LIGHT-ABSORBING COMPOSITION AND OPTICAL FILTER
20200270455 · 2020-08-27
Inventors
Cpc classification
C08K5/56
CHEMISTRY; METALLURGY
International classification
Abstract
A light-absorbing composition according to the present invention contains a light absorber formed by a particular phosphonic acid and copper ion and an alkoxysilane monomer for dispersing the light absorber, and does not contain a phosphoric acid ester having a polyoxyalkyl group. The light-absorbing composition contains the alkoxysilane monomer in such a manner that a normalized transmittance spectrum has a wavelength band in which the spectral transmittance is 70% or more in a wavelength range from 300 nm to 700 nm and the difference between the maximum value and the minimum value of the wavelength in the wavelength band is 100 nm or more.
Claims
1. A light-absorbing composition comprising: a light absorber formed by a phosphonic acid represented by the following formula (a) and copper ion; and an alkoxysilane monomer for dispersing the light absorber, wherein the light-absorbing composition does not contain a phosphoric acid ester having a polyoxyalkyl group, the light-absorbing composition contains the alkoxysilane monomer in such a manner that a normalized transmittance spectrum has a wavelength band in which a spectral transmittance is 70% or more in a wavelength range from 300 nm to 700 nm and a difference between a maximum value and a minimum value among wavelengths in the wavelength band is 100 nm or more, and the normalized transmittance spectrum is obtained by normalizing a transmittance spectrum such that a spectral transmittance at a wavelength of 700 nm is 20%, the transmittance spectrum being obtained when light having a wavelength from 300 nm to 1200 nm is perpendicularly incident on a light-absorbing layer that is formed by subjecting a film formed of the light-absorbing composition to a drying treatment and a humidifying treatment: ##STR00004## where R.sub.11 is an alkyl group, an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom.
2. The light-absorbing composition according to claim 1, wherein the alkoxysilane monomer comprises an alkyl group-containing alkoxysilane monomer represented by the following formula (b):
(R.sub.2).sub.nSi(OR.sub.3).sub.4-n (b) where R.sub.2 is an alkyl group having 1 to 4 carbon atoms, R.sub.3 is an alkyl group having 1 to 8 carbon atoms, and n is an integer of 1 to 3.
3. The light-absorbing composition according to claim 2, wherein the phosphonic acid comprises a phosphonic acid represented by the formula (a) where R.sub.11 is an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom, the alkoxysilane monomer comprises the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 and a tetrafunctional alkoxysilane monomer represented by the formula (c), and a ratio of a content of the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 to a content of the copper ion is 2.5 or more on an amount-of-substance basis:
Si(OR.sub.4).sub.4 (c) where R.sub.4 is an alkyl group having 1 to 8 carbon atoms.
4. An optical filter comprising: a light absorbing layer that contains a light absorber formed by a phosphonic acid represented by the following formula (a) and copper ion and a hydrolysis-polycondensation product of an alkoxysilane monomer and does not contain a phosphoric acid ester having a polyoxyalkyl group, wherein a normalized transmittance spectrum has a first wavelength band in which a spectral transmittance is 70% or more in a wavelength range from 300 nm to 700 nm and a difference between a maximum value and a minimum value among wavelengths in the first wavelength band is 100 nm or more, and the normalized transmittance spectrum is obtained by normalizing a transmittance spectrum such that the spectral transmittance at a wavelength of 700 nm is 20%, the transmittance spectrum being obtained when light having a wavelength from 300 nm to 1200 nm is perpendicularly incident on the optical filter: ##STR00005## where R.sub.11 is an alkyl group, an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom.
5. The optical filter according to claim 4, wherein the normalized transmittance spectrum has a second wavelength band in which the spectral transmittance is 80% or more in the wavelength range from 300 nm to 700 nm and a difference between a maximum value and a minimum value among wavelengths in the second wavelength band is 40 nm or more.
6. The optical filter according to claim 4, wherein the normalized transmittance spectrum has a third wavelength band in which the spectral transmittance is 20% or less in a wavelength range from 700 nm to 1200 nm and a difference between a maximum value and a minimum value among wavelengths in the third wavelength band is 120 nm or more.
7. The optical filter according to claim 4, wherein the normalized transmission spectrum has a fourth wavelength band in which the spectral transmittance decreases with an increase in wavelength and a fifth wavelength band that includes a wavelength shorter than a minimum wavelength in the fourth wavelength band and in which the spectral transmittance increases with an increase in wavelength, a first cut-off wavelength at which the spectral transmittance is 50% in the fourth wavelength band is present in a wavelength range from 600 nm to 650 nm, a second cut-off wavelength at which the spectral transmittance is 50% in the fifth wavelength band is present in a wavelength range from 350 nm to 420 nm, and a difference obtained by subtracting the second cut-off wavelength from the first cut-off wavelength is 200 nm to 290 nm.
8. The optical filter according to claim 4, wherein, in the normalized transmittance spectrum, a maximum wavelength at which a maximum spectral transmittance is found is present in a wavelength range from 500 nm to 550 nm and a minimum wavelength at which a minimum spectral transmittance in a wavelength range from 700 nm to 1200 nm is found is present in a wavelength range from 750 nm to 900 nm, and a difference obtained by subtracting the maximum wavelength from the minimum wavelength is from 240 nm to 360 nm.
9. The optical filter according to claim 4, wherein, in the normalized transmittance spectrum, a difference obtained by subtracting a minimum spectral transmittance in a wavelength range from 700 nm to 1200 nm from a maximum spectral transmittance in the normalized transmittance spectrum is 68% or more.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0019]
[0020]
[0021]
[0022]
[0023]
[0024]
[0025]
[0026]
[0027]
[0028]
[0029]
[0030]
[0031]
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
DESCRIPTION OF EMBODIMENTS
[0040] The inventor of the present invention considered that the phosphoric acid ester used in the technique described in Patent Literature 1 is not an optimum material in terms of weather resistance because the phosphoric acid ester has a polyoxyalkyl group and thus is hydrolyzed easily when exposed to water. In the technique described in Patent Literature 1, if a sufficient amount of resin is present with the near-infrared absorber, the weather resistance of the near-infrared cut filter is expected to reach a satisfactory level. This, however, requires a relatively large amount of resin. On this account, the inventor also considered that the near-infrared cut filter according to the technique disclosed in Patent Literature 1 tends to have a large thickness. In light of the foregoing, the inventor conducted in-depth studies to find a novel material suitable for dispersing a light absorber formed by a particular phosphonic acid and copper ion. As a result, the inventor newly found that proper dispersion of a light absorber can be achieved using an alkoxysilane monomer, without using a phosphoric acid ester having a polyoxyalkyl group. On the basis of this new finding, the inventor developed the light-absorbing composition and the optical filter according to the present invention.
[0041] Hereinafter, embodiments of the present invention will be described with reference to the drawings. The following description is directed to some examples of the present invention, and the present invention is not limited by these examples.
[0042] The light-absorbing composition according to the present invention contains a light absorber and an alkoxysilane monomer. The light absorber is formed of a phosphonic acid represented by the following formula (a) and copper ion. The alkoxysilane monomer disperses the light absorber. In addition, the light-absorbing composition does not contain a phosphoric acid ester having a polyoxyalkyl group. The light-absorbing composition contains the alkoxysilane monomer in such a manner that a normalized transmittance spectrum has a wavelength band in which the spectral transmittance is 70% or more in a wavelength range from 300 nm to 700 nm and the difference between the maximum value and the minimum value among wavelengths in this wavelength band is 100 nm or more. In other words, the type and the amount of the alkoxysilane monomer in the light-absorbing composition are determined in such a manner that the normalized transmittance spectrum has a wavelength band in which the spectral transmittance is 70% or more in a wavelength range from 300 nm to 700 nm and the difference between the maximum value and the minimum value of the wavelength in this wavelength band is 100 nm or more. With this configuration, an optical filter produced using the light-absorbing composition is likely to have desired optical properties. The normalized transmittance spectrum is obtained by normalizing a transmittance spectrum such that a spectral transmittance at a wavelength of 700 nm is 20%. The transmittance spectrum is obtained when light having a wavelength from 300 nm to 1200 nm is perpendicularly incident on a light-absorbing layer that is formed by subjecting a film formed of this light-absorbing composition to a drying treatment and a humidifying treatment.
##STR00003##
In the formula, R.sub.11 is an alkyl group, an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom.
[0043] Although the light-absorbing composition does not contain a phosphoric acid ester having a polyoxyalkyl group, the light absorber is properly dispersed in the light-absorbing composition owing to the action of the alkoxysilane monomer. Further, the light-absorbing composition can be used to produce an optical filter. In this case, a hydrolysis reaction and a polycondensation reaction of the alkoxysilane monomer contained in the light-absorbing composition occur, whereby a siloxane bond (SiOSi) is formed. In other words, a hydrolysis-polycondensation product of the alkoxysilane monomer is produced. A particular functional group of the hydrolysis-polycondensation product of the alkoxysilane monomer enters between fine particles of the light absorber to cause steric hindrance, thereby preventing aggregation of the light absorber. Accordingly, the light-absorbing composition according to the present invention can impart desired optical properties to an optical filter even though it does not contain a phosphoric acid ester compound having a polyoxyalkyl group.
[0044] Examples of the phosphoric acid ester having a polyoxyalkyl group include, but not particularly limited to, PLYSURF A208N (polyoxyethylene alkyl (C12, C13) ether phosphoric acid ester), PLYSURF A208F (polyoxyethylene alkyl (C8) ether phosphoric acid ester), PLYSURF A208B (polyoxyethylene lauryl ether phosphoric acid ester), PLYSURF A219B (polyoxyethylene lauryl ether phosphoric acid ester), PLYSURF AL (polyoxyethylene styrenated phenylether phosphoric acid ester), PLYSURF A212C (polyoxyethylene tridecyl ether phosphoric acid ester), and PLYSURF A215C (polyoxyethylene tridecyl ether phosphoric acid ester). They are all products manufactured by DKS Co., Ltd. The phosphoric acid ester may be NIKKOL DDP-2 (polyoxyethylene alkyl ether phosphoric acid ester), NIKKOL DDP-4 (polyoxyethylene alkyl ether phosphoric acid ester), or NIKKOL DDP-6 (polyoxyethylene alkyl ether phosphoric acid ester). They are all products manufactured by Nikko Chemicals Co., Ltd.
[0045] Desirably, the light-absorbing composition is substantially free of; (i) any other compound that has a polyoxyethylene alkyl group; (ii) a compound that has a sulfonate group or a sulfate ester group and exhibits an action advantageous in dispersing the light absorber when the compound is added; and (iii) a compound that contains an amine salt or a quaternary ammonium salt. The light-absorbing composition can prevent aggregation of the light absorber even though it does not contain such compounds.
