Synthesis of zeolite with the CHA crystal structure, synthesis process and use thereof for catalytic applications

Abstract

Disclosed is a synthesis process of a crystalline material with the CHA structure, which comprises the following steps: i) Preparation of a mixture that comprises one source of water, one source of a tetravalent element Y, one source of an alkaline or alkaline earth cation (A), one source of a trivalent element X, and one organic molecule (OSDA1) with the structure [R.sup.1R.sup.2R.sup.3R.sup.4N.sup.+]Q.sup., being the molar composition: n X.sub.2O.sub.3:YO.sub.2:a A:m OSDA1:z H.sub.2O, ii) crystallisation of the mixture obtained in i) in a reactor, iii) recovery of the crystalline material obtained in ii).

Claims

1. A zeolite material with the CHA structure having the diffraction pattern as shown in FIG. 1, and having the following molar composition after being calcined:
nX.sub.2O.sub.3:YO.sub.2 where X is a trivalent element; Y is a tetravalent element; and n ranges between 0 and 0.1.

2. The zeolite material with the CHA structure according to claim 1, wherein the tetravalent element Y is selected from silicon, tin, titanium, germanium, and combinations thereof.

3. The zeolite material with the CHA structure according to claim 1, wherein the tetravalent element Y is silicon.

4. The zeolite material with the CHA structure according to claim 1, wherein the trivalent element X is selected from aluminium, boron, iron, indium, gallium, and combinations thereof.

5. The zeolite material with the CHA structure according to claim 1, wherein the trivalent element X is aluminium.

6. A material which comprises the zeolite material with the CHA structure according to claim 1 having ion exchanged cations.

7. The material according to claim 6, wherein the ion exchanged cations are selected from metals, protons, proton precursors, and mixtures thereof.

8. The material according to claim 7, wherein the ion exchanged cations are of a metal selected from rare earth metals, metals of groups IIA, IIIA, IVA, VA, IB, BB, III, IVB, VB, VIB, VIIB, and VIII, and combinations thereof.

9. The material according to claim 8, wherein the metal is copper.

10. A method for converting, eliminating, or separating feeds formed by organic compounds in a high-added-value product, which comprises bringing said feed into contact with a zeolite material according to claim 1.

11. A method of producing an olefin, which comprises contacting an oxygenated organic compound with a zeolite material according to claim 1.

12. A method of selective catalytic reduction (SCR) of NOx (nitrogen oxides) in a gas stream, which comprises contacting the gas stream with a zeolite material according to claim 1.

13. A material which is obtainable by eliminating the organic content retained inside zeolite material according to claim 1 by means of a heat treatment at temperatures ranging between 100 C. and 1000 C. for a period of time ranging between 2 minutes and 25 hours.

14. A method for converting, eliminating, or separating feeds formed by organic compounds in a high-added-value product, which comprises bringing said feed into contact with a material according to claim 13.

15. A method of producing an olefin, which comprises contacting an oxygenated organic compound with a material according to claim 13.

16. A method of selective catalytic reduction (SCR) of NOx (nitrogen oxides) in a gas stream, which comprises contacting the gas stream with a material according to claim 13.

Description

BRIEF DESCRIPTION OF THE FIGURES

(1) FIG. 1 shows the diffraction pattern of the material obtained in Example 1 of the present invention.

(2) The present invention is illustrated by means of the following examples, which are not intended to limit the scope of the invention.

EXAMPLES

Example 1: Synthesis of CHA Using Tetraethylammonium as the OSDA

(3) 1037.2 mg of an aqueous solution of tetraethylammonium hydroxide (TEAOH, Sigma Aldrich, 35% by weight in water) are mixed with 477.1 mg of a 20%-by-weight aqueous solution of sodium hydroxide (NaOH, Sigma-Aldrich, 98%) and 34 mg of Milli-Q water. The mixture is homogenised by being kept under stirring. Finally, 791.0 mg of zeolite Y (CBV-720, SiO.sub.2/Al.sub.2O.sub.3 molar ratio=21) are added, and the mixture is kept under stirring until the desired concentration is achieved. The composition of the final gel is SiO.sub.2/0.047 Al.sub.2O.sub.3/0.2 TEAOH/0.2 NaOH/5 H.sub.2O. This gel is transferred to a teflon-lined steel autoclave and heated at 160 C. for 7 days. Once this time has elapsed, the product obtained is recovered by means of filtration and washed abundantly with water. By means of X-ray diffraction, it is observed that the solid obtained presents the characteristic peaks of the CHA structure (see FIG. 1). The solid yield obtained is greater than 85%.

(4) The material is calcined at 550 C. for 4 h in an air atmosphere in order to eliminate the organic matter retained inside it.

Example 2: Synthesis of CHA Using Tetraethylammonium as the OSDA

(5) 4494.4 mg of an aqueous solution of tetraethylammonium hydroxide (TEAOH, Sigma Aldrich, 35% by weight in water) are mixed with 2047.1 mg of a 20%-by-weight aqueous solution of sodium hydroxide (NaOH, Sigma-Aldrich, 98%) and 9525.0 mg of Milli-Q water. The mixture is homogenised by being kept under stirring. Finally, 3670.2 mg of zeolite Y (CBV-712, SiO.sub.2/Al.sub.2O.sub.3 molar ratio=12) are added, and the mixture is kept under stirring until the desired concentration is achieved. The composition of the final gel is SiO.sub.2/0.083 Al.sub.2O.sub.3/0.2 TEAOH/0.2 NaOH/15 H.sub.2O. This gel is transferred to a teflon-lined steel autoclave and heated at 160 C. for 7 days. Once this time has elapsed, the product obtained is recovered by means of filtration and washed abundantly with water. By means of X-ray diffraction, it is observed that the solid obtained presents the characteristic peaks of the CHA structure. The solid yield obtained is greater than 85%.

