Corona Shielding Material With An Adjustable Resistance

Abstract

The present disclosure relates to a corona shielding material. The teachings thereof may be embodied in a material with an adjustable resistance and/or a corona shielding system which comprises an overhang corona shielding system (OCS). In some embodiments, a corona shielding material may include: a matrix; and a filler comprising doped and undoped particles in a given size fraction. A resistance of the corona shielding material is set by a concentration of doped particles in the filler particle size fraction.

Claims

1. A corona shielding material comprising: a matrix; and a filler comprising doped and undoped particles in a given size fraction; wherein a resistance of the corona shielding material is set by a concentration of doped particles in the filler particle size fraction.

2. The corona shielding material as claimed in claim 1, the filler includes SiC particles.

3. The corona shielding material as claimed in claim 1, wherein the filler comprises SiC particles in a particle size of SiC1000, SiC800, SiC600, or SiC400.

4. The corona shielding material as claimed in claim 1, wherein the matrix includes a polymeric resin.

5. The corona shielding material as claimed in claim 1, wherein the filler comprises above 40% by weight of a total weight of the corona shielding material.

6. The corona shielding material as claimed in claim 1, wherein the filler includes particles with a globular form.

7. The corona shielding material as claimed in claim 1, wherein the corona shielding material comprises part of an overhang corona shielding system.

8. An electrical machine comprising: a corona shielding system including: a matrix; and a filler comprising doped and undoped particles in a given size fraction; wherein a resistance of the corona shielding material is set by a concentration of doped particles in the filler particle size fraction.

9. An electrical machine as claimed in claim 8, wherein the electrical machine comprises a high-voltage machine.

10. The electrical machine as claimed in claim 8, wherein the corona shielding system includes: an inner potential grading or an external corona shielding; and an overhang corona shielding.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIG. 1 shows a prior art system wherein a cross section through a sliding arrangement at the end of a generator winding bar without OCS with sketched nonlinear potential reduction is schematically illustrated;

[0020] FIG. 2 shows the same sliding arrangement as FIG. 1 only with an overhang corona shielding (OCS) 7 at the end of a generator winding bar; and

[0021] FIG. 3 shows a curve in which the mass fractions of doped SiC in the particle mixture of a corona shielding material are plotted against the square resistance in ohms.

DETAILED DESCRIPTION

[0022] Known system may suffer a first disadvantage in the complicated doping for setting the electrical resistance. A second disadvantage may require different particle sizes for setting a desired resistance in the OCS. A particle mixture containing different particle sizes is not particularly storage stable because it easily separates owing to the different particle sizes. Therefore, mixing is not performed in practice since it would be too complicated and therefore too expensive to store the mixtures in a stable fashion. There are therefore, for example, 4 fillers with different fraction sizes and respective doping. Therefore, resistances per unit length which cover the relevant regions can be produced point by point.

[0023] The teachings of the present disclosure may provide a resistance per unit length for a corona shielding system with a filler, in which the resistance can be set in an exact, cost-effective and simple manner. Accordingly, a corona shielding material may comprises a matrix and filler particles in a fraction, that is to say a particle size distribution, wherein the resistance in the corona shielding material can be set by the concentrations of doped particles in the filler particle fraction.

[0024] The resistance in the corona shielding material is influenced by the filler. In known systems, the desired resistance has been produced firstly by different particle sizes and secondly by different concentrations of doped particles in the corona shielding material. According to the teachings herein, a resistance in the corona shielding material can be set solely with a particle size of filler particles, solely by varying the concentration of doped particles within the fraction.

[0025] The filler is formed with particles with dimensions of, at least on (in particular arithmetic) average, that is to say a particle size distribution, of at most one millimeter e.g., of, at least on (particular arithmetic) average, at most 100 micrometers. The filler may comprise partial discharge-resistant and electrically conductive and/or semiconducting particles, such as silicon carbide. The particles may comprise a partial discharge-resistant core and a partial discharge-resistant coating which is conductive.

[0026] In a corona shielding system, the filler may comprise globular and/or planar particles. Globular particles include those particles in which the dimensions in different spatial directions differ by less than a factor of at most 3, e.g., at most 1.5. Planar particles include those particles of which the dimensions in at least one spatial direction differ by a factor of at least 3, e.g., at least 5, from the dimensions in a direction and/or two directions, perpendicular thereto. Owing to the deliberate mixing of doped and undoped filler particles of the same particle size distribution, it is possible to cover a resistance range of more than one decade when the particle mixtures are incorporated into a corresponding matrix.

[0027] In some embodiments, the filler is present in the corona shielding material in a quantity of more than 40% by weight, in particular more than 50% by weight, in a quantity of more than 70% by weight and/or in a quantity of more than 80% by weight. The resistance in the corona shielding material drops as the content of doped filler increases. A resistance which is customized for field control of an electrical machine can be set by mixing the doped and undoped filler.

[0028] The filler fractions used are, for example, the commercially available particle sizes of, for example, SiC400, SiC600, SiC800 and SiC1000. Here, the number following the material designation “SiC” for silicon carbide represents the number of particles per unit area. Therefore, SiC400 describes larger particles than SiC1000.

[0029] As the size of the particle fraction increases, larger particles on average, a lower resistance is generated in the corona shielding material, and vice versa. This is explained by the number of contact resistances between two particles, wherein this number increases with smaller particles, as does the resulting resistance. To cover the required resistance range of a corona shielding system such as an overhang corona shielding system, particle sizes such as SiC400, SiC600, SiC800 and SiC1000 may be used. In case of SiC1000, the dimensions of the particles are approximately 40 μm on average, with a minimum of approximately 4 μm and a maximum of approximately 50 μm.

[0030] For the initial range, SiC is also sometimes mixed with carbon black, in order to lower the resistance. The particles may be doped with aluminum or boron.

[0031] In some embodiments, the corona shielding system further comprises a support such as a belt and/or a fabric. In some embodiments, at least a portion of the corona shielding material forms a belt and/or a coating in the case of the corona shielding system.

[0032] In some embodiments, the corona shielding material comprises a matrix, for example a polymeric matrix, e.g., a plastic matrix and/or a resin. The polymeric matrix may comprise a thermoplastic and/or a thermoset and/or an elastomer.

[0033] In some embodiments, the corona shielding material has an electrical resistance which becomes lower the greater an electrical operating field of the electrical machine in which the corona shielding material, during operation, is located.

[0034] In some embodiments, OCS corona shielding materials which cover 2 decades of resistances can be produced solely by two filler fractions.

[0035] FIG. 3 shows a curve in which the mass fractions of doped SiC in the particle mixture of a corona shielding material are plotted against the square resistance in ohms. Said curve exhibits a profile which is linear within the measurement accuracies with an increasing proportion of undoped SiC in the particle mixture the resistance in ohms also arises. It is shown here that the electrical resistance can be set in nuances according to the teachings herein, e.g., to set virtually any desired resistance value in the corona shielding material by varying the quantity of doped particles.

[0036] In some embodiments, the set mixtures are storage-stable to a virtually unlimited extent because the fundamental uniformity of the particle size prevents separation into relatively large and relatively small particle fractions over relatively long-term storage. Therefore, a reproducible electrical resistance per unit length is produced.

[0037] In some embodiments, there is a corona shielding material for a corona shielding system which comprises an overhang corona shielding system (OCS). Here, a corona shielding material is introduced in which the filler is present in a single particle size fraction, embedded in a matrix, and a desired electrical resistance can be set.