[0046] The alkoxysilane monomer desirably includes an alkyl group-containing alkoxysilane monomer represented by the following formula (b). In this case, during the production of a hydrolysis-polycondensation product of the alkoxysilane monomer, an alkyl group of the alkyl group-containing alkoxysilane monomer enters between fine particles of the light absorber, whereby aggregation of the light absorber can be prevented more reliably.
(R.sub.2).sub.nSi(OR.sub.3).sub.4-n (b)
In the formula, R.sub.2 is an alkyl group having 1 to 4 carbon atoms, R.sub.3 is an alkyl group having 1 to 8 carbon atoms, and n is an integer of 1 to 3.
[0047] The alkoxysilane monomer is not particularly limited as long as the normalized transmission spectrum satisfies the above conditions, and examples thereof include tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, dimethyldiethoxysilane, dimethyldimethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, and 3-glycidoxypropylmethyldiethoxysilane.
[0048] The phosphonic acid represented by the formula (a) is not particularly limited. When the phosphonic acid is a phosphonic acid (alkyl-based phosphonic acid) represented by the formula (a) in which R.sub.11 is an alkyl group, the phosphonic acid is, for example, a phosphonic acid in which the alkyl group has 1 to 8 carbon atoms. When the phosphonic acid is a phosphonic acid (aryl-based phosphonic acid) represented by the formula (a) in which R.sub.11 is an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group, the phosphonic acid represented by the formula (a) is, for example, phenylphosphonic acid, nitrophenylphosphonic acid, hydroxyphenylphosphonic acid, bromophenylphosphonic acid, dibromophenylphosphonic acid, fluorophenylphosphonic acid, difluorophenylphosphonic acid, chlorophenylphosphonic acid, dichlorophenylphosphonic acid, benzylphosphonic acid, bromobenzylphosphonic acid, dibromobenzylphosphonic acid, fluorobenzylphosphonic acid, difluorobenzylphosphonic acid, chlorobenzylphosphonic acid, or dichlorobenzylphosphonic acid.
[0049] The source of copper ion in the light-absorbing composition is, for example, a copper salt. The copper salt is, for example, copper acetate or a hydrate of copper acetate. The copper salt may be an anhydride or a hydrate of copper chloride, copper formate, copper stearate, copper benzoate, copper pyrophosphate, copper naphthenate, or copper citrate. For example, copper acetate monohydrate is represented by Cu(CH.sub.3COO).sub.2.H.sub.2O, and 1 mol of copper acetate monohydrate supplies 1 mol of copper ion.
[0050] The relationship among the content of the phosphonic acid, the content of the copper ion, and the content of the alkoxysilane monomer in the light-absorbing composition is not particularly limited as long as the normalized transmittance spectrum satisfies the above conditions. For example, the ratio of the content of the alkoxysilane monomer to the content of the copper ion is 2.0 or more, desirably 2.5 or more, on an amount-of-substance basis. Further, the ratio of the content of the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 to the content of the copper ion is, for example, 1.5 or more on an amount-of-substance basis.
[0051] For example, when the following conditions (1) and (1) are satisfied, the ratio of the content of the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 to the content of the copper ion is 2.5 or more on an amount-of-substance basis. In this case, an optical filter produced using the light-absorbing composition is likely to have desired optical properties. [0052] (1) The phosphonic acid includes a phosphonic acid represented by the formula (a) where R.sub.11 is an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom. [0053] (1) The alkoxysilane monomer includes an alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 and a tetrafunctional alkoxysilane monomer represented by the formula (c).
Si(OR.sub.4).sub.4 (c)
In the formula, R.sub.4 is an alkyl group having 1 to 8 carbon atoms.
[0054] When the following conditions (2) and (2) are satisfied, for example, the ratio of the content of the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 to the content of the copper ion is 3.0 or more on an amount-of-substance basis. In this case, an optical filter produced using the light-absorbing composition is likely to have desired optical properties. [0055] (2) The phosphonic acid includes a phosphonic acid represented by the formula (a) where R.sub.11 is an aryl group, a nitroaryl group, a hydroxyaryl group, or a halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom. [0056] (2) The alkoxysilane monomer includes an alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 and does not include a tetrafunctional alkoxysilane monomer represented by the formula (c).
[0057] When the following conditions (3) and (3) are satisfied, for example, the ratio of the content of the alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2 to the content of the copper ion is 1.5 or more on an amount-of-substance basis. In this case, an optical filter produced using the light-absorbing composition is likely to have desired optical properties. [0058] (3) The phosphonic acid includes only a phosphonic acid represented by the the formula (a) where R.sub.11 is an alkyl group. [0059] (3) The alkoxysilane monomer includes an alkyl group-containing alkoxysilane monomer represented by the formula (b) where n=1 or 2.
[0060] The light-absorbing composition may further contain a resin when necessary, or may be free of a resin in some cases. In the light-absorbing composition, the ratio of the solid content of the resin composition to the sum of the content of the phosphonic acid, the content of the copper ion, and the content of the alkoxysilane monomer as expressed in terms of the hydrolysis-polycondensation product is, for example, 0 to 3.0, desirably 0 to 2.7, on a mass basis. Since the light-absorbing composition requires a small amount of resin as described above, an optical filter produced using the light-absorbing composition is likely to have a small thickness.
[0061] When the light-absorbing composition further contains a resin, the resin is not limited to a particular resin as long as the normalized transmittance spectrum satisfies the above conditions, and may be, for example, a silicone resin. The silicone resin is a compound having a siloxane bond (SiOSi) in its structure. In this case, since the hydrolysis-polycondensation product of the alkoxysilane monomer also has a siloxane bond, the alkoxysilane monomer hydrolysis-polycondensation product derived from the alkoxysilane monomer is compatible with the resin in the optical filter.
[0062] The resin is desirably a silicone resin containing an aryl group such as a phenyl group. When the resin contained in the optical filter is excessively hard (rigid), the risk that a layer containing the resin may crack owing to cure shrinkage during the production process of the optical filter increases as the thickness of the layer increases. When the resin is a silicone resin containing an aryl group, the layer formed of the light-absorbing composition is likely to have high crack resistance. The silicone resin containing an aryl group has high compatibility with the phosphonic acid represented by the formula (a), and thus aggregation of the light absorber is unlikely to occur. Specific examples of the silicone resin used as a matrix resin include KR-255, KR-300, KR-2621-1, KR-211, KR-311, KR-216, KR-212, KR-251, and KR-5230. They are all silicone resins manufactured by Shin-Etsu Chemical Co., Ltd.
[0063] The light absorber in the light-absorbing composition is formed by, for example, coordination of the phosphonic acid represented by the formula (a) to the copper ion. For example, fine particles containing at least the light absorber are formed in the light-absorbing composition. In this case, as described above, owing to the action of the alkoxysilane monomer, the fine particles are dispersed in the light-absorbing composition without causing aggregation. The average particle diameter of the fine particles is, for example, 5 nm to 200 nm. When the average particle diameter of the fine particles is 5 nm or more, no particular ultramiconization process is required in order to obtain the fine particles, and the risk of structural destruction of the fine particles containing at least the light absorber is low. In addition, the fine particles are well dispersed in the light-absorbing composition. When the average particle diameter of the fine particles is 200 nm or less, it is possible to reduce the influence of Mie scattering, to increase the visible transmittance of an optical filter, and to prevent deterioration of the properties such as contrast and haze of an image captured by an imaging apparatus. Desirably, the average particle diameter of the fine particles is 100 nm or less. In this case, the influence of Rayleigh scattering is reduced, whereby an optical filter produced using the light-absorbing composition can have improved transparency to visible light. More desirably, the average particle diameter of the fine particles is 75 nm or less. In this case, an optical filter produced using the light-absorbing composition exhibits an especially high transparency to visible light. The average particle diameter of the fine particles can be measured by dynamic light scattering.
[0064] An example of a method for preparing the light-absorbing composition according to the present invention will be described. For example, when the light-absorbing composition contains a phosphonic acid (aryl-based phosphonic acid) represented by the formula (a) where R.sub.11 is an aryl group, a nitroaryl group, a hydroxyaryl group, or an halogenated aryl group in which at least one hydrogen atom in an aryl group is substituted by a halogen atom, a solution D is prepared in the following manner. First, a copper salt such as copper acetate monohydrate is added to a given solvent such as tetrahydrofuran (THF), and the mixture is stirred to prepare a copper salt solution as a solution A. Next, an aryl-based phosphonic acid is added to a given solvent such as THF, and the mixture is stirred to prepare a solution B. When a plurality of aryl-based phosphonic acids are used as the phosphonic acids represented by the formula (a), the solution B may be prepared by adding the aryl-based phosphonic acids to given solvents such as THF, respectively, stirring the mixtures to prepare a plurality of preliminary solutions containing the respective aryl-based phosphonic acids, and then mixing the thus-prepared preliminary solutions together. For example, an alkoxysilane monomer is added in the preparation of the solution B. The solution B is added to the solution A while stirring the solution A, and the mixture is further stirred for a given period of time. To this solution is then added a given solvent such as toluene, and the mixture is stirred to obtain a solution C. Subsequently, the solution C is subjected to solvent removal for a given period of time under heating to obtain a solution D. Through this process, the solvent such as THF and the component such as acetic acid (boiling point: about 118 C.) generated by disassociation of the copper salt are removed, whereby a light absorber is generated by the phosphonic acid represented by the formula (a) and copper ion. The heating temperature of the solution C is determined on the basis of the boiling point of the to-be-removed component disassociated from the copper salt. During the solvent removal, the solvent such as toluene (boiling point: about 110 C.) used to obtain the solution C is also evaporated. A certain amount of this solvent desirably remains in the light-absorbing composition. This is preferably taken into account in determining the amount of the solvent to be added and the time period of the solvent removal. To obtain the solution C, o-xylene (boiling point: about 144 C.) may be used instead of toluene. In this case, the amount of o-xylene to be added may be about one-fourth of the amount of toluene to be added, because the boiling point of o-xylene is higher than that of toluene.
[0065] When the light-absorbing composition contains a phosphonic acid (alkyl-based phosphonic acid) represented by the formula (a) where R.sub.11 is an alkyl group, a solution H is further prepared in the following manner, for example. First, a copper salt such as copper acetate monohydrate is added to a given solvent such as tetrahydrofuran (THF), and the mixture is stirred to obtain a copper salt solution as a solution E. Further, an alkyl-based phosphonic acid is added to a given solvent such as THF, and the mixture is stirred to prepare a solution F. When a plurality of phosphonic acids are used as the alkyl-based phosphonic acids, the solution F may be prepared by adding the alkyl-based phosphonic acids to given solvents such as THF, respectively, stirring the mixtures to prepare a plurality of preliminary solutions containing the respective alkyl-based phosphonic acids, and then mixing the thus-prepared preliminary solutions together. For example, an alkoxysilane monomer is added in the preparation of the solution F. The solution F is added to the solution E while stirring the solution E, and the mixture is further stirred for a given period of time. To the resultant solution is then added a given solvent such as toluene, and the mixture is stirred to obtain a solution G. Subsequently, the solution G is subjected to solvent removal for a given period of time under heating to obtain a solution H. Through this process, the solvent such as THF and the component such as acetic acid generated by disassociation of the copper salt are removed. The heating temperature of the solution G is determined in the same manner as that for the solution C, and the solvent used to obtain the solution G is also determined in the same manner as that for the solution C.
