: Concentrate System Development

[0092] Table 8 shows comparative examples that were prepared utilising the balance of the anionic and non-ionic surfactant systems to create (a) a 40% concentrate, (b) stable emulsified systems and (c) performance after initial coating application. The preferred method of synthesis is through the inversion point method whereby the surfactants are dissolved in half of the oil (C8) followed by shear mixing for a period of 5 minutes. The remaining oil is added slowly under high shear until a gel is formed. The remaining ingredients are then added slowly, under shear, until the inversion point is reached as noticeable by a significant decrease in viscosity of the system.

TABLE-US-00009 TABLE 8 Amounts are in wt.-%, wherein the sum is 100 wt.-% Tween 60 Span 60 Span 65 (polyoxyethyelne (sorbitan (sorbitan sorbitan Sodium Example Water C8 SLS monostearate) tristearate) monostearate) Bicarbonate Observation 21 57.2 40 0.2 2.8 0 0 0.8 Stable emulsion 22 57.2 40 0.2 0 2.8 0 0.8 Stable emulsion 23 57.3 40 0.2 0 2 0.5 0.8 Stable emulsion

[0093] Up-Formulation for Coating Application:

[0094] The concentrates, as displayed in Table 8, were further up-formulated prior to application. Table 9 shows the diluted formulation details that were prepared and subsequently coated and tested on polyester (Table 10).

TABLE-US-00010 TABLE 9 highlighting dilution levels for all of the sample displayed in Table 8 Components Wt.-% Concentrate Table 8 12.5 Extender 1.5 Acetic Acid 1.0 Deionised Water 85.5

[0095] Table 10 shows performance tests with emulsions according, as formulated Table 9, to the present invention comprising organic acids and Baygard 40178 (extender), which were applied via Pad Application on polyester. The cure time was always 300 seconds with a cure temperature of 160 C. It can clearly be seen by altering the surfactant system to contain a lower amount of the sodium lauryl sulfate that 0 wash performance (i.e. performance after 0 wash cycles, i.e. directly after treatment/application) is obtainable. This is most prominent for sample 22 which contains Span 65 (sorbitan tristearate).

TABLE-US-00011 TABLE 10 Wash Cycles Sample 0 1 5 10 21 80 100 100 100 22 90 100 100 100 23 80 100 100 100