(6) The material is calcined at 550 C. for 4 h in an air atmosphere in order to eliminate the organic matter.

Example 3: Synthesis of Triethylpropylammonium Hydroxide

(7) 12.8 ml of triethylamine (C.sub.6H.sub.15N, Sigma Aldrich, 99%) are dissolved in 250 ml of acetonitrile (CH.sub.3CN, Scharlau, 99%). This solution is kept under stirring whilst 44 ml of 1-iodopropane (C.sub.3HI, Sigma Aldrich, 99%) are added drop by drop. After the addition is completed, the mixture is heated under reflux at 80 C. for 3 days. Once this time has elapsed, the mixture is partially concentrated in the rotary evaporator and an excess of diethyl ether (C.sub.4H.sub.10O, Scharlau, 99.5%) is added in order to precipitate the final product triethylpropylammonium iodide, which is vacuum filtered and washed with diethyl ether, to obtain a yield of 88%.

(8) Finally, ion exchange of the triethylpropylammonium halide is performed with the corresponding hydroxide. To this end, a solution of 10 g of triethylpropylammonium iodide in 73.7 g of water is prepared, and 37 g of the ion-exchange resin Amberlite (Amberlite IRN78, hydroxide form, Supelco) are added to this mixture. The mixture is kept under stirring overnight and, once this time has elapsed, it is vacuum filtered in order to separate the final product, triethylpropylammonium hydroxide, from the resin. The solution obtained is titrated with hydrochloric acid (HCl, Sigma Aldrich, 0.1 M), resulting in a concentration of 7.1% by weight and 75% exchange.

Example 4: Synthesis of CHA Using Triethyl Propylammonium as the OSDA

(9) 3064.5 mg of a solution of triethylpropylammonium hydroxide (TEPrOH, 7.1% by weight, prepared according to Example 3 of the present invention) are mixed with 274.0 mg of a 20%-by-weight solution of sodium hydroxide (NaOH, 98%) in water. The mixture is homogenised by being kept under stirring. Finally, 435.0 mg of zeolite Y (CBV-720, SiO.sub.2/Al.sub.2O.sub.3 molar ratio=21) are added, and the mixture is kept under stirring until the desired concentration is achieved. The composition of the final gel is SiO.sub.2/0.047 Al.sub.2O.sub.3/0.2 TEPrOH/0.2 NaOH/5 H.sub.2O. This gel is transferred to a teflon-lined steel autoclave and heated at 160 C. for 7 days. Once this time has elapsed, the product obtained is recovered by means of filtration and washed abundantly with water. By means of X-ray diffraction, it is observed that the solid obtained primarily presents the characteristic peaks of the CHA structure.

(10) The material is calcined at 550 C. for 4 h in an air atmosphere in order to eliminate the organic matter.

Example 5: Preparation of the Cu-Exchanged Zeolite CHA (Cu-CHA)

(11) The sample synthesised and calcined according to the method explained in Example 1 is washed with 150 g of a 0.04 M aqueous solution of sodium nitrate (NaNO.sub.3, Fluka, 99% by weight) per gram of zeolite.

(12) 33.63 mg of copper acetate [(CH.sub.3COO).sub.2Cu.H.sub.2O, Probus, 99%] are dissolved in 30 g of water, and 303.3 mg of the previously washed zeolite are added. The suspension is kept under stirring for 24 h. Once this time has elapsed, the product obtained is recovered by means of filtration and washed abundantly with water. Finally the material is calcined in air at 550 C. for 4 h.

Example 6: Catalytic Assay of the SCR Reaction of NOx

(13) The catalytic activity of the Cu-CHA sample synthesised according to Example 5 of the present invention in the selective catalytic reduction of NOx is studied using a fixed-bed tubular quartz reactor 1.2 cm in diameter and 20 cm long. In a typical experiment, the catalyst is compacted into particles with a size ranging between 0.25-0.42 mm; these are introduced into the reactor and the temperature is increased until 550 C. are reached (see the reaction conditions in Table 1); subsequently, this temperature is maintained for one hour under a flow of nitrogen. Once the desired temperature has been reached, the reaction mixture is fed. The SCR of NOx is studied using NH.sub.3 as the reducing agent. The NOx present in the reactor outlet gas is continuously analysed by means of a chemiluminiscent detector (Thermo 62C).

(14) TABLE-US-00001 TABLE 1 Reaction conditions for the SCR of NOx Total gas flow (ml/min) 300 Catalyst load (mg) 40 NO concentration (ppm) 500 NH.sub.3 concentration (ppm) 530 O.sub.2 concentration (%) 7 H.sub.2O concentration 5 Tested temperature range ( C.) 170-550

(15) The catalytic results of the Cu-CHA catalyst prepared according to Example 5 of the present invention are summarized in Table 2.

(16) TABLE-US-00002 TABLE 2 Conversion (%) of NOx at different temperatures (200 C., 250 C., 300 C., 350 C., 400 C., 450 C., 500 C.) using the Cu-CHA catalyst prepared according to Example 5 of the present invention Conversion (%) of NOx at different temperatures 210 C. 250 C. 300 C. 350 C. 400 C. 450 C. 500 C. 550 C. Example 5 94.9 100.0 100.0 100.0 100.0 99.7 95.5 90.8