[0066] The light-absorbing composition can be prepared by, for example, mixing the solution D and the solution H at a predetermined mixing ratio, and when necessary, adding a resin such as a silicone resin. In some cases, the light-absorbing composition can be prepared by adding a resin such as a silicone resin to either one of the solution D and the solution H. Also, the solution D and the solution H each can be a light-absorbing composition by itself.
[0067] Next, an optical filter according to the present invention will be described. As shown in
[0068] Although the optical filters 1a to 1d do not contain a phosphoric acid ester having a polyoxyalkyl group, proper dispersion of the light absorber is achieved in the optical filters 1a to 1d owing to the action of the hydrolysis-polycondensation product of the alkoxysilane monomer. Accordingly, the normalized transmittance spectra satisfies the above-described conditions. Besides, since the hydrolysis-polycondensation product of the alkoxysilane monomer has a siloxane bond (SiOSi), the light-absorbing layer 10 is moderately rigid and excellent in heat resistance, and also is unlikely to be deteriorated when exposed to water and thus excellent in weather resistance. When the optical filters 1a to 1d are configured such that the normalized transmittance spectra satisfy the above conditions, the optical filters 1a to 1d exhibit high spectral transmittances over a wide range in the visible light region. The hydrolysis-polycondensation product of the alkoxysilane monomer has a structure similar to that of silicate glass and thus is highly transparent to visible light. This also advantageously contributes to allowing the normalized transmittance spectra to satisfy the above conditions.
[0069] Examples of the phosphoric acid ester having a polyoxyalkyl group include, but not limited to, PLYSURF A208N (polyoxyethylene alkyl (C12, C13) ether phosphoric acid ester), PLYSURF A208F (polyoxyethylene alkyl (C8) ether phosphoric acid ester), PLYSURF A208B (polyoxyethylene lauryl ether phosphoric acid ester), PLYSURF A219B (polyoxyethylene lauryl ether phosphoric acid ester), PLYSURF AL (polyoxyethylene styrenated phenylether phosphoric acid ester), PLYSURF A212C (polyoxyethylene tridecyl ether phosphoric acid ester), and PLYSURF A215C (polyoxyethylene tridecyl ether phosphoric acid ester). They are all products manufactured by DKS Co., Ltd. The phosphoric acid ester may be NIKKOL DDP-2 (polyoxyethylene alkyl ether phosphoric acid ester), NIKKOL DDP-4 (polyoxyethylene alkyl ether phosphoric acid ester), or NIKKOL DDP-6 (polyoxyethylene alkyl ether phosphoric acid ester). They are all products manufactured by Nikko Chemicals Co., Ltd.
[0070] In each of the optical filters 1a to 1d, the normalized transmittance spectrum desirably has a second wavelength band in which the spectral transmittance is 80% or more in the wavelength range from 300 nm to 700 nm. The difference between the maximum value and the minimum value among wavelengths in this second wavelength band is 40 nm or more. In this case, the optical filters 1a to 1d have desirable optical properties in the visible light region.
[0071] In each of the optical filters 1a to 1d, the normalized transmittance spectrum desirably has a third wavelength band in which the spectral transmittance is 20% or less in a wavelength range from 700 nm to 1200 nm. The difference between the maximum value and the minimum value among wavelengths in this third wavelength band is 120 nm or more. In this case, the optical filters 1a to 1d can properly block light in the predetermined wavelength band in the wavelength range from 700 nm to 1200 nm. Accordingly, the optical filters 1a to 1d have desirable optical properties in the wavelength range from 700 nm to 1200 nm.
[0072] In each of the optical filters 1a to 1d, the normalized transmission spectrum desirably has a fourth wavelength band and a fifth wavelength band. The fourth wavelength band is a wavelength band in which the spectral transmittance decreases with an increase in wavelength. The fifth wavelength band is a wavelength band that includes a wavelength shorter than the minimum wavelength in the fourth wavelength band and in which the spectral transmittance increases with an increase in wavelength. A first cut-off wavelength at which the spectral transmittance is 50% in the fourth wavelength band is present in a wavelength range from 600 nm to 650 nm. A second cut-off wavelength at which the spectral transmittance is 50% in the fifth wavelength band is present in a wavelength range from 350 nm to 420 nm. The difference obtained by subtracting the second cut-off wavelength from the first cut-off wavelength is 200 nm to 290 nm. In this case, the optical filters 1a to 1d can block light having particular wavelengths and thus have optical properties advantageous in being disposed ahead of a solid-state imaging sensor, for example. In the present specification, the first cut-off wavelength is also referred to as IR cut-off wavelength and the second cut-off wavelength is also referred to as UV cut-off wavelength.
[0073] In the normalized transmittance spectrum of each of the optical filters 1a to 1d, a maximum wavelength at which the maximum spectral transmittance is found is desirably present in a wavelength range from 500 nm to 550 nm. A minimum wavelength at which the minimum spectral transmittance in a wavelength range from 700 nm to 1200 nm is found is present in a wavelength range from 750 nm to 900 nm. In addition, the difference obtained by subtracting the maximum wavelength from the minimum wavelength is from 240 nm to 360 nm. In this case, the minimum wavelength and the maximum wavelength are in desirable ranges in the normalized transmittance spectra, and the optical filters 1a to 1d have desirable optical properties.
[0074] In the normalized transmittance spectrum of each of the optical filters 1a to 1d, the difference obtained by subtracting the minimum spectral transmittance in the wavelength range from 700 nm to 1200 nm in the normalized transmittance spectrum from the maximum spectral transmittance in the normalized transmittance spectrum is desirably 68% or more. In this case, the difference is large enough to impart desirable optical properties to the optical filters 1a to 1d. The difference is desirably 70% or more.
[0075] In each of the optical filters 1a to 1d, the light-absorbing layer 10 is typically formed by subjecting a film formed of the above-described light-absorbing composition to a drying treatment and a humidifying treatment. Through this process, a hydrolysis reaction and a polycondensation reaction of the alkoxysilane monomer contained in the light-absorbing composition occur, whereby the alkoxysilane monomer is converted to a hydrolysis-polycondensation product.
[0076] An example of a method for producing the light-absorbing layer 10 will be described. For example, the light-absorbing composition is applied onto a given substrate by a method such as spin coating or application using a dispenser to form a coating film of the light-absorbing composition, and a drying treatment of this coating film is performed through heating. For example, the coating film is exposed to an environment at a temperature from 50 C. to 200 C. Next, the dried coating film is subjected to a humidifying treatment in order to sufficiently promote a hydrolysis reaction and a polycondensation reaction of the alkoxysilane monomer. For example, the dried coating film is exposed to an environment at a temperature from 50 C. to 100 C. and a relative humidity from 60% to 100%. Through this process, repeating structures (SiO).sub.n of a siloxane bond are formed. In this manner, the light-absorbing layer 10 is formed. From the viewpoint of forming a firm light-absorbing layer 10 as well as improving the optical properties of the optical filters 1a to 1d, the maximum value of the ambient temperature at which the coating film is subjected to the drying treatment is, for example, 85 C. or higher. The conditions for the humidifying treatment of the coating film are not particularly limited as long as the hydrolysis reaction and the polycondensation reaction of the alkoxysilane monomer can be promoted sufficiently. The humidifying treatment of the coating film is performed by, for example, exposing the coating film for a given period of time to an environment in which the temperature condition, which is 50 C. to 100 C., and the relative humidity condition, which is 60% to 100%, are combined as appropriate. An example of the combination of the temperature condition and relative humidity condition of the humidifying treatment of the coating film is the combination of a temperature of 85 C. and a relative humidity of 85%.
[0077] In each of the optical filters 1a to 1d, the light-absorbing layer 10 has a thickness of, for example, 400 m or less, desirably 300 m or less, and more desirably 250 m or less. With this configuration, the optical filters 1a to 1d are likely to have desired optical properties. As described above, the light-absorbing composition can reduce the amount of resin to be used therein. Accordingly, by using the light-absorbing composition, such a small thickness of the light-absorbing layer 10 can be achieved easily. The small thickness of the light-absorbing layer 10 is advantageous for reducing the height of a device on which each of the optical filters 1a to 1d is to be mounted. In each of the optical filters 1a to 1d, the light-absorbing layer 10 has a thickness of 30 m or more, for example.
[0078] As shown in
[0079] The type of the transparent dielectric substrate 20 is not particularly limited as long as the normalized transmittance spectrum of the optical filter 1a satisfies the above-described conditions. In some cases, the transparent dielectric substrate 20 may have the ability to absorb light in the infrared region. The transparent dielectric substrate 20 may have an average spectral transmittance of 90% or more in, for example, a wavelength range from 350 nm to 900 nm. The material of the transparent dielectric substrate 20 is not limited to any particular material, and the material is, for example, a certain type of glass or resin. When the material of the transparent dielectric substrate 20 is glass, the transparent dielectric substrate 20 is, for example, a transparent glass substrate made of a silicate glass such as soda-lime glass or borosilicate glass, or an infrared cut glass substrate. The infrared cut glass substrate is made of, for example, phosphate glass or fluorophosphate glass, each containing CuO.
[0080] When the material of the transparent dielectric substrate 20 is a resin, the resin is, for example, a cyclic olefin-based resin such as a norbornene-based resin, a polyarylate-based resin, an acrylic resin, a modified acrylic resin, a polyimide resin, a polyetherimide resin, a polysulfone resin, a polyethersulfone resin, a polycarbonate resin, or a silicone resin.
[0081] The optical filter 1b according to another example of the present invention has the same configuration as the optical filter 1a, unless otherwise stated. The descriptions regarding the optical filter 1a also apply to the optical filter 1b, unless technically incompatible.
[0082] As shown in
[0083] The method for forming the infrared-reflecting films 30 of the optical filter 1b is not particularly limited, and any of vacuum deposition, sputtering, chemical vapor deposition (CVD), and sol-gel process employing spin coating or spray coating can be used according to the type of the material forming the infrared-reflecting films 30.
[0084] As shown in
[0085] As shown in
[0086] As shown in
EXAMPLES
[0087] The present invention will be described in more detail by way of examples. It is to be noted, however, that the present invention is not limited to the examples to be described below. First, methods for evaluating optical filters according to examples and comparative examples will be described.
