REPAIR PATCH FOR AN ELASTOMER COMPONENT WITH AN IMPROVED CONNECTION LAYER

Abstract

A repair patch for an elastomeric element, particularly for a vehicle tire, use thereof and method for bonding a repair patch to an elastomeric element. The repair patch (1) comprises: a top layer (10), a bonding layer (30) for covering a wall (80) of the elastomeric element (40), and at least one intermediate layer (20) arranged between the bonding layer (30) and the top layer (10), wherein prior to vulcanization with the elastomeric element (40), the bonding layer (30) has a first and a second natural rubber component, wherein the first natural rubber component has a lower molecular weight Mw than the second natural rubber component, such that a mixture of the first and second natural rubber components has a bimodal molecular weight distribution.

Claims

1. A repair patch for an elastomeric element, particularly for a vehicle tire, comprising: a top layer, a bonding layer for covering a wall of the elastomeric element, and at least one intermediate layer disposed between the bonding layer and the top layer, wherein prior to vulcanization with the elastomeric element, the bonding layer has a first and a second natural rubber component, wherein the first natural rubber component has a lower molecular weight Mw than the second natural rubber component, such that a mixture of the first and second natural rubber components has a bimodal molecular weight distribution.

2. The repair patch according claim 1, wherein a Mooney viscosity of the first natural rubber component and the second natural rubber component is different by at least a factor of 2.

3. The repair patch according to claim 2, wherein the Mooney viscosity ML=1+4/100° C. of the first natural rubber component is 35 to 40 MU.

4. The repair patch according to claim 2, wherein the Mooney viscosity ML=1+4/100° C. of the second natural rubber component is 70 to 90 MU.

5. The repair patch according to claim 1, wherein the first natural rubber component and/or the second natural rubber component consist of a mixture of natural rubbers.

6. The repair patch according to claim 1, wherein the first natural rubber component and/or the second natural rubber component consist of a single natural rubber.

7. The repair patch according to claim 1, wherein the first natural rubber component has a molecular weight of Mw=1×10.sup.6 g/mol, and wherein the molecular weight is determined by diffusion-sedimentation and/or osmosis.

8. The repair patch according to claim 1, wherein the second natural rubber component has a molecular weight of Mw=2×10.sup.6 g/mol, and wherein the molecular weight is determined by diffusion-sedimentation and/or osmosis.

9. The repair patch according to claim 1, wherein a proportion of the first natural rubber component is 25 to 50 wt. % based on the total mass of the first and second natural rubber components, and a proportion of the second natural rubber component is 50 to 75 wt. % based on the total mass of the first and second natural rubber components.

10. The repair patch according to claim 1, wherein the bonding layer additionally comprises a filler system of a precipitated silica 5 to 15%, a silica 20 to 30% and a colourant.

11. The repair patch according to claim 1, wherein the bonding layer comprises at least 2% sulfur.

12. The repair patch according to claim 1, wherein a removable protective film is provided which protects the bonding layer from contamination until it is used.

13. The repair patch according to claim 1, wherein the intermediate layer comprises a plurality of fibrous inserts arranged in a substantially structured manner.

14. The repair patch according to claim 1, wherein the repair patch is used for repairing a damaged vehicle tire.

15. A method for bonding a repair patch according to claim 1 to an elastomeric element, comprising the steps: preparing a bonding layer comprising first and second natural rubber components, wherein the first natural rubber component has a lower molecular weight Mw, than the second natural rubber component, such that a mixture of the first and second natural rubber components has a bimodal molecular weight distribution, by: (a) homogenizing the second natural rubber component in an internal mixer; (b) re-extracting the second natural rubber component; and (c) mixing the first and homogenized second natural rubber components; providing the elastomeric element; applying the repair patch to the elastomeric element over the bonding layer, in particular at a repair area; and vulcanizing the repair patch to the elastomeric element.

16. The method according to claim 15, wherein in step c) of manufacturing the bonding layer, the first and the homogenized second natural rubber components are additionally mixed with at least 2% sulfur, and a filler system comprising a precipitated silica 5 to 15%, a silica 20 to 30% and a colourant.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0027] FIG. 1 schematically illustrates a sectional view of a repair patch for a vehicle tire according to an embodiment.

[0028] FIG. 2 schematically illustrates a bimodal molecular weight distribution resulting from the superposition of two unimodal molecular weight distributions of a first and a second natural rubber component.

[0029] FIG. 3 illustrates a block diagram of a portion of a method for bonding a repair patch to an elastomeric element according to an embodiment.

[0030] FIG. 4 illustrates a bar diagram of the different adhesive strengths of a bonding layer with natural rubber in unimodal and bimodal molecular weight distribution.

