MULTI-STAGE WATER FILTRATION SYSTEM

Abstract

The invention provides a water filtration system for removing heavy metals, residual chlorine, estrogens, bacteria and dust from tap water. The system includes a first adsorbent stage cartridge including approximately 40-65 wt. % of silver-impregnated activated carbon, approximately 1-10 wt. % of activated alumina, approximately 15-35 wt. % of ceramic balls, approximately 0.5-1 wt. % of chitosan and approximately 0.5-1 wt. % of kinetic degradation fluxion media. The second filtration stage cartridge includes an antifouling electrospun nanofiber membrane. A flow path is provided between the first adsorbent stage cartridge and the second filtration stage cartridge. The multiple stage water filtration system is capable of filtering water at a volume rate of at least approximately 2 liters per minute. In one embodiment, the nanofibers may be polyvinylidene fluoride doped with polyacrylonitrile and including bacteria-repellent methoxy polyethylene glycol side chains such that the nanofiber membrane has a water contact angle of approximately 55 degrees or less.

Claims

1. A multiple stage water filtration system for purifying tap water, the water filtration system comprising: a first adsorbent stage cartridge including approximately 40-65 wt. % of silver-impregnated activated carbon, approximately 1-10 wt. % of activated alumina, approximately 15-35 wt. % of ceramic balls, approximately 0.5-1 wt. % of chitosan and approximately 0.5-1 wt. % of kinetic degradation fluxion media that includes zinc and brass; a second filtration stage cartridge including an antifouling electrospun nanofiber membrane, the nanofibers having a diameter from approximately 100 nanometers to 1 micron; a flow path provided between the first adsorbent stage cartridge and the second filtration stage cartridge; the multiple stage water filtration system being capable of filtering water at a volume rate of at least approximately 2 liters per minute.

2. The water filtration system of claim 1, wherein the electrospun nanofiber membrane comprises a polyvinylidene fluoride base material, the base material being doped with polyacrylonitrile and including bacteria-repellent methoxy polyethylene glycol side chains such that the nanofiber membrane has a water contact angle of approximately 55 degrees or less.

3. The water filtration system of claim 1, wherein a water filtration pathway is from the first adsorbent stage cartridge to the second filtration stage cartridge.

4. The water filtration system of claim 2, wherein the electrospun nanofiber membrane is produced by electrospinning a solution of 5-15 wt. % of polyvinylidene fluoride, 0.1-1.0 wt. % of polyacrylonitrile, and 0.01-0.1 wt. % of lithium chloride (LiCl) in a dimethylformamide (DMF) solvent.

5. The water filtration system of claim 1, wherein the filters are configured to remove heavy metals, inorganic pollutants, bacteria and particulates.

6. The water filtration system of claim 5, wherein said heavy metals comprise one or more of cadmium, chromium, lead, barium, or arsenic.

7. The water filtration system of claim 5, wherein said inorganic pollutants comprise nitrates and fluorides.

8. The water filtration system of claim 5, wherein said bacteria comprise E. coli.

9. The water filtration system of claim 1, wherein the filtration system capacity is at least 6,000 liters.

10. The water filtration system of claim 1, system is configured to remove water impurities up to 99.99%.

11. The water filtration system of claim 1, wherein a water output purity conforms to WHO drinking water standards.

12. The water filtration system of claim 1, further comprising one or more total dissolved solids sensors.

13. The water filtration system of claim 12, wherein a first total dissolved solids sensor is positioned to measure the total dissolved solids at a water inlet and a second total dissolved solids sensor is positioned to measure the total dissolved solids at a water outlet.

14. The water filtration system of claim 13, further comprising a communication module to communicate total dissolved solids information to an external computing device.

15. The water filtration system of claim 14, wherein the external computing device is a mobile phone.

16. The water filtration system of claim 15, wherein the mobile phone includes a computer program that displays the total dissolved solids content and notifies a user when it is time to change a water filtration system cartridge.

17. The water filtration system of claim 1, wherein the nanofibers have a diameter from 200-600 nm.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] FIG. 1A-1B schematically depict a water filtration system according to an embodiment of the present invention.