[0088] <Measurement of Thickness of Light-Absorbing Layer>
[0089] The thicknesses of the optical filters according to the examples and the comparative examples were measured with a digital micrometer. In most of the examples, the thickness of a light-absorbing layer included in each of the optical filters was calculated by subtracting the thickness of a transparent glass substrate from the thickness of the optical filter. In Example 35, the thickness of the light-absorbing layer was measured directly with a digital micrometer.
[0090] <Measurement of Transmittance Spectrum of Optical Filter>
[0091] Transmittance spectra obtained when light having wavelengths in a range from 300 nm to 1200 nm was incident on the optical filters according to the examples and the comparative examples were measured using an ultraviolet-visible spectrophotometer (manufactured by JASCO Corporation, product name: V-670). In this measurement, the incident angle of the light incident on each optical filter was set to 0 (degree).
[0092] <Determination of Normalized Transmittance Spectrum>
[0093] The light absorption property, i.e., the transmittance spectrum, of an optical filter changes according to the thickness of a light-absorbing layer in the optical filter. When various samples are prepared to compare their performances or to adjust the production conditions, it is appropriate to evaluate the measured transmittance spectra of optical filters by normalizing them on the basis of a certain index. Accordingly, transmittance spectra of the optical filters according to the examples and comparative examples measured in a wavelength range from 300 nm to 1200 nm were normalized in such a manner that the spectral transmittance at a wavelength of 700 nm was 20%, thereby determining the normalized transmittance spectra. Specifically, the following calculations (1) to (4) were performed. [0094] (1) In the transmittance spectrum measured for each of the optical filters according to the examples and comparative examples, the spectral transmittance for each wavelength was multiplied by 100/92 to obtain a second spectral transmittance in which reflection on both surfaces of the optical filter was approximately canceled. [0095] (2) In consideration of the fact that a transparent glass substrate (manufactured by SCHOTT AG, product name: D 263 T eco) provided in each of the optical filters of most of the examples and the comparative examples does not substantially absorb light having wavelengths in a range from 350 nm to 1200 nm, the absorption coefficient of the light-absorbing layer was determined for each wavelength from the thickness of the light-absorbing layer in the optical filter and the second spectral transmittance. [0096] (3) Next, regarding the optical filter provided with the light-absorbing layer having the thus-determined absorption coefficient, the spectral transmittance when the thickness of the light-absorbing layer was changed was calculated for each wavelength. In this case, each of the calculated values was multiplied by 100/92 to calculate the spectral transmittance with consideration given to the surface reflection of the optical filter beforehand. The thickness (calculated thickness) of the light-absorbing layer was determined in such a manner that the thus-calculated spectral transmittance at 700 nm was 20%. [0097] (4) On the basis of the calculated thickness of the light-absorbing layer determined in the step (3), the spectral transmittance of the optical filter according to each of the examples and the comparative examples was determined for each wavelength to obtain a transmittance spectrum. The thus-obtained transmittance spectrum was determined as a normalized transmittance spectrum.
Example 1
[0098] 1.125 g of copper acetate monohydrate and 60 g of tetrahydrofuran (THF) were mixed together, and the mixture was stirred for 3 hours to obtain a solution A. Next, 10 g of THF was added to 0.447 g of phenylphosphonic acid, and the mixture was stirred for 30 minutes to obtain a solution B-1. Further, 10 g of THF was added to 0.670 g of 4-bromophenylphosphonic acid, and the mixture was stirred for 30 minutes to obtain a solution B-2. Next, the solutions B-1 and B-2 were mixed together, and the mixture was stirred for 1 minute. 5.415 g of methyltriethoxysilane (MTES, manufactured by Shin-Etsu Chemical Co., Ltd.) and 1.775 g of tetraethoxysilane (TEOS, manufactured by KISHIDA CHEMICAL Co., Ltd., special grade) were added thereto, and the mixture was stirred for another 1 minute to obtain a solution B. The solution B was added to the solution A while stirring the solution A, and the mixture was stirred at room temperature for 1 minute. Next, 40 g of toluene was added to this solution, and the mixture was then stirred at room temperature for 1 minute to obtain a solution C. This solution C was poured into a flask and subjected to solvent removal using a rotary evaporator (manufactured by Tokyo Rikakikai Co. Ltd., model: N-1110SF) under heating by means of an oil bath (manufactured by Tokyo Rikakikai Co. Ltd., model: OSB-2100). The temperature of the oil bath was controlled to 85 C. A solution D obtained after the solvent removal was collected from the flask. The solution D, which is a dispersion of fine particles of copper phenyl-based phosphonate (light absorber), was transparent, and the fine particles were well dispersed therein.
[0099] 0.450 g of copper acetate monohydrate and 24 g of THF were mixed together, and the mixture was stirred for 3 hours to obtain a solution E. Further, 10 g of THF was added to 0.257 g of n-butylphosphonic acid (manufactured by Nippon Chemical Industries), and the mixture was stirred for 30 minutes. 2.166 g of methyltriethoxysilane (MTES: manufactured by Shin-Etsu Chemical Co., Ltd.) and 0.710 g of tetraethoxysilane (TEOS, manufactured by KISHIDA CHEMICAL Co., Ltd., special grade) were further added thereto, and the mixture was stirred for another 1 minute to obtain a solution F. The solution F was added to the solution E while stirring the solution E, and the mixture was stirred at room temperature for 1 minute. Next, 16 g of toluene was added to this solution, and the mixture was then stirred at room temperature for 1 minute to obtain a solution G. This solution G was poured into a flask and subjected to solvent removal using a rotary evaporator under heating by means of an oil bath. The temperature of the oil bath was controlled to 85 C. A solution H obtained after the solvent removal was collected from the flask. The solution H, which is a dispersion of fine particles of copper butylphosphonate (light absorber) was transparent, and the fine particles were well dispersed therein.
[0100] 16 g of silicone resin KR-311 (Shin-Etsu Chemical Co., Ltd., the content of nonvlatile components: 60 mass %) and 4 g of silicone resin KR -300 (Shin-Etsu Chemical Co., Ltd., the non-volatile content: 50 mass %) were mixed together, and the mixture was stirred for 10 minutes to obtain a resin composition Y. The solid (non-volatile) content of the resin composition Y was determined to be 58 mass % as per the relationship of: 60 mass %16/20+50 mass %4/20.
[0101] 8.800 g of the resin composition Y was added to the solution D, and the mixture was stirred for 5 minutes to obtain a solution I. The solution H was added to the thus-obtained solution I, and the mixture was stirred for 10 minutes. Thus, a light-absorbing composition according to Example 1 was obtained. The contents of the respective components in the light-absorbing composition according to Example 1 on a mass basis and on an amount-of-substance basis are shown in Table 1 and Table 2, respectively. The solid content of the alkoxysilane monomer was determined by converting the content of the alkoxysilane monomer into the amount of a hydrolysis-polycondensation product of the alkoxysilane monomer.
[0102] The light-absorbing composition according to Example 1 was applied using a dispenser to a 30 mm30 mm central region of one principal surface of a transparent glass substrate (SCHOTT AG, product name: D263 T eco) made of borosilicate glass and having dimensions of 76 mm76 mm0.21 mm to form a coating film of the light-absorbing composition. At this time, a frame having an opening corresponding to the application area of the light-absorbing composition was placed on the one principal surface of the transparent glass substrate to prevent the light-absorbing composition from flowing over the application area. Next, the transparent glass substrate with the undried coating film was placed in an oven and heat-treated at 85 C. for 6 hours to cure the coating film. Thereafter, the transparent glass substrate provided with the coating film was subjected to a humidifying treatment by being placed in a thermo-hygrostat set at a temperature of 85 C. and a relative humidity of 85% for 2 hours. Then, a portion where the light-absorbing layer with a fixed thickness was formed was cut out to produce an optical filter according to Example 1. The thickness of the light-absorbing layer in the optical filter according to Example 1 was 158 m. The normalized transmittance spectrum of the optical filter according to Example 1 is shown in
Other Examples and Comparative Examples
[0103] Light-absorbing compositions according to Examples 2 to 63 and light-absorbing compositions according to Comparative Example 1 to 12 were prepared in the same manner as in Example 1, except that the amounts of respective components of the light-absorbing compositions were adjusted as shown in Tables 1 to 6. The light-absorbing compositions according to Examples 11, 36, and 37 contained methyltrimethoxysilane (MTMS) instead of MTES, and the light-absorbing compositions of Examples 12, 13, 38, and 39 contained dimethyldiethoxysilane (DMDES) instead of MTES. 8 g of silicone resin KR-212(Shin-Etsu Chemical Co., Ltd., the non-volatile content: 70 mass %) and 12 g of silicone resin KR-300 (Shin-Etsu Chemical Co., Ltd., the non-volatile content: 50 mass %) were mixed together, and the mixture was stirred for 10 minutes to obtain a resin composition X. Also, silicone resin KR-5230 (Shin-Etsu Chemical Co., Ltd., the non-volatile content: 60 mass %) was used as a resin composition Z. The solid content of the resin composition X was determined to be 58 mass % in the same manner as that for determining the solid content of the resin composition Y. The solid content of the resin composition Z was determined to be 60 mass %.
[0104] Optical filters according to Examples 2 to 63 were produced in the same manner as in Example 1, except that, instead of the light-absorbing composition according to Example 1, the light-absorbing compositions according to Examples 2 to 63 were used, respectively. The optical filter according to Example 35 was produced by separating the light-absorbing layer from the transparent glass substrate, and thus was constituted only by the light-absorbing layer. Optical filters according to Comparative Examples 1 to 4, 6 to 9, and 11 were produced in the same manner as in Example 1, except that, instead of the light-absorbing composition according to Example 1, the light-absorbing compositions according to Comparative Examples 1 to 4, 6 to 9, and 11 were used, respectively.
[0105] The normalized transmittance spectra of the optical filters according to Examples 2 and 10 are shown in
[0106] From the results obtained regarding the optical filters according to Example 1 to 10 as shown in Table 7, it can be seen that an optical filter having good optical properties can be produced even if the type and the amount of silicone resin used in the light-absorbing composition are changed.
Comparative Examples 1 and 2
[0107] The normalized transmittance spectrum of the optical filter according to Comparative Example 2 is shown in
[0108] In Comparative Example 1, the solution containing the light absorber formed by the alkyl-based phosphonic acid and copper ion was transparent, whereas the solution containing the light absorber formed by the phenyl-based phosphonic acid and copper ion was turbid. In addition, the optical filter of Comparative Example 1 was whitish, and the optical filter of Comparative Example 1 exhibited a very low transmittance in the visible light region. The reason for this is considered to be that the content of the alkoxysilane monomer in the light-absorbing composition was not sufficient.