[0031] FIG. 5 illustrates a bar diagram relating to the structural resistance of a bonding layer with natural rubber in unimodal and bimodal molecular weight distribution.

DETAILED DESCRIPTION OF THE FIGURES AND PREFERRED EMBODIMENTS

[0032] Examples or embodiments of the present invention are schematically described below with reference to the accompanying figures. It is noted, however, that the present invention is in no way limited or restricted to the examples of embodiments and their features described below, but further encompasses modifications of the examples of embodiments, in particular those encompassed by modification of the features of the examples described or by combination of individual or multiple features of the examples described within the scope of protection of the claims.

[0033] With reference to FIG. 1, a repair patch 1 for vehicle tires according to the present invention is schematically illustrated. A top layer 10 is formed on the upper surface of the repair patch 1, which has no ready-made tack before and after repair. An intermediate layer 20 is formed adjacent to the top layer 10. In a preferred embodiment, the intermediate layer 20 may comprise a plurality of fibrous inserts 70. These inserts 70 may be arranged in one or more layers across the thickness of the intermediate layer 20, and each individual layer may have a structural arrangement of the fibrous inserts 70. The orientation of the individual layers in the intermediate layer 20 may be different from each other. Particularly, in the case of major damage in the tread or sidewall area, these inserts 70 may serve to bridge the reinforcing members interrupted in the damage area.

[0034] The bonding layer 30 is formed underneath the repair patch 1, which is in contact with the wall 80 of the vehicle tire during and after the repair. Furthermore, the bonding layer 30 is in contact with a raw rubber composition 50 before and after vulcanization of the vehicle tire. The bonding layer 30 and its specific properties are described in detail below with reference to FIG. 2.

[0035] As part of the repair of the damaged vehicle tire, the damaged area of the vehicle tire is roughened to remove dust and dirt and to expose an undamaged layer of components contained within the vehicle tire, forming a substantially conical shape for a repair area 60 in the vehicle tire. The repair area 60 is then filled with the raw rubber composition 50 prior to vulcanization of the bonding layer 30.

[0036] The repair patch 1 is then placed on the repair area 60, the dimensions of which are chosen so that the repair area 60 is completely covered by it. Furthermore, the dimensions of the repair patch 1 should be chosen such that the tire wall 80 is sufficiently covered by the bonding layer 30 for a stable bond. The repair patch 1 may, for example, be preheated to an appropriate joining temperature.

[0037] After the repair patch 1 has been applied to the tire, the repair area 60 and the repair patch 1 are vulcanized under pressure and temperature by means of a suitable device or in an autoclave.

[0038] In a preferred embodiment, a removable protective film may also be provided to protect the bonding layer 30 from contamination until it is used.

[0039] The structure of the vehicle tire is shown as an example for the sidewall region of a radial truck tire in such a way that the wall 80 of the vehicle tire is formed by the inner liner 90, the carcass 100 adjoining the inner liner and having the cord 120 in the form of an insert. Adjacent to the carcass 100 is the sidewall rubber 110 of vehicle tire.

[0040] Referring to FIG. 2, a bimodal molecular weight distribution (solid line) is schematically shown from the superposition of two unimodal molecular weight distributions for a first (dashed line) and a second (dotted line) natural rubber component respectively. As shown in FIG. 2, the first natural rubber component has a lower molecular weight Mw than the second natural rubber component, as indicated by the position of the maximum. Both the first and the second natural rubber components have a unimodal molecular weight distribution. This results from the fact that natural rubber generally always has a certain molecular weight distribution, wherein the width of the curve may be an indicator of the purity or quality of the natural rubber.

[0041] If the first and second natural rubber components are now mixed together, the bimodal molecular weight distribution results from the superposition of the two unimodal molecular weight distributions corresponding to the mixing proportions. The position of the two maxima in the bimodal molecular weight distribution is also determined by the difference of the maxima of the unimodal molecular weight distributions. If, for example, the maxima of the two unimodal molecular weight distributions are close to each other, i.e., if the first and second natural rubber components have molecular weights that are close to each other, this is also reflected in the bimodal distribution. The same applies in the reverse case. According to the invention, a bimodal molecular weight distribution is thus bimodal as long as two maxima may be identified. However, in a preferred embodiment, the first natural rubber component may have a molecular weight of Mw=1×10.sup.6 g/mol. In a further preferred embodiment, the second natural rubber component may have a molecular weight of Mw=2×10.sup.6 g/mol. In both embodiments, the molecular weight may be determined by diffusion sedimentation and/or osmosis.