[0016] FIG. 2 depicts a cartridge of the water filtration system of FIG. 1.

[0017] FIGS. 3A-3B depict electrospun nanofibers for use in the water filtration system of FIG. 1.

[0018] FIGS. 4A-4B depict electrospun nanofibers for use in the water filtration system of FIG. 1.

[0019] FIGS. 5A-5B depict electrospun nanofibers for use in the water filtration system of FIG. 1.

[0020] FIGS. 6A-B depict the water contact angle for the electrospun nanofibers of the water filtration system of FIG. 1.

[0021] FIG. 7 is a plot a wavelength vs. absorbance for influent and filtered effluent demonstrating the filtration of particulates.

[0022] FIG. 8 is a plot of wavelength vs. absorbance for influent and filtered effluent demonstrating the filtration of particulates.

[0023] FIG. 9 depicts a printed circuit board for a TDS sensor for the water filtrations system of FIG. 1.

[0024] FIG. 10 depicts a mobile phone display of an application showing the readings of the TDS sensor of FIG. 9.

DETAILED DESCRIPTION

[0025] Turning to the drawings in detail, FIGS. 1A-1B depict a water filtration system 100 according to an embodiment of the present invention. In the embodiment of FIG. 1, the water filtration system 100 includes at least two cartridges, cartridges 130 and 140, that are two stages of the water filtration system. The cartridges may be positioned within a housing 110; optionally, as will be discussed in further detail below, the housing 110 may include an indicator region 120 which may include status indicators concerning water quality and the need to change one or more filter cartridges. Although not shown in FIGS. 1A-1B, the water filtration system 100 may include adapters to allow the system to be positioned at the output of a household water tap; this may include a diverter valve to allow the user to select between filtered and unfiltered water. Alternatively, the water filtration system 100 may be installed in a water line upstream of a water faucetfor example in an under sink installation. When installed under the sink, the water filtration system of 100 may be made larger with a higher filtration capacity. In such an embodiment, the water filtration system may supply a separate filtered-water tap or may be in the water line for the main tap.

[0026] The two-stage water filtration system 100 of FIGS. 1A-1B includes a first stage optimized to remove trace heavy metals, residual chlorine, and pharmaceuticals such as estrogens etc. The second stage is optimized to remove bacteria, rusts and small particles, significantly reducing water turbidity.

[0027] FIG. 2 schematically depicts a first stage cartridge, 130. In the first stage, adsorbent media 160 is included, in loose, particulate form. The adsorbent media includes approximately 40-65 wt. % of silver-impregnated activated carbon, approximately 1-10 wt. % of activated alumina, approximately 15-35 wt. % of ceramic balls, approximately 0.5-1 wt. % of chitosan and approximately 0.5-1 wt. % of kinetic degradation fluxion media. The materials may be mixed together as separate components, or one or more components may be mixed with each other and formed into particles. Optionally, all of the media may be combined and formed into a porous shaped solid with a binder phase.

[0028] FIGS. 3A-3B depict a membrane of the second stage filter cartridge. The membrane is a non-woven mat of nanofibers. In one embodiment, the non-woven mat of nanofibers may be an electrospun mat of nanofibers formed on a substrate. The substrate may itself be a mat of non-woven fabric such as a mat of polyethylene terephthalate (PET). The electrospun nanofibers may be polyvinylidene fluoride (PVDF) nanofibers. As will be discussed in further detail in the examples below, to enhance the wetting angle of the PVDF fibers and increase the antifouling capacity of the membrane, the PVDF fibers may be doped with a small amount of a wetting-enhancing dopant. The dopant may be polyacrylonitrile (PAN). To enhance the ability of the membrane to repel bacteria, methoxy polyethylene glycol side chains may further be introduced to the fibers. The nanofibers of the membrane are engineered such that the water contact angle is approximately 55 degrees or less (water contact angle and wetting angle are used interchangeably herein as water contact angle is a measure of wettability).