[0109] In Comparative Example 2, the solution containing the light absorber formed by the alkyl-based phosphonic acid and copper ion and the solution containing the light absorber formed by the phenyl-based phosphonic acid and copper ion had a high transparency. However, the optical filter according to Comparative Example 2 had a low transmittance in the visible light region. The results obtained in Comparative Example 2 suggest that the content of the alkoxysilane monomer in the light-absorbing composition according to Comparative Example 2 was slightly lower than the amount required for producing an optical filter having good optical properties.
Examples 11 to 13
[0110] The normalized transmittance spectra of the optical filters according to Examples 11 and 12 are shown in
[0111] The light-absorbing compositions according to Examples 12 and 13 contained, as the alkoxysilane monomer, DMDES instead of MTES. The content of DMDES in each of the light-absorbing compositions of Examples 12 and 13 was adjusted so as to be roughly equivalent to the content of MTES in the light-absorbing composition of Example 1 as expressed in terms of solid components of the alkoxysilane monomer on a mass basis. From the results obtained regarding Examples 12 and 13 as shown in Table 8, it can be seen that an optical filter having good optical properties can be produced using DMDES as the alkoxysilane monomer. DMDES has two methyl groups, and it was expected that these methyl groups contribute to steric hindrance, and similar to MTES, DMDES would bring about advantageous effects. The effects as expected were obtained in the optical filters according to Examples 12 and 13. These results demonstrate that the light-absorbing composition can properly disperse the light absorber regardless of the number of alkyl groups of the alkoxysilane monomer contained therein.
Example 14
[0112] The normalized transmittance spectrum of the optical filter according to Example 14 is shown in
Comparative Example 3
[0113] The normalized transmittance spectrum of the optical filter according to Comparative Example 3 is shown in
Comparative Example 4
[0114] Optical properties read from the normalized transmittance spectrum of the optical filter according to Comparative Example 4 are shown in Table 12. As shown in Table 5, in the light-absorbing composition according to Comparative Example 4, the ratio between the amount of the solid components of MTES and the amount of the solid components of TEOS was adjusted to about 1: 1 on a mass basis. The content of the alkoxysilane monomer in the light-absorbing composition according to Comparative Example 4 was adjusted so as to be roughly equivalent to the content of the alkoxysilane monomer in the light-absorbing composition of Comparative Example 2 as expressed in terms of solid components of the alkoxysilane monomer on a mass basis. The optical filter according to Comparative Example 4 had a low transmittance in the visible light region. The reason for this is considered to be that the alkoxysilane monomer could not sufficiently exhibit the function of suppressing aggregation of the light absorber. From this result, it can be seen that, in order to impart good optical properties to an optical filter by a light-absorbing composition, the added amount of an alkoxysilane monomer having an alkyl group makes more advantageous contribution than the added amount of an alkoxysilane monomer and the final amount of solid components of an alkoxysilane monomer. It is suggested that the steric hindrance caused by the methyl group of MTES allows an optical filter to exhibit good optical properties.
Example 15
[0115] Optical properties read from the normalized transmittance spectrum of the optical filter according to Example 15 are shown in Table 8. As shown in Table 1, in the light-absorbing composition according to Example 15, the ratio between the amount of solid components of MTES and the amount of solid components of TEOS was adjusted to about 1:1 on a mass basis, as in Comparative Example 4. The content of the alkoxysilane monomer in the light-absorbing composition according to Example 15 was adjusted so as to be roughly equivalent to the content of the alkoxysilane monomer in the light-absorbing composition of Example 1 as expressed in terms of solid components of the alkoxysilane monomer on a mass basis. As shown in Table 8, the optical filter according to Example 15 had good optical properties. It is considered that the difference in optical properties between the optical filter of Example 15 and the optical filter of Comparative Example 4 is caused by the fact that the content of MTES in the light-absorbing composition of Example 15 was sufficient to prevent aggregation of the light absorber.
Examples 16 and 17
[0116] The normalized transmittance spectrum of the optical filter according to Example 16 is shown in
Comparative Example 5
[0117] As shown in Table 5, the light-absorbing composition according to Comparative Example 5 contained only TEOS as the alkoxysilane monomer. Although the content of TEOS in the light-absorbing composition of Comparative Example 5 was relatively large, the light-absorbing composition of Comparative Example 5 was turbid and a suitable optical filter could not be obtained.
Examples 18 and 19
[0118] The normalized transmittance spectrum of the optical filter according to Example 18 is shown in
Examples 20 and 21
[0119] The normalized transmittance spectrum of the optical filter according to Example 20 is shown in
Examples 22 and 23
[0120] The normalized transmittance spectrum of the optical filter according to Example 22 is shown in
Examples 24 to 49 and Comparative Examples 6 to 10
[0121] The normalized transmittance spectrum of the optical filter according to Example 24 is shown in
Examples 34 and 35
[0122] The normalized transmittance spectra of the optical filters according to Examples 34 and 35 are shown in
[0123] As described above, the optical filter according to Example 35 was constituted only by the light-absorbing layer. From the results obtained regarding Example 35, it can be seen that the light-absorbing composition containing a sufficient amount of alkoxysilane monomer can eliminate the necessity of using a phosphoric acid ester and a silicone resin and also can produce an optical filter that does not require a substrate. In other words, an alkoxysilane monomer alone can play the roles of a phosphate ester, a silicone resin, and a transparent glass substrate.
Examples 50 to 63 and Comparative Examples 11 and 12
[0124] The normalized transmittance spectrum of the optical filter according to Example 50 is shown in
[0125] Comparison between Examples 1 to 23 and Comparative Examples 1, 2, and 4 suggests that, in the following case (I), the ratio of the content of a bifunctional or trifunctional alkoxysilane monomer having an alkyl group to the content of copper ion is desirably 2.5 or more on an amount-of-substance basis in order to obtain an optical filter having good optical properties.
(I) The light-absorbing composition contains a phenyl-based phosphonic acid and an alkyl-based phosphonic acid, and also contains a tetrafunctional alkoxysilane monomer and a bifunctional or trifunctional alkoxysilane monomer.
[0126] Comparison between Examples 24 to 49 and Comparative Examples 6, 7, 9, and 10 suggests that, in the following case (II), the ratio of the content of a bifunctional or trifunctional alkoxysilane monomer having an alkyl group to the content of copper ion is desirably 2.5 or more on an amount-of-substance basis in order to obtain an optical filter having good optical properties.
(II) The light-absorbing composition contains a phenyl-based phosphonic acid and does not contain an alkyl-based phosphonic acid, and also contains a tetrafunctional alkoxysilane monomer and a bifunctional or trifunctional alkoxysilane monomer.