[0042] Since natural rubber as a natural product contains insoluble gel components, the molecular weight of natural rubber is often difficult to determine. Alternatively, or additionally, the so-called Mooney viscosity may therefore be used for characterization. In a preferred embodiment, a Mooney viscosity of the first natural rubber component and the second natural rubber component may therefore differ by at least a factor of 2. In a particularly preferred embodiment, the Mooney viscosity ML=1+4/100° C. of the first natural rubber component may be 35 to 40 MU. In a further preferred embodiment, the Mooney viscosity ML=1+4/100° C. of the second natural rubber component may be 70 to 90 MU. The Mooney viscosity may be determined according to DIN 53523, for example.

[0043] As also shown in FIG. 2, the bonding layer's adhesive strength may be adjusted via the proportion of the first natural rubber component and the intensity of load via the second natural rubber component. According to the invention, the proportion of the first and second natural rubber components in the mixture is not limited. However, in a preferred embodiment, a proportion of the first natural rubber component may be 25 to 50 wt % based on the total mass of the first and second natural rubber components, and a proportion of the second natural rubber component may be 50 to 75% wt % based on the total mass of the first and second natural rubber components. Particularly preferably the proportion of the first natural rubber component may be 35 to 45 wt % and the proportion of the second natural rubber component may be 55 to 65 wt %. Even further particularly preferably the proportion of the first natural rubber component may be 44 wt % and the proportion of the second natural rubber component may be 56 wt %. Advantageously, however, greater importance is attached to the adhesive strength, so that the proportion of the first natural rubber component is selected so that the adhesive strength is high even with improved intensity of load.

[0044] According to the invention, it is not of any significance whether the first and/or the second natural rubber component is a single natural rubber or a mixture of natural rubbers. As mentioned above, natural rubber, considered as a single component, will generally always already have a certain molecular weight distribution. However, this is equally true for mixtures of two or more individual natural rubbers, which may be prepared to have a corresponding unimodal molecular weight distribution. In a preferred embodiment, therefore, the first natural rubber component and/or the second natural rubber component may comprise a mixture of natural rubbers. In another preferred embodiment, the first natural rubber component and/or the second natural rubber component may comprise a single natural rubber.

[0045] Furthermore, in a preferred embodiment, the bonding layer 30 may additionally comprise, in addition to the first natural rubber component and the second natural rubber component, a filler system of a precipitated silica 5 to 15%, a silica 20 to 30% and a colourant.

[0046] Furthermore, in another preferred embodiment, the bonding layer may contain at least 2% sulfur. During vulcanization, the first and second natural rubber components may thus be cross-linked via sulfur bridges.

[0047] With reference to FIG. 3, a portion of a method for bonding a repair patch to an elastomeric element according to an embodiment is described below. As shown in FIG. 3, in order to produce a bonding layer comprising a first and a second natural rubber component, wherein the first natural rubber component has a lower molecular weight Mw than the second natural rubber component, in such a way a mixture of the first and the second natural rubber component has a bimodal molecular weight distribution, the second natural rubber component is first homogenized in an internal mixer in step S101. After homogenization, the second natural rubber component is removed from the internal mixer again in step S102. The now homogenized second natural rubber component is then mixed with the first natural rubber component. According to the embodiment shown in FIG. 3, in step S103 the homogenized second natural rubber component may be mixed with the first natural rubber component, the filler system described above and at least 2% sulfur.

[0048] The steps described with reference to FIG. 3 are part of the process according to the invention, which further comprises the following steps: Providing an elastomeric element; applying the repair patch to the elastomeric element over the bonding layer, in particular at a repair area; and vulcanizing the repair patch to the elastomeric element.

[0049] The advantages of the present invention will now be explained with reference to FIGS. 4 and 5. In particular, the repair patch and method described herein allow the properties of the bonding layer to be tailored based on the bimodal molecular weight distribution of the two natural rubber components with respect to the compatibility of the repair patch with different tire casings or different roughened structures of damaged areas. As may be seen from FIGS. 4 and 5, the mixture of the first and second natural rubber components with bimodal molecular weight distribution not only exhibits improved adhesive strength compared to a respective unimodal distribution in the natural rubber component, but also simultaneously exhibits improved structural resistance. In other words, a bonding layer having a bimodal molecular weight distribution by mixing a first and a second natural rubber component shows an improved ability to bond to roughened surfaces due to the proportion of low molecular weight natural rubber, whereas due to the proportion of high molecular weight natural rubber, an increased structural resistance of the bonding layer may be achieved, resulting in improved durability.

LIST OF REFERENCE SIGNS

[0050] 1 repair patch [0051] 10 top layer [0052] 20 intermediate layer [0053] 30 bonding layer [0054] 40 elastomeric element [0055] 50 raw rubber composition [0056] 60 repair area [0057] 70 fibrous insert [0058] 80 wall [0059] 90 inner liner [0060] 100 carcass [0061] 110 sidewall rubber of vehicle tire [0062] 120 cord