LASHING BAR MADE OF A COMPOSITE MATERIAL AND METHOD OF MANUFACTURING SAME

Abstract

Disclosed is a lashing bar of a composite material formed through filament winding to provide light weight and capacity to withstand high tensile loads, and a method of manufacturing the same. The lashing bar includes continuous fibers with high tensile strength wound around the core in the center and the exteriors of thimbles with holes and encased by a composite material, and metal parts provided in certain areas where loads are concentrated.

Claims

1. A method of manufacturing lashing bars made of composite material, comprising, (a) forming a forming mold for a lashing bar by assembling a first thimble made of a metallic material on a first end of a cylindrical core made of a metallic material and a second thimble made of a metallic material on a second end of the cylindrical core; (b) loading the forming mold onto a filament winding machine; (c) winding continuous fibers around an outer circumference of the forming mold, by going and coming back from the first thimble to the second thimble via an outer surface of the cylindrical core, using filament winding technique; and (d) curing the continuous fibers wound around the outer circumference of the forming mold to form a lashing bar in which the cylindrical core is included inside cured continuous fibers, wherein the step of (c) includes: (c1) aligning the continuous fibers passing through the first thimble or the second thimble at 0 degree lengthwise on the outer surface of the cylindrical core; (c2) winding the continuous fibers passing through the first thimble or the second thimble on the outer surface of the cylindrical core at degrees not exceeding 15 lengthwise along said cylindrical core; (c3) winding the continuous fibers passing through the first thimble or the second thimble on the outer surface of the cylindrical core at 40 to 50 degrees lengthwise along the cylindrical core; and (c4) repeating the steps of (c1) to (c3) in order a plurality of number of times while applying a tension on the continuous fibers.

2. The method of claim 1, wherein the continuous fibers include glass fiber having tensile strength 3,1000-3,800 Mpa and tensile elasticity 75-78 Gpa,

3. The method of claim 1, wherein the continuous fibers include carbon fiber having tensile strength 4,200-6,100 Mpa and tensile elasticity 230-300 Gpa.

4. The method of claim 1, wherein the continuous fibers include aramid fiber having tensile strength approximately 3,600 Mpa and tensile elasticity 41-186 Gpa.

5. The method of claim 1, wherein the continuous fibers include polyethylene fiber having tensile strength 2,200-3,500 Mpa and tensile elasticity 89-116 Gpa.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIG. 1 shows conventional container lashing equipment.

[0020] FIGS. 2A and 2B are illustrative views of the shapes of conventional lashing bars made from metal.

[0021] FIG. 3 is a process flow chart to describe a method of manufacturing a lashing bar of a composite material according to the present invention.

[0022] FIG. 4 is a part drawing used in the manufacturing method of FIG. 3.

[0023] FIG. 5A to 5C show the process of winding continuous fibers through the filament winding technique used in the manufacturing method of FIG. 3.

[0024] FIGS. 6 and 7 show the lashing bar made of a composite material according to the invention.

[0025] FIG. 8 illustrates a table which shows tensile strengths of glass, carbon, aramid, and polyethylene fibers.

DETAILED DESCRIPTION

[0026] The following is a detailed description of a preferred embodiment of the present invention with reference to the accompanying drawings.

[0027] FIG. 3 is a process flow chart to describe a method of manufacturing a lashing bar of a composite material according to the present invention, FIG. 4 is a part drawing used in the manufacturing method of FIG. 3, FIG. 5A to 5C show the process of winding continuous fibers through the filament winding technique used in the manufacturing method of FIG. 3, and FIGS. 6 and 7 show the lashing bar made of a composite material according to the invention.

[0028] To begin with, a method of manufacturing a lashing bar made of a composite material according to the present invention with reference to FIG. 3 is described as the step in which the prepared parts are assembled as shown in FIG. 4 and then loaded onto the filament winding machine (step 110).

[0029] According to this embodiment, the prepared parts consist of a cylindrical core (210), hook-type thimbles (220), and two ring-type thimbles (230).

[0030] The said cylindrical core (210) constitutes the core of the center portion and a metal pipe thick enough to resist bending when tension is applied during the winding of continuous fibers.

[0031] On one end of the cylindrical core (210) are assembled the hook-type thimbles (220) and on the other end are assembled one or two ring-type thimbles (230) facing each other.

[0032] In this embodiment, the aforementioned thimbles (220, 230) are made from metal and serve as a framework for the winding of continuous fibers during the lashing bar manufacturing process and later constitute the coupling portion of a lashing bar that can be coupled to the hooks of a container and put on other rings.