[0127] Comparison between Examples 50 to 63 and Comparative Examples 11 and 12 suggests that, in the following case (III), the ratio of the content of a bifunctional or trifunctional alkoxysilane monomer having an alkyl group to the content of copper ion is desirably 1.5 or more on an amount-of-substance basis in order to obtain an optical filter having good optical properties.
(III) The light-absorbing composition contains an alkyl-based phosphonic acid and does not contain a phenyl-based phosphonic acid, and also contains a tetrafunctional alkoxysilane monomer and a bifunctional or trifunctional alkoxysilane monomer.
TABLE-US-00001 TABLE 1 Phenyl-based phosphonic acid Halogenated phenyl Alkyl- phosphonic based acid phos- 4- 4- phonic bromo chloro acid Phenyl phenyl phenyl n-butyl phos- phos- phos- phos- phonic phonic phonic phonic Copper Alkoxysilane monomer acid acid acid acid ion MTES MTMS DMDES TEOS (g) (g) (g) (g) (g) (g) (g) (g) (g) Ex. 1 0.447 0.670 0 0.257 0.551 7.581 0 0 2.485 Ex. 2 0.447 0.670 0 0.257 0.551 4.549 0 0 1.491 Ex. 3 0.447 0.670 0 0.257 0.551 4.549 0 0 1.491 Ex. 4 0.447 0.670 0 0.257 0.551 4.549 0 0 1.491 Ex. 5 0.447 0.670 0 0.257 0.551 4.549 0 0 1.491 Ex. 6 0.447 0.670 0 0.257 0.551 4.549 0 0 1.491 Ex. 7 0.447 0.670 0 0.257 0.551 5.761 0 0 1.889 Ex. 8 0.447 0.670 0 0.257 0.551 10.007 0 0 3.280 Ex. 9 0.447 0.670 0 0.257 0.551 13.646 0 0 4.473 Ex. 10 0.447 0.670 0 0.257 0.551 27.292 0 0 8.946 Ex. 11 0.447 0.670 0 0.257 0.551 0 5.799 0 2.485 Ex. 12 0.447 0.670 0 0.257 0.551 0 0 5.712 2.485 Ex. 13 0.447 0.670 0 0.257 0.551 0 0 5.712 2.485 Ex. 14 0.447 0.670 0 0.257 0.551 9.477 0 0 0 Ex. 15 0.447 0.670 0 0.257 0.551 4.738 0 0 6.213 Ex. 16 0.447 0.670 0 0.257 0.551 5.965 0 0 18.252 Ex. 17 0.447 0.670 0 0.257 0.551 5.965 0 0 18.252 Ex. 18 0.894 0 0 0.257 0.551 7.581 0 0 2.485 Ex. 19 0.894 0 0 0.257 0.551 7.581 0 0 2.485 Ex. 20 0.268 0.938 0 0.257 0.551 7.581 0 0 2.485 Ex. 21 0.268 0.938 0 0.257 0.551 7.581 0 0 2.485 Ex. 22 0.447 0 0.544 0.257 0.551 7.581 0 0 2.485 Ex. 23 0.447 0 0.544 0.257 0.551 7.581 0 0 2.485 Ex. 24 0.447 0.670 0 0 0.394 5.415 0 0 1.775 Ex. 25 0.447 0.670 0 0 0.394 3.249 0 0 1.065 Ex. 26 0.447 0.670 0 0 0.394 3.249 0 0 1.065 Ex. 27 0.447 0.670 0 0 0.394 3.249 0 0 1.065 Ex. 28 0.447 0.670 0 0 0.394 3.249 0 0 1.065 Ex. 29 0.447 0.670 0 0 0.394 3.249 0 0 1.065 Ex. 30 0.447 0.670 0 0 0.394 4.115 0 0 1.349 Alkoxysilane monomer Silicone resin solid content Resin composition MTES MTMS DMDES TEOS X Y Z (g) (g) (g) (g) (g) (g) (g) (1) Ex. 1 2.854 0 0 0.717 0 8.800 0 0.929 Ex. 2 1.712 0 0 0.430 8.800 0 0 1.255 Ex. 3 1.712 0 0 0.430 0 8.800 0 1.255 Ex. 4 1.712 0 0 0.430 0 0 4.400 0.649 Ex. 5 1.712 0 0 0.430 0 0 8.800 1.298 Ex. 6 1.712 0 0 0.430 0 0 13.200 1.947 Ex. 7 2.169 0 0 0.545 0 8.800 0 1.100 Ex. 8 3.767 0 0 0.946 0 8.800 0 0.769 Ex. 9 5.137 0 0 1.290 0 8.800 0 0.611 Ex. 10 10.274 0 0 2.580 0 8.800 0 0.345 Ex. 11 0 2.857 0 0.717 0 8.800 0 0.928 Ex. 12 0 0 2.857 0.717 8.800 0 0 0.928 Ex. 13 0 0 2.857 0.717 0 8.800 0 0.928 Ex. 14 3.567 0 0 0 0 8.800 0 0.929 Ex. 15 1.784 0 0 1.792 0 8.800 0 0.928 Ex. 16 2.245 0 0 5.264 8.800 0 0 0.541 Ex. 17 2.245 0 0 5.264 0 8.800 0 0.541 Ex. 18 2.854 0 0 0.717 8.800 0 0 0.968 Ex. 19 2.854 0 0 0.717 0 8.800 0 0.968 Ex. 20 2.854 0 0 0.717 8.800 0 0 0.914 Ex. 21 2.854 0 0 0.717 0 8.800 0 0.914 Ex. 22 2.854 0 0 0.717 8.800 0 0 1.058 Ex. 23 2.854 0 0 0.717 0 8.800 0 1.058 Ex. 24 2.038 0 0 0.512 0 8.800 0 1.257 Ex. 25 1.223 0 0 0.307 8.800 0 0 1.679 Ex. 26 1.223 0 0 0.307 0 8.800 0 1.679 Ex. 27 1.223 0 0 0.307 0 0 4.400 0.868 Ex. 28 1.223 0 0 0.307 0 0 8.800 1.736 Ex. 29 1.223 0 0 0.307 0 0 13.200 2.605 Ex. 30 1.549 0 0 0.389 0 8.800 0 1.480
TABLE-US-00002 TABLE 2 Phenyl-based phosphonic acid Halogenated phenyl phosphonic acid Alkyl-based 4-bromo 4-chloro phosphonic Phenyl phenyl phenyl acid phos- phos- phos- n-butyl Alkoxysilane phonic phonic phonic phosphonic Copper monomer acid acid acid acid Ion MTES (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 mol) mol) mol) mol) mol) mol) Ex. 1 2.828 2.827 0 1.863 8.671 42.518 Ex. 2 2.828 2.827 0 1.863 8.671 25.513 Ex. 3 2.828 2.827 0 1.863 8.671 25.513 Ex. 4 2.828 2.827 0 1.863 8.671 25.513 Ex. 5 2.828 2.827 0 1.863 8.671 25.513 Ex. 6 2.828 2.827 0 1.863 8.671 25.513 Ex. 7 2.828 2.827 0 1.863 8.671 32.311 Ex. 8 2.828 2.827 0 1.863 8.671 56.124 Ex. 9 2.828 2.827 0 1.863 8.671 76.534 Ex. 10 2.828 2.827 0 1.863 8.671 153.067 Ex. 11 2.828 2.827 0 1.863 8.671 0 Ex. 12 2.828 2.827 0 1.863 8.671 0 Ex. 13 2.828 2.827 0 1.863 8.671 0 Ex. 14 2.828 2.827 0 1.863 8.671 53.152 Ex. 15 2.828 2.827 0 1.863 8.671 26.573 Ex. 16 2.828 2.827 0 1.863 8.671 33.455 Ex. 17 2.828 2.827 0 1.863 8.671 33.455 Ex. 18 5.655 0 0 1.863 8.671 42.518 Ex. 19 5.655 0 0 1.863 8.671 42.518 Ex. 20 1.695 3.958 0 1.863 8.671 42.518 Ex. 21 1.695 3.958 0 1.863 8.671 42.518 Ex. 22 2.828 0 2.825 1.863 8.671 42.518 Ex. 23 2.828 0 2.825 1.863 8.671 42.518 Ex. 24 2.828 2.827 0 0 6.194 30.370 Ex. 25 2.828 2.827 0 0 6.194 18.222 Ex. 26 2.828 2.827 0 0 6.194 18.222 Ex. 27 2.828 2.827 0 0 6.194 18.222 Ex. 28 2.828 2.827 0 0 6.194 18.222 Ex. 29 2.828 2.827 0 0 6.194 18.222 Ex. 30 2.828 2.827 0 0 6.194 23.079 Amount- of- substance Amount- ratio of of- trifunctional substance and ratio of bifunctional Alkoxysilane monomer alkoxysilane alkoxysilane MTMS DMDES TEOS monomer monomer (10.sup.3 (10.sup.3 (10.sup.3 to copper to copper mol) mol) mol) ion ion Ex. 1 0 0 11.928 6.279 4.903 Ex. 2 0 0 7.157 3.768 2.942 Ex. 3 0 0 7.157 3.768 2.942 Ex. 4 0 0 7.157 3.768 2.942 Ex. 5 0 0 7.157 3.768 2.942 Ex. 6 0 0 7.157 3.768 2.942 Ex. 7 0 0 9.067 4.772 3.726 Ex. 8 0 0 15.745 8.288 6.472 Ex. 9 0 0 21.471 11.302 8.826 Ex. 10 0 0 42.942 22.604 17.652 Ex. 11 42.570 0 11.928 6.285 4.909 Ex. 12 0 38.523 11.928 5.818 4.443 Ex. 13 0 38.523 11.928 5.818 4.443 Ex. 14 0 0 0 6.129 6.129 Ex. 15 0 0 29.823 6.504 3.064 Ex. 16 0 0 87.612 13.962 3.858 Ex. 17 0 0 87.612 13.962 3.858 Ex. 18 0 0 11.928 6.279 4.903 Ex. 19 0 0 11.928 6.279 4.903 Ex. 20 0 0 11.928 6.279 4.903 Ex. 21 0 0 11.928 6.279 4.903 Ex. 22 0 0 11.928 6.279 4.903 Ex. 23 0 0 11.928 6.279 4.903 Ex. 24 0 0 8.520 6.279 4.903 Ex. 25 0 0 5.112 3.767 2.942 Ex. 26 0 0 5.112 3.767 2.942 Ex. 27 0 0 5.112 3.767 2.942 Ex. 28 0 0 5.112 3.767 2.942 Ex. 29 0 0 5.112 3.767 2.942 Ex. 30 0 0 6.475 4.772 3.726
TABLE-US-00003 TABLE 3 Phenyl-based phosphonic acid Halogenated Alkyl- phenyl based phosphonic phos- acid phonic 4-bromo 4-chloro acid Phenyl phenyl phenyl n-butyl phos- phos- phos- phos- phonic phonic phonic phonic Copper Alkoxysilane monomer acid acid acid acid ion MTES MTMS DMDES TEOS (g) (g) (g) (g) (g) (g) (g) (g) (g) Ex. 31 0.447 0.670 0 0 0.394 7.148 0 0 2.343 Ex. 32 0.447 0.670 0 0 0.394 9.747 0 0 3.195 Ex. 33 0.447 0.670 0 0 0.394 19.494 0 0 6.390 Ex. 34 0.447 0.670 0 0 0.394 19.494 0 0 6.390 Ex. 35 0.447 0.670 0 0 0.394 19.494 0 0 6.390 Ex. 36 0.447 0.670 0 0 0.394 0 4.142 0 1.775 Ex. 37 0.447 0.670 0 0 0.394 0 4.142 0 1.775 Ex. 38 0.447 0.670 0 0 0.394 0 0 4.080 1.775 Ex. 39 0.447 0.670 0 0 0.394 0 0 4.080 1.775 Ex. 40 0.447 0.670 0 0 0.394 6.769 0 0 0 Ex. 41 0.447 0.670 0 0 0.394 3.384 0 0 1.438 Ex. 42 0.447 0.670 0 0 0.394 4.261 0 0 13.037 Ex. 43 0.447 0.670 0 0 0.394 4.261 0 0 13.037 Ex. 44 0.894 0 0 0 0.394 5.415 0 0 1.775 Ex. 45 0.894 0 0 0 0.394 5.415 0 0 1.775 Ex. 46 0.268 0.938 0 0 0.394 5.415 0 0 1.775 Ex. 47 0.268 0.938 0 0 0.394 5.415 0 0 1.775 Ex. 48 0.447 0 0.544 0 0.394 5.415 0 0 1.775 Ex. 49 0.447 0 0.544 0 0.394 5.415 0 0 1.775 Ex. 50 0 0 0 0.643 0.394 5.415 0 0 1.775 Ex. 51 0 0 0 0.643 0.394 5.415 0 0 1.775 Ex. 52 0 0 0 0.643 0.394 3.249 0 0 1.065 Ex. 53 0 0 0 0.643 0.394 4.115 0 0 1.349 Ex. 54 0 0 0 0.643 0.394 7.148 0 0 2.343 Ex. 55 0 0 0 0.643 0.394 9.747 0 0 3.195 Ex. 56 0 0 0 0.643 0.394 19.494 0 0 6.390 