[0029] The electrospinning technique used to form the PVDF-based nanofibers creates the desirable filtration properties of the cartridge material. In one embodiment, the electrospinning technique is from a precursor solution including 5-15 wt. % PVDF, 0.1-1.0 wt. % of PAN and 0.01-0.1 wt. % of lithium chloride (LiCl) in a dimethylformamide (DMF) solution. When enhanced antifouling properties are desired, the electrospinning solution further includes 0.1-5 wt. % of methoxypolyethylene glycol (mPEG).

[0030] With the combination of the two cartridges, the two-stage water filtration system 100 removes pollutants in tap water can be removed up to 99.99% at a flow rate of at least approximately 2.0 L/min with a filtration capacity of at least approximately 6,000 liters of water.

[0031] Water quality is significantly variable in different geographic regions; even within the same household, the water quality may vary considerably throughout different seasons of the year (e.g., rainy season vs. dry season). As a result, volume sensors to indicate that cartridge media need to be replaced are inadequate to ensure water quality. For example, water with a higher quantity of pollutants may require more frequent replacement of filtering media. Similarly, water with low levels of pollutants may require considerably less frequent replacement of filtering media. To this end, the water filtration system of the present invention may optionally incorporate a total dissolved solids (TDS) sensor and, optionally, a total volume counter. An exemplary circuit board including an inlet TDS 210, an output TDS 220, and a volume meter 230 is depicted in FIG. 9.

[0032] The total dissolved solids are the combined inorganic and organic impurities in a water supply. These solids may be in dissolved form (molecular or ionized) or suspended in the water. A TDS meter measures an electrical charge generated by these impurities; the charge is measured between a pair of electrodes immersed in water. If there are no soluble materials in the water, the water will not indicate a charge and the impurity content will be zero parts per million (0 ppm). When various substances are present in the water the conductivity increases and this increase in conductivity can be converted into a parts per million figure for impurities.

[0033] The TDS meter readings may be shown on the display region 120 of the water filtration system 100. However, a raw number indicating an impurity content may not provide enough information to the user regarding whether the output water is safe to drink or whether it is time to change one or more of the filter cartridges. To this end, the TDS meter readings may optionally be sent to an external data processing device such as a computer or mobile phone. The data processing device may include an application that relates the TDS meter readings, either individually or historically, to the need to change the filtration media. The raw TDS number in ppm may be displayed and, based on historical readings, the calculated remaining lifetime of the filter cartridges may be displayed. The use may be notified that it is time to replace the filter cartridges when the TDS readings consistently fall below a predetermined level.

EXAMPLES

Example 1 Adsorbent Cartridge

[0034] 40-65 wt. % of silver-impregnated activated carbon, 1-10 wt. % of activated alumina, 15-35 wt. % of ceramic balls, 0.5-1 wt. % of chitosan and 0.5-1 wt. % of KDF 55 were well mixed before packing into the cartridge. FIG. 2 schematically depicts the well mixed adsorbent media in the adsorbent cartridge.

Example 2 PVDF Nanofiber Membrane

[0035] 5 wt %-15 wt % of PVDF was dissolved in DMF. The polymer solution was loaded into an electrospinning system in which electrospinning of the polymer solution was performed under the following condition to form a polymer nanofiber membrane on a PET nonwoven fiber mat. For the electrospinning process, the working range of the applied voltage is 30-80 kv; the working range of the distance is 10-30 cm and the working range of the solution flow rate is 2-20 ml/h. The SEM image of the resultant PVDF nanofiber membrane is shown in FIGS. 3A-3B.

Example 3 Modified PVDF Nanofiber Membrane with Addition of PAN and LiCl

[0036] In another aspect of the invention, a PVDF nanofiber membrane was fabricated with a further modification of adding 0.1-1.0 wt. % PAN and 0.01-0.1 wt. % LiCl. The modified solution was electrospun at an applied voltage of 30-80 kv; a distance of 10-30 cm and solution flow rate of 2-20 ml/h. The SEM image of the modified PVDF nanofiber membrane with addition of PAN and LiCl is shown in FIGS. 4A-4B.