[0033] The parts thus assembled are loaded onto the filament winding machine as the lashing bar forming mold (200) and then help wind the continuous fibers (240) according to the filament winding program (step 120).

[0034] Generally, the filament winding process is a fabrication technique by which the continuous filaments of fiber-reinforced plastic (FRP) are wound around and attached onto the surface of a mandrel through the application of tension, heated and cured, and then removed from the mandrel. The technique is used in the manufacture of rotationally symmetrical structures such as cylindrical or spherical pressure vessels, tanks, and pipes.

[0035] In the present invention, as shown in FIG. 5A or 5C, the aforementioned filament winding technique is applied to the alignment of the continuous fibers forming a composite material in the lashing bar forming mold (200) assembled with the central portion core (210) and the thimbles on both ends (220, 230).

[0036] In aligning continuous fibers, as shown in the plan view of FIG. 5B, the most effective method of transmitting lengthwise tensile strength is the sub-step of {circle around (1)} by which to align the continuous fibers (240) passed through the holes of the hook-type thimbles (220) lengthwise (0 degrees).

[0037] Then, in the second alignment sub-step ({circle around (2)}), the continuous fibers (240) are aligned at degrees not exceeding 15 to minimize the loss of tensile strength while the fibers are evenly distributed lengthwise along the cylindrical core (210).

[0038] Then, in the third alignment sub-step ({circle around (3)}), the continuous fibers (240) are aligned at 40 to 50 degrees to efficiently and adequately resist torsion loads that arise during installation.

[0039] In alignment order of {circle around (1)}.fwdarw.{circle around (2)}.fwdarw.{circle around (3)}, the winding of the continuous fibers (240) is to be repeated a certain number of times until the fibers are attached through the application of tension to the surface of the lashing bar forming mold (20).

[0040] FIG. 5c shows a front view of the alignment of the continuous fibers.

[0041] The types of the continuous fibers (240) to be applied in the present invention are glass, carbon, aramid, and polyethylene fibers. The tensile strengths of these fibers are generally higher than the tensile strength of high-tensile steels as shown in Table in FIG. 8.

[0042] While the continuous fibers (240) forming the aforementioned composite material are wound and attached by tension to the surface of the lashing bar forming mold (200), the product is mounted in a rotating curing oven and then cured (step 130). Then, the product is transferred to the stripping/finishing process by which sharp edges on the surface are removed in a finishing workshop equipped with a dust collector (step 140).

[0043] Next, the stripped/finished product is tested for its capacity to withstand tensile and torsion loads (step 150) and, when the product meets its requirements, it is packaged and shipped (step 160).

[0044] A lashing bar made of a composite material manufactured and finished through the aforementioned processes according to the present invention will have the shape shown in FIGS. 6 and 7.

[0045] As shown in FIGS. 6 and 7, the lashing bar made of a composite material provided in the present invention (300) is an eye type comprising a bar-shaped central portion (310), an oval coupling portion on one end (320) and a hook coupling portion on the opposite end (330).

[0046] As shown in an enlarged view, the oval coupling portion (320) comprises a hook-type metal thimble (220) featuring a hole into which the continuous fiber composite material (240) is integrated.

[0047] In the middle of the bar-shaped central portion (310) is located the metal cylindrical core (210) and on its outer circumference, the continuous fiber composite material (240) is integrated.

[0048] While its two metal ring-type thimbles (230) face each other, the hook coupling portion (330) is coupled to the container hook (250) in between the thimbles, and the bolts (260) pass the holes on the thimbles (230) fastening these hooks. Meanwhile, the continuous fiber composite material (240) is integrated into the holes of the ring-type thimbles (230).

[0049] Therefore, the lashing bar made of a composite material manufactured through the present invention (300) provides light weight and capacity to withstand tensile loads.

[0050] The foregoing description illustrates an embodiment of the invention pertaining to the manufacturing of eye-type lashing bars, but it will become apparent to those skilled in the art having read this detailed description that they can manufacture knob-type lashing bars through the alignment of continuous fibers through the above-described process of assembling the lashing bar forming mold (200) using the cylindrical core (210) on which stoppers are formed lengthwise at certain intervals.

[0051] The disclosed embodiment of the present invention is given by way of illustration only, and various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art. Therefore, such changes and modifications may be made without departing from the scope of the invention defined in claims.