Ex. 57 0 0 0 0.643 0.394 2.978 0 0 0 Ex. 58 0 0 0 0.643 0.394 6.769 0 0 0 Ex. 59 0 0 0 0.643 0.394 6.769 0 0 0 Ex. 60 0 0 0 0.643 0.394 2.031 0 0 2.663 Ex. 61 0 0 0 0.643 0.394 3.384 0 0 4.438 Ex. 62 0 0 0 0.643 0.394 4.261 0 0 13.037 Ex. 63 0 0 0 0.643 0.394 4.261 0 0 13.037 Alkoxysilane monomer Silicone resin solid content Resin composition MTES MTMS DMDES TEOS X Y Z (g) (g) (g) (g) (g) (g) (g) (1) Ex. 31 2.691 0 0 0.676 0 8.800 0 1.047 Ex. 32 3.669 0 0 0.921 0 8.800 0 0.837 Ex. 33 7.338 0 0 1.843 0 8.800 0 0.477 Ex. 34 7.338 0 0 1.843 0 0 0 0.000 Ex. 35 7.338 0 0 1.843 0 0 0 0.000 Ex. 36 0 2.041 0 0.512 8.800 0 0 1.256 Ex. 37 0 2.041 0 0.512 0 8.800 0 1.256 Ex. 38 0 0 2.040 0.512 8.800 0 0 1.256 Ex. 39 0 0 2.040 0.512 0 8.800 0 1.256 Ex. 40 2.548 0 0 0.000 0 8.800 0 1.258 Ex. 41 1.274 0 0 1.280 0 8.800 0 1.256 Ex. 42 1.604 0 0 3.760 8.800 0 0 0.742 Ex. 43 1.604 0 0 3.760 0 8.800 0 0.742 Ex. 44 2.038 0 0 0.512 8.800 0 0 1.330 Ex. 45 2.038 0 0 0.512 0 8.800 0 1.330 Ex. 46 2.038 0 0 0.512 8.800 0 0 1.230 Ex. 47 2.038 0 0 0.512 0 8.800 0 1.230 Ex. 48 2.038 0 0 0.512 8.800 0 0 1.505 Ex. 49 2.038 0 0 0.512 0 8.800 0 1.505 Ex. 50 2.038 0 0 0.512 8.800 0 0 1.423 Ex. 51 2.038 0 0 0.512 0 8.800 0 1.423 Ex. 52 1.223 0 0 0.307 8.800 0 0 1.988 Ex. 53 1.549 0 0 0.389 8.800 0 0 1.716 Ex. 54 2.691 0 0 0.676 0 8.800 0 1.159 Ex. 55 3.669 0 0 0.921 0 8.800 0 0.907 Ex. 56 7.338 0 0 1.843 8.800 0 0 0.500 Ex. 57 1.121 0 0 0 8.800 0 0 2.366 Ex. 58 2.548 0 0 0 8.800 0 0 1.424 Ex. 59 2.548 0 0 0 0 8.800 0 1.424 Ex. 60 0.765 0 0 0.768 8.800 0 0 1.987 Ex. 61 1.274 0 0 1.280 8.800 0 0 1.422 Ex. 62 1.604 0 0 3.760 8.800 0 0 0.797 Ex. 63 1.604 0 0 3.760 0 8.800 0 0.797 (1) Mass ratio of resin composition (solid content) to sum of phosphonic acid, copper ion, and alkoxysilane monomer as expressed in terms of hydrolysis-polycondensation product
TABLE-US-00004 TABLE 4 Phenyl-based phosphonic acid Halogenated phenyl Alkyl- Amount-of- phosphonic based substance acid phosphonic Amount-of- ratio of 4-bromo- 4-chloro- acid substance trifunctional Phenyl phenyl phenyl n-butyl ratio of and phosphonic phosphonic phosphonic phosphonic Copper Alkoxysilane monomer alkoxysilane bifunctional acid acid acid acid Ion MTES MTMS DMDES TEOS monomer alkoxysilane (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 to copper monomer to mol) mol) mol) mol) mol) mol) mol) mol) mol) ion copper ion Ex. 31 2.828 2.827 0 0 6.194 40.090 0 0 11.247 8.288 6.472 Ex. 32 2.828 2.827 0 0 6.194 54.666 0 0 15.336 11.302 8.826 Ex. 33 2.828 2.827 0 0 6.194 109.332 0 0 30.673 22.604 17.652 Ex. 34 2.828 2.827 0 0 6.194 109.332 0 0 30.673 22.604 17.652 Ex. 35 2.828 2.827 0 0 6.194 109.332 0 0 30.673 22.604 17.652 Ex. 36 2.828 2.827 0 0 6.194 0 30.406 0 8.520 6.285 4.909 Ex. 37 2.828 2.827 0 0 6.194 0 30.406 0 8.520 6.285 4.909 Ex. 38 2.828 2.827 0 0 6.194 0 0 27.516 8.520 5.818 4.443 Ex. 39 2.828 2.827 0 0 6.194 0 0 27.516 8.520 5.818 4.443 Ex. 40 2.828 2.827 0 0 6.194 37.964 0 0 0 6.129 6.129 Ex. 41 2.828 2.827 0 0 6.194 18.979 0 0 21.303 6.504 3.064 Ex. 42 2.828 2.827 0 0 6.194 23.898 0 0 62.580 13.962 3.858 Ex. 43 2.828 2.827 0 0 6.194 23.898 0 0 62.580 13.962 3.858 Ex. 44 5.655 0 0 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 45 5.655 0 0 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 46 1.695 3.958 0 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 47 1.695 3.958 0 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 48 2.828 0 2.825 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 49 2.828 0 2.825 0 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 50 0 0 0 4.660 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 51 0 0 0 4.660 6.194 30.370 0 0 8.520 6.279 4.903 Ex. 52 0 0 0 4.660 6.194 18.222 0 0 5.112 3.767 2.942 Ex. 53 0 0 0 4.660 6.194 23.079 0 0 6.475 1.772 3.726 Ex. 54 0 0 0 4.660 6.194 40.090 0 0 11.247 8.288 6.472 Ex. 55 0 0 0 4.660 6.194 54.666 0 0 15.336 11.302 8.826 Ex. 56 0 0 0 4.660 6.194 109.332 0 0 30.673 22.604 17.652 Ex. 57 0 0 0 4.660 6.194 16.702 0 0 0 2.697 2.697 Ex. 58 0 0 0 4.660 6.194 37.964 0 0 0 6.129 6.129 Ex. 59 0 0 0 4.660 6.194 37.964 0 0 0 6.129 6.129 Ex. 60 0 0 0 4.660 6.194 11.391 0 0 12.783 3.903 1.839 Ex. 61 0 0 0 4.660 6.194 18.979 0 0 21.303 6.504 3.064 Ex. 62 0 0 0 4.660 6.194 23.898 0 0 62.580 13.962 3.858 Ex. 63 0 0 0 4.660 6.194 23.898 0 0 62.580 13.962 3.858
TABLE-US-00005 TABLE 5 Phenyl-based phosphonic acid Halogenated Alkyl- phenyl based phosphonic phos- acid phonic 4-bromo 4-chlor acid Phenyl phenyl phenyl n-butyl phos- phos- phos- phos- phonic phonic phonic phonic Copper Alkoxysilane monomer acid acid acid acid ion MTES MTMS DMDES TEOS (g) (g) (g) (g) (g) (g) (g) (g) (g) Comp. 0.447 0.670 0 0.257 0.551 1.516 0 0 0.497 Ex. 1 Comp. 0.447 0.670 0 0.257 0.551 3.336 0 0 1.093 Ex. 2 Comp. 0.447 0.670 0 0.257 0.551 4.169 0 0 0 Ex. 3 Comp. 0.447 0.670 0 0.257 0.551 2.843 0 0 3.728 Ex. 4 Comp. 0.447 0.670 0 0.257 0.551 0 0 0 12.425 Ex. 5 Comp. 0.447 0.670 0 0 0.394 1.083 0 0 0.355 Ex. 6 Comp. 0.447 0.670 0 0 0.394 2.383 0 0 0.781 Ex. 7 Comp. 0.447 0.670 0 0 0.394 2.978 0 0 0 Ex. 8 Comp. 0.447 0.670 0 0 0.394 2.031 0 0 2.663 Ex. 9 Comp. 0.447 0.670 0 0 0.394 0 0 0 8.875 Ex. 10 Comp. 0 0 0 0.643 0.394 1.083 0 0 0.355 Ex. 11 Comp. 0 0 0 0.643 0.394 0 0 0 8.875 Ex. 12 Alkoxysilane monomer Silicone resin solid content Resin composition MTES MTMS DMDES TEOS X Y Z (g) (g) (g) (g) (g) (g) (g) (1) Comp. 0.571 0 0 0.143 0 8.800 0 1.934 Ex. 1 Comp. 1.256 0 0 0.315 0 8.800 0 1.460 Ex. 2 Comp. 1.569 0 0 0 0 8.800 0 1.461 Ex. 3 Comp. 1.070 0 0 1.075 0 8.800 0 1.254 Ex. 4 Comp. 0 0 0 3.584 0 0 0 0.000 Ex. 5 Comp. 0.408 0 0 0.102 0 8.800 0 2.526 Ex. 6 Comp. 0.897 0 0 0.225 0 8.800 0 1.939 Ex. 7 Comp. 1.121 0 0 0 0 8.800 0 1.939 Ex. 8 Comp. 0.765 0 0 0.768 0 8.800 0 1.677 Ex. 9 Comp. 0 0 0 2.560 0 0 0 0.000 Ex. 10 Comp. 0.408 0 0 0.102 8.800 0 0 0.000 Ex. 11 Comp. 0 0 0 2.560 0 0 0 0.000 Ex. 12 (1) Mass ratio of resin composition (solid content) to sum of phosphonic acid, copper ion, and alkoxysilane monomer as expressed in terms of hydrolysis-polycondensation product
TABLE-US-00006 TABLE 6 Phenyl-based phosphonic acid Halogenated phenyl Alkyl- Amount-of- phosphonic based substance acid phosphonic Amount-of- ratio of 4-bromo 4-chloro acid substance trifunctional Phenyl phenyl phenyl n-butyl ratio of and phosphonic phosphonic phosphonic phosphonic Copper Alkoxysilane monomer alkoxysilane bifunctional acid acid acid acid Ion MTES MTMS DMDES TEOS monomer alkoxysilane (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 (10.sup.3 to copper monomer to mol) mol) mol) mol) mol) mol) mol) mol) mol) ion copper ion Comp. Ex. 1 2.828 2.827 0 1.863 8.671 8.502 0 0 2.386 1.256 0.981 Comp. Ex. 2 2.828 2.827 0 1.863 8.671 18.710 0 0 5.247 2.763 2.158 Comp. Ex. 3 2.828 2.827 0 1.863 8.671 23.382 0 0 0 2.696 2.696 Comp. Ex. 4 2.828 2.827 0 1.863 8.671 15.945 0 0 17.895 3.902 1.839 Comp. Ex. 5 2.828 2.827 0 1.863 8.671 0 0 0 59.642 6.878 0 Comp. Ex. 6 2.828 2.827 0 0 6.194 6.074 0 0 1.704 1.256 0.981 Comp. Ex. 7 2.828 2.827 0 0 6.194 13.365 0 0 3.749 2.763 2.158 Comp. Ex. 8 2.828 2.827 0 0 6.194 16.702 0 0 0 2.697 2.697 Comp. Ex. 9 2.828 2.827 0 0 6.194 11.391 0 0 12.783 3.903 1.839 Comp. Ex. 10 2.828 2.827 0 0 6.194 0 0 0 42.601 6.878 0 Comp. Ex. 11 0 0 0 4.660 6.194 6.074 0 0 1.704 1.256 0.981 Comp. Ex. 12 0 0 0 4.660 6.194 0 0 0 42.601 6.878 0