Example 4 Integration of an Antifouling Function by Introducing mPEG

[0037] By further introducing 1-5% of mPEG into the solution, methoxy-terminated PEG side chains were introduced in the nanofiber. An electrospinning process using the solution described above, with or without PAN and LiCl (with the addition of 1-5% mPEG), the working range of the applied voltage is 30-80 kv; the working range of the distance is 10-30 cm and the working range of the solution flow rate is 2-20 ml/h. The SEM image of an anti-fouling PVDF-PAN-mPEG nanofiber is shown in FIGS. 5A-5B; an anti-fouling test result is shown in Table 1.

TABLE-US-00001 TABLE 1 Comparison of Anti-fouling performance by the untreated and mPEG treated nanofiber membrane Untreated mPEG treated sample sample Logarithmic Logarithmic value of value of viable cell viable count (after cell count Antibacterial Bacteria 24-hour (after 24-hour activity inoculated incubation) * incubation) * (R)# Escherichia coli 3.39 0.204 3.595 (ATCC 25922) Notes: The value of antibacterial activity (R) must be equal to or greater than 2; The inoculated count of Escherichia coli on the untreated sample was 2,400 CFU/cm.sup.2.

Example 5 Water Contact Angle of PVDF-PAN-mPEG Antifouling Nanofiber

[0038] A PVDF-PAN-mPEG antifouling membrane was cut into 35 cm rectangular plate. The plate was amounted on the sample stage of contact angle goniometer. Water droplets were generated from a flat tip needle connected with a micrometer-controlled syringe. The volume of the water droplet is accurate to 1 L. When the water droplet emerges, the sample stage is raised to adhere the water droplet to the membrane surface. The contact angle was measured through a CCD camera image programmed to determine the boundary of the water droplet and the fiber. The software imitates the outline of water droplet through the CCD camera image the droplet on the fiber to give the contact angle. The image of a water contact angle for a PVDF fiber is shown in FIG. 6A; the angle is 144.6 degrees. As seen in FIG. 6B, the contact angle for the PVDF-PAN-mPEG antifouling membrane was measured to be 51.3 degrees showing the enhanced wetting properties of the doped fiber.

Example 6 Water Purification by the Two-Stage Water Filter

[0039] The two cartridges are packed together as the water filter system of FIGS. 1A-1B in the sequence of adsorbent cartridge followed by membrane cartridge. The system of FIGS. 1A-1B is particularly suited for tap water filtration; the system may be place on the faucet itself or on the countertop or in under-sink placement and attachment to an outlet of a faucet.

Example 7 Removal Performance of the Two-Stage Water Filter at 2.5 L/Min

[0040] The system of Example 6 is provided using a first stage filter of a cartridge filled with mixture of silver-impregnated activated carbon, activated alumina, ceramic balls, chitosan and KDF 55, and a second stage membrane cartridge with PVDF-PAN-mPEG nanofiber membrane. Five liters of water containing different pollutants is filtered through the system. The flow rate of the system is set to 2.5 L/min by the pump supplying the water. The initial concentrations of the different pollutants in the water sample are listed in Table 2. The removal efficiency of filtering system at 2.5 L/min is shown in Table 3.

TABLE-US-00002 TABLE 2 Initial concentrations of various pollutants. Concentration (mg/L) Heavy Lead 0.15 Metal Cadmium 1 Removal Arsenic 0.05 Barium 10 Chromium 0.3 Inorganic NO.sub.3.sup. as N 27 Removal F.sup. 8 Bacterial E.Coli 10.sup.5 CFU/L

TABLE-US-00003 TABLE 3 Removal efficiency of the filtration system at 2.5 L/min. Removal efficiency Testing Capacity (L) 5 Flow Rate (L/min) 2.5 Heavy Lead >99% Metal Cadmium 96% Removal Arsenic >80% Barium >95% Chromium 92% Inorganic Nitrate as NO.sub.3.sup. 79% Removal F.sup. 86% Bacterial E. Coli >99.99%

[0041] The filtration system demonstrates excellent removal performance of heavy metals, inorganic pollutants and bacteria. The effluent concentrations achieved the level recommended by the WHO drinking water guidelines. The mixture of activated carbon, ceramic balls, activated alumina, chitosan and KDF55 can remove most heavy metals and around 80% of other inorganic pollutants. The mPEG-modified nanofiber membrane removed over 99.99% of E. Coli with no clogging or significant decrease of flow rate being observed during filtration.

Example 8 Removal Performance of 0.6 m Polystyrene Beads by the Water Filter at 2.5 L/Min

[0042] Five liters of water including 10 ppm of 0.6 m polystyrene beads were filtered by the filtration system to assess the capability of removing particulates. The turbid influent with the beads became clear following filtration using the system of FIGS. 1A-1B. The absorbance of 0.6 m polystyrene beads is at 308 nm. UV-vis spectroscopy in FIG. 7 shows that more than 99% of the 0.6 m polystyrene beads were filtered by the filtration system.

Example 9 Removal Capacity of the Filtering System, 6,000 L Challenging Water at 2.5 L/Min Flow Rate

[0043] A total of 6,000 L of challenging water was filtered by the filtering system. The daily load of challenging influent is 400 L, it was prepared daily with a base of deionized water having the spiked concentrations listed in Table 4 below:

TABLE-US-00004 TABLE 4 Spiked concentration of influent Parameter Influent Conc. Lead 0.15 mg/L Chlorine 2 mg/L Estrone 140 ng/L

[0044] The filter system is conditioned with 100 L deionized water, total loading of 6,000 L influent (400 L per day) is applied to the filter at 2.5 L/min (30 psi). Influent and effluent samples were taken at 25% (1500th L), 50% (3000th L), 75% (4500th L) and 100% (6,000th L) loading. The filter system can effectively remove the pollutants in Table 3 for 6,000 L, the results of the removal efficiency are shown in Table 5.

TABLE-US-00005 TABLE 5 Removal efficiency of the water filter for 6,000 L challenging water at 2.5 L/min 1500 L 3000 L 4500 L 6,000 L Spiked 25% 25% 50% 50% 75% 75% 100% 100% Influent Loading Loading % Loading Loading % Loading Loading % Loading Loading % Analyte Conc. Before After Removal Before After Removal Before After Removal Before After Removal Lead, ug/L 150 127.2 3.9 97 121.2 3.3 97 142.5 3 98 135.5 2.4 98 Chlorine, 2 2.2 <0.1 >95 2.2 <0.1 >95 2.2 <0.1 >95 2.1 <0.1 >95 mg/L Estrone, 140 150 <10 >90 130 <10 >90 140 <10 >90 130 <10 >90 ng/L

Example 10 Removal Performance of 0.6 m Polystyrene Beads of the Water Filter at 2.5 L/Min after 6,000 L Filtration of Challenging Water

[0045] After filtering 6,000 L of challenging water with contaminants, the filtration system was further tested for the removal performance of 0.6 m polystyrene beads. The filtering system was conditioned with 50 L DI water; 10 L water containing 10 ppm of 0.6 m polystyrene beads was then pumped through the filtering system. More than 99% of beads were removed by the filtering system; the UV-vis spectra demonstrating the removal are shown in FIG. 8.

Example 11 Water Quality and Use of the Water Filter Monitored by Mobile Application

[0046] The water filter is equipped with a TDS sensor and total volume counter and is connected via WI-FI to mobile phone to permit users to monitor the water quality and the use of water through a mobile application. Two TDS sensors, as seen in FIG. 9, show the dissolved solids content at the input and the output of the filtration system. The volume of daily use and total use of water filtered by the filtration system is displayed in the mobile application. Notifications are sent to the user's mobile phone when the filter cartridges need to be changed; a mobile phone display using the mobile application is depicted in FIG. 10.

[0047] It should be apparent to those skilled in the art that many modifications besides those already described are possible without departing from the inventive concepts herein. The inventive subject matter, therefore, is not to be restricted except in the spirit of the disclosure. Moreover, in interpreting the disclosure, all terms should be interpreted in the broadest possible manner consistent with the context. In particular, the terms includes, including, comprises and comprising should be interpreted as referring to elements, components, or steps in a non-exclusive manner, indicating that the referenced elements, components, or steps may be present, or utilized, or combined with other elements, components, or steps that are not expressly referenced.