TABLE-US-00007 TABLE 7 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Ex. 1 156 403 597 194 437 571 134 700 952 252 Ex. 2 216 414 593 179 457 564 107 700 1015 315 Ex. 3 162 410 595 185 456 564 108 700 1004 304 Ex. 4 93 392 596 204 432 567 135 700 867 167 Ex. 5 99 397 593 196 448 562 114 700 845 145 Ex. 6 112 398 596 198 437 568 131 700 849 149 Ex. 7 187 406 598 192 444 571 127 700 1018 318 Ex. 8 167 404 597 193 435 571 136 700 971 271 Ex. 9 175 408 596 188 452 566 114 700 1032 332 Ex. 10 212 411 591 180 447 561 114 700 987 287 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Ex. 1 384 633 249 86.0 519 9.6 807 288 76.4 Ex. 2 389 631 242 85.0 518 8.0 830 312 77.0 Ex. 3 387 632 245 84.2 518 7.9 851 333 76.3 Ex. 4 370 632 262 84.0 522 12.7 775 253 71.2 Ex. 5 368 629 261 83.5 517 14.1 773 256 69.4 Ex. 6 370 631 261 85.0 517 13.7 775 258 71.2 Ex. 7 386 635 249 85.4 520 7.0 851 331 78.3 Ex. 8 385 633 248 86.6 520 9.1 816 296 77.5 Ex. 9 387 633 246 84.5 522 6.9 826 304 77.6 Ex. 10 389 629 240 85.1 514 9.4 813 299 75.7 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength
TABLE-US-00008 TABLE 8 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Ex. 11 131 400 594 194 431 568 137 700 893 193 Ex. 12 132 412 597 185 460 569 109 700 899 199 Ex. 13 144 413 597 184 461 567 106 700 906 206 Ex. 14 173 416 587 171 477 551 74 700 962 262 Ex. 15 157 401 598 197 433 570 137 700 1001 301 Ex. 16 154 402 600 198 436 574 138 700 949 249 Ex. 17 167 400 600 200 427 574 147 700 962 262 Ex. 18 131 393 603 210 441 579 138 700 890 190 Ex. 19 187 390 602 212 427 577 150 700 911 211 Ex. 20 70 414 597 183 458 568 110 700 1003 303 Ex. 21 161 410 597 187 443 570 127 700 1005 305 Ex. 22 166 425 591 166 487 555 68 700 1054 354 Ex. 23 180 423 583 160 700 1064 364 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Ex. 11 379 630 251 86.1 520 12.5 781 261 73.6 Ex. 12 384 633 249 84.4 525 11.4 782 257 73.0 Ex. 13 385 633 248 84.1 520 11.3 790 270 72.8 Ex. 14 387 628 241 82.1 522 101.1 819 297 72.0 Ex. 15 383 634 251 85.6 520 7.6 852 332 78.0 Ex. 16 382 635 253 86.7 526 9.4 811 285 77.3 Ex. 17 382 635 253 87.0 523 8.9 812 289 78.1 Ex. 18 369 637 268 86.1 524 11.1 783 259 75.0 Ex. 19 371 636 265 86.3 521 10.4 787 266 75.9 Ex. 20 391 634 243 84.3 521 7.2 857 336 77.1 Ex. 21 390 633 243 85.8 521 7.7 851 330 78.1 Ex. 22 392 631 239 82.1 526 6.7 830 304 75.4 Ex. 23 390 627 237 79.6 512 7.3 852 340 72.3 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength
TABLE-US-00009 TABLE 9 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Ex. 24 161 402 607 205 428 582 154 700 930 230 Ex. 25 206 416 606 190 459 578 119 700 953 253 Ex. 26 177 411 607 196 444 581 137 700 953 253 Ex. 27 72 390 606 216 430 579 149 700 897 197 Ex. 28 100 399 600 201 459 568 109 700 885 185 Ex. 29 142 399 599 200 456 568 112 700 885 185 Ex. 30 139 409 611 202 441 585 144 700 951 251 Ex. 31 170 405 607 202 434 581 147 700 938 238 Ex. 32 166 406 610 204 434 585 151 700 947 247 Ex. 33 193 411 603 192 452 573 121 700 948 248 Ex. 34 104 409 607 198 447 574 127 700 985 285 Ex. 35 97 403 612 209 419 587 168 700 998 298 Ex. 36 149 403 602 199 438 577 139 700 908 208 Ex. 37 152 401 603 202 428 578 150 700 913 213 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Ex. 24 385 641 256 86.9 529 9.3 801 272 77.6 Ex. 25 392 641 249 85.2 530 8.3 813 283 76.8 Ex. 26 391 643 252 85.8 520 8.0 816 296 77.8 Ex. 27 370 640 270 85.0 535 10.5 788 253 74.5 Ex. 28 369 636 267 83.4 526 11.5 782 256 71.9 Ex. 29 370 636 266 83.6 526 11.5 783 257 72.1 Ex. 30 390 645 255 86.0 524 7.5 852 328 78.5 Ex. 31 387 642 255 86.0 520 8.9 802 282 77.2 Ex. 32 389 644 255 86.6 522 7.9 814 292 78.7 Ex. 33 390 639 249 84.7 519 8.9 812 293 75.9 Ex. 34 391 644 253 83.9 520 8.0 828 308 75.9 Ex. 35 390 646 256 88.4 521 5.8 840 319 82.5 Ex. 36 382 637 255 86.2 525 10.9 787 262 75.3 Ex. 37 383 637 254 87.2 520 10.6 797 277 76.6 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength
TABLE-US-00010 TABLE 10 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Ex. 38 121 406 606 200 454 578 124 700 911 211 Ex. 39 130 403 605 202 442 578 136 700 906 206 Ex. 40 177 415 601 186 471 569 98 700 938 238 Ex. 41 148 406 611 205 431 586 155 700 953 253 Ex. 42 154 405 609 204 435 585 150 700 939 239 Ex. 43 157 401 611 210 420 588 168 700 938 238 Ex. 44 181 376 610 234 394 589 195 700 881 181 Ex. 45 259 375 613 238 386 593 207 700 886 186 Ex. 46 157 421 611 190 465 583 118 700 964 264 Ex. 47 152 415 612 197 443 586 143 700 961 261 Ex. 48 159 429 600 171 511 558 47 700 941 241 Ex. 49 182 424 597 173 503 553 50 700 949 249 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Ex. 38 383 640 257 84.3 538 10.0 794 256 74.3 Ex. 39 382 639 257 85.4 525 10.3 793 268 75.1 Ex. 40 389 639 250 83.4 524 9.2 808 284 74.2 Ex. 41 390 645 255 87.0 525 7.6 815 290 79.4 Ex. 42 387 643 256 86.8 529 8.5 815 286 78.3 Ex. 43 386 644 258 87.9 526 8.2 809 283 79.7 Ex. 44 356 641 285 88.1 532 10.7 785 253 77.4 Ex. 45 358 643 285 90.3 528 10.3 779 251 80.0 Ex. 46 399 645 246 84.8 534 7.1 825 291 77.7 Ex. 47 397 646 249 86.3 531 7.1 824 293 79.2 Ex. 48 392 638 246 81.1 539 9.0 809 270 72.1 Ex. 49 392 637 245 81.0 535 9.0 815 280 72.0 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength
TABLE-US-00011 TABLE 11 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Ex. 50 220 408 588 180 447 557 110 700 957 257 Ex. 51 342 411 582 171 453 548 95 700 988 288 Ex. 52 311 425 581 156 485 542 57 700 1024 324 Ex. 53 241 428 575 147 700 975 275 Ex. 54 150 406 588 182 441 558 117 700 958 258 Ex. 55 345 409 587 178 443 559 116 700 1036 336 Ex. 56 305 408 587 179 436 562 126 700 928 228 Ex. 57 295 453 556 103 700 1174 474 Ex. 58 215 400 592 192 427 564 137 700 922 222 Ex. 59 231 402 586 184 438 553 115 700 971 271 Ex. 60 237 412 589 177 459 556 97 700 954 254 Ex. 61 218 415 586 171 475 547 72 700 961 261 Ex. 62 222 395 597 202 418 571 153 700 917 217 Ex. 63 249 397 595 198 420 570 150 700 936 236 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Ex. 50 384 628 244 84.5 513 10.7 813 300 73.8 Ex. 51 386 624 238 83.6 510 10.2 822 312 73.4 Ex. 52 391 623 232 81.6 510 8.8 853 343 72.8 Ex. 53 391 621 230 79.8 510 10.9 813 303 68.9 Ex. 54 384 627 243 85.2 512 10.8 805 293 74.4 Ex. 55 386 626 240 85.7 510 8.1 852 342 77.6 Ex. 56 387 625 238 87.5 505 12.5 794 289 75.0 Ex. 57 394 613 219 75.3 519 4.7 863 344 70.6 Ex. 58 380 630 250 87.2 505 11.5 794 289 75.6 Ex. 59 379 628 249 84.9 505 9.8 812 307 75.1 Ex. 60 385 628 243 83.7 517 10.7 810 293 73.0 Ex. 61 385 628 243 82.0 509 10.5 818 309 71.5 Ex. 62 377 633 256 87.7 511 11.3 794 283 76.4 Ex. 63 379 632 253 88.3 506 10.9 798 292 77.4 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength
TABLE-US-00012 TABLE 12 Wavelength range in which Wavelength Wavelength transmittance range in range in is 20% or less which which within wavelength transmittance transmittance range from is 70% or more is 80% or more 700 to 1200 nm Minimum Maximum Minimum Maximum Minimum Maximum Calculated wave- wave- wave- wave- wave- wave- thickness length length Range.sup.*1 length length Range.sup.*1 length length Range.sup.*1 (m) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) (nm) Comp. 85 300 1198 898 Ex. 1 Comp. 169 505 568 63 700 1091 391 Ex. 2 Comp. 171 700 975 275 Ex. 3 Comp. 171 700 1095 395 Ex. 4 Comp. 161 300 1196 896 Ex.6 Comp. 170 700 976 276 Ex. 7 Comp. 169 700 953 253 Ex. 8 Comp. 188 300 1158 858 Ex. 9 Comp. 351 700 1025 325 Ex. 11 Minimum transmittance in wavelength range from Maximum 700 to .sub.IR- transmittance 1200 nm min- Tmax- .sub.UV.sup.*2 .sub.IR.sup.*3 .sub.UV T.sup.*4max .sup.*5max T.sup.*4min .sup.*5min max Tmin (nm) (%) (nm) (%) (nm) (%) (nm) (nm) (%) Comp. 17.0 545 9.7 860 315 7.3 Ex. 1 Comp. 415 626 211 72.3 539 5.8 853 314 66.5 Ex. 2 Comp. 423 622 199 68.8 543 9.4 823 280 59.3 Ex. 3 Comp. 470 601 131 57.6 547 7.1 851 304 50.5 Ex. 4 Comp. 6.5 565 4.0 865 300 2.6 Ex.6 Comp. 436 633 197 67.8 557 7.6 823 266 60.2 Ex. 7 Comp. 495 617 122 56.7 568 9.4 817 249 47.3 Ex. 8 Comp. 19.7 574 11.0 851 277 8.6 Ex. 9 Comp. 456 596 140 58.4 535 9.9 851 316 48.5 Ex. 11 .sup.*1Value obtained by subtracting minimum wavelength from maximum wavelength .sup.*2.sub.UV = UV cut-off wavelength .sup.*3.sub.IR = IR cut-off wavelength .sup.*4T = Transmittance .sup.*5 